WO2021182518A1 - Ｆｅ－Ｃｏ系合金棒材の製造方法およびＦｅ－Ｃｏ系合金棒材 - Google Patents

Ｆｅ－Ｃｏ系合金棒材の製造方法およびＦｅ－Ｃｏ系合金棒材 Download PDF

Info

Publication number
WO2021182518A1
WO2021182518A1 PCT/JP2021/009570 JP2021009570W WO2021182518A1 WO 2021182518 A1 WO2021182518 A1 WO 2021182518A1 JP 2021009570 W JP2021009570 W JP 2021009570W WO 2021182518 A1 WO2021182518 A1 WO 2021182518A1
Authority
WO
WIPO (PCT)
Prior art keywords
heating
hot
bar
based alloy
alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Ceased
Application number
PCT/JP2021/009570
Other languages
English (en)
French (fr)
Inventor
藤吉　優
上坂　修治郎
興司 小林
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Proterial Ltd
Original Assignee
Hitachi Metals Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hitachi Metals Ltd filed Critical Hitachi Metals Ltd
Priority to CN202180019418.5A priority Critical patent/CN115279926B/zh
Priority to US17/909,438 priority patent/US12522898B2/en
Priority to JP2022507248A priority patent/JP7746984B2/ja
Publication of WO2021182518A1 publication Critical patent/WO2021182518A1/ja
Anticipated expiration legal-status Critical
Priority to US19/404,024 priority patent/US20260098325A1/en
Ceased legal-status Critical Current

Abstract

優れた磁気特性を安定して得ることが可能な、Ｆｅ－Ｃｏ系合金棒材とその製造方法を提供する。　Ｆｅ－Ｃｏ系合金の熱間圧延材に対して、前記熱間圧延材の温度を５００～９００℃に加熱しながら引張応力を付与する加熱真直工程を含む、Ｆｅ－Ｃｏ系合金棒材の製造方法。好ましくは、前記加熱真直工程の加熱手段に、通電加熱を用いる。また、ＧＯＳ値（Ｇｒａｉｎ　Ｏｒｉｅｎｔａｔｉｏｎ　Ｓｐｒｅａｄ）が０．５°以上を示す結晶粒を面積比率で２０％以上有する、Ｆｅ－Ｃｏ系合金棒材。

Description

Ｆｅ－Ｃｏ系合金棒材の製造方法およびＦｅ－Ｃｏ系合金棒材
　本発明は、Ｆｅ－Ｃｏ系合金棒材の製造方法およびＦｅ－Ｃｏ系合金棒材に関するものである。
　優れた磁気特性を有する合金として知られる、パーメンダー（パーメンジュール）に代表されるＦｅ－Ｃｏ系合金の棒材は、センサーや円筒形磁気シールド、電磁弁、磁心等様々な製品に使用されている。このＦｅ－Ｃｏ系合金棒材の製造方法としては、例えば特許文献１に、インゴットを１０００℃～１１００℃に加熱後、φ９０ｍｍ程度のビレットに熱間加工し、表面の傷等の除去を旋盤で行い、１０００℃～１１００℃に加熱後、φ６～φ９ｍｍ程度に熱間圧延した素材（棒材）を作製する旨が記載されている。
特開平７－１６６２３９号公報
　上述した製品の高性能化に伴い、素材にもさらなる磁気特性の向上が求められている。特許文献１に記載されているような従来の製法では安定して高い磁気特性を得ることが困難であり、さらなる検討の余地が残されている。
　そこで本発明の目的は、優れた磁気特性を安定して得ることが可能な、Ｆｅ－Ｃｏ系合金棒材とその製造方法を提供することである。
　本発明の一態様は、Ｆｅ－Ｃｏ系合金の熱間圧延材に対して、前記熱間圧延材の温度を５００～９００℃に加熱しながら引張応力を付与する加熱真直工程を含む、Ｆｅ－Ｃｏ系合金棒材の製造方法である。
　好ましくは、前記熱間圧延材の温度を５００～８５０℃とする。
　好ましくは、前記加熱真直工程の加熱手段に、通電加熱を用いる。
　好ましくは、前記加熱真直工程の前に、溶体化処理を行う。
　本発明の別の一態様は、ＧＯＳ（Ｇｒａｉｎ　Ｏｒｉｅｎｔａｔｉｏｎ　Ｓｐｒｅａｄ）値が０．５°以上となる結晶粒を面積比率で２０％以上有する、Ｆｅ－Ｃｏ系合金棒材である。
　好ましくは、平均結晶粒度番号が６．０以上９．５以下である。
　好ましくは、平均結晶粒度番号が６．０以上８．５以下である。
　本発明によれば、優れた磁気特性を有するＦｅ－Ｃｏ系合金棒材を、安定して得ることができる。
　以下に本発明の実施形態について説明する。まず、本発明のＦｅ－Ｃｏ系合金棒材の製造方法について説明する。本発明のＦｅ－Ｃｏ系合金棒材は、断面形状が円形（楕円形含む）、角形のものを含む直棒状の棒材である。本実施形態の棒材は特に記載が無い限り、断面形状が円形である丸棒である。
　＜熱間圧延材組成＞
　まず本実施形態では、Ｆｅ－Ｃｏ系合金の熱間圧延材を準備する。本発明におけるＦｅ－Ｃｏ系合金とは、質量％でＦｅ＋Ｃｏが９５％以上であり、且つ、Ｃｏを２５～６０％含有する合金材料のことを指す。これにより、高い磁束密度を発揮することができる。
　次に、本発明のＦｅ－Ｃｏ系合金に含有されていても良い元素について説明する。本発明のＦｅ－Ｃｏ系合金は加工性や磁気特性を向上させるために、Ｖ、Ｓｉ、Ｍｎ、Ａｌ、Ｚｒ、Ｂ、Ｎｉ、Ｔａ、Ｎｂ、Ｗ、Ｔｉ、Ｍｏ、Ｃｒの一種または二種以上の元素を、質量％にて合計で最大５．０％まで含有しても良い。その他、不可避的に含まれる不純物元素として、例えばＣ、Ｓ、Ｐ、Ｏが挙げられ、例えばそのそれぞれの上限を０．１％とすることが好ましい。
　本実施形態では、Ｆｅ－Ｃｏ系合金棒材の中間素材として、前述成分を有するＦｅ－Ｃｏ系合金鋼塊から得られたビレットに熱間圧延を施し、熱間圧延材を得ることができる。この中間素材には熱間圧延による酸化層が形成されていることから、例えば、機械的、或いは化学的に酸化層を除去する研磨工程を導入してもよい。
この熱間圧延材は、例えば、Ｆｅ－Ｃｏ系合金棒材に相当した“熱間圧延棒材”の形状を有する。そして、後工程における加工性を考慮して、直径５～２０ｍｍとしてもよい。なお丸棒以外の棒材に関しては、横断面の円相当径が５～２０ｍｍとしてもよい。
　＜溶体化処理工程＞
　本実施形態では、後述する加熱真直工程を行う前の熱間圧延材に対して、少なくとも１回の溶体化処理を行ってもよい。この溶体化処理を行うことによって、熱間圧延材の成分偏析を除去して磁気特性を向上させ、加工性を改善する効果も期待できるため好ましい。この溶体化処理時の加熱温度は、低すぎると加工性を劣化させる傾向にあり、高すぎると磁気特性の劣化を招くため、８００～１０５０℃の温度で実施することが好ましい。より好ましい温度の下限は、８５０℃である。より好ましい温度の上限は、９５０℃であり、さらに好ましい温度の上限は９００℃である。また加熱時間は１０分～６０分に設定することもできる。また溶体化処理工程では、有害な析出物を析出させずに固溶させ、規則化を抑制して加工性を向上させるため、加熱後に急冷処理を実施する。なお、溶体化処理工程を省略しても、後述する加熱真直工程の加熱温度を調整することで、本発明の効果を得ることができる。
　＜加熱真直工程＞
　本実施形態では上述した熱間圧延材に対して、加熱しながら引張応力を付与する、加熱真直工程を行う。このとき、熱間圧延材が“棒材”の形状であるなら、この熱間圧延棒材の長さ方向に引張って、上記の引張応力を付与する。この工程により、熱間圧延材に残留歪みを付与させつつ、非常に良好な磁気特性および真直性を有する棒材を得ることができる。このときの加熱温度は、５００～９００℃に設定する。５００℃より低い場合、加工性が低下し、引張応力を付与する際、棒材が破断するおそれがある。一方で加熱温度が９００℃超の場合、熱間圧延材に好ましい残留歪みを付与させることができない。加熱真直工程における好ましい加熱温度の下限は６００℃であり、より好ましくは７００℃である。また、好ましい加熱温度の上限は８５０℃であり、より好ましくは８３０℃であり、さらに好ましくは８００℃である。なお、上述した溶体化処理工程を省略する場合、好ましい加熱温度の下限は７００℃であり、より好ましくは７３０℃であり、さらに好ましくは７４０℃である。
　この加熱真直工程には、通電加熱、誘導加熱等の加熱手段を用いることができるが、熱間圧延材における結晶粒の磁化容易軸を一定方向へ揃えやすくする効果を得たり、急速（例えば１分以内。）かつ均一に材料を目標温度まで加熱できるという利点から、通電加熱を適用することが好ましい。また、加熱真直工程時の張力は、所望の残留歪みをより確実に得るために、１～４ＭＰａに調整することが好ましい。また、加熱真直工程前の全長に対して３～１０％の伸長に調整することが好ましい。
　本実施形態では加熱真直工程を終えた棒材に対して、例えばセンタレスグラインダを用いたセンタレス研磨を実施してもよい。これにより棒材表層の黒皮を除去し、形状の真円度や公差精度をより高めることができる。本発明では、加熱真直工程により棒材の真直度が向上しているため、長さが１０００ｍｍ以上の長尺棒材も切断せずにセンタレス研磨を実施することができる。
　続いて、上述した本発明の製造方法によって得ることが出来る、本発明のＦｅ－Ｃｏ系合金棒材について説明する。本発明のＦｅ－Ｃｏ系合金棒材は、ＧＯＳ（Ｇｒａｉｎ　Ｏｒｉｅｎｔａｔｉｏｎ　Ｓｐｒｅａｄ）値が０．５°以上となる結晶粒を面積比率で２０％以上有する。このＧＯＳ値は、従来知られる「ＳＥＭ－ＥＢＳＤ法（電子線後方散乱回折法）」によって測定することができ、結晶粒を構成する点（ピクセル）の方位差を計算することで導出することができる。ＧＯＳ値により得られる結晶方位差は加工によって合金中に付与される歪みを示す指標であり、ＧＯＳ値が０．５°以上となる結晶粒を面積比率で２０％以上有する場合、結晶粒成長の駆動力が棒材に導入されており、良好な磁気特性を得る利点がある。ＧＯＳ値が０．５°以上の領域が２０％未満の場合、結晶粒成長の駆動力が不十分な棒材のため、良好な磁気特性を得ることができない。ＧＯＳ値が０．５°以上となる結晶粒において、好ましくは面積比率で４０％以上であり、より好ましい面積比率は５０％以上であり、さらに好ましい面積比率は６０％以上であり、よりさらに好ましい面積比率は７０％以上であり、特に好ましい面積比率は８０％以上であり、最も好ましい面積比率は９０％以上である。なお上記のＧＯＳ値が０．５°以上となる結晶粒は、棒材の軸直角方向断面で観察することができる。また、面積比率を観察する断面は、軸直角方向断面と軸方向断面もあるが、棒材の軸直角方向断面および軸方向断面で観察した場合の両方において、面積比率で２０％以上（より好ましくは４０％以上、さらに好ましくは５０％以上、よりさらに好ましくは６０％以上、特に好ましくは７０％以上、最も好ましくは８０％以上）であることが好ましい。これは熱間圧延工程時に母材に生じた圧延痕による歪みの影響は棒材の軸方向断面において観察されやすく、軸直角方向断面で観察した面積比率よりも軸方向断面で観察した面積比率が小さくなる可能性があるためである。よって、面積比率が小さい傾向にある軸方向断面でも、上記の面積比率の数値を満たしていれば、本発明の効果をより確実に達成することができる。
　また、本発明のＦｅ－Ｃｏ系合金棒材は、平均結晶粒度番号が６．０以上９．５以下であることが好ましい。これにより磁性焼鈍後に高い磁気特性を発揮しやすくなるとともに、加工性もより向上する傾向にある。より好ましい平均結晶粒度番号の下限は６．５以上であり、より好ましい平均結晶粒度番号の上限は９．０以下である。さらに好ましい平均結晶粒度番号の上限は８．５以下であり、よりさらに好ましくは８．０以下である。なお平均結晶粒度番号は、ＪＩＳ　Ｇ　０５５１に基づいて測定することができる。そして、棒材の軸直角方向断面または軸方向断面で測定することができる。
（実施例１）
　表１に示す組成を有するＦｅ－Ｃｏ系合金鋼塊を分塊後、熱間圧延を行ってΦ１１．５ｍｍの熱間圧延棒材を準備した。
＜試料Ｎｏ．１、試料Ｎｏ．２＞
前述の熱間圧延棒材を８５０℃で加熱した後急冷する溶体化処理を行った後、棒材の温度が７５０℃になるように加熱しながら張力２．７ＭＰａの条件で、その長さ方向に熱間圧延棒材を引っ張る加熱真直工程を実施し、本発明例である試料Ｎｏ．１、２のＦｅ－Ｃｏ系合金棒材を作製した。
＜試料Ｎｏ．３＞
前述の熱間圧延棒材に溶体化処理を行わず、加熱真直工程を実施して本発明例である試料Ｎｏ．３のＦｅ－Ｃｏ系合金棒材を作製した。加熱真直工程の条件は試料Ｎｏ．１と同じとした。
＜試料Ｎｏ．４＞
前述の熱間圧延棒材に試料Ｎｏ．１と同条件の溶体化処理を行い、加熱真直工程を行わず、その他の工程は本発明と同じである比較例である試料Ｎｏ．４のＦｅ－Ｃｏ系合金棒材も作製した。
Figure JPOXMLDOC01-appb-T000001
　続いて本発明例と比較例の試料の平均結晶粒度、ＧＯＳ値および直流磁気特性を確認した。平均結晶粒度は、横断面（軸直角方向断面）において、オリンパス製の光学顕微鏡を用い、５００μｍ×３５０μｍの視野を１０視野観察し、ＪＩＳ　Ｇ　０５５１に則り、結晶粒度標準図プレートＩにて粒度番号を判定した。ＧＯＳ値については、ＺＥＩＳＳ製の電界放射型走査電子顕微鏡とＴＳＬ社製のＥＢＳＤ測定・解析システムＯＩＭ（Ｏｒｉｅｎｔａｔｉｏｎ－Ｉｍａｇｉｎｇ－Ｍｉｃｒｏｇｒａｐｈ）とを用いて行った。試料Ｎｏ．１と試料Ｎｏ．４に関しては横断面（軸直角方向断面）を観察し、試料Ｎｏ．２と試料Ｎｏ．３は上述した試料の横断面に加えて、縦断面（中心軸を通る軸方向断面）も観察した。測定視野は１００μｍ×１００μｍであり、隣接するピクセル間のステップ距離は０．２μｍとした。また、隣接するピクセル間の方位差が５°以上の境界を結晶粒界と判別する条件で観察を行い、得られたＧＯＳ値のマップから、ＧＯＳ値が０．５°以上の結晶粒が占める観察視野全体に対する面積率を求めた。直流磁気特性については、得られた棒材から試料を採取後、８５０℃×３時間の磁性焼鈍を施し、直流磁化特定試験装置を用いて最大透磁率と保磁力とを測定した。表２に観察結果を示す。
Figure JPOXMLDOC01-appb-T000002
　表２より、本発明例である試料Ｎｏ．１および試料Ｎｏ．２は平均結晶粒度番号が比較例よりも小さく（結晶粒径が比較例よりも大きく）、溶体化処理を行っていない試料Ｎｏ．３は比較例と平均結晶粒度番号が同じであった。ＧＯＳ値が０．５°以上となる結晶粒の面積比率について、本発明例が比較例よりも非常に大きい値であることが確認できた。磁気特性に関して、試料Ｎｏ．１～Ｎｏ．３は比較例よりも高透磁率かつ低保磁力であった。このことから、本発明例は何れも比較例より優れた磁気特性を有していることが確認できた。
（実施例２）
　表３に示す組成を有するＦｅ－Ｃｏ系合金鋼塊を分塊後、熱間圧延を行ってΦ１１．５ｍｍの熱間圧延棒材を準備した。その後溶体化処理を行わず、棒材の温度が表４に示した温度となるように加熱しつつ張力２．７ＭＰａの条件で加熱真直工程を実施し、試料Ｎｏ．５～７のＦｅ－Ｃｏ合金棒材を作製した。表４の結果より、棒材温度５００～９００℃で加熱真直工程を実施した試料Ｎｏ．５～７は、いずれも低保磁力であり、優れた磁気特性を有していることが確認できた。
Figure JPOXMLDOC01-appb-T000003
Figure JPOXMLDOC01-appb-T000004
 

Claims (7)

  1. 　Ｆｅ－Ｃｏ系合金の熱間圧延材に対して、
    　前記熱間圧延材の温度を５００～９００℃に加熱しながら引張応力を付与する加熱真直工程を含む、Ｆｅ－Ｃｏ系合金棒材の製造方法。
  2. 　前記熱間圧延材の温度を５００～８５０℃とする、請求項１に記載のＦｅ－Ｃｏ系合金棒材の製造方法。
  3. 　前記加熱真直工程の加熱手段に、通電加熱を用いる、請求項１または請求項２に記載のＦｅ－Ｃｏ系合金棒材の製造方法。
  4. 　前記加熱真直工程の前に、溶体化処理を行う、請求項１ないし請求項３のいずれかに記載のＦｅ－Ｃｏ系合金棒材の製造方法。
  5. 　ＧＯＳ値（Ｇｒａｉｎ　Ｏｒｉｅｎｔａｔｉｏｎ　Ｓｐｒｅａｄ）が０．５°以上を示す結晶粒を面積比率で２０％以上有する、Ｆｅ－Ｃｏ系合金棒材。
  6. 　平均結晶粒度番号が６．０以上９．５以下である、請求項５に記載のＦｅ－Ｃｏ系合金棒材。
  7. 　平均結晶粒度番号が６．０以上８．５以下である、請求項５に記載のＦｅ－Ｃｏ系合金棒材。

     
PCT/JP2021/009570 2020-03-10 2021-03-10 Ｆｅ－Ｃｏ系合金棒材の製造方法およびＦｅ－Ｃｏ系合金棒材 Ceased WO2021182518A1 (ja)