WO2020162010A1 - 着色硬化性樹脂組成物 - Google Patents

着色硬化性樹脂組成物 Download PDF

Info

Publication number
WO2020162010A1
WO2020162010A1 PCT/JP2019/047176 JP2019047176W WO2020162010A1 WO 2020162010 A1 WO2020162010 A1 WO 2020162010A1 JP 2019047176 W JP2019047176 W JP 2019047176W WO 2020162010 A1 WO2020162010 A1 WO 2020162010A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
formula
parts
resin
meth
Prior art date
Application number
PCT/JP2019/047176
Other languages
English (en)
French (fr)
Inventor
崇夫 土谷
Original Assignee
住友化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友化学株式会社 filed Critical 住友化学株式会社
Priority to CN201980091164.0A priority Critical patent/CN113383021B/zh
Priority to KR1020217027746A priority patent/KR102701187B1/ko
Publication of WO2020162010A1 publication Critical patent/WO2020162010A1/ja

Abstract

本発明は吸光度保持率に優れたカラーフィルタを形成できる着色硬化性樹脂組成物を提供することを課題とする。　本発明は、着色剤、樹脂、重合性化合物、及び重合開始剤を含み、前記着色剤が、式（Ｉ）で表されるスクアリリウム染料を含む着色剤であり、前記樹脂の固形分換算における酸価が、１００～２００ｍｇ－ＫＯＨ／ｇである着色硬化性樹脂組成物に関する。

Description

着色硬化性樹脂組成物
　本発明は、着色硬化性樹脂組成物に関する。
　液晶表示装置、エレクトロルミネッセンス表示装置及びプラズマディスプレイ等の表示装置やＣＣＤやＣＭＯＳセンサなどの固体撮像素子に使用されるカラーフィルタは、着色樹脂組成物から製造される。このような着色樹脂組成物に用いられる着色剤として、スクアリリウム染料が知られている（特許文献１、２など）。
特開２０１５－８６３７９号公報 特開２０１５－８６３８０号公報
　本発明は吸光度保持率に優れたカラーフィルタを形成できる着色硬化性樹脂組成物を提供することを課題とする。
　本発明の要旨は以下の通りである。
［１］　着色剤、樹脂、重合性化合物、及び重合開始剤を含み、
　前記着色剤が、式（Ｉ）で表されるスクアリリウム染料を含む着色剤であり、
　前記樹脂の固形分換算における酸価が、１００～２００ｍｇ－ＫＯＨ／ｇである着色硬化性樹脂組成物。
Figure JPOXMLDOC01-appb-C000003
 ［式（Ｉ）中、
　Ｒ1～Ｒ4は、それぞれ独立に、水素原子、ハロゲン原子、ヒドロキシ基又は置換基を有していてもよい炭素数１～２０の１価の飽和炭化水素基を表す。該１価の飽和炭化水素基を構成する炭素原子間に、酸素原子又は硫黄原子が挿入されていてもよい。
　Ｒ5～Ｒ8は、それぞれ独立に、水素原子又はヒドロキシ基を表す。
　Ａｒ1及びＡｒ2は、それぞれ独立に、置換基を有していてもよい炭素数１～２０の１価の飽和炭化水素基又は式（ｉ）で表される基を表す。
Figure JPOXMLDOC01-appb-C000004
 ［式（ｉ）中、
　Ｒ12は、置換基を有していてもよい炭素数１～２０の１価の飽和炭化水素基又は置換
基を有していてもよい炭素数２～２０の１価の不飽和炭化水素基を表し、ｍは０～５の整数を表す。該１価の飽和炭化水素基を構成する炭素原子間に、酸素原子又は硫黄原子が
挿入されていてもよい。ｍが２以上のとき、複数のＲ12は、それぞれ同一であっても異なっていてもよい。＊は、窒素原子との結合手を表す。］
　Ｒ9及びＲ10は、それぞれ独立に、置換基を有していてもよい炭素数１～２０の１価の飽和炭化水素基又は式（ｉ）で表される基を表す。該１価の飽和炭化水素基を構成する
炭素原子間に、酸素原子又は硫黄原子が挿入されていてもよい。］
［２］　［１］に記載の着色硬化性樹脂組成物から形成されるカラーフィルタ。
［３］　［２］に記載のカラーフィルタを含む表示装置。
　本発明の着色硬化性樹脂組成物によれば吸光度保持率に優れたカラーフィルタを提供できる。
　本発明の着色硬化性樹脂組成物は、着色剤（以下、着色剤（Ａ）という場合がある）、樹脂（以下、樹脂（Ｂ）という場合がある）、重合性化合物（以下、重合性化合物（Ｃ）という場合がある）、及び重合開始剤（以下、重合開始剤（Ｄ）という場合がある）を含む。
　着色剤は、式（Ｉ）で表されるスクアリリウム染料（以下、化合物（Ｉ）という場合がある）を含む。
　樹脂の固形分換算の酸価は、１００～２００ｍｇ－ＫＯＨ／ｇである。
　本発明の着色硬化性樹脂組成物は、さらに溶剤（以下、溶剤（Ｅ）という場合がある）を含むことが好ましい。
　本発明の着色硬化性樹脂組成物は、レベリング剤（以下、レベリング剤（Ｆ）という場合がある）を含んでもよい。
　本明細書において、各成分として例示する化合物は、特に断りのない限り、単独で又は複数種を組合せて使用することができる。
＜着色剤（Ａ）＞
　着色剤（Ａ）は、化合物（Ｉ）を含む。以下、式（Ｉ）を用いて本発明について詳述するが、化合物（Ｉ）には、式（Ｉ）の共鳴構造や、式（Ｉ）中の各基を単結合の結合軸周りに回転させて得られる化合物も含まれることとする。
Figure JPOXMLDOC01-appb-C000005
［式（Ｉ）中、
　Ｒ1～Ｒ4は、それぞれ独立に、水素原子、ハロゲン原子、ヒドロキシ基又は置換基を有していてもよい炭素数１～２０の１価の飽和炭化水素基を表す。該１価の飽和炭化水素基を構成する炭素原子間に、酸素原子又は硫黄原子が挿入されていてもよい。
　Ｒ5～Ｒ8は、それぞれ独立に、水素原子又はヒドロキシ基を表す。
　Ａｒ1及びＡｒ2は、それぞれ独立に、置換基を有していてもよい炭素数１～２０の１価の飽和炭化水素基又は式（ｉ）で表される基を表し、好ましくは式（ｉ）で表される基
を表す。
Figure JPOXMLDOC01-appb-C000006
 ［式（ｉ）中、
　Ｒ12は、置換基を有していてもよい炭素数１～２０の１価の飽和炭化水素基又は置換
基を有していてもよい炭素数２～２０の１価の不飽和炭化水素基を表し、ｍは０～５の整数を表す。該１価の飽和炭化水素基を構成する炭素原子間に、酸素原子又は硫黄原子が
挿入されていてもよい。ｍが２以上のとき、複数のＲ12は、それぞれ同一であっても異なっていてもよい。＊は、窒素原子との結合手を表す。］
　Ｒ9及びＲ10は、それぞれ独立に、置換基を有していてもよい炭素数１～２０の１価の飽和炭化水素基又は式（ｉ）で表される基を表す。該１価の飽和炭化水素基を構成する
炭素原子間に、酸素原子又は硫黄原子が挿入されていてもよい。］
　式（Ｉ）中、Ｒ1～Ｒ4におけるハロゲン原子としては、フッ素原子、塩素原子、臭素原子又はヨウ素原子が挙げられる。
　Ｒ1～Ｒ4、Ｒ9、Ｒ10、Ｒ12、Ａｒ1及びＡｒ2における炭素数１～２０の１価の飽和炭化水素基としては、例えば、メチル基、エチル基、プロピル基、ブチル基、ペンチル基、
ヘキシル基、ヘプチル基、オクチル基、ノニル基、デシル基、ドデシル基、ヘキサデシル基及びイコシル基等の炭素数１～２０の直鎖状アルキル基；イソプロピル基、イソブチル基、ｓｅｃ－ブチル基、ｔｅｒｔ－ブチル基、イソペンチル基、ネオペンチル基及び２－エチルヘキシル基等の炭素数３～２０の分岐鎖状アルキル基；シクロプロピル基、シクロペンチル基、シクロヘキシル基、シクロヘプチル基、シクロオクチル基、トリシクロデシル基及びアダマンチル基等の炭素数３～２０の脂環式飽和炭化水素基が挙げられる。
　これらの飽和炭化水素基の置換基としては、フッ素原子、塩素原子、ヨウ素等のハロゲン原子；ヒドロキシ基；カルボキシ基；－ＮＲaＲb(Ｒa及びＲbは、それぞれ独立に、水素原子又は炭素数１～２０のアルキル基である)；ニトロ基；メトキシカルボニル基、
エトキシカルボニル基等の炭素数１～１０のアルコキシカルボニル基；等が挙げられ、置換基を有している炭素数１～２０の１価の飽和炭化水素基としては、例えば、下記式で表される基が挙げられる。下記式中、＊は結合手を表す。
Figure JPOXMLDOC01-appb-C000007
　これらの飽和炭化水素基を構成する炭素原子間に、酸素原子又は硫黄原子が挿入され
ている基としては、例えば、下記式で表される基が挙げられる。下記式中、＊は結合手を表す。
Figure JPOXMLDOC01-appb-C000008
　Ｒ12における炭素数２～２０の１価の不飽和炭化水素基としては、例えば、ビニル基、プロペニル基、ブテニル基、ペンテニル基、ヘキセニル基、ヘプテニル基、オクテニル基、ノネニル基、デセニル基が挙げられる。
　該不飽和炭化水素基の置換基としては、フッ素原子、塩素原子、ヨウ素等のハロゲン原子；ヒドロキシ基；カルボキシ基；－ＮＲcＲd(Ｒc及びＲdは、それぞれ独立に、水素原子又は炭素数１～２０のアルキル基である)；ニトロ基；メトキシ基、エトキシ基等の
炭素数１～１０のアルコキシ基；メトキシカルボニル基、エトキシカルボニル基等の炭素数１～１０のアルコキシカルボニル基；等が挙げられる。
　Ｒ1～Ｒ4としては、水素原子、ヒドロキシ基及び炭素数１～４のアルキル基が好ましく、水素原子、ヒドロキシ基及びメチル基がより好ましく、水素原子がさらに好ましい。
　Ｒ5～Ｒ8は、少なくとも１つがヒドロキシ基であることが好ましい。Ｒ5及びＲ6の少なくとも一方がヒドロキシ基であり、Ｒ7及びＲ8の少なくとも一方がヒドロキシ基であることがより好ましい。
　Ｒ9及びＲ10としては、置換基を有していてもよい炭素数３～１４のアルキル基及び式（ｉ）で表される基が好ましく、置換基を有していてもよい炭素数３～６の直鎖状アルキ
ル基、置換基を有していてもよい炭素数７～１４の直鎖状又は分岐鎖状のアルキル基（例えば、オクチル基、ノニル基、デシル基、ドデシル基、２－エチルヘキシル基など）、及び式（ｉ）で表される基がより好ましく、末端にヒドロキシ基を有する炭素数３～５の直鎖状アルキル基、末端にカルボキシ基を有する炭素数３～５の直鎖状アルキル基、及び２－エチルヘキシル基がさらに好ましい。
　Ｒ12の飽和炭化水素基としては、炭素数１～４のアルキル基が好ましく、メチル基、エチル基、イソプロピル基がより好ましい。
　Ｒ12の不飽和炭化水素基としては、炭素数２～４のアルケニル基が好ましく、ビニル基、アリル基がより好ましい。
　ｍが２以上の場合、少なくとも１つのＲ12が飽和炭化水素基であることが好ましい。ｍが２以上の場合、全てのＲ12が飽和炭化水素基である態様、又は一部のＲ12が飽和炭化水素基であって一部のＲ12が不飽和炭化水素基である態様がより好ましい。
　ｍは、好ましくは１～５であり、より好ましくは１～３である。
　式（ｉ）で表される基としては、例えば、次のような基が挙げられる。＊は、窒素原子との結合手を表す。
Figure JPOXMLDOC01-appb-C000009
　式（Ｉ）中、
Figure JPOXMLDOC01-appb-C000010
 で表される基をＸ1、
Figure JPOXMLDOC01-appb-C000011
 で表される基をＸ2としたとき、Ｘ1及びＸ2で表される基としては、例えば、式（Ａ２－１）～（Ａ２－９）で表される基が挙げられる。＊は、炭素原子との結合手を表す。
Figure JPOXMLDOC01-appb-C000012
　化合物（Ｉ）として、例えば、表１に示す化合物（ＡＩＩ－１）～化合物（ＡＩＩ－２７）が挙げられる。
Figure JPOXMLDOC01-appb-T000013
　化合物（ＡＩＩ－１０）～化合物（ＡＩＩ－１８）がより好ましい。
　式（Ｉ）で表される化合物は、式（ｐｔ１）で表される化合物と、式（ｐｔ２）で表される化合物と、式（ｐｔ３）で表される化合物を、反応させることにより製造できる。本反応において、式（ｐｔ３）で表される化合物の使用量は、式（ｐｔ１）で表される化合物及び式（ｐｔ２）で表される化合物の合計１モルに対して、好ましくは０．０５モル以上０．８モル以下であり、より好ましくは０．１モル以上０．６モル以下である。
Figure JPOXMLDOC01-appb-C000014
　式中、Ｒ1～Ｒ10、Ａｒ1及びＡｒ2は、それぞれ上記と同じ意味を表す。
　反応温度は、３０℃～１８０℃が好ましく、８０℃～１４０℃がより好ましい。反応時間は、１時間～１２時間が好ましく、３時間～８時間がより好ましい。
　反応は、収率の点から、有機溶剤中で行うことが好ましい。有機溶剤としては、トルエン、キシレン等の炭化水素溶剤；クロロベンゼン、ジクロロベンゼン、クロロホルム等のハロゲン化炭化水素溶剤；メタノール、エタノール、イソプロパノール、ブタノール等のアルコール溶剤；ニトロベンゼン等のニトロ炭化水素溶剤；メチルイソブチルケトン等のケトン溶剤；１－メチル－２－ピロリドン等のアミド溶剤；等が挙げられ、これらを混合して使用してもよい。中でもブタノール及びトルエンの混合溶剤が好ましい。有機溶剤
の使用量は、式（ｐｔ１）で表される化合物及び式（ｐｔ２）で表される化合物の合計１質量部に対して、好ましくは１０質量部以上２００質量部以下であり、より好ましくは３０質量部以上１５０質量部以下である。
　反応混合物から目的化合物である化合物（Ｉ）を取り出す方法は特に限定されず、公知の種々の方法が使用できる。例えば反応終了後に冷却し、析出した結晶を濾取する方法が挙げられる。濾取した結晶は、水などで洗浄し、次いで乾燥することが好ましい。また必要に応じて、再結晶などの公知の方法によってさらに精製してもよい。
　式（ＩＶ－２）で表される化合物と式（ＩＶ－３）で表される化合物とを反応させて、式（ＩＶ－４）で表される化合物を製造した後、式（ＩＶ－４）で表される化合物と式（ＩＶ－５）で表される化合物とを反応させることにより、式（ｐｔ１）で表される化合物を製造することができる。
Figure JPOXMLDOC01-appb-C000015
　式（ＩＶ－２）～式（ＩＶ－５）中、Ｒ1、Ｒ2、Ｒ5、Ｒ6、Ｒ9及びＡｒ1は、それぞ
れ上記と同じ意味を表す。
　式（ＩＶ－２）で表される化合物と式（ＩＶ－３）で表される化合物とから、式（ＩＶ－４）で表される化合物を製造する方法としては、公知の種々の方法、例えば、Eur. J. Org. Chem. 2012, 3105-3111．に記載されている方法が挙げられる。
　式（ＩＶ－４）で表される化合物と式（ＩＶ－５）で表される化合物とから、式（ｐｔ１）で表される化合物を製造する方法としては、公知の種々の方法、例えばJ.Polymer Sciene Science Part A:Polymer Chemistry 2012, 50, 3788-3796に記載されている方法が
挙げられる。
　上記と同様の方法を用いて、式（ｐｔ２）で表される化合物を製造することができる。
　着色剤（Ａ）は、化合物（Ｉ）以外に、化合物（Ｉ）とは異なる着色剤を含んでいてもよく、該化合物（Ｉ）とは異なる着色剤は、染料（以下、染料（Ａ１）という場合がある。）、及び顔料（以下、顔料（Ａ２）という場合がある。）のいずれでもよく、化合物（Ｉ）とは異なる着色剤は、これら染料（Ａ１）及び顔料（Ａ２）の一方又は両方を含んでいてもよい。
　染料（Ａ１）は、化合物（Ｉ）を包含しない限り、特に限定されず公知の染料を使用することができ、溶剤染料、酸性染料、直接染料、媒染染料等が挙げられる。染料としては、例えば、カラーインデックス（The Society of Dyers and Colourists出版）でピグメント以外で色相を有するものに分類されている化合物や、染色ノート（色染社）に記載さ
れている公知の染料が挙げられる。また、化学構造によれば、アゾ染料、シアニン染料、トリフェニルメタン染料、キサンテン染料、フタロシアニン染料、アントラキノン染料、ナフトキノン染料、キノンイミン染料、メチン染料、アゾメチン染料、アクリジン染料、スチリル染料、クマリン染料、キノリン染料及びニトロ染料等が挙げられる。これらのうち、有機溶剤可溶性染料が好ましい。
　具体的には、Ｃ．Ｉ．ソルベントイエロー４（以下、Ｃ．Ｉ．ソルベントイエローの記載を省略し、番号のみの記載とする。）、１４、１５、２３、２４、３８、６２、６３、６８、８２、９４、９８、９９、１１７、１６２、１６３、１６７、１８９；
　Ｃ．Ｉ．ソルベントレッド４５、４９、１１１、１２５、１３０、１４３、１４５、１４６、１５０、１５１、１５５、１６８、１６９、１７２、１７５、１８１、２０７、２１８、２２２、２２７、２３０、２４５、２４７；
　Ｃ．Ｉ．ソルベントオレンジ２、７、１１、１５、２６、５６、７７、８６；
　Ｃ．Ｉ．ソルベントバイオレット１１、１３、１４、２６、３１、３６、３７、３８、４５、４７、４８、５１、５９、６０；
　Ｃ．Ｉ．ソルベントブルー４、５、１４、１８、３５、３６、３７、４５、５８、５９、５９：１、６３、６７、６８、６９、７０、７８、７９、８３、９０、９４、９７、９８、１００、１０１、１０２、１０４、１０５、１１１、１１２、１２２、１２８、１３２、１３６、１３９；
　Ｃ．Ｉ．ソルベントグリーン１、３、４、５、７、２８、２９、３２、３３、３４、３５等のＣ．Ｉ．ソルベント染料、
　Ｃ．Ｉ．アシッドイエロー１、３、７、９、１１、１７、２３、２５、２９、３４、３６、３８、４０、４２、５４、６５、７２、７３、７６、７９、９８、９９、１１１、１１２、１１３、１１４、１１６、１１９、１２３、１２８、１３４、１３５、１３８、１３９、１４０、１４４、１５０、１５５、１５７、１６０、１６１、１６３、１６８、１６９、１７２、１７７、１７８、１７９、１８４、１９０、１９３、１９６、１９７、１９９、２０２、２０３、２０４、２０５、２０７、２１２、２１４、２２０、２２１、２２８、２３０、２３２、２３５、２３８、２４０、２４２、２４３、２５１；
　Ｃ．Ｉ．アシッドレッド１、４、８、１４、１７、１８、２６、２７、２９、３１、３３、３４、３５、３７、４０、４２、４４、５０、５１、５２、５７、６６、７３、７６、８０、８７、８８、９１、９２、９４、９５、９７、９８、１０３、１０６、１１１、１１４、１２９、１３３、１３４、１３８、１４３、１４５、１５０、１５１、１５５、１５８、１６０、１７２、１７６、１８２、１８３、１９５、１９８、２０６、２１１、２１５、２１６、２１７、２２７、２２８、２４９、２５２、２５７、２５８、２６０、２６１、２６６、２６８、２７０、２７４、２７７、２８０、２８１、２８９、３０８、３１２、３１５、３１６、３３９、３４１、３４５、３４６、３４９、３８２、３８３、３８８、３９４、４０１、４１２、４１７、４１８、４２２、４２６；
　Ｃ．Ｉ．アシッドオレンジ６、７、８、１０、１２、２６、５０、５１、５２、５６、６２、６３、６４、７４、７５、９４、９５、１０７、１０８、１６９、１７３；
　Ｃ．Ｉ．アシッドバイオレット６Ｂ、７、９、１５、１６、１７、１９、２１、２３、２４、２５、３０、３４、３８、４９、７２、１０２；
　Ｃ．Ｉ．アシッドブルー１、３、５、７、９、１１、１３、１５、１７、１８、２２、２３、２４、２５、２６、２７、２９、３４、３８、４０、４１、４２、４３、４５、４８、５１、５４、５９、６０、６２、７０、７２、７４、７５、７８、８０、８２、８３、８６、８７、８８、９０、９０：１、９１、９２、９３、９３：１、９６、９９、１００、１０２、１０３、１０４、１０８、１０９、１１０、１１２、１１３、１１７、１１９、１２０、１２３、１２６、１２７、１２９、１３０、１３１、１３８、１４０、１４２、１４３、１４７、１５０、１５１、１５４、１５８、１６１、１６６、１６７、１６８、１７０、１７１、１７５、１８２、１８３、１８４、１８７、１９２、１９９、２０３、２０４、２０５、２１０、２１３、２２９、２３４、２３６、２４２、２４３、２５６、２５９、２６７、２６９、２７８、２８０、２８５、２９０、２９６、３１５、３２４：１、３３５、３４０；
　Ｃ．Ｉ．アシッドグリーン１、３、５、６、７、８、９、１１、１３、１４、１５、１６、２２、２５、２７、２８、４１、５０、５０：１、５８、６３、６５、８０、１０４、１０５、１０６、１０９等のＣ．Ｉ．アシッド染料、
　Ｃ．Ｉ．ダイレクトイエロー２、３３、３４、３５、３８、３９、４３、４７、５０、５４、５８、６８、６９、７０、７１、８６、９３、９４、９５、９８、１０２、１０８、１０９、１２９、１３６、１３８、１４１；
　Ｃ．Ｉ．ダイレクトレッド７９、８２、８３、８４、９１、９２、９６、９７、９８、９９、１０５、１０６、１０７、１７２、１７３、１７６、１７７、１７９、１８１、１８２、１８４、２０４、２０７、２１１、２１３、２１８、２２０、２２１、２２２、２３２、２３３、２３４、２４１、２４３、２４６、２５０；
　Ｃ．Ｉ．ダイレクトオレンジ２６、３４、３９、４１、４６、５０、５２、５６、５７、６１、６４、６５、６８、７０、９６、９７、１０６、１０７；
　Ｃ．Ｉ．ダイレクトバイオレット４７、５２、５４、５９、６０、６５、６６、７９、８０、８１、８２、８４、８９、９０、９３、９５、９６、１０３、１０４；
　Ｃ．Ｉ．ダイレクトブルー１、２、３、６、８、１５、２２、２５、２８、２９、４０、４１、４２、４７、５２、５５、５７、７１、７６、７７、７８、８０、８１、８４、８５、８６、９０、９３、９４、９５、９７、９８、９９、１００、１０１、１０６、１０７、１０８、１０９、１１３、１１４、１１５、１１７、１１９、１２０、１３７、１４９、１５０、１５３、１５５、１５６、１５８、１５９、１６０、１６１、１６２、１６３、１６４、１６５、１６６、１６７、１６８、１７０、１７１、１７２、１７３、１８８、１８９、１９０、１９２、１９３、１９４、１９５、１９６、１９８、１９９、２００、２０１、２０２、２０３、２０７、２０９、２１０、２１２、２１３、２１４、２２２、２２５、２２６、２２８、２２９、２３６、２３７、２３８、２４２、２４３、２４４、２４５、２４６、２４７、２４８、２４９、２５０、２５１、２５２、２５６、２５７、２５９、２６０、２６８、２７４、２７５、２９３；
　Ｃ．Ｉ．ダイレクトグリーン２５、２７、３１、３２、３４、３７、６３、６５、６６、６７、６８、６９、７２、７７、７９、８２等のＣ．Ｉ．ダイレクト染料、
　Ｃ．Ｉ．ディスパースイエロー５１、５４，７６；
　Ｃ．Ｉ．ディスパースバイオレット２６、２７；
　Ｃ．Ｉ．ディスパースブルー１、１４、５６、６０等のＣ．Ｉ．ディスパース染料、
　Ｃ．Ｉ．ベーシックレッド１、１０；
　Ｃ．Ｉ．ベーシックブルー１、３、５、７、９、１９、２１、２２、２４、２５、２６、２８、２９、４０、４１、４５、４７、５４、５８、５９、６０、６４、６５、６６、６７、６８、８１、８３、８８、８９；
　Ｃ．Ｉ．ベーシックバイオレット２；
　Ｃ．Ｉ．ベーシックレッド９；
　Ｃ．Ｉ．ベーシックグリーン１等のＣ．Ｉ．ベーシック染料、
　Ｃ．Ｉ．リアクティブイエロー２，７６，１１６；
　Ｃ．Ｉ．リアクティブオレンジ１６；
　Ｃ．Ｉ．リアクティブレッド３６等のＣ．Ｉ．リアクティブ染料、
　Ｃ．Ｉ．モーダントイエロー５、８、１０、１６、２０、２６、３０、３１、３３、４２、４３、４５、５６、６１、６２、６５；
　Ｃ．Ｉ．モーダントレッド１、２、３、４、９、１１、１２、１４、１７、１８、１９、２２、２３、２４、２５、２６、２７、２９、３０、３２、３３、３６、３７、３８、３９、４１、４２、４３、４５、４６、４８、５２、５３、５６、６２、６３、７１、７４、７６、７８、８５、８６、８８、９０、９４、９５；
　Ｃ．Ｉ．モーダントオレンジ３、４、５、８、１２、１３、１４、２０、２１、２３、２４、２８、２９、３２、３４、３５、３６、３７、４２、４３、４７、４８；
　Ｃ．Ｉ．モーダントバイオレット１、１：１、２、３、４、５、６、７、８、１０、１１、１４、１５、１６、１７、１８、１９、２１、２２、２３、２４、２７、２８、３０、３１、３２、３３、３６、３７、３９、４０、４１、４４、４５、４７、４８、４９、５３、５８；
　Ｃ．Ｉ．モーダントブルー１、２、３、７、８、９、１２、１３、１５、１６、１９、２０、２１、２２、２３、２４、２６、３０、３１、３２、３９、４０、４１、４３、４４、４８、４９、５３、６１、７４、７７、８３、８４；
　Ｃ．Ｉ．モーダントグリーン１、３、４、５、１０、１３、１５、１９、２１、２３、２６、２９、３１、３３、３４、３５、４１、４３、５３等のＣ．Ｉ．モーダント染料、　Ｃ．Ｉ．バットグリーン１等のＣ．Ｉ．バット染料等が挙げられる。
　これらの染料は、所望するカラーフィルタの分光スペクトルに合わせて適宜選択すればよい。
　顔料（Ａ２）としては、特に限定されず公知の顔料を使用することができ、例えば、カラーインデックス（The Society of Dyers and Colourists出版）でピグメントに分類されている顔料が挙げられる。
　顔料としては、例えば、Ｃ．Ｉ．ピグメントイエロー１、３、１２、１３、１４、１５、１６、１７、２０、２４、３１、５３、８３、８６、９３、９４、１０９、１１０、１１７、１２５、１２８、１３７、１３８、１３９、１４７、１４８、１５０、１５３、１５４、１６６、１７３、１９４、２１４などの黄色顔料；
Ｃ．Ｉ．ピグメントオレンジ１３、３１、３６、３８、４０、４２、４３、５１、５５、５９、６１、６４、６５、７１、７３などのオレンジ色の顔料；
Ｃ．Ｉ．ピグメントレッド９、９７、１０５、１２２、１２３、１４４、１４９、１６６、１６８、１７６、１７７、１８０、１９２、２０９、２１５、２１６、２２４、２４２、２５４、２５５、２６４、２６５などの赤色顔料；
Ｃ．Ｉ．ピグメントブルー１５：６、６０などの青色顔料；
Ｃ．Ｉ．ピグメントバイオレット１、１９、２３、２９、３２、３６、３８などのバイオレット色顔料；
Ｃ．Ｉ．ピグメントグリーン７、３６、５８などの緑色顔料；
Ｃ．Ｉ．ピグメントブラウン２３、２５などのブラウン色顔料；
Ｃ．Ｉ．ピグメントブラック１、７などの黒色顔料等が挙げられる。
　顔料は、必要に応じて、ロジン処理、酸性基又は塩基性基が導入された顔料誘導体等を用いた表面処理、高分子化合物等による顔料表面へのグラフト処理、硫酸微粒化法等による微粒化処理、又は不純物を除去するための有機溶剤や水等による洗浄処理、イオン性不純物のイオン交換法等による除去処理等が施されていてもよい。
　顔料は、粒径が均一であることが好ましい。顔料分散剤を含有させて分散処理を行うことで、顔料が溶液中で均一に分散した状態の顔料分散液を得ることができる。
　前記の顔料分散剤としては、例えば、カチオン系、アニオン系、ノニオン系、両性、ポリエステル系、ポリアミン系、アクリル系等の界面活性剤が挙げられる。これらの顔料分散剤は、単独でも２種以上を組み合わせて用いてもよい。顔料分散剤としては、商品名でＫＰ（信越化学工業（株）製）、フローレン（共栄社化学（株）製）、ソルスパース（ゼネカ（株）製）、ＥＦＫＡ（ＣＩＢＡ社製）、アジスパー（味の素ファインテクノ（株）製）、Ｄｉｓｐｅｒｂｙｋ（ビックケミー社製）などが挙げられる。
　顔料分散剤を用いる場合、その使用量は、顔料（Ａ２）の総量に対して、好ましくは１質量％以上１００質量％以下であり、より好ましくは５質量％以上５０質量％以下である。顔料分散剤の使用量が前記の範囲にあると、均一な分散状態の顔料分散液が得られる傾向がある。
　着色硬化性樹脂組成物における着色剤（Ａ）の含有率は、固形分の総量に対して、好ましくは０．１質量％以上７０質量％以下であり、より好ましくは０．５質量％以上６０質量％以下であり、さらに好ましくは１質量％以上５０質量％以下である。着色剤（Ａ）の含有率が前記の範囲内であると、カラーフィルタとしたときの色濃度が十分であり、かつ組成物中に樹脂（Ｂ）や重合性化合物（Ｃ）を必要量含有させることができるので、機械的強度が十分なパターンを形成することができる。
　ここで、本明細書における「固形分の総量」とは、着色硬化性樹脂組成物の総量から溶剤の含有量を除いた量のことをいう。固形分の総量及びこれに対する各成分の含有量は、例えば、液体クロマトグラフィー又はガスクロマトグラフィーなどの公知の分析手段で測定することができる。
　化合物（Ｉ）の含有率は、着色剤（Ａ）の総量中、１質量％以上であることが好ましく、より好ましくは３質量％以上であり、１００質量％であってもよく、９０質量％以下であってもよく、６０質量％以下であってもよく、４０質量％以下であってもよい。
＜樹脂（Ｂ）＞
　樹脂（Ｂ）は、所定の酸価を有するアルカリ可溶性樹脂である。本発明の着色硬化性樹脂組成物が式（Ｉ）で表される化合物と所定の酸価を有する樹脂（Ｂ）とを含有することにより、カラーフィルタの吸光度保持率が向上する。
　樹脂（Ｂ）としては、以下の樹脂［Ｋ１］～［Ｋ６］等が挙げられる。
　樹脂［Ｋ１］；不飽和カルボン酸及び不飽和カルボン酸無水物からなる群から選ばれる少なくとも１種の単量体（ａ）（以下「（ａ）」という場合がある）に由来する構造単位と、炭素数２～４の環状エーテル構造とエチレン性不飽和結合とを有する単量体（ｂ）（以下「（ｂ）」という場合がある）に由来する構造単位とを有する共重合体；
　樹脂［Ｋ２］；（ａ）に由来する構造単位と、（ｂ）に由来する構造単位と、（ａ）と共重合可能な単量体（ｃ）（ただし、（ａ）及び（ｂ）とは異なる。）（以下「（ｃ）」という場合がある）に由来する構造単位とを有する共重合体；
　樹脂［Ｋ３］；（ａ）に由来する構造単位と、（ｃ）に由来する構造単位とを有する共重合体；
　樹脂［Ｋ４］；（ａ）に由来する構造単位と、（ａ）に由来する構造単位に（ｂ）を付加させた構造単位と、（ｃ）に由来する構造単位とを有する共重合体；
　樹脂［Ｋ５］；（ａ）に由来する構造単位と、（ｂ）に由来する構造単位に（ａ）を付加させた構造単位と、（ｃ）に由来する構造単位とを有する共重合体；
　樹脂［Ｋ６］；（ａ）に由来する構造単位と、（ｂ）に由来する構造単位に（ａ）を付加させ、カルボン酸無水物をさらに付加させた構造単位と、（ｃ）に由来する構造単位とを有する共重合体。
　前記（ａ）に由来する構造単位は、（ａ）が有するカルボキシ基又はカルボン酸無水物が未反応のまま残っていることが好ましい。また樹脂［Ｋ１］、［Ｋ２］では、前記（ｂ）に由来する構造単位は、（ｂ）が有する炭素数２～４の環状エーテル構造が未反応のまま残っていることが好ましい。
　（ａ）としては、具体的には、例えば、アクリル酸、メタクリル酸、クロトン酸、ｏ－、ｍ－、ｐ－ビニル安息香酸等の不飽和モノカルボン酸類；
　マレイン酸、フマル酸、シトラコン酸、メサコン酸、イタコン酸、３－ビニルフタル酸、４－ビニルフタル酸、３，４，５，６－テトラヒドロフタル酸、１，２，３，６－テトラヒドロフタル酸、ジメチルテトラヒドロフタル酸、１、４－シクロヘキセンジカルボン酸等の不飽和ジカルボン酸類；
　メチル－５－ノルボルネン－２，３－ジカルボン酸、５－カルボキシビシクロ［２．２．１］ヘプト－２－エン、５，６－ジカルボキシビシクロ［２．２．１］ヘプト－２－エン、５－カルボキシ－５－メチルビシクロ［２．２．１］ヘプト－２－エン、５－カルボキシ－５－エチルビシクロ［２．２．１］ヘプト－２－エン、５－カルボキシ－６－メチルビシクロ［２．２．１］ヘプト－２－エン、５－カルボキシ－６－エチルビシクロ［２．２．１］ヘプト－２－エン等のカルボキシ基を含有するビシクロ不飽和化合物類；
　無水マレイン酸、シトラコン酸無水物、イタコン酸無水物、３－ビニルフタル酸無水物、４－ビニルフタル酸無水物、３，４，５，６－テトラヒドロフタル酸無水物、１，２，３，６－テトラヒドロフタル酸無水物、ジメチルテトラヒドロフタル酸無水物、５，６－ジカルボキシビシクロ［２．２．１］ヘプト－２－エン無水物等の不飽和ジカルボン酸類無水物；
　こはく酸モノ〔２－（メタ）アクリロイルオキシエチル〕、フタル酸モノ〔２－（メタ）アクリロイルオキシエチル〕等の２価以上の多価カルボン酸の不飽和モノ〔（メタ）アクリロイルオキシアルキル〕エステル類；
　α－（ヒドロキシメチル）アクリル酸のような、同一分子中にヒドロキシ基及びカルボキシ基を含有する不飽和アクリレート類等が挙げられる。
　これらのうち、共重合反応性の点や得られる樹脂のアルカリ水溶液への溶解性の点から、アクリル酸、メタクリル酸、無水マレイン酸等が好ましい。
　（ｂ）は、例えば、炭素数２～４の環状エーテル構造（例えば、オキシラン環、オキセタン環及びテトラヒドロフラン環からなる群から選ばれる少なくとも１種）とエチレン性不飽和結合とを有する重合性化合物をいう。（ｂ）は、炭素数２～４の環状エーテルと（メタ）アクリロイルオキシ基とを有する単量体が好ましい。
　尚、本明細書において、「（メタ）アクリル酸」とは、アクリル酸及びメタクリル酸よりなる群から選ばれる少なくとも１種を表す。「（メタ）アクリロイル」及び「（メタ）アクリレート」等の表記も、同様の意味を有する。
　（ｂ）としては、例えば、オキシラニル基とエチレン性不飽和結合とを有する単量体（ｂ１）（以下「（ｂ１）」という場合がある）、オキセタニル基とエチレン性不飽和結合とを有する単量体（ｂ２）（以下「（ｂ２）」という場合がある）、テトラヒドロフリル基とエチレン性不飽和結合とを有する単量体（ｂ３）（以下「（ｂ３）」という場合がある）等が挙げられる。
　（ｂ１）としては、例えば、直鎖状又は分枝鎖状の脂肪族不飽和炭化水素がエポキシ化された構造を有する単量体（ｂ１－１）（以下「（ｂ１－１）」という場合がある）、脂環式不飽和炭化水素がエポキシ化された構造を有する単量体（ｂ１－２）（以下「（ｂ１－２）」という場合がある）が挙げられる。
　（ｂ１－１）としては、グリシジル（メタ）アクリレート、β－メチルグリシジル（メタ）アクリレート、β－エチルグリシジル（メタ）アクリレート、グリシジルビニルエーテル、ｏ－ビニルベンジルグリシジルエーテル、ｍ－ビニルベンジルグリシジルエーテル、ｐ－ビニルベンジルグリシジルエーテル、α－メチル－ｏ－ビニルベンジルグリシジルエーテル、α－メチル－ｍ－ビニルベンジルグリシジルエーテル、α－メチル－ｐ－ビニルベンジルグリシジルエーテル、２，３－ビス（グリシジルオキシメチル）スチレン、２，４－ビス（グリシジルオキシメチル）スチレン、２，５－ビス（グリシジルオキシメチル）スチレン、２，６－ビス（グリシジルオキシメチル）スチレン、２，３，４－トリス（グリシジルオキシメチル）スチレン、２，３，５－トリス（グリシジルオキシメチル）スチレン、２，３，６－トリス（グリシジルオキシメチル）スチレン、３，４，５－トリス（グリシジルオキシメチル）スチレン、２，４，６－トリス（グリシジルオキシメチル）スチレン等が挙げられる。
　（ｂ１－２）としては、ビニルシクロヘキセンモノオキサイド、１，２－エポキシ－４－ビニルシクロヘキサン（例えば、セロキサイド２０００；（株）ダイセル製）、３，４－エポキシシクロヘキシルメチル（メタ）アクリレート（例えば、サイクロマーＡ４００；（株）ダイセル製）、３，４－エポキシシクロヘキシルメチル（メタ）アクリレート（例えば、サイクロマーＭ１００；（株）ダイセル製）、式（ＢＩ）で表される化合物及び式（ＢＩＩ）で表される化合物等が挙げられる。
Figure JPOXMLDOC01-appb-C000016
［式（ＢＩ）及び式（ＢＩＩ）中、Ｒe及びＲfは、水素原子、又は炭素数１～４のアルキル基を表し、該アルキル基に含まれる水素原子は、ヒドロキシ基で置換されていてもよい。
　Ｘe及びＸfは、単結合、＊－Ｒg－、＊－Ｒg－Ｏ－、＊－Ｒg－Ｓ－又は＊－Ｒg－ＮＨ－を表す。
　Ｒgは、炭素数１～６のアルカンジイル基を表す。
　＊は、Ｏとの結合手を表す。］
　炭素数１～４のアルキル基としては、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ｎ－ブチル基、ｓｅｃ－ブチル基、ｔｅｒｔ－ブチル基等が挙げられる。
　水素原子がヒドロキシで置換されたアルキル基としては、ヒドロキシメチル基、１－ヒドロキシエチル基、２－ヒドロキシエチル基、１－ヒドロキシプロピル基、２－ヒドロキシプロピル基、３－ヒドロキシプロピル基、１－ヒドロキシ－１－メチルエチル基、２－ヒドロキシ－１－メチルエチル基、１－ヒドロキシブチル基、２－ヒドロキシブチル基、３－ヒドロキシブチル基、４－ヒドロキシブチル基等が挙げられる。
