WO2021153044A1 - 二次電池用正極活物質、二次電池用正極および二次電池 - Google Patents

二次電池用正極活物質、二次電池用正極および二次電池 Download PDF

Info

Publication number
WO2021153044A1
WO2021153044A1 PCT/JP2020/046511 JP2020046511W WO2021153044A1 WO 2021153044 A1 WO2021153044 A1 WO 2021153044A1 JP 2020046511 W JP2020046511 W JP 2020046511W WO 2021153044 A1 WO2021153044 A1 WO 2021153044A1
Authority
WO
WIPO (PCT)
Prior art keywords
positive electrode
secondary battery
metal alkoxide
active material
electrode active
Prior art date
Application number
PCT/JP2020/046511
Other languages
English (en)
French (fr)
Inventor
一顕 遠藤
博信 久保田
Original Assignee
株式会社村田製作所
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社村田製作所 filed Critical 株式会社村田製作所
Priority to JP2021574513A priority Critical patent/JP7331958B2/ja
Priority to EP20917128.9A priority patent/EP4063325A1/en
Priority to CN202080091213.3A priority patent/CN114902449B/zh
Publication of WO2021153044A1 publication Critical patent/WO2021153044A1/ja
Priority to US17/875,978 priority patent/US20220384793A1/en

Abstract

二次電池は、二次電池用正極と、負極と、電解液とを備え、その二次電池用正極は、二次電池用正極活物質を含む。この二次電池用正極活物質は、１５μｍ以上３０μｍ以下のメジアン径Ｄ５０を有すると共にリチウム含有化合物を含む複数の第１粒子と、１μｍ以上１０μｍ以下のメジアン径Ｄ５０を有すると共にリチウム含有化合物を含む中心部とその中心部の表面に設けられた被覆部とを含む複数の第２粒子とを備える。この被覆部は、中心部に近い側から順に、金属原子にアルキル基が結合されていない第１金属アルコキシドの反応物を含む下地層と、金属原子にアルキル基が結合されている第２金属アルコキシドの反応物を含むと共にその第２金属アルコキシドの反応物が第１金属アルコキシドの反応物に結合されている表面層とを含む。

Description

二次電池用正極活物質、二次電池用正極および二次電池
　本技術は、二次電池用正極活物質、二次電池用正極活物質および二次電池に関する。
　携帯電話機などの多様な電子機器が普及しているため、小型かつ軽量であると共に高エネルギー密度を得ることが可能である電源として、二次電池の開発が進められている。この二次電池は、正極（二次電池用正極）および負極と共に電解液を備えており、その正極は、正極活物質（二次電池用正極活物質）を含んでいる。
　二次電池の構成は、電池特性に影響を及ぼすため、その二次電池の構成に関しては、様々な検討がなされている。
　具体的には、塗工性に優れた正極活物質を得るために、ポリアニオン系化合物および炭素からなる大粒径の正極活物質粒子と、ポリアニオン系化合物および炭素からなる小粒径の正極活物質粒子のカーボン複合化物とが用いられている（例えば、特許文献１参照。）。被覆層の厚さを均一化するために、Ｓｉ・遷移金属表面組成比が８０％以上である被覆層により被覆されたリチウム－遷移金属複合酸化物粉末が用いられている（例えば、特許文献２参照。）。高温下の連続充電時においてガス発生を抑制するために、シランカップリング剤により表面処理された層（表面処理層）を有する正極活物質が用いられている（例えば、特許文献３参照。）。優れた電気伝導度を得るために、ポリアニオン系化合物および炭素からなる粒子が親油化処理剤により被覆された正極活物質が用いられている（例えば、特許文献４参照。）。二次電池の膨れを抑制するために、リチウムイオンを吸蔵放出可能である正極材料を含む粒子と、その正極材料と結合可能であるシランカップリング剤と、そのシランカップリング剤と結合可能である高分子化合物とから得られる正極活物質が用いられている（例えば、特許文献５参照。）。
特開２０１１－０３４７７６号公報 特開２０１２－１９９１０１号公報 特開２０１２－１６９２４９号公報 特開２０１１－０４９１６１号公報 特開２０１３－１９１５３９号公報
　二次電池の電池特性を改善するために様々な検討がなされているが、その二次電池のサイクル特性および負荷特性は未だ十分でないため、改善の余地がある。
　本技術はかかる問題点に鑑みてなされたもので、その目的は、優れたサイクル特性および優れた負荷特性を得ることが可能である二次電池用正極活物質、二次電池用正極および二次電池を提供することにある。
　本技術の一実施形態の二次電池用正極活物質は、１５μｍ以上３０μｍ以下のメジアン径Ｄ５０を有すると共にリチウム含有化合物を含む複数の第１粒子と、１μｍ以上１０μｍ以下のメジアン径Ｄ５０を有すると共にリチウム含有化合物を含む中心部とその中心部の表面に設けられた被覆部とを含む複数の第２粒子とを備えたものである。この被覆部は、中心部に近い側から順に、金属原子にアルキル基が結合されていない第１金属アルコキシドの反応物を含む下地層と、金属原子にアルキル基が結合されている第２金属アルコキシドの反応物を含むと共にその第２金属アルコキシドの反応物が第１金属アルコキシドの反応物に結合されている表面層とを含む。
　本技術の一実施形態の二次電池用正極は、二次電池用正極活物質を含む正極活物質層を備え、その二次電池用正極活物質が上記した本技術の一実施形態の二次電池用正極活物質の構成と同様の構成を有するものである。
　本技術の一実施形態の二次電池は、二次電池用正極と負極と電解液とを備え、その二次電池用正極が上記した本技術の一実施形態の二次電池用正極の構成と同様の構成を有するものである。
　本技術の一実施形態の二次電池用正極活物質、二次電池用正極または二次電池によれば、その二次電池用正極活物質が複数の第１粒子（メジアン径Ｄ５０＝１５μｍ～３０μｍ）および複数の第２粒子（メジアン径＝１μｍ～１０μｍ）を含んでおり、その第２粒子の被覆部が下地層（第１金属アルコキシドの反応物）および表面層（第２金属アルコキシドの反応物）を含んでいるので、優れたサイクル特性および優れた負荷特性を得ることができる。
　なお、本技術の効果は、必ずしもここで説明された効果に限定されるわけではなく、後述する本技術に関連する一連の効果のうちのいずれの効果でもよい。
本技術の一実施形態における二次電池用正極活物質の構成を模式的に表す断面図である。 図１に示した小粒径粒子の表面近傍の構成を模式的に表す図である。 図１に示した小粒径粒子の表面近傍の構成を模式的に表す他の図である。 本技術の一実施形態における二次電池（二次電池用正極）の構成を表す斜視図である。 図４に示した電池素子の構成を表す断面図である。 二次電池の適用例（電池パック：単電池）の構成を表すブロック図である。 二次電池の適用例（電池パック：組電池）の構成を表すブロック図である。 二次電池の適用例（電動車両）の構成を表すブロック図である。
　以下、本技術の一実施形態に関して、図面を参照しながら詳細に説明する。なお、説明する順序は、下記の通りである。

　１．二次電池用正極活物質
　　１－１．構成
　　１－２．動作
　　１－３．製造方法
　　１－４．作用および効果
　２．二次電池（二次電池用正極）
　　２－１．構成
　　２－２．動作
　　２－３．製造方法
　　２－４．作用および効果
　３．変形例
　４．二次電池の用途
　　４－１．電池パック（単電池）
　　４－２．電池パック（組電池）
　　４－３．電動車両
　　４－４．その他
＜１．二次電池用正極活物質＞
　まず、本技術の一実施形態の二次電池用正極活物質に関して説明する。
　ここで説明する二次電池用正極活物質（以下、単に「正極活物質」と呼称する。）は、電極反応物質を吸蔵放出可能である物質であり、二次電池に用いられる。この正極活物質が用いられる二次電池の詳細に関しては、後述する。
　電極反応物質の種類は、特に限定されないが、アルカリ金属およびアルカリ土類金属などの軽金属である。アルカリ金属は、リチウム、ナトリウムおよびカリウムなどであると共に、アルカリ土類金属は、ベリリウム、マグネシウムおよびカルシウムなどである。
　以下では、電極反応物質がリチウムである場合を例に挙げる。すなわち、以下で説明する正極活物質は、リチウムを吸蔵放出可能である物質であり、その正極活物質では、リチウムがイオン状態で吸蔵放出される。
＜１－１．構成＞
　図１は、正極活物質の断面構成を模式的に表していると共に、図２および図３のそれぞれは、図１に示した小粒径粒子２００の表面近傍の構成を模式的に表している。ただし、図２では、線図を用いて被覆部２２０の構成を示していると共に、図３では、線図と共に化学式を用いて被覆部２２０の構成を示している。
　この正極活物質は、複数の粒子状（複数の正極活物質粒子）であり、その複数の正極活物質粒子は、図１に示したように、平均粒径、より具体的にはメジアン径Ｄ５０（μｍ）が互いに異なる２種類の複数の粒子（複数の大粒径粒子１００および複数の小粒径粒子２００）を備えている。ただし、図１では、複数の大粒径粒子１００のうちの１個の大粒径粒子１００だけを示していると共に、複数の小粒径粒子２００のうちの１個の小粒径粒子２００だけを示している。
　この「複数の正極活物質粒子は平均粒径が互いに異なる２種類の複数の粒子を含んでいる」とは、その複数の正極活物質粒子の粒度分布（粒子径分布）を測定した際に、上記した２種類の複数の粒子に起因した２個のピークが検出されることを意味している。
［複数の大粒径粒子］
　複数の大粒径粒子１００は、相対的に大きいメジアン径Ｄ５０を有する複数の第１粒子であり、より具体的には、複数の小粒径粒子２００のメジアン径Ｄ５０よりも大きいメジアン径Ｄ５０を有している。
　大粒径粒子１００は、図１に示したように、小粒径粒子２００とは異なり、後述する被覆部２２０に相当する構成要素を含んでいない粒子である。具体的には、複数の大粒径粒子１００のメジアン径Ｄ５０は、１５μｍ～３０μｍである。複数の小粒径粒子２００のメジアン径Ｄ５０との関係において、複数の大粒径粒子１００のメジアン径Ｄ５０が適正化されるため、その複数の大粒径粒子１００の間の隙間に小粒径粒子２００が充填されやすくなるからである。
　この大粒径粒子１００は、リチウム含有化合物のうちのいずれか１種類または２種類以上を含んでいる。リチウム含有化合物は、リチウムを構成元素として含む化合物の総称であり、そのリチウム含有化合物の種類は、特に限定されない。ここでは、リチウム含有化合物は、リチウムおよび遷移金属元素を構成元素として含む化合物（リチウム遷移金属化合物）であり、その遷移金属元素の種類は、１種類でもよいし、２種類以上でもよい。ただし、リチウム遷移金属化合物は、さらに、リチウムおよび遷移金属元素以外の任意の元素のうちのいずれか１種類または２種類以上を含んでいてもよい。リチウム遷移金属化合物の種類は、特に限定されないが、具体的には、酸化物、リン酸化合物、ケイ酸化合物およびホウ酸化合物などである。
