WO2022009759A1 - 二成分型室温速硬化性オルガノポリシロキサン組成物、該組成物の硬化物及び物品 - Google Patents
二成分型室温速硬化性オルガノポリシロキサン組成物、該組成物の硬化物及び物品 Download PDFInfo
- Publication number
- WO2022009759A1 WO2022009759A1 PCT/JP2021/024888 JP2021024888W WO2022009759A1 WO 2022009759 A1 WO2022009759 A1 WO 2022009759A1 JP 2021024888 W JP2021024888 W JP 2021024888W WO 2022009759 A1 WO2022009759 A1 WO 2022009759A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- agent
- carbon atoms
- component
- room temperature
- Prior art date
Abstract
二成分型の脱アルコールタイプの室温硬化性オルガノポリシロキサン組成物であって、硬化剤として下記式（３）で示される加水分解性オルガノシラン化合物及び／又はその部分加水分解縮合物を含む第一剤と、硬化触媒を含む第二剤とからなる二成分型室温速硬化性オルガノポリシロキサン組成物が、とりわけ速硬化性、深部硬化性に優れ、同時に保存安定性、耐久性も良好な硬化物を与える。（Ｒ6は炭素数１～２０の非置換又は置換の１価炭化水素基、Ｒ7は炭素数１～２０の非置換若しくは置換のアルキル基、又は炭素数３～２０の非置換若しくは置換のシクロアルキル基、ａは１～３。）
Description
本発明は、二成分型室温速硬化性オルガノポリシロキサン組成物、特には１分子中に２個の加水分解性シリル基と、該２個の加水分解性シリル基中にそれぞれ１個ずつ存在するケイ素原子に炭素－炭素二重結合が連結した構造の基、即ち、アルコキシシリル－ビニレン基（アルコキシシリル－エテニレン基）を１分子中に２個（同一のケイ素原子上に）有するビスシリル型の加水分解性オルガノシラン化合物及び／又はその部分加水分解縮合物（加水分解性オルガノシロキサンオリゴマー）を、硬化剤（架橋剤）として含む二成分型室温硬化性オルガノポリシロキサン組成物、該組成物を有する各種物品、及び該二成分型室温硬化性オルガノポリシロキサン組成物を硬化して得られるエラストマーの成形物（シリコーンゴム硬化物）等に関するものである。
従来、空気中の水分（湿気）と接触することによって加水分解・縮合反応により架橋し、室温（２３℃±１５℃）で硬化してエラストマー硬化物（シリコーンゴム硬化物）になる室温硬化性オルガノポリシロキサン組成物は、種々のタイプのものが公知である。とりわけ架橋時の縮合反応によりアルコールを放出して硬化する脱アルコールタイプのものは不快臭がない、金属類を腐食しないという特徴により、電気・電子機器等のシーリング用、接着用、コーティング用に好んで使用されている。
かかる組成物の代表例としては、シラノール基末端封鎖直鎖状オルガノポリシロキサンとアルコキシシランと有機チタン化合物からなる組成物、アルコキシシリル基末端封鎖直鎖状オルガノポリシロキサンとアルコキシシランとアルコキシチタンからなる組成物、シルエチレン基を含むアルコキシシリル基で末端が封鎖された直鎖状オルガノポリシロキサンとアルコキシシランとアルコキシチタンからなる組成物、更に、シラノール基末端封鎖直鎖状オルガノポリシロキサン又はアルコキシ基末端封鎖直鎖状オルガノポリシロキサンとアルコキシ－α－シリルエステル化合物からなる組成物などが挙げられる（特許文献１～４：特公昭３９－２７６４３号公報、特開昭５５－４３１１９号公報、特公平７－３９５４７号公報、特開平７－３３１０７６号公報）。
これらの組成物は、ある程度の保存安定性、耐水性、耐湿性が得られているが、これらの物性を完全に満足するには至っていない。更に、速硬化性に関しても、まだ不十分であった。
上述した通り、加水分解性（反応性）アルコキシシリル基を末端に有する直鎖状オルガノシロキサンポリマーは、従来公知である。この直鎖状オルガノシロキサンポリマーを主成分とする組成物は、予め、ポリマーの末端基がアルコキシシリル基で封鎖されているため、経時的に硬化性が低下し難く、保存安定性に優れている。また、作業性（粘度、チキソ性等）を任意に調整可能である。更にポリマーが空気中の水分と反応し、架橋することで、エラストマー（オルガノポリシロキサン組成物の硬化物）を形成する。このエラストマーは、優れた特性（硬度、引張り強さ、切断時伸び）も有している。
しかしながら、脱アルコールタイプの室温硬化性オルガノポリシロキサン組成物は、従来公知の他の硬化タイプである脱オキシムタイプ、脱酢酸タイプ、脱アセトンタイプの室温硬化性オルガノポリシロキサン組成物等と比較すると、空気中の水分との反応性が低いため、硬化性が不十分であった。
一方で、脱アルコールタイプの室温硬化性オルガノポリシロキサン組成物の中でも、二成分型の脱アルコールタイプの室温硬化性オルガノポリシロキサン組成物は、１成分系の脱アルコールタイプの室温硬化性オルガノポリシロキサン組成物に比べ、硬化性に優れるが、深部での硬化性が遅く、短時間での十分な硬化は得られていなかった。
本発明者らは、速硬化性に優れ、かつ耐湿性（耐湿条件下での保存後の硬化性）に優れた硬化物を与えることが可能な室温硬化性オルガノポリシロキサン組成物の開発を目的として、アルコキシシリル－ビニレン基（アルコキシシリル－エテニレン基）を分子鎖末端に有する直鎖状オルガノポリシロキサンポリマー並びにそのポリマーを主成分とする室温硬化性オルガノポリシロキサン組成物を提案している（特許文献５、６：特許第５９６０８４３号公報、特許第５９９７７７８号公報）。これらの組成物は、特性上は、申し分ない。しかし、各種分子量、置換基構造を有するポリマーを新たに合成する必要があるため、工業的に有利に製造できるものではない。そのため、アルコキシシリル－ビニレン基（アルコキシシリル－エテニレン基）の末端構造を有したケイ素化合物及びこのケイ素化合物からなる１成分系のオルガノポリシロキサン組成物を提案した（特許文献７：国際公開第２０１５／１９４３４０号）。しかしながら、さらなる速硬化性の向上が生産効率の向上につながると期待されるため、例えば二成分型での速硬化性を向上させた二成分型室温硬化性オルガノポリシロキサン組成物が望まれる。
本発明は、上記事情に鑑みなされたもので、脱アルコールタイプの室温硬化性オルガノポリシロキサン組成物であって、二成分型で速硬化性、深部硬化性に優れる二成分型室温速硬化性オルガノポリシロキサン組成物、該組成物を有する各種物品、及び該室温速硬化性オルガノポリシロキサン組成物を硬化して得られるエラストマーの成形物（シリコーンゴム硬化物）等を提供することを目的とする。
上述したような従来の脱アルコールタイプの室温硬化性オルガノポリシロキサン組成物の硬化性が不十分であるという問題に関して、本発明者らは、アルコキシシリル基の連結基がビニレン基（エテニレン基）である構造を有する化合物が、該アルコキシシリル基中のアルコキシ基の加水分解性が顕著に優れることを見出した。加えて、この知見に基づき、本発明者らは、後述する式（３）で示される１分子中に２個の加水分解性シリル基を有するオルガノシラン化合物であって、該２個の加水分解性シリル基中にそれぞれ１個ずつ存在するケイ素原子に炭素－炭素二重結合が連結した構造の基、即ちアルコキシシリル－ビニレン基（アルコキシシリル－エテニレン基）を１分子中の同一のケイ素原子上に２個有するビスシリル型の加水分解性オルガノシラン化合物及び／又はその部分加水分解縮合物（加水分解性オルガノシロキサンオリゴマー）を架橋剤（硬化剤）として使用することにより、とりわけ速硬化性に優れ、同時に保存安定性、耐久性も良好な硬化物を与える脱アルコールタイプの室温硬化性オルガノポリシロキサン組成物が得られることを見出した。
そして、従来１成分系の脱アルコールタイプの室温硬化性オルガノポリシロキサン組成物に比べ、二成分型の脱アルコールタイプの室温硬化性オルガノポリシロキサン組成物の方が硬化性に優れるが、深部での硬化性が遅く短時間での十分な硬化が得られなかった問題に関して、本発明者らは、更なる検討を行った結果、反応性の後述する式（３）で示される加水分解性オルガノシラン化合物及び／又はその部分加水分解縮合物を第一剤に、硬化触媒を第二剤に、それぞれ別々に配合した二成分型の材料とすることで、後述する式（３）で示される加水分解性オルガノシラン化合物及び／又はその部分加水分解縮合物を含む第一剤と、硬化触媒を含む第二剤を混合することによって、更なる速硬化性、深部硬化性を与える二成分型室温速硬化性オルガノポリシロキサン組成物が得られることを見出し、本発明をなすに至った。
即ち、本発明は、下記の二成分型室温速硬化性オルガノポリシロキサン組成物、該二成分型室温速硬化性オルガノポリシロキサン組成物を含有するシール剤、コーティング剤又は接着剤、及び該二成分型室温硬化性オルガノポリシロキサン組成物のエラストマー状硬化物（シリコーンゴム硬化物）からなる成形物等を提供するものである。
［１］
（Ａ）下記一般式（１）又は（２）で示されるオルガノポリシロキサン：１００質量部、
（一般式（１）中、Ｒ1は独立に炭素数１～２０の非置換又は置換の１価炭化水素基であり、ｎは１０以上の整数である。）
（一般式（２）中、Ｒ2は独立に炭素数１～２０の非置換又は置換の１価炭化水素基であり、Ｒ3は酸素原子又は炭素数１～４のアルキレン基であり、Ｒ4は独立に炭素数１～２０の脂肪族不飽和結合を含有しない非置換又は置換の１価炭化水素基であり、Ｒ5は独立に炭素数１～４の、アルキル基、アルコキシアルキル基、アルケニル基又はアシル基であり、ｘは０～２の整数であり、ｍは１０以上の整数である。）
（Ｂ）下記一般式（３）で示される加水分解性オルガノシラン化合物及び／又はその部分加水分解縮合物：第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して０．１～３０質量部
（一般式（３）中、Ｒ6は独立に炭素数１～２０の非置換又は置換の１価炭化水素基であり、Ｒ7は独立に炭素数１～２０の非置換若しくは置換のアルキル基、又は炭素数３～２０の非置換若しくは置換のシクロアルキル基であり、ａはケイ素原子毎に独立に１～３の整数である。）
を含有してなる第一剤と、
（Ａ）下記一般式（１）又は（２）で示されるオルガノポリシロキサン：１０～１００質量部、
（一般式（１）中、Ｒ1は独立に炭素数１～２０の非置換又は置換の１価炭化水素基であり、ｎは１０以上の整数である。）
（一般式（２）中、Ｒ2は独立に炭素数１～２０の非置換又は置換の１価炭化水素基であり、Ｒ3は酸素原子又は炭素数１～４のアルキレン基であり、Ｒ4は独立に炭素数１～２０の脂肪族不飽和結合を含有しない非置換又は置換の１価炭化水素基であり、Ｒ5は独立に炭素数１～４の、アルキル基、アルコキシアルキル基、アルケニル基又はアシル基であり、ｘは０～２の整数であり、ｍは１０以上の整数である。）
（Ｃ）硬化触媒：第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して０．００１～１０質量部
を含有してなる第二剤と
からなるものである二成分型室温速硬化性オルガノポリシロキサン組成物。
［２］
更に、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して（Ｄ）充填剤を、第一剤及び第二剤中にそれぞれ０～１，０００質量部含有する（ただし、少なくとも第一剤、第二剤のいずれか一方に０．１質量部以上含有する）ものである［１］に記載の二成分型室温速硬化性オルガノポリシロキサン組成物。
［３］
更に、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して（Ｅ）接着促進剤を、第一剤及び第二剤中にそれぞれ０～３０質量部含有する（ただし、少なくとも第一剤、第二剤のいずれか一方に０．００１質量部以上含有する）ものである［１］又は［２］に記載の二成分型室温速硬化性オルガノポリシロキサン組成物。
［４］
更に、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して（Ｆ）下記一般式（４）で示されるオルガノポリシロキサンを、第一剤及び第二剤中にそれぞれ０～１００質量部含有する（ただし、少なくとも第一剤、第二剤のいずれか一方が０．０１質量部以上含有する）ものである［１］～［３］のいずれかに記載の二成分型室温速硬化性オルガノポリシロキサン組成物。
（一般式（４）中、Ｒ8は独立に炭素数１～２０の脂肪族不飽和結合を含有しない非置換又は置換の１価炭化水素基であり、ｐは１～２，０００の整数である。）
［５］
第一剤と第二剤との割合が質量比で１：１～１０：１である［１］～［４］のいずれかに記載の二成分型室温速硬化性オルガノポリシロキサン組成物。
［６］
［１］～［５］のいずれかに記載の二成分型室温速硬化性オルガノポリシロキサン組成物を含有するシール剤。
［７］
［１］～［５］のいずれかに記載の二成分型室温速硬化性オルガノポリシロキサン組成物を含有するコーティング剤。
［８］
［１］～［５］のいずれかに記載の二成分型室温速硬化性オルガノポリシロキサン組成物を含有する接着剤。
［９］
［１］～［５］のいずれかに記載の二成分型室温速硬化性オルガノポリシロキサン組成物の硬化物。
［１０］
［９］に記載の二成分型室温速硬化性オルガノポリシロキサン組成物の硬化物からなる成形物。
［１］
（Ａ）下記一般式（１）又は（２）で示されるオルガノポリシロキサン：１００質量部、
（Ｂ）下記一般式（３）で示される加水分解性オルガノシラン化合物及び／又はその部分加水分解縮合物：第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して０．１～３０質量部
を含有してなる第一剤と、
（Ａ）下記一般式（１）又は（２）で示されるオルガノポリシロキサン：１０～１００質量部、
（Ｃ）硬化触媒：第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して０．００１～１０質量部
を含有してなる第二剤と
からなるものである二成分型室温速硬化性オルガノポリシロキサン組成物。
［２］
更に、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して（Ｄ）充填剤を、第一剤及び第二剤中にそれぞれ０～１，０００質量部含有する（ただし、少なくとも第一剤、第二剤のいずれか一方に０．１質量部以上含有する）ものである［１］に記載の二成分型室温速硬化性オルガノポリシロキサン組成物。
［３］
更に、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して（Ｅ）接着促進剤を、第一剤及び第二剤中にそれぞれ０～３０質量部含有する（ただし、少なくとも第一剤、第二剤のいずれか一方に０．００１質量部以上含有する）ものである［１］又は［２］に記載の二成分型室温速硬化性オルガノポリシロキサン組成物。
［４］
更に、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して（Ｆ）下記一般式（４）で示されるオルガノポリシロキサンを、第一剤及び第二剤中にそれぞれ０～１００質量部含有する（ただし、少なくとも第一剤、第二剤のいずれか一方が０．０１質量部以上含有する）ものである［１］～［３］のいずれかに記載の二成分型室温速硬化性オルガノポリシロキサン組成物。
［５］
第一剤と第二剤との割合が質量比で１：１～１０：１である［１］～［４］のいずれかに記載の二成分型室温速硬化性オルガノポリシロキサン組成物。
［６］
［１］～［５］のいずれかに記載の二成分型室温速硬化性オルガノポリシロキサン組成物を含有するシール剤。
［７］
［１］～［５］のいずれかに記載の二成分型室温速硬化性オルガノポリシロキサン組成物を含有するコーティング剤。
［８］
［１］～［５］のいずれかに記載の二成分型室温速硬化性オルガノポリシロキサン組成物を含有する接着剤。
［９］
［１］～［５］のいずれかに記載の二成分型室温速硬化性オルガノポリシロキサン組成物の硬化物。
［１０］
［９］に記載の二成分型室温速硬化性オルガノポリシロキサン組成物の硬化物からなる成形物。
本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、第一剤と第二剤の二成分型からなる。これにより、第一剤と第二剤を混合した際に、速硬化性、深部硬化性に優れる。
本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、特に、室温における空気中での速硬化性に優れ、作業性も良好である。更に保存安定性を備える。そのため本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、長期間、例えば６か月間の貯蔵後でも、第一剤と第二剤とを混合し、空気中に曝すと速やかに硬化して、優れた物性を示す。従って、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、耐熱性、耐水性、耐湿性が必要な個所のシール剤、コーティング剤、接着剤として有用である。とりわけ、耐湿性、耐水性が必要な建築用途、電気電子用接着剤用途として有効に使用することができる。
更に、上記一般式（３）で示される、２つのアルコキシシリル－ビニレン基を有する加水分解性オルガノシラン化合物及び／又はその部分加水分解縮合物、別言すれば、分子内の２つの加水分解性シリル基中に１つずつ存在する２個のケイ素原子同士を、それぞれエテニレン基（炭素－炭素二重結合）を介して同一のケイ素原子に結合させた（加水分解性シリル基－エテニレン基－ケイ素原子－エテニレン基－加水分解性シリル基）、ビス（加水分解性シリル）型のオルガノシラン等の加水分解性オルガノシラン化合物及び／又はその部分加水分解縮合物（加水分解性シロキサンオリゴマー）を、硬化剤（（Ｂ）成分）として使用することにより、本発明は、とりわけ速硬化性、深部硬化性に優れ、同時に保存安定性、耐久性も良好な硬化物を与えることができる。
（Ｂ）成分の出発原料としては汎用品のクロロシランやヒドロシラン（ジオルガノジクロロシランやモノヒドロアルコキシシラン等）を用いることができるため、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物を工業的に有利に製造することができる。更に上記の通り、第一剤と第二剤とを混合することにより速硬化性、深部硬化性に優れた室温速硬化性オルガノポリシロキサン組成物を調製することができる。
以下、本発明を更に詳細に説明する。
＜二成分型室温速硬化性オルガノポリシロキサン組成物＞
本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、後述する（Ａ）成分及び（Ｂ）成分の特定量を含有してなる第一剤と、（Ａ）成分及び（Ｃ）成分の特定量を含有してなる第二剤とからなるものである。なお、第一剤には（Ｃ）成分を含まないものであり、第二剤には（Ｂ）成分を含まないものである。
以下に、各成分について詳述する。
＜二成分型室温速硬化性オルガノポリシロキサン組成物＞
本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、後述する（Ａ）成分及び（Ｂ）成分の特定量を含有してなる第一剤と、（Ａ）成分及び（Ｃ）成分の特定量を含有してなる第二剤とからなるものである。なお、第一剤には（Ｃ）成分を含まないものであり、第二剤には（Ｂ）成分を含まないものである。
以下に、各成分について詳述する。
－（Ａ）成分：オルガノポリシロキサン－
（Ａ）成分は、後述する一般式（１）又は（２）で示されるオルガノポリシロキサンであり、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物において主剤（ベースポリマー）として作用するものである。
（Ａ）成分は、後述する一般式（１）又は（２）で示されるオルガノポリシロキサンであり、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物において主剤（ベースポリマー）として作用するものである。
下記一般式（１）で示されるオルガノポリシロキサンは、分子鎖両末端がケイ素原子に結合した水酸基（シラノール基）あるいはジオルガノヒドロキシシロキシ基で封鎖され、主鎖がジオルガノシロキサン単位（（Ｒ1）2ＳｉＯ2/2）の繰り返し構造からなる直鎖状ジオルガノポリシロキサンである。
（一般式（１）中、Ｒ1は独立に炭素数１～２０の非置換又は置換の１価炭化水素基であり、ｎは１０以上の整数である。）
上記式（１）中、Ｒ1の非置換又は置換の１価炭化水素基としては、その炭素数が１～２０であり、好ましくは炭素数１～１０であり、より好ましくは炭素数１～８である。Ｒ1の非置換の１価炭化水素基として、具体的には、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基、ｔｅｒｔ－ブチル基、ペンチル基、ネオペンチル基、ヘキシル基、ヘプチル基、オクチル基、ノニル基、デシル基、ウンデシル基、ドデシル基、トリデシル基、テトラデシル基、ペンタデシル基、ヘキサデシル基、ヘプタデシル基、オクタデシル基、ノナデシル基、エイコシル基等のアルキル基；シクロペンチル基、シクロヘキシル基、シクロヘプチル基等のシクロアルキル基；ビニル基、アリル基、プロペニル基、イソプロペニル基、ブテニル基、ペンテニル基、ヘキセニル基等のアルケニル基；フェニル基、トリル基、キシリル基、α－，β－ナフチル基、ビフェニリル基等のアリール基；ベンジル基、２－フェニルエチル基、３－フェニルプロピル基、２－メチル－２－フェニルエチル基、メチルベンジル基等のアラルキル基が挙げられる。また、Ｒ1の置換の１価炭化水素基としては、非置換の１価炭化水素基の水素原子の一部又は全部が、Ｆ、Ｃｌ、Ｂｒ等のハロゲン原子やシアノ基等で置換された基が挙げられる。このような基としては、３－クロロプロピル基、３，３，３－トリフルオロプロピル基、２－シアノエチル基等を例示することができる。Ｒ1としては、これらの非置換又は置換の１価炭化水素基の中でも、メチル基、エチル基、フェニル基が好ましく、入手の容易さ、生産性、コストの面からメチル基、フェニル基が特に好ましい。複数のＲ1は互いに同一であっても、異なっていてもよい。
また、一般式（１）で示される（Ａ）成分のオルガノポリシロキサンは、２３℃における粘度が２０～１，０００，０００ｍＰａ・ｓのものが好ましく、より好ましくは５０～５００，０００ｍＰａ・ｓのもの、特に好ましくは１００～１００，０００ｍＰａ・ｓのもの、更に好ましくは５００～８０，０００ｍＰａ・ｓのものである。２３℃における前記オルガノポリシロキサンの粘度が２０ｍＰａ・ｓ以上であれば、物理的・機械的強度に優れたコーティング塗膜を得ることが容易であるため好ましい。１，０００，０００ｍＰａ・ｓ以下であれば、組成物の粘度が高くなり過ぎず使用時における作業性が良いので好ましい。本発明において、粘度は、特に明示しない限り、いずれも回転粘度計で測定された数値である（以下、同じ）。回転粘度計としては、例えば、ＢＬ型、ＢＨ型、ＢＳ型、コーンプレート型等のものが挙げられる。
上記式（１）におけるｎの値は、１０以上の整数であり、１分子中に存在する２官能性ジオルガノシロキサン単位（（Ｒ1）2ＳｉＯ2/2）の数又は重合度である。（Ａ）成分のオルガノポリシロキサンが上記の好ましい範囲内の粘度を取り得る態様では、一般式（１）中、ｎで表される２官能性ジオルガノシロキサン（（Ｒ1）2ＳｉＯ2/2）の単位数又は重合度は、１０～２，０００の整数であり、好ましくは３０～１，５００であり、より好ましくは５０～１，２００であり、更に好ましくは１００～１，０００である。なお、本発明において、重合度（又は分子量）は、トルエン等を展開溶媒としてゲルパーミエーションクロマトグラフィ（ＧＰＣ）分析におけるポリスチレン換算の数平均重合度（又は数平均分子量）等として求めたものである（以下、同じ）。
また、下記一般式（２）で示されるオルガノポリシロキサンは、分子鎖両末端がアルコキシシリル基等の加水分解性シリル基で封鎖された直鎖状オルガノポリシロキサンである。
（一般式（２）中、Ｒ2は独立に炭素数１～２０の非置換又は置換の１価炭化水素基であり、Ｒ3は酸素原子又は炭素数１～４のアルキレン基であり、Ｒ4は独立に炭素数１～２０の脂肪族不飽和結合を含有しない非置換又は置換の１価炭化水素基であり、Ｒ5は独立に炭素数１～４の、アルキル基、アルコキシアルキル基、アルケニル基又はアシル基であり、ｘは０～２の整数であり、ｍは１０以上の整数である。）
上記式（２）中、Ｒ2は独立に炭素数１～２０、好ましくは炭素数１～１０、より好ましくは炭素数１～６、更に好ましくは炭素数１～３の非置換又は置換の１価炭化水素基であり、その例としては、直鎖状アルキル基、分岐鎖状アルキル基、環状アルキル基、アルケニル基、アリール基、アラルキル基、ハロゲン化アルキル基等が挙げられる。直鎖状アルキル基としては、例えば、メチル基、エチル基、プロピル基、ヘキシル基、オクチル基、ノニル基、デシル基、ウンデシル基、ドデシル基、トリデシル基、テトラデシル基、ペンタデシル基、ヘキサデシル基、ヘプタデシル基、オクタデシル基、ノナデシル基、エイコシル基が挙げられる。分岐鎖状アルキル基としては、例えば、イソプロピル基、イソブチル基、ｔｅｒｔ－ブチル基、２－エチルヘキシル基が挙げられる。環状アルキル基としては、例えば、シクロペンチル基、シクロヘキシル基、シクロヘプチル基が挙げられる。アルケニル基としては、例えば、ビニル基、アリル基、プロペニル基、イソプロペニル基、ブテニル基、ペンテニル基、ヘキセニル基が挙げられる。アリール基としては、例えば、フェニル基、トリル基、キシリル基、α－，β－ナフチル基、ビフェニリル基が挙げられる。アラルキル基としては、例えば、ベンジル基、２－フェニルエチル基、３－フェニルプロピル基、２－メチル－２－フェニルエチル基、メチルベンジル基が挙げられる。ハロゲン化アルキル基としては、例えば、３－クロロプロピル基、３，３，３－トリフルオロプロピル基、２－（ノナフルオロブチル）エチル基、２－（ヘプタデカフルオロオクチル）エチル基が挙げられる。Ｒ2としては、メチル基、フェニル基が好ましい。
上記式（２）中、Ｒ3は酸素原子又は炭素数１～４のアルキレン基であり、Ｒ3の炭素数１～４のアルキレン基としては、例えば、メチレン基、エチレン基、プロピレン基、ブチレン基等が挙げられる。Ｒ3としては、酸素原子、エチレン基が好ましい。
また、Ｒ4は独立に炭素数１～２０、好ましくは炭素数１～１０、より好ましくは炭素数１～６、更に好ましくは炭素数１～３の脂肪族不飽和結合を含有しない非置換又は置換の１価炭化水素基である。Ｒ4としては、例えば、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基、ｔｅｒｔ－ブチル基、ペンチル基、ネオペンチル基、ヘキシル基、ヘプチル基、オクチル基、ノニル基、デシル基、ウンデシル基、ドデシル基、トリデシル基、テトラデシル基、ペンタデシル基、ヘキサデシル基、ヘプタデシル基、オクタデシル基、ノナデシル基、エイコシル基等のアルキル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基等のシクロアルキル基、フェニル基、トリル基、キシリル基、α－，β－ナフチル基、ビフェニリル基等のアリール基、ベンジル基、２－フェニルエチル基、３－フェニルプロピル基、２－メチル－２－フェニルエチル基、メチルベンジル基等のアラルキル基、並びにこれらの基の炭素原子が結合している水素原子の一部又は全部が、フッ素、塩素、臭素等のハロゲン原子、シアノ基等で置換された基等が挙げられ、このような基としては、３－クロロプロピル基、３，３，３－トリフルオロプロピル基、２－シアノエチル基等を例示することができる。Ｒ4としては、メチル基、エチル基、フェニル基が好ましい。
また、Ｒ4は独立に炭素数１～２０、好ましくは炭素数１～１０、より好ましくは炭素数１～６、更に好ましくは炭素数１～３の脂肪族不飽和結合を含有しない非置換又は置換の１価炭化水素基である。Ｒ4としては、例えば、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基、ｔｅｒｔ－ブチル基、ペンチル基、ネオペンチル基、ヘキシル基、ヘプチル基、オクチル基、ノニル基、デシル基、ウンデシル基、ドデシル基、トリデシル基、テトラデシル基、ペンタデシル基、ヘキサデシル基、ヘプタデシル基、オクタデシル基、ノナデシル基、エイコシル基等のアルキル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基等のシクロアルキル基、フェニル基、トリル基、キシリル基、α－，β－ナフチル基、ビフェニリル基等のアリール基、ベンジル基、２－フェニルエチル基、３－フェニルプロピル基、２－メチル－２－フェニルエチル基、メチルベンジル基等のアラルキル基、並びにこれらの基の炭素原子が結合している水素原子の一部又は全部が、フッ素、塩素、臭素等のハロゲン原子、シアノ基等で置換された基等が挙げられ、このような基としては、３－クロロプロピル基、３，３，３－トリフルオロプロピル基、２－シアノエチル基等を例示することができる。Ｒ4としては、メチル基、エチル基、フェニル基が好ましい。
上記式（２）中、Ｒ5は独立に炭素数１～４の、アルキル基、アルコキシアルキル基、アルケニル基又はアシル基である。上記Ｒ5のアルキル基としては、例えば、Ｒ2について例示したものと同様の、炭素数１～４のアルキル基等が挙げられる。Ｒ5のアルコキシアルキル基としては、例えば、メトキシエチル基、メトキシプロピル基等の炭素数２～４のものが挙げられる。Ｒ5のアルケニル基としては、例えば、Ｒ2について例示したものと同様の、炭素数２～４のアルケニル基が挙げられる。上記Ｒ5のアシル基としては、例えば、アセチル基、プロピオニル基等の炭素数１～４のものが挙げられる。Ｒ5はアルキル基であることが好ましく、特にはメチル基、エチル基であることが好ましい。
上記式（２）中、ｘは０～２の整数（０、１又は２）であり、好ましくは０又は１であり、より好ましくは０である。なお、加水分解性基であるＯＲ5で示されるケイ素原子に結合したアルコキシ基等のオルガノオキシ基の数は、１分子中に２～６個、好ましくは４～６個、より好ましくは４個又は６個である。
また、一般式（２）で示される（Ａ）成分のオルガノポリシロキサンは、２３℃における粘度が２０～１，０００，０００ｍＰａ・ｓのものが好ましく、より好ましくは５０～５００，０００ｍＰａ・ｓのもの、特に好ましくは１００～２００，０００ｍＰａ・ｓのもの、更に好ましくは５００～１００，０００ｍＰａ・ｓのものである。２３℃における前記オルガノポリシロキサンの粘度が２０ｍＰａ・ｓ以上であれば、物理的・機械的強度に優れたコーティング塗膜を得ることが容易であるため好ましい。１，０００，０００ｍＰａ・ｓ以下であれば、組成物の粘度が高くなり過ぎず使用時における作業性が良いので好ましい。
上記式（２）におけるｍの値は、１０以上の整数であり、１分子中に存在する２官能性ジオルガノシロキサン単位（（Ｒ2）2ＳｉＯ2/2）の数又は重合度である。（Ａ）成分のオルガノポリシロキサンが上記の好ましい範囲内の粘度を取り得る態様では、一般式（２）中、ｍで表される２官能性ジオルガノシロキサン（（Ｒ2）2ＳｉＯ2/2）の単位数又は重合度は、１０～２，０００の整数であり、好ましくは５０～１，８００であり、より好ましくは１００～１，７００であり、更に好ましくは２００～１，６００である。
（Ａ）成分のオルガノポリシロキサンは１種又は２種以上を併用することができる。
（Ａ）成分のオルガノポリシロキサンは１種又は２種以上を併用することができる。
－（Ｂ）成分：加水分解性オルガノシラン化合物及び／又はその部分加水分解縮合物－
本発明に係る（Ｂ）成分は、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物において硬化剤（架橋剤）として作用するものである。（Ｂ）成分は、下記一般式（３）で示される同一ケイ素原子上に２個のアルコキシシリル－ビニレン基（アルコキシシリル－エテニレン基）を有する加水分解性オルガノシラン化合物及び／又はその部分加水分解縮合物である。
なお、本発明において部分加水分解縮合物とは、上記加水分解性オルガノシランを部分的に加水分解縮合して生成する、１分子中に少なくとも３個の残存加水分解性基を有するオルガノシロキサンオリゴマーを意味する。本発明では、残存加水分解性基を２個有するオルガノシロキサンオリゴマーを併用してもよい。
本発明に係る（Ｂ）成分は、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物において硬化剤（架橋剤）として作用するものである。（Ｂ）成分は、下記一般式（３）で示される同一ケイ素原子上に２個のアルコキシシリル－ビニレン基（アルコキシシリル－エテニレン基）を有する加水分解性オルガノシラン化合物及び／又はその部分加水分解縮合物である。
なお、本発明において部分加水分解縮合物とは、上記加水分解性オルガノシランを部分的に加水分解縮合して生成する、１分子中に少なくとも３個の残存加水分解性基を有するオルガノシロキサンオリゴマーを意味する。本発明では、残存加水分解性基を２個有するオルガノシロキサンオリゴマーを併用してもよい。
ここで、上記式（３）中、各Ｒ6の非置換又は置換の１価炭化水素基としては、その炭素数が１～２０であり、好ましくは炭素数１～１０であり、より好ましくは炭素数１～８である。Ｒ6の非置換の１価炭化水素基の例としては、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基、ｔｅｒｔ－ブチル基、ペンチル基、ネオペンチル基、ヘキシル基、ヘプチル基、オクチル基、ノニル基、デシル基、ウンデシル基、ドデシル基、トリデシル基、テトラデシル基、ペンタデシル基、ヘキサデシル基、ヘプタデシル基、オクタデシル基、ノナデシル基、エイコシル基等のアルキル基；シクロペンチル基、シクロヘキシル基、シクロヘプチル基等のシクロアルキル基；ビニル基、アリル基、プロペニル基、イソプロペニル基、ブテニル基、ペンテニル基、ヘキセニル基等のアルケニル基；フェニル基、トリル基、キシリル基、α－，β－ナフチル基、ビフェニリル基等のアリール基；ベンジル基、２－フェニルエチル基、３－フェニルプロピル基、２－メチル－２－フェニルエチル基、メチルベンジル基等のアラルキル基が挙げられる。また、Ｒ6の置換の１価炭化水素基としては、これらの非置換の１価炭化水素基の水素原子の一部又は全部が、Ｆ、Ｃｌ、Ｂｒ等のハロゲン原子やシアノ基等で置換された基、例えば、３－クロロプロピル基、３，３，３－トリフルオロプロピル基、２－シアノエチル基等を例示することができる。Ｒ6の非置換又は置換の１価炭化水素基としては、これらの中でも、メチル基、エチル基、フェニル基が好ましく、入手の容易さ、生産性、コストの面からメチル基、フェニル基が特に好ましい。複数のＲ6は、互いに同一であっても、異なっていてもよい。
式（３）において、Ｒ7は炭素数１～２０の非置換若しくは置換のアルキル基、又は炭素数３～２０の非置換若しくは置換のシクロアルキル基である。非置換若しくは置換のアルキル基の炭素数は１～２０であり、好ましくは炭素数１～６であり、より好ましくは炭素数１～４である。該非置換アルキル基の例としては、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基、ｔｅｒｔ－ブチル基、ペンチル基、ネオペンチル基、ヘキシル基、ヘプチル基、オクチル基、ノニル基、デシル基、ウンデシル基、ドデシル基、トリデシル基、テトラデシル基、ペンタデシル基、ヘキサデシル基、ヘプタデシル基、オクタデシル基、ノナデシル基、エイコシル基等が挙げられる。非置換若しくは置換のシクロアルキル基の炭素数は３～２０であり、好ましくは炭素数４～８であり、より好ましくは炭素数５又は６である。非置換シクロアルキル基の例としては、シクロペンチル基、シクロヘキシル基、シクロヘプチル基等が挙げられる。また、これら非置換アルキル基や非置換シクロアルキル基の水素原子の一部又は全部が、Ｆ、Ｃｌ、Ｂｒ等のハロゲン原子やシアノ基等で置換されていてもよい。置換アルキル基や置換シクロアルキル基としては、例えば、３－クロロプロピル基、３，３，３－トリフルオロプロピル基、２－シアノエチル基等が挙げられる。Ｒ7としては、これらの中でも、加水分解性などの点から、メチル基、エチル基が好ましく、メチル基が特に好ましい。
上記式（３）において、ａは、アルコキシシリル－ビニレン基のケイ素原子にそれぞれ結合するアルコキシ基の数であり、ケイ素原子毎に独立に１～３の整数であり、２又は３であることが硬化性の点から好ましい。特に、１分子中、２つのアルコキシシリル－ビニレン基が、それぞれ、メトキシ基等の３個のアルコキシ基を有するもの、即ち、１分子中に合計６個のアルコキシ基を有するものは、３官能のアルコキシシラン部位が１分子中に２個あるため、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物の硬化剤（架橋剤）として有用である。
（Ｂ）成分の加水分解性オルガノシラン化合物としては、例えば、
ビス（トリメトキシシリルエテニル）ジメチルシラン、
ビス（トリメトキシシリルエテニル）ジエチルシラン、
ビス（トリメトキシシリルエテニル）メチルエチルシラン、
ビス（トリメトキシシリルエテニル）メチルフェニルシラン、
ビス（トリエトキシシリルエテニル）ジメチルシラン、
ビス（トリエトキシシリルエテニル）ジエチルシラン、
ビス（トリエトキシシリルエテニル）メチルエチルシラン、
ビス（トリエトキシシリルエテニル）メチルフェニルシラン、
ビス（メチルジメトキシシリルエテニル）ジメチルシラン、
ビス（メチルジメトキシシリルエテニル）ジエチルシラン、
ビス（メチルジメトキシシリルエテニル）メチルエチルシラン、
ビス（メチルジメトキシシリルエテニル）メチルフェニルシラン、
ビス（エチルジメトキシシリルエテニル）ジメチルシラン、
ビス（エチルジメトキシシリルエテニル）ジエチルシラン、
ビス（エチルジメトキシシリルエテニル）メチルエチルシラン、
ビス（エチルジメトキシシリルエテニル）メチルフェニルシラン、
ビス（メチルジエトキシシリルエテニル）ジメチルシラン、
ビス（メチルジエトキシシリルエテニル）ジエチルシラン、
ビス（メチルジエトキシシリルエテニル）メチルエチルシラン、
ビス（メチルジエトキシシリルエテニル）メチルフェニルシラン、
などのような、１分子中の同一ケイ素原子上に２個のトリメトキシシリル－ビニレン基やトリエトキシシリル－ビニレン基等のトリアルコキシシリル－ビニレン基を有するか、又は、１分子中の同一ケイ素原子上に２個の（オルガノ）ジメトキシシリル－ビニレン基や（オルガノ）ジエトキシシリル－ビニレン基等の（オルガノ）ジアルコキシシリル－ビニレン基を有する加水分解性オルガノシラン化合物や、その部分加水分解縮合物が挙げられる。
ビス（トリメトキシシリルエテニル）ジメチルシラン、
ビス（トリメトキシシリルエテニル）ジエチルシラン、
ビス（トリメトキシシリルエテニル）メチルエチルシラン、
ビス（トリメトキシシリルエテニル）メチルフェニルシラン、
ビス（トリエトキシシリルエテニル）ジメチルシラン、
ビス（トリエトキシシリルエテニル）ジエチルシラン、
ビス（トリエトキシシリルエテニル）メチルエチルシラン、
ビス（トリエトキシシリルエテニル）メチルフェニルシラン、
ビス（メチルジメトキシシリルエテニル）ジメチルシラン、
ビス（メチルジメトキシシリルエテニル）ジエチルシラン、
ビス（メチルジメトキシシリルエテニル）メチルエチルシラン、
ビス（メチルジメトキシシリルエテニル）メチルフェニルシラン、
ビス（エチルジメトキシシリルエテニル）ジメチルシラン、
ビス（エチルジメトキシシリルエテニル）ジエチルシラン、
ビス（エチルジメトキシシリルエテニル）メチルエチルシラン、
ビス（エチルジメトキシシリルエテニル）メチルフェニルシラン、
ビス（メチルジエトキシシリルエテニル）ジメチルシラン、
ビス（メチルジエトキシシリルエテニル）ジエチルシラン、
ビス（メチルジエトキシシリルエテニル）メチルエチルシラン、
ビス（メチルジエトキシシリルエテニル）メチルフェニルシラン、
などのような、１分子中の同一ケイ素原子上に２個のトリメトキシシリル－ビニレン基やトリエトキシシリル－ビニレン基等のトリアルコキシシリル－ビニレン基を有するか、又は、１分子中の同一ケイ素原子上に２個の（オルガノ）ジメトキシシリル－ビニレン基や（オルガノ）ジエトキシシリル－ビニレン基等の（オルガノ）ジアルコキシシリル－ビニレン基を有する加水分解性オルガノシラン化合物や、その部分加水分解縮合物が挙げられる。
（Ｂ）成分は、出発原料として汎用品のクロロシランやヒドロシラン（ジオルガノジクロロシランやモノヒドロアルコキシシラン等）を用いることができる。
具体的には、（Ｂ）成分の同一ケイ素原子上に２個のアルコキシシリル－ビニレン基（アルコキシシリル－エテニレン基）等の加水分解性シリル－ビニレン基（加水分解性シリル－エテニレン基）を有する加水分解性オルガノシラン化合物は、例えば、工業的に汎用品であるジオルガノジクロロシランから誘導される、同一ケイ素原子上にエチニル基を２個有するオルガノシランに対して２倍モルのモノヒドロアルコキシシラン等の加水分解性基含有ヒドロシランをヒドロシリル化付加反応させる等の方法によって容易に製造することができる。この反応式は、例えば、下記式（３－１）で表される。
（式中、Ｒ6、Ｒ7、ａは前記一般式（３）の通りである。）
具体的には、（Ｂ）成分の同一ケイ素原子上に２個のアルコキシシリル－ビニレン基（アルコキシシリル－エテニレン基）等の加水分解性シリル－ビニレン基（加水分解性シリル－エテニレン基）を有する加水分解性オルガノシラン化合物は、例えば、工業的に汎用品であるジオルガノジクロロシランから誘導される、同一ケイ素原子上にエチニル基を２個有するオルガノシランに対して２倍モルのモノヒドロアルコキシシラン等の加水分解性基含有ヒドロシランをヒドロシリル化付加反応させる等の方法によって容易に製造することができる。この反応式は、例えば、下記式（３－１）で表される。
ここで、モノヒドロアルコキシシラン等の加水分解性基含有ヒドロシランを付加させる際に用いるヒドロシリル化付加反応触媒としては、白金族金属系触媒、例えば白金系、パラジウム系、ロジウム系、ルテニウム系のものがあるが、白金系のものが特に好適である。この白金系のものとしては、白金黒あるいはアルミナ、シリカ等の担体に固体白金を担持させたもの、塩化白金酸、アルコール変性塩化白金酸、塩化白金酸とオレフィンとの錯体あるいは白金とビニルシロキサンとの錯体等を例示することができる。これらの白金の使用量は、所謂触媒量でよく、例えばモノヒドロアルコキシシラン等の加水分解性基含有ヒドロシラン類に対して、白金族金属の質量換算で０．１～１，０００ｐｐｍ、特に０．５～１００ｐｐｍ程度で使用できる。
この反応は、一般に５０～１２０℃、特に６０～１００℃の温度で、０．５～１２時間、特に１～６時間行うことが望ましく、また溶媒を使用せずに行うことができるが、上記ヒドロシリル化付加反応等に悪影響を与えない限りにおいて、必要によりトルエン、キシレン等の適当な溶剤を使用することができる。
この反応は、一般に５０～１２０℃、特に６０～１００℃の温度で、０．５～１２時間、特に１～６時間行うことが望ましく、また溶媒を使用せずに行うことができるが、上記ヒドロシリル化付加反応等に悪影響を与えない限りにおいて、必要によりトルエン、キシレン等の適当な溶剤を使用することができる。
（Ｂ）成分の加水分解性オルガノシラン化合物及び／又はその部分加水分解縮合物は、１種単独で使用しても、２種以上を併用してもよい。
（Ｂ）成分の配合量は、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して０．１～３０質量部であり、好ましくは０．５～２５質量部である。（Ｂ）成分の配合量が少なすぎると組成物を硬化させる際に十分な架橋が得られず、多すぎると得られる硬化物（シリコーンゴム硬化物）の機械特性（ゴム物性）も低下し、経済的に不利となるという問題が発生する場合がある。
（Ｂ）成分の配合量は、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して０．１～３０質量部であり、好ましくは０．５～２５質量部である。（Ｂ）成分の配合量が少なすぎると組成物を硬化させる際に十分な架橋が得られず、多すぎると得られる硬化物（シリコーンゴム硬化物）の機械特性（ゴム物性）も低下し、経済的に不利となるという問題が発生する場合がある。
－（Ｃ）成分－
（Ｃ）成分の硬化触媒は、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物と空気中の水分との加水分解縮合反応を促進させるために使用され、一般的に硬化触媒と呼ばれるものである。これは湿分の存在下で硬化する室温硬化性シリコーン樹脂組成物に通常使用されている公知のものを使用することができる。
（Ｃ）成分の硬化触媒は、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物と空気中の水分との加水分解縮合反応を促進させるために使用され、一般的に硬化触媒と呼ばれるものである。これは湿分の存在下で硬化する室温硬化性シリコーン樹脂組成物に通常使用されている公知のものを使用することができる。
（Ｃ）成分の硬化触媒のうち、非金属系有機触媒は特に制限されないが、縮合硬化型オルガノポリシロキサン組成物の硬化促進剤として公知のものを使用することができる。例えば、Ｎ，Ｎ，Ｎ’，Ｎ’，Ｎ''，Ｎ''－ヘキサメチル－Ｎ'''－（トリメチルシリルメチル）－ホスホリミディックトリアミド等のホスファゼン含有化合物；ヘキシルアミン、リン酸ドデシルアミン等のアミン化合物又はその塩；ベンジルトリエチルアンモニウムアセテート等の第４級アンモニウム塩；ジメチルヒドロキシルアミン、ジエチルヒドロキシルアミン等のジアルキルヒドロキシルアミン；Ｎ，Ｎ，Ｎ’，Ｎ’－テトラメチルグアニジルプロピルトリメトキシシラン、Ｎ，Ｎ，Ｎ’，Ｎ’－テトラメチルグアニジルプロピルメチルジメトキシシラン、Ｎ，Ｎ，Ｎ’，Ｎ’－テトラメチルグアニジルプロピルトリス（トリメチルシロキシ）シラン等のグアニジル基を含有するシラン及びシロキサン等が挙げられる。また、非金属系有機触媒は１種単独で使用してもよく、２種以上混合して使用してもよい。
（Ｃ）成分の硬化触媒のうち、金属系触媒は特に制限されないが、縮合硬化型オルガノポリシロキサンの硬化触媒として公知のものを使用することができる。例えば、ジブチルスズジアセテート、ジブチルスズジラウレート、ジブチルスズジオクトエート、ジメチルスズジネオデカノエート、ジオクチルスズジネオデカノエート、ジ－ｎ－ブチル－ジメトキシスズ等のアルキルスズエステル化合物；テトライソプロポキシチタン、テトラ－ｎ－ブトキシチタン、テトラキス（２－エチルヘキソキシ）チタン、ジプロポキシビス（アセチルアセトナト）チタン、チタニウムイソプロポキシオクチレングリコール等のチタン酸エステル又はチタンキレート化合物；ナフテン酸亜鉛、ステアリン酸亜鉛、亜鉛－２－エチルオクトエート；アルミニウムイソプロピレート、アルミニウムセカンダリーブチレートなどのアルコレートアルミニウム化合物；アルミニウムアルキルアセテート・ジイソプロピレート、アルミニウムビスエチルアセトアセテート・モノアセチルアセトネート等のアルミニウムキレート化合物；ネオデカン酸ビスマス（ＩＩＩ）、２－エチルヘキサン酸ビスマス（ＩＩＩ）、クエン酸ビスマス（ＩＩＩ）、オクチル酸ビスマス、鉄－２－エチルヘキソエート、コバルト－２－エチルヘキソエート、マンガン－２－エチルヘキソエート、ナフテン酸コバルト等の有機金属化合物；酢酸カリウム、酢酸ナトリウム、シュウ酸リチウム等のアルカリ金属の低級脂肪酸塩が挙げられる。金属系触媒はこれらに限定されない。金属系触媒は、１種単独で使用してもよく、２種以上混合して使用してもよい。
（Ｃ）成分の配合量は、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して０．００１～１０質量部であり、特に０．００５～８質量部、更に０．０１～５質量部が好ましい。０．００１質量部未満であると良好な硬化性を得ることができないため、硬化速度が遅れる不具合を生じる。逆に、１０質量部を超える量になると、組成物の硬化性が速すぎるため、組成物塗布後の作業時間の許容範囲が短くなったり、得られるゴムの機械特性が低下したりする虞がある。
－（Ｄ）成分：充填剤－
（Ｄ）成分は充填剤（無機質充填剤及び／又は有機樹脂充填剤）であり、必要に応じて配合できる任意成分であり、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物から形成される硬化物に十分な機械的強度を与えるために使用される。この充填剤としては公知のものを使用することができ、例えば、微粉末シリカ、煙霧質シリカ、沈降性シリカなどの湿式シリカ、これらのシリカ表面を有機ケイ素化合物で疎水化処理したシリカなどの補強性シリカ系充填剤、ガラスビーズ、ガラスバルーン、透明樹脂ビーズ、シリカエアロゲル、珪藻土、酸化鉄、酸化亜鉛、酸化チタン、煙霧状金属酸化物などの金属酸化物、石英粉末（結晶性シリカ微粉末）、カーボンブラック、タルク、ゼオライト及びベントナイト等の補強剤、アスベスト、ガラス繊維、炭素繊維、炭酸カルシウム、炭酸マグネシウム、炭酸亜鉛などの金属炭酸塩、アスベスト、ガラスウール、微粉マイカ、溶融シリカ粉末（ここまで無機質充填剤）、ポリスチレン、ポリ塩化ビニル、ポリプロピレンなどの合成樹脂粉末等が使用される。これらの充填剤のうち、シリカ、炭酸カルシウム、ゼオライトなどの無機質充填剤が好ましく、特に表面を疎水化処理した煙霧質シリカ、炭酸カルシウムが好ましい。
（Ｄ）成分は充填剤（無機質充填剤及び／又は有機樹脂充填剤）であり、必要に応じて配合できる任意成分であり、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物から形成される硬化物に十分な機械的強度を与えるために使用される。この充填剤としては公知のものを使用することができ、例えば、微粉末シリカ、煙霧質シリカ、沈降性シリカなどの湿式シリカ、これらのシリカ表面を有機ケイ素化合物で疎水化処理したシリカなどの補強性シリカ系充填剤、ガラスビーズ、ガラスバルーン、透明樹脂ビーズ、シリカエアロゲル、珪藻土、酸化鉄、酸化亜鉛、酸化チタン、煙霧状金属酸化物などの金属酸化物、石英粉末（結晶性シリカ微粉末）、カーボンブラック、タルク、ゼオライト及びベントナイト等の補強剤、アスベスト、ガラス繊維、炭素繊維、炭酸カルシウム、炭酸マグネシウム、炭酸亜鉛などの金属炭酸塩、アスベスト、ガラスウール、微粉マイカ、溶融シリカ粉末（ここまで無機質充填剤）、ポリスチレン、ポリ塩化ビニル、ポリプロピレンなどの合成樹脂粉末等が使用される。これらの充填剤のうち、シリカ、炭酸カルシウム、ゼオライトなどの無機質充填剤が好ましく、特に表面を疎水化処理した煙霧質シリカ、炭酸カルシウムが好ましい。
（Ｄ）成分を配合する場合、その配合量は、第一剤又は第二剤中に含まれる（Ａ）成分の合計１００質量部に対して、第一剤及び第二剤中にそれぞれ０～１，０００質量部とする（ただし、少なくとも第一剤、第二剤のいずれか一方に０．１質量部以上含有する）ことが好ましく、０～５００質量部とする（ただし、少なくとも第一剤、第二剤のいずれか一方に０．１質量部以上含有する）ことがより好ましい。１，０００質量部よりも多量に使用すると、組成物の粘度が増大して作業性が悪くなるばかりでなく、硬化後のゴム強度が低下してゴム弾性が得難くなる。即ち、（Ｄ）成分を配合する場合の組成物中における総配合量は、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して０．１～２，０００質量部、特に０．１～１，０００質量部であることが好ましい。
－（Ｅ）成分：接着促進剤－
（Ｅ）成分は接着促進剤であり、必要に応じて配合できる任意成分であり、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物から形成される硬化物に十分な接着性を与えるために使用される。接着促進剤としては公知のものが好適に使用され、官能性基含有加水分解性シラン等のシランカップリング剤、具体的には、ビニルシランカップリング剤、（メタ）アクリルシランカップリング剤、エポキシシランカップリング剤、アミノシランカップリング剤（但し、グアニジル基含有加水分解性オルガノシラン化合物を除く）、メルカプトシランカップリング剤、イソシアネートシランカップリング剤などが例示され、具体的には、ビニルトリス（β－メトキシエトキシ）シラン、γ－メタクリロキシプロピルトリメトキシシラン、β－（３，４－エポキシシクロヘキシル）エチルトリメトキシシラン、γ－グリシドキシプロピルトリメトキシシラン、γ－グリシドキシプロピルメチルジエトキシシラン、Ｎ－β－（アミノエチル）γ－アミノプロピルトリメトキシシラン、γ－アミノプロピルトリエトキシシラン、３－２－（アミノエチルアミノ）プロピルトリメトキシシラン、γ－メルカプトプロピルトリメトキシシラン、３－イソシアネートプロピルトリエトキシシラン等が例示される。
これらの中でも、特にγ－アミノプロピルトリエトキシシラン、Ｎ－β－（アミノエチル）γ－アミノプロピルトリメトキシシラン等のアミノシラン類、γ－グリシドキシプロピルトリメトキシシラン、β－（３，４－エポキシシクロヘキシル）エチルトリメトキシシラン等のエポキシシラン類、３－イソシアネートプロピルトリエトキシシラン等のイソシアネートシラン類が好ましい。
（Ｅ）成分は接着促進剤であり、必要に応じて配合できる任意成分であり、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物から形成される硬化物に十分な接着性を与えるために使用される。接着促進剤としては公知のものが好適に使用され、官能性基含有加水分解性シラン等のシランカップリング剤、具体的には、ビニルシランカップリング剤、（メタ）アクリルシランカップリング剤、エポキシシランカップリング剤、アミノシランカップリング剤（但し、グアニジル基含有加水分解性オルガノシラン化合物を除く）、メルカプトシランカップリング剤、イソシアネートシランカップリング剤などが例示され、具体的には、ビニルトリス（β－メトキシエトキシ）シラン、γ－メタクリロキシプロピルトリメトキシシラン、β－（３，４－エポキシシクロヘキシル）エチルトリメトキシシラン、γ－グリシドキシプロピルトリメトキシシラン、γ－グリシドキシプロピルメチルジエトキシシラン、Ｎ－β－（アミノエチル）γ－アミノプロピルトリメトキシシラン、γ－アミノプロピルトリエトキシシラン、３－２－（アミノエチルアミノ）プロピルトリメトキシシラン、γ－メルカプトプロピルトリメトキシシラン、３－イソシアネートプロピルトリエトキシシラン等が例示される。
これらの中でも、特にγ－アミノプロピルトリエトキシシラン、Ｎ－β－（アミノエチル）γ－アミノプロピルトリメトキシシラン等のアミノシラン類、γ－グリシドキシプロピルトリメトキシシラン、β－（３，４－エポキシシクロヘキシル）エチルトリメトキシシラン等のエポキシシラン類、３－イソシアネートプロピルトリエトキシシラン等のイソシアネートシラン類が好ましい。
（Ｅ）成分を配合する場合、その配合量は、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して、第一剤及び第二剤中にそれぞれ０～３０質量部とする（ただし、少なくとも第一剤、第二剤のいずれか一方に０．００１質量部以上含有する）ことが好ましく、特に０．１～２０質量部とすることが好ましい。即ち、（Ｅ）成分を配合する場合の組成物中における総配合量は、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して０．００１～６０質量部、特に０．１～４０質量部であることが好ましい。充填剤及び被着体により接着促進剤を使用しなくても接着するときは、これを使用しなくてもよい。
－（Ｆ）成分：オルガノポリシロキサン－
本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、上記（Ａ）～（Ｅ）成分に加えて、更に（Ｆ）下記一般式（４）で表される直鎖状のジオルガノポリシロキサン（いわゆる無官能性シリコーンオイル）を必要に応じて配合できる任意成分として含有してもよい。
（一般式（４）中、Ｒ8は独立に炭素数１～２０の脂肪族不飽和結合を含有しない非置換又は置換の１価炭化水素基であり、ｐは１～２，０００の整数である。）
本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、上記（Ａ）～（Ｅ）成分に加えて、更に（Ｆ）下記一般式（４）で表される直鎖状のジオルガノポリシロキサン（いわゆる無官能性シリコーンオイル）を必要に応じて配合できる任意成分として含有してもよい。
上記式（４）中、Ｒ8の脂肪族不飽和結合を含有しない非置換又は置換の１価炭化水素基としては、その炭素数が１～２０であり、好ましくは炭素数１～１０であり、より好ましくは炭素数１～８である。複数のＲ8は互いに同一であっても異なっていてもよい。Ｒ8の非置換の１価炭化水素基としては、メチル基、エチル基、プロピル基、イソプロピル基、ブチル基、イソブチル基、ｔｅｒｔ－ブチル基、ペンチル基、ネオペンチル基、ヘキシル基、ヘプチル基、オクチル基、ノニル基、デシル基、ウンデシル基、ドデシル基、トリデシル基、テトラデシル基、ペンタデシル基、ヘキサデシル基、ヘプタデシル基、オクタデシル基、ノナデシル基、エイコシル基等のアルキル基；シクロペンチル基、シクロヘキシル基、シクロヘプチル基等のシクロアルキル基；フェニル基、トリル基、キシリル基、α－，β－ナフチル基、ビフェニリル基等のアリール基；ベンジル基、２－フェニルエチル基、３－フェニルプロピル基、２－メチル－２－フェニルエチル基、メチルベンジル基等のアラルキル基を例示することができる。また、置換の１価炭化水素基としては、これらの非置換炭化水素基の水素原子の一部又は全部が、Ｆ、Ｃｌ、Ｂｒ等のハロゲン原子やシアノ基等で置換された基、例えば、３－クロロプロピル基、３，３，３－トリフルオロプロピル基、２－シアノエチル基等を例示することができる。これらの中でも、メチル基、エチル基、フェニル基が好ましく、入手の容易さ、生産性、コストの面からメチル基、フェニル基がより好ましい。特に、Ｒ8はいずれもメチル基であることが好ましく、分子鎖の両末端がトリメチルシロキシ基で封鎖されたジメチルポリシロキサンであることが好ましい。
式（４）中、ｐは、（Ｆ）成分の重合度を示す数値で、１～２，０００の整数であり、特に２～２，０００の整数が好ましく、２０～２，０００の整数がより好ましい。ｐが、上記の範囲内の数値である場合、（Ｆ）成分のジオルガノポリシロキサンの２３℃における粘度は、１．５～１，０００，０００ｍＰａ・ｓ、好ましくは３０～１００，０００ｍＰａ・ｓとなる。
（Ｆ）成分を配合する場合、その配合量は、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して、第一剤及び第二剤中にそれぞれ０～１００質量部である（ただし、少なくとも第一剤、第二剤のいずれか一方が０．０１質量部以上含有する）ことが好ましく、より好ましくは１０～８０質量部である。即ち、（Ｆ）成分を配合する場合の組成物中における総配合量は、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して０．０１～２００質量部、特に１０～１６０質量部であることが好ましい。（Ｆ）成分の量が上記範囲内にあると本発明の二成分型室温速硬化性オルガノポリシロキサン組成物の硬化物（シリコーンゴム）の機械特性や難燃性を損なわない点で好ましい。また硬化前の組成物を施工上取り扱い易い粘度に調整することができる。
－その他の成分－
また、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、（Ａ）、（Ｂ）及び（Ｃ）成分を必須成分とし、更に必要に応じて（Ｄ）、（Ｅ）、（Ｆ）成分を配合することが好ましい。その他、添加剤として、顔料、染料、老化防止剤、酸化防止剤、帯電防止剤、酸化アンチモン、塩化パラフィン等の難燃剤など公知の添加剤を配合することができる。更に、チクソ性向上剤としてのポリエーテル、防かび剤、抗菌剤を配合することもできる。
また、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、（Ａ）、（Ｂ）及び（Ｃ）成分を必須成分とし、更に必要に応じて（Ｄ）、（Ｅ）、（Ｆ）成分を配合することが好ましい。その他、添加剤として、顔料、染料、老化防止剤、酸化防止剤、帯電防止剤、酸化アンチモン、塩化パラフィン等の難燃剤など公知の添加剤を配合することができる。更に、チクソ性向上剤としてのポリエーテル、防かび剤、抗菌剤を配合することもできる。
また、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物には、必要に応じて有機溶剤を用いてもよい。有機溶剤としては、ｎ－ヘキサン、ｎ－ヘプタン、イソオクタン、イソドデカンなどの脂肪族炭化水素系化合物；トルエン、キシレンなどの芳香族炭化水素系化合物；ヘキサメチルジシロキサン、オクタメチルトリシロキサン、デカメチルテトラシロキサン、ドデカメチルペンタシロキサン、２－（トリメチルシロキシ）－１，１，１，２，３，３，３－ヘプタメチルトリシロキサンなどの鎖状シロキサン；オクタメチルシクロペンタシロキサン、デカメチルシクロペンタシロキサンなどの環状シロキサンなどが挙げられる。有機溶剤の量は本発明の効果を妨げない範囲で適宜調製すればよい。
［室温速硬化性オルガノポリシロキサン組成物の調製］
本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、（Ａ）成分の一部及び（Ｂ）成分の全部を含有してなり、（Ｃ）成分を含有しない第一剤と、（Ａ）成分の残部及び（Ｃ）成分の全部を含有してなり、（Ｂ）成分を含有しない第二剤とからなるものである。
第一剤は、（Ａ）成分の一部と、（Ｂ）成分の全部と、必要により（Ｄ）、（Ｅ）、（Ｆ）成分及びその他の成分の一部又は全部とを常法に従い混合することによって調製できる。また、第二剤は、（Ａ）成分の残部と、（Ｃ）成分の全部と、必要により（Ｄ）、（Ｅ）、（Ｆ）成分及びその他の成分の残部又は全部とを常法に従い混合することによって調製できる。
本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、（Ａ）成分の一部及び（Ｂ）成分の全部を含有してなり、（Ｃ）成分を含有しない第一剤と、（Ａ）成分の残部及び（Ｃ）成分の全部を含有してなり、（Ｂ）成分を含有しない第二剤とからなるものである。
第一剤は、（Ａ）成分の一部と、（Ｂ）成分の全部と、必要により（Ｄ）、（Ｅ）、（Ｆ）成分及びその他の成分の一部又は全部とを常法に従い混合することによって調製できる。また、第二剤は、（Ａ）成分の残部と、（Ｃ）成分の全部と、必要により（Ｄ）、（Ｅ）、（Ｆ）成分及びその他の成分の残部又は全部とを常法に従い混合することによって調製できる。
なお、（Ａ）成分は第一剤と第二剤に配合するが、この割合としては、第一剤と第二剤を質量比で１００：１０～１００：１００、特に１００：２５～１００：１００となるように配合することが作業性や第一剤と第二剤を混合する際の組成物の均一性（混ざり易さ）の点から好ましい。また、任意成分である（Ｄ）、（Ｅ）、（Ｆ）成分及びその他の成分は、第一剤と第二剤のどちらに配合してもよく、どちらか一方に配合しても両方に配合してもよいが、特には、第一剤に（Ｄ）、（Ｅ）、（Ｆ）成分を配合し、第二剤に（Ｄ）、（Ｆ）成分を配合することが好ましい。
本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、上記のようにして製造された第一剤及び第二剤を、湿分を避けた雰囲気下で保存することができる。
［室温速硬化性オルガノポリシロキサン組成物の硬化方法］
本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、これらを適する比率、具体的には第一剤と第二剤との割合が質量比で１：１～１０：１、特には１：１～４：１で混合することにより、通常、室温にて１０分～５日で硬化する。
本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、速硬化性を有するものであって、通常は３日～５日であるものが、１０分～３日と短時間で硬化するものである。
また、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、深部硬化性を有するものであって、通常は２時間であるものが、３０分と短時間で深部まで硬化するものである。
本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、これらを適する比率、具体的には第一剤と第二剤との割合が質量比で１：１～１０：１、特には１：１～４：１で混合することにより、通常、室温にて１０分～５日で硬化する。
本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、速硬化性を有するものであって、通常は３日～５日であるものが、１０分～３日と短時間で硬化するものである。
また、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、深部硬化性を有するものであって、通常は２時間であるものが、３０分と短時間で深部まで硬化するものである。
また、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、各種の基材表面上で硬化させて該基材上に良好に接着したオルガノポリシロキサン硬化物層（シリコーンゴム層）を形成することができる。ここで、基材としては、特に制限されるものではないが、金属（アルミニウム、鉄、ＳＵＳ、銅等）、有機樹脂（ポリカーボネート樹脂、アクリル樹脂、エポキシガラス（ガラエポ）樹脂等）、ガラスなどの種々の基材が適用できる。
［室温速硬化性オルガノポリシロキサン組成物の用途］
本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、特に、室温における空気中での速硬化性、深部硬化性に優れ、作業性も良好である。更に保存安定性を備える。そのため本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、長期間、例えば６か月間の貯蔵後でも、第一剤と第二剤とを混合し、空気中に曝すと速やかに硬化して、優れた物性を示す。即ち、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、耐熱性、耐水性、耐湿性に優れた硬化物となる。従って、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、耐熱性、耐水性、耐湿性が必要な個所のシール剤、コーティング剤、接着剤として有用である。とりわけ、耐湿性、耐水性が必要な建築用途、電気電子用接着剤用途として有効に使用することができる。あるいは、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物を硬化させて、耐熱性、耐水性、耐湿性を有する硬化物からなる成形物としてもよい。
なお、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物をシール剤、コーティング剤又は接着剤として使用する方法は、従来公知の方法に従えばよい。
本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、特に、室温における空気中での速硬化性、深部硬化性に優れ、作業性も良好である。更に保存安定性を備える。そのため本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、長期間、例えば６か月間の貯蔵後でも、第一剤と第二剤とを混合し、空気中に曝すと速やかに硬化して、優れた物性を示す。即ち、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、耐熱性、耐水性、耐湿性に優れた硬化物となる。従って、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物は、耐熱性、耐水性、耐湿性が必要な個所のシール剤、コーティング剤、接着剤として有用である。とりわけ、耐湿性、耐水性が必要な建築用途、電気電子用接着剤用途として有効に使用することができる。あるいは、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物を硬化させて、耐熱性、耐水性、耐湿性を有する硬化物からなる成形物としてもよい。
なお、本発明の二成分型室温速硬化性オルガノポリシロキサン組成物をシール剤、コーティング剤又は接着剤として使用する方法は、従来公知の方法に従えばよい。
以下、本発明を具体的に説明する実施例及び比較例を示すが、本発明は下記実施例に制限されるものではない。粘度は回転粘度計による測定値である。
［実施例１］
第一剤ａの調製
２３℃における粘度が５，０００ｍＰａ・ｓの分子鎖両末端がシラノール基（ケイ素原子に結合した水酸基）で封鎖されたジメチルポリシロキサン７５質量部と、２３℃における粘度が７００ｍＰａ・ｓの分子鎖両末端がシラノール基で封鎖されたジメチルポリシロキサン１５質量部と、ＢＥＴ比表面積が１３０ｍ2／ｇの乾式シリカ（煙霧質シリカ）８質量部と、ビス（トリメトキシシリルエテニル）ジメチルシラン３．５質量部と、γ－アミノプロピルトリエトキシシラン２質量部と、Ｎ－β（アミノエチル）γ－アミノプロピルトリメトキシシラン２質量部とを減圧下にて均一に混合して第一剤ａを調製した。
第一剤ａの調製
２３℃における粘度が５，０００ｍＰａ・ｓの分子鎖両末端がシラノール基（ケイ素原子に結合した水酸基）で封鎖されたジメチルポリシロキサン７５質量部と、２３℃における粘度が７００ｍＰａ・ｓの分子鎖両末端がシラノール基で封鎖されたジメチルポリシロキサン１５質量部と、ＢＥＴ比表面積が１３０ｍ2／ｇの乾式シリカ（煙霧質シリカ）８質量部と、ビス（トリメトキシシリルエテニル）ジメチルシラン３．５質量部と、γ－アミノプロピルトリエトキシシラン２質量部と、Ｎ－β（アミノエチル）γ－アミノプロピルトリメトキシシラン２質量部とを減圧下にて均一に混合して第一剤ａを調製した。
第二剤ｂの調製
２３℃における粘度が５，０００ｍＰａ・ｓの分子鎖両末端がシラノール基で封鎖されたジメチルポリシロキサン７５質量部と、２３℃における粘度が７００ｍＰａ・ｓの分子鎖両末端がシラノール基で封鎖されたジメチルポリシロキサン１５質量部と、ＢＥＴ比表面積が１３０ｍ2／ｇの乾式シリカ（煙霧質シリカ）８質量部と、ジメチルスズジネオデカノエート０．１質量部を減圧下にて均一に混合して第二剤ｂを調製した。
２３℃における粘度が５，０００ｍＰａ・ｓの分子鎖両末端がシラノール基で封鎖されたジメチルポリシロキサン７５質量部と、２３℃における粘度が７００ｍＰａ・ｓの分子鎖両末端がシラノール基で封鎖されたジメチルポリシロキサン１５質量部と、ＢＥＴ比表面積が１３０ｍ2／ｇの乾式シリカ（煙霧質シリカ）８質量部と、ジメチルスズジネオデカノエート０．１質量部を減圧下にて均一に混合して第二剤ｂを調製した。
上記第一剤ａと第二剤ｂを混合比（質量比）１：１で均一に混合して組成物１を製造した後、該組成物１を厚さが２．５ｍｍになるように基材上に塗布した。その後、２３℃，５０％ＲＨ条件下で、１日間及び３日間それぞれ静置して硬化させ、硬化物１－１、１－２を得た。
［実施例２］
第一剤ａのビス（トリメトキシシリルエテニル）ジメチルシランの代わりに、ビス（メチルジメトキシシリルエテニル）ジメチルシラン４．８質量部を用いた以外は実施例１と同様にして組成物２を製造し、同様にして硬化物２－１、２－２を得た。
第一剤ａのビス（トリメトキシシリルエテニル）ジメチルシランの代わりに、ビス（メチルジメトキシシリルエテニル）ジメチルシラン４．８質量部を用いた以外は実施例１と同様にして組成物２を製造し、同様にして硬化物２－１、２－２を得た。
［実施例３］
第二剤ｂのジメチルスズジネオデカノエートの代わりに、Ｎ，Ｎ，Ｎ’，Ｎ’－テトラメチルグアニジルプロピルトリメトキシシラン１質量部を用いた以外は実施例１と同様にして組成物３－１、３－２を製造し、同様にして硬化物３を得た。
第二剤ｂのジメチルスズジネオデカノエートの代わりに、Ｎ，Ｎ，Ｎ’，Ｎ’－テトラメチルグアニジルプロピルトリメトキシシラン１質量部を用いた以外は実施例１と同様にして組成物３－１、３－２を製造し、同様にして硬化物３を得た。
［比較例１］
第一剤ａのビス（トリメトキシシリルエテニル）ジメチルシランの代わりに、メチルトリメトキシシラン２．７質量部を用いた以外は実施例１と同様にして組成物４－１、４－２を製造し、同様にして硬化物４を得た。
第一剤ａのビス（トリメトキシシリルエテニル）ジメチルシランの代わりに、メチルトリメトキシシラン２．７質量部を用いた以外は実施例１と同様にして組成物４－１、４－２を製造し、同様にして硬化物４を得た。
［比較例２］
第一剤ａのビス（トリメトキシシリルエテニル）ジメチルシランの代わりに、ビニルトリメトキシシラン２．９質量部を用いた以外は実施例１と同様にして組成物５を製造し、同様にして硬化物５－１、５－２を得た。
第一剤ａのビス（トリメトキシシリルエテニル）ジメチルシランの代わりに、ビニルトリメトキシシラン２．９質量部を用いた以外は実施例１と同様にして組成物５を製造し、同様にして硬化物５－１、５－２を得た。
［試験方法］
上記実施例１～３及び比較例１、２で調製した各組成物を用いて、下記に示す方法により、硬化性、ゴム物性、接着性を評価した。
上記実施例１～３及び比較例１、２で調製した各組成物を用いて、下記に示す方法により、硬化性、ゴム物性、接着性を評価した。
［硬化性］
実施例１～３及び比較例１、２で調製した各組成物を用いて、ＪＩＳ Ａ－５７５８に規定する方法に準じてタックフリータイム（指触乾燥時間）を測定した。
また、内径が１０ｍｍのガラスシャーレに実施例１～３及び比較例１、２で調製した各組成物を充填し、２３℃，５０％ＲＨで２０分後に空気に触れた表面部分から硬化した部分までの厚さを測定し、深部硬化性を評価した。
実施例１～３及び比較例１、２で調製した各組成物を用いて、ＪＩＳ Ａ－５７５８に規定する方法に準じてタックフリータイム（指触乾燥時間）を測定した。
また、内径が１０ｍｍのガラスシャーレに実施例１～３及び比較例１、２で調製した各組成物を充填し、２３℃，５０％ＲＨで２０分後に空気に触れた表面部分から硬化した部分までの厚さを測定し、深部硬化性を評価した。
［ゴム物性］
実施例１～３及び比較例１、２で調製した調製直後の各組成物を厚さ２ｍｍのシート状に押し出し、２３℃，５０％ＲＨの空気に曝し、次いで、該シートを同じ雰囲気下に１日間又は３日間放置して得た硬化物のゴム物性（硬さ、切断時伸び、引張強さ）を、ＪＩＳ Ｋ－６２４９に準拠して測定した。なお、硬さは、ＪＩＳ Ｋ－６２４９のデュロメーターＡ硬度計を用いて測定した。
実施例１～３及び比較例１、２で調製した調製直後の各組成物を厚さ２ｍｍのシート状に押し出し、２３℃，５０％ＲＨの空気に曝し、次いで、該シートを同じ雰囲気下に１日間又は３日間放置して得た硬化物のゴム物性（硬さ、切断時伸び、引張強さ）を、ＪＩＳ Ｋ－６２４９に準拠して測定した。なお、硬さは、ＪＩＳ Ｋ－６２４９のデュロメーターＡ硬度計を用いて測定した。
［接着性］
実施例１～３及び比較例１，２で調製した組成物より、幅２５ｍｍ、長さ１００ｍｍのアルミニウム又はガラス被着体として、それぞれ同材の被着体同士を、上記組成物を用いて、各試験片の接着面積２．５ｍｍ2、接着厚さ１ｍｍで接着したせん断（シア）接着試験体を作製し、２３℃，５０％ＲＨで１日間又は３日間養生した後、これらの試験体を用いてアルミニウム又はガラスに対するせん断接着力をＪＩＳ Ｋ－６２４９に規定する方法に準じて測定した。
実施例１～３及び比較例１，２で調製した組成物より、幅２５ｍｍ、長さ１００ｍｍのアルミニウム又はガラス被着体として、それぞれ同材の被着体同士を、上記組成物を用いて、各試験片の接着面積２．５ｍｍ2、接着厚さ１ｍｍで接着したせん断（シア）接着試験体を作製し、２３℃，５０％ＲＨで１日間又は３日間養生した後、これらの試験体を用いてアルミニウム又はガラスに対するせん断接着力をＪＩＳ Ｋ－６２４９に規定する方法に準じて測定した。
実施例１～３の試験結果を表１に、比較例１、２の試験結果を表２に示す。
なお、本発明は、上記実施形態に限定されるものではない。上記実施形態は例示であり、本発明の特許請求の範囲に記載された技術的思想と実質的に同一な構成を有し、同様な作用効果を奏するものは、いかなるものであっても本発明の技術的範囲に包含される。
Claims (10)
- （Ａ）下記一般式（１）又は（２）で示されるオルガノポリシロキサン：１００質量部、
（Ｂ）下記一般式（３）で示される加水分解性オルガノシラン化合物及び／又はその部分加水分解縮合物：第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して０．１～３０質量部
を含有してなる第一剤と、
（Ａ）下記一般式（１）又は（２）で示されるオルガノポリシロキサン：１０～１００質量部、
（Ｃ）硬化触媒：第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して０．００１～１０質量部
を含有してなる第二剤と
からなるものである二成分型室温速硬化性オルガノポリシロキサン組成物。 - 更に、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して（Ｄ）充填剤を、第一剤及び第二剤中にそれぞれ０～１，０００質量部含有する（ただし、少なくとも第一剤、第二剤のいずれか一方に０．１質量部以上含有する）ものである請求項１に記載の二成分型室温速硬化性オルガノポリシロキサン組成物。
- 更に、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して（Ｅ）接着促進剤を、第一剤及び第二剤中にそれぞれ０～３０質量部含有する（ただし、少なくとも第一剤、第二剤のいずれか一方に０．００１質量部以上含有する）ものである請求項１又は２に記載の二成分型室温速硬化性オルガノポリシロキサン組成物。
- 更に、第一剤及び第二剤中に含まれる（Ａ）成分の合計１００質量部に対して（Ｆ）下記一般式（４）で示されるオルガノポリシロキサンを、第一剤及び第二剤中にそれぞれ０～１００質量部含有する（ただし、少なくとも第一剤、第二剤のいずれか一方が０．０１質量部以上含有する）ものである請求項１～３のいずれか１項に記載の二成分型室温速硬化性オルガノポリシロキサン組成物。
- 第一剤と第二剤との割合が質量比で１：１～１０：１である請求項１～４のいずれか１項に記載の二成分型室温速硬化性オルガノポリシロキサン組成物。
- 請求項１～５のいずれか１項に記載の二成分型室温速硬化性オルガノポリシロキサン組成物を含有するシール剤。
- 請求項１～５のいずれか１項に記載の二成分型室温速硬化性オルガノポリシロキサン組成物を含有するコーティング剤。
- 請求項１～５のいずれか１項に記載の二成分型室温速硬化性オルガノポリシロキサン組成物を含有する接着剤。
- 請求項１～５のいずれか１項に記載の二成分型室温速硬化性オルガノポリシロキサン組成物の硬化物。
- 請求項９に記載の二成分型室温速硬化性オルガノポリシロキサン組成物の硬化物からなる成形物。