　Ｒe及びＲfとしては、好ましくは水素原子、メチル基、ヒドロキシメチル基、１－ヒドロキシエチル基、２－ヒドロキシエチル基が挙げられ、より好ましくは水素原子、メチル基が挙げられる。
　アルカンジイル基としては、メチレン基、エチレン基、プロパン－１，２－ジイル基、プロパン－１，３－ジイル基、ブタン－１，４－ジイル基、ペンタン－１，５－ジイル基、ヘキサン－１，６－ジイル基等が挙げられる。
　Ｘe及びＸfとしては、好ましくは単結合、メチレン基、エチレン基、＊－ＣＨ2－Ｏ－及び＊－ＣＨ2ＣＨ2－Ｏ－が挙げられ、より好ましくは単結合、＊－ＣＨ2ＣＨ2－Ｏ－が
挙げられる（＊はＯとの結合手を表す）。
　式（ＢＩ）で表される化合物としては、式（ＢＩ－１）～式（ＢＩ－１５）のいずれかで表される化合物等が挙げられる。中でも、式（ＢＩ－１）、式（ＢＩ－３）、式（ＢＩ－５）、式（ＢＩ－７）、式（ＢＩ－９）又は式（ＢＩ－１１）～式（ＢＩ－１５）で表される化合物が好ましく、式（ＢＩ－１）、式（ＢＩ－７）、式（ＢＩ－９）又は式（ＢＩ－１５）で表される化合物がより好ましい。
Figure JPOXMLDOC01-appb-C000017
　式（ＢＩＩ）で表される化合物としては、式（ＢＩＩ－１）～式（ＢＩＩ－１５）のいずれかで表される化合物等が挙げられる。中でも、式（ＢＩＩ－１）、式（ＢＩＩ－３）、式（ＢＩＩ－５）、式（ＢＩＩ－７）、式（ＢＩＩ－９）又は式（ＢＩＩ－１１）～式（ＢＩＩ－１５）で表される化合物が好ましく、式（ＢＩＩ－１）、式（ＢＩＩ－７）、式（ＢＩＩ－９）又は式（ＢＩＩ－１５）で表される化合物がより好ましい。
Figure JPOXMLDOC01-appb-C000018
　式（ＢＩ）で表される化合物及び式（ＢＩＩ）で表される化合物は、それぞれ単独で用いても、２種以上を併用してもよい。式（ＢＩ）で表される化合物及び式（ＢＩＩ）で表される化合物を併用する場合、これらの含有比率〔式（ＢＩ）で表される化合物：式（ＢＩＩ）で表される化合物〕はモル基準で、好ましくは５：９５～９５：５、より好ましくは２０：８０～８０：２０である。
　（ｂ２）としては、オキセタニル基と（メタ）アクリロイルオキシ基とを有する単量体がより好ましい。（ｂ２）としては、３－メチル－３－メタクリルロイルオキシメチルオキセタン、３－メチル－３－アクリロイルオキシメチルオキセタン、３－エチル－３－メタクリロイルオキシメチルオキセタン、３－エチル－３－アクリロイルオキシメチルオキセタン、３－メチル－３－メタクリロイルオキシエチルオキセタン、３－メチル－３－アクリロイルオキシエチルオキセタン、３－エチル－３－メタクリロイルオキシエチルオキセタン、３－エチル－３－アクリロイルオキシエチルオキセタン等が挙げられる。
　（ｂ３）としては、テトラヒドロフリル基と（メタ）アクリロイルオキシ基とを有する単量体がより好ましい。（ｂ３）としては、具体的には、テトラヒドロフルフリルアクリレート（例えば、ビスコートＶ＃１５０、大阪有機化学工業（株）製）、テトラヒドロフルフリルメタクリレート等が挙げられる。
　（ｂ）としては、得られるカラーフィルタの耐熱性、耐薬品性等の信頼性をより高くすることができる点で、（ｂ１）であることが好ましい。さらに、着色硬化性樹脂組成物の保存安定性が優れるという点で、（ｂ１－２）がより好ましい。
　（ｃ）としては、例えば、メチル（メタ）アクリレート、エチル（メタ）アクリレート、ｎ－ブチル（メタ）アクリレート、ｓｅｃ－ブチル（メタ）アクリレート、ｔｅｒｔ－ブチル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、ドデシル（メタ）アクリレート、ラウリル（メタ）アクリレート、ステアリル（メタ）アクリレート、シクロペンチル（メタ）アクリレート、シクロヘキシル（メタ）アクリレート、２－メチルシクロヘキシル（メタ）アクリレート、トリシクロ［５．２．１．０2,6］デカン－８－イル（メタ）アクリレート（当該技術分野では、慣用名として「ジシクロペンタニル（
メタ）アクリレート」といわれている。また、「トリシクロデシル（メタ）アクリレート」という場合がある。）、トリシクロ［５．２．１．０2,6］デセン－８－イル（メタ）アクリレート（当該技術分野では、慣用名として「ジシクロペンテニル（メタ）アクリレ
ート」といわれている。）、ジシクロペンタニルオキシエチル（メタ）アクリレート、イソボルニル（メタ）アクリレート、アダマンチル（メタ）アクリレート、アリル（メタ）アクリレート、プロパルギル（メタ）アクリレート、フェニル（メタ）アクリレート、ナフチル（メタ）アクリレート、ベンジル（メタ）アクリレート等の（メタ）アクリル酸エステル類；
　２－ヒドロキシエチル（メタ）アクリレート、２－ヒドロキシプロピル（メタ）アクリレート等のヒドロキシ基含有（メタ）アクリル酸エステル類；
　マレイン酸ジエチル、フマル酸ジエチル、イタコン酸ジエチル等のジカルボン酸ジエステル；
　ビシクロ［２．２．１］ヘプト－２－エン、５－メチルビシクロ［２．２．１］ヘプト－２－エン、５－エチルビシクロ［２．２．１］ヘプト－２－エン、５－ヒドロキシビシクロ［２．２．１］ヘプト－２－エン、５－ヒドロキシメチルビシクロ［２．２．１］ヘプト－２－エン、５－（２’－ヒドロキシエチル）ビシクロ［２．２．１］ヘプト－２－エン、５－メトキシビシクロ［２．２．１］ヘプト－２－エン、５－エトキシビシクロ［２．２．１］ヘプト－２－エン、５，６－ジヒドロキシビシクロ［２．２．１］ヘプト－２－エン、５，６－ジ（ヒドロキシメチル）ビシクロ［２．２．１］ヘプト－２－エン、５，６－ジ（２’－ヒドロキシエチル）ビシクロ［２．２．１］ヘプト－２－エン、５，６－ジメトキシビシクロ［２．２．１］ヘプト－２－エン、５，６－ジエトキシビシクロ［２．２．１］ヘプト－２－エン、５－ヒドロキシ－５－メチルビシクロ［２．２．１］ヘプト－２－エン、５－ヒドロキシ－５－エチルビシクロ［２．２．１］ヘプト－２－エン、５－ヒドロキシメチル－５－メチルビシクロ［２．２．１］ヘプト－２－エン、５－ｔｅｒｔ－ブトキシカルボニルビシクロ［２．２．１］ヘプト－２－エン、５－シクロヘキシルオキシカルボニルビシクロ［２．２．１］ヘプト－２－エン、５－フェノキシカルボニルビシクロ［２．２．１］ヘプト－２－エン、５，６－ビス（ｔｅｒｔ－ブトキシカルボニル）ビシクロ［２．２．１］ヘプト－２－エン、５，６－ビス（シクロヘキシルオキシカルボニル）ビシクロ［２．２．１］ヘプト－２－エン等のビシクロ不飽和化合物類；
　Ｎ－フェニルマレイミド、Ｎ－シクロヘキシルマレイミド、Ｎ－ベンジルマレイミド、Ｎ－スクシンイミジル－３－マレイミドベンゾエート、Ｎ－スクシンイミジル－４－マレイミドブチレート、Ｎ－スクシンイミジル－６－マレイミドカプロエート、Ｎ－スクシンイミジル－３－マレイミドプロピオネート、Ｎ－（９－アクリジニル）マレイミド等のＮ－置換マレイミド類；
　スチレン、α－メチルスチレン、ｍ－メチルスチレン、ｐ－メチルスチレン、ビニルトルエン、ｐ－メトキシスチレン、アクリロニトリル、メタクリロニトリル、塩化ビニル、塩化ビニリデン、アクリルアミド、メタクリルアミド、酢酸ビニル、１，３－ブタジエン、イソプレン、２，３－ジメチル－１，３－ブタジエン等が挙げられる。
