WO2022259815A1 - Composition durcissable, et objet durci - Google Patents

Composition durcissable, et objet durci Download PDF

Info

Publication number
WO2022259815A1
WO2022259815A1 PCT/JP2022/020196 JP2022020196W WO2022259815A1 WO 2022259815 A1 WO2022259815 A1 WO 2022259815A1 JP 2022020196 W JP2022020196 W JP 2022020196W WO 2022259815 A1 WO2022259815 A1 WO 2022259815A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
meth
formula
polymer
curable composition
Prior art date
Application number
PCT/JP2022/020196
Other languages
English (en)
Japanese (ja)
Inventor
修一 後藤
智広 安江
慧斌 文
Original Assignee
綜研化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 綜研化学株式会社 filed Critical 綜研化学株式会社
Priority to CN202280040628.7A priority Critical patent/CN117529524A/zh
Priority to JP2023527583A priority patent/JPWO2022259815A1/ja
Publication of WO2022259815A1 publication Critical patent/WO2022259815A1/fr

Abstract

L'invention a pour objet de fournir une composition durcissable présentant un durcissement rapide y compris sans mise en œuvre de catalyseur de durcissement à base d'étain, et permettant de former un objet durci excellent en termes de stabilité de stockage et de propriétés mécaniques, ou une composition durcissable excellente en termes d'adhérence.　Cette composition durcissable est caractéristique en ce qu'elle comprend : un polymère (méth)acrylique (A) possédant un groupe représenté par la formule (1), présentant une masse moléculaire moyenne en nombre (Mn) supérieure ou égale à 1000, et comprenant ５００ｐｐｍ ou plus d'un élément silicium ; et un agent de couplage au silane (B) représenté par la formule (2) et présentant une masse moléculaire inférieure à １０００. Formule （１）：－Ｘ－ＣＨ2－ＳｉＲ1 3； formule （２）：Ｙ－ＣＨ2－ＳｉＲ1 3
PCT/JP2022/020196 2021-06-08 2022-05-13 Composition durcissable, et objet durci WO2022259815A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN202280040628.7A CN117529524A (zh) 2021-06-08 2022-05-13 固化性组合物以及固化物
JP2023527583A JPWO2022259815A1 (fr) 2021-06-08 2022-05-13

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2021-096153 2021-06-08
JP2021096153 2021-06-08

Publications (1)

Publication Number Publication Date
WO2022259815A1 true WO2022259815A1 (fr) 2022-12-15

Family

ID=84424851

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2022/020196 WO2022259815A1 (fr) 2021-06-08 2022-05-13 Composition durcissable, et objet durci

Country Status (3)

Country Link
JP (1) JPWO2022259815A1 (fr)
CN (1) CN117529524A (fr)
WO (1) WO2022259815A1 (fr)

Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010202863A (ja) * 2009-02-04 2010-09-16 Cemedine Co Ltd 硬化性組成物
JP2012122048A (ja) * 2010-11-18 2012-06-28 Kaneka Corp ポリオキシアルキレン系重合体を含有する硬化性組成物
JP2012136685A (ja) * 2010-12-09 2012-07-19 Kaneka Corp （メタ）アクリル系重合体を含有する硬化性組成物
JP2012214755A (ja) * 2011-03-31 2012-11-08 Kaneka Corp 硬化性組成物

Patent Citations (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010202863A (ja) * 2009-02-04 2010-09-16 Cemedine Co Ltd 硬化性組成物
JP2012122048A (ja) * 2010-11-18 2012-06-28 Kaneka Corp ポリオキシアルキレン系重合体を含有する硬化性組成物
JP2012136685A (ja) * 2010-12-09 2012-07-19 Kaneka Corp （メタ）アクリル系重合体を含有する硬化性組成物
JP2012214755A (ja) * 2011-03-31 2012-11-08 Kaneka Corp 硬化性組成物

Also Published As

Publication number Publication date
CN117529524A (zh) 2024-02-06
JPWO2022259815A1 (fr) 2022-12-15

Similar Documents

Publication Publication Date Title
EP3728423B1 (fr) Compositions polymères préparées avec un initiateur radicalaire contrôlé
JP2001040037A (ja) 反応性アクリル系重合体、硬化性アクリル系重合体、硬化性組成物、硬化体およびこれらの用途
US20220396654A1 (en) Modified Diene Copolymers and Their Use
CN103319923A (zh) 活性能量射线固化性组合物以及涂装薄膜
WO2015098314A1 (fr) Composition pour agent adhésif, agent adhésif, et feuille adhésive
EP2222803B1 (fr) Revêtements acryliques modifiés par des alpha-silanes à durcissement par l'humidité
JP7241872B2 (ja) 硬化性組成物および硬化物
WO2022259815A1 (fr) Composition durcissable, et objet durci
WO2021132523A1 (fr) Composition adhésive durcissable à l'humidité
WO2021192815A1 (fr) Composition durcissable et produit durci
WO2022259816A1 (fr) Composition durcissable, objet durci, et composition durcissable à deux constituants
JP5922985B2 (ja) 湿気硬化型接着剤組成物
JPWO2019073980A1 (ja) 光硬化性粘着剤組成物、及び接着方法
JP3765343B2 (ja) 非水分散型樹脂組成物及び硬化性塗料
JP6814454B2 (ja) 組成物、ガスバリア材、コーティング材、接着剤、成形体、積層体及び成形体の製造方法
WO2022259783A1 (fr) Composition durcissable, et objet durci
JP5691312B2 (ja) シーラント用の硬化促進剤およびこれを用いるシーラントの施工方法
WO2020262273A1 (fr) Copolymère séquencé et composition de résine, et procédé de production de copolymère séquencé
WO2006033147A1 (fr) Polymère greffé de polysilsesquioxane, procédé servant à produire celui-ci et adhésif autocollant
WO2019039537A1 (fr) Polymère à base d'ester alkylique d'acide (méth)acrylique et utilisation associée
JP2022064209A (ja) 硬化性組成物および硬化物
US20100029838A1 (en) Use of Copolymers as Adhesion Promoters in Lacquers
JP2018100322A (ja) 反応性ホットメルト接着剤組成物
JP4964440B2 (ja) 油性インク組成物
WO2022202173A1 (fr) Composition de résine durcissable et son utilisation

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 22819998

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2023527583

Country of ref document: JP

WWE Wipo information: entry into national phase

Ref document number: 202280040628.7

Country of ref document: CN

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 22819998

Country of ref document: EP

Kind code of ref document: A1