WO2023136680A1 - 비수 전해질용 첨가제를 포함하는 비수 전해질 및 이를 포함하는 리튬 이차전지 - Google Patents
비수 전해질용 첨가제를 포함하는 비수 전해질 및 이를 포함하는 리튬 이차전지 Download PDFInfo
- Publication number
- WO2023136680A1 WO2023136680A1 PCT/KR2023/000700 KR2023000700W WO2023136680A1 WO 2023136680 A1 WO2023136680 A1 WO 2023136680A1 KR 2023000700 W KR2023000700 W KR 2023000700W WO 2023136680 A1 WO2023136680 A1 WO 2023136680A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- carbon atoms
- aqueous electrolyte
- formula
- based compounds
- Prior art date
Abstract
Description
용량 유지율 (%) | |
실시예 1 | 76.9 |
실시예 2 | 77.8 |
실시예 3 | 79.1 |
실시예 4 | 79.5 |
실시예 5 | 75.2 |
실시예 6 | 77.3 |
비교예 1 | 73.9 |
저항 증가율 (%) | |
실시예 1 | 29.5 |
실시예 2 | 22.6 |
실시예 3 | 21.0 |
실시예 4 | 8.3 |
실시예 5 | 35.8 |
실시예 6 | 26.4 |
비교예 1 | 45.4 |
Claims (15)
- 하기 화학식 1로 표시되는 반복단위 및 화학식 2로 표시되는 반복단위를 포함하는 비수 전해질용 첨가제를 포함하는 비수 전해질:[화학식 1]상기 화학식 1에서 X 는 탄소수 1 내지 10의 퍼플루오로알킬기이고,R1 은 H, 탄소수 1 내지 10의 알킬기, 탄소수 2 내지 20의 알케닐기, 탄소수 2 내지 20의 알키닐기, 탄소수 1 내지 20의 알콕시기, 탄소수 3 내지 12의 사이클로알킬기, 탄소수 3 내지 12의 사이클로알케닐기, 탄소수 6 내지 12의 아릴기, 할로겐 원자 및 니트릴기로 이루어지는 군으로부터 선택된 어느 하나이며,[화학식 2]상기 화학식 2 에서 R 은 니트릴기가 하나 이상 치환된 탄소수 1 내지 10 의 알킬기이고,R2 는 H, 탄소수 1 내지 10의 알킬기, 탄소수 2 내지 20의 알케닐기, 탄소수 2 내지 20의 알키닐기, 탄소수 1 내지 20의 알콕시기, 탄소수 3 내지 12의 사이클로알킬기, 탄소수 3 내지 12의 사이클로알케닐기, 탄소수 6 내지 12의 아릴기, 할로겐 원자 및 니트릴기로 이루어지는 군으로부터 선택된 어느 하나임.
- 청구항 1에 있어서,상기 X 는 CF3이고, R은 CH2CH2CN인 비수 전해질.
- 청구항 2에 있어서,상기 X 는 CF3이고, R은 CH2CH2CN인 비수 전해질.
- 청구항 2에 있어서,상기 m 은 10 내지 50 의 정수이고, 상기 n 은 60 내지 100의 정수인 비수 전해질.
- 청구항 1에 있어서,상기 비수 전해질용 첨가제는 비수 전해질 100 중량부에 대하여 0.01 중량부 내지 5 중량부의 함량으로 포함되는 것인 비수 전해질.
- 청구항 1에 있어서,LiCl, LiBr, LiI, LiBF4, LiClO4, LiB10Cl10, LiAlCl4, LiAlO2, LiPF6, LiCF3SO3, LiCH3CO2, LiCF3CO2, LiAsF6, LiSbF6, LiCH3SO3, LiN(SO2F)2, LiN(SO2CF2CF3)2 및 LiN(SO2CF3)2로 이루어진 군으로부터 선택된 하나 이상의 적어도 하나 이상의 리튬염을 추가로 포함하는 것인 비수 전해질.
- 청구항 7에 있어서,상기 리튬염은 0.5 M 내지 4.0 M의 농도로 포함되는 것인 비수 전해질.
- 청구항 1에 있어서,추가로 유기 용매를 더 포함하는 비수 전해질.
- 청구항 9에 있어서,상기 유기 용매는 환형 카보네이트계 유기용매를 포함하는 비수 전해질.
- 청구항 10에 있어서,상기 환형 카보네이트계 유기용매는 플루오로 에틸렌 카보네이트(FEC)인 비수 전해질.
- 청구항 1에 있어서,첨가제로서 환형 카보네이트계 화합물, 할로겐 치환된 카보네이트계 화합물, 설톤계 화합물, 설페이트계 화합물, 포스페이트계 화합물, 보레이트계 화합물, 니트릴계 화합물, 벤젠계 화합물, 아민계 화합물, 실란계 화합물 및 리튬염계 화합물들로 이루어진 군으로부터 선택된 1종 이상의 화합물을 더 포함하는 비수 전해질.
- 양극;음극; 및청구항 1 의 비수 전해질을 포함하는 리튬 이차전지.
- 청구항 13에 있어서,상기 음극은 음극 활물질로서 SiOx(0≤x≤2)를 포함하는 것인 리튬 이차전지.