　（ｃ）としては、共重合反応性及び耐熱性の点から、スチレン、ビニルトルエン、Ｎ－置換マレイミド、ビシクロ［２．２．１］ヘプト－２－エン等が好ましい。
　樹脂［Ｋ１］において、それぞれに由来する構造単位の比率は、樹脂［Ｋ１］を構成する全構造単位中、
（ａ）に由来する構造単位；２～６０モル％
（ｂ）に由来する構造単位；４０～９８モル％
であることが好ましく、
（ａ）に由来する構造単位；１０～５０モル％
（ｂ）に由来する構造単位；５０～９０モル％
であることがより好ましい。
　樹脂［Ｋ１］の構造単位の比率が、上記の範囲にあると、着色硬化性樹脂組成物から得られるカラーフィルタの吸光保持率をより一層向上できる。
　樹脂［Ｋ１］は、例えば、文献「高分子合成の実験法」（大津隆行著　発行所（株）化学同人　第１版第１刷　１９７２年３月１日発行）に記載された方法及び当該文献に記載された引用文献を参考にして製造することができる。
　具体的には、（ａ）及び（ｂ）の所定量、重合開始剤及び溶剤等を反応容器中に入れて、例えば、窒素により酸素を置換することにより、脱酸素雰囲気にし、攪拌しながら、加熱及び保温する方法が挙げられる。なお、ここで用いられる重合開始剤及び溶剤等は、特に限定されず、当該分野で通常使用されているものを使用することができる。例えば、重合開始剤としては、アゾ化合物（２，２’－アゾビスイソブチロニトリル、２，２’－アゾビス（２，４－ジメチルバレロニトリル）等）や有機過酸化物（ベンゾイルペルオキシド等）が挙げられ、溶剤としては、各モノマーを溶解するものであればよく、本発明の着色硬化性樹脂組成物の溶剤（Ｅ）として後述する溶剤等が挙げられる。
　なお、得られた共重合体は、反応後の溶液をそのまま使用してもよいし、濃縮あるいは希釈した溶液を使用してもよいし、再沈殿等の方法で固体（粉体）として取り出したものを使用してもよい。特に、この重合の際に溶剤として、本発明の着色硬化性樹脂組成物に含まれる溶剤を使用することにより、反応後の溶液をそのまま本発明の着色硬化性樹脂組成物の調製に使用することができるため、本発明の着色硬化性樹脂組成物の製造工程を簡略化することができる。
　樹脂［Ｋ２］において、それぞれに由来する構造単位の比率は、樹脂［Ｋ２］を構成する全構造単位中、
（ａ）に由来する構造単位；２～６０モル％
（ｂ）に由来する構造単位；２～９５モル％
（ｃ）に由来する構造単位；１～６５モル％
であることが好ましく、
（ａ）に由来する構造単位；５～５０モル％
（ｂ）に由来する構造単位；５～８０モル％
（ｃ）に由来する構造単位；５～６０モル％
であることがより好ましい。
　樹脂［Ｋ２］の構造単位の比率が、上記の範囲にあると、着色硬化性樹脂組成物から得られるカラーフィルタの吸光保持率をより一層向上できる。
　樹脂［Ｋ２］は、例えば、樹脂［Ｋ１］の製造方法として記載した方法と同様に製造することができる。
　樹脂［Ｋ３］において、それぞれに由来する構造単位の比率は、樹脂［Ｋ３］を構成する全構造単位中、
（ａ）に由来する構造単位；２～６０モル％
（ｃ）に由来する構造単位；４０～９８モル％
であることが好ましく、
（ａ）に由来する構造単位；１０～５０モル％
（ｃ）に由来する構造単位；５０～９０モル％
であることがより好ましい。
　樹脂［Ｋ３］の構造単位の比率が、上記の範囲にあると、着色硬化性樹脂組成物から得られるカラーフィルタの吸光保持率をより一層向上できる。
　樹脂［Ｋ３］は、例えば、樹脂［Ｋ１］の製造方法として記載した方法と同様に製造することができる。
　樹脂［Ｋ４］は、（ａ）と（ｃ）との共重合体を得て、（ｂ）が有する炭素数２～４の環状エーテルを（ａ）が有するカルボン酸及び／又はカルボン酸無水物に付加させることにより製造することができる。また（ｂ）のモル量を（ａ）よりも少なくすることで、（ａ）に由来する構造単位の一部を（ｂ）と反応させることなく残しておくことができる。
　まず（ａ）と（ｃ）との共重合体を、樹脂［Ｋ１］の製造方法として記載した方法と同様に製造する。この場合、それぞれに由来する構造単位の比率は、樹脂［Ｋ３］で挙げたもの同じ比率であることが好ましい。
　次に、前記共重合体中の（ａ）に由来するカルボン酸及び／又はカルボン酸無水物の一部に、（ｂ）が有する炭素数２～４の環状エーテルを反応させる。
　（ａ）と（ｃ）との共重合体の製造に引き続き、フラスコ内雰囲気を窒素から空気に置換し、（ｂ）、カルボン酸又はカルボン酸無水物と環状エーテルとの反応触媒（例えばトリス（ジメチルアミノメチル）フェノール等）及び重合禁止剤（例えばハイドロキノン等）等をフラスコ内に入れて、例えば、６０～１３０℃で、１～１０時間反応することにより、樹脂［Ｋ４］を製造することができる。
　（ｂ）の使用量は、（ａ）１００モルに対して、５～８０モルが好ましく、より好ましくは１０～７５モルである。この範囲にすることにより、着色硬化性樹脂組成物の保存安定性、パターンを形成する際の現像性、並びに、得られるパターンの耐溶剤性、耐熱性、機械強度及び感度のバランスが良好になる傾向がある。環状エーテルの反応性が高く、未反応の（ｂ）が残存しにくいことから、樹脂［Ｋ４］に用いる（ｂ）としては（ｂ１）が好ましい。
　前記反応触媒の使用量は、（ａ）、（ｂ）及び（ｃ）の合計量１００質量部に対して０．００１～５質量部が好ましい。前記重合禁止剤の使用量は、（ａ）、（ｂ）及び（ｃ）の合計量１００質量部に対して０．００１～５質量部が好ましい。
　仕込方法、反応温度及び時間等の反応条件は、製造設備や重合による発熱量等を考慮して適宜調整することができる。なお、重合条件と同様に、製造設備や重合による発熱量等を考慮し、仕込方法や反応温度を適宜調整することができる。
　樹脂［Ｋ５］は、第一段階として、上述した樹脂［Ｋ１］の製造方法と同様にして、（ａ）と（ｂ）と（ｃ）との共重合体を得る。上記と同様に、得られた共重合体は、反応後の溶液をそのまま使用してもよいし、濃縮あるいは希釈した溶液を使用してもよいし、再沈殿等の方法で固体（粉体）として取り出したものを使用してもよい。
　（ａ）、（ｂ）及び（ｃ）に由来する構造単位の比率は、前記の共重合体を構成する全構造単位の合計モル数に対して、それぞれ、
（ａ）に由来する構造単位；２～６０モル％
（ｂ）に由来する構造単位；２～９５モル％
（ｃ）に由来する構造単位；１～６５モル％
であることが好ましく、
（ａ）に由来する構造単位；５～５０モル％
（ｂ）に由来する構造単位；５～８０モル％
（ｃ）に由来する構造単位；５～６０モル％
であることがより好ましい。
　さらに、樹脂［Ｋ４］の製造方法と同様の条件で、（ａ）と（ｂ）と（ｃ）との共重合体が有する（ｂ）に由来する環状エーテルに、（ａ）が有するカルボン酸又はカルボン酸無水物を反応させることにより、樹脂［Ｋ５］を得ることができる。
　前記の共重合体に反応させる（ａ）の使用量は、（ｂ）１００モルに対して、５～８０モルが好ましい。環状エーテルの反応性が高く、未反応の（ｂ）が残存しにくいことから、樹脂［Ｋ５］に用いる（ｂ）としては（ｂ１）が好ましい。
　樹脂［Ｋ６］は、樹脂［Ｋ５］に、さらにカルボン酸無水物を反応させた樹脂である。
　環状エーテルとカルボン酸又はカルボン酸無水物との反応により発生する樹脂［Ｋ５］のヒドロキシ基に、カルボン酸無水物を反応させることで樹脂［Ｋ６］を製造できる。
