WO2021125020A1 - ポリビニルアルコール系樹脂組成物、懸濁重合用分散安定剤及びビニル系樹脂の製造方法 - Google Patents

ポリビニルアルコール系樹脂組成物、懸濁重合用分散安定剤及びビニル系樹脂の製造方法 Download PDF

Info

Publication number
WO2021125020A1
WO2021125020A1 PCT/JP2020/045918 JP2020045918W WO2021125020A1 WO 2021125020 A1 WO2021125020 A1 WO 2021125020A1 JP 2020045918 W JP2020045918 W JP 2020045918W WO 2021125020 A1 WO2021125020 A1 WO 2021125020A1
Authority
WO
WIPO (PCT)
Prior art keywords
vinyl
polyvinyl alcohol
based resin
polymerization
alcohol
Prior art date
Application number
PCT/JP2020/045918
Other languages
English (en)
French (fr)
Inventor
渡辺　亘
真典 松本
Original Assignee
デンカ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by デンカ株式会社 filed Critical デンカ株式会社
Priority to CN202080071275.8A priority Critical patent/CN114555696B/zh
Priority to US17/764,914 priority patent/US20220348756A1/en
Priority to EP20901825.8A priority patent/EP4079769A4/en
Priority to JP2021565520A priority patent/JP7483754B2/ja
Publication of WO2021125020A1 publication Critical patent/WO2021125020A1/ja

Abstract

塩化ビニルのようなビニル系化合物を懸濁重合するに際して、微細で粒度の均一性が高く、かさ比重が高く、可塑剤吸収性が適正な樹脂粒子を得るのに適した分散安定剤として有用なポリビニルアルコール系樹脂組成物を提供する。一般式（Ｉ）に示すポリオキシアルキレン単位がポリビニルアルコール鎖と結合した変性ビニルアルコール系重合体（Ａ）と、ポリビニルアルコール鎖に二重結合を有する変性ビニルアルコール系重合体（Ｂ）を含むポリビニルアルコール系樹脂組成物。（式中、Ｒ1及びＲ2はそれぞれ独立にメチル基又はエチル基又は水素原子であり、Ｒ3はアルキル基又は水素原子である。ｎは繰り返し単位数を表し、５≦ｎ≦７０の整数である。）

Description

ポリビニルアルコール系樹脂組成物、懸濁重合用分散安定剤及びビニル系樹脂の製造方法
　本発明は、変性ビニルアルコール系重合体を含むポリビニルアルコール系樹脂組成物に関する。また、本発明は、懸濁重合用分散安定剤、とりわけビニル系化合物、特に塩化ビニルの懸濁重合に適した分散安定剤に関するものである。
　塩化ビニル単量体又は塩化ビニル単量体とこれに共重合し得る単量体との混合物を懸濁重合する場合において、各種の分散安定剤を使用することは必須であり、ポリビニルアルコール、メチロールセルロース等の分散安定剤が用いられているが、中でもポリビニルアルコール（ＰＶＡ）は優れた性質を有しており、一般に最も使用されている。例えば、ビニル系化合物の懸濁重合用分散安定剤として、ビニルアルコール系重合体の末端にアルデヒド由来のカルボニル基を導入し、ケン化時に脱水反応又は脱酢酸反応を受けることで不飽和二重結合を導入することや（例えば特許文献１参照）、側鎖に特定のオキシアルキレン基を有する変性ＰＶＡを用いる方法等が提案されている（例えば特許文献２～３参照）。
特開平８－２０８７２４号公報 国際公開第２０１０／１１３５６９号 国際公開第２０１３／１１５２３９号
　これらの方法では、近年用いられる大型重合缶等、様々なタイプの重合缶に充分対応できていない。すなわち、分散力が乏しく可塑剤吸収性の低いビニル系樹脂粒子となったり、分散力が強い一方で保護コロイド性に乏しく粗大化したビニル系樹脂粒子が得られ加工性が低下したり、微細なビニル系樹脂粒子ではあるがかさ比重が低い等、安定して満足したビニル系樹脂粒子を得るのには不十分であった。
　上記事情に鑑み、本発明は一実施形態において、塩化ビニルのようなビニル系化合物を懸濁重合するに際して、微細で粒度の均一性が高く、かさ比重が高く、可塑剤吸収性が適正な樹脂粒子を得るのに適した分散安定剤として有用なポリビニルアルコール系樹脂組成物を提供することを課題の一つとする。
　本発明者等は、上記の課題を解決すべく鋭意研究を重ねた結果、所定のポリオキシアルキレン単位（以下、「アルキレン変性基」という。）を有する変性ビニルアルコール系重合体（Ａ）と、ポリビニルアルコール鎖に二重結合を有する変性ビニルアルコール系重合体（Ｂ）を含むポリビニルアルコール系樹脂組成物を使用することが有効であることを見出した。
　従って、本発明は一側面において、一般式（Ｉ）に示すポリオキシアルキレン単位がポリビニルアルコール鎖と結合した変性ビニルアルコール系重合体（Ａ）と、ポリビニルアルコール鎖に二重結合を有する変性ビニルアルコール系重合体（Ｂ）を含むポリビニルアルコール系樹脂組成物である。
Figure JPOXMLDOC01-appb-C000002
 （式中、Ｒ1及びＲ2はそれぞれ独立にメチル基又はエチル基又は水素原子であり、Ｒ3はアルキル基又は水素原子である。ｎは繰り返し単位数を表し、５≦ｎ≦７０の整数である。）
　本発明の一側面に係るポリビニルアルコール系樹脂組成物の一実施形態においては、前記変性ビニルアルコール系重合体（Ａ）と前記変性ビニルアルコール系重合体（Ｂ）との重量比（Ａ／Ｂ）が１５／８５～８５／１５である。
　本発明の一側面に係るポリビニルアルコール系樹脂組成物の別の一実施形態においては、前記変性ビニルアルコール系重合体（Ｂ）の０．２重量％水溶液の、光路長１ｃｍ、波長２８０ｎｍにおけるＵＶ吸光度（Ａｂｓ）が０．１以上３．０以下である。
　本発明に係るポリビニルアルコール系樹脂組成物の更に別の一実施形態においては、前記変性ビニルアルコール系重合体（Ａ）のポリオキシアルキレン単位の変性率が０．０１～５モル％である。
　本発明は別の一側面において、本発明に係るポリビニルアルコール系樹脂組成物を含有する懸濁重合用分散安定剤である。
　本発明は更に別の一側面において、本発明に係る懸濁重合用分散安定剤を用いて、ビニル系化合物単量体、又はビニル系化合物単量体とそれに共重合し得る単量体との混合物を水中に分散させて懸濁重合を行うことを含むビニル系樹脂の製造方法である。
　本発明の懸濁重合用分散安定剤を用いてビニル系化合物の懸濁重合を行った場合には、粗大粒子の形成が少なく、粒子径の均一性が高い樹脂粒子が得られる。粗大粒子の形成が少ないために重合時のブロック化が抑制され、粒子径の均一性が高い粒子が得られることからスケール付着が低減する。また、高いかさ比重の樹脂が得られ、樹脂加工時の生産性が向上する。更に、可塑剤吸収性が適正な樹脂粒子を得ることも可能となる。このように、本発明の懸濁重合用分散安定剤は従来技術では達成することが難しかった要求性能を兼備することができる。
　本発明の懸濁重合用分散安定剤は一実施形態において、一般式（Ｉ）に示すポリオキシアルキレン単位がポリビニルアルコール鎖と結合した変性ビニルアルコール系重合体（Ａ）と、ポリビニルアルコール鎖に二重結合を有する変性ビニルアルコール系重合体（Ｂ）を含む。なお、以下の説明における「変性ＰＶＡ」は変性ビニルアルコール系重合体を指す。
Figure JPOXMLDOC01-appb-C000003
 （式中、Ｒ1及びＲ2はそれぞれ独立にメチル基又はエチル基又は水素原子であり、Ｒ3はアルキル基又は水素原子である。ｎは繰り返し単位数を表し、５≦ｎ≦７０の整数である。）
　一般式（Ｉ）においてｎは５以上が好ましく、１０以上がより好ましく、１５以上が更により好ましく、２０以上が最も好ましい。また、ｎは７０以下が好ましく、６０以下がより好ましい。
　Ｒ3を表すアルキル基は、例えば炭素数が１～１０のアルキル基とすることができ、炭素数が１～５のアルキル基が好ましく、炭素数が１～３のアルキル基がより好ましい。Ｒ3を表すアルキル基の具体例としては、メチル基、エチル基、ｎ－プロピル基、イソプロピル基が挙げられる。
　一般式（Ｉ）に示す部分は、エーテル結合及び／又は炭素－炭素結合のみを介してポリビニルアルコール鎖と結合していることがｐＨの変化で脱離し、性能を発揮できないことを防止する観点から好ましい。
　一実施形態において、ポリビニルアルコール鎖に二重結合を有する変性ビニルアルコール系重合体（Ｂ）は、一般式（ＩＩ）に示す構造をポリビニルアルコール鎖内に有する。
Figure JPOXMLDOC01-appb-C000004
 （式中、ｎは繰り返し単位数を表し、１≦ｎ≦１０の整数である。）
　一般式（ＩＩ）においてｎは１以上が好ましく、２以上がより好ましい。また、ｎは１０以下が好ましく、５以下がより好ましい。
　本発明のポリビニルアルコール系樹脂組成物は前記変性ビニルアルコール系重合体（Ａ）と前記変性ビニルアルコール系重合体（Ｂ）との重量比（Ａ／Ｂ）が１５／８５～８５／１５であることが好ましい。前記重量比（Ａ／Ｂ）が１５／８５以下となると、分散力が発揮されず、結果としてビニル系樹脂の可塑剤吸収性が低下する。また、重量比（Ａ／Ｂ）が８５／１５以上となると、変性ビニルアルコール系重合体（Ｂ）に起因する保護コロイド性が不足し、ビニル系樹脂が粗大化してしまう懸念がある。したがって、前記変性ビニルアルコール系重合体（Ａ）と前記変性ビニルアルコール系重合体（Ｂ）との重量比（Ａ／Ｂ）が１５／８５～８５／１５であることが好ましく、２０／８０～８０／２０がより好ましく、２５／７５が更により好ましい。なお、本発明においては、一般式（Ｉ）に示すポリオキシアルキレン単位がポリビニルアルコール鎖と結合しており、且つ、ポリビニルアルコール鎖に二重結合を有する変性ビニルアルコール系重合体は、変性ビニルアルコール系重合体（Ａ）及び変性ビニルアルコール系重合体（Ｂ）の何れにも該当しないものとして取り扱う。
　前記変性ビニルアルコール系重合体（Ｂ）は０．２重量％水溶液の、光路長１ｃｍ、波長２８０ｎｍにおけるＵＶ吸光度（Ａｂｓ）が０．１以上３．０以下であることが好ましい。この波長２８０ｎｍの吸収は共役二重結合の二連鎖に相当し、吸光度が０．１未満であると、二重結合が不足し、保護コロイド性が低下したりするため、結果として適度な粒子径を有するビニル系樹脂を得にくい。また、吸光度が３．０以上とすると着色が顕著になり、分散剤として使用した際、ビニル系樹脂の着色に影響を与える。また、化学的に不安定となり、水溶液の粘度が高くなったり、ゲル化したりする場合がある。そのため、変性ビニルアルコール系重合体（Ｂ）の０．２重量％水溶液の波長２８０ｎｍにおけるＵＶ吸光度は０．１以上３．０以下が必要であり、０．２以上２．５以下が好ましく、０．３以上２．０以下が更に好ましい。
　前記変性ビニルアルコール系重合体（Ａ）は、一般式（Ｉ）で示されるポリオキシアルキレン単位の種類にも依存するが、当該アルキレン単位の変性率（以下、「アルキレン変性率」ともいう。）が０．０１モル％以上５モル％以下であることが好ましい。アルキレン変性率が５モル％を超えると、変性ＰＶＡ（Ａ）の一分子当りに含まれる親水基・疎水基のバランスが保てず、分散力が強い一方で保護コロイド性に乏しくなることがあり、その場合は懸濁重合用分散安定剤として用いることが困難となる。よって、アルキレン変性率は５モル％以下であることが好ましく、４モル％以下であることがより好ましく、２モル％以下であることが更により好ましい。一方、アルキレン変性率が０．０１モル％未満の場合、該変性ＰＶＡ（Ａ）中に含まれる変性基の数が少なく、要求物性が十分に発現しない。よって、アルキレン変性率は０．０１モル％以上であることが重要であり、０．０５モル％以上であることが好ましく、０．１モル％以上であることがより好ましい。
　アルキレン変性率とは、変性ＰＶＡ（Ａ）のポリビニルアルコール鎖を構成する全単量体単位のモル数に対する、上記一般式（Ｉ）に示す部分を有するポリオキシアルキレン単位と結合している前記単量体単位のモル数の割合（モル％）である。アルキレン変性率はプロトンＮＭＲで求めることができる。具体的には、変性ＰＶＡをケン化度９９．９５モル％以上にケン化した後、十分にメタノール洗浄を行い、分析用の変性ＰＶＡを作製する。作製した分析用の変性ＰＶＡを重水に溶解し、更にＮａＯＨ重水溶液を数滴加えｐＨ＝１４にした後、プロトンＮＭＲを用いて８０℃で測定する。オキシエチレン部分（例：Ｒ1＝Ｈ、Ｒ2＝Ｈ）から算出する場合、変性ＰＶＡのポリビニルアルコール鎖のメチレン基に帰属される１．２～１．８ｐｐｍのピークの積分値と、オキシエチレン部分に帰属される３．６～３．７ｐｐｍのピークの積分値とから常法により含有量を算出する。具体的には、変性ＰＶＡのポリビニルアルコール鎖のメチレン基の積分値をｂとし、オキシエチレン部分の積分値をａ、オキシエチレン部分の繰り返し単位数をｘとすると、プロトン数（メチレン基は２Ｈ、エチレン基は４Ｈ）を鑑み、アルキレン変性率は｛ａ／（４×ｘ）｝／（ｂ／２）×１００（ｍｏｌ％）と計算される。例えば、ａ＝１、ｘ＝１、ｂ＝１００の場合は、０．５ｍｏｌ％と計算される。また、オキシブチレン又はオキシプロピレン部分から算出する場合、変性ＰＶＡのポリビニルアルコール鎖のメチレン基に帰属される１．２～１．８ｐｐｍのピークの積分値と、オキシブチレン部分（Ｒ1＝Ｈ、Ｒ2＝ＣＨ2ＣＨ3（又はＲ1＝ＣＨ2ＣＨ3、Ｒ2＝Ｈ））又はオキシプロピレン部分（Ｒ1＝Ｈ、Ｒ2＝ＣＨ3（又はＲ1＝ＣＨ3、Ｒ2＝Ｈ））の末端メチル基に帰属される０．８０～０．９５ｐｐｍのピークの積分値とから常法により含有量を算出する。具体的には、変性ＰＶＡのポリビニルアルコール鎖のメチレン基の積分値をｂとし、オキシブチレン部分又はオキシプロピレン部分の積分値をｃ、繰り返し単位数をｙとすると、プロトン数（メチレン基は２Ｈ、メチル基は３Ｈ）を鑑み、アルキレン変性率は｛ｃ／（３×ｙ）｝／（ｂ／２）×１００（ｍｏｌ％）と計算される。例えば、ｃ＝１、ｙ＝１、ｂ＝１００の場合は、０．６７ｍｏｌ％と計算される。なお、変性ＰＶＡがオキシエチレン部分と、オキシプロピレン部分又はオキシブチレン部分との双方を有する場合は、オキシエチレン部分から算出されるアルキレン変性率よりも、オキシプロピレン部分又はオキシブチレン部分の末端メチル基に帰属されるピークの積分値に基づいて算出されるアルキレン変性率のほうが測定精度が高いため、両者の値に相違がある場合には、オキシプロピレン部分又はオキシブチレン部分の末端メチル基に帰属されるピークの積分値に基づいて算出されるアルキレン変性率を採用することとする。
　前記変性ビニルアルコール系重合体（Ａ）の粘度平均重合度は、ビニル系化合物を懸濁重合する際の分散安定性を高めるために４００以上であることが好ましく、５００以上であることがより好ましい。また、変性ＰＶＡの粘度平均重合度は分散力を低下させないために３０００以下であることが好ましく、２０００以下であることがより好ましく、１５００以下であることが更により好ましく、１０００以下であることが更により好ましい。
　前記変性ビニルアルコール系重合体（Ｂ）の粘度平均重合度は、ビニル系化合物を懸濁重合する際の分散安定性を高めるために６００以上であることが好ましく、７００以上であることがより好ましい。また、変性ＰＶＡの粘度平均重合度は分散力を低下させないために４０００以下であることが好ましく、３０００以下であることがより好ましく、２０００以下であることが更により好ましく、１５００以下であることが更により好ましい。
　粘度平均重合度は、ＪＩＳ　Ｋ６７２６：１９９４に準拠して測定される。すなわち、変性ＰＶＡを完全にケン化し、精製した後、３０℃の水またはジメチルスルホキシド（ＤＭＳＯ）中で測定した極限粘度［η］から求める。
　前記変性ビニルアルコール系重合体（Ａ）のケン化度は、水溶性の観点から、６５モル％以上であることが必要である。また、変性ＰＶＡのケン化度は、ビニル系化合物を懸濁重合した際に得られる粒子のポロシティを高めて可塑剤吸収性を高めるために、９９．９モル％以下であることが好ましく、９０モル％以下であることがより好ましく、８０モル％以下であることが更により好ましい。
　前記変性ビニルアルコール系重合体（Ｂ）のケン化度は、水溶性の観点から、６５モル％以上であることが必要である。また、変性ＰＶＡのケン化度は、ビニル系化合物を懸濁重合した際に得られる粒子のポロシティを高めて可塑剤吸収性を高めるために、９９．９モル％以下であることが好ましく、９０モル％以下であることがより好ましく、８０モル％以下であることが更により好ましい。
　変性ＰＶＡのケン化度は、ＪＩＳ　Ｋ６７２６：１９９４に準拠して測定される。すなわち、水酸化ナトリウムで試料中の残存酢酸基（モル％）を定量し、１００から差し引くことで求めることができる。
　前記変性ビニルアルコール系重合体（Ａ）の製造方法は特に制限されず、ＰＶＡの水酸基とポリオキシアルキレン基及び有機酸を反応させ、グラフトする方法等を用いることができるが、酢酸ビニルに代表されるビニルエステル系単量体を、有機酸の共存下で、一般式（Ｉ）に示すポリオキシアルキレン単位を有する不飽和単量体と共重合して変性ビニルエステル系重合体を得る工程と、得られた変性ビニルエステル系重合体をケン化する方法が容易で経済的であり、好適に用いられる。
　一般式（Ｉ）で示される変性構造を誘導する不飽和単量体としてはポリオキシアルキレンアルケニルエーテル、ポリオキシアルキレンモノ（メタ）アリルエーテル、ポリオキシアルキレンモノビニルエーテル等が挙げられ、具体的には、ポリオキシブチレンポリオキシエチレンアルケニルエーテル、ポリオキシプロピレンポリオキシエチレンアルケニルエーテル、ポリオキシブチレンアルケニルエーテル、ポリオキシブチレンポリオキシプロピレンアルケニルエーテル、ポリオキシプロピレンアルケニルエーテル、ポリオキシプロピレンポリオキシエチレンアルケニルエーテル、ポリオキシブチレンポリオキシエチレンモノアリルエーテル、ポリオキシプロピレンポリオキシエチレンモノアリルエーテル、ポリオキシブチレンモノアリルエーテル、ポリオキシブチレンポリオキシプロピレンモノアリルエーテル、ポリオキシプロピレンモノアリルエーテル、ポリオキシプロピレンポリオキシエチレンモノアリルエーテル、ポリオキシブチレンポリオキシエチレンモノビニルエーテル、ポリオキシプロピレンポリオキシエチレンモノビニルエーテル、ポリオキシブチレンモノビニルエーテル、ポリオキシブチレンポリオキシプロピレンモノビニルエーテル、ポリオキシプロピレンモノビニルエーテル、ポリオキシプロピレンポリオキシエチレンモノビニルエーテルなどが挙げられる。なかでも、下記の一般式（ＩＩＩ）に示すようなエーテルが反応性や性能の面から更に好適に用いられる。一般式（ＩＩＩ）に示すようなポリオキシアルキレンアルケニルエーテルの具体例としては、ポリオキシブチレンポリオキシエチレンアルケニルエーテルが挙げられる。
Figure JPOXMLDOC01-appb-C000005
 （一般式（ＩＩＩ）中、Ｒ1及びＲ2はそれぞれ独立にメチル基又はエチル基又は水素原子であり、Ｒ3はアルキル基又は水素原子である。ｎは繰り返し単位数を表し、５≦ｎ≦７０の整数である。Ｒ4及びＲ5は一方がメチル基又はエチル基であり、他方が水素原子である。ｍは繰り返し単位数を表し、１≦ｍ≦３０の整数である。但し、繰り返し単位数ｎの部分と、繰り返し単位数ｍの部分は異なる。）
　ビニルエステル系単量体としては、酢酸ビニルの他、蟻酸ビニル、プロピオン酸ビニル、バレリン酸ビニル、カプリン酸ビニル、ラウリン酸ビニル、ステアリン酸ビニル、安息香酸ビニル、ピバリン酸ビニル及びバーサティック酸ビニル等が挙げられる。
　前記変性ビニルアルコール系重合体（Ｂ）に一般式（ＩＩ）に示すような二重結合を導入する方法としては、特に限定されず、周知の重合方法、例えば無変性ＰＶＡ系樹脂を過酸化水素や過ヨウ素酸などの酸化剤で酸化処理し熱処理する方法、たとえば、カルボニル基を含有するアルデヒドやケトンなどの連鎖移動剤や不飽和カルボン酸のような共重合モノマー共存下で重合し、得られたポリ酢酸ビニルをケン化して脱水反応を起こして導入する方法、酸素を吹き込みながら重合し、得られたポリ酢酸ビニルをケン化して脱水反応を起こして導入する方法が挙げられる。工業的にはカルボニル基を含有するアルデヒドやケトンなどの連鎖移動剤や不飽和カルボン酸のような共重合モノマー共存下で重合し、得られたポリ酢酸ビニルをケン化して脱水反応を起こしてポリビニルアルコール鎖に炭素－炭素二重結合を有する変性ＰＶＡ系樹脂を得る方法が特に有利である。
　前記変性ビニルアルコール系重合体（Ｂ）に二重結合を誘導するための変性種としては、ビニルエステル系単量体と共重合できるマレイン酸ジメチル、マレイン酸モノメチル等の不飽和カルボン酸アルキルエステル、アセトアルデヒド、プロピオンアルデヒド、ｎ－ブチルアルデヒド等のアルキルアルデヒド、四塩化炭素やブロモブタン等のハロゲン系炭化水素が挙げられる。
　本共重合を行うのに採用される重合方式としては、回分重合、半回分重合、連続重合、半連続重合のいずれでもよい。重合方法としては、塊状重合法、溶液重合法、懸濁重合法、乳化重合法等公知の方法の中から、任意の方法を採用することができる。その中でも、用いる変性種は重合粒子径に影響を与える水溶性や界面活性能を持つことが多いため重合粒子径を制御する必要のある懸濁重合及び乳化重合ではなく、アルコール系溶媒存在下で重合を行う溶液重合法又は溶媒を用いないで重合を行う塊状重合法が好適に採用される。溶液重合法に用いられるアルコール系溶媒としては、メタノール、エタノール、イソプロパノール等を用いることができるが、これらに限定されるものではない。またこれらの溶媒は単独で使用してもよいし、２種類以上のものを併用することもできる。
　ビニルエステル系単量体をラジカル重合する際の重合開始剤は、特に限定するものではないが、アゾビスイソブチロニトリル、アゾビス－２，４－ジメチルバレロニトリル、アゾビス（４－メトキシ－２，４－ジメチルバレロニトリル）、アゾビスジメチルバレロニトリル、アゾビスメトキシバレロニトリルなどのアゾ化合物、アセチルパーオキサイド、ベンゾイルパーオキサイド、ラウロイルパーオキサイド、アセチルシクロヘキシルスルホニルパーオキサイド、２，４，４－トリメチルペンチル－２－パーオキシフェノキシアセテートなどの過酸化物、ジイソプロピルパーオキシジカーボネート、ジ－２－エチルヘキシルパーオキシジカーボネート、ジエトキシエチルパーオキシジカーボネートなどのパーカーボネート化合物、ｔ－ブチルパーオキシネオデカネート、α－クミルパーオキシネオデカネートなどのパーエステル化合物などを単独で又は二種以上組み合わせて使用することができる。
　また、共重合を高い温度で行った場合、ビニルエステル系単量体の分解に起因するＰＶＡの着色等が見られることがある。その場合には着色防止の目的で重合系にクエン酸のような酸化防止剤を１ｐｐｍ以上１００ｐｐｍ以下（ビニルエステル系単量体の質量に対して）程度添加することはなんら差し支えない。
　本発明に係る変性ＰＶＡを製造する際のケン化方法も特に限定されるものではなく、前述した方法で得られた重合体を、常法に従い、アルコール類を溶媒兼用で用いることが好ましい。アルコールとしてはメタノール、エタノール、ブタノール等が挙げられる。アルコール中の重合体の濃度は２０～５０質量％の範囲から選ぶことができる。アルカリ触媒としては水酸化ナトリウム、水酸化カリウム、ナトリウムメチラート、ナトリウムエチラート、カリウムメチラート等のアルカリ金属の水酸化物やアルコラートの如きアルカリ触媒を用いることができ、酸触媒としては、塩酸、硫酸等の無機酸水溶液、ｐ－トルエンスルホン酸等の有機酸を用いることができる。これら触媒の使用量はビニルエステル系単量体に対して１～１００ミリモル当量にすることが必要である。ケン化温度は特に制限はないが、通常１０～７０℃の範囲であり、好ましくは３０～５０℃の範囲から選ぶのが望ましい。反応は通常０．５～３時間にわたって行われる。
　本発明の懸濁重合用分散安定剤は、本発明の趣旨を損なわない範囲で、上記変性ＰＶＡ以外のＰＶＡや、その他の各種添加剤を含有してもよい。該添加剤としては、例えば、アルデヒド類、ハロゲン化炭化水素類、メルカプタン類などの重合調整剤；フェノール化合物、イオウ化合物、Ｎ－オキサイド化合物などの重合禁止剤；ｐＨ調整剤；架橋剤；防腐剤；防黴剤、ブロッキング防止剤；消泡剤等が挙げられる。本発明の効果を有意に発揮するという観点から、本発明の懸濁重合用分散安定剤は変性ＰＶＡ（Ａ）及び変性ＰＶＡ（Ｂ）を合計で１０質量％以上含有することが好ましく、３０質量％以上含有することがより好ましく、７０質量％以上含有することが更により好ましい。
　本発明の懸濁重合用分散安定剤は、特にビニル系化合物の懸濁重合に好適に用いることができる。従って、本発明の別の一側面によれば、懸濁重合用分散安定剤を用いて、ビニル系化合物単量体、又はビニル系化合物単量体とそれに共重合し得る単量体との混合物を水中に分散させて懸濁重合を行うことを含むビニル系樹脂の製造方法が提供される。
　ビニル系化合物としては、塩化ビニル等のハロゲン化ビニル；酢酸ビニル、プロピオン酸ビニル等のビニルエステル；アクリル酸、メタクリル酸、これらのエステル及び塩；マレイン酸、フマル酸、これらのエステル及び無水物；スチレン、アクリロニトリル、塩化ビニリデン、ビニルエーテル等が挙げられる。これらの中でも、本発明の一実施形態に係る懸濁重合用分散安定剤は、特に好適には塩化ビニルを単独で、又は塩化ビニルを塩化ビニルと共重合することが可能な単量体と共に懸濁重合する際に用いられる。塩化ビニルと共重合することができる単量体としては、酢酸ビニル、プロピオン酸ビニルなどのビニルエステル；（メタ）アクリル酸メチル、（メタ）アクリル酸エチルなどの（メタ）アクリル酸エステル；エチレン、プロピレンなどのα－オレフィン；無水マレイン酸、イタコン酸などの不飽和ジカルボン酸類；アクリロニトリル、スチレン、塩化ビニリデン、ビニルエーテル等が挙げられる。
　本発明の懸濁重合用分散安定剤は、単独でもまた他の安定剤、例えばセルロース系誘導体、界面活性剤等と併用することができる。
　本発明の懸濁重合用分散安定剤を使用することにより、樹脂粒子のかさ比重が高く、粒度分布が均一で物性の非常に優れた塩化ビニル樹脂が得られる。以下、ビニル系化合物の重合法について例を挙げ具体的に説明するが、これらに限定されるものではない。
　塩化ビニル樹脂粒子等のビニル系化合物の樹脂粒子を製造する場合には、ビニル系化合物単量体に対し、上述の懸濁重合用分散安定剤を０．０１質量％～０．３質量％、好ましくは０．０４質量％～０．１５質量％添加する。また、ビニル系化合物と水の比は質量比でビニル系化合物：水＝１：０．９～１：３とすることができ、好ましくはビニル系化合物：水＝１：１～１：１．５である。
　重合開始剤は、ビニル系化合物の重合に従来使用されているものでよく、これにはジイソプロピルパーオキシジカーボネート、ジ－２－エチルヘキシルパーオキシジカーボネート、ジエトキシエチルパーオキシジカーボネート等のパーカーボネート化合物、ｔ－ブチルパーオキシネオデカノエート、α－クミルパーオキシネオデカノエート等のパーエステル化合物、アセチルシクロヘキシルスルホニルパーオキシド、２，４，４－トリメチルペンチル－２－パーオキシフェノキシアセテート等の過酸化物、アゾビス－２，４－ジメチルバレロニトリル、アゾビス（４－メトキシ－２，４－ジメチルパレロニトリル）等のアゾ化合物、更には過硫酸カリウム、過硫酸アンモニウム、過酸化水素等を単独又は組み合わせて使用することができる。
　更に、ビニル系化合物の重合に適宜使用される重合調整剤、連鎖移動剤、ゲル化改良剤、帯電防止剤、ＰＨ調整剤等を添加することも任意である。
　ビニル系化合物の重合を実施するに当たっての各成分の仕込み割合、重合温度等はビニル系化合物の懸濁重合で従来採用されている条件に準じて定めればよく、特に限定する理由は存在しない。
　以下、本発明について実施例を挙げて更に詳しく説明する。
（ＰＶＡ１の製造）
　酢酸ビニル１８５０ｇ、メタノール１０００ｇ、変性種として一般式（ＩＩＩ）で示され、ｍ＝５～９、ｎ＝４５～５５であるポリオキシアルキレンアルケニルエーテル（単量体Ａ）１３３ｇを重合缶に仕込み、３０分間系内を窒素置換した。単量体Ａについてｍ＝５～９、ｎ＝４５～５５であることは、ＮＭＲにより確認した。アゾビスイソブチロニトリル０．２５ｇを重合缶に仕込み、６０℃で９時間重合した後、冷却して重合を停止した。次いで常法により未反応の酢酸ビニルを除去し、得られた重合体を常法により水酸化ナトリウムメタノール溶液でケン化してＰＶＡ１を作製した。得られたＰＶＡ１の粘度平均重合度、ケン化度及び変性率を先述した分析法によって測定したところ、粘度平均重合度は７５０、ケン化度は７３モル％、変性率は０．１８モル％であった。
　紫外可視近赤外分光光度計（（株）島津製作所製分光光度計ＵＶ１８００）を用いて、光路長１ｃｍ、波長２８０ｎｍにおける、ポリビニルアルコール系分散剤の０．２重量％水溶液の吸光度を測定したところ、０．０２Ａｂｓであった。なお、厚さ１ｃｍの試料容器（セル）を用いた。
（ＰＶＡ２の製造）
　酢酸ビニル１８００ｇ、メタノール６１２ｇ、マレイン酸ジメチル４ｇを重合缶に仕込み、３０分間系内を窒素置換した。アゾビスイソブチロニトリル０．３ｇを重合缶に仕込み、酢酸ビニル４００ｇ、マレイン酸ジメチル３５ｇを滴下しながら、６０℃で１１時間重合した後、滴下を止め、冷却して重合を停止した。次いで常法により未反応の酢酸ビニルを除去し、得られた重合体を常法により水酸化ナトリウムメタノール溶液でケン化してＰＶＡ２を作製した。有機酸変性率を求める方法は特に限定されず、酸価等で求めることができるが、プロトンＮＭＲで求めるのが簡便であるのでここではプロトンＮＭＲにより求めた。具体的には、変性ＰＶＡをケン化度９９．９５モル％以上に完全にケン化した後、十分にメタノール洗浄を行い、分析用の変性ＰＶＡを作製する。変性種としてマレイン酸ジメチルを使用する場合、完全にケン化する過程で、カルボキシル基が生成する。従って、変性種の変性率は、有機酸変性率に等しい。作製した分析用の変性ＰＶＡを重水に溶解し、更にＮａＯＨ重水溶液を数滴加えｐＨ＝１４にした後、８０℃で測定し1Ｈ－ＮＭＲスペクトルを得た。変性ＰＶＡのポリビニルアルコール鎖のメチレン基（１．２～１．８ｐｐｍ）のピークの積分値を基準として有機酸変性率を算出した。例えば、有機酸単位がカルボキシル基を有する場合はカルボキシル基に隣接する炭素の水素原子である２．２～２．９ｐｐｍのピークから算出する。有機酸単位がカルボキシル基を有する場合を例にすると、変性ＰＶＡのポリビニルアルコール鎖のメチレン基の積分値をｂとし、カルボキシル基に隣接する炭素の水素原子の積分値をａとすると、プロトン数（メチレン基は２Ｈ）を鑑み、変性率はａ／（ｂ／２）×１００（ｍｏｌ％）と計算される。例えば、ａ＝１、ｂ＝１００の場合は、２．０ｍｏｌ％と計算される。
　ＰＶＡ２の粘度平均重合度、ケン化度、変性率、及び０．２重量％水溶液の波長２８０ｎｍにおけるＵＶ吸光度を先述した分析法によって測定した。結果を表１に示す。
