WO2023238797A1 - Composition - Google Patents
Composition Download PDFInfo
- Publication number
- WO2023238797A1 WO2023238797A1 PCT/JP2023/020651 JP2023020651W WO2023238797A1 WO 2023238797 A1 WO2023238797 A1 WO 2023238797A1 JP 2023020651 W JP2023020651 W JP 2023020651W WO 2023238797 A1 WO2023238797 A1 WO 2023238797A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- filler
- composition
- thermally conductive
- polymer
- present
- Prior art date
Abstract
L'invention fournit une composition qui comprend un fluoroélastomère ou un polymère de tétrafluoroéthylène thermofusible, la composition étant appropriée pour une utilisation en tant que matériau d'interface thermique et permettant de former des articles moulés, tels que des feuilles, qui ont d'excellentes propriétés mécaniques et une excellente résistance à la chaleur, ont un faible coefficient de dilatation linéaire, une constante diélectrique et une tangente diélectrique, et, en particulier, ont une excellente conductivité thermique tout en étant toujours électriquement isolantes. Une composition selon la présente invention comprend un fluoroélastomère ou un polymère de tétrafluoroéthylène thermofusible qui a une température de fusion supérieure à 100 °C, mais pas supérieure à 325 °C, une charge minérale thermoconductrice qui a un diamètre de particule moyen d'au moins 10 µm, et une charge thermoconductrice qui a un diamètre de particule moyen inférieur à 2 µm.
Applications Claiming Priority (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2022-092826 | 2022-06-08 | ||
JP2022092826 | 2022-06-08 | ||
JP2022092827 | 2022-06-08 | ||
JP2022-092827 | 2022-06-08 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2023238797A1 true WO2023238797A1 (fr) | 2023-12-14 |
Family
ID=89118323
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/JP2023/020651 WO2023238797A1 (fr) | 2022-06-08 | 2023-06-02 | Composition |
Country Status (1)
Country | Link |
---|---|
WO (1) | WO2023238797A1 (fr) |
Citations (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH07102274A (ja) * | 1993-09-13 | 1995-04-18 | Dow Corning Corp | フッ素化ポリマー油及び六方格子窒化ホウ素を用いたグリース組成物 |
JP2007070492A (ja) * | 2005-09-07 | 2007-03-22 | Hitachi Ltd | 熱伝導性グリース、接着剤、及びエラストマー組成物、並びに冷却装置 |
WO2007135875A1 (fr) * | 2006-05-19 | 2007-11-29 | Daikin Industries, Ltd. | Composition de résine fluorée thermoplastique contenant du silicone, article moulé formé à partir de celle-ci et procédé servant à préparer une composition de résine fluorée thermoplastique contenant du silicone |
JP2008524028A (ja) * | 2004-12-16 | 2008-07-10 | イー・アイ・デュポン・ドウ・ヌムール・アンド・カンパニー | 改良された熱伝達性質および耐磨耗性を有するフルオロポリマー剥離コーティング |
JP2011195710A (ja) * | 2010-03-19 | 2011-10-06 | Sumitomo Electric Ind Ltd | 白色樹脂成形体及びled用リフレクタ |
JP2014185294A (ja) * | 2013-03-25 | 2014-10-02 | Mitsubishi Chemicals Corp | 樹脂組成物、反射部材、発光装置、及び照明器具 |
JP2015048414A (ja) * | 2013-09-02 | 2015-03-16 | 日東電工株式会社 | 絶縁性熱伝導シート |
JP2019089957A (ja) * | 2017-11-15 | 2019-06-13 | 積水化学工業株式会社 | 樹脂組成物及び積層体 |
JP2022098733A (ja) * | 2020-12-22 | 2022-07-04 | Agc株式会社 | テトラフルオロエチレン系ポリマーの組成物、該組成物を含む液状組成物、およびシート |
-
2023
- 2023-06-02 WO PCT/JP2023/020651 patent/WO2023238797A1/fr unknown
Patent Citations (9)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH07102274A (ja) * | 1993-09-13 | 1995-04-18 | Dow Corning Corp | フッ素化ポリマー油及び六方格子窒化ホウ素を用いたグリース組成物 |
JP2008524028A (ja) * | 2004-12-16 | 2008-07-10 | イー・アイ・デュポン・ドウ・ヌムール・アンド・カンパニー | 改良された熱伝達性質および耐磨耗性を有するフルオロポリマー剥離コーティング |
JP2007070492A (ja) * | 2005-09-07 | 2007-03-22 | Hitachi Ltd | 熱伝導性グリース、接着剤、及びエラストマー組成物、並びに冷却装置 |
WO2007135875A1 (fr) * | 2006-05-19 | 2007-11-29 | Daikin Industries, Ltd. | Composition de résine fluorée thermoplastique contenant du silicone, article moulé formé à partir de celle-ci et procédé servant à préparer une composition de résine fluorée thermoplastique contenant du silicone |
JP2011195710A (ja) * | 2010-03-19 | 2011-10-06 | Sumitomo Electric Ind Ltd | 白色樹脂成形体及びled用リフレクタ |
JP2014185294A (ja) * | 2013-03-25 | 2014-10-02 | Mitsubishi Chemicals Corp | 樹脂組成物、反射部材、発光装置、及び照明器具 |
JP2015048414A (ja) * | 2013-09-02 | 2015-03-16 | 日東電工株式会社 | 絶縁性熱伝導シート |
JP2019089957A (ja) * | 2017-11-15 | 2019-06-13 | 積水化学工業株式会社 | 樹脂組成物及び積層体 |
JP2022098733A (ja) * | 2020-12-22 | 2022-07-04 | Agc株式会社 | テトラフルオロエチレン系ポリマーの組成物、該組成物を含む液状組成物、およびシート |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
JP6947158B2 (ja) | 熱伝導シートおよびその製造方法、ならびに放熱装置 | |
CN107406728B (zh) | 粘接组合物片材及其制造方法以及半导体器件 | |
JP2023143942A (ja) | 放熱装置 | |
WO2023238797A1 (fr) | Composition | |
WO2023238798A1 (fr) | Composition | |
JP2022061412A (ja) | 液状組成物の製造方法及び積層体の製造方法 | |
TW202405083A (zh) | 組成物 | |
TW202405082A (zh) | 組成物 | |
JP2022098733A (ja) | テトラフルオロエチレン系ポリマーの組成物、該組成物を含む液状組成物、およびシート | |
WO2023276946A1 (fr) | Composition | |
WO2023163025A1 (fr) | Composition | |
JP2023114333A (ja) | 組成物 | |
JP2023114334A (ja) | 組成物 | |
JP2023028091A (ja) | 組成物及び積層体の製造方法 | |
WO2023054649A1 (fr) | Composition, procédé de production de composition et procédé de production de feuille | |
JP2022151685A (ja) | 非酸化物系セラミックスの加工用材料及び積層基板 | |
WO2023013569A1 (fr) | Procédé de fabrication de feuille, procédé de fabrication de feuille stratifiée et feuille | |
JP2023127137A (ja) | テトラフルオロエチレン系ポリマーを含む層を有する積層体の製造方法 | |
JP2023127849A (ja) | テトラフルオロエチレン系ポリマーを含むポリマー層付基材の製造方法 | |
WO2023238505A1 (fr) | Dispersion liquide | |
WO2024053554A1 (fr) | Composition liquide et procédé de production d'un stratifié utilisant la composition liquide | |
JP2023075825A (ja) | 改質粉体の製造方法 | |
WO2023017811A1 (fr) | Dispersion aqueuse et procédé de production de stratifié | |
JP2022072333A (ja) | テトラフルオロエチレン系ポリマーの組成物、該組成物を含む液状組成物、積層体およびフィルム | |
WO2023224050A1 (fr) | Procédé pour la production d'une dispersion aqueuse et dispersion aqueuse |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |