WO2022107325A1 - 一次電池 - Google Patents

一次電池 Download PDF

Info

Publication number
WO2022107325A1
WO2022107325A1 PCT/JP2020/043449 JP2020043449W WO2022107325A1 WO 2022107325 A1 WO2022107325 A1 WO 2022107325A1 JP 2020043449 W JP2020043449 W JP 2020043449W WO 2022107325 A1 WO2022107325 A1 WO 2022107325A1
Authority
WO
WIPO (PCT)
Prior art keywords
negative electrode
positive electrode
primary battery
battery
active material
Prior art date
Application number
PCT/JP2020/043449
Other languages
English (en)
French (fr)
Inventor
正也 野原
三佳誉 岩田
博章 田口
武志 小松
Original Assignee
日本電信電話株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日本電信電話株式会社 filed Critical 日本電信電話株式会社
Priority to JP2022563535A priority Critical patent/JPWO2022107325A1/ja
Priority to US18/251,042 priority patent/US20230387379A1/en
Priority to PCT/JP2020/043449 priority patent/WO2022107325A1/ja
Publication of WO2022107325A1 publication Critical patent/WO2022107325A1/ja

Abstract

一次電池であって、オキシ水酸化鉄を含む正極１０１と、マグネシウムまたはアルミニウムを含む負極１０３と、前記正極１０１と前記負極１０３との間に配置された電解質１０２と、を備える。

Description

一次電池
　本発明は、一次電池に関する。
　従来、小型デバイス、センサ、モバイル機器等に、使い捨ての一次電池及び、充電可能な二次電池としてアルカリ電池、マンガン電池、高性能なコイン型リチウム一次電池、ニカド電池、ニッケル水素電池、リチウムイオン電池等が広く使用されている。また、近年のＩｏＴ（Ｉｎｔｅｒｎｅｔ　ｏｆ　Ｔｈｉｎｇｓ）の発展において、土壌や森の中等自然界の至る所に設置して用いるばらまき型センサの開発も進んでいる。
　現在一般に用いられている電池は、リチウム、ニッケル、マンガン、コバルトなどのレアメタルで構成されている場合が多く、資源枯渇の問題がある。
　また、低環境負荷な空気電池の検討がされている（特許文献１）。
ＷＯ２０１８／００３７２４
　特許文献１の電池原理は空気電池であり、空気中の酸素を正極活物質として利用するため、電池に空気取り込み口が必須となる。そのため、空気電池には、上記空気取り込み口から電解液が揮発し、長期保存には不向きという欠点が存在する。したがって、密閉系での電池反応が可能な、新しい低環境負荷な電池が求められている。
　本発明は、上記事情に鑑みてなされたものであり、低環境負荷で、長期保存が可能な一次電池を提供することを目的とする。
　本発明の一態様の一次電池は、オキシ水酸化鉄を含む正極と、マグネシウムまたはアルミニウムを含む負極と、前記正極と前記負極との間に配置された電解質と、を備える。
　本発明によれば、低環境負荷で、長期保存が可能な一次電池を提供することができる。
図１は、本実施形態の一次電池の基本的な概略図である。 図２は、コイン型一次電池の構造を示す概略断面図である。 図３Ａは、バイポーラ型のスタック一次電池の構成例を示す構成図である。 図３Ｂは、バイポーラ型のスタック一次電池の構成例を示す平面図である。 実施例１の一次電池の放電曲線を示すグラフである。
　以下、本発明の実施の形態について図を参照して説明する。
　［一次電池の構成］
　図１は、本発明の実施の形態における一次電池の構成を示す構成図である。この一次電池は、オキシ水酸化鉄を含む正極１０１と、マグネシウムまたはアルミニウムを含む負極１０３と、正極１０１と負極１０３との間に配置された電解質１０２と、を備える。電解質１０２として、水系電解液１０２を用いることが好ましい。以下に説明する本実施形態では、電解質１０２に水系電解液１０２を用いた場合を一例として説明するが、これに限定されない。
　具体的には、正極１０１は、活物質としてオキシ水酸化鉄を用いて構成される。負極１０３は、活物質としてマグネシウムまたはアルミニウムを用いて構成される。水系電解液（電解質）１０２は、正極１０１および負極１０３と接するように配置される。このように、本実施形態の一次電池は、正極１０１にオキシ水酸化鉄の活物質を含み、負極１０３にマグネシウムまたはアルミニウムの活物質を含むことを特徴とする。
　正極１０１での放電反応は、次のように表すことができる。
　２ＦｅＯＯＨ＋２Ｈ２Ｏ＋２ｅ－→２Ｆｅ（ＯＨ）２＋２ＯＨ－・・・（１）
　上式中の水酸化物イオン（ＯＨ－）は、正極１０１から電気化学還元により水系電解液１０２中に溶解し、水系電解液１０２中を負極１０３の表面まで移動する。
　負極１０３での放電反応は次のように表すことができる。下記には一例として、負極１０３にマグネシウム（Ｍｇ）を用いた反応を示す。
　Ｍｇ＋２ＯＨ－→Ｍｇ（ＯＨ）2＋２ｅ－・・・（２）
　上式中の水酸化物イオン（ＯＨ－）と負極１０３とが反応することにより、水酸化マグネシウム（Ｍｇ（ＯＨ）2）が生成（析出）される。負極１０３にアルミニウム（Ａｌ）を用いた場合の反応も、マグネシウム（Ｍｇ）と同様に、水酸化アルミニウム（Ａｌ（ＯＨ）３）が析出される。
　これら式（１）～（２）の反応により、放電が可能であり、全反応は、次のように表すことができる。
　２ＦｅＯＯＨ＋Ｍｇ＋２Ｈ２Ｏ→２Ｆｅ（ＯＨ）２＋Ｍｇ（ＯＨ）２・・・（３）
　また、理論起電力は約１．７Ｖ（正極活物質にα―ＦｅＯＯＨ及び負極活物質にＭｇ使用時）と約１．６Ｖ（正極活物質にα―ＦｅＯＯＨ及び負極活物質にＡｌ使用時）となっている。
　本実施形態の一次電池は、正極活物質にオキシ水酸化鉄を使用し、負極活物質にマグネシウムまたはアルミニウムを使用し、電解質に水系電解液を用いることで、安価な材料で構成される、低環境負荷な電池として期待できる。
　正極１０１は、正極活物質及び導電助剤を構成要素に含むことができる。また、正極１０１には、前記材料を一体化するための結着剤を含むことが好ましい。
　負極１０３は、負極活物質及び導電助剤を構成要素に含むことができる。また、負極１０３には、前記材料を一体化するための結着剤を含むことが好ましい。
　以下に上記の各構成要素について説明する。
　（１）正極
　正極は、正極活物質を少なくとも含み、必要に応じて導電助剤、結着剤等の添加物を含むことができる。正極は、銅、鉄およびカーボンからなる群より選択される少なくとも１つを含むシート状集電体に形成されてもよい。
　（１－１）正極活物質
　本実施形態の正極活物質は、少なくともオキシ水酸化鉄（ＦｅＯＯＨ）を含む。オキシ水酸化鉄は、結晶形の異なるα相、β相、γ相、δ相の四相が存在するが、コスト及び生産性の観点から、α相が好ましい。
　また正極活物質の粒子径は、０．３μｍ～１０μｍが好ましく、０．５μｍ～５μｍがより好適である。
　これは、粒子径が小さいほど、反応するサイトが増加し、出力性能が向上する一方、充放電サイクルを繰り返すことで、正極活物資、導電助剤、集電体との電気的接触が損なわれ、サイクル性能が低下するためである。
　オキシ水酸化鉄は、ｐＨ制御した水溶液中で水酸化鉄（Ｆｅ（ＯＨ）２）を酸化する手法、塩化鉄（ＦｅＣｌ３）水溶液を加熱する手法、水酸化鉄（Ｆｅ（ＯＨ）２）分散液に過酸化水素（Ｈ２Ｏ２）を加える手法等、既存の手法で作製することができる。また、市販のオキシ水酸化鉄を使用することも可能である。
　（１－２）導電助剤
　本実施形態では、正極に導電助剤を含んでもよい。導電助剤には、例えばカーボンなどを用いることができる。具体的には、ケッチェンブラック、アセチレンブラックなどのカーボンブラック類、活性炭類、グラファイト類、カーボン繊維類などを挙げることができる。正極中で反応部位を十分確保するために、カーボンは粒子が小さいものが適している。具体的には、粒子径が１μｍ以下のものが望ましい。これらのカーボンは、例えば市販品として、又は公知の合成により入手することが可能である。
　正極活物質に直接カーボンをコーティングしても良い。コーティングする手法には、蒸着、スパッタリング、遊星ボールミルといった物理的手法、有機物をコーティングした後に熱処理するといった化学的手法、又は公知の手法によりコーティングが可能である。
　（１－３）結着剤
　正極は、結着剤を含んでもよい。結着剤は、特に限定されないが、ポリテトラフルオロエチレン（ＰＴＦＥ）、ポリフッ化ビニリデン（ＰＶＤＦ）、スチレンブタジエンゴム、エチレンプロピレンジエンゴム、天然ゴムなどを例として挙げることができる。環境負荷及び廃棄物処理の観点から、フッ素が使用されていないスチレンブタジエンゴム、エチレンプロピレンジエンゴム、天然ゴムがより好ましい。
　これらの結着剤は、粉末として又は分散液として用いることができる。
　本実施形態の正極における上記正極活物質、導電助剤及び結着剤の含有量は、正極全体の重量を基準として、正極活物質が０重量％より大きく９９％以下、好ましくは７０～９５重量％であり、導電助剤が０～９０重量％、好ましくは１～３０重量％であり、結着剤が０～５０重量％、好ましくは１～３０重量％である。
　（１－４）正極の調製
　正極は以下のように調製することができる。正極活物質であるオキシ水酸化鉄粉末、カーボン粉末、及び必要に応じて、スチレンブタジエンゴムのような分散液を混合し、この混合物を集電体に塗布し乾燥することにより、正極を形成することができる。
　集電体は、特に限定されないが、例えば、銅、鉄、チタン、ニッケルおよびカーボンからなる群より選択される少なくとも１つ（１つの元素）を用いたシート状またはメッシュ状の集電体を使用することができる。
　後述するバイポーラ型のスタック構造に電池を組み立てるためには、集電体は、シート状であることが好ましい。また、環境負荷及び廃棄の観点から、銅、鉄およびカーボンからなる群より選択される少なくとも１つを含むシート状集電体がより好ましい。このように正極は、銅、鉄およびカーボンからなる群より選択される少なくとも１つを含むシート状集電体に塗布されることが好ましい。
　電極の強度を高めるために、乾燥後の電極に冷間プレスまたはホットプレスを適用することによって、より安定性に優れた正極を作製することができる。
　以上のように、正極活物質であるオキシ水酸化鉄を含む正極を作製することで、充電反応及び放電反応に対して高活性な正極を得ることができる。更に、上記のような構成の一次電池の正極を作製することにより、正極活物質であるオキシ水酸化鉄のポテンシャルを十分引き出すことが可能である。
　（２）負極
　負極は、負極活物質を少なくとも含み、必要に応じて導電助剤、結着剤等の添加物を含むことができる。負極は、銅、鉄およびカーボンからなる群より選択される少なくとも１つを含むシート状集電体に形成されてもよい。
　（２－１）負極活物質
　本実施形態の負極活物質は、少なくともマグネシウム（Ｍｇ）またはアルミニウム（Ａｌ）を含む。
　負極活物質は、主成分としてマグネシウム（Ｍｇ）またはアルミニウム（Ａｌ）を含めばよく、他にも、亜鉛（Ｚｎ）、カルシウム（Ｃａ）、リチウム（Ｌｉ）、マンガン（Ｍｎ）、鉄（Ｆｅ）、錫（Ｓｎ）、カーボン（Ｃ）からなら群から選ばれる少なくとの１つの成分を含む合金であっても良い。
　負極活物質は、マグネシウム（Ｍｇ）箔またはアルミニウム（Ａｌ）箔を所定の形状に成形することで作製することが可能である。
　マグネシウム（Ｍｇ）またはアルミニウム（Ａｌ）を粉末で使用してもよい。ただし、粉末で使用すると、反応するサイトが増加し、出力性能が向上する一方、マグネシウム（Ｍｇ）またはアルミニウム（Ａｌ）の酸化及び電解液による腐食の進行が加速してしまう。このため、マグネシウム（Ｍｇ）またはアルミニウム（Ａｌ）は、箔状またはバルク状で使用することが好ましい。
　（２－２）導電助剤
　負極活物質を粉末で使用する場合、負極は導電助剤を含んでもよい。導電助剤には、例えばカーボンなどを用いることができる。具体的には、ケッチェンブラック、アセチレンブラックなどのカーボンブラック類、活性炭類、グラファイト類、カーボン繊維類などを挙げることができる。負極中で反応部位を十分確保するために、カーボンは粒子が小さいものが適している。具体的には、粒子径が１μｍ以下のものが望ましい。これらのカーボンは、例えば市販品として、または公知の合成により入手することが可能である。
　負極活物質に直接カーボンをコーティングしても良い。コーティングする手法には、蒸着、スパッタリング、遊星ボールミルといった物理的手法、有機物をコーティングした後に熱処理するといった化学的手法、または公知の手法によりコーティングが可能である。
　（２－３）結着剤
　負極活物質を粉末で使用する場合、負極は結着剤を含んでもよい。結着剤は、特に限定されないが、ポリテトラフルオロエチレン（ＰＴＦＥ）、ポリフッ化ビニリデン（ＰＶＤＦ）、スチレンブタジエンゴム、エチレンプロピレンジエンゴム、天然ゴムなどを例として挙げることができる。環境負荷及び廃棄物処理の観点から、フッ素が使用されていないスチレンブタジエンゴム、エチレンプロピレンジエンゴム、天然ゴムがより好ましい。これらの結着剤は、粉末として又は分散液として用いることができる。
　負極活物質を粉末で使用する場合、上記負極活物質、導電助剤及び結着剤の含有量は、負極全体の重量を基準として、負極活物質が０重量％より大きく９９％以下、好ましくは７０～９５重量％であり、導電助剤が０～９０重量％、好ましくは１～３０重量％であり、結着剤が０～５０重量％、好ましくは１～３０重量％である。
　（２－４）負極の調製
　負極は、以下のように調製することができる。マグネシウム（Ｍｇ）またはアルミニウム（Ａｌ）を所定の形状に加工し、この負極活物質を集電体に溶接等で張り付けることにより、負極を形成することができる。
　集電体は、特に限定されないが、例えば、銅、鉄、チタン、ニッケルおよびカーボンからなる群より選択される少なくとも１つ（１つの元素）を用いたシート状またはメッシュ状の集電体を使用することができる。
　後述するバイポーラ型のスタック構造に電池を組み立てるためには、集電体は、シート状であることが好ましい。また、環境負荷及び廃棄の観点から、銅、鉄およびカーボンからなる群より選択される少なくとも１つを含むシート状集電体がより好ましい。このように負極は、銅、鉄およびカーボンからなる群より選択される少なくとも１つを含むシート状集電体に形成されることが好ましい。
　また、負極活物質を粉末で使用する場合は以下のように調製することができる。負極活物質であるマグネシウム（Ｍｇ）粉末またはアルミニウム（Ａｌ）粉末、カーボン粉末、及び必要に応じて、スチレンブタジエンゴムのような分散液を混合し、この混合物を集電体に塗布し乾燥することにより、負極を形成することができる。
　電極の強度を高めるために、乾燥後の電極を冷間プレスやホットプレスを適用することによって、より安定性に優れた負極を作製することができる。
　以上のように、負極活物質であるマグネシウム（Ｍｇ）またはアルミニウム（Ａｌ）を含む負極を作製することで、高活性な負極を得ることができる。更に、上記のような構成の一次電池の負極を作製することにより、負極活物質であるマグネシウム（Ｍｇ）またはアルミニウム（Ａｌ）のポテンシャルを十分引き出すことが可能である。
　（３）水系電解液（電解質）
　本実施形態の一次電池は、水系電解液を含む。この水系電解液は、正極及び負極で水酸化物イオン（ＯＨ－）の移動が可能な電解質を含む水溶液である。水系電解液は、主溶媒として水を用い、水以外の溶媒を含んでもよい。水系電解液には、例えば、酢酸塩、炭酸塩、リン酸塩、ピロリン酸塩、メタリン酸塩、クエン酸塩、ホウ酸塩、アンモニウム塩、ギ酸塩、炭酸水素塩、水酸化物、塩化物からなら群より選ばれる少なくとも１つの電解質を水に溶解させた水溶液を用いることができる。
　本実施形態では、電解質に水系電解液を用いるが、ゲル状、固体状などの固体電解質を用いてもよい。すなわち、電解質は、液状、クリーム状、ゲル状、固体状などのいずれの形態であってもよい。また、電解質は、水系でも非水系でもよい。
　水系電解液に、酸性水溶液またはアルカリ水溶液を使用する場合は、電解液のｐＨは、５．８以上８．６以下であることが好ましい。通常、電解液は、強アルカリであるほど性能が向上するが、国の法律である水質汚濁防止法では、海域以外の公共用水域に排出される排液のｐＨ（水素イオン濃度）の許容限度は、５．８以上８．６以下と定められている。このため、環境負荷及び廃棄処理の観点から、性能を犠牲にしてでも、水系電解液のｐＨ（水素イオン濃度）は、５．８以上８．６以下が好ましい。
　（４）他の要素
　本実施形態の一次電池は、上記構成要素に加え、セパレータ、電池ケースなどの構造部材、その他一次電池に要求される要素を含むことができる。これらは、従来公知のものが使用できるが、環境負荷及び廃棄処理の観点から、有害物質、レアメタル、レアアース等を含まないことが好ましい。更に、これらの他の要素は、生物由来、生分解性材料であることがより好適である。
　（５）一次電池の製造方法
　本実施形態の一次電池は、上述した通り、少なくとも正極、負極及び水系電解液を含み、図１に例示されるように、正極と負極との間に、正極および負極に接するように水系電解液が配置される。このような構成の一次電池は、従来型の一次電池と同様に調製することができる。
　例えば、一次電池は、上述したようなオキシ水酸化鉄を含む正極活物質、導電助剤および結着剤を含む正極と、マグネシウム（Ｍｇ）またはアルミニウム（Ａｌ）を含む負極と、正極と負極とに接すように配置された水系電解液とを、従来技術に従って各要素を組み立てればよい。
　（５－１）コイン型一次電池の製造方法
　一次電池の製造方法の一実施形態として、例えばコイン型一次電池を製造することができる。
　図２は、コイン型一次電池の構造を示す概略断面図である。具体的には、まず、上記正極１０１を設置した正極ケース２０１に、図示しないセパレータを載置し、載置したセパレータに電解液１０２を注入する。次に、電解液１０２の上に負極１０３を設置し、負極ケース２０２を正極ケース２０１に被せる。次に、コインセルカシメ機で正極ケース２０１及び負極ケース２０２の周縁部をかしめることにより、プロピレンガスケット２０３を含むコイン型一次電池を作製することが可能である。
　図示するコイン型一次電池は、正極活物質としてオキシ水酸化鉄粉末を利用する。そのため、正極活物質に空気中の酸素を用いる空気電池とは異なり、本実施形態の正極ケース２０１には空気取り込み口を設ける必要がない。すなわち、本実施形態では、密閉型の電池を作製することができる。したがって、本実施形態の一次電池は、空気取り込み口から電解液が揮発することなく、長期保存することができる。
　（５－２）バイポーラ型のスタック構造一次電池の製造方法
　一次電池の製造方法の一実施形態として、例えばバイポーラ型のスタック構造を有する一次電池を製造することができる。
　図３Ａは、バイポーラ型のスタック一次電池の構成例を示す構成図である。図３Ｂは、バイポーラ型のスタック一次電池の構成例を示す平面図である。
　本実施形態の一次電池は、使用する電解液のｐＨを５．８以上８．６以下とした場合、出力性能に期待が出来ない。このため、スタック構造の一次電池とすることで、出力を上げることが好ましい。
　具体的には、まず、銅箔等の集電体３２２の両面にそれぞれ、上記正極１０１と上記負極１０３とを接合し、１枚の集電体３２２に正極１０１及び負極１０３をそれぞれ形成する。これにより、正極及１０１および負極１０３がそれぞれ集電体３２２の片面に形成されたバイポーラ電極３２０を作製する。
　また、最外層用の各集電体３０３Ａ、３０３Ｂは、片面のみの電極形成でよく、電気を取り出すためのタブ３１３Ａ、３１３Ｂがあることが好ましい。図示する最外層の集電体３０３Ａには、片面のみに正極１０１が形成され、タブ３１３Ａが形成されている。最外層の集電体３０３Ｂには、片面のみに負極１０３が形成され、タブ３１３Ｂが形成されている。
　タブ３１３Ａ、３１３Ｂは、集電体３０３Ａ、３０３Ｂに突起を有する形状で加工しても良く、集電体３０３Ａ、３０３Ｂに別の金属タブを超音波溶接、スポット溶接等により接合しても良い。
　正極１０１および負極１０３を形成した集電体３２２を、正極１０１及び負極１０３が向かい合うように重ね、正極１０１と負極１０３に接するようにセパレータ３０１を挿入する。正極１０１または負極１０３を形成した最外層用の各集電体３０３Ａ、３０３Ｂについても、同様に、正極１０１及び負極１０３が向かい合うように重ね、正極１０１と負極１０３に接するようにセパレータ３０１を挿入する。
　集電体３０３Ａ、３０３Ｂ、３２２およびセパレータ３０１を積層したら、集電体の各銅箔同士の周縁部を熱融着シート３０２を使用して、熱プレスすることでシールする。ただし、周縁部は後述する水系電解液を注入するために１辺（一部）は熱プレスを実施せずに開けておく必要がある。
　作製したスタックをアルミラミネートフィルム３０４等で挟み、水系電解液を各セル（各部屋）に注液後、スタックの封止していない一辺とアルミラミネートフィルムの周縁部を真空シールすることで、バイポーラ型のスタック構造一次電池を作製が可能である。
　このような一次電池は、正極活物質に空気中の酸素を用いる空気電池とは異なり、空気取り込み口が不要な、密閉型の電池である。したがって、本実施形態の一次電池は、空気取り込み口から電解液が揮発することなく、長期保存することができる。
　［実施例］
　以下に本実施形態に係る一次電池の実施例を詳細に説明する。各実施例では、負極にマグネシウム（Ｍｇ）を用いた一次電池と、負極にアルミニウム（Ａｌ）を用いた一次電池とを、それぞれ作製した。なお、本発明は下記の実施例に示したものに限定されるものではなく、その要旨を変更しない範囲において適宜変更して実施できるものである。
　＜実施例１＞
　実施例１では、前述したコイン型の一次電池（図２）を以下の手順で作製した。また、負極活物資として、マグネシウム（Ｍｇ）箔及びアルミニウム（Ａｌ）箔をそれぞれ使用した。水系電解液には、アルカリ電解液（ｐＨが約９）として１．０×１０－４ｍｏｌ／Ｌの水酸化カリウム水溶液（ＫＯＨ）を使用した。
　（正極の調製）
　オキシ水酸化鉄粉末（粒径１μｍ、高純度化学研究所）、ケッチェンブラック粉末（ＥＣ６００ＪＤ、ライオン・スペシャリティ・ケミカルズ社）、ポリテトラフルオロエチレン（ＰＴＦＥ）粉末を、８０：１０：１０の重量比でらいかい機を用いて十分に粉砕混合し、ロール成形して、シート状電極（厚さ：０．５ｍｍ）を作製した。このシート状電極を直径１６ｍｍの円形に切り抜き、銅メッシュ上にプレスすることにより、正極を得た。
　（負極の調製）
　マグネシウム（Ｍｇ）箔（厚さ１５０μｍ、ニラコ社）、及びアルミニウム（Ａｌ）箔（厚さ１５０μｍ、ニラコ社）をそれぞれ直径１６ｍｍの円形に切り抜き、負極を得た。
　（一次電池の調製）
　コイン電池用ケース（宝泉社）を使用して、図２に示すコイン型一次電池を作製した。　　　
　上記の方法で調整した正極１０１を設置した正極ケース２０１に直径１８ｍｍに切り抜いたセルロース系セパレータ（ニッポン高度紙工業社）を載置し、載置したセパレータに１．０×１０－４ｍｏｌ／Ｌの水酸化カリウム水溶液（ＫＯＨ）を水系電解液１０２として注入する。水系電解液１０２の上に上記負極１０３を設置し、負極ケース２０２を正極ケース２０１に被せ、コインセルカシメ機で正極ケース２０１及び負極ケース２０２の周縁部をかしめることにより、プロピレンガスケット２０３を含むコイン型一次電池を得た。
　（電池性能）
　以上の手順で調整した一次電池の電池性能を測定した。電池のサイクル試験は、充放電測定システム（Ｂｉｏ　Ｌｏｇｉｃ社製）を用いて、正極の有効面積当たりの電流密度で１ｍＡ／ｃｍ２を通電し、開回路電圧から電池電圧が、０．６０Ｖに低下するまで放電電圧の測定を行った。電池の放電試験は、通常の生活環境下で行った。放電容量は正極活物質（オキシ水酸化鉄）単位重量当たりの値（ｍＡｈ／ｇ）で表した。
　図４に、負極にマグネシウム（Ｍｇ）を用いた放電曲線を示す。図４より、オキシ水酸化鉄を正極活物質に用いたときの平均放電電圧は１．０８Ｖ、放電容量は２５４ｍＡｈ／ｇであることが分かる。ここで、平均放電電圧は、全放電容量の１／２の放電容量（ここでは、１２７ｍＡｈ／ｇ）の時の放電電圧と定義する。
　以下の表１に、負極にマグネシウム（Ｍｇ）およびアルミニウム（Ａｌ）をそれぞれ用いた一次電池の放電電圧及び放電容量を示す。このように、実施例１の各一次電池は、優れた電池性能を有していることが分かった。
Figure JPOXMLDOC01-appb-T000001
 　
　＜実施例２＞
　実施例２では、前述したコイン型の一次電池を以下の手順で作製した。また、正極は銅のシート状集電体に塗布して調製し、負極は銅のシート状集電体に溶接して調製した。水系電解液にはアルカリ電解液（ｐＨが約９）として１．０×１０－４ｍｏｌ／Ｌの水酸化カリウム水溶液（ＫＯＨ）を使用した。電池の作製及び評価法は、実施例１と同様にして行った。
　（正極の調製）
　オキシ水酸化鉄粉末（粒径１μｍ、高純度化学研究所）、ケッチェンブラック粉末（ＥＣ６００ＪＤ、ライオン・スペシャリティ・ケミカルズ社）、スチレンブタジエンゴム（ＡＡポータブルパワー社）が、重量比で８０：１０：１０になるように、混錬機（シンキー社）を使用して十分に混合し、スラリーを作製した。このスラリーを銅箔（ニラコ社）に塗布し、１００℃の真空乾燥機で１２時間乾燥させた。その後、１２０℃でプレスし、このシート状電極を直径１６ｍｍの円形に切り抜き、正極を得た。
　（負極の調製）
　マグネシウム（Ｍｇ）箔（厚さ１５０μｍ、ニラコ社）、及び、アルミニウム（Ａｌ）箔（厚さ１５０μｍ、ニラコ社）を、それぞれ直径１６ｍｍの円形に切り抜き、これらをそれぞれ銅箔（ニラコ社）に超音波溶接機を使用して接合させた。
　（電池性能）
　実施例２の一次電池の放電容量及び放電電圧を、表１に示す。表１に示すように、負極にマグネシウム（Ｍｇ）を用いた電池における実施例２の放電容量は、２７０ｍＡｈ／ｇを示し、実施例１よりも大きい値であった。負極にアルミニウム（Ａｌ）を用いた電池においても、実施例２の放電容量は実施例１よりも大きい値であった。
　また、表１に示すように、実施例２の放電電圧は、実施例１の放電電圧よりも大きい。すなわち、実施例２では、実施例１よりも過電圧の減少が見られ、放電のエネルギー効率の改善を達成することができた。
　これらの特性の向上は、銅のシート状集電体に正極及び負極をそれぞれ接合して形成したため、電池の内部抵抗が減少し、電池反応がスムーズに行われたことによると考えられる。
　＜実施例３＞
　実施例３では、前述したコイン型の一次電池を以下の手順で作製した。水系電解液には、ｐＨ（水素イオン濃度）が５．８の塩化アンモニウム水溶液（ＮＨ４Ｃｌ）を使用した。ｐＨ５．８は、水質汚濁防止法で規定された、海域以外の公共用水域へ排出可能な排液の許容限度である。
　水系電解液以外の正極及び負極の調整、電池の作製及び評価法は、実施例２と同様とした。
　（電池性能）
　実施例３の一次電池の放電容量及び放電電圧を表１に示す。表１に示すように、負極にマグネシウム（Ｍｇ）を用いた電池における実施例３の放電容量は、２５１ｍＡｈ／ｇを示し、実施例１と同等であった。負極にアルミニウム（Ａｌ）を用いた電池においても、実施例３の放電容量は実施例１と同等であった。
　また、表１に示すように、放電電圧についても、実施例１と同等であり、低環境負荷で、安全性が高い水系電解液を使用しても、十分な放電のエネルギー効率を達成することができた。
　これは、本実施形態の一次電池の反応効率が高く、中性に近い水系電解液を使用しても電池反応がスムーズに行われたことによると考えられる。
　＜実施例４＞
　実施例４では、前述したバイポーラ型の３スタック構造の一次電池を、以下の手順で作製した。
　図３Ａは、バイポーラ型の３スタック構造の一次電池の分解図である。水系電解液には、実施例３と同様に、ｐＨ（水素イオン濃度）が５．８の塩化アンモニウム水溶液（ＮＨ４Ｃｌ）を使用した。
　電池の評価法は、実施例３と同様に行った。但し、充放電試験の測定は、放電電圧が１．００Ｖまで低下するまで行った。
　（正極及び負極の調製）
　負極１０３として、マグネシウム（Ｍｇ）箔（厚さ１５０μｍ、ニラコ社）及びアルミニウム（Ａｌ）箔（厚さ１５０μｍ、ニラコ社）をそれぞれ２ｃｍ×２ｃｍに切り抜き、これらを、銅箔（ニラコ社）に超音波溶接機を使用して接合させた。
　次に、正極１０１として、オキシ水酸化鉄粉末（粒径１μｍ、高純度化学研究所）、ケッチェンブラック粉末（ＥＣ６００ＪＤ、ライオン・スペシャリティ・ケミカルズ社）、スチレンブタジエンゴム（ＡＡポータブルパワー社）が重量比で８０：１０：１０になるように、混錬機（シンキー社）を使用して十分に混合し、スラリーを作製した。このスラリー、を先ほどの負極を接合させた銅箔の裏面に２ｃｍ×２ｃｍで塗布し、１００℃の真空乾燥機で１２時間乾燥させた。その後、１２０℃でプレスし、正極及１０１および負極１０３がそれぞれ片面ずつ接合されたバイポーラ電極３２０を得た。
　但し、最外層の正極用電極１０１および負極用電極１０３は、前述の銅箔（集電体３０３Ａ、３０３Ｂ）の片面のみ前述の正極１０１または負極１０３をそれぞれ接合した。調整方法は上記と同様である。この最外層の銅箔（集電体集電体３０３Ａ、３０３Ｂ）には、タブ３１３Ａ、３１３Ｂを有する形状で切り抜いたものを使用した。
　（一次電池の調製）
　アルミラミネートフィルム３０４を使用して、図３に示すバイポーラ型の３スタック構造の一次電池を作製した。
　上記の方法で調整したバイポーラ電極３２０を２枚、正極１０１及び負極１０３が向かい合うように重ね、バイポーラ電極３２０同士の間に２．２ｃｍ×２．２ｃｍに切り抜いたセパレータ３０１と、中心部を切り抜いたフレーム形状の熱融着シート３０２とを挿入する。積層したら、各集電体３２２同士の周縁部３辺を１８０℃で熱プレスすることでシールする。
　最外層も上記と同様に、正極１０１及び負極１０３が向かい合うように最外層の負極１０３、正極１０１、セパレータ３０１、熱融着シート３０２も重ね、上記でシールした辺と同一の３辺を熱プレスすることでシールする。
　このようにして作製したスタックを、アルミラミネートフィルム３０４と熱融着シート３０２とで挟み、上記でシールした辺と同一の３辺を熱プレスすることでアルミラミネートフィルムを袋状にする。
　その後、ｐＨが５．８の塩化アンモニウム水溶液（ＮＨ４Ｃｌ）をスタック構造の各セル（部屋）に注入し、セパレータ３０１を十分に浸漬させた後、アルミラミネートフィルム３０４の封止していない一辺を真空シールし、最後に、スタックの封止していない一辺をアルミラミネートフィルム３０４の上から封止することで、バイポーラ型のスタック一次電池を得た。
　なお、実施例４では、３スタックであるが、３スタック以上のバイポーラ型のスタック一次電池の作製も可能で、その場合は、積層するバイポーラ電極３２０の積層数を増やせば良い。
　（電池性能）
　本実施例の一次電池の放電容量及び放電電圧を表１に示す。表１に示すように、負極にマグネシウム（Ｍｇ）を用いた電池における実施例４の放電容量は、２７２ｍＡｈ／ｇを示し、実施例２と同等であった。負極にアルミニウム（Ａｌ）を用いた電池においても、実施例３の放電容量は実施例２と同等であった。
　また、表１に示すように放電電圧についても、実施例１の３倍程度であり、バイポーラ型のスタック構造一次電池にすることで、従来のリチウムイオン電池と同等の電圧を達成することができる。
　以上の結果より、本実施形態の一次電池は、正極活物質としてオキシ水酸化鉄を用い、負極活物質としてマグネシウムまたはアルミニウムを用いることにより、低環境負荷で、廃棄処理を簡便化することができる。
　また、本実施形態の一次電池は、空気電池とは異なり空気取り込み口が不要な、密閉型の電池である。そのため、本実施形態の一次電池は、空気取り込み口から電解液が揮発することなく、長期保存することができる。
　電解質に水系電解液を用いることが好ましい。有機系電解液を用いた場合、燃えやすいため火災、爆発などの原因になる恐れがあり、また、漏洩時に人体や環境に対する悪影響が懸念される。これに対し、本実施形態では、水系電解液を用いることで、安全性が高く、安価な電池を作製することができる。
　水系電解液のｐＨは、５．８以上８．６以下であることが好ましい。これにより、環境に配慮した、廃棄処理が容易な電池を作製することができる。
　したがって、本実施形態の一次電池は、小型デバイス、センサ、モバイル機器などの様々な電子機器の新しい駆動源として有効利用することができる。
　なお、本発明は上記実施形態に限定されるものではなく、本発明の技術的思想内で、様々な変形および組み合わせが可能である。
　１０１：正極
　１０２：水系電解液（電解質）
　１０３：負極
　２０１：正極ケース
　２０２：負極ケース
　２０３：プロピレンガスケット
　３０１：セパレータ
　３０２：熱融着シート
　３０３Ａ、３０３Ｂ：最外層集電体
　３０４：アルミラミネートフィルム
　３２０：バイポーラ電極
　３２２：集電体

Claims (4)

  1. 　オキシ水酸化鉄を含む正極と、
    　マグネシウムまたはアルミニウムを含む負極と、
    　前記正極と前記負極との間に配置された電解質と、を備える
    　一次電池。
  2. 　前記電解質は水系電解液であって、前記水系電解液のｐＨは、５．８以上８．６以下である
    　請求項１に記載の一次電池。
  3. 　前記正極及び前記負極は、銅、鉄およびカーボンからなる群より選択される少なくとも１つを含むシート状集電体に形成される
    　請求項１または２に記載の一次電池。
  4. 　バイポーラ型のスタック構造を有する
    　請求項１から３のいずれか１項に記載の一次電池。
PCT/JP2020/043449 2020-11-20 2020-11-20 一次電池 WO2022107325A1 (ja)