（ＰＶＡ３の製造）
　酢酸ビニル１８２５ｇ、メタノール１７４０ｇ、マレイン酸ジメチル２ｇを重合缶に仕込み、３０分間系内を窒素置換した。アゾビスイソブチロニトリル０．３ｇを重合缶に仕込み、酢酸ビニル５５０ｇ、マレイン酸ジメチル２２ｇを滴下しながら、６０℃で１１時間重合した後、滴下を止め、冷却して重合を停止した。次いで常法により未反応の酢酸ビニルを除去し、得られた重合体を常法により水酸化ナトリウムメタノール溶液でケン化してＰＶＡ３を作製した。ＰＶＡ３の粘度平均重合度、ケン化度、変性率、及び０．２重量％水溶液の波長２８０ｎｍにおけるＵＶ吸光度を先述した分析法によって測定した。結果を表１に示す。
（ＰＶＡ４の製造）
　酢酸ビニル１８００ｇ、メタノール６１２ｇ、マレイン酸ジメチル７ｇを重合缶に仕込み、３０分間系内を窒素置換した。アゾビスイソブチロニトリル０．３ｇを重合缶に仕込み、酢酸ビニル４００ｇ、マレイン酸ジメチル６３ｇを滴下しながら、６０℃で１１時間重合した後、滴下を止め、冷却して重合を停止した。次いで常法により未反応の酢酸ビニルを除去し、得られた重合体を常法により水酸化ナトリウムメタノール溶液でケン化してＰＶＡ４を作製した。ＰＶＡ４の粘度平均重合度、ケン化度、変性率、及び０．２重量％水溶液の波長２８０ｎｍにおけるＵＶ吸光度を先述した分析法によって測定した。結果を表１に示す。
（ＰＶＡ５の製造）
　酢酸ビニル１８００ｇ、メタノール６１２ｇ、マレイン酸ジメチル１０ｇを重合缶に仕込み、３０分間系内を窒素置換した。アゾビスイソブチロニトリル０．３ｇを重合缶に仕込み、酢酸ビニル４００ｇ、マレイン酸ジメチル８８ｇを滴下しながら、６０℃で１１時間重合した後、滴下を止め、冷却して重合を停止した。次いで常法により未反応の酢酸ビニルを除去し、得られた重合体を常法により水酸化ナトリウムメタノール溶液でケン化してＰＶＡ５を作製した。ＰＶＡ５の粘度平均重合度、ケン化度、変性率、及び０．２重量％水溶液の波長２８０ｎｍにおけるＵＶ吸光度を先述した分析法によって測定した。結果を表１に示す。
（ＰＶＡ６の製造）
　酢酸ビニル３０００ｇ、変性種のアセトアルデヒド１５ｇを重合缶に仕込み、３０分間系内を窒素置換した。アゾビスイソブチロニトリル０．２ｇを重合缶に仕込み、６５～７５℃で６時間重合した後冷却して重合を停止した。次いで常法により未反応の酢酸ビニルを除去し、得られた重合体を常法により水酸化ナトリウムメタノール溶液でケン化し、１２０℃で６時間乾燥させて、ＰＶＡ６を作製した。変性種としてアセトアルデヒドを使用する場合の変性率は、カルボニル変性率に等しい。カルボニル変性率はプロトンＮＭＲで求めた。具体的には、変性ＰＶＡをケン化度９９．９５モル％以上に完全にケン化した後、十分にメタノール洗浄を行い、分析用の変性ＰＶＡを作製した。作製した分析用の変性ＰＶＡを重水に溶解し、更にＮａＯＨ重水溶液を数滴加えｐＨ＝１４にした後、８０℃で測定し1Ｈ－ＮＭＲスペクトルを得る。変性ＰＶＡの主鎖のメチレン基（１．２～１．８ｐｐｍ）のピークの積分値を基準として、アセトアルデヒドの場合、メチル基末端（２．１５～２．３５ｐｐｍ）のピークの積分値で算出する。具体的には、変性ＰＶＡの主鎖のメチレン基の積分値をｂとし、アセトアルデヒドのメチル基末端の積分値をｄとすると、プロトン数（メチレン基は２、アセトアルデヒドのメチル基末端はＸ＝３）を鑑み、カルボニル変性率は（ｄ／３）／（ｂ／２）×１００（ｍｏｌ％）と計算される。ＰＶＡ６の粘度平均重合度、ケン化度、変性率、及び０．２重量％水溶液の波長２８０ｎｍにおけるＵＶ吸光度を先述した分析法によって測定した。結果を表１に示す。
（ＰＶＡ７の製造）
　酢酸ビニル１２２０ｇ、メタノール１３５０ｇ、変性種として一般式（ＩＩＩ）で示され、ｍ＝５～９、ｎ＝１５～２５であるポリオキシアルキレンアルケニルエーテル（単量体Ｂ）５２ｇを重合缶に仕込み、３０分間系内を窒素置換した。単量体Ｂについてｍ＝５～９、ｎ＝１５～２５であることは、ＮＭＲにより確認した。アゾビスイソブチロニトリル０．２５ｇを重合缶に仕込み、６０℃で９時間重合した後、冷却して重合を停止した。次いで常法により未反応の酢酸ビニルを除去し、得られた重合体を常法により水酸化ナトリウムメタノール溶液でケン化してＰＶＡ７を作製した。ＰＶＡ７の粘度平均重合度、ケン化度、変性率、及び０．２重量％水溶液の波長２８０ｎｍにおけるＵＶ吸光度を先述した分析法によって測定した。結果を表１に示す。
（ＰＶＡ８の製造）
　単量体Ａの代わりに、ｎ＝１５～２５のポリエチレングリコールアリルエーテル（単量体Ｃ）（日油株式会社提供ユニオックスＰＫＡ－５００５）５６ｇを重合缶に仕込んだ以外、ＰＶＡ１と同様にＰＶＡ８を作製した。なお、単量体Ｃについてｎ＝１５～２５であることは、ＮＭＲにより確認した。ＰＶＡ８の粘度平均重合度、ケン化度、変性率、及び０．２重量％水溶液の波長２８０ｎｍにおけるＵＶ吸光度を先述した分析法によって測定した。結果を表１に示す。
（ＰＶＡ９の製造）
　単量体Ａの代わりに、一般式（ＩＩＩ）で示され、ｍ＝１５～２５、ｎ＝１５～２５であるポリエチレングリコールポリプロピレングリコールアリルエーテル（単量体Ｄ）（日油株式会社提供ユニルーブＰＫＡ－５０１３）７４ｇを重合缶に仕込んだ以外、実施例１と同様にＰＶＡ９を作製した。単量体Ｄについてｍ＝１５～２５、ｎ＝１５～２５であることは、ＮＭＲにより確認した。ＰＶＡ９の粘度平均重合度、ケン化度、変性率、及び０．２重量％水溶液の波長２８０ｎｍにおけるＵＶ吸光度を先述した分析法によって測定した。結果を表１に示す。
