WO2021062940A1 - Système de dispersion continue, appareil et procédé de synthèse par lots de catalyseurs - Google Patents

Système de dispersion continue, appareil et procédé de synthèse par lots de catalyseurs Download PDF

Info

Publication number
WO2021062940A1
WO2021062940A1 PCT/CN2019/123880 CN2019123880W WO2021062940A1 WO 2021062940 A1 WO2021062940 A1 WO 2021062940A1 CN 2019123880 W CN2019123880 W CN 2019123880W WO 2021062940 A1 WO2021062940 A1 WO 2021062940A1
Authority
WO
WIPO (PCT)
Prior art keywords
ultrasonic
dispersion
module
catalyst
material circulation
Prior art date
Application number
PCT/CN2019/123880
Other languages
English (en)
Chinese (zh)
Inventor
王中奇
高正飞
Original Assignee
青岛创启新能催化科技有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 青岛创启新能催化科技有限公司 filed Critical 青岛创启新能催化科技有限公司
Publication of WO2021062940A1 publication Critical patent/WO2021062940A1/fr

Abstract

La présente invention concerne un système de dispersion continue, un appareil de dispersion de support de carbone et un appareil, et un procédé de synthèse de catalyseur. Le système de dispersion continue comprend un module d'agitation, un module à ultrasons, et un mécanisme de circulation de matériau. La puissance du module à ultrasons n'est pas inférieure à 500 W, et est utilisée pour disperser des matériaux. Le module d'agitation est utilisé pour disperser des matériaux. Le mécanisme de circulation de matériau fait communiquer le module à ultrasons avec le module d'agitation, de sorte que les matériaux dans le module à ultrasons et le module d'agitation puissent circuler l'un avec l'autre. Selon le système de dispersion continue, d'une part, le module à ultrasons et le module d'agitation dispersent ensemble les matériaux afin de maintenir la dispersion uniforme des matériaux dans le système de dispersion continue ; d'autre part, la conduction thermique de la dispersion ultrafine à l'échelle nanométrique est accélérée par la circulation du module d'agitation et du module à ultrasons. Ceci est répété de manière circulaire, de sorte que la dispersion de masse des matériaux soit poursuivie sans à-coups, et l'effet de dispersion de la dispersion de masse est considérablement amélioré, ce qui permet d'améliorer l'efficacité de production de la synthèse de nanomatériaux.
PCT/CN2019/123880 2019-09-30 2019-12-09 Système de dispersion continue, appareil et procédé de synthèse par lots de catalyseurs WO2021062940A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
CN201910944411.9 2019-09-30
CN201910944411.9A CN110639415A (zh) 2019-09-30 2019-09-30 连续分散系统、催化剂批量合成装置及方法

Publications (1)

Publication Number Publication Date
WO2021062940A1 true WO2021062940A1 (fr) 2021-04-08

Family

ID=69012257

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2019/123880 WO2021062940A1 (fr) 2019-09-30 2019-12-09 Système de dispersion continue, appareil et procédé de synthèse par lots de catalyseurs

Country Status (2)

Country Link
CN (1) CN110639415A (fr)
WO (1) WO2021062940A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115872734A (zh) * 2022-10-27 2023-03-31 先导薄膜材料（广东）有限公司 一种ito废靶重制ito粉、高密度靶材及其制备方法

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111185120B (zh) * 2020-01-09 2022-02-25 吕梁学院 一种石墨烯生产用的高效分散配料装置
CN114177858B (zh) * 2021-12-13 2023-06-16 清氢(北京)科技有限公司 电催化剂宏量制备方法及宏量制备装置

Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN102423545A (zh) * 2011-10-21 2012-04-25 北京弘祥隆生物技术股份有限公司 用于天然产物或化学药物结晶纯化的超声结晶设备
KR20120085447A (ko) * 2011-01-24 2012-08-01 엄재홍 정제유를 물과 혼합하는 장치
CN106058272A (zh) * 2016-07-25 2016-10-26 北京工业大学 小粒径且分散均匀的贵金属纳米颗粒电催化剂的绿色一步合成法
CN206045913U (zh) * 2016-06-29 2017-03-29 昆明纳太科技有限公司 连续分散纳米材料的设备
CN206911273U (zh) * 2017-06-16 2018-01-23 北京华科讯能石墨烯新技术研究院有限公司 石墨烯剥离三元复合机械设备
CN208786191U (zh) * 2018-08-23 2019-04-26 湖南金华达建材有限公司 一种用于生产混凝土脱模剂的高效装置
CN208865563U (zh) * 2018-08-09 2019-05-17 扬州北方三山工业陶瓷有限公司 一种新型超声波搅拌磨联合循环制浆装置

Patent Citations (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR20120085447A (ko) * 2011-01-24 2012-08-01 엄재홍 정제유를 물과 혼합하는 장치
CN102423545A (zh) * 2011-10-21 2012-04-25 北京弘祥隆生物技术股份有限公司 用于天然产物或化学药物结晶纯化的超声结晶设备
CN206045913U (zh) * 2016-06-29 2017-03-29 昆明纳太科技有限公司 连续分散纳米材料的设备
CN106058272A (zh) * 2016-07-25 2016-10-26 北京工业大学 小粒径且分散均匀的贵金属纳米颗粒电催化剂的绿色一步合成法
CN206911273U (zh) * 2017-06-16 2018-01-23 北京华科讯能石墨烯新技术研究院有限公司 石墨烯剥离三元复合机械设备
CN208865563U (zh) * 2018-08-09 2019-05-17 扬州北方三山工业陶瓷有限公司 一种新型超声波搅拌磨联合循环制浆装置
CN208786191U (zh) * 2018-08-23 2019-04-26 湖南金华达建材有限公司 一种用于生产混凝土脱模剂的高效装置

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115872734A (zh) * 2022-10-27 2023-03-31 先导薄膜材料（广东）有限公司 一种ito废靶重制ito粉、高密度靶材及其制备方法

Also Published As

Publication number Publication date
CN110639415A (zh) 2020-01-03

Similar Documents

Publication Publication Date Title
WO2021062940A1 (fr) Système de dispersion continue, appareil et procédé de synthèse par lots de catalyseurs
CN211302832U (zh) 一种无机粉体改性系统
JP2014004496A (ja) 反応凝集粒子の製造方法、リチウムイオン電池用正極活物質の製造方法、リチウムイオン電池の製造方法及び反応凝集粒子の製造装置
JP2017218667A (ja) 金属微粒子の製造方法及び金属微粒子の製造装置
WO2002070409A1 (fr) Procede pour produire des poudres de l'ordre du nanometre
US20080245184A1 (en) Preparation method of metal nano particle using micro mixer
CN105664745B (zh) 一种强化输送的机械搅拌式连续乳化器及乳化方法
CN102179526A (zh) 一种油水界面法制备立方晶型纳米银材料的方法
CN211411860U (zh) 连续分散系统、碳载体分散装置及催化剂批量合成装置
CN105642217B (zh) 一种强化输送的外循环式烷基化反应器及烷基化反应方法
RU2692541C2 (ru) Способ диспергирования углеродных нанотрубок ультразвуком
CN102145389B (zh) 纳米银粉的制备方法
CN107673394A (zh) 一种利用超声辅助微通道反应装置制备微米级三角锥形溴化亚铜的方法
CN217535491U (zh) 一种制备高均匀性镍钴氢氧化物颗粒的装置
RU2736287C1 (ru) Микрореактор с закрученными потоками растворов реагентов
Tang et al. An optimized miniaturized annular rotating flow reactor for controllable continuous preparation of functionalized polysilsesquioxane microspheres
CN102896326A (zh) 一种利用油酸的油水界面法制备立方晶型纳米银材料的方法
CN205627930U (zh) 一种外循环式烷基化反应器
JP2004149897A (ja) 鎖状金属粉末とその製造方法およびそれに用いる製造装置
JP2011168806A (ja) 金属ナノ粒子およびその製造方法
CN105597582A (zh) 一种机械搅拌式连续乳化器及乳化方法
JP2011194366A (ja) 微粒子製造方法及び微粒子製造装置
CN205850826U (zh) 一种强化输送的外循环式烷基化反应器
JP2004508171A (ja) 化学プロセス及びプラント
CN212068704U (zh) 一种具有恒温加热微乳液功能的搅拌装置

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19948115

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19948115

Country of ref document: EP

Kind code of ref document: A1