WO2024043273A1 - リチウム一次電池 - Google Patents

リチウム一次電池 Download PDF

Info

Publication number
WO2024043273A1
WO2024043273A1 PCT/JP2023/030295 JP2023030295W WO2024043273A1 WO 2024043273 A1 WO2024043273 A1 WO 2024043273A1 JP 2023030295 W JP2023030295 W JP 2023030295W WO 2024043273 A1 WO2024043273 A1 WO 2024043273A1
Authority
WO
WIPO (PCT)
Prior art keywords
primary battery
lithium
compound
mass
positive electrode
Prior art date
Application number
PCT/JP2023/030295
Other languages
English (en)
French (fr)
Inventor
仁志 西谷
Original Assignee
パナソニックＩｐマネジメント株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by パナソニックＩｐマネジメント株式会社 filed Critical パナソニックＩｐマネジメント株式会社
Publication of WO2024043273A1 publication Critical patent/WO2024043273A1/ja

Abstract

リチウム一次電池は、正極と、負極と、非水電解液と、を備える。正極は二酸化マンガンを含み、負極はリチウム合金を含む。リチウム合金はマグネシウムを含み、リチウム合金中のマグネシウムの含有量は１０質量％以下である。

Description

リチウム一次電池
　本開示は、リチウム一次電池に関する。
　リチウム一次電池は、高エネルギー密度であり、自己放電が少ないことから、多くの電子機器の電源として使用されている。リチウム一次電池の正極には、二酸化マンガンなどが用いられる。リチウム一次電池の負極には、例えば、シート状（箔状）の金属リチウムもしくはリチウム合金が用いられる。
　特許文献１では、電池缶内に、正極と負極と溶質及び有機溶媒から成る電解液とを備え、上記溶質としてトリフルオロメタンスルホン酸リチウムが用いられた非水系電解液電池において、前記負極はリチウム合金から成ることを特徴とする非水系電解液電池が提案されている。特許文献１の実施例では、リチウム合金に、Ｌｉ－Ａｌ、Ｌｉ－Ｉｎ、またはＬｉ－Ｓｎが用いられている。
特開平２－１５５６６号公報
　リチウム一次電池において、負極の劣化により電池容量が低下することがある。
　本開示の一側面は、正極と、負極と、非水電解液と、を備え、前記正極は、二酸化マンガンを含み、前記負極は、リチウム合金を含み、前記リチウム合金は、マグネシウムを含み、前記リチウム合金中の前記マグネシウムの含有量は、１０質量％以下である、リチウム一次電池に関する。
　本開示によれば、リチウム一次電池の容量低下を抑制することができる。
　本発明の新規な特徴を添付の請求の範囲に記述するが、本発明は、構成および内容の両方に関し、本発明の他の目的および特徴と併せ、図面を照合した以下の詳細な説明によりさらによく理解されるであろう。
本開示の実施形態に係るリチウム一次電池の一部を断面にした正面図である。
　以下では、本開示の実施形態について例を挙げて説明するが、本開示は以下で説明する例に限定されない。以下の説明では、具体的な数値や材料を例示する場合があるが、本開示の効果が得られる限り、他の数値や材料を適用してもよい。この明細書において、「数値Ａ～数値Ｂ」という記載は、数値Ａおよび数値Ｂを含み、「数値Ａ以上で数値Ｂ以下」と読み替えることが可能である。以下の説明において、特定の物性や条件などの数値に関して下限と上限とを例示した場合、下限が上限以上とならない限り、例示した下限のいずれかと例示した上限のいずれかとを任意に組み合わせることができる。複数の材料が例示される場合、その中から１種を選択して単独で用いてもよく、２種以上を組み合わせて用いてもよい。
　また、本開示は、添付の特許請求の範囲に記載の複数の請求項から任意に選択される２つ以上の請求項に記載の事項の組み合わせを包含する。つまり、技術的な矛盾が生じない限り、添付の特許請求の範囲に記載の複数の請求項から任意に選択される２つ以上の請求項に記載の事項を組み合わせることができる。
　本開示の実施形態に係るリチウム一次電池は、正極と、負極と、非水電解液と、を備える。正極は二酸化マンガンを含み、負極はリチウム合金を含む。リチウム合金はマグネシウム（Ｍｇ）を含み、リチウム合金中のＭｇの含有量は１０質量％以下である。
　リチウム合金がＭｇを含むことにより、負極の強度が大きくなり、放電時の正極の膨張に起因する負極の部分的欠損もしくは破断が抑制され、強度低下に起因する容量低下が抑制される。また、リチウム合金がＭｇを含むことにより、負極と電解液との副反応が抑制され、当該副反応に起因する容量低下が抑制される。当該副反応は高温環境下で生じ易い。リチウム合金中のＭｇ含有量が１０質量％以下である場合、負極に占めるＬｉ量（Ｌｉ絶対量）の減少による容量低下を抑制することができる。その結果、初期および長期保存後のいずれの場合においても高容量が得られ、保存後の容量劣化率を大幅に低減できる。リチウム合金中のＭｇ含有量を１０質量％よりも大きくすると、Ｍｇ含有による強度向上および副反応抑制の効果は大きくなるが、負極に占めるＬｉ量（Ｌｉ絶対量）が減少し、容量が低下する。
　負極に用いられるリチウム合金は、例えば、箔状（シート状）である。高容量化の観点から、リチウム合金中のＬｉの含有量は、例えば、９０質量％以上であってもよく、９５質量％以上であってもよい。
　リチウム合金中のＭｇ含有量は、１０質量％以下であり、０．０１質量％以上、１０質量％以下であってもよく、０．５質量％以上、５質量％以下であってもよい。
　リチウム合金中において、Ｍｇは、分散していてもよく、偏在していてもよい。リチウム合金箔中において、Ｍｇは、当該箔の厚み方向および／または面方向に偏在していてもよい。Ｍｇの分散および偏在のいずれの場合でも、Ｍｇを含む負極では、強度が大きくなり、Ｍｇを含まない負極と比べて容量低下が抑制され、高温保存時の負極の劣化が抑制される。
　リチウム合金は、Ｌｉ、Ｍｇ以外の他の金属元素を含んでもよい。他の金属元素としては、Ａｌ、Ｓｎ、Ｎｉ、Ｐｂ、Ｉｎ、Ｋ、Ｆｅ、Ｓｉなどが挙げられる。リチウム合金に含まれるリチウム以外の金属元素の全体の含有量は、放電容量の確保や内部抵抗の安定化の観点から、０．０５質量％以上、１５質量％以下（もしくは１０質量％以下）であってもよい。
　リチウム合金の各元素の含有量は、誘導結合プラズマ（ＩＣＰ）発光分光分析法または原子吸光分析法（ＡＡＳ）により求められる。
（非水電解液の添加剤）
　非水電解液は、環状イミド化合物、フタル酸エステル化合物、およびイソシアネート化合物からなる群より選択される少なくとも１種の添加剤を含むことが好ましい。非水電解液が上記の添加剤を含む場合、Ｍｇを含むリチウム合金（負極）の表面に、リチウム合金由来のＭｇと、添加剤由来の成分とを含む複合被膜を形成し得る。当該被膜は化学的安定性に優れているとともに、当該被膜がリチウム合金由来のＭｇを含むことから負極の非水電解液に対する濡れ性が向上し、負極の抵抗が低減される。当該被膜により、負極表面でのＬｉの消費がより均一に行われ易い。
　非水電解液中の添加剤の含有量は、例えば、０．０１質量％以上、５質量％以下である。なお、非水電解液中の添加剤の含有量は、非水電解液全体に対する添加剤の質量比（百分率）である。例えば、電池の製造直後（もしくは非水電解液の調製時）において、非水電解液中の添加剤の含有量が上記範囲内であることが望ましい。これに対して、製造直後から一定期間経過した電池では、添加剤の一部は被膜の形成に消費されており、非水電解液中の添加剤の含有量は、上記範囲よりも小さい値であってもよい。この場合、非水電解液中の添加剤の含有量が少量（例えば検出限界に近い値）であっても、添加剤による上記効果は認められる。後述する環状イミド化合物などの各種化合物の含有量についても、同様のことが言える。
（環状イミド化合物）
　環状イミド化合物としては、例えば、環状のジアシルアミン化合物が挙げられる。環状イミド化合物は、ジアシルアミン環（以下、イミド環とも称する。）を有していればよい。イミド環には、他の環（以下、第２の環とも称する。）が縮合していてもよい。環状イミド化合物は、非水電解液に、イミドの状態で含まれていてもよく、アニオンまたは塩の形態で含まれていてもよい。非水電解液に環状イミド化合物がイミドの状態で含まれる場合、フリーのＮＨ基を有する形態で含まれていてもよく、三級アミンの形態で含まれていてもよい。
　第２の環としては、芳香環、飽和または不飽和脂肪族環などが挙げられる。第２の環には、少なくとも１つのヘテロ原子が含まれていてもよい。ヘテロ原子としては、酸素原子、イオウ原子、および窒素原子などが挙げられる。
　環状イミド化合物としては、例えば、脂肪族ジカルボン酸イミド化合物、第２の環を有する環状イミド化合物などが挙げられる。脂肪族ジカルボン酸イミド化合物としては、例えば、コハク酸イミドなどが挙げられる。第２の環を有する環状イミド化合物としては、芳香族または脂環族ジカルボン酸のイミド化合物などが挙げられる。芳香族ジカルボン酸または脂環族ジカルボン酸は、例えば、環を構成する隣接する２つの原子にそれぞれカルボキシ基を有するものが挙げられる。第２の環を有する環状イミド化合物としては、例えば、フタルイミド、フタルイミドの水素添加体が挙げられる。フタルイミドの水素添加体としては、シクロヘキサ－３－エン－１，２－ジカルボキシミド、シクロヘキサン－１，２－ジカルボキシミドなどが挙げられる。
　イミド環は、イミドの窒素原子に置換基を有するＮ－置換イミド環であってもよい。このような置換基としては、ヒドロキシ基、アルキル基、アルコキシ基、ハロゲン原子などが挙げられる。アルキル基としては、例えば、Ｃ１～Ｃ４のアルキル基が挙げられ、メチル基、エチル基などであってもよい。アルコキシ基としては、例えば、Ｃ１～Ｃ４のアルコキシ基が挙げられ、メトキシ基、エトキシ基などであってもよい。ハロゲン原子としては、塩素原子、フッ素原子などが挙げられる。
　環状イミド化合物は、フタルイミドおよびＮ－置換フタルイミドからなる群より選択される少なくとも１種が好ましい。Ｎ－置換フタルイミドの窒素原子上の置換基としては、Ｎ－置換イミド環について例示した置換基から選択できる。Ｎ－置換フタルイミドは、例えば、Ｎ－ヒドロキシフタルイミド、Ｎ－（２－ヒドロキシエチル）フタルイミド、Ｎ－（シクロヘキシルチオ）フタルイミド、およびＮ－（フェニルチオ）フタルイミドからなる群より選択される少なくとも１種を含むことが好ましい。フタルイミドおよび／またはＮ－置換フタルイミドが、環状イミド化合物の５０質量％以上、更には７０質量％以上もしくは９０質量％以上を占めてもよい。
　非水電解液は、環状イミド化合物を１種含んでいてもよく、２種以上含んでいてもよい。非水電解液中の環状イミド化合物の含有量は、１質量％以下であってもよく、０．００１質量％以上、１質量％以下であってもよく、０．００１質量％以上、０．８質量％以下であってもよい。
（フタル酸エステル化合物）
　フタル酸エステル化合物は、フタル酸エステルおよびその誘導体を含む。誘導体は、フタル酸に由来する芳香環に結合する置換基を有してもよい。このような置換基としては、ヒドロキシ基、アルキル基、アルコキシ基、ハロゲン原子などが挙げられる。アルキル基としては、例えば、Ｃ１～Ｃ４のアルキル基が挙げられ、メチル基、エチル基などであってもよい。アルコキシ基としては、例えば、Ｃ１～Ｃ４のアルコキシ基が挙げられ、メトキシ基、エトキシ基などであってもよい。ハロゲン原子としては、塩素原子、フッ素原子などが挙げられる。
　フタル酸エステル化合物は、フタル酸モノエステル化合物でもよいが、生成する被膜がＬｉ合金表面を保護し易いという観点から、フタル酸ジエステル化合物が望ましい。フタル酸（もしくはその誘導体）とエステルを構成するアルコールとしては、Ｃ１～Ｃ２０（好ましくはＣ１～Ｃ６）の飽和または不飽和の脂肪族アルコールが望ましい。
　フタル酸ジエステル化合物の具体例としては、フタル酸ジメチル、フタル酸ジエチル、フタル酸ジアリル、フタル酸ジブチル、フタル酸ジイソブチル、フタル酸ビス（２－エチルヘキシル）などが挙げられる。これらは単独で用いてもよく、２種以上を組み合わせて用いてもよい。フタル酸ジエステル化合物は、フタル酸エステル化合物の５０質量％以上、更には７０質量％以上もしくは９０質量％以上を占めてもよい。
