WO2024090189A1 - リサイクル可能な硬化性シリコーン樹脂組成物 - Google Patents
リサイクル可能な硬化性シリコーン樹脂組成物 Download PDFInfo
- Publication number
- WO2024090189A1 WO2024090189A1 PCT/JP2023/036668 JP2023036668W WO2024090189A1 WO 2024090189 A1 WO2024090189 A1 WO 2024090189A1 JP 2023036668 W JP2023036668 W JP 2023036668W WO 2024090189 A1 WO2024090189 A1 WO 2024090189A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- formula
- silicone resin
- resin composition
- curable silicone
- Prior art date
Abstract
加熱により容易に液状化することが可能で、かつリサイクルが可能なシリコーン樹脂組成物の提供。 （Ａ）数平均分子量が５００～４０，０００のフラニル基含有オルガノポリシロキサンと、（Ｂ）数平均分子量が５００～４０，０００のマレイミド基含有オルガノポリシロキサンとを含む硬化性シリコーン樹脂組成物。該硬化性シリコーン樹脂組成物の硬化物を１３０℃以上に加熱する工程を有する、硬化性シリコーン樹脂組成物のリサイクル方法。
Description
本発明は、リサイクル可能な硬化性シリコーン樹脂組成物に関する。
シリコーン樹脂は、建築向けのシーリングや車体のコーティング剤など様々な分野で使用されている。しかし、シリコーン樹脂は熱硬化性樹脂であるため、加熱による解体及び再資源化（リサイクル）が困難である。酸や塩基を用いたり、４００℃を超えるような超高温環境に曝したりして主鎖クラッキングによる解重合は可能である。しかし、中和工程に伴う廃液処理の問題や、再重合に要するエネルギーの問題があるためリサイクルは難しい。
特許文献１では熱膨張性マイクロカプセルをシリコーン樹脂に配合することで、解体性を付与する試みが開示されている。しかし、解体後のシリコーン樹脂のリサイクルについては述べられていない。
従って、本発明は、加熱により容易に液状化することが可能で、かつ、リサイクルが可能なシリコーン樹脂組成物を提供することを目的とする。
本発明者は、上記の課題を解決すべく、鋭意研究を重ねた結果、フラニル基含有オルガノポリシロキサンと、マレイミド基含有オルガノポリシロキサンとを含むシリコーン樹脂組成物が、１３０℃以上の温度で液状化する、リサイクル可能な硬化性シリコーン樹脂組成物であることを見出し、本発明を完成させた。
即ち、本発明は、下記のリサイクル可能な硬化性シリコーン樹脂組成物を提供する。
［１］
下記（Ａ）及び（Ｂ）成分；
（Ａ）下記式（１）で表される数平均分子量が５００～４０，０００のフラニル基含有オルガノポリシロキサン、
（式（１）中、Ｒ1は、独立して、水素原子、炭素数１～１０の１価炭化水素基、炭素数１～４のアルコキシ基、水酸基並びに下記式（２）及び（３）で表されるフラニル基からなる群から選択される基であり、１分子中のＲ1のうち２個以上は下記式（２）又は（３）で表されるフラニル基である。ａは２以上の数、ｂは０以上の数、ｃは０以上の数、ｄは０以上の数で、かつ、２≦ａ＋ｂ＋ｃ＋ｄ≦５００である。）
（式（２）及び（３）中、Ｒ2及びＲ3は、それぞれ独立して、水素原子又は炭素数１～１０の直鎖アルキル基である。破線は結合手を示す。）
（Ｂ）下記式（４）で表される数平均分子量が５００～４０，０００のマレイミド基含有オルガノポリシロキサン、
（式（４）中、Ｒ4は、独立して、炭素数１～１０の１価炭化水素基又は下記式（５）で表されるマレイミド基であり、１分子中のＲ4のうち２個以上は下記式（５）で表されるマレイミド基である。ｅは２以上の数、ｆは０以上の数、ｇは０以上の数、ｈは０以上の数で、かつ、２≦ｅ＋ｆ＋ｇ＋ｈ≦５００である。）
（式（５）中、Ｒ5は、独立して、水素原子又はメチル基である。破線は結合手を示す。）
を含む硬化性シリコーン樹脂組成物。
［２］
式（１）のｄ、及び式（４）のｈの両方あるいはいずれか一方が０である、［１］に記載の硬化性シリコーン樹脂組成物。
［３］
式（１）のｃ、及び式（４）のｇの両方あるいはいずれか一方が０である、［１］又は［２］に記載の硬化性シリコーン樹脂組成物。
［４］
式（１）のｃ、ｄ及び式（４）のｇ、ｈがすべて０である、［１］～［３］のいずれか１項に記載の硬化性シリコーン樹脂組成物。
［５］
［１］～［４］のいずれか１項に記載の硬化性シリコーン樹脂組成物の硬化物を１３０℃以上に加熱する工程を有する、硬化性シリコーン樹脂組成物のリサイクル方法。
下記（Ａ）及び（Ｂ）成分；
（Ａ）下記式（１）で表される数平均分子量が５００～４０，０００のフラニル基含有オルガノポリシロキサン、
（Ｂ）下記式（４）で表される数平均分子量が５００～４０，０００のマレイミド基含有オルガノポリシロキサン、
を含む硬化性シリコーン樹脂組成物。
［２］
式（１）のｄ、及び式（４）のｈの両方あるいはいずれか一方が０である、［１］に記載の硬化性シリコーン樹脂組成物。
［３］
式（１）のｃ、及び式（４）のｇの両方あるいはいずれか一方が０である、［１］又は［２］に記載の硬化性シリコーン樹脂組成物。
［４］
式（１）のｃ、ｄ及び式（４）のｇ、ｈがすべて０である、［１］～［３］のいずれか１項に記載の硬化性シリコーン樹脂組成物。
［５］
［１］～［４］のいずれか１項に記載の硬化性シリコーン樹脂組成物の硬化物を１３０℃以上に加熱する工程を有する、硬化性シリコーン樹脂組成物のリサイクル方法。
本発明によれば、１３０℃以上の温度で加熱すると、液状化する、リサイクル可能な硬化性シリコーン樹脂組成物を提供することができる。また、このシリコーン樹脂組成物は、０℃以上１００℃以下という比較的低温で硬化可能である。また、本発明の硬化性シリコーン樹脂組成物は、接着剤、粘着剤、封止剤、コーティング剤などの用途に有用である。
以下、本発明について詳細に説明する。
［（Ａ）フラニル基含有オルガノポリシロキサン］
本発明の（Ａ）成分である、数平均分子量で５００～４０，０００の、フラニル基含有オルガノポリシロキサンは、下記式（１）で示されるものである。
本発明の（Ａ）成分である、数平均分子量で５００～４０，０００の、フラニル基含有オルガノポリシロキサンは、下記式（１）で示されるものである。
上記式（１）中、Ｒ1は、独立して、水素原子、炭素数１～１０の１価炭化水素基、炭素数１～４のアルコキシ基、水酸基並びに下記式（２）及び（３）で表されるフラニル基からなる群から選択される基であり、１分子中のＲ1のうち２個以上は下記式（２）又は（３）で表されるフラニル基である。ａは２以上の数、ｂは０以上の数、ｃは０以上の数、ｄは０以上の数で、かつ、２≦ａ＋ｂ＋ｃ＋ｄ≦５００である。
上記式（２）及び（３）中、Ｒ2及びＲ3は、それぞれ独立して水素原子又は炭素数１～１０の直鎖アルキル基である。破線は結合手を示す。
上記式（１）中、Ｒ1は、独立して、水素原子、炭素数１～１０の１価炭化水素基、炭素数１～４のアルコキシ基、水酸基並びに上記式（２）及び（３）で表されるフラニル基からなる群から選択される基である。式（１）中、Ｒ1で表される炭素数１～１０の１価炭化水素基としては、メチル基、エチル基、プロピル基及びブチル基等のアルキル基；シクロペンチル基及びシクロヘキシル基等のシクロアルキル基；フェニル基及びトリル基等のアリール基等が挙げられ、炭素数１～４のアルコキシ基としては、メトキシ基、エトキシ基、プロポキシ基及びブトキシ基等が挙げられる。
１分子中のＲ1のうち２個以上、好ましくは２～４個は、上記式（２）又は（３）で表されるフラニル基である。このフラニル基以外の基としては、アルキル基、シクロアルキル基及びアリール基が好ましく、メチル基、フェニル基がより好ましい。
１分子中のＲ1のうち２個以上、好ましくは２～４個は、上記式（２）又は（３）で表されるフラニル基である。このフラニル基以外の基としては、アルキル基、シクロアルキル基及びアリール基が好ましく、メチル基、フェニル基がより好ましい。
上記式（２）及び式（３）中、Ｒ2及びＲ3は、それぞれ独立して、水素原子又は炭素数１～１０の直鎖アルキル基である。式（２）及び式（３）中、Ｒ2又はＲ3で表される炭素数１～１０の直鎖アルキル基としては、メチル基、エチル基、プロピル基及びブチル基等が挙げられる。中でもＲ2及びＲ3としては、水素原子あるいはメチル基が好ましい。
上記式（１）中、ａは２以上、好ましくは２～１２の数、ｂは０以上、好ましくは１～４９８、より好ましくは５～３００の数、ｃは０以上、好ましくは０～１０の数、より好ましくは０である。ｄは０以上、好ましくは０～５の数、より好ましくは０である。かつ、２≦ａ＋ｂ＋ｃ＋ｄ≦５００であり、２≦ａ＋ｂ＋ｃ＋ｄ≦３００が好ましく、３≦ａ＋ｂ＋ｃ＋ｄ≦３００がより好ましく、４≦ａ＋ｂ＋ｃ＋ｄ≦１５０が更に好ましい。ａ＋ｂ＋ｃ＋ｄが５００より大きいと、フラニル基含有オルガノポリシロキサンの粘度が高くなり、作業性が悪くなる場合がある。
本発明のフラニル基含有オルガノポリシロキサンの分子量は、数平均分子量で５００～４０，０００であり、１，０００～２０，０００であることが好ましく、１，０００～１０，０００であることがより好ましい。該分子量が５００未満であると、（ポリ）シロキサンに由来する柔軟性などの特性が発現しない場合があり、４０，０００を超えると、フラニル基含有オルガノポリシロキサンの粘度が高くなり、作業性が悪くなる場合があるため、好ましくない。
なお、本発明において数平均分子量は、下記条件によるポリスチレンを標準物質としたＧＰＣ（ゲルパーミエーションクロマトグラフィー）分析による値である（以下同様）。
［測定条件］
展開溶媒：テトラヒドロフラン（ＴＨＦ）
流量：０．６ｍＬ／ｍｉｎ
検出器：示差屈折率検出器（ＲＩ）
カラム：ＴＳＫ Ｇｕａｒｄｃｏｌｕｍｎ ＳｕｐｅｒＨ－Ｈ
ＴＳＫｇｅｌ ＳｕｐｅｒＨＭ－Ｎ（６．０ｍｍＩ．Ｄ．×１５ｃｍ×１）
ＴＳＫｇｅｌ ＳｕｐｅｒＨ２５００（６．０ｍｍＩ．Ｄ．×１５ｃｍ×１）
（いずれも東ソー社製）
カラム温度：４０℃
試料注入量：５０μＬ（濃度０．３質量％のＴＨＦ溶液）
展開溶媒：テトラヒドロフラン（ＴＨＦ）
流量：０．６ｍＬ／ｍｉｎ
検出器：示差屈折率検出器（ＲＩ）
カラム：ＴＳＫ Ｇｕａｒｄｃｏｌｕｍｎ ＳｕｐｅｒＨ－Ｈ
ＴＳＫｇｅｌ ＳｕｐｅｒＨＭ－Ｎ（６．０ｍｍＩ．Ｄ．×１５ｃｍ×１）
ＴＳＫｇｅｌ ＳｕｐｅｒＨ２５００（６．０ｍｍＩ．Ｄ．×１５ｃｍ×１）
（いずれも東ソー社製）
カラム温度：４０℃
試料注入量：５０μＬ（濃度０．３質量％のＴＨＦ溶液）
［（Ｂ）マレイミド基含有オルガノポリシロキサン］
本発明の（Ｂ）成分である、数平均分子量が５００～４０，０００の、マレイミド基含有オルガノポリシロキサンは、下記式（４）で示される。
本発明の（Ｂ）成分である、数平均分子量が５００～４０，０００の、マレイミド基含有オルガノポリシロキサンは、下記式（４）で示される。
上記式（４）中、Ｒ4は、独立して、炭素数１～１０の１価炭化水素基又は下記式（５）で表されるマレイミド基であり、１分子中のＲ4のうち２個以上、好ましくは２～８個は、下記式（５）で表されるマレイミド基である。ｅは２以上の数、ｆは０以上の数、ｇは０以上の数、ｈは０以上の数で、かつ、２≦ｅ＋ｆ＋ｇ＋ｈ≦５００である。
上記式（５）中、Ｒ5は、独立して、水素原子又はメチル基である。破線は結合手を示す。
上記式（４）中、Ｒ4は、独立して、炭素数１～１０の１価炭化水素基又は上記式（５）で表されるマレイミド基であり、１分子中のＲ4のうち２個以上は上記式（５）で表されるマレイミド基である。式（４）中、Ｒ4で表される炭素数１～１０の１価炭化水素基としては、メチル基、エチル基、プロピル基及びブチル基等のアルキル基；シクロペンチル基及びシクロヘキシル基等のシクロアルキル基；フェニル基及びトリル基等のアリール基等が挙げられる。中でも、アルキル基、シクロアルキル基及びアリール基が好ましく、メチル基、フェニル基がより好ましい。
上記式（５）中、Ｒ5は、水素原子又はメチル基である。中でも、水素原子が好ましい。
上記式（４）中、ｅは２以上、好ましくは２～１２の数、ｆは０以上、好ましくは１～４９８、より好ましくは５～３００の数、ｇは０以上、好ましくは０～１０の数、より好ましくは０である。ｈは０以上、好ましくは０～５の数、より好ましくは０である。かつ、２≦ｅ＋ｆ＋ｇ＋ｈ≦５００であり、２≦ｅ＋ｆ＋ｇ＋ｈ≦３００が好ましく、３≦ｅ＋ｆ＋ｇ＋ｈ≦３００がより好ましく、４≦ｅ＋ｆ＋ｇ＋ｈ≦１５０が更に好ましい。ｅ＋ｆ＋ｇ＋ｈが５００より大きいと、マレイミド基含有オルガノポリシロキサンの粘度が高くなり、作業性が悪くなる場合がある。
本発明のマレイミド基含有オルガノポリシロキサンの分子量は、数平均分子量で５００～４０，０００であり、１，０００～２０，０００であることが好ましく、１，０００～１０，０００であることがより好ましい。該分子量が５００未満であると、（ポリ）シロキサンに由来する柔軟性などの特性が発現しない場合があり、４０，０００を超えると、マレイミド基含有オルガノポリシロキサンの粘度が高くなり、作業性が悪くなる場合がある。
（Ｂ）成分の配合量は、（Ａ）成分中のフラニル基１当量に対して、（Ｂ）成分中のマレイミド基が１～２当量であることが好ましく、１．１～１．５当量であることがより好ましい。
なお、本発明の組成物において、（Ａ）成分及び（Ｂ）成分は６０～１００質量％含むことが好ましく、８０～１００質量％含むことがより好ましく、９０～１００質量％含むことが更に好ましい。
なお、本発明の組成物において、（Ａ）成分及び（Ｂ）成分は６０～１００質量％含むことが好ましく、８０～１００質量％含むことがより好ましく、９０～１００質量％含むことが更に好ましい。
［その他の成分］
本発明の硬化性シリコーン樹脂組成物は、本発明の効果を損なわない範囲で、上記成分以外の成分を添加してもよい。上記成分以外の成分としては、例えば、シリカ粉末や金属フィラー等の結着剤が挙げられる。
本発明の硬化性シリコーン樹脂組成物は、本発明の効果を損なわない範囲で、上記成分以外の成分を添加してもよい。上記成分以外の成分としては、例えば、シリカ粉末や金属フィラー等の結着剤が挙げられる。
［硬化性シリコーン樹脂組成物の製造方法］
本発明のリサイクル可能な硬化性シリコーン樹脂組成物の製造方法としては、液状物質の混合方法として公知の手段を利用することができる。特に、（Ａ）フラニル基含有オルガノポリシロキサンと、（Ｂ）マレイミド基含有オルガノポリシロキサンとは互いに相溶性に優れるため、室温（２５℃）下で単純混合するだけでも均一な組成物が得られる。
（Ａ）フラニル基含有オルガノポリシロキサン及び（Ｂ）マレイミド基含有オルガノポリシロキサン以外の成分を本発明の組成物に添加する場合は、該成分を公知の手法で（Ａ）及び／又は（Ｂ）成分中に予め分散させたものを室温（２５℃）下で単純混合することが好ましい。
本発明のリサイクル可能な硬化性シリコーン樹脂組成物の製造方法としては、液状物質の混合方法として公知の手段を利用することができる。特に、（Ａ）フラニル基含有オルガノポリシロキサンと、（Ｂ）マレイミド基含有オルガノポリシロキサンとは互いに相溶性に優れるため、室温（２５℃）下で単純混合するだけでも均一な組成物が得られる。
（Ａ）フラニル基含有オルガノポリシロキサン及び（Ｂ）マレイミド基含有オルガノポリシロキサン以外の成分を本発明の組成物に添加する場合は、該成分を公知の手法で（Ａ）及び／又は（Ｂ）成分中に予め分散させたものを室温（２５℃）下で単純混合することが好ましい。
［硬化性シリコーン樹脂組成物の硬化方法］
本発明の硬化性シリコーン樹脂組成物の硬化方法としては、０℃以上１００℃以下、好ましくは１５℃以上８０℃以下の温度で、１２～９６時間、好ましくは２４～７２時間の硬化条件で硬化することが好ましい。
本発明の硬化性シリコーン樹脂組成物の硬化方法としては、０℃以上１００℃以下、好ましくは１５℃以上８０℃以下の温度で、１２～９６時間、好ましくは２４～７２時間の硬化条件で硬化することが好ましい。
［硬化性シリコーン樹脂のリサイクル方法］
本発明の硬化性シリコーン樹脂組成物の硬化物であるシリコーン樹脂のリサイクル方法は、１３０℃以上、好ましくは１３０℃以上１６０℃以下の温度で、３～３０分、好ましくは３～１０分加熱する工程を有する。該加熱工程により、本発明の硬化性シリコーン樹脂組成物の硬化物は液状化し、液状化した硬化性シリコーン樹脂組成物は、上記硬化条件で再び硬化し、リサイクルが可能となる。
本発明の硬化性シリコーン樹脂組成物の硬化物であるシリコーン樹脂のリサイクル方法は、１３０℃以上、好ましくは１３０℃以上１６０℃以下の温度で、３～３０分、好ましくは３～１０分加熱する工程を有する。該加熱工程により、本発明の硬化性シリコーン樹脂組成物の硬化物は液状化し、液状化した硬化性シリコーン樹脂組成物は、上記硬化条件で再び硬化し、リサイクルが可能となる。
以下に実施例を挙げて本発明をさらに具体的に説明するが、本発明の範囲は以下に示す具体例により限定的に解釈されない。
＜実施例１＞
下記式（６）で表されるフラニル基含有オルガノポリシロキサン（数平均分子量７，５７０）３．７９ｇと、下記式（７）で表されるマレイミド基含有オルガノポリシロキサン（数平均分子量６，８８０）２．５８ｇとを室温（２５℃）で５分間撹拌し、得られたシリコーン樹脂組成物を室温で３日間静置し、硬化した。硬化したシリコーン樹脂組成物を１５０℃のオーブンで５分間加熱したところ、すべて液状化した。液状化した組成物を再度室温で３日間静置したところ、再び硬化した。
下記式（６）で表されるフラニル基含有オルガノポリシロキサン（数平均分子量７，５７０）３．７９ｇと、下記式（７）で表されるマレイミド基含有オルガノポリシロキサン（数平均分子量６，８８０）２．５８ｇとを室温（２５℃）で５分間撹拌し、得られたシリコーン樹脂組成物を室温で３日間静置し、硬化した。硬化したシリコーン樹脂組成物を１５０℃のオーブンで５分間加熱したところ、すべて液状化した。液状化した組成物を再度室温で３日間静置したところ、再び硬化した。
＜実施例２＞
下記式（８）で表されるフラニル基含有オルガノポリシロキサン（数平均分子量７，６８０）３．８４ｇと、上記式（７）で表されるマレイミド基含有オルガノポリシロキサン（数平均分子量６，８８０）２．５８ｇとを室温（２５℃）で５分間撹拌し、得られたシリコーン組成物を室温で３日間静置し、硬化させた。硬化したシリコーン樹脂組成物を１５０℃のオーブンで５分間加熱したところ、すべて液状化した。液状化した組成物を再度室温で３日間静置したところ、再び硬化した。
下記式（８）で表されるフラニル基含有オルガノポリシロキサン（数平均分子量７，６８０）３．８４ｇと、上記式（７）で表されるマレイミド基含有オルガノポリシロキサン（数平均分子量６，８８０）２．５８ｇとを室温（２５℃）で５分間撹拌し、得られたシリコーン組成物を室温で３日間静置し、硬化させた。硬化したシリコーン樹脂組成物を１５０℃のオーブンで５分間加熱したところ、すべて液状化した。液状化した組成物を再度室温で３日間静置したところ、再び硬化した。
＜実施例３＞
下記式（９）で表されるフラニル基含有オルガノポリシロキサン（数平均分子量６，３１０）２．１０ｇと、上記式（７）で表されるマレイミド基含有オルガノポリシロキサン（数平均分子量６，８８０）２．５８ｇとを室温（２５℃）で５分間撹拌し、得られたシリコーン組成物を室温で３日間静置し、硬化させた。硬化したシリコーン樹脂組成物を１５０℃のオーブンで５分間加熱したところ、すべて液状化した。液状化した組成物を再度室温で３日間静置したところ、再び硬化した。
下記式（９）で表されるフラニル基含有オルガノポリシロキサン（数平均分子量６，３１０）２．１０ｇと、上記式（７）で表されるマレイミド基含有オルガノポリシロキサン（数平均分子量６，８８０）２．５８ｇとを室温（２５℃）で５分間撹拌し、得られたシリコーン組成物を室温で３日間静置し、硬化させた。硬化したシリコーン樹脂組成物を１５０℃のオーブンで５分間加熱したところ、すべて液状化した。液状化した組成物を再度室温で３日間静置したところ、再び硬化した。
＜実施例４＞
下記式（１０）で表されるフラニル基含有オルガノポリシロキサン（数平均分子量６，４００）２．１３ｇと、上記式（７）で表されるマレイミド基含有オルガノポリシロキサン（数平均分子量６，８８０）２．５８ｇとを室温（２５℃）で５分間撹拌し、得られたシリコーン組成物を室温で３日間静置し、硬化させた。硬化したシリコーン樹脂組成物を１５０℃のオーブンで５分間加熱したところ、すべて液状化した。液状化した組成物を再度室温で３日間静置したところ、再び硬化した。
下記式（１０）で表されるフラニル基含有オルガノポリシロキサン（数平均分子量６，４００）２．１３ｇと、上記式（７）で表されるマレイミド基含有オルガノポリシロキサン（数平均分子量６，８８０）２．５８ｇとを室温（２５℃）で５分間撹拌し、得られたシリコーン組成物を室温で３日間静置し、硬化させた。硬化したシリコーン樹脂組成物を１５０℃のオーブンで５分間加熱したところ、すべて液状化した。液状化した組成物を再度室温で３日間静置したところ、再び硬化した。
＜比較例１＞
下記式（１１）で表されるフラニル基含有オルガノポリシロキサン（数平均分子量２９０）０．３ｇと、上記式（７）で表されるマレイミド基含有オルガノポリシロキサン（数平均分子量６，８８０）２．５８ｇとを室温（２５℃）で５分間撹拌し、得られたシリコーン組成物を室温で３日間静置したが、増粘するのみで硬化しなかった。
下記式（１１）で表されるフラニル基含有オルガノポリシロキサン（数平均分子量２９０）０．３ｇと、上記式（７）で表されるマレイミド基含有オルガノポリシロキサン（数平均分子量６，８８０）２．５８ｇとを室温（２５℃）で５分間撹拌し、得られたシリコーン組成物を室温で３日間静置したが、増粘するのみで硬化しなかった。
Claims (5)
- 下記（Ａ）及び（Ｂ）成分；
（Ａ）下記式（１）で表される数平均分子量が５００～４０，０００のフラニル基含有オルガノポリシロキサン、
（Ｂ）下記式（４）で表される数平均分子量が５００～４０，０００のマレイミド基含有オルガノポリシロキサン、
を含む硬化性シリコーン樹脂組成物。 - 式（１）のｄ、及び式（４）のｈの両方あるいはいずれか一方が０である、請求項１に記載の硬化性シリコーン樹脂組成物。
- 式（１）のｃ、及び式（４）のｇの両方あるいはいずれか一方が０である、請求項１に記載の硬化性シリコーン樹脂組成物。
- 式（１）のｃ、ｄ及び式（４）のｇ、ｈがすべて０である、請求項１に記載の硬化性シリコーン樹脂組成物。
- 請求項１～４のいずれか１項に記載の硬化性シリコーン樹脂組成物の硬化物を１３０℃以上に加熱する工程を有する、硬化性シリコーン樹脂組成物のリサイクル方法。