WO2020213306A1 - 熱伝導性組成物、熱伝導性部材、バッテリモジュール - Google Patents

熱伝導性組成物、熱伝導性部材、バッテリモジュール Download PDF

Info

Publication number
WO2020213306A1
WO2020213306A1 PCT/JP2020/010511 JP2020010511W WO2020213306A1 WO 2020213306 A1 WO2020213306 A1 WO 2020213306A1 JP 2020010511 W JP2020010511 W JP 2020010511W WO 2020213306 A1 WO2020213306 A1 WO 2020213306A1
Authority
WO
WIPO (PCT)
Prior art keywords
agent
conductive composition
heat conductive
thermally conductive
heat
Prior art date
Application number
PCT/JP2020/010511
Other languages
English (en)
French (fr)
Inventor
寛 梅谷
慶太 石田
Original Assignee
積水ポリマテック株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 積水ポリマテック株式会社 filed Critical 積水ポリマテック株式会社
Priority to JP2021514826A priority Critical patent/JPWO2020213306A1/ja
Priority to EP20791325.2A priority patent/EP3957688A4/en
Priority to CN202080028308.0A priority patent/CN113692427B/zh
Publication of WO2020213306A1 publication Critical patent/WO2020213306A1/ja

Abstract

優れた接着性を有し、かつ反復して振動等が加えられても被着体から剥離しにくい熱伝導性部材を提供する。　硬化性オルガノポリシロキサン（Ａ）と、アルコキシシラン化合物（Ｂ）と、熱伝導性充填剤（Ｃ）とを含む熱伝導性組成物であって、前記アルコキシシラン化合物（Ｂ）が、長鎖アルケニル基含有アルコキシシランである、熱伝導性組成物。

Description

熱伝導性組成物、熱伝導性部材、バッテリモジュール
　本発明は、熱伝導性組成物、熱伝導性部材、および、該熱伝導性部材を隙間材とするバッテリモジュールに関する。
　硬化可能な液状の熱伝導性組成物を、発熱体と放熱体の間に充填し、その後、硬化することで形成される硬化物は、発熱体が発する熱を放熱体に伝える熱伝導性部材として使用されている。硬化可能な液状の熱伝導性組成物は、流動性があるため、発熱体と放熱体の間の任意の隙間を埋めることができる。そのため、形成される硬化物は、発熱体と放熱体の隙間が一定でなくても確実にその隙間を埋めることができ、熱伝導性の間隙材として利用されている。熱伝導性の間隙材は、発熱体の表面、および、放熱体の表面と密着させることで、良好な熱伝導性を発揮できる。
　熱伝導性の間隙材は、例えば特許文献１に開示されるように、バッテリモジュールに使用されることが知られている。バッテリモジュールにおける間隙材は、発熱体であるバッテリセルと放熱体であるモジュール筐体の間に配置されて、バッテリセルの熱を外部に放熱する役割を果たす。また、バッテリセルとバッテリセルの間に配置されこれらを固定して、離間状態を保持することにも利用されている。
国際公開公報2018/173860号
　熱伝導性の間隙材は、熱伝導効率を上げるため、あるいは、バッテリセル間を固定するために、バッテリセルなどの発熱体や、モジュール筐体などの放熱体に高い接着力で接着させる必要がある。また、間隙材は、例えばバッテリモジュールにおいて自動車などの振動が作用される用途で使用されることがある。
　しかしながら、従来の熱伝導性部材は、接着性を十分に高くすることが難しく、振動などが作用されると、被着体との界面で剥がれるなどの不具合が生じやすい。
　本発明は、上記事情を考慮してなされたものであり、優れた接着性を有し、かつ反復して振動等が加えられても被着体から剥離しにくい熱伝導性部材、及びその熱伝導性部材を形成するための熱伝導性組成物を提供することを目的とする。
　本発明者らは、鋭意検討の結果、熱伝導性組成物に、シランカップリング剤として、特定のシラン化合物を添加することで、上記課題が解決できることを見出し、本発明を完成させた。本発明は、以下の［１］～［１０］を提供する。
［１］硬化性オルガノポリシロキサン（Ａ）と、アルコキシシラン化合物（Ｂ）と、熱伝導性充填剤（Ｃ）とを含む熱伝導性組成物であって、前記アルコキシシラン化合物（Ｂ）が、炭素数が８～１８の長鎖アルケニル基含有アルコキシシランである、熱伝導性組成物。
［２］第１剤と第２剤を組み合わせてなる、２液型の熱伝導性組成物であって、前記第１剤中には、アルケニル基含有オルガノポリシロキサン（Ａ１）と、アルコキシシラン化合物（Ｂ）と、付加反応触媒（Ｘ）とが含まれ、前記第２剤中には、ハイドロジェンオルガノポリシロキサン（Ａ２）が含まれ、かつ、アルコキシシラン化合物（Ｂ）が含まれず、前記第１剤及び前記第２剤の少なくともいずれか一方に熱伝導性充填剤（Ｃ）を含み、前記アルコキシシラン化合物（Ｂ）が、炭素数が８～１８の長鎖アルケニル基含有アルコキシシランである、熱伝導性組成物。
［３］前記第２剤中に、アルケニル基含有オルガノポリシロキサン（Ａ１）が含有される、［２］に記載の熱伝導性組成物。
［４］前記硬化性オルガノポリシロキサン（Ａ）が、付加反応硬化型オルガノポリシロキサンである、［１］に記載の熱伝導性組成物。
［５］該熱伝導性組成物の硬化物の硬度は、Ａ硬度で３０以上６０未満である、［１］～［４］のいずれかに記載の熱伝導性組成物。
［６］前記アルコキシシラン化合物（Ｂ）が、オクテニルトリメトキシシランである、［１］～［５］のいずれかに記載の熱伝導性組成物。
［７］前記アルコキシシラン化合物（Ｂ）の含有量が、硬化性オルガノポリシロキサン（Ａ）とアルコキシシラン化合物（Ｂ）の合計質量に対して、１～１０質量％である、［１］～［６］のいずれかに記載の熱伝導性組成物。
［８］硬化した際の引張せん断強さが１ＭＰａ以上である、［１］～［７］のいずれかに記載の熱伝導性組成物。
［９］［１］～［８］のいずれかに記載の熱伝導性組成物を硬化してなる熱伝導性部材。
［１０］［９］に記載の熱伝導性部材からなる間隙材と、複数のバッテリセルと、前記複数のバッテリセルを格納するモジュール筐体とを備え、前記間隙材がモジュール筐体の内部に配置されるバッテリモジュール。
　本発明によれば、被着体に対して優れた接着力を有するとともに、振動等の外力が作用されても剥離しにくい熱伝導性部材、及びその熱伝導性部材を形成するための熱伝導性組成物を提供できる。
本発明に係るバッテリモジュールの代表的構成を示す斜視図である。 バッテリモジュールが有するバッテリセルの代表的構成を示す斜視図である。
　以下、本発明の熱伝導性組成物、該熱伝導性組成物の硬化物からなる熱伝導性部材、及び、バッテリモジュールについて、実施形態を用いて説明する。
［熱伝導性組成物］
　本発明の熱伝導性組成物は、硬化性オルガノポリシロキサン（Ａ）と、アルコキシシラン化合物（Ｂ）と、熱伝導性充填剤（Ｃ）とを含む熱伝導性組成物である。以下、各成分について詳細に説明する。
＜硬化性オルガノポリシロキサン（Ａ）＞
　硬化性オルガノポリシロキサン（Ａ）は、硬化可能なオルガノポリシロキサンであり、反応性基を有するポリオルガノシロキサンを含む。硬化性オルガノポリシロキサンは、例えば、付加反応硬化型シリコーン、ラジカル反応硬化型シリコーン、縮合反応硬化型シリコーン、紫外線又は電子線硬化型シリコーン、及び湿気硬化型シリコーンが挙げられ、上記の中では、付加反応硬化型オルガノポリシロキサンであることが好ましい。付加反応硬化型オルガノポリシロキサンは、アルミニウムなどの金属に対する接着力が低くなりやすいが、本発明では、後述するように特定のアルコキシシラン化合物（Ｂ）を使用することで、アルミニウムなどに対する接着性も高くなる。
　付加反応硬化型オルガノポリシロキサンとしては、アルケニル基含有オルガノポリシロキサン（主剤，Ａ１）とハイドロジェンオルガノポリシロキサン（硬化剤，Ａ２）とを含むものがより好ましい。アルケニル基含有オルガノポリシロキサン（Ａ１）は、ビニル基（ＣＨ２＝ＣＨ－）を末端に有する、ビニル末端オルガノポリシロキサンであることが好ましい。
　硬化性オルガノポリシロキサン（Ａ）は、硬化することでシリコーンゴムとなるものであり、付加反応硬化型オルガノポリシロキサンの場合には、上記主剤と硬化剤を付加反応触媒（Ｘ）による付加反応によって硬化させるとよい。付加反応触媒（Ｘ）は、白金触媒であることが好ましい。
　硬化性オルガノポリシロキサン（Ａ）は、１種単独で使用してもよいし、２種以上を併用してもよい。
＜アルコキシシラン化合物（Ｂ）＞
　アルコキシシラン化合物（Ｂ）は、長鎖アルケニル基含有アルコキシシランである。アルコキシシラン化合物（Ｂ）における長鎖アルケニル基は、炭素数８以上のアルケニル基であり、より具体的には炭素数８～１８のアルケニル基である。
　本発明の熱伝導性組成物は、特定のアルコキシシラン化合物（Ｂ）を含有することで、金属などに対する優れた接着性を確保しつつ、振動等の外力が作用されても剥離等が生じにくくなる。その原理は定かではないが、以下のように推定される。本発明の熱伝導性組成物の硬化物は、アルコキシシラン化合物（Ｂ）が、長鎖のアルケニル基とアルコキシ基とを含有することで、被着体に対する接着性のみならず、硬化物自体の強度と柔軟性も良好になる。そのため、熱伝導性組成物の硬化物は、引張せん断強さが高くなり、かつ外力が作用された際に一定量変位できるようになり、それにより、被着体に対する優れた接着性を確保しつつ、振動等の外力が作用されても剥離等が生じにくくなると推定される。
　なお、本発明では、熱伝導性組成物の硬化物は、被着体に対する接着性が向上し、破壊モードは界面剥離よりも凝集破壊が支配的となる。そのため、熱伝導性組成物の硬化物は、接着性のみならず、硬化物自体の強度と柔軟性を良好にすることで、例えば被着体を強固に保持できるようになる。
　長鎖アルケニル基含有アルコキシシランは、具体的には以下の一般式（１）で表される。
Figure JPOXMLDOC01-appb-C000001
　一般式（１）において、Ｒ１は炭素数８～１８のアルケニル基を表す。Ｒ２は互いに独立に炭素数１～４のアルキル基であり、Ｒ３は互いに独立に炭素数１～４のアルキル基であり、ａは１～３の整数である。
　Ｒ２はメチル基、エチル基が好ましく、メチル基であることが更に好ましい。Ｒ３はメチル基、エチル基が好ましく、メチル基であることが更に好ましい。ａは１～３であるが、好ましくは３である。したがって、化合物（Ｂ）は、アルケニルトリエトキシシラン及びアルケニルトリメトキシシランが好ましく、さらに好ましくはアルケニルトリメトキシシランである。
　アルケニル基含有アルコキシシランにおける長鎖アルケニル基（すなわち、一般式（１）におけるＲ１）は、直鎖状又は分岐状でもよいが、直鎖状であることが好ましい。長鎖アルケニル基は、ビニル基（ＣＨ２＝ＣＨ－）を末端に有することが好ましく、より好ましくは直鎖の末端がビニル基である。長鎖アルケニル基（すなわち、Ｒ１）の炭素数は、８～１２がより好ましく、８～１０がさらに好ましく、８が最も好ましい。
　長鎖アルケニル基含有アルコキシシランは、具体的にはオクテニルトリメトキシシランが好適に使用でき、特に、７－オクテニルトリメトキシシランを使用することが好ましい。
　アルコキシシラン化合物（Ｂ）は、１種単独で使用してもよいし、２種以上を併用してもよい。
　本発明の熱伝導性組成物におけるアルコキシシラン化合物（Ｂ）の含有量は、硬化性オルガノポリシロキサン（Ａ）とアルコキシシラン化合物（Ｂ）の合計量に対して、１～１０質量％の範囲であることが好ましい。１質量％以上とすると熱伝導性組成物の硬化物の剥離応力が高くなり、被着体に対する接着性が良好になる。また、外力が作用された際の変位量も多くなり、振動等が作用されても剥離されにくくなる。一方で、１０質量％以下とすることで、適正な量の硬化性オルガノポリシロキサン（Ａ）を組成物中に含有させることが可能になり、シリコーンゴムとして良好な特性を得やすくなる。
　アルコキシシラン化合物（Ｂ）の上記含有量は、２質量％以上がより好ましく、２．５質量％以上がさらに好ましい。これら含有量以上とすることで、特に引張せん断強さが高くなり、振動等が作用されても剥離されたり、硬化物自体が破壊されたりすることを防止できる。また、アルコキシシラン化合物（Ｂ）の上記含有量は、各種性能をバランスよく良好にする観点から、７質量％以下がより好ましく、５質量％以下がさらに好ましい。
＜熱伝導性充填材（Ｃ）＞
　熱伝導性充填材（Ｃ）は、熱伝導性組成物の硬化体に熱伝導性を付与する物質であり、電気絶縁性に優れ、かつ熱伝導性が良好なものを用いることができる。例えば、酸化アルミニウム、窒化ホウ素、窒化アルミニウム、炭化ケイ素、水酸化アルミニウムなどは、電気絶縁性や熱伝導性に優れる点で好ましい。これらの粒子は、球状、繊維状、針状、鱗片状などの形状であってよい。熱伝導性充填材は１種単独で使用してもよいし、２種以上を併用してもよい。上記した中でも、酸化アルミニウム及び水酸化アルミニウムから選択される１種以上がより好ましく、これら両方を使用することがさらに好ましい。
　流動性を有する熱伝導性組成物中において、不定形微粒子状の水酸化アルミニウムは、液状シリコーンと熱伝導性充填材の分離を抑制することができる。また、酸化アルミニウムは、熱伝導性が高く、大粒径の粒子を用いることでき、熱伝導性組成物の硬化体中において、効果的に熱伝導率を高めることができる。
　例えば、熱伝導性充填材（Ｃ）として、酸化アルミニウムと水酸化アルミニウムを使用する際には、酸化アルミニウムの形状は球状が好ましい。球状とすれば、比表面積を小さくし易い。特に、水酸化アルミニウムと酸化アルミニウムを合わせた熱伝導性充填材を用いる場合に、比表面積が小さければ、大粒径の酸化アルミニウムの割合を増やしても液状の熱伝導性組成物の流動性が低下しにくい。
　熱伝導性組成物における、熱伝導性充填材（Ｃ）の含有量は、上記（Ａ）及び（Ｂ）成分の合計量１００質量部に対して、例えば１００～１５００質量部の範囲、好ましくは８００～１２００質量部の範囲に選択することができる。熱伝導性充填材の含有量を１００質量部以上とすることで、熱伝導性部材の熱伝導性が良好となる。また、１５００質量部以下とすることで、熱伝導性組成物の粘度が適切になり、充填時における取扱い性が良好となる。
　熱伝導性組成物は、一般的に液状であり、その２５℃における粘度は、５０～２０００Ｐａ・ｓの範囲より選択されることが好ましい。粘度が５０Ｐａ・ｓ以上とすることで、熱伝導性充填材の含有量が十分となり、作製される硬化体において、十分な熱伝導率が得られる。一方、粘度が２０００Ｐａ・ｓ以下とすると、熱伝導性充填材の含有量が不必要に高くなることを防止でき、熱伝導性組成物をディスペンスなどしやすくなり、作業性が良好となる。また、所望の熱伝導率を満たすことと、ディスペンスする際の吐出安定性とのバランスを良くする観点から、熱伝導性充填材の含有量を調節し、粘度を、１００～１０００Ｐａ・ｓの範囲とするとより好ましく、２００～６００Ｐａ・ｓの範囲とすることが特に好ましい。なお、熱伝導性組成物の粘度は、硬化が進行していない時点での粘度であり、例えば、後述する２液型では、第１剤に第２剤を混合直後の粘度を測定するとよい。
　本発明の熱伝導性組成物中には、熱伝導性充填材に加えて、種々の添加剤を含有させることができる。例えば、触媒、分散剤、難燃剤、可塑剤、硬化遅延剤、酸化防止剤、着色剤などが挙げられる。
　本発明の熱伝導性組成物の形態は、１液型でもよいし、第１剤と第２剤を組み合わせてなる２液型のいずれでもよい。２液型は、使用時に第１剤と第２剤とを混合させて熱伝導性組成物を得るものである。１液型の熱伝導性組成物としては、（Ａ）成分として湿気硬化型シリコーンを含有するものが挙げられる。２液型の熱伝導性組成物としては、（Ａ）成分として付加反応硬化型シリコーンを含有する組成物が挙げられる。これらのなかでは、保存安定性の観点から、２液型であることが好ましい。
　なお、２液型の熱伝導性組成物において、第１剤と第２剤の質量比（第２剤／第１剤）は、１又は１に近い値であることが好ましく、具体的には０．９～１．１が好ましく、０．９５～１．０５がより好ましい。このように、第１剤と第２剤の質量比を１又は１に近い値とすることで、熱伝導性組成物の調製が容易になる。また、２液型の熱伝導性組成物において、第１剤と第２剤の粘度比（第２剤／第１剤）も、１又は１に近い値であることが好ましく、具体的には０．５～２．０が好ましく、０．８～１．２がより好ましい。このように、第１剤と第２剤の質量比を１又は１に近い値とすることで、熱伝導性組成物を均一に混合しやすくなる。なお、質量比や粘度比を調整する方法は後述する。
　２液型の熱伝導性組成物は、より具体的には、第１剤がアルケニル基含有オルガノポリシロキサン（Ａ１）(主剤)を含み、第２剤がハイドロジェンオルガノポリシロキサン（Ａ２）（硬化剤）を含むものである。また、２液型の熱伝導性組成物の一実施形態において、アルコキシシラン化合物（Ｂ）と付加反応触媒（Ｘ）が第１剤に含有される一方で、第２剤にはアルコキシシラン化合物（Ｂ）が含有されない。
　一般的な付加反応型の２液型シリコーン樹脂組成物は、付加反応触媒（Ｘ）が主剤側である第１剤に含有されるが、本実施形態では、付加反応触媒（Ｘ）に加えてアルコキシシラン化合物（Ｂ）も第１剤に含有される。このように、第１剤に付加反応触媒（Ｘ）に加えてアルコキシシラン化合物（Ｂ）を含有させると、長期保管後でも硬化が適切に進行して、硬化により得られる熱伝導性部材の各種物性を良好にできる。
　その要因は定かではないが、白金触媒などの付加反応触媒（Ｘ）が、（Ａ１）及び（Ｂ）成分の付加反応部位である、アルケニル基に配位した状態となり、硬化が進行しやすいためと推定される。一方で、第１剤及び第２剤を混合する前には、アルコキシシラン化合物（Ｂ）が硬化剤であるハイドロジェンオルガノポリシロキサン（Ａ２）に接触させないことで、これらが反応などすることが防止されるためと推定される。
　また、上記一実施形態において、熱伝導性充填材（Ｃ）は、第１剤及び第２剤の少なくともいずれか一方に含有されるとよいが、好ましくは第１剤及び第２剤の両方に含有させる。熱伝導性充填材（Ｃ）を第１剤及び第２剤の両方に含有させると、第１剤と第２剤を混合しやすくなる。また、熱伝導性組成物を作製する際の第１剤に対する第２剤の質量比および粘度比を１又は１に近い値にできるため、２液型として使用しやすくなる。
　また、第２剤は、アルケニル基含有オルガノポリシロキサン（Ａ１）を含有することが好ましい。第２剤が硬化剤（Ａ２）に加えて主剤（Ａ１）も含有することで、熱伝導性組成物を作製する際の第１剤に対する第２剤の質量比および粘度比を１又は１に近い値に調整しやすくなる。一方で、第１剤には、硬化剤であるハイドロジェンオルガノポリシロキサン（Ａ２）が含有されないとよい。このようにすることで、第１剤に含まれる硬化性オルガノポリシロキサンと、第２剤に含まれる硬化性オルガノポリシロキサンの質量および粘度を近いものにできる。そのため、それぞれ略等量の熱伝導性組成物を加えることで、第１剤に対する第２剤の質量比および粘度比を１又は１に近い値にでき、２液型として使用しやすくなる。
　また、第１剤は付加反応触媒を含有し、第２剤は実質的に付加反応触媒を含まないことが好ましい。そうすることで、第１剤と第２剤とは混合前は保存安定性に優れ、混合後には反応が促進され、速やかに硬化するものとすることができる。
　第２剤が硬化剤（Ａ２）に加えて主剤（Ａ１）と微量の付加反応触媒も含有する形態を採る場合、保存時における付加反応硬化を防止するため、硬化遅延剤を添加し、第２剤中に添加された付加反応触媒による常温時における反応促進効果を相殺することで、実質的に付加反応触媒が含まれていない状態を達成することもできる。
　具体的には、付加反応型の２液型熱伝導性組成物の第２剤中に、微量の付加反応触媒が含有されている際、保存中、付加反応触媒による硬化剤（Ａ２）と主剤（Ａ１）との反応を抑制するために、硬化遅延剤を添加することができる。硬化遅延剤として、例えば、３－メチル－１－ブチン－３－オール、３，５－ジメチル－１－ヘキシン－３－オール、フェニルブチノール、１－エチニル－１－シクロヘキサノール等の炭素－炭素三重結合を有するアルコール誘導体；３－メチル－３－ペンテン－１－イン、３，５－ジメチル－３－ヘキセン－１－イン等のエンイン化合物；テトラメチルテトラビニルシクロテトラシロキサン、テトラメチルテトラヘキセニルシクロテトラシロキサン等のアルケニル基含有低分子量シロキサン；メチル－トリス（３－メチル－１－ブチン－３－オキシ）シラン、ビニル－トリス（３－メチル－１－ブチン－３－オキシ）シラン等のアルキン含有シランが例示される。
　また、第２剤には、硬化遅延剤が含有されない場合でも、常温時は反応が促進されない程度の量の付加反応触媒が含有されてもよい。
　付加反応触媒として利用される、例えば、塩化白金酸、塩化白金酸とオレフィン類、ビニルシロキサン又はアセチレン化合物との錯化合物等の白金触媒は、硬化剤（Ａ２）に作用し、その反応性を高める活性化の機能を有している。第２剤を保存中、硬化剤（Ａ２）の不要な活性化を回避する手段としては、第２剤中に付加反応触媒を含有しないことが最も有効である。
　熱伝導性組成物は、硬化剤として利用されるハイドロジェンオルガノポリシロキサンの種類、配合量、ならびに、添加される付加反応触媒の種類、添加量に応じて、硬化温度を選択すればよい。例えば、２液型において、第１剤と第２剤とは混合して常温下で放置するだけで硬化する形態とすればよいが、加熱させることで硬化を促進させる形態を選択することもできる。　
　熱伝導性組成物を硬化した際の引張せん断強さは、１ＭＰａ以上であることが好ましい。１ＭＰａ以上であれば、熱伝導性組成物の硬化物の被着体に対する剥離応力が良好となり、かつ硬化物自体の強度も高くなる。そのため、熱伝導性組成物を例えば後述するバッテリモジュールの間隙材として使用すると、間隙材とバッテリセルとの間、および間隙材とモジュール筐体の密着性が優れたものとなる。そして、バッテリモジュール内でバッテリセルを安定的に保持することができ、振動が作用されてもバッテリセルの固定位置のずれを抑えることができる。これら観点から熱伝導性組成物の引張せん断強さは、より好ましくは１．５ＭＰａ以上であり、さらに好ましくは１．９ＭＰａ以上である。また、引張せん断強さの上限は、特に限定されないが、例えば５ＭＰａ以下である。
　なお、熱伝導性組成物を硬化した際の引張せん断強さは、２枚のアルミニウム板を熱伝導性組成物の硬化物で固定して、ＪＩＳ　Ｋ６８５０：１９９９の引張せん断試験に準拠して測定することで求めることができ、詳細には、後述する実施例に記載の方法で測定すればよい。
［熱伝導性部材］
　本発明の熱伝導性組成物を硬化することで、熱伝導性部材を形成することができる。熱伝導性部材（すなわち、熱伝導性組成物の硬化物）の硬度は、ＪＩＳ　Ｋ　６２５３のタイプＡの硬度計によって測定される値（以下「Ａ硬度」という）で例えば２０～８０、好ましくは３０～８０の範囲、より好ましくは３０以上６０未満の範囲である。
　Ａ硬度を８０以下とすることで、発熱体や放熱体の形状に沿って良好に追従する柔軟性と、発熱体や放熱体との密着性とを十分に確保することができる。さらに、Ａ硬度が６０未満であれば、外力が作用された際の変位量が多くなり、振動が作用されても被着体から剥離したり、熱伝導性部材自体が破断したりすることを防止できる。そのため、例えば、後述するバッテリモジュールの間隙材として使用すると、間隙材によるバッテリセルの保持性がより一層向上する。また、Ａ硬度を３０以上とすることで、引張せん断強さを高くしやすくなる。
　熱伝導性部材（すなわち、熱伝導性組成物の硬化物）の熱伝導率は、２．５Ｗ／ｍ・Ｋ以上であることが好ましく、３．０Ｗ／ｍ・Ｋ以上であることが好ましい。これら下限値以上とすることで、熱伝導性が良好となる。そのため、例えばバッテリセルモジュールの間隙材として使用する場合には、バッテリセルから発生する熱を、間隙材を経由して、モジュール筐体に効率的に伝えることができ、バッテリセルの温度の過度の上昇を抑えることができる。熱伝導性部材の熱伝導率は、高ければ高いほどよいが、実用的には、例えば７Ｗ／ｍ・Ｋ以下である。
［バッテリモジュール］
　本発明に係るバッテリモジュールは、複数のバッテリセルと、前記複数のバッテリセルを格納するモジュール筐体と、前記モジュール筐体の内部に配置される間隙材とを備える。モジュール筐体の内部に配置される間隙材は、上記した本発明の熱伝導性部材からなる。
　熱伝導性部材からなる間隙材は、バッテリセル相互間、及びバッテリセルとモジュール筐体間に充填されており、充填されている間隙材は、バッテリセル、及びモジュール筐体に密着する。これにより、バッテリセル間の間隙材は、バッテリセル相互間の離間状態を保持する機能を有している。また、バッテリセルとモジュール筐体との間の間隙材は、バッテリセルとモジュール筐体の双方に密着し、バッテリセルで発生する熱をモジュール筐体に伝える機能を有している。
　図１は、バッテリモジュールの具体的な構成を示す。図２は各バッテリセルの具体的な構成を示す。図１で示すように、バッテリモジュール１０の内部には、複数のバッテリセル１１が配置される。各バッテリセル１１は、可撓性の外装フィルム内にラミネートして封入したものであり、全体的な形状は、高さや幅の大きさに比べて厚さが薄い偏平体である。こうしたバッテリセル１１は、図２で示すように、正極１１ａと負極１１ｂが外部に表れ、偏平面の中央部１１ｃは圧着された端部１１ｄよりも肉厚に形成されている。
　図１に示すように、各バッテリセル１１は、その偏平面同士が対向するように配置されている。図１の構成において、間隙材１３は、モジュール筐体１２の内部に格納される、複数のバッテリセル１１の全体を覆うようには充填されていない。間隙材１３は、モジュール筐体１２の内部の一部分（底側部分）に存在する間隙を満たすように充填されている。間隙材１３は、バッテリセル１１相互間、および、バッテリセル１１とモジュール筐体１２の間に充填され、この部分のバッテリセル１１の表面、および、モジュール筐体１２の内面と密着されている。
　バッテリセル１１相互の間に充填される間隙材１３は、双方のバッテリセル１１の表面に接着されているが、間隙材１３自体は、上記した硬度を有することで、適度の弾性と柔軟性を有しており、バッテリセル１１相互の間隔を変位する外力が印加されても、外力による歪み変形を緩和することができる。したがって、間隙材１３は、バッテリセル１１Ａ相互間の離間状態を保持する機能を有している。
　バッテリセル１１とモジュール筐体１２の内面との間の間隙に充填されている間隙材１３も、バッテリセル１１の表面と、モジュール筐体１２の内面に、密に接着されている。その結果、バッテリセル１１の内部で発生する熱は、バッテリセル１１の表面に接着している間隙材１３を経由して、該間隙材１３の他の面により密着されているモジュール筐体１２の内面へと伝えられる。
　バッテリモジュール１０内への間隙材１３の形成は、一般的なディスペンサーを用いて、液状の熱伝導性組成物を塗布した後、その液状の熱伝導性組成物を硬化させることで行うとよい。この際、上記の通り２液型の熱伝導性組成物を使用することが好ましい。２液型は、保管が容易であるとともに、使用直前に混合すればディスペンサーで塗布する作業時には硬化し難く、塗布後は速やかに硬化させることができる。また、ディスペンサーでの塗布は、バッテリモジュール１０の筐体１２内の比較的奥深くまで、液状の熱導電性組成物を充填させることができる点でも好ましい。
　バッテリセル１１を覆う間隙材１３は、バッテリセル１１の一方側において、各バッテリセル１１の２０～４０％覆うことが好ましい。２０％以上とすることで、バッテリセル１１を安定的に保持することができる。また、発熱量が大きいバッテリセルを十分に覆うことで、放熱効率が良好となる。一方で、４０％以下とすることで、バッテリセル１１から発生する熱の放熱を効率的に行うことができ、重量増大や、作業性の悪化等も防げる。また、放熱効率を良好にするために、バッテリセル１１の電極１１ａ，１１ｂがある側を間隙材１３で覆うことが好ましく、電極１１ａ，１１ｂの全体を間隙材１３で覆うことがより好ましい。　
　以上のとおり、バッテリモジュール１０は、バッテリセル１１から発生した熱を、間隙材１３を経由して、モジュール筐体１２に逃がすことができる。また、間隙材１３に本発明の熱伝導性部材を用いているので、バッテリセル１１やモジュール筐体１２との接着性が良好になる。特に、バッテリセル１１の表面材がアルミニウムであったり、モジュール筐体１２にアルミニウム板が使用されたりすることがあるが、そのような場合、接着力はより一層高くなる。
　本発明の熱伝導性部材（シリコーンゴム）は、弾性を有し、硬さは、例えばＡ硬度で、２０～８０、好ましくは３０～８０の範囲、より好ましくは３０以上６０未満の範囲であり、エポキシ系やウレタン系材料に比べて比較的低い。さらに、本発明の熱伝導性部材は、引張せん断強さが高いうえに、上記したように外力が作用された場合に変位しやすい。そのため、本発明の熱伝導性部材は、例えば自動車の発進や停止、走行時に振動や衝撃を受けても、ある程度緩和でき、かつ破損しにくいので、間隙材１３によってバッテリセル１１を十分に保持できる。
　以下、本発明を実施例により更に詳細に説明するが、本発明はこれらの例によってなんら限定されるものではない。
　なお、本発明では、以下の方法により熱伝導性組成物及び熱伝導性部材を評価する。
［粘度］
　熱伝導性組成物の調製直後（後述する第１剤及び第２剤の混合直後）の２５℃における粘度（Ｐａ・ｓ）を、Ｂ型粘度計（ＢＲＯＯＫＦＩＥＬＤ社製回転粘度計、ＤＶ－Ｅ）を用いて、スピンドル（ＳＣ４－１４）の回転速度を１０ｒｐｍに設定して測定した。
［引張せん断強さ］
　引張せん断強さは、ＪＩＳ　Ｋ６８５０：１９９９の引張せん断試験に準拠して測定した。試験片は、縦１００ｍｍ、横２５ｍｍ、厚さ２ｍｍのアルミニウム板を２枚準備し、互いのアルミニウム板の先端が縦横２５ｍｍ×２５ｍｍの長さで重なる状態に配置し、その間に厚さが１．５ｍｍとなるように、液状の熱伝導性組成物を塗布して、６０℃の恒温槽で２４時間、常置して硬化させることで作製した。引張試験機（東洋精機製作所「STROGRAFH　VE50」）を用いて、室温２５℃、引張速度１００ｍｍ／ｍｉｎの条件で引張試験を行い、引張せん断強さを測定した。また、引張せん断強さが最大となる歪み量を最大引張強さ時の変位とした。
［Ａ硬度］
　熱伝導性部材を、ＪＩＳ　Ｋ　６２５３のタイプＡの硬度計によって測定した。
［熱伝導率］
　熱伝導性部材を厚さ２０ｍｍの板状に切り出し、ＡＳＴＭ　Ｄ５４７０に基づいて熱伝導率を測定した。　
［実施例１～６、比較例１～７］
　表１～３に示す配合にしたがって、第１剤及び第２剤を用意し、第１剤及び第２剤を質量比１：１で混合して、各実施例、比較例の熱伝導性組成物を得た。得られた熱伝導性組成物を室温（２３℃）で２４時間放置することで硬化させて熱伝導性部材を得た。
［実施例７～１０、比較例８～１２］
　表１、４に示す配合にしたがって、第１剤及び第２剤を用意し、第１剤及び第２剤を質量比１：１で混合して、各実施例、比較例の熱伝導性組成物を得た。得られた熱伝導性組成物を室温（２３℃）で２４時間放置することで硬化させて熱伝導性部材を得た。
　なお、実施例７、８では、実施例４に比べて、ビニル基の数に対するＳｉＨ基の数の割合が少なくなるように、また、実施例９、１０では多くなるように、各硬化剤の種類と量を調整した。比較例８、９では、比較例１に比べて、ビニル基の数に対するＳｉＨ基の数の割合が少なくなるように、比較例１０、１１では多くなるように、各硬化剤の種類と量を調整した。
Figure JPOXMLDOC01-appb-T000002
※表１における数値は、質量部である。
※上記液剤（１）及び（２）は、以下のとおりである。
　液剤（１）：ビニル末端オルガノポリシロキサンと、白金触媒を含む液剤。白金触媒は、オルガノポリシロキサンに比べて微量であり、液剤（１）の量は、ビニル末端オルガノポリシロキサンの量とみなす。
　液剤（２）：ビニル末端オルガノポリシロキサンと、Ｓｉ－Ｈ官能基の数が異なる２種のオルガノハイドロジェンポリシロキサンを含む硬化剤を含む液剤。
　各実施例、比較例におけるアルコキシシラン化合物の種類、配合量は、表２～４に示すとおりである。
Figure JPOXMLDOC01-appb-T000003
※表２～４における質量％とは、硬化性オルガノポリシロキサンとアルコキシシラン化合物の合計量に対する、アルコキシシラン化合物の割合（質量％）である。
Figure JPOXMLDOC01-appb-T000004
Figure JPOXMLDOC01-appb-T000005
　以上の実施例では、長鎖アルケニル基含有アルコキシシラン化合物を使用することで、引張せん断強さが高くなり、かつ最大引張強さ時の変位量が大きくなった。そのため、被着体に対する優れた接着性を確保しつつ、外力が作用された際に一定量変位できるようになるので、振動等の外力が作用されても剥離等が生じにくくなる。
　それに対して、比較例では、長鎖アルケニル基含有アルコキシシラン化合物を使用しなかったため、引張せん断強さ及び最大引張強さ時の変位量がいずれも不十分であった。そのため、被着体に対する十分な接着性を確保できず、また、振動等の外力が作用されると剥離等が生じやすくなる。
［実施例１１、参考例１、２］
　実施例２、５、６と同様に、第１剤、第２剤を用意し、常温で１日間放置した。その後、第１剤及び第２剤を質量比１：１で混合して、実施例１１、参考例１、２の熱伝導性組成物を得た。得られた熱伝導性組成物を室温（２３℃）で２４時間放置することで硬化させたところ、実施例１１では硬化したが、参考例１、２では十分に硬化が進行せずに熱伝導性部材が得られなかった。
　以上の実施例１１、参考例１，２から明らかなように、２液型においては、アルコキシシラン化合物（Ｂ）と付加反応触媒（Ｘ）を第１剤に含有させる一方で、第２剤にこれらを含有させないことで、保管後でも硬化が適切に進行し、保存安定性に優れることが理解できる。
　１０　バッテリモジュール
　１１　バッテリセル
　１２　バッテリモジュールの筐体（モジュール筐体）
　１３　隙間材

Claims (10)

  1. 　硬化性オルガノポリシロキサン（Ａ）と、アルコキシシラン化合物（Ｂ）と、熱伝導性充填剤（Ｃ）とを含む熱伝導性組成物であって、
    　前記アルコキシシラン化合物（Ｂ）が、炭素数が８～１８の長鎖アルケニル基含有アルコキシシランである、熱伝導性組成物。
  2. 　第１剤と第２剤を組み合わせてなる、２液型の熱伝導性組成物であって、
    　前記第１剤中には、アルケニル基含有オルガノポリシロキサン（Ａ１）と、アルコキシシラン化合物（Ｂ）と、付加反応触媒（Ｘ）とが含まれ、
    　前記第２剤中には、ハイドロジェンオルガノポリシロキサン（Ａ２）が含まれ、かつ、アルコキシシラン化合物（Ｂ）が含まれず、
    　前記第１剤及び前記第２剤の少なくともいずれか一方に熱伝導性充填剤（Ｃ）を含み、
    　前記アルコキシシラン化合物（Ｂ）が、炭素数が８～１８の長鎖アルケニル基含有アルコキシシランである、熱伝導性組成物。
  3. 　前記第２剤中に、アルケニル基含有オルガノポリシロキサン（Ａ１）が含有される、請求項２に記載の熱伝導性組成物。
  4. 　前記硬化性オルガノポリシロキサン（Ａ）が、付加反応硬化型オルガノポリシロキサンである、請求項１に記載の熱伝導性組成物。
  5. 　該熱伝導性組成物の硬化物の硬度は、Ａ硬度で３０以上６０未満である、請求項１～４のいずれか１項に記載の熱伝導性組成物。
  6. 　前記アルコキシシラン化合物（Ｂ）が、オクテニルトリメトキシシランである、請求項１～５のいずれか１項に記載の熱伝導性組成物。
  7. 　前記アルコキシシラン化合物（Ｂ）の含有量が、硬化性オルガノポリシロキサン（Ａ）とアルコキシシラン化合物（Ｂ）の合計質量に対して、１～１０質量％である、請求項１～６のいずれか１項に記載の熱伝導性組成物。
  8. 　硬化した際の引張せん断強さが１ＭＰａ以上である、請求項１～７のいずれか１項に記載の熱伝導性組成物。
  9. 　請求項１～８のいずれか１項に記載の熱伝導性組成物を硬化してなる熱伝導性部材。
  10. 　請求項９に記載の熱伝導性部材からなる間隙材と、複数のバッテリセルと、前記複数のバッテリセルを格納するモジュール筐体とを備え、前記間隙材がモジュール筐体の内部に配置されるバッテリモジュール。
PCT/JP2020/010511 2019-04-15 2020-03-11 熱伝導性組成物、熱伝導性部材、バッテリモジュール WO2020213306A1 (ja)