　カルボン酸無水物としては、無水マレイン酸、シトラコン酸無水物、イタコン酸無水物、３－ビニルフタル酸無水物、４－ビニルフタル酸無水物、３，４，５，６－テトラヒドロフタル酸無水物、１，２，３，６－テトラヒドロフタル酸無水物、ジメチルテトラヒドロフタル酸無水物、５，６－ジカルボキシビシクロ［２．２．１］ヘプト－２－エン無水物等が挙げられる。カルボン酸無水物の使用量は、上記環状エーテルとカルボン酸又はカルボン酸無水物との反応により発生したヒドロキシ基１モルに対して、０．５～１モルが好ましい。
　樹脂（Ｂ）としては、具体的に、３，４－エポキシシクロヘキシルメチル（メタ）アクリレート／（メタ）アクリル酸共重合体、３，４－エポキシトリシクロ［５．２．１．０2.6］デシルアクリレート／（メタ）アクリル酸共重合体等の樹脂［Ｋ１］；グリシジル（メタ）アクリレート／ベンジル（メタ）アクリレート／（メタ）アクリル酸共重合体、
グリシジル（メタ）アクリレート／スチレン／（メタ）アクリル酸共重合体、３，４－エポキシトリシクロ［５．２．１．０2,6］デシルアクリレート／（メタ）アクリル酸／Ｎ－シクロヘキシルマレイミド共重合体、３－メチル－３－（メタ）アクリルロイルオキシ
メチルオキセタン／（メタ）アクリル酸／スチレン共重合体等の樹脂［Ｋ２］；ベンジル（メタ）アクリレート／（メタ）アクリル酸共重合体、スチレン／（メタ）アクリル酸共重合体等の樹脂［Ｋ３］；ベンジル（メタ）アクリレート／（メタ）アクリル酸共重合体にグリシジル（メタ）アクリレートを付加させた樹脂、トリシクロデシル（メタ）アクリレート／スチレン／（メタ）アクリル酸共重合体にグリシジル（メタ）アクリレートを付加させた樹脂、トリシクロデシル（メタ）アクリレート／ベンジル（メタ）アクリレート／（メタ）アクリル酸共重合体にグリシジル（メタ）アクリレートを付加させた樹脂等の樹脂［Ｋ４］；トリシクロデシル（メタ）アクリレート／（メタ）アクリル酸／グリシジル（メタ）アクリレートの共重合体に（メタ）アクリル酸を反応させた樹脂、トリシクロデシル（メタ）アクリレート／（メタ）アクリル酸／スチレン／グリシジル（メタ）アクリレートの共重合体に（メタ）アクリル酸を反応させた樹脂等の樹脂［Ｋ５］；トリシクロデシル（メタ）アクリレート／（メタ）アクリル酸／グリシジル（メタ）アクリレートの共重合体に（メタ）アクリル酸を反応させた樹脂にさらにテトラヒドロフタル酸無水物を反応させた樹脂等の樹脂［Ｋ６］等が挙げられる。
　中でも、樹脂（Ｂ）としては、樹脂［Ｋ１］及び樹脂［Ｋ２］が好ましい。
　樹脂（Ｂ）は２種以上の樹脂を混合してもよく、例えば樹脂［Ｋ１］～樹脂［Ｋ６］からなる群より選ばれる２種以上を混合してもよい。
　樹脂（Ｂ）のポリスチレン換算の重量平均分子量は、好ましくは３，０００～１００，０００であり、より好ましくは５，０００～５０，０００であり、さらに好ましくは５，０００～３０，０００である。分子量が前記の範囲内にあると、カラーフィルタの硬度が向上し、残膜率が高く、未露光部の現像液に対する溶解性が良好で、着色パターンの解像度が向上する傾向がある。
　樹脂（Ｂ）の分散度［重量平均分子量（Ｍｗ）／数平均分子量（Ｍｎ）］は、好ましくは１．１～６であり、より好ましくは１．２～４である。
　樹脂（Ｂ）の合計酸価は、固形分換算で、１００～２００ｍｇ－ＫＯＨ／ｇであり、好ましくは１０５ｍｇ－ＫＯＨ／ｇ以上、より好ましくは１１０ｍｇ－ＫＯＨ／ｇ以上であり、好ましくは１９５ｍｇ－ＫＯＨ／ｇ以下、より好ましくは１９０ｍｇ－ＫＯＨ／ｇ以下である。ここで酸価は樹脂（Ｂ）１ｇを中和するために必要な水酸化カリウムの量（ｍｇ）として測定される値であり、例えば水酸化カリウム水溶液を用いて滴定することにより求めることができる。酸価の値が好ましい範囲に近いほど、着色硬化性樹脂組成物から得られるカラーフィルタの吸光度保持率、パターン現像性及び耐熱性を向上できる。
　樹脂（Ｂ）が２種以上の樹脂を混合したものである場合、樹脂（Ｂ）の酸価は、各々の樹脂の酸価と混合比率を用いて算出される。例えば、酸価が２００ｍｇ－ＫＯＨ／ｇである樹脂５０質量部と酸価が１００ｍｇ－ＫＯＨ／ｇである樹脂５０質量部とを混合した場合、得られる樹脂の酸価は１５０ｍｇ－ＫＯＨ／ｇとなる。
　樹脂（Ｂ）の含有率は、固形分の総量に対して、好ましくは７～６５質量％であり、より好ましくは１３～６０質量％であり、さらに好ましくは１７～５５質量％である。樹脂（Ｂ）の含有率が、前記の範囲内にあると、着色パターンが形成でき、また着色パターンの解像度及び残膜率が向上する傾向がある。
＜重合性化合物（Ｃ）＞
　重合性化合物（Ｃ）は、重合開始剤（Ｄ）から発生した活性ラジカル及び／又は酸によって重合しうる化合物であり、例えば、重合性のエチレン性不飽和結合を有する化合物が挙げられ、好ましくは（メタ）アクリル酸エステル化合物である。
　中でも、重合性化合物（Ｃ）は、エチレン性不飽和結合を３つ以上有する重合性化合物であることが好ましい。このような重合性化合物としては、例えば、トリメチロールプロパントリ（メタ）アクリレート、ペンタエリスリトールトリ（メタ）アクリレート、ペンタエリスリトールテトラ（メタ）アクリレート、ジペンタエリスリトールペンタ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート、トリペンタエリスリトールオクタ（メタ）アクリレート、トリペンタエリスリトールヘプタ（メタ）アクリレート、テトラペンタエリスリトールデカ（メタ）アクリレート、テトラペンタエリスリトールノナ（メタ）アクリレート、トリス（２－（メタ）アクリロイルオキシエチル）イソシアヌレート、エチレングリコール変性ペンタエリスリトールテトラ（メタ）アクリレート、エチレングリコール変性ジペンタエリスリトールヘキサ（メタ）アクリレート、プロピレングリコール変性ペンタエリスリトールテトラ（メタ）アクリレート、プロピレングリコール変性ジペンタエリスリトールヘキサ（メタ）アクリレート、カプロラクトン変性ペンタエリスリトールテトラ（メタ）アクリレート、カプロラクトン変性ジペンタエリスリトールヘキサ（メタ）アクリレートが挙げられる。
　中でも、ジペンタエリスリトールペンタ（メタ）アクリレート及びジペンタエリスリトールヘキサ（メタ）アクリレートが好ましい。
　重合性化合物（Ｃ）の含有率は、固形分の総量に対して、１～６５質量％であることが好ましく、より好ましくは５～６０質量％であり、さらに好ましくは１０～５５質量％である。重合性化合物（Ｃ）の含有率が、前記の範囲内にあると、着色パターン形成時の残膜率及びカラーフィルタの耐薬品性が向上する傾向がある。
＜重合開始剤（Ｄ）＞
　重合開始剤（Ｄ）は、光や熱の作用により活性ラジカル、酸等を発生し、重合を開始しうる化合物であれば特に限定されることなく、公知の重合開始剤を用いることができる。
活性ラジカルを発生する重合開始剤としては、例えば、Ｏ－アシルオキシム化合物、アルキルフェノン化合物、トリアジン化合物、アシルホスフィンオキサイド化合物及びビイミダゾール化合物が挙げられる。
　前記Ｏ－アシルオキシム化合物としては、例えば、Ｎ－ベンゾイルオキシ－１－（４－フェニルスルファニルフェニル）ブタン－１－オン－２－イミン、Ｎ－ベンゾイルオキシ－１－（４－フェニルスルファニルフェニル）オクタン－１－オン－２－イミン、Ｎ－ベンゾイルオキシ－１－（４－フェニルスルファニルフェニル）－３－シクロペンