WO2022137950A1 - Forêt de nanotubes de carbone modifiée, agrégat aligné de nanotubes de carbone, feuille perméable aux gaz, électrode de catalyseur pour piles à combustible, élément électroconducteur, élément électroconducteur de type fil, matériau thermoconducteur intercouche, et méthode de production de forêt de nanotubes de carbone modifiée - Google Patents

Forêt de nanotubes de carbone modifiée, agrégat aligné de nanotubes de carbone, feuille perméable aux gaz, électrode de catalyseur pour piles à combustible, élément électroconducteur, élément électroconducteur de type fil, matériau thermoconducteur intercouche, et méthode de production de forêt de nanotubes de carbone modifiée Download PDF

Info

Publication number
WO2022137950A1
WO2022137950A1 PCT/JP2021/042904 JP2021042904W WO2022137950A1 WO 2022137950 A1 WO2022137950 A1 WO 2022137950A1 JP 2021042904 W JP2021042904 W JP 2021042904W WO 2022137950 A1 WO2022137950 A1 WO 2022137950A1
Authority
WO
WIPO (PCT)
Prior art keywords
cnt
carbon nanotube
forest
modified
continuum
Prior art date
Application number
PCT/JP2021/042904
Other languages
English (en)
Japanese (ja)
Inventor
翼 井上
Original Assignee
株式会社シーディアイ
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社シーディアイ filed Critical 株式会社シーディアイ
Priority to JP2022571986A priority Critical patent/JP7549912B2/ja
Publication of WO2022137950A1 publication Critical patent/WO2022137950A1/fr
Priority to JP2024014780A priority patent/JP2024052746A/ja

Abstract

Le but de la présente invention est de fournir : une forêt de CNT modifiée où une forêt de CNT est modifiée avec une autre substance ; un agrégat aligné de CNT qui comprend un produit filé de la forêt de CNT modifiée ; une feuille perméable aux gaz qui comprend l'agrégat aligné de CNT ; une électrode de catalyseur pour des piles à combustible, qui est pourvue de la feuille perméable aux gaz ; un élément électroconducteur et un élément électroconducteur de type fil, chacun d'entre eux comprenant la forêt de CNT modifiée ou l'agrégat aligné de CNT ; un matériau thermoconducteur intercouche qui comprend l'élément électroconducteur ; et une méthode de production de la forêt de CNT modifiée.　La forêt de nanotubes de carbone modifiée (40) selon la présente invention comprend des nanotubes de carbone (50) qui sont alignés dans une direction prédéterminée et des microparticules (70) supportées sur les nanotubes de carbone (50), peut être filée, et a de préférence un rapport R supérieur ou égal à 3, où le rapport R est défini par la formule (1) ci-dessous à l'aide d'une distance d'espace adjacent D1 entre les nanotubes de carbone (50) et d'un diamètre moyen de particule D2 des microparticules (70). De préférence, les microparticules (70) ont une électroconductivité.　(1) : R = D1/D2 La distance d'espace adjacent D1 est exprimée par la formule (2) en utilisant la densité en nombre A (unité : nanotubes de carbone/m2) de la forêt de nanotubes de carbone modifiée (40) et le diamètre moyen D3 des nanotubes de carbone (50).　(2) : D1 = A-1/2-D3
PCT/JP2021/042904 2020-12-22 2021-11-24 Forêt de nanotubes de carbone modifiée, agrégat aligné de nanotubes de carbone, feuille perméable aux gaz, électrode de catalyseur pour piles à combustible, élément électroconducteur, élément électroconducteur de type fil, matériau thermoconducteur intercouche, et méthode de production de forêt de nanotubes de carbone modifiée WO2022137950A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
JP2022571986A JP7549912B2 (ja) 2020-12-22 2021-11-24 導電性部材の製造方法、および層間熱伝導材料の製造方法
JP2024014780A JP2024052746A (ja) 2020-12-22 2024-02-02 修飾カーボンナノチューブフォレスト、カーボンナノチューブ連続体および層間熱伝導材料

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020-212289 2020-12-22
JP2020212289 2020-12-22

Publications (1)

Publication Number Publication Date
WO2022137950A1 true WO2022137950A1 (fr) 2022-06-30

Family

ID=82159059

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/042904 WO2022137950A1 (fr) 2020-12-22 2021-11-24 Forêt de nanotubes de carbone modifiée, agrégat aligné de nanotubes de carbone, feuille perméable aux gaz, électrode de catalyseur pour piles à combustible, élément électroconducteur, élément électroconducteur de type fil, matériau thermoconducteur intercouche, et méthode de production de forêt de nanotubes de carbone modifiée

Country Status (2)

Country Link
JP (2) JP7549912B2 (fr)
WO (1) WO2022137950A1 (fr)

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20080039227A (ko) * 2006-10-31 2008-05-07 삼성전자주식회사 팔라듐 촉매 유도 탄소 나노구조체를 구비하는 소자 및 그제조 방법
JP2011064684A (ja) * 2009-09-15 2011-03-31 Qinghua Univ ラマン散乱基板及びそれを採用したラマンスペクトル測定システム

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5353689B2 (ja) 2009-12-28 2013-11-27 株式会社デンソー Ｃｎｔ繊維及びその製造方法

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20080039227A (ko) * 2006-10-31 2008-05-07 삼성전자주식회사 팔라듐 촉매 유도 탄소 나노구조체를 구비하는 소자 및 그제조 방법
JP2011064684A (ja) * 2009-09-15 2011-03-31 Qinghua Univ ラマン散乱基板及びそれを採用したラマンスペクトル測定システム

Also Published As

Publication number Publication date
JPWO2022137950A1 (fr) 2022-06-30
JP7549912B2 (ja) 2024-09-12
JP2024052746A (ja) 2024-04-12

Similar Documents

Publication Publication Date Title
US9573812B2 (en) CNT-infused metal fiber materials and process therefor
US6455021B1 (en) Method for producing carbon nanotubes
JP4504453B2 (ja) 線状カーボンナノチューブ構造体の製造方法
KR101913170B1 (ko) 탄소나노튜브를 포함하는 탄소 재료 및 탄소나노튜브 제조 방법
US7754283B2 (en) Continuous production of carbon nanotubes
US9963781B2 (en) Carbon nanotubes grown on nanostructured flake substrates and methods for production thereof
EP1810950A1 (fr) Agrégat de nanotube de carbone et procédé de fabrication idoine
US20120058352A1 (en) Metal substrates having carbon nanotubes grown thereon and methods for production thereof
US20030175462A1 (en) Iron-carbon composite, carbonaceous material comprising said iron-carbon composite and process for preparing the same
US20100239849A1 (en) Composite material
TWI380949B (zh) 奈米碳管長線結構
CN110734053B (zh) 碳纳米管的制备方法，碳纳米管纤维
WO2013109442A1 (fr) Conducteur à nanotubes de carbone possédant une conductivité électrique améliorée
JPH11116218A (ja) 単層ナノチューブの製造方法
US11512390B2 (en) Method of site-specific deposition onto a free-standing carbon article
WO2022137950A1 (fr) Forêt de nanotubes de carbone modifiée, agrégat aligné de nanotubes de carbone, feuille perméable aux gaz, électrode de catalyseur pour piles à combustible, élément électroconducteur, élément électroconducteur de type fil, matériau thermoconducteur intercouche, et méthode de production de forêt de nanotubes de carbone modifiée
JP5353689B2 (ja) Ｃｎｔ繊維及びその製造方法
JP6972627B2 (ja) カーボンナノチューブ複合体の製造方法及び積層体
US9970130B2 (en) Carbon nanofibers with sharp tip ends and a carbon nanofibers growth method using a palladium catalyst
JP5494322B2 (ja) Ｃｎｔワイヤの製造方法
Suda et al. Syntheses and electronic applications of Helical carbon nanofibers
Hekmat et al. Effect of Template on the Structure of Carbon Nanotubes Grown by Catalytic Chemical Vapor Deposition Method
JP2021167471A (ja) 複合糸及びその製造方法
TWI345794B (en) Method for making cable
Miao et al. The growth of bunched and multi-circularly wrapped carbon nanotubes on bulk magnetic alloys by microwave enhanced hot-filament CVD with a dilute gas of ammonia

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21910103

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 2022571986

Country of ref document: JP

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21910103

Country of ref document: EP

Kind code of ref document: A1