　非水電解液は、フタル酸エステル化合物を１種含んでいてもよく、２種以上含んでいてもよい。非水電解液中のフタル酸エステル化合物の含有量は、１質量以下であってもよく、０．１質量％以上、１質量％以下であってもよい。
（イソシアネート化合物）
　イソシアネート化合物は、例えば、少なくとも１つのイソシアネート基と、Ｃ１～Ｃ２０の脂肪族炭化水素基またはＣ６～Ｃ２０の芳香族炭化水素基を有する。イソシアネート化合物を構成する脂肪族炭化水素基および芳香族炭化水素基は置換基を有してもよい。置換基は、安定に存在し得る基であればよく、例えば、ハロゲン原子でもよく、ニトリル基でもよい。脂肪族基は、脂環式脂肪族基でもよく、直鎖状または分岐鎖状の脂肪族基でもよい。芳香族炭化水素基は、芳香環を１つ以上有する炭化水素基であり、芳香環と脂肪族基とが連結した基でもよい。
　イソシアネート化合物は、イソシアネート基を１つ有するモノイソシアネート化合物でもよいが、イソシアネート基を２つ有するジイソシアネート化合物が望ましい。ジイソシアネート化合物は、モノイソシアネート化合物よりも化学的安定性の高い複合被膜を生成し、トリイソシアネートよりも低抵抗な複合被膜を生成すると考えられる。また、ジイソシアネート化合物は、少量でも複合被膜を形成する能力が高く、電池内での安定性に優れる。
　ジイソシアネート化合物の具体例としては、ＯＣＮ－ＣｎＨ２ｎ－ＮＣＯ（ｎは１～１０の整数である。）で表される化合物（例えば、ヘキサメチレンジイソシアネート）、脂環式ジイル基を有する化合物（例えば、１，３－ビス（イソシアナトメチル）シクロヘキサン、ジシクロヘキシルメタン－４,４’－ジイソシアネート、ビシクロ［２．２．１］ヘプタン－２，５－ジイルビス（メチルイソシアネート）、ビシクロ［２．２．１］ヘプタン－２，６－ジイルビス（メチルイソシアネート）、イソホロンジイソシアネート）、２，２，４－トリメチルヘキサメチレンジイソシアネート、２，４，４－トリメチルヘキサメチレンジイソシアネート、ヘキシルイソシアネートなどが挙げられる。これらの中でも、ヘキサメチレンジイソシアネート、１，３－ビス（イソシアナトメチル）シクロヘキサン、およびイソホロンジイソシアネートからなる群より選択される少なくとも１種が好ましい。これらがイソシアネート化合物の５０質量％以上、更には７０質量％以上もしくは９０質量％以上を占めてもよい。
　非水電解液にジイソシアネート化合物を添加する場合、電池内（非水電解液中）においてジイソシアネート化合物同士が反応して、イソシアヌレート体、ウレア体、ビュレット体を形成し得る。よって、電池を分解して非水電解液の分析を行う場合、ジイソシアネート化合物由来のイソシアヌレート体、ウレア体、ビュレット体が検出される場合がある。
　非水電解液は、イソシアネート化合物を１種含んでいてもよく、２種以上含んでいてもよい。非水電解液中のイソシアネート化合物の含有量は、３質量％以下であってもよく、０．０１質量％以上、２質量％以下であってもよく、０．０１質量％以上、１．５質量％以下であってもよい。
　非水電解液（添加剤）の分析には、例えば、液体クロマトグラフィー質量分析法（ＬＣ／ＭＳ）やガスクロマトグラフィー質量分析法（ＧＣ／ＭＳ）を用いることができる。核磁気共鳴分析（ＮＭＲ）、赤外吸収分光分析(ＩＲ)、質量分析（ＭＳ）とともに紫外分光分析（ＵＶ）を行ってもよい。
　以下、本開示のリチウム一次電池について、より具体的に説明する。
［リチウム一次電池］
（正極）
　正極は、正極活物質として二酸化マンガンを含む。二酸化マンガンとしては、電解二酸化マンガンが好適に用いられる。二酸化マンガンを含む正極は、比較的高電圧を発現し、パルス放電特性に優れている。二酸化マンガンは、複数種の結晶状態を含む混晶状態であってもよい。正極には、二酸化マンガン以外のマンガン酸化物が含まれていてもよい。二酸化マンガン以外のマンガン酸化物としては、ＭｎＯ、Ｍｎ３Ｏ４、Ｍｎ２Ｏ３、Ｍｎ２Ｏ７などが挙げられる。正極に含まれるマンガン酸化物の主成分が二酸化マンガンであることが好ましい。ここでいう主成分とは、マンガン酸化物中に占める二酸化マンガンの割合が５０質量％以上であることを意味する。マンガン酸化物中に占める二酸化マンガンの割合は、７０質量％以上であってもよく、９０質量％以上であってもよい。