（ＰＶＡ１０、１１）
　ＰＶＡ８とＰＶＡ９はそれぞれデンカ（株）製ポリビニルアルコールＷ－２４ＮとＢ－２４を用いた。ＰＶＡ８、ＰＶＡ９の粘度平均重合度、ケン化度、変性率、及び０．２重量％水溶液の波長２８０ｎｍにおけるＵＶ吸光度を先述した分析法によって測定した。結果を表１に示す。
Figure JPOXMLDOC01-appb-T000006
（実施例１～１０及び比較例１～４）
　表２に示した重量比率で各ＰＶＡをナウターミキサ（登録商標）でブレンドし、ポリビニルアルコール系樹脂組成物を得た。それらを分散安定剤とし、塩化ビニルの懸濁重合を行い、評価した。
〈塩化ビニルの懸濁重合〉
　攪拌器を備えた容量３０Ｌのステンレス製オートクレーブ中に攪拌下３０℃の水１０．１ｋｇ、ポリビニルアルコール系樹脂組成物を５．８ｇ、重合開始剤としてｔ－ブチルパーオキシネオデカノエートを４．６ｇ、α－クミルパーオキシネオデカノエートを１ｇ仕込んだ。オートクレーブを真空で脱気した後、塩化ビニル単量体を７．２ｋｇ加え、５７℃で４時間重合した。
〈塩化ビニル樹脂の評価〉
　得られた塩化ビニル樹脂の平均粒径、粒度分布、可塑剤吸収量、及びかさ比重について以下の方法で評価した。
　平均粒径の測定はＪＩＳ　Ｚ８８１５：１９９４に準拠して、６０メッシュ（目開き２５０μｍ）、８０メッシュ（目開き１８０μｍ）、１００メッシュ（目開き１５０μｍ）、１５０メッシュ（目開き１０６μｍ）、２００メッシュ（目開き７５μｍ）の篩を用いて、全体量に対する６０メッシュ（目開き２５０μｍ）上の粒子量比率を粗粒量、累積頻度５０％（質量基準）の粒子径（Ｄ５０）を平均粒径、累積頻度８０％（質量基準）の粒子径（Ｄ８０）と累積頻度２０％（質量基準）の粒子径（Ｄ２０）の差を粒度分布とした。
　かさ比重は、ＪＩＳ　Ｋ６７２０－２：１９９９に準拠して測定した。
　可塑剤吸収量は以下の手順で測定した。内径２５ｍｍ、深さ８５ｍｍのアルミニウム合金製容器の底にグラスファイバーを詰め、塩化ビニル樹脂１０ｇを投入した。これに可塑剤（ジオクチルフタレート、以下ＤＯＰとする）１５ｍＬを加え、３０分放置してＤＯＰを塩化ビニル樹脂に充分浸透させた。その後１５００Ｇの加速度下に過剰のＤＯＰを遠心分離し、塩化ビニル樹脂１０ｇに吸収されたＤＯＰの質量を測定して、塩化ビニル樹脂１００質量部当たりのＤＯＰ質量部（ｐｈｒ）に換算した。
　結果を表２に示す。比較例１、３、４ではポリビニルアルコール鎖に二重結合を有する変性ビニルアルコール系重合体（Ｂ）を使用しなかったため、塩化ビニル樹脂粒子が粗大化し、粗粒量が多く、粒子径の均一性が悪かった。変性ビニルアルコール系重合体（Ａ）を使用しなかった比較例２では可塑剤吸収性の悪い塩化ビニル粒子となった。これに対して、実施例１～１０に示したポリビニルアルコール系樹脂組成物を使用すると塩化ビニル樹脂中に粗大粒子の形成が少なく、粒子径の均一性が高い粒子が得られたことが分かる。また、可塑剤吸収性に優れており、さらに、重合時のブロック化やスケール付着が低減し、脱モノマー性に優れた重合体粒子が得られた。よって、実施例１～１０に係る分散安定剤は工業的に極めて有利なものである。
Figure JPOXMLDOC01-appb-T000007

Claims (6)

  1. 　一般式（Ｉ）に示すポリオキシアルキレン単位がポリビニルアルコール鎖と結合した変性ビニルアルコール系重合体（Ａ）と、ポリビニルアルコール鎖に二重結合を有する変性ビニルアルコール系重合体（Ｂ）を含むポリビニルアルコール系樹脂組成物。
    Figure JPOXMLDOC01-appb-C000001
     （式中、Ｒ1及びＲ2はそれぞれ独立にメチル基又はエチル基又は水素原子であり、Ｒ3はアルキル基又は水素原子である。ｎは繰り返し単位数を表し、５≦ｎ≦７０の整数である。）
  2. 　前記変性ビニルアルコール系重合体（Ａ）と前記変性ビニルアルコール系重合体（Ｂ）との重量比（Ａ／Ｂ）が１５／８５～８５／１５である請求項１に記載のポリビニルアルコール系樹脂組成物。
  3. 　前記変性ビニルアルコール系重合体（Ｂ）の０．２重量％水溶液の、光路長１ｃｍ、波長２８０ｎｍにおけるＵＶ吸光度（Ａｂｓ）が０．１以上３．０以下である請求項１又は２に記載のポリビニルアルコール系樹脂組成物。
  4. 　前記変性ビニルアルコール系重合体（Ａ）のポリオキシアルキレン単位の変性率が０．０１～５モル％である請求項１～３の何れか一項に記載のポリビニルアルコール系樹脂組成物。
  5. 　請求項１～４の何れか一項に記載のポリビニルアルコール系樹脂組成物を含有する懸濁重合用分散安定剤。
  6. 　請求項５に記載された懸濁重合用分散安定剤を用いて、ビニル系化合物単量体、又はビニル系化合物単量体とそれに共重合し得る単量体との混合物を水中に分散させて懸濁重合を行うことを含むビニル系樹脂の製造方法。
PCT/JP2020/045918 2019-12-17 2020-12-09 ポリビニルアルコール系樹脂組成物、懸濁重合用分散安定剤及びビニル系樹脂の製造方法 WO2021125020A1 (ja)