　中でも、リチウム含有化合物（リチウム遷移金属化合物）は、式（１）～式（３）のそれぞれで表される化合物のうちのいずれか１種類または２種類以上を含んでいることが好ましい。高いエネルギー密度が得られるからである。ただし、式（１）～式（３）のそれぞれに示したリチウムの組成は、充放電の状態に応じて異なるが、ａの値は、完全放電状態の値である。
　Ｌｉa Ｎｉ(1-b-c) Ｍｎb Ｍ１c Ｏ(2-d) Ｘe 　・・・（１）
（Ｍ１は、長周期型周期表の２族～１５族に属する元素（ただし、ＮｉおよびＭｎを除く。）のうちの少なくとも１種である。Ｘは、長周期型周期表の１６族および１７族に属する元素（ただし、Ｏを除く。）のうちの少なくとも１種である。ａ、ｂ、ｃ、ｄおよびｅは、０≦ａ≦１．５、０≦ｂ≦１、０≦ｃ≦１、－０．１≦ｄ≦０．２および０≦ｅ≦０．２を満たす。）
　Ｌｉa Ｃｏ(1-b) Ｍ２b Ｏ(2-c) 　・・・（２）
（Ｍ２は、Ｖ、Ｃｕ、Ｚｒ、Ｚｎ、Ｍｇ、Ａｌ、Ｇａ、ＹおよびＦｅのうちの少なくとも１種である。ａ、ｂおよびｃは、０．９≦ａ≦１．１、０≦ｂ≦０．３および－０．１≦ｃ≦０．１を満たす。）
　Ｌｉa Ｎｉb Ｃｏc Ｍｎd Ｍ３(1-b-c-d) Ｏ(2-e) 　・・・（３）
（Ｍ３は、Ｖ、Ｃｕ、Ｚｒ、Ｚｎ、Ｍｇ、Ａｌ、Ｇａ、ＹおよびＦｅのうちの少なくとも１種である。ａ、ｂ、ｃ、ｄおよびｅは、－０．１≦ａ≦０．１、０．９≦ｂ≦１．１、０＜ｃ＜１、０＜ｄ＜１、０＜ｅ＜０．５および０≦１－ｂ－ｃ－ｄを満たす。）
　式（１）に示した化合物は、主要な遷移金属元素としてニッケルを含むリチウム複合酸化物（ニッケル系リチウム複合酸化物）である。ニッケル系リチウム複合酸化物の具体例は、特に限定されないが、ＬｉＮｉＯ2 、ＬｉＮｉ0.5 Ｃｏ0.2 Ｍｎ0.3 Ｏ2 およびＬｉＮｉ0.8 Ｃｏ0.15Ａｌ0.05Ｏ2 などである。
　式（２）に示した化合物は、主要な遷移金属元素としてコバルトを含むリチウム複合酸化物（コバルト系リチウム複合酸化物）である。コバルト系リチウム複合酸化物の具体例は、特に限定されないが、ＬｉＣｏＯ2 およびＬｉＣｏ0.98Ａｌ0.01Ｍｇ0.01Ｏ2 などである。
　式（３）に示した化合物は、主要な遷移金属元素としてニッケル、コバルトおよびマンガンを含むリチウム複合酸化物（三元系リチウム複合酸化物）である。三元系リチウム複合酸化物の具体例は、特に限定されないが、ＬｉＮｉ0.5 Ｃｏ0.2 Ｍｎ0.3 Ｏ2 、ＬｉＮｉ0.33Ｃｏ0.33Ｍｎ0.33Ｏ2 、Ｌｉ1.2 Ｍｎ0.52Ｃｏ0.175 Ｎｉ0.1 Ｏ2 およびＬｉ1.15（Ｍｎ0.65Ｎｉ0.22Ｃｏ0.13）Ｏ2 などである。
［複数の小粒径粒子］
　複数の小粒径粒子２００は、相対的に小さいメジアン径Ｄ５０を有する複数の第２粒子であり、より具体的には、複数の大粒径粒子１００のメジアン径Ｄ５０よりも小さいメジアン径Ｄ５０を有している。
　具体的には、複数の小粒径粒子２００のメジアン径Ｄ５０は、１μｍ～１０μｍである。複数の大粒径粒子１００のメジアン径Ｄ５０との関係において、複数の小粒径粒子２００のメジアン径Ｄ５０が適正化されるため、その複数の大粒径粒子１００の間の隙間に小粒径粒子２００が充填されやすくなるからである。
　小粒径粒子２００は、図１に示したように、中心部２１０および被覆部２２０を含んでいるため、その被覆部２２０により中心部２１０の表面が被覆されている被覆粒子である。
（中心部）
　中心部２１０は、リチウム含有化合物を含んでおり、そのリチウム含有化合物に関する詳細は、上記した通りである。ただし、中心部２１０に含まれているリチウム含有化合物の種類と大粒径粒子１００に含まれているリチウム含有化合物の種類とは、互いに同じでもよいし、互いに異なってもよい。
（被覆部）
　被覆部２２０は、中心部２１０の表面に設けられているため、その中心部２１０の表面を被覆している。ただし、被覆部２２０は、中心部２１０の表面のうちの全体を被覆していてもよいし、中心部２１０の表面のうちの一部だけを被覆していてもよい。後者（一部被覆）の場合には、互いに離隔された複数の場所において複数の被覆部２２０が中心部２１０の表面を被覆していてもよい。
　この被覆部２２０は、図２および図３に示したように、下地層２２１および表面層２２２を含んでおり、その下地層２２１および表面層２２２は、中心部２１０に近い側から順に配置されている。すなわち、被覆部２２０は、中心部２１０に近い側から順に下地層２２１および表面層２２２が積層された２層構造を有している。
　ここで説明する被覆部２２０は、下地層２２１および表面層２２２を含んでいるため、後述するように、第１金属アルコキシドの反応物および第２金属アルコキシドの反応物を含む有機無機ハイブリッド膜である。
（下地層）
　下地層２２１は、第１金属アルコキシドの反応物のうちのいずれか１種類または２種類以上を含んでいる。この第１金属アルコキシドは、金属原子にアルコキシ基が結合されている化合物である。より具体的には、第１金属アルコキシドは、後述する第２金属アルコキシドとは異なり、金属原子にアルコキシ基が結合されていると共に金属原子にアルキル基が結合されていない化合物である。
　被覆部２２０が下地層２２１（第１金属アルコキシドの反応物）を含んでいるのは、その下地層２２１により小粒径粒子２００のイオン伝導性が担保されるからである。この場合には、後述するように、第１金属アルコキシドの反応物が複数の細孔２２１Ｋを有しているため、その複数の細孔２２１Ｋを経由してリチウムイオンが移動しやすくなる（式（４１）参照）。
　金属原子の種類は、金属アルコキシドを形成可能である金属原子であれば、特に限定されないが、具体的には、ケイ素原子、チタン原子、アルミニウム原子およびジルコニウム原子のうちのいずれかである。中でも、ケイ素原子が好ましい。上記した複数の細孔２２１Ｋを有する第１金属アルコキシドの反応物が容易かつ安定に形成されやすくなるからである。
　具体的には、第１金属アルコキシドは、式（４）で表される化合物のうちのいずれか１種類または２種類以上を含んでいる。ただし、第１金属アルコキシドが複数のＲ１１を含んでいる場合には、その複数のＲ１１の種類は、互いに同じでもよいし、互いに異なってもよい。もちろん、複数のＲ１１のうちの一部だけが互いに同じ種類でもよい。
　Ｍ１１－ＯＲ１１a 　・・・（４）
（Ｍ１１は、金属原子である。Ｒ１１は、炭素数が１以上１０以下のアルキル基である。ａは、Ｍ１１の価数に応じて決定される値である。）
　金属原子（Ｍ１１）に関する詳細は、上記した通りであり、すなわち、金属原子は、ケイ素原子、チタン原子、アルミニウム原子およびジルコニウム原子のうちのいずれかであり、中でも、ケイ素原子が好ましい。
　アルキル基（Ｒ１１）は、炭素および水素により構成される１価の基であり、直鎖状でもよいし、１個または２個以上の側鎖を有する分岐状でもよい。アルキル基の具体例は、炭素数が１～１０であるため、メチル基、エチル基、プロピル基およびブチル基などである。
　ただし、炭素数が３以上であるアルキル基は、上記したように、直鎖状でもよいし、分岐状でもよい。具体的には、炭素数が３であるプロピル基を例に挙げると、そのプロピル基は、ｎ－プロピル基でもよいし、イソプロピル基でもよい。また、炭素数が４であるブチル基を例に挙げると、そのブチル基は、ｎ－ブチル基でもよいし、ｓｅｃ－ブチル基でもよいし、イソブチル基でもよいし、ｔｅｒｔ－ブチル基でもよい。
　ａの値は、金属原子の価数の値と同じ値である。より具体的には、金属原子が上記したケイ素原子などである場合には、３または４である。
　金属原子がケイ素原子である場合における第１金属アルコキシドの具体例は、特に限定されないが、Ｓｉ－（ＯＣＨ3 ）4 、Ｓｉ－（ＯＣ2 Ｈ5 ）4 、Ｓｉ－（ＯＣ3 Ｈ7 ）4 およびＳｉ－（ＯＣ4 Ｈ9 ）4 などである。
　金属原子がチタン原子である場合における第１金属アルコキシドの具体例は、特に限定されないが、Ｔｉ－（ＯＣＨ3 ）4 、Ｔｉ－（ＯＣ2 Ｈ5 ）4 、Ｔｉ－（ＯＣ3 Ｈ7 ）4 およびＴｉ－（ＯＣ4 Ｈ9 ）4 などである。
　金属原子がアルミニウム原子である場合における第１金属アルコキシドの具体例は、特に限定されないが、Ａｌ－（ＯＣＨ3 ）3 、Ａｌ－（ＯＣ2 Ｈ5 ）3 、Ａｌ－（ＯＣ3 Ｈ7 ）3 およびＡｌ－（ＯＣ4 Ｈ9 ）3 などである。
　金属原子がジルコニウム原子である場合における第１金属アルコキシドの具体例は、特に限定されないが、Ｚｒ－（ＯＣＨ3 ）4 、Ｚｒ－（ＯＣ2 Ｈ5 ）4 、Ｚｒ－（ＯＣ3 Ｈ7 ）4 およびＺｒ－（ＯＣ4 Ｈ9 ）4 などである。
　第１金属アルコキシドの反応物の構成は、特に限定されない。ここで、金属原子がケイ素原子であり、より具体的には第１金属アルコキシドがＳｉ－（ＯＣ2 Ｈ5 ）4 である場合を例に挙げると、その第１金属アルコキシドの反応物は、式（４１）で表される構成を有している。
Figure JPOXMLDOC01-appb-C000001
　式（４１）に示した第１金属アルコキシドの反応物では、ケイ素原子同士が酸素原子を介して互いに結合されているため、第１金属アルコキシドの反応物は、複数のケイ素原子－酸素原子結合を含んでいる。これにより、第１金属アルコキシドの反応物は、主にケイ素原子および酸素原子により形成された網目状の構造を有している。
　この第１金属アルコキシドの反応物では、式（４１）に示したように、ケイ素原子および酸素原子が交互に結合されることにより、複数の環が形成されているため、各環の内側に空間（細孔２２１Ｋ）が形成されている。このため、第１金属アルコキシドの反応物は、複数の細孔２２１Ｋを有している。
　これにより、下地層２２１は、図２および図３に示したように、上記した網目状の構造（ケイ素原子および酸素原子）を母体とする層であり、より具体的には、中心部２１０の表面を被覆する被膜状の層である。
　もちろん、ここでは具体的な構成を示さないが、金属原子がチタン原子である場合においても同様に、第１金属アルコキシドの反応物は、複数のチタン原子－酸素原子結合を含む網目状の構造を有しているため、複数の細孔２２１Ｋを有している。
　金属原子がアルミニウム原子である場合においても同様に、第１金属アルコキシドの反応物は、複数のアルミニウム原子－酸素原子結合を含む網目状の構造を有しているため、複数の細孔２２１Ｋを有している。
　金属原子がジルコニウム原子である場合においても同様に、第１金属アルコキシドの反応物は、複数のジルコニウム原子－酸素原子結合を含む網目状の構造を有しているため、複数の細孔２２１Ｋを有している。
　被覆部２２０中における下地層２２１（第１金属アルコキシドの反応物）の含有量、すなわち被覆部２２０の重量に対する第１金属アルコキシドの反応物の重量の割合（重量％）は、特に限定されないが、中でも、２重量％～９５重量％であることが好ましい。第１金属アルコキシドの反応物により、上記した網目状の構造が形成されやすくなるからである。
　なお、下地層２２１は、さらに、第３金属アルコキシドの反応物のうちのいずれか１種類または２種類以上を含んでいることが好ましい。この第３金属アルコキシドは、２つの金属原子がアルキレン基を介して互いに結合されている化合物である。より具体的には、第３金属アルコキシドは、上記した第１金属アルコキシドとは異なり、２個の金属原子の間にアルキレン基が介在している化合物である。
　下地層２２１がさらに第３金属アルコキシドの反応物を含んでいると、小粒径粒子２００のイオン伝導性がより向上する。この場合には、後述するように、複数の細孔２２１Ｋを有する第３金属アルコキシドの反応物において、その細孔２２１Ｋの孔径が増大するため、その細孔２２１Ｋを経由してリチウムイオンがより移動しやすくなる（式（５１）参照）。
　具体的には、第３金属アルコキシドは、式（６）で表される化合物である。ただし、Ｍ１３の種類およびＭ１４の種類は、互いに同じでもよいし、互いに異なってもよい。ここで説明したことは、Ｒ１５の種類およびＲ１６の種類に関しても同様である。また、第３金属アルコキシドが複数のＲ１５を含んでいる場合には、その複数のＲ１５の種類は、互いに同じでもよいし、互いに異なってもよい。もちろん、複数のＲ１５のうちの一部だけが互いに同じ種類でもよい。ここで説明したことは、第３金属アルコキシドが複数のＲ１６を含んでいる場合において、その複数のＲ１６の種類に関しても同様である。
　（Ｒ１５Ｏ）c －Ｍ１３－Ｒ１４－Ｍ１４－（ＯＲ１６）d 　・・・（６）
（Ｍ１３およびＭ１４のそれぞれは、金属原子である。Ｒ１４は、炭素数が１以上１０以下のアルキレン基であると共に、Ｒ１５およびＲ１６のそれぞれは、炭素数が１以上１０以下のアルキル基である。ｃは、Ｍ１３の価数に応じて決定される値であると共に、ｄは、Ｍ１４の価数に応じて決定される値である。）
　金属原子（Ｍ１３およびＭ１４）およびアルキル基（Ｒ１５およびＲ１６）のそれぞれに関する詳細は、上記した通りである。ｃの値は、金属原子（Ｍ１３）の価数－１に相当する値であり、より具体的には、金属原子が上記したケイ素原子などである場合には、２または３である。ｄの値は、金属原子（Ｍ１４）の価数－１に相当する値であり、より具体的には、金属原子が上記したケイ素原子などである場合には、２または３である。
　アルキレン基（Ｒ１４）は、炭素および水素により構成される２価の基であり、直鎖状でもよいし、１個または２個以上の側鎖を有する分岐状でもよい。アルキレン基の具体例は、炭素数が１～１０であるため、エチレン基、ブチレン基およびヘキセン基などである。
　金属原子がケイ素原子である場合における第３金属アルコキシドの具体例は、特に限定されないが、（Ｈ3 ＣＯ）3 －Ｓｉ－Ｃ2 Ｈ4 －Ｓｉ－（ＯＣＨ3 ）3 、（Ｈ3 ＣＯ）3 －Ｓｉ－Ｃ4 Ｈ8 －Ｓｉ－（ＯＣＨ3 ）3 および（Ｈ3 ＣＯ）3 －Ｓｉ－Ｃ6 Ｈ12－Ｓｉ－（ＯＣＨ3 ）3 などである。
　金属原子がチタン原子である場合における第３金属アルコキシドの具体例は、特に限定されないが、（Ｈ3 ＣＯ）3 －Ｔｉ－Ｃ2 Ｈ4 －Ｔｉ－（ＯＣＨ3 ）3 、（Ｈ3 ＣＯ）3 －Ｔｉ－Ｃ4 Ｈ8 －Ｔｉ－（ＯＣＨ3 ）3 および（Ｈ3 ＣＯ）3 －Ｔｉ－Ｃ6 Ｈ12－Ｔｉ－（ＯＣＨ3 ）3 などである。
　金属原子がアルミニウム原子である場合における第３金属アルコキシドの具体例は、特に限定されないが、（Ｈ3 ＣＯ）2 －Ａｌ－Ｃ2 Ｈ4 －Ａｌ－（ＯＣＨ3 ）2 、（Ｈ3 ＣＯ）2 －Ａｌ－Ｃ4 Ｈ8 －Ａｌ－（ＯＣＨ3 ）2 および（Ｈ3 ＣＯ）2 －Ａｌ－Ｃ6 Ｈ12－Ａｌ－（ＯＣＨ3 ）2 などである。
　金属原子がジルコニウム原子である場合における第３金属アルコキシドの具体例は、特に限定されないが、（Ｈ3 ＣＯ）3 －Ｚｒ－Ｃ2 Ｈ4 －Ｚｒ－（ＯＣＨ3 ）3 、（Ｈ3 ＣＯ）3 －Ｚｒ－Ｃ4 Ｈ8 －Ｚｒ－（ＯＣＨ3 ）3 および（Ｈ3 ＣＯ）3 －Ｚｒ－Ｃ6 Ｈ12－Ｚｒ－（ＯＣＨ3 ）3 などである。
　第３金属アルコキシドの反応物の構成は、特に限定されない。ここで、金属原子がケイ素原子であり、より具体的には第３金属アルコキシドが（Ｈ3 ＣＯ）3 －Ｓｉ－Ｃ2 Ｈ4 －Ｓｉ－（ＯＣＨ3 ）3 である場合を例に挙げると、その第３金属アルコキシドの反応物は、式（５１）で表される構成を有している。
Figure JPOXMLDOC01-appb-C000002
　式（５１）に示した第３金属アルコキシドの反応物では、一部のケイ素原子同士がアルキレン基を介して互いに結合されていることを除いて、式（４１）に示した第１金属アルコキシドの反応物の構成と同様の構成を有している。すなわち、第３金属アルコキシドの反応物では、ケイ素原子同士が酸素原子を介して互いに結合されているため、その第３金属アルコキシドの反応物は、複数のケイ素原子－酸素原子結合を含んでいる。また、第３金属アルコキシドの反応物では、ケイ素原子同士がアルキレン基（炭素原子）を介して互いに結合されているため、その第３金属アルコキシドの反応物は、複数のケイ素原子－炭素原子結合を含んでいる。これにより、第３金属アルコキシドの反応物は、網目状の構造を有しているため、複数の細孔２２１Ｋを有している。
　この第３金属アルコキシドの反応物では、第１金属アルコキシドの反応物と比較して、２個のケイ素原子の間にスペーサ２２１Ｓ（アルキレン基）が介在している分だけ細孔２２１Ｋの孔径が増加している。よって、第３金属アルコキシドの反応物では、細孔２２１Ｋを経由してリチウムイオンがより移動しやすくなっている。
　もちろん、ここでは具体的な構成を示さないが、金属原子がチタン原子である場合においても同様に、第３金属アルコキシドの反応物は、複数のチタン原子－酸素原子結合および複数のチタン原子－炭素原子結合を含む網目状の構造を有しているため、複数の細孔２２１Ｋを有していると共に、その細孔２２１Ｋの孔径は、スペーサ２２１Ｓを利用して増加している。
　金属原子がアルミニウム原子である場合においても同様に、第３金属アルコキシドの反応物は、複数のアルミニウム原子－酸素原子結合および複数のアルミニウム原子－炭素原子結合を含む網目状の構造を有しているため、複数の細孔２２１Ｋを有していると共に、その細孔２２１Ｋの孔径は、スペーサ２２１Ｓを利用して増加している。
　金属原子がジルコニウム原子である場合においても同様に、第３金属アルコキシドの反応物は、複数のジルコニウム原子－酸素原子結合および複数のジルコニウム原子－炭素原子結合を含む網目状の構造を有しているため、複数の細孔２２１Ｋを有していると共に、その細孔２２１Ｋの孔径は、スペーサ２２１Ｓを利用して増加している。
　被覆部２２０中における下地層２２１（第３金属アルコキシドの反応物）の含有量、すなわち被覆部２２０の重量に対する第３金属アルコキシドの反応物の重量の割合（重量％）は、特に限定されないが、中でも、２重量％～９０重量％であることが好ましい。第３金属アルコキシドの反応物により、十分な孔径を有する複数の細孔２２１Ｋが形成されやすくなるからである。
（表面層）
　表面層２２２は、第２金属アルコキシドの反応物のうちのいずれか１種類または２種類以上を含んでいる。この第２金属アルコキシドは、金属原子にアルコキシ基が結合されている化合物である。より具体的には、第２金属アルコキシドは、上記した第１金属アルコキシドとは異なり、金属原子にアルコキシ基が結合されていると共にアルキル基も結合されている化合物である。第２金属アルコキシドの反応物は、第１金属アルコキシドの反応物に結合されているため、表面層２２２は、下地層２２１に連結されている。
　被覆部２２０が表面層２２２（第２金属アルコキシドの反応物）を含んでいるのは、その表面層２２２により小粒径粒子２００の充填性が担保されるからである。この場合には、後述するように、第２金属アルコキシドの反応物が複数の炭化水素鎖２２２Ｎを有しているため、表面層２２２の表面自由エネルギーが低下する。これにより、小粒径粒子２００の表面の滑り性が向上するため、複数の大粒径粒子１００の間の隙間に小粒径粒子２００が充填されやすくなる（図２参照）。
　具体的には、第２金属アルコキシドは、式（５）で表される化合物である。ただし、第２金属アルコキシドが複数のＲ１３を含んでいる場合には、その複数のＲ１３の種類は、互いに同じでもよいし、互いに異なってもよい。もちろん、複数のＲ１３のうちの一部だけが互いに同じ種類でもよい。
　Ｒ１２－Ｍ１２－ＯＲ１３b 　・・・（５）
（Ｍ１２は、金属原子である。Ｒ１２は、炭素数が８以上３０以下のアルキル基であると共に、Ｒ１３は、炭素数が１以上１０以下のアルキル基である。ｂは、Ｍ１２の価数に応じて決定される値である。）
　金属原子（Ｍ１２）およびアルキル基（Ｒ１２およびＲ１３）のそれぞれに関する詳細は、上記した通りである。アルキル基（Ｒ１２）の具体例は、炭素数が８～３０であるため、オクチル基、デシル基、ヘキサデシル基、エイコシル基およびトリアコンチル基などである。ｂの値は、金属原子の価数－１に相当する値であり、より具体的には、金属原子が上記したケイ素原子などである場合には、２または３である。
　ここで、Ｍ１２がケイ素原子である場合を例に挙げると、第２金属アルコキシドの具体例は、特に限定されないが、Ｈ17Ｃ8 －Ｓｉ－（ＯＣＨ3 ）3 、Ｈ21Ｃ10－Ｓｉ－（ＯＣＨ3 ）3 、Ｈ33Ｃ16－Ｓｉ－（ＯＣＨ3 ）3 、Ｈ41Ｃ20－Ｓｉ－（ＯＣＨ3 ）3 およびＨ61Ｃ30Ｓｉ－（ＯＣＨ3 ）3 などである。
　第２金属アルコキシドの反応物の構成は、特に限定されない。ここで、第２金属アルコキシドがＨ33Ｃ16Ｓｉ－（ＯＣ3 Ｈ7 ）3 である場合を例に挙げると、その第２金属アルコキシドの反応物は、図２および図３に示した構成を有している。
　図２および図３に示したように、第２金属アルコキシドの反応物の一端部は、下地層２２１に含まれている第１金属アルコキシドの反応物（網目状の構造）に結合されていると共に、第２金属アルコキシドの反応物の他端部（複数の炭化水素鎖２２２Ｎである－Ｃ16Ｈ33）は、下地層２２１から離れる方向に向かって放射状に延在している。複数の炭化水素鎖２２２Ｎは、間隔を介して互いに離隔されながら配列されている。なお、図３中のＹは、第２金属アルコキシドの反応物の一部を表している。
　これにより、表面層２２２は、図２および図３に示したように、上記した複数の炭化水素鎖２２２Ｎを母体とする層であり、より具体的には、中心部２１０から放射状に延在する髭状の層である。
　被覆部２２０中における表面層２２２（第２金属アルコキシドの反応物）の含有量、すなわち被覆部２２０の重量に対する第２金属アルコキシドの反応物の重量の割合（重量％）は、特に限定されないが、中でも、５重量％～９０重量％であることが好ましい。第２金属アルコキシドの反応物において、上記した複数の炭化水素鎖２２２Ｎが安定に配列されやすくなるからである。
［混合比］
　複数の大粒径粒子１００と複数の小粒径粒子２００との混合比は、特に限定されない。中でも、複数の大粒径粒子１００の重量と複数の小粒径粒子２００の重量との総和に対する複数の小粒径粒子２００の重量の割合（重量％）は、１重量％～３０重量％であることが好ましい。複数の大粒径粒子１００の間の隙間に複数の小粒径粒子２００が充填されやすくなる。
　上記した割合は、割合（重量％）＝［複数の小粒径粒子２００の重量／（複数の大粒径粒子１００の重量＋複数の小粒径粒子２００の重量）］×１００により算出される。
＜１－２．動作＞
　この正極活物質（複数の大粒径粒子１００および複数の小粒径粒子２００）では、電極反応時において、リチウムが吸蔵放出される。この場合には、リチウムがイオン状態で吸蔵放出される。
＜１－３．製造方法＞
　正極活物質を製造する場合には、最初に、複数の大粒径粒子１００（粉末状のリチウム含有化合物）と、複数の中心部２１０（粉末状のリチウム含有化合物）とを準備する。
　続いて、浸積法を用いて中心部２１０の表面に被覆部２２０を形成することにより、複数の小粒径粒子２００を製造する。
　具体的には、最初に、アルカリ性溶媒中に、複数の中心部２１０と、第１金属アルコキシドと、第２金属アルコキシドとを投入したのち、その溶媒を撹拌する。このアルカリ性溶媒は、エタノールとアンモニア水との混合物などのうちのいずれか１種類または２種類以上である。これにより、アルカリ性溶媒中において、複数の中心部２１０が分散されると共に、第１金属アルコキシドおよび第２金属アルコキシドのそれぞれが溶解されるため、準備溶液が調製される。この準備溶液中では、第１金属アルコキシドおよび第２金属アルコキシドのそれぞれが溶解された溶液中に、複数の中心部２１０が分散されるため、その溶液が中心部２１０の表面に付着する。
　この場合には、アルカリ性溶媒中に、さらに、第３金属アルコキシドを投入してもよい。これにより、アルカリ性溶媒中において、さらに第３金属アルコキシドが溶解された準備溶液が調製される。