　正極活物質として二酸化マンガン以外の他の活物質を含んでもよい。他の活物質としては、フッ化黒鉛、二硫化鉄、三硫化アンチモンなどが挙げられる。正極活物質全体に占める二酸化マンガン以外の他の活物質の割合は、０．５質量％以上、１０質量％以下であってもよい。
　正極は、正極活物質、結着剤、導電剤などを含む正極合剤を含んでもよい。結着剤としては、例えば、ポリテトラフルオロエチレンなどのフッ素樹脂、ゴム粒子、アクリル樹脂、ポリイミド樹脂が挙げられる。導電剤としては、例えば、導電性炭素材料が挙げられる。導電性炭素材料としては、例えば、天然黒鉛、人造黒鉛、カーボンブラック、炭素繊維、カーボンナノチューブが挙げられる。
　正極は、さらに正極合剤を保持する正極集電体を含み得る。正極集電体の材質としては、例えば、ステンレス鋼、アルミニウム、チタンなどが挙げられる。
　コイン形電池の場合、断面がＬ字型のリング状の正極集電体を正極合剤ペレットに装着して正極を構成してもよく、正極合剤ペレットのみで正極を構成してもよい。正極合剤ペレットは、例えば、正極活物質などに適量の水を加えて調製した湿潤状態の正極合剤を圧縮成形し、乾燥することにより得られる。
　円筒形電池の場合、シート状の正極集電体と、正極集電体に保持された正極合剤層と、を備える正極を用いることができる。シート状の正極集電体としては、有孔の集電体が好ましい。有孔の集電体としては、エキスパンドメタル、ネット、パンチングメタルなどが挙げられる。正極合剤層は、例えば、上記の湿潤状態の正極合剤をシート状の正極集電体の表面に塗布または正極集電体に充填し、厚み方向に加圧し、乾燥することにより得られる。
（負極）
　負極は、上記のリチウム合金を含む。リチウム合金は、リチウム一次電池の形状、寸法、規格性能などに応じて、任意の形状および厚さに成形される。負極は、リチウム合金シートとともに、銅箔などの負極集電体を備えてもよい。リチウム合金がＭｇを含み、放電末期に比較的強度が高いＭｇが残ることから、負極集電体を用いずに、リチウム合金シート（箔）のみを用いて負極を構成してもよい。Ｍｇを含むリチウム合金では、放電末期の負極の部分的欠損もしくは破断が抑制され、負極中のＬｉを余すことなく有効に用いることができる。
　コイン形電池の場合、フープ状のリチウム合金を、円板状に打ち抜いたものを負極に用いてもよい。円筒形電池の場合、シート状のリチウム合金を負極に用いてもよい。シートは、例えば、押し出し成形により得られる。より具体的には、円筒形電池では、長手方向と短手方向とを有する形状を備える、リチウム合金箔などが用いられる。
　負極は、リチウムイオンの吸蔵および放出が可能な炭素材料および／またはシリコン含有材料を含む活物質層を備えてもよい。
（非水電解液）
　非水電解液は、例えば、非水溶媒と、リチウム塩と、を含む。非水電解液に含まれるリチウムイオンの濃度（リチウム塩の合計濃度）は、例えば、０．２ｍｏｌ／Ｌ以上、２．０ｍｏｌ／Ｌ以下であり、０．３ｍｏｌ／Ｌ以上、１．５ｍｏｌ／Ｌ以下であってもよい。
　非水溶媒としては、リチウム一次電池の非水電解液に一般的に用いられ得る有機溶媒が挙げられる。非水溶媒としては、エーテル、エステル、炭酸エステルなどが挙げられる。非水溶媒としては、ジメチルエーテル、γ－ブチルラクトン、プロピレンカーボネート（ＰＣ）、エチレンカーボネート（ＥＣ）、ジメチルカーボネート、ジエチルカーボネート、エチルメチルカーボネート、１，２－ジメトキシエタン（ＤＭＥ）、１，２－ジエトキシエタン、酢酸メチル、酢酸エチル、酢酸プロピルなどを用いることができる。非水電解液は、一種の非水溶媒を含んでいてもよく、二種以上の非水溶媒を含んでいてもよい。
　リチウム一次電池の放電特性を向上させる観点から、非水溶媒は、沸点が高い環状炭酸エステルと、低温下でも低粘度である鎖状エーテルとを含んでいることが好ましい。環状炭酸エステルは、ＰＣおよびＥＣよりなる群から選択される少なくとも一種を含むことが好ましく、ＰＣが特に好ましい。鎖状エーテルは、ＤＭＥを含むことが好ましい。
　リチウム塩としては、例えば、リチウム一次電池で溶質として用いられるリチウム塩が挙げられる。このようなリチウム塩としては、例えば、ＬｉＣＦ３ＳＯ３、ＬｉＣｌＯ４、ＬｉＢＦ４、ＬｉＰＦ６、ＬｉＲａＳＯ３（Ｒａは炭素数１～４のフッ化アルキル基）、ＬｉＦＳＯ３、ＬｉＮ（ＳＯ２Ｒｂ）（ＳＯ２Ｒｃ）（ＲｂおよびＲｃはそれぞれ独立に炭素数１～４のフッ化アルキル基）、ＬｉＮ（ＦＳＯ２）２、ＬｉＮ（ＳＯ２ＣＦ３）２、ＬｉＮ（ＳＯ２Ｆ）（ＰＯＦ２）、ＬｉＰＯ２Ｆ２、ＬｉＢ（Ｃ２Ｏ４）２、ＬｉＢＦ２（Ｃ２Ｏ４）が挙げられる。中でも、Ｍｇを含むリチウム合金に対する安定性の観点から、ＬｉＣＦ３ＳＯ３、ＬｉＢＦ４、およびＬｉＮ（ＦＳＯ２）２からなる群より選択される少なくとも１種が好ましい。非水電解液は、これらのリチウム塩を一種含んでいてもよく、二種以上含んでいてもよい。
　非水電解液は、上記の添加剤などの他の成分を更に含んでもよい。上記の添加剤以外の他の成分としては、プロパンスルトン、プロペンスルトン、エチレンサルファイト、３，２－ジオキサチオラン－２，２－ジオキサイド、ビニレンカーボネート、ビニルエチレンカーボネート、フルオロエチレンカーボネート、アジポニトリル、スクシノニトリル、無水コハク酸などが挙げられる。他の成分は、リチウム塩であってもよく、リチウムイオンを生成可能であってもよい。
（セパレータ）
　リチウム一次電池は、通常、正極と負極との間に介在するセパレータを備えている。セパレータとしては、リチウム一次電池の内部環境に対して耐性を有する絶縁性材料で形成された多孔質シートを使用すればよい。具体的には、合成樹脂製の不織布、合成樹脂製の微多孔膜、またはこれらの積層体などが挙げられる。
　不織布に用いられる合成樹脂としては、例えば、ポリプロピレン、ポリフェニレンサルファイド、ポリブチレンテレフタレートなどが挙げられる。微多孔膜に用いられる合成樹脂としては、例えば、ポリエチレン、ポリプロピレン、エチレン－プロピレン共重合体などのポリオレフィン樹脂などが挙げられる。微多孔膜は、必要により、無機粒子を含有してもよい。
　セパレータの厚みは、例えば、５μｍ以上、１００μｍ以下である。
　リチウム一次電池の構造は特に限定されない。リチウム一次電池は、円板状の正極と円板状の負極とをセパレータを介して積層して構成された積層型電極群を備えるコイン形電池でもよい。帯状の正極と帯状の負極とをセパレータを介して渦巻き状に捲回して構成された捲回型電極群を備える円筒形電池でもよい。
　図１に、本開示の一実施形態に係る円筒形のリチウム一次電池の一部を断面にした正面図を示す。リチウム一次電池１０は、正極１と、負極２とが、セパレータ３を介して捲回された電極群が、非水電解液（図示せず）とともに電池ケース９に収容されている。電池ケース９の開口部には封口板８が装着されている。封口板８には、正極１の集電体１ａに接続された正極リード４が接続されている。負極２に接続された負極リード５は、電池ケース９に接続されている。また、電極群の上部と下部には、内部短絡防止のためにそれぞれ上部絶縁板６、下部絶縁板７が配置されている。
《付記》
　以上の実施形態の記載により、以下の技術が開示される。
（技術１）
　正極と、負極と、非水電解液と、を備え、
　前記正極は、二酸化マンガンを含み、
　前記負極は、リチウム合金を含み、
　前記リチウム合金は、マグネシウムを含み、
　前記リチウム合金中の前記マグネシウムの含有量は、１０質量％以下である、リチウム一次電池。
（技術２）
　前記非水電解液は、環状イミド化合物、フタル酸エステル化合物、およびイソシアネート化合物からなる群より選択される少なくとも１種の添加剤を含む、技術１に記載のリチウム一次電池。
（技術３）
　前記環状イミド化合物は、フタルイミドおよびＮ－置換フタルイミドからなる群より選択される少なくとも１種を含む、技術２に記載のリチウム一次電池。
（技術４）
　前記Ｎ－置換フタルイミドは、Ｎ－ヒドロキシフタルイミド、Ｎ－（２－ヒドロキシエチル）フタルイミド、Ｎ－（シクロヘキシルチオ）フタルイミド、およびＮ－（フェニルチオ）フタルイミドからなる群より選択される少なくとも１種を含む、技術３に記載のリチウム一次電池。
（技術５）
　前記非水電解液中の前記環状イミド化合物の含有量は、１質量％以下である、技術２～４のいずれか１つに記載のリチウム一次電池。
（技術６）
　前記フタル酸エステル化合物は、フタル酸ジエステル化合物を含む、技術２～５のいずれか１つに記載のリチウム一次電池。
（技術７）
　前記フタル酸ジエステル化合物は、フタル酸ジメチルを含む、技術６に記載のリチウム一次電池。
（技術８）
　前記非水電解液中の前記フタル酸エステル化合物の含有量は、１質量％以下である、技術２～７のいずれか１つに記載のリチウム一次電池。
（技術９）
　前記イソシアネート化合物は、ジイソシアネート化合物を含む、技術２～８のいずれか１つに記載のリチウム一次電池。
（技術１０）
　前記ジイソシアネート化合物は、ヘキサメチレンジイソシアネート、１，３－ビス（イソシアナトメチル）シクロヘキサン、およびイソホロンジイソシアネートからなる群より選択される少なくとも１種を含む、技術９に記載のリチウム一次電池。
（技術１１）
　前記非水電解液中の前記イソシアネート化合物の含有量は、３質量％以下である、技術２～１０のいずれか１つに記載のリチウム一次電池。
［実施例］
　以下、本開示を実施例および比較例に基づいて具体的に説明するが、本開示は以下の実施例に限定されるものではない。
《実施例１～５、比較例１～２》
（正極の作製）
　正極活物質１００質量部に、導電剤であるケッチェンブラック５質量部と、結着剤であるポリテトラフルオロエチレン５質量部と、適量の純水と、を加えて混錬し、湿潤状態の正極合剤を調製した。正極活物質には、電解二酸化マンガン（ＭｎＯ２）を用いた。
　次に、正極合剤を、ステンレス鋼（ＳＵＳ４４４）製の厚み０．１ｍｍのエキスパンドメタルからなる正極集電体に充填して、正極前駆体を作製した。その後、正極前駆体を、乾燥させ、ロールプレスにより圧延し、縦３．５ｃｍおよび横２０ｃｍのサイズに裁断することにより、正極を得た。続いて、充填された正極合剤の一部を剥離し、正極集電体を露出させた部分にＳＵＳ４４４製の正極リードの一端部を抵抗溶接した。
（負極の作製）
　リチウム合金箔（厚み２５０μｍ）を縦３．７ｃｍおよび横２２ｃｍのサイズに裁断することにより、負極を得た。負極の所定箇所にニッケル製の負極リードの一端部を圧接により接続した。リチウム合金箔には、Ｍｇ含有量が表１に示す値であるＬｉ－Ｍｇ合金箔、または、Ｌｉ－Ａｌ合金箔（Ａｌ含有量：２質量％）を用いた。Ｍｇ等の含有量はＩＣＰ発光分光分析または原子吸光分析により求められ、リチウム合金のＭｇ等の含有量の欄における「－」は、ＩＣＰ発光分光分析または原子吸光分析によりＭｇ等が検出されなかったことを示す。
（電極群の作製）
　正極と負極とをセパレータを介して捲回することで、電極群を作製した。セパレータには厚み２５μｍのポリプロピレン製の微多孔膜を用いた。
（非水電解液の調製）
　ＰＣとＥＣとＤＭＥとの混合溶媒（体積比３：２：５）にＬｉＣＦ３ＳＯ３を０．５ｍｏｌ／Ｌの濃度で溶解させ、非水電解液を調製した。
（リチウム一次電池の組み立て）
　負極端子を兼ねる円筒形状の電池ケースに電極群を収容した。電池ケースには、鉄製ケース（外径１７ｍｍ、高さ４５．５ｍｍ）を用いた。次いで、電池ケース内に非水電解液を注入した後、正極端子を兼ねる金属製の封口板を用いて電池ケースの開口部を閉じた。正極リードの他端部を封口板に接続し、負極リードの他端部を電池ケースの内底面に接続した。このようにして、リチウム一次電池を作製した。なお、表１中、Ａ１～Ａ５は実施例１～５の電池であり、Ｂ１～Ｂ２は比較例１～２の電池である。
　得られた実施例および比較例の各電池について、組み立て後に４５℃の雰囲気下で３日間のエージングを行い、以下の評価を行った。
［評価］
（初期容量）
　エージング後の電池について、２０℃の環境下、電池電圧が０．９Ｖに達するまで２．５ｍＡで定電流放電を行った。このときの放電時間を測定し、初期容量を求めた。
（保存後容量）
　エージング後の電池を８５℃の環境下で３か月保存した。保存後の電池について、２０℃の環境下、電池電圧が０．９Ｖに達するまで２．５ｍＡで定電流放電を行った。このときの放電時間を測定し、保存後容量を求めた。
（保存後の容量劣化率）
　上記で求められた初期容量および保存後容量を用いて、下記式により保存後の容量劣化率を求めた。
　保存後の容量劣化率（％）＝｛１－（保存後容量／初期容量）｝×１００
　評価結果を表１に示す。なお、表１中の初期容量および保存後の容量は、比較例１の電池Ｂ１の初期容量を１００とするときの相対値（指数）として表す。
Figure JPOXMLDOC01-appb-T000001
　電池Ａ１～Ａ５では、電池Ｂ１～Ｂ２と比べて、初期および保存後の容量が大きく、容量劣化率が小さく抑えられた。
《実施例６～１４》
　負極の作製において、リチウム合金箔には、Ｍｇ含有量が１質量％であるリチウム合金箔を用いた。非水電解液の調製において、必要に応じて、非水電解液に添加剤を更に含ませた。添加剤には、表２に示す化合物を用いた。非水電解液中の添加剤の含有量は、表２に示す値とした。
　上記以外、実施例１の電池Ａ１と同様にして、実施例６～１４の電池Ａ６～Ａ１４を作製し、評価した。
　評価結果を表２に示す。なお、表２中の初期容量および保存後の容量は、比較例１の電池Ｂ１の初期容量を１００とするときの相対値（指数）として表す。
Figure JPOXMLDOC01-appb-T000002
　電池Ａ６～Ａ１４のいずれも、初期および保存後の容量が大きく、容量劣化率が小さかった。非水電解液に添加剤を含ませた電池Ａ７～Ａ１４では、容量劣化率が更に低減された。
　本開示のリチウム一次電池は、例えば、各種メータ（例えば、電気、水道、ガスなどのスマートメータ）の主電源、メモリーバックアップ電源として好適に用いられる。
　本発明を現時点での好ましい実施態様に関して説明したが、そのような開示を限定的に解釈してはならない。種々の変形および改変は、上記開示を読むことによって本発明に属する技術分野における当業者には間違いなく明らかになるであろう。したがって、添付の請求の範囲は、本発明の真の精神および範囲から逸脱することなく、すべての変形および改変を包含する、と解釈されるべきものである。
　１：正極、１ａ：正極集電体、２：負極、３：セパレータ、４：正極リード、５：負極リード、６：上部絶縁板、７：下部絶縁板、８：封口板、９：電池ケース、１０：リチウム一次電池
 
 
 

Claims (11)

  1. 　正極と、負極と、非水電解液と、を備え、
    　前記正極は、二酸化マンガンを含み、
    　前記負極は、リチウム合金を含み、
    　前記リチウム合金は、マグネシウムを含み、
    　前記リチウム合金中の前記マグネシウムの含有量は、１０質量％以下である、リチウム一次電池。
  2. 　前記非水電解液は、環状イミド化合物、フタル酸エステル化合物、およびイソシアネート化合物からなる群より選択される少なくとも１種の添加剤を含む、請求項１に記載のリチウム一次電池。
  3. 　前記環状イミド化合物は、フタルイミドおよびＮ－置換フタルイミドからなる群より選択される少なくとも１種を含む、請求項２に記載のリチウム一次電池。
  4. 　前記Ｎ－置換フタルイミドは、Ｎ－ヒドロキシフタルイミド、Ｎ－（２－ヒドロキシエチル）フタルイミド、Ｎ－（シクロヘキシルチオ）フタルイミド、およびＮ－（フェニルチオ）フタルイミドからなる群より選択される少なくとも１種を含む、請求項３に記載のリチウム一次電池。
  5. 　前記非水電解液中の前記環状イミド化合物の含有量は、１質量％以下である、請求項２に記載のリチウム一次電池。
  6. 　前記フタル酸エステル化合物は、フタル酸ジエステル化合物を含む、請求項２に記載のリチウム一次電池。
  7. 　前記フタル酸ジエステル化合物は、フタル酸ジメチルを含む、請求項６に記載のリチウム一次電池。
  8. 　前記非水電解液中の前記フタル酸エステル化合物の含有量は、１質量％以下である、請求項２に記載のリチウム一次電池。
  9. 　前記イソシアネート化合物は、ジイソシアネート化合物を含む、請求項２に記載のリチウム一次電池。
  10. 　前記ジイソシアネート化合物は、ヘキサメチレンジイソシアネート、１，３－ビス（イソシアナトメチル）シクロヘキサン、およびイソホロンジイソシアネートからなる群より選択される少なくとも１種を含む、請求項９に記載のリチウム一次電池。
  11. 　前記非水電解液中の前記イソシアネート化合物の含有量は、３質量％以下である、請求項２に記載のリチウム一次電池。
     
     
     
PCT/JP2023/030295 2022-08-24 2023-08-23 リチウム一次電池 WO2024043273A1 (ja)