WO2021205750A1 - Solution électrolytique pour dispositif électrochimique, et dispositif électrochimique - Google Patents

Solution électrolytique pour dispositif électrochimique, et dispositif électrochimique Download PDF

Info

Publication number
WO2021205750A1
WO2021205750A1 PCT/JP2021/005681 JP2021005681W WO2021205750A1 WO 2021205750 A1 WO2021205750 A1 WO 2021205750A1 JP 2021005681 W JP2021005681 W JP 2021005681W WO 2021205750 A1 WO2021205750 A1 WO 2021205750A1
Authority
WO
WIPO (PCT)
Prior art keywords
lithium
additive
electrolytic solution
salt
concentration
Prior art date
Application number
PCT/JP2021/005681
Other languages
English (en)
Japanese (ja)
Inventor
続木武男
加納幸司
Original Assignee
太陽誘電株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 太陽誘電株式会社 filed Critical 太陽誘電株式会社
Publication of WO2021205750A1 publication Critical patent/WO2021205750A1/fr

Abstract

La présente solution électrolytique pour dispositifs électrochimiques comprend un solvant et un électrolyte dissous dans celui-ci, la solution électrolytique étant caractérisée en ce que le solvant comprend un carbonate cyclique et un carbonate à chaîne et l'électrolyte comprend un sel de lithium à base d'imide et un sel de lithium n'étant pas à base d'imide et en ce qu'un additif comprenant du difluorophosphate de lithium, de l'oxalatophosphate de lithium et de l'oxalatoborate de lithium a été ajouté à la solution électrolytique et la concentration de l'additif dans la solution électrolytique est de 0,5 à 2,0 % en poids, le rapport entre le poids du difluorophosphate de lithium et le poids total de l'oxalatophosphate de lithium et de l'oxalatoborate de lithium étant de 1:9 à 3:7 et le rapport entre le poids de l'oxalatophosphate de lithium et le poids de l'oxalatoborate de lithium étant de 1:1 à 3:1.　
PCT/JP2021/005681 2020-04-07 2021-02-16 Solution électrolytique pour dispositif électrochimique, et dispositif électrochimique WO2021205750A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2020069022A JP2021166244A (ja) 2020-04-07 2020-04-07 電気化学デバイス用電解液および電気化学デバイス
JP2020-069022 2020-04-07

Publications (1)

Publication Number Publication Date
WO2021205750A1 true WO2021205750A1 (fr) 2021-10-14

Family

ID=78022234

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2021/005681 WO2021205750A1 (fr) 2020-04-07 2021-02-16 Solution électrolytique pour dispositif électrochimique, et dispositif électrochimique

Country Status (2)

Country Link
JP (1) JP2021166244A (fr)
WO (1) WO2021205750A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114566712A (zh) * 2022-03-03 2022-05-31 湖北亿纬动力有限公司 含有二氟磷酸锂的高电压锂离子电池电解液及其制备方法和锂离子电池

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2010079565A1 (fr) * 2009-01-06 2010-07-15 株式会社村田製作所 Accumulateur à électrolyte non aqueux
JP2016100100A (ja) * 2014-11-19 2016-05-30 セントラル硝子株式会社 非水電解液電池用電解液及びリチウム非水電解液電池
JP2017004947A (ja) * 2015-06-09 2017-01-05 ステラケミファ株式会社 二次電池用非水電解液及びそれを備えた二次電池
WO2019054418A1 (fr) * 2017-09-12 2019-03-21 セントラル硝子株式会社 Additif d'électrolyte non aqueux, électrolyte non aqueux, et batterie à électrolyte non aqueux
JP2019175578A (ja) * 2018-03-27 2019-10-10 三井化学株式会社 電池用非水電解液及びリチウム二次電池
JP2020053488A (ja) * 2018-09-25 2020-04-02 太陽誘電株式会社 電気化学デバイス用電解液および電気化学デバイス

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2010079565A1 (fr) * 2009-01-06 2010-07-15 株式会社村田製作所 Accumulateur à électrolyte non aqueux
JP2016100100A (ja) * 2014-11-19 2016-05-30 セントラル硝子株式会社 非水電解液電池用電解液及びリチウム非水電解液電池
JP2017004947A (ja) * 2015-06-09 2017-01-05 ステラケミファ株式会社 二次電池用非水電解液及びそれを備えた二次電池
WO2019054418A1 (fr) * 2017-09-12 2019-03-21 セントラル硝子株式会社 Additif d'électrolyte non aqueux, électrolyte non aqueux, et batterie à électrolyte non aqueux
JP2019175578A (ja) * 2018-03-27 2019-10-10 三井化学株式会社 電池用非水電解液及びリチウム二次電池
JP2020053488A (ja) * 2018-09-25 2020-04-02 太陽誘電株式会社 電気化学デバイス用電解液および電気化学デバイス

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN114566712A (zh) * 2022-03-03 2022-05-31 湖北亿纬动力有限公司 含有二氟磷酸锂的高电压锂离子电池电解液及其制备方法和锂离子电池

Also Published As

Publication number Publication date
JP2021166244A (ja) 2021-10-14

Similar Documents

Publication Publication Date Title
KR101954600B1 (ko) 축전 장치용 수계 전해액, 및 당해 수계 전해액을 포함하는 축전 장치
KR100570359B1 (ko) 하이브리드 전지
JP6818723B2 (ja) 電気化学デバイス用電解液および電気化学デバイス
US10483049B2 (en) Lithium ion capacitor
JP5165862B2 (ja) 非水電解液およびそれを用いた電気化学エネルギー蓄積デバイス
JP7352781B2 (ja) 電気化学デバイスおよびその製造方法
JP4281030B2 (ja) 非水電解質電池
WO2021205750A1 (fr) Solution électrolytique pour dispositif électrochimique, et dispositif électrochimique
CN109559903B (zh) 电化学器件用电解液和电化学器件
JPH1012272A (ja) 非水電解液二次電池
JP2016167476A (ja) 蓄電デバイス
US10580589B2 (en) Lithium ion capacitor
JP6718905B2 (ja) リチウムイオンキャパシタ
JP2019179609A (ja) 電池用非水電解液及びリチウム二次電池
CN111354977A (zh) 锂离子电池电解液，其制备方法，包含其的锂电池
JPWO2019188760A1 (ja) 電気化学デバイス
WO2022004166A1 (fr) Dispositif électrochimique
WO2021200778A1 (fr) Dispositif électrochimique
WO2020262440A1 (fr) Dispositif électrochimique
JP7200465B2 (ja) 電池用非水電解液及びリチウム二次電池
JP2018190569A (ja) 電池用非水電解液、電池用添加剤、及びリチウム二次電池
JP2019169700A (ja) 電気化学デバイス用電解液および電気化学デバイス
JP2016086153A (ja) 電気化学デバイス
JP2021177470A (ja) 非水電解液、半固体電解質層、二次電池用シート及び二次電池
KR100706714B1 (ko) 하이브리드 전지

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 21783991

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 21783991

Country of ref document: EP

Kind code of ref document: A1