　続いて、準備溶液中から複数の中心部２１０を濾別したのち、洗浄用の溶媒を用いて複数の中心部２１０を洗浄する。この洗浄用の溶媒は、アセトンなどの有機溶剤のうちのいずれか１種類または２種類以上である。
　最後に、複数の中心部２１０を加熱することにより、その複数の中心部２１０を乾燥させる。これにより、中心部２１０の表面において第１金属アルコキシドおよび第２金属アルコキシドのそれぞれが反応するため、その第１金属アルコキシドの反応物により下地層２２１が形成されると共に、その第２金属アルコキシドの反応物により表面層２２２が形成される。この場合には、第１金属アルコキシドの反応物と第２金属アルコキシドの反応物とが互いに結合されるため、表面層２２２が下地層２２１に連結される。よって、下地層２２１および表面層２２２を含む被覆部２２０が中心部２１０の表面に形成されるため、複数の小粒径粒子２００が得られる。
　なお、アルカリ性溶媒中において、さらに、第３金属アルコキシドが溶解された準備溶液を用いた場合には、第１金属アルコキシドの反応物と共に第３金属アルコキシドの反応物により下地層２２１が形成される。
　上記した手順により、複数の小粒径粒子２００を得たのち、複数の大粒径粒子１００と複数の小粒径粒子２００とを互いに混合させる。これにより、複数の大粒径粒子１００および複数の小粒径粒子２００を含む正極活物質が製造される。
　なお、ここでは、複数の小粒径粒子２００を製造するために浸漬法を用いたが、その複数の小粒径粒子２００を製造するために、浸漬法以外の他の方法のうちのいずれか１種類または２種類以上を用いてもよい。この他の方法は、塗布法およびスプレー法などである。塗布法を用いる場合には、中心部２１０の表面に準備溶液を塗布する。スプレー法を用いる場合には、中心部２１０の表面に準備溶液を噴き付ける。
＜１－４．作用および効果＞
　この正極活物質によれば、複数の大粒径粒子１００（メジアン径Ｄ５０＝１５μｍ～３０μｍ）および複数の小粒径粒子２００（メジアン径Ｄ５０＝１μｍ～１０μｍ）を含んでおり、その小粒径粒子２００（中心部２１０および被覆部２２０）の被覆部２２０が下地層２２１（第１金属アルコキシドの反応物）および表面層２２２（第２金属アルコキシドの反応物）を含んでいる。
　この場合には、上記したように、第１金属アルコキシドの反応物を含む下地層２２１において、小粒径粒子２００のイオン伝導性が担保されると共に、第２金属アルコキシドの反応物を含む表面層２２２において、小粒径粒子２００の充填性が担保される。
　詳細には、表面層２２２が第２金属アルコキシドの反応物（複数の炭化水素鎖２２２Ｎ）を含んでいるため、その表面層２２２の表面自由エネルギーが低下することに起因して小粒径粒子２００の表面の滑り性が向上する。これにより、複数の大粒径粒子１００の間に設けられた隙間の内部に小粒径粒子２００が入りやすくなるため、その隙間に小粒径粒子２００が充填されやすくなる。よって、正極活物質（複数の大粒径粒子１００および複数の小粒径粒子２００）の充填性が向上するため、高いエネルギー密度が得られる。
　しかしながら、正極活物質の充填性が向上すると、被覆部２２０、特に中心部２１０と表面層２２２との間に介在する下地層２２１を経由してリチウムイオンが移動しにくくなるため、そのリチウムイオンのイオン伝導性が低下する。これにより、正極活物質では、イオン伝導性の低下に起因して電気抵抗が上昇する。
　この場合には、下地層２２１が第１金属アルコキシドの反応物（複数の細孔２２１Ｋ）を含んでいると、その複数の細孔２２１Ｋを経由してリチウムイオンが移動しやすくなるため、そのリチウムイオンのイオン伝導性が向上する。これにより、正極活物質では、イオン伝導性の向上に起因して電気抵抗が低下する。
　これらのことから、小粒径粒子２００の被覆部２２０が下地層２２１（第１金属アルコキシドの反応物）および表面層２２２（第２金属アルコキシドの反応物）を含んでいると、小粒径粒子２００においてイオン伝導性が担保されながら充填性が向上するため、高いエネルギー密度が得られながらリチウムイオンが吸蔵放出されやすくなる。よって、小粒径粒子２００において充填性の向上とイオン伝導性の向上とが両立されるため、正極活物質を用いた二次電池において優れたサイクル特性および優れた負荷特性を得ることができる。
　特に、金属原子がケイ素原子などであれば、複数の細孔２２１Ｋを有する第１金属アルコキシドの反応物（網目状の構造）が容易かつ安定に形成されやすくなるため、より高い効果を得ることができる。この場合には、金属原子がケイ素原子であれば、網目状の構造がより容易かつ安定に形成されやすくなるため、さらに高い効果を得ることができる。
　また、第１金属アルコキシドが式（４）に示した化合物を含んでいれば、その第１金属アルコキシドの反応物が容易かつ安定に形成されやすくなるため、より高い効果を得ることができる。しかも、第２金属アルコキシドが式（５）に示した化合物を含んでいれば、その第２金属アルコキシドの反応物が容易かつ安定に形成されやすくなるため、より高い効果を得ることができる。
　また、リチウム含有化合物が式（１）～式（３）のそれぞれに示した化合物のうちのいずれか１種類または２種類以上を含んでいれば、高いエネルギー密度が得られるため、より高い効果を得ることができる。
　また、下地層２２１がさらに第３金属アルコキシドの反応物を含んでいれば、複数の小粒径粒子２００のイオン伝導性がより向上するため、より高い効果を得ることができる。この場合には、第３金属アルコキシドが式（６）に示した化合物を含んでいれば、その第３金属アルコキシドの反応物が容易かつ安定に形成されやすくなるため、さらに高い効果を得ることができる。
＜２．二次電池（二次電池用正極）＞
　次に、上記した正極活物質を用いた本技術の一実施形態の二次電池に関して説明する。
　なお、本技術の一実施形態の二次電池用正極（以下、単に「正極」と呼称する。）は、ここで説明する二次電池の一部（一構成要素）であるため、その正極に関しては、以下で併せて説明する。
　以下では、上記したように、電極反応物質がリチウムである場合を例に挙げる。リチウムの吸蔵放出を利用して電池容量が得られる二次電池は、いわゆるリチウムイオン二次電池である。
＜２－１．構成＞
　図４は、二次電池の斜視構成を表していると共に、図５は、図４に示した電池素子１０の断面構成を表している。ただし、図４では、電池素子１０と外装フィルム２０とが互いに分離された状態を示していると共に、図５では、電池素子１０の一部の断面を示している。以下では、随時、既に説明した図１～図３を参照する。
　この二次電池は、図４に示したように、電池素子１０と、外装フィルム２０と、正極リード１４と、負極リード１５とを備えている。電池素子１０は、外装フィルム２０の内部に収納されていると共に、正極リード１４および負極リード１５のそれぞれは、外装フィルム２０の内部から外部に向かって互いに共通する方向に導出されている。
　ここで説明する二次電池は、電池素子１０を収納するための外装部材として、可撓性（または柔軟性）を有する外装部材（外装フィルム２０）を用いたラミネートフィルム型の二次電池である。
［外装フィルム］
　外装フィルム２０は、図４に示したように、１枚のフィルム状の部材であり、矢印Ｒ（一点鎖線）の方向に折り畳み可能である。この外装フィルム２０は、上記したように、電池素子１０を収納しているため、正極１１、負極１２および電解液を収納している。なお、外装フィルム２０には、電池素子１０を収容するための窪み部２０Ｕ（いわゆる深絞り部）が設けられている。
　具体的には、外装フィルム２０は、融着層、金属層および表面保護層が内側からこの順に積層された３層のラミネートフィルムであり、その外装フィルム２０が折り畳まれた状態では、互いに対向する融着層のうちの外周縁部同士が互いに融着されている。融着層は、ポリプロピレンなどの高分子化合物を含んでいる。金属層は、アルミニウムなどの金属材料を含んでいる。表面保護層は、ナイロンなどの高分子化合物を含んでいる。
　ただし、外装フィルム２０の構成（層数）は、特に、限定されないため、１層または２層でもよいし、４層以上でもよい。
　外装フィルム２０と正極リード１４との間には、密着フィルム２１が挿入されていると共に、外装フィルム２０と負極リード１５との間には、密着フィルム２２が挿入されている。密着フィルム２１，２２のそれぞれは、外装フィルム２０の内部に外気が意図せずに侵入することを防止する部材であり、正極リード１４および負極リード１５のそれぞれに対して密着性を有するポリオレフィンなどの高分子化合物のうちのいずれか１種類または２種類以上を含んでいる。このポリオレフィンは、ポリエチレン、ポリプロピレン、変性ポリエチレンおよび変性ポリプロピレンなどである。ただし、密着フィルム２１，２２のうちの一方または双方は、省略されてもよい。
［電池素子］
　電池素子１０は、図４および図５に示したように、正極１１と、負極１２と、セパレータ１３と、液状の電解質である電解液（図示せず）とを備えており、その電解液は、正極１１、負極１２およびセパレータ１３のそれぞれに含浸されている。
　ここでは、電池素子１０は、正極１１および負極１２がセパレータ１３を介して巻回された構造体であり、いわゆる巻回電極体である。より具体的には、巻回電極体である電池素子１０では、正極１１および負極１２がセパレータ１３を介して互いに積層されていると共に、その正極１１、負極１２およびセパレータ１３が巻回軸（Ｙ軸方向に延在する仮想軸）を中心として巻回されている。すなわち、正極１１および負極１２は、セパレータ１３を介して互いに対向しながら、そのセパレータ１３と一緒に巻回されている。
　巻回軸と交差する電池素子１０の断面（ＸＺ面に沿った断面）の形状は、長軸および短軸により規定される扁平形状であり、より具体的には、扁平な略楕円形である。この長軸は、Ｘ軸方向に延在すると共に相対的に大きい長さを有する軸（横軸）であると共に、短軸は、Ｘ軸方向と交差するＹ軸方向に延在すると共に相対的に小さい長さを有する軸（縦軸）である。
（正極）
　正極１１は、図５に示したように、正極活物質層１１Ｂを備えている。より具体的には、正極１１は、正極集電体１１Ａと、その正極集電体１１Ａの両面に設けられた２個の正極活物質層１１Ｂとを含んでいる。ただし、正極活物質層１１Ｂは、正極集電体１１Ａの片面だけに設けられていてもよい。
　正極集電体１１Ａは、金属材料などの導電性材料のうちのいずれか１種類または２種類以上を含んでおり、その金属材料は、アルミニウム、ニッケルおよびステンレスなどである。正極活物質層１１Ｂは、リチウムを吸蔵放出可能である正極活物質のうちのいずれか１種類または２種類以上を含んでいる。ただし、正極活物質層１１Ｂは、さらに、正極結着剤および正極導電剤などを含んでいてもよい。
　正極活物質に関する詳細は、上記した通りである。すなわち、正極活物質は、複数の大粒径粒子１００および複数の小粒径粒子２００を含んでおり、その複数の小粒径粒子２００のそれぞれは、中心部２１０および被覆部２２０を含んでいる。
　正極結着剤は、合成ゴムおよび高分子化合物などのうちのいずれか１種類または２種類以上を含んでいる。合成ゴムは、スチレンブタジエン系ゴム、フッ素系ゴムおよびエチレンプロピレンジエンなどである。高分子化合物は、ポリフッ化ビニリデン、ポリイミドおよびカルボキシメチルセルロースなどである。
　正極導電剤は、炭素材料などの導電性材料のうちのいずれか１種類または２種類以上を含んでおり、その炭素材料は、黒鉛、カーボンブラック、アセチレンブラックおよびケッチェンブラックなどである。ただし、導電性材料は、金属材料および高分子化合物などでもよい。
（負極）
　負極１２は、図５に示したように、負極集電体１２Ａと、その負極集電体１２Ａの両面に設けられた２個の負極活物質層１２Ｂとを含んでいる。ただし、負極活物質層１２Ｂは、負極集電体１２Ａの片面だけに設けられていてもよい。
　負極集電体１２Ａは、金属材料などの導電性材料のうちのいずれか１種類または２種類以上を含んでおり、その金属材料は、銅、アルミニウム、ニッケルおよびステンレスなどである。負極活物質層１２Ｂは、リチウムを吸蔵放出可能である負極活物質のうちのいずれか１種類または２種類以上を含んでいる。ただし、負極活物質層１２Ｂは、さらに、負極結着剤および負極導電剤などを含んでいてもよい。負極結着剤に関する詳細は、正極結着剤に関する詳細と同様であると共に、負極導電剤に関する詳細は、正極導電剤に関する詳細と同様である。
　負極活物質の種類は、特に限定されないが、具体的には、炭素材料および金属系材料などである。炭素材料は、易黒鉛化性炭素、難黒鉛化性炭素および黒鉛などであり、その黒鉛は、天然黒鉛および人造黒鉛などである。金属系材料は、リチウムと合金を形成することが可能である金属元素および半金属元素のうちのいずれか１種類または２種類以上を含む材料であり、その金属元素および半金属元素は、ケイ素およびスズなどである。ただし、金属系材料は、単体でもよいし、合金でもよいし、化合物でもよいし、それらの２種類以上の混合物でもよい、それらの２種類以上の相を含む材料でもよい。
　金属系材料の具体例は、ＳｉＢ4 、ＳｉＢ6 、Ｍｇ2 Ｓｉ、Ｎｉ2 Ｓｉ、ＴｉＳｉ2 、ＭｏＳｉ2 、ＣｏＳｉ2 、ＮｉＳｉ2 、ＣａＳｉ2 、ＣｒＳｉ2 、Ｃｕ5 Ｓｉ、ＦｅＳｉ2 、ＭｎＳｉ2 、ＮｂＳｉ2 、ＴａＳｉ2 、ＶＳｉ2 、ＷＳｉ2 、ＺｎＳｉ2 、ＳｉＣ、Ｓｉ3 Ｎ4 、Ｓｉ2 Ｎ2 Ｏ、ＳｉＯv （０＜ｖ≦２）、ＬｉＳｉＯ、ＳｎＯw （０＜ｗ≦２）、ＳｎＳｉＯ3 、ＬｉＳｎＯおよびＭｇ2 Ｓｎなどである。ただし、ＳｉＯv のｖは、０．２＜ｖ＜１．４を満たしていてもよい。
　負極活物質層１２Ｂの形成方法は、特に限定されないが、具体的には、塗布法、気相法、液相法、溶射法および焼成法（焼結法）などのうちのいずれか１種類または２種類以上である。
（セパレータ）
　セパレータ１３は、図５に示したように、正極１１と負極１２との間に介在しており、その正極１１と負極１２との接触に起因する短絡を防止しながらリチウムイオンを通過させる絶縁性の多孔質膜である。この多孔質膜は、ポリテトラフルオロエチレン、ポリプロピレンおよびポリエチレンなどの高分子化合物のうちのいずれか１種類または２種類以上を含んでいる。
（電解液）
　電解液は、溶媒および電解質塩を含んでいる。
　溶媒は、非水溶媒（有機溶剤）のうちのいずれか１種類または２種類以上を含んでおり、その非水溶媒を含んでいる電解液は、いわゆる非水電解液である。この非水溶媒は、エステル類およびエーテル類などであり、より具体的には、炭酸エステル系化合物、カルボン酸エステル系化合物およびラクトン系化合物などである。
　炭酸エステル系化合物は、環状炭酸エステルおよび鎖状炭酸エステルなどである。環状炭酸エステルは、炭酸エチレンおよび炭酸プロピレンなどであると共に、鎖状炭酸エステルは、炭酸ジメチル、炭酸ジエチルおよび炭酸メチルエチルなどである。カルボン酸エステル系化合物は、酢酸エチル、プロピオン酸エチルおよびトリメチル酢酸エチルなどである。ラクトン系化合物は、γ－ブチロラクトンおよびγ－バレロラクトンなどである。エーテル類は、上記したラクトン系化合物の他、１，２－ジメトキシエタン、テトラヒドロフラン、１，３－ジオキソランおよび１，４－ジオキサンなどである。
　また、非水溶媒は、不飽和環状炭酸エステル、ハロゲン化炭酸エステル、スルホン酸エステル、リン酸エステル、酸無水物、ニトリル化合物およびイソシアネート化合物などである。電解液の化学的安定性が向上するからである。
　具体的には、不飽和環状炭酸エステルは、炭酸ビニレン、炭酸ビニルエチレンおよび炭酸メチレンエチレンなどである。ハロゲン化炭酸エステルは、モノフルオロ炭酸エチレンおよびジフルオロ炭酸エチレンなどである。スルホン酸エステルは、１，３－プロパンスルトンおよび１，３－プロペンスルトンなどである。リン酸エステルは、リン酸トリメチルなどである。
　酸無水物は、環状カルボン酸無水物、環状ジスルホン酸無水物および環状カルボン酸スルホン酸無水物などである。環状カルボン酸無水物は、コハク酸無水物、グルタル酸無水物およびマレイン酸無水物などである。環状ジスルホン酸無水物は、エタンジスルホン酸無水物およびプロパンジスルホン酸無水物などである。環状カルボン酸スルホン酸無水物は、スルホ安息香酸無水物、スルホプロピオン酸無水物およびスルホ酪無水物などである。
　ニトリル化合物は、アセトニトリル、アクリロニトリル、マロノニトリル、スクシノニトリル、グルタロニトリル、アジポニトリル、セバコニトリルおよびフタロニトリルなどである。イソシアネート化合物は、ヘキサメチレンジイソシアネートなどである。
　電解質塩は、リチウム塩などの軽金属塩のうちのいずれか１種類または２種類以上を含んでいる。このリチウム塩は、六フッ化リン酸リチウム（ＬｉＰＦ6 ）、四フッ化ホウ酸リチウム（ＬｉＢＦ4 ）、トリフルオロメタンスルホン酸リチウム（ＬｉＣＦ3 ＳＯ3 ）、ビス（フルオロスルホニル）イミドリチウム（ＬｉＮ（ＦＳＯ2 ）2 ）、ビス（トリフルオロメタンスルホニル）イミドリチウム（ＬｉＮ（ＣＦ3 ＳＯ2 ）2 ）、リチウムトリス（トリフルオロメタンスルホニル）メチド（ＬｉＣ（ＣＦ3 ＳＯ2 ）3 ）およびビス（オキサラト）ホウ酸リチウム（ＬｉＢ（Ｃ2 Ｏ4 ）2 ）などである。
　電解質塩の含有量は、特に限定されないが、具体的には、溶媒に対して０．３ｍｏｌ／ｋｇ～３．０ｍｏｌ／ｋｇである。高いイオン伝導性が得られるからである。
［正極リードおよび負極リード］
　正極リード１４は、正極１１に接続された正極端子であり、アルミニウムなどの導電性材料のうちのいずれか１種類または２種類以上を含んでいる。負極リード１５は、負極１２に接続された負極端子であり、銅、ニッケルおよびステンレスなどの導電性材料のうちのいずれか１種類または２種類以上を含んでいる。正極リード１４および負極リード１５のそれぞれの形状は、薄板状および網目状などである。
　なお、正極リード１４の数は、特に限定されないため、１本でもよいし、２本以上でもよい。この場合には、特に、正極リード１４の数が２本以上であれば、二次電池の電気抵抗が低下する。ここで説明したことは、負極リード１５の数に関しても同様である。
＜２－２．動作＞
　二次電池の充電時には、正極１１からリチウムが放出されると共に、そのリチウムが電解液を介して負極１２に吸蔵される。また、二次電池の放電時には、負極１２からリチウムが放出されると共に、そのリチウムが電解液を介して正極１１に吸蔵される。この充放電時には、リチウムがイオン状態で吸蔵放出される。
＜２－３．製造方法＞
　二次電池を製造する場合には、以下で説明する手順により、正極１１および負極１２を作製したのち、その正極１１および負極１２を用いて二次電池を作製する。以下では、随時、既に説明した図１～図５を参照する。
［正極の作製］
　最初に、正極活物質（複数の大粒径粒子１００および複数の小粒径粒子２００）と、正極結着剤および正極導電剤などとを混合することにより、正極合剤とする。続いて、有機溶剤などの溶媒に正極合剤を投入することにより、ペースト状の正極合剤スラリーを調製する。最後に、正極集電体１１Ａの両面に正極合剤スラリーを塗布することにより、正極活物質層１１Ｂを形成する。こののち、ロールプレス機を用いて正極活物質層１１Ｂを圧縮成型してもよい。この場合には、正極活物質層１１Ｂを加熱してもよいし、圧縮成型を複数回繰り返してもよい。
［負極の作製］
　上記した正極１１の作製手順と同様の手順により、負極集電体１２Ａの両面に負極活物質層１２Ｂを形成する。具体的には、負極活物質と、負極結着剤および負極導電剤などとを混合することにより、負極合剤としたのち、有機溶剤などに負極合剤を投入することにより、ペースト状の負極合剤スラリーを調製する。続いて、負極集電体１２Ａの両面に負極合剤スラリーを塗布することにより、負極活物質層１２Ｂを形成する。こののち、負極活物質層１２Ｂを圧縮成型してもよい。
［二次電池の組み立て］
　最初に、溶接法などを用いて正極１１に正極リード１４を接続させると共に、溶接法などを用いて負極１２に負極リード１５を接続させる。この場合には、あらかじめ正極集電体１１Ａの一部を露出させておき、その正極集電体１１Ａの一部に正極リード１４を接続させてもよいと共に、あらかじめ負極集電体１２Ａの一部を露出させておき、その負極集電体１２Ａの一部に負極リード１５を接続させてもよい。続いて、セパレータ１３を介して正極１１および負極１２を互いに積層させたのち、その正極１１、負極１２およびセパレータ１３を巻回させることにより、巻回体を作製する。この巻回体は、正極１１、負極１２およびセパレータ１３のそれぞれに電解液が含浸されていないことを除いて、電池素子１０の構成と同様の構成を有している。
　続いて、窪み部２０Ｕの内部に巻回体を収容したのち、矢印Ｒの方向に外装フィルム２０を折り畳む。続いて、熱融着法などを用いて外装フィルム２０（融着層）のうちの２辺の外周縁部同士を互いに接着させることにより、袋状の外装フィルム２０の内部に巻回体を収納する。
　最後に、溶媒に電解質塩が添加された電解液を袋状の外装フィルム２０の内部に注入したのち、熱融着法などを用いて外装フィルム２０（融着層）のうちの残りの１辺の外周縁部同士を互いに接着させる。この場合には、外装フィルム２０と正極リード１４との間に密着フィルム２１を挿入すると共に、外装フィルム２０と負極リード１５との間に密着フィルム２２を挿入する。これにより、巻回体に電解液が含浸されるため、電池素子１０が作製される。よって、袋状の外装フィルム２０の内部に電池素子１０が封入されるため、二次電池が組み立てられる。
［二次電池の安定化］
　組み立て後の二次電池を充放電させる。環境温度、充放電回数（サイクル数）および充放電条件などの各種条件は、任意に設定可能である。これにより、負極１２などの表面に被膜が形成されるため、二次電池の状態が電気化学的に安定化する。よって、外装フィルム２０を用いた二次電池、すなわちラミネートフィルム型の二次電池が完成する。
＜２－４．作用および効果＞
　この二次電池によれば、正極１１の正極活物質層１１Ｂが正極活物質を含んでおり、その正極活物質が上記した構成（複数の大粒径粒子１００および複数の小粒径粒子２００）を有している。よって、上記した理由により、正極活物質において充填性の向上とイオン伝導性の向上とが両立されるため、優れたサイクル特性および優れた負荷特性を得ることができる。
　また、正極１１によれば、正極活物質を含む正極活物質層１１Ｂを備えており、その正極活物質が上記した構成（複数の大粒径粒子１００および複数の小粒径粒子２００）を有しているので、その正極１１を備えた二次電池において優れたサイクル特性および優れた負荷特性を得ることができる。
　これ以外の二次電池および正極１１のそれぞれに関する作用および効果は、上記した正極活物質に関する作用および効果と同様である。
＜３．変形例＞
　次に、上記した二次電池の変形例に関して説明する。二次電池の構成は、以下で説明するように、適宜、変更可能である。ただし、以下で説明する一連の変形例のうちの任意の２種類以上は、互いに組み合わされてもよい。
［変形例１］
　多孔質膜であるセパレータ１３を用いた。しかしながら、ここでは具体的に図示しないが、多孔質膜であるセパレータ１３の代わりに、高分子化合物層を含む積層型のセパレータを用いてもよい。
　具体的には、積層型のセパレータは、上記した多孔質膜と、その多孔質膜の片面または両面に設けられた高分子化合物層とを含んでいる。正極１１および負極１２のそれぞれに対するセパレータの密着性が向上するため、電池素子１０の位置ずれが発生しにくくなるからである。これにより、電解液の分解反応などが発生しても、二次電池が膨れにくくなる。高分子化合物層は、ポリフッ化ビニリデンなどの高分子化合物を含んでいる。物理的強度に優れていると共に、電気化学的に安定だからである。
　なお、多孔質膜および高分子化合物層のうちの一方または双方は、複数の無機粒子および複数の樹脂粒子などの複数の粒子のうちのいずれか１種類または２種類以上を含んでいてもよい。二次電池の発熱時において複数の粒子が放熱するため、その二次電池の耐熱性および安全性が向上するからである。無機粒子の種類は、特に限定されないが、酸化アルミニウム（アルミナ）、窒化アルミニウム、ベーマイト、酸化ケイ素（シリカ）、酸化チタン（チタニア）、酸化マグネシウム（マグネシア）および酸化ジルコニウム（ジルコニア）などの粒子である。
　積層型のセパレータを作製する場合には、高分子化合物および有機溶剤などを含む前駆溶液を調製したのち、基材層の片面または両面に前駆溶液を塗布する。
　この積層型のセパレータを用いた場合においても、正極１１と負極１２との間においてリチウムイオンが移動可能になるため、同様の効果を得ることができる。
［変形例２］
　液状の電解質である電解液を用いた。しかしながら、ここでは具体的に図示しないが、電解液の代わりに、ゲル状の電解質である電解質層を用いてもよい。
　電解質層を用いた電池素子１０では、セパレータ１３および電解質層を介して正極１１および負極１２が互いに積層されたのち、その正極１１、負極１２、セパレータ１３および電解質層が巻回されている。この電解質層は、正極１１とセパレータ１３との間に介在していると共に、負極１２とセパレータ１３との間に介在している。
　具体的には、電解質層は、電解液と共に高分子化合物を含んでおり、その電解質層中では、電解液が高分子化合物により保持されている。電解液の構成は、上記した通りである。高分子化合物は、ポリフッ化ビニリデンなどを含んでいる。電解質層を形成する場合には、電解液、高分子化合物および有機溶剤などを含む前駆溶液を調製したのち、正極１１および負極１２のそれぞれの片面または両面に前駆溶液を塗布する。
　この電解質層を用いた場合においても、正極１１と負極１２との間において電解質層を介してリチウムイオンが移動可能になるため、同様の効果を得ることができる。
＜４．二次電池の用途＞
　次に、上記した二次電池の用途（適用例）に関して説明する。
　二次電池の用途は、主に、駆動用の電源または電力蓄積用の電力貯蔵源などとして二次電池を利用可能である機械、機器、器具、装置およびシステム（複数の機器などの集合体）などであれば、特に限定されない。電源として用いられる二次電池は、主電源でもよいし、補助電源でもよい。主電源とは、他の電源の有無に関係なく、優先的に用いられる電源である。補助電源は、主電源の代わりに用いられる電源でもよいし、必要に応じて主電源から切り替えられる電源でもよい。二次電池を補助電源として用いる場合には、主電源の種類は二次電池に限られない。
　二次電池の用途の具体例は、以下の通りである。ビデオカメラ、デジタルスチルカメラ、携帯電話機、ノート型パソコン、コードレス電話機、ヘッドホンステレオ、携帯用ラジオ、携帯用テレビおよび携帯用情報端末などの電子機器（携帯用電子機器を含む。）である。電気シェーバなどの携帯用生活器具である。バックアップ電源およびメモリーカードなどの記憶用装置である。電動ドリルおよび電動鋸などの電動工具である。着脱可能な電源としてノート型パソコンなどに搭載される電池パックである。ペースメーカおよび補聴器などの医療用電子機器である。電気自動車（ハイブリッド自動車を含む。）などの電動車両である。非常時などに備えて電力を蓄積しておく家庭用バッテリシステムなどの電力貯蔵システムである。なお、二次電池の電池構造は、上記したラミネートフィルム型および円筒型でもよいし、それら以外の他の電池構造でもよい。また、電池パックおよび電池モジュールなどとして、複数の二次電池が用いられてもよい。
　中でも、電池パックおよび電池モジュールは、電動車両、電力貯蔵システムおよび電動工具などの比較的大型の機器などに適用されることが有効である。電池パックは、後述するように、単電池を用いてもよいし、組電池を用いてもよい。電動車両は、二次電池を駆動用電源として作動（走行）する車両であり、上記したように、二次電池以外の駆動源を併せて備えた自動車（ハイブリッド自動車など）でもよい。電力貯蔵システムは、二次電池を電力貯蔵源として用いるシステムである。家庭用の電力貯蔵システムでは、電力貯蔵源である二次電池に電力が蓄積されているため、その電力を利用して家庭用の電気製品などを使用可能である。
　ここで、二次電池のいくつかの適用例に関して具体的に説明する。以下で説明する適用例の構成は、あくまで一例であるため、適宜、変更可能である。以下の適用例に用いられる二次電池の種類は、特に限定されないため、ラミネートフィルム型でもよいし、円筒型でもよい。
＜４－１．電池パック（単電池）＞
　図６は、電池パックのブロック構成を表している。ここで説明する電池パックは、１個の二次電池を用いた簡易型の電池パック（いわゆるソフトパック）であり、スマートフォンに代表される電子機器などに搭載される。
　この電池パックは、図６に示したように、電源３１と、回路基板３２とを備えている。この回路基板３２は、電源３１に接続されていると共に、正極端子３３、負極端子３４および温度検出端子３５を含んでいる。この温度検出端子３５は、いわゆるＴ端子である。
　電源３１は、１個の二次電池を含んでいる。この二次電池では、正極リードが正極端子３３に接続されていると共に、負極リードが負極端子３４に接続されている。この電源３１は、正極端子３３および負極端子３４を介して外部と接続可能であるため、その正極端子３３および負極端子３４を介して充放電可能である。回路基板３２は、制御部３６と、スイッチ３７と、熱感抵抗素子（ＰＴＣ（Positive Temperature Coefficient）素子）３８と、温度検出部３９とを含んでいる。ただし、ＰＴＣ素子３８は省略されてもよい。
　制御部３６は、中央演算処理装置（ＣＰＵ：Central Processing Unit ）およびメモリなどを含んでおり、電池パック全体の動作を制御する。この制御部３６は、必要に応じて電源３１の使用状態の検出および制御を行う。
　なお、制御部３６は、電源３１（二次電池）の電池電圧が過充電検出電圧または過放電検出電圧に到達すると、スイッチ３７を切断することにより、電源３１の電流経路に充電電流が流れないようにする。また、制御部３６は、充電時または放電時において大電流が流れると、スイッチ３７を切断することにより、充電電流を遮断する。過充電検出電圧および過放電検出電圧は、特に限定されない。一例を挙げると、過充電検出電圧は、４．２Ｖ±０．０５Ｖであると共に、過放電検出電圧は、２．４Ｖ±０．１Ｖである。
　スイッチ３７は、充電制御スイッチ、放電制御スイッチ、充電用ダイオードおよび放電用ダイオードなどを含んでおり、制御部３６の指示に応じて電源３１と外部機器との接続の有無を切り換える。このスイッチ３７は、金属酸化物半導体を用いた電界効果トランジスタ（ＭＯＳＦＥＴ：Metal-Oxide-Semiconductor Field-Effect Transistor ）などを含んでおり、充放電電流は、スイッチ３７のＯＮ抵抗に基づいて検出される。
　温度検出部３９は、サーミスタなどの温度検出素子を含んでおり、温度検出端子３５を用いて電源３１の温度を測定すると共に、その温度の測定結果を制御部３６に出力する。温度検出部３９により測定される温度の測定結果は、異常発熱時において制御部３６が充放電制御を行う場合および残容量の算出時において制御部３６が補正処理を行う場合などに用いられる。
＜４－２．電池パック（組電池）＞
　図７は、組電池を用いた電池パックのブロック構成を表している。以下の説明では、随時、単電池を用いた電池パック（図６参照）の構成要素を引用する。
　この電池パックは、図７に示したように、正極端子５１および負極端子５２を含んでいる。具体的には、電池パックは、筐体４０の内部に、制御部４１と、電源４２と、スイッチ４３と、電流測定部４４と、温度検出部４５と、電圧検出部４６と、スイッチ制御部４７と、メモリ４８と、温度検出素子４９と、電流検出抵抗５０とを備えている。
　電源４２は、２個以上の二次電池が互いに接続された組電池を含んでおり、その２個以上の二次電池の接続形式は、特に限定されない。このため、接続方式は、直列でもよいし、並列でもよいし、双方の混合型でもよい。一例を挙げると、電源４２は、２並列３直列となるように互いに接続された６個の二次電池を含んでいる。
　制御部４１、スイッチ４３、温度検出部４５および温度検出素子４９のそれぞれの構成は、制御部３６、スイッチ３７および温度検出部３９（温度検出素子）のそれぞれの構成と同様である。電流測定部４４は、電流検出抵抗５０を用いて電流を測定すると共に、その電流の測定結果を制御部４１に出力する。電圧検出部４６は、電源４２（二次電池）の電池電圧を測定すると共に、アナログ－デジタル変換された電圧の測定結果を制御部４１に供給する。
　スイッチ制御部４７は、電流測定部４４および電圧検出部４６から入力される信号に応じてスイッチ４３の動作を制御する。このスイッチ制御部４７は、電池電圧が過充電検出電圧または過放電検出電圧に到達すると、スイッチ４３（充電制御スイッチ）を切断させることにより、電源４２の電流経路に充電電流が流れないようにする。これにより、電源４２では、放電用ダイオードを介して放電だけが可能になり、または充電用ダイオードを介して充電だけが可能になる。また、スイッチ制御部４７は、充電時または放電時において大電流が流れると、充電電流または放電電流を遮断する。
　なお、スイッチ制御部４７を省略することにより、制御部４１がスイッチ制御部４７の機能を兼ねてもよい。過充電検出電圧および過放電検出電圧は、特に限定されないが、単電池を用いた電池パックに関して説明した場合と同様である。
　メモリ４８は、不揮発性メモリであるＥＥＰＲＯＭ（Electrically Erasable Programmable Read-Only Memory ）などを含んでおり、そのメモリ４８には、制御部４１により演算された数値および製造工程において測定された二次電池の情報（初期状態の内部抵抗、満充電容量および残容量など）などが記憶されている。
　正極端子５１および負極端子５２は、電池パックを用いて稼働する外部機器（ノート型のパーソナルコンピュータなど）および電池パックを充電するために用いられる外部機器（充電器など）などに接続される端子である。電源４２（二次電池）は、正極端子５１および負極端子５２を介して充放電可能である。
＜４－３．電動車両＞
　図８は、電動車両の一例であるハイブリッド自動車のブロック構成を表している。この電動車両は、図８に示したように、筐体６０の内部に、制御部６１と、エンジン６２と、電源６３と、モータ６４と、差動装置６５と、発電機６６と、トランスミッション６７およびクラッチ６８と、インバータ６９，７０と、各種センサ７１とを備えている。また、電動車両は、差動装置６５およびトランスミッション６７に接続された前輪用駆動軸７２および一対の前輪７３と、後輪用駆動軸７４および一対の後輪７５とを備えている。
　この電動車両は、エンジン６２およびモータ６４のうちのいずれか一方を駆動源として用いて走行可能である。エンジン６２は、ガソリンエンジンなどの主要な動力源である。エンジン６２を動力源とする場合には、駆動部である差動装置６５、トランスミッション６７およびクラッチ６８を介してエンジン６２の駆動力（回転力）が前輪７３および後輪７５に伝達される。なお、エンジン６２の回転力が発電機６６に伝達されるため、その回転力を利用して発電機６６が交流電力を発生させると共に、その交流電力がインバータ７０を介して直流電力に変換されるため、その直流電力が電源６３に蓄積される。一方、変換部であるモータ６４を動力源とする場合には、電源６３から供給された電力（直流電力）がインバータ６９を介して交流電力に変換されるため、その交流電力を利用してモータ６４が駆動する。モータ６４により電力から変換された駆動力（回転力）は、駆動部である差動装置６５、トランスミッション６７およびクラッチ６８を介して前輪７３および後輪７５に伝達される。
　なお、制動機構を介して電動車両が減速すると、その減速時の抵抗力がモータ６４に回転力として伝達されるため、その回転力を利用してモータ６４が交流電力を発生させてもよい。この交流電力は、インバータ６９を介して直流電力に変換されるため、その直流回生電力は、電源６３に蓄積される。
　制御部６１は、ＣＰＵなどを含んでおり、電動車両全体の動作を制御する。電源６３は、１個または２個以上の二次電池を含んでおり、外部電源と接続されている。この場合には、電源６３は、外部電源から電力を供給されることにより、電力を蓄積させてもよい。各種センサ７１は、エンジン６２の回転数を制御すると共に、スロットルバルブの開度（スロットル開度）を制御するために用いられる。この各種センサ７１は、速度センサ、加速度センサおよびエンジン回転数センサなどのうちのいずれか１種類または２種類以上を含んでいる。
　なお、電動車両がハイブリッド自動車である場合を例に挙げたが、その電動車両は、エンジン６２を用いずに電源６３およびモータ６４だけを用いて作動する車両（電気自動車）でもよい。
＜４－４．その他＞
　ここでは具体的に図示しないが、二次電池の適用例としては他の適用例も考えられる。
　具体的には、二次電池は、電力貯蔵システムに適用可能である。この電力貯蔵システムは、一般住宅および商業用ビルなどの家屋の内部に、制御部と、１個または２個以上の二次電池を含む電源と、スマートメータと、パワーハブとを備えている。
　電源は、家屋の内部に設置された冷蔵庫などの電気機器に接続されていると共に、その家屋の外部に停車されたハイブリッド自動車などの電動車両に接続可能である。また、電源は、家屋に設置された太陽光発電機などの自家発電機にパワーハブを介して接続されていると共に、スマートメータおよびパワーハブを介して外部の火力発電所などの集中型電力系統に接続されている。
　または、二次電池は、電動ドリルおよび電動鋸などの電動工具に適用可能である。この電動工具は、ドリル部および鋸刃部などの可動部が取り付けられた筐体の内部に、制御部と、１個または２個以上の二次電池を含む電源とを備えている。
　本技術の実施例に関して説明する。
（実験例１～２５）
　以下で説明するように、図１～図３に示した正極活物質（複数の大粒径粒子１００および複数の小粒径粒子２００）を製造すると共に、図４および図５に示したラミネートフィルム型の二次電池（リチウムイオン二次電池）を作製したのち、その二次電池の電池特性を評価した。
［正極活物質の製造］
　正極活物質を製造するために、浸漬法を用いて複数の小粒径粒子２００を製造した。
　具体的には、最初に、エタノール２５ｇにアンモニア水（濃度＝２８重量％）６ｇを添加したのち、そのエタノールを撹拌した。これにより、エタノール中においてアンモニア水が溶解されたため、アルカリ性溶媒が得られた。
　続いて、アルカリ性溶媒に複数の中心部２１０（リチウム含有化合物である粉末状のコバルト酸リチウム（ＬｉＣｏＯ2 ），平均一次粒径＝２０μｍ）３５ｇを添加した。続いて、アルカリ性溶媒に第１金属アルコキシドおよび第２金属アルコキシドを添加したのち、室温環境中（温度＝２０℃）中においてアルカリ性溶媒を撹拌（撹拌時間＝１２０分間）した。この場合には、必要に応じて、アルカリ性溶媒にさらに第３金属アルコキシドを添加した。第１金属アルコキシドおよび第２金属アルコキシドのそれぞれの添加量（含有量（重量％））は、表１に示した通りである。また、第３金属アルコキシドの有無および第３金属アルコキシドの添加量（含有量（重量％））は、表１に示した通りである。ここで説明した含有量（重量％）は、複数の中心部２１０の重量を１００重量％とした場合において何重量％に相当するかを表している。これにより、準備溶液が調製された。
　ここでは、第１金属アルコキシドとして、Ｓｉ－（ＯＣ2 Ｈ5 ）4 （ＴＥＳ）と、Ｔｉ－（ＯＣ4 Ｈ9 ）4 （ＴＢＴ）と、Ａｌ－（ＯＣＨ（ＣＨ3 ）2 ）3 （ＴＩＰＡ）と、Ｚｒ－（ＯＣ4 Ｈ9 ）4 （ＺＴＢ）とを用いた。第２金属アルコキシドとして、Ｈ33Ｃ16Ｓｉ－（ＯＣＨ3 ）3 （ＨＤＴＭＳ）を用いた。第３金属アルコキシドとして、（Ｈ3 ＣＯ）3 －Ｓｉ－Ｃ2 Ｈ4 －Ｓｉ－（ＯＣＨ3 ）3 （ＢＴＥＳＥ）および（Ｈ3 ＣＯ）3 －Ｓｉ－Ｃ6 Ｈ12－Ｓｉ－（ＯＣＨ3 ）3 （ＢＴＥＳＨ）を用いた。
　続いて、準備溶液を濾別することにより、その準備溶液が表面に付着された複数の中心部２１０を回収したのち、洗浄用の溶媒（アセトン）を用いて複数の中心部２１０を洗浄した。
　続いて、複数の中心部２１０を加熱（加熱温度＝８０℃および加熱時間＝１２０分間）することにより、その複数の中心部２１０を乾燥させた。これにより、中心部２１０の表面に、第１金属アルコキシドの反応物を含むと共に必要に応じてさらに第３金属アルコキシドの反応物を含む下地層２２１と、第２金属アルコキシドの反応物を含む表面層２２２とが形成された。すなわち、下地層２２１および表面層２２２を含む有機無機ハイブリッド膜である被覆部２２０（厚さ＝１０ｎｍ）が形成された。よって、中心部２１０および被覆部２２０（下地層２２１および表面層２２２）を含む複数の小粒径粒子２００が製造された。複数の小粒径粒子２００のメジアン径Ｄ５０（μｍ）は、表１に示した通りである。
　最後に、複数の大粒径粒子１００（リチウム複合酸化物である粉末状のコバルト酸リチウム）と、複数の小粒径粒子２００とを互いに混合させた。複数の大粒径粒子１００のメジアン径Ｄ５０（μｍ）は、表１に示した通りである。この場合には、複数の大粒径粒子１００と複数の小粒径粒子２００との混合比（重量比）を複数の大粒径粒子１００：複数の小粒径粒子２００＝８０：２０とした。
　よって、複数の大粒径粒子１００および複数の小粒径粒子２００を含む正極活物質が得られた（実験例１～１４）。
［二次電池の作製］
　以下の手順により、上記した正極活物質（複数の大粒径粒子１００および複数の小粒径粒子２００）を用いて二次電池を作製した。
（正極の作製）
　最初に、正極活物質９０質量部と、正極結着剤（ポリフッ化ビニリデン）５質量部と、正極導電剤（ケッチェンブラック）５質量部とを混合することにより、正極合剤とした。続いて、有機溶剤（Ｎ－メチル－２－ピロリドン）に正極合剤を投入したのち、その有機溶剤を撹拌することにより、ペースト状の正極合剤スラリーを調製した。続いて、コーティング装置を用いて正極集電体１１Ａ（帯状のアルミニウム箔，厚さ＝１５μｍ）の両面に正極合剤スラリーを塗布したのち、その正極合剤スラリーを乾燥させることにより、正極活物質層１１Ｂを形成した。最後に、ロールプレス機を用いて正極活物質層１１Ｂを圧縮成型（ロール温度＝１３０℃，線圧＝０．７ｇ／ｃｍ，プレス速度＝１０ｍ／分）した。
（負極の作製）
　最初に、負極活物質（炭素材料である人造黒鉛，平均一次粒径＝２０μｍ）９０質量部と、ポリアミック酸を含むＮ－メチル－２－ピロリドン溶液（濃度＝２０重量％）１０質量部とを混合したのち、そのＮ－メチル－２－ピロリドン溶液を撹拌することにより、ペースト状の負極合剤スラリーを調製した。続いて、バーコータ（ギャップ＝３５μｍ）を用いて負極集電体１２Ａ（帯状の銅箔，厚さ＝１５μｍ）の両面に負極合剤スラリーを塗布したのち、その塗膜を乾燥（温度＝８０℃）させた。最後に、ロールプレス機を用いて塗膜を圧縮成型したのち、その塗膜を加熱（加熱時間＝７００℃，加熱時間＝３時間）することにより、負極結着剤としてポリイミドを含む負極活物質層１２Ｂを形成した。
（電解液の調製）
　溶媒（環状炭酸エステルである炭酸エチレンおよび鎖状炭酸エステルである炭酸エチルメチル）に電解質塩（六フッ化リン酸リチウム（ＬｉＰＦ6 ））を添加したのち、その溶媒を撹拌した。この場合には、溶媒の混合比（重量比）を炭酸エチレン：炭酸エチルメチル＝５０；５０としたと共に、電解質塩の含有量を溶媒に対して１ｍｏｌ／ｌ（＝１ｍｏｌ／ｄｍ3 ）とした。
（二次電池の組み立て）
　最初に、正極集電体１１Ａにアルミニウム製の正極リード１４を溶接したと共に、負極集電体１２Ａに銅製の負極リード１５を溶接した。続いて、セパレータ１３（微多孔性ポリエチレンフィルム，厚さ＝２５μｍ）を介して正極１１および負極１２を互いに積層させたのち、その正極１１、負極１２およびセパレータ１３を巻回させることにより、巻回体を作製した。続いて、プレス機を用いて巻回体をプレスすることにより、断面の形状が扁平形状となるように巻回体を成型した。
　続いて、窪み部２０Ｕに収容された巻回体を挟むように外装フィルム２０を折り畳んだのち、その外装フィルム２０のうちの２辺の外周縁部同士を互いに熱融着させることにより、袋状の外装フィルム２０の内部に巻回体を収納した。外装フィルム２０としては、融着層（ポリプロピレンフィルム，厚さ＝３０μｍ）と、金属層（アルミニウム箔，厚さ＝４０μｍ）と、表面保護層（ナイロンフィルム，厚さ＝２５μｍ）とが内側からこの順に積層された防湿性のアルミラミネートフィルムを用いた。
　最後に、袋状の外装フィルム２０の内部に電解液を注入したのち、減圧環境中において外装フィルム２０のうちの残りの１辺の外周縁部同士を熱融着した。この場合には、外装フィルム２０と正極リード１４との間に密着フィルム２１（ポリプロピレンフィルム，厚さ＝５μｍ）を挿入したと共に、外装フィルム２０と負極リード１５との間に密着フィルム２２（ポリプロピレンフィルム，厚さ＝５μｍ）を挿入した。これにより、巻回体に電解液が含浸されたため、電池素子１０が形成された。よって、外装フィルム２０の内部に電池素子１０が封入されたため、二次電池が組み立てられた。
（二次電池の安定化）
　常温環境中（温度＝２０℃）において、二次電池を１サイクル充放電させた。充放電条件は、後述するサイクル特性を調べる場合の充放電条件と同様にした。これにより、負極１２などの表面に被膜が形成されたため、二次電池の状態が安定化した。よって、ラミネートフィルム型の二次電池が完成した。
［比較例の二次電池の作製］
　比較のために、表２に示したように、以下で説明する手順を用いたことを除いて同様の手順により、正極活物質を製造したと共に、その正極活物質を用いて二次電池を作製した。
　第１に、中心部２１０の表面に被覆部２２０を形成せずに、その中心部２１０をそのまま用いた（実験例１５）。
　第２に、複数の大粒径粒子１００のメジアン径Ｄ５０（μｍ）および複数の小粒径粒子２００のメジアン径Ｄ５０（μｍ）のそれぞれを極端に大きな値または極端に小さな値となるように変更した（実験例１６～１９）。
　第３に、複数の小粒径粒子２００の製造工程において、中心部２１０の表面に被覆部２２０を形成せずに、複数の大粒径粒子１００の製造工程において、大粒径粒子１００の表面に被覆部２２０を形成した（実験例２０）。また、複数の小粒径粒子２００の製造工程において、中心部２１０の表面に被覆部２２０を形成したことに加えて、複数の大粒径粒子１００の製造工程において、大粒径粒子１００の表面にも被覆部２２０を形成した（実験例２１）。この大粒径粒子１００の表面に形成された被覆部２２０の構成は、中心部２１０の表面に形成された被覆部２２０の構成と同様にした。
　第４に、下地層２２１および表面層２２２のうちのいずれか一方だけを含む被覆部２２０を形成した（実験例２２，２３）。
　第５に、複数の大粒径粒子１００および複数の小粒径粒子２００のうちのいずれか一方だけを用いた（実験例２４，２５）。
［電池特性の評価］
　二次電池の電池特性（サイクル特性および負荷特性）を評価したところ、表１および表２に示した結果が得られた。
（サイクル特性）
　サイクル特性を調べる場合には、最初に、常温環境中（温度＝２０℃）において二次電池を充放電させることにより、放電容量（１サイクル目の放電容量）を測定した。充電時には、０．５Ａの電流で電圧が４．２Ｖに到達するまで定電流充電したのち、その４．２Ｖの電圧で電流が初期値の１／１０の値（０．０５Ａ）に到達するまで定電圧充電した。放電時には、０．２Ａの電流で電圧が３．０Ｖに到達するまで定電流放電した。
　続いて、高温環境中（温度＝４５℃）において、サイクル数の総数が３００サイクルに到達するまで二次電池を繰り返して充放電させることにより、放電容量（３００サイクル目の放電容量）を測定した。充放電条件は、放電時の電流を０．５Ｃに変更したことを除いて、１サイクル目の充放電条件と同様にした。この０．５Ｃとは、１サイクル目の放電容量を１Ｃとした場合において０．５Ｃに相当する電流値であり、より具体的には１サイクル目の放電容量を１時間で放電しきる電流値である。
　最後に、サイクル維持率（％）＝（３００サイクル目の放電容量／１サイクル目の放電容量）×１００を算出した。
（負荷特性）
　負荷特性を調べる場合には、最初に、常温環境中（温度＝２０℃）において二次電池を充放電させることにより、放電容量（１サイクル目の放電容量）を測定した。充電時には、０．５Ａの電流で電圧が４．２Ｖに到達するまで定電流充電したのち、その４．２Ｖの電圧で電流が初期値の１／１０の値（０．０５Ａ）に到達するまで定電圧充電した。放電時には、０．２Ａの電流で電圧が３．０Ｖに到達するまで定電流放電した。
　続いて、同環境中において二次電池を充放電させることにより、放電容量（２サイクル目の放電容量）を測定した。充放電条件は、放電時の電流を０．１Ｃに変更したことを除いて、１サイクル目の充放電条件と同様にした。この０．１Ｃとは、１サイクル目の放電容量を１Ｃとした場合において０．１Ｃに相当する電流値であり、より具体的には１サイクル目の放電容量を１０時間で放電しきる電流値である。
　続いて、同環境中において二次電池を充放電させることにより、放電容量（３サイクル目の放電容量）を測定した。充放電条件は、放電時の電流を２Ｃに変更したことを除いて、１サイクル目の充放電条件と同様にした。この２Ｃとは、１サイクル目の放電容量を１Ｃとした場合において２Ｃに相当する電流値であり、より具体的には１サイクル目の放電容量を０．５時間で放電しきる電流値である。
　最後に、負荷維持率（％）＝（３サイクル目の放電容量（放電時の電流＝２Ｃ）／２サイクル目の放電容量（放電時の電流＝０．１Ｃ））×１００を算出した。
（正極活物質の充填性）
　ここでは、上記したサイクル特性および負荷特性を調べる他、正極活物質の充填性を評価するために、完成後の正極１１（正極活物質層１１Ｂ）を用いて体積密度（ｇ／ｃｃ＝ｇ／ｃｍ3 ）を測定した。この場合には、ハイト計を用いて正極活物質層１１Ｂの厚さ（ｃｍ）などの寸法を測定すると共に、その正極活物質層１１Ｂの重量を測定したのち、その寸法および重量に基づいて体積密度を算出した。
Figure JPOXMLDOC01-appb-T000003
Figure JPOXMLDOC01-appb-T000004
［考察］
　表１および表２に示したように、サイクル特性および負荷特性は、正極活物質の構成に応じて大きく変動した。以下では、大粒径粒子１００および小粒径粒子２００のいずれもが被覆部２２０を含んでいない場合（実験例１５）の評価結果（体積密度、サイクル維持率および負荷維持率）を比較基準とする。
　具体的には、大粒径粒子１００が被覆部２２０を含んでおらずに小粒径粒子２００だけが被覆部２２０を含んでおり、複数の大粒径粒子１００のメジアン径Ｄ５０が１５μｍ～３０μｍであると共に複数の小粒径粒子２００のメジアン径Ｄ５０が１μｍ～１０μｍであるという条件が満たされている場合（実験例１～１４）には、上記した比較基準と比較して、ほぼ同等の負荷維持率が担保されながら、体積密度が安定に増加したと共に、サイクル維持率も増加した。よって、体積密度が増加したため、サイクル維持率および負荷維持率の双方が高くなった。
　これに対して、上記した条件が満たされていない場合（実験例１６～２５）には、場合によっては体積密度が増加したものの、サイクル維持率および負荷維持率のうちの一方または双方が減少した。よって、体積密度が安定に増加しなかったため、サイクル維持率および負荷維持率の双方が高くならなかった。
　特に、上記した条件が満たされている場合には、以下の傾向が得られた。第１に、下地層２２１が第１金属アルコキシドの反応物と共に第３金属アルコキシドの反応物を含んでいると（実験例１０，１１）、下地層２２１が第１金属アルコキシドの反応物だけを含んでいる場合（実験例２）と比較して、サイクル維持率および負荷維持率の双方がより増加した。第２に、第１金属アルコキシドの金属原子としてチタン原子などを用いた場合（実験例１２～１４）においても、その金属原子としてケイ素原子を用いた場合（実験例１０）と同様に、体積密度が増加したため、高いサイクル維持率が得られると共に高い負荷維持率も得られた。第３に、第１金属アルコキシドの金属原子としてケイ素原子を用いた場合（実験例１０）には、その金属原子としてチタン原子などを用いた場合（実験例１２～１４）と比較して、負荷維持率がより増加した。
［まとめ］
　表１および表２に示した結果から、正極活物質が複数の大粒径粒子１００（メジアン径Ｄ５０＝１５μｍ～３０μｍ）および複数の小粒径粒子２００（メジアン径＝１μｍ～１０μｍ）を含んでおり、その小粒径粒子２００の被覆部２２０が下地層２２１（第１金属アルコキシドの反応物）および表面層２２２（第２金属アルコキシドの反応物）を含んでいると、体積密度が増加したと共に、高い容量維持率および高い負荷維持率が得られた。よって、二次電池において優れたサイクル特性および優れた負荷特性が得られた。
　以上、一実施形態および実施例を挙げながら本技術に関して説明したが、その本技術の構成は、一実施形態および実施例において説明された構成に限定されないため、種々に変形可能である。
　具体的には、二次電池の電池構造がラミネートフィルム型である場合に関して説明したが、その電池構造は、特に限定されないため、円筒型、角型、コイン型およびボタン型などの他の電池構造でもよい。
　また、電池素子の素子構造が巻回型である場合に関して説明したが、その電池素子の素子構造は、特に限定されないため、電極（正極および負極）が積層された積層型および電極（正極および負極）がジグザグに折り畳まれた九十九折り型などの他の素子構造でもよい。
　また、電極反応物質がリチウムである場合に関して説明したが、その電極反応物質は、特に限定されない。具体的には、電極反応物質は、上記したように、ナトリウムおよびカリウムなどの他のアルカリ金属でもよいし、ベリリウム、マグネシウムおよびカルシウムなどのアルカリ土類金属でもよい。この他、電極反応物質は、アルミニウムなどの他の軽金属でもよい。
　さらに、正極が二次電池に用いられる場合に関して説明したが、その正極の用途は、特に限定されないため、キャパシタなどの他の電子デバイスでもよい。
　本明細書中に記載された効果は、あくまで例示であるため、本技術の効果は、本明細書中に記載された効果に限定されない。よって、本技術に関して、他の効果が得られてもよい。

Claims (10)

  1. 　１５μｍ以上３０μｍ以下のメジアン径Ｄ５０を有すると共に、リチウム含有化合物を含む複数の第１粒子と、
    　１μｍ以上１０μｍ以下のメジアン径Ｄ５０を有すると共に、リチウム含有化合物を含む中心部と前記中心部の表面に設けられた被覆部とを含む複数の第２粒子と
    　を備え、
    　前記被覆部は、前記中心部に近い側から順に、
    　金属原子にアルキル基が結合されていない第１金属アルコキシドの反応物を含む下地層と、
    　前記金属原子に前記アルキル基が結合されている第２金属アルコキシドの反応物を含むと共に、前記第２金属アルコキシドの反応物が前記第１金属アルコキシドの反応物に結合されている表面層と
    　を含む、二次電池用正極活物質。
  2. 　前記金属原子は、ケイ素原子、チタン原子、アルミニウム原子およびジルコニウム原子のうちのいずれかである、
    　請求項１記載の二次電池用正極活物質。
  3. 　前記金属原子は、前記ケイ素原子である、
    　請求項２記載の二次電池用正極活物質。
  4. 　前記第１金属アルコキシドは、式（４）で表される化合物を含み、
    　前記第２金属アルコキシドは、式（５）で表される化合物を含む、
    　請求項１ないし請求項３のいずれか１項に記載の二次電池用正極活物質。
    　Ｍ１１－ＯＲ１１a 　・・・（４）
    （Ｍ１１は、金属原子である。Ｒ１１は、炭素数が１以上１０以下のアルキル基である。ａは、Ｍ１１の価数に応じて決定される値である。）
    　Ｒ１２－Ｍ１２－ＯＲ１３b 　・・・（５）
    （Ｍ１２は、金属原子である。Ｒ１２は、炭素数が８以上３０以下のアルキル基であると共に、Ｒ１３は、炭素数が１以上１０以下のアルキル基である。ｂは、Ｍ１２の価数に応じて決定される値である。）
  5. 　前記リチウム含有化合物は、式（１）～式（３）のそれぞれで表される化合物のうちの少なくとも１種を含む、
    　請求項１ないし請求項４のいずれか１項に記載の二次電池用正極活物質。
    　Ｌｉa Ｎｉ(1-b-c) Ｍｎb Ｍ１c Ｏ(2-d) Ｘe 　・・・（１）
    （Ｍ１は、長周期型周期表の２族～１５族に属する元素（ただし、ＮｉおよびＭｎを除く。）のうちの少なくとも１種である。Ｘは、長周期型周期表の１６族および１７族に属する元素（ただし、Ｏを除く。）のうちの少なくとも１種である。ａ、ｂ、ｃ、ｄおよびｅは、０≦ａ≦１．５、０≦ｂ≦１、０≦ｃ≦１、－０．１≦ｄ≦０．２および０≦ｅ≦０．２を満たす。）
    　Ｌｉa Ｃｏ(1-b) Ｍ２b Ｏ(2-c) 　・・・（２）
    （Ｍ２は、Ｖ、Ｃｕ、Ｚｒ、Ｚｎ、Ｍｇ、Ａｌ、Ｇａ、ＹおよびＦｅのうちの少なくとも１種である。ａ、ｂおよびｃは、０．９≦ａ≦１．１、０≦ｂ≦０．３および－０．１≦ｃ≦０．１を満たす。）
    　Ｌｉa Ｎｉb Ｃｏc Ｍｎd Ｍ３(1-b-c-d) Ｏ(2-e) 　・・・（３）
    （Ｍ３は、Ｖ、Ｃｕ、Ｚｒ、Ｚｎ、Ｍｇ、Ａｌ、Ｇａ、ＹおよびＦｅのうちの少なくとも１種である。ａ、ｂ、ｃ、ｄおよびｅは、－０．１≦ａ≦０．１、０．９≦ｂ≦１．１、０＜ｃ＜１、０＜ｄ＜１、０＜ｅ＜０．５および０≦１－ｂ－ｃ－ｄを満たす。）
  6. 　前記下地層は、さらに、２つの前記金属原子がアルキレン基を介して互いに結合されている第３金属アルコキシドの反応物を含む、
    　請求項１ないし請求項５のいずれか１項に記載の二次電池用正極活物質。
  7. 　前記第３金属アルコキシドは、式（６）で表される化合物を含む、
    　請求項６記載の二次電池用正極活物質。
    　（Ｒ１５Ｏ）c －Ｍ１３－Ｒ１４－Ｍ１４－（ＯＲ１６）d 　・・・（６）
    （Ｍ１３およびＭ１４のそれぞれは、金属原子である。Ｒ１４は、炭素数が１以上１０以下のアルキレン基であると共に、Ｒ１５およびＲ１６のそれぞれは、炭素数が１以上１０以下のアルキル基である。ｃは、Ｍ１３の価数に応じて決定される値であると共に、ｄは、Ｍ１４の価数に応じて決定される値である。）
  8. 　請求項１ないし請求項７のいずれか１項に記載の二次電池用正極活物質を含む正極活物質層を備えた、二次電池用正極。
  9. 　請求項８記載の二次電池用正極と、
    　負極と、
    　電解液と
    　を備えた、二次電池。
  10. 　リチウムイオン二次電池である、
    　請求項９記載の二次電池。
PCT/JP2020/046511 2020-01-31 2020-12-14 二次電池用正極活物質、二次電池用正極および二次電池 WO2021153044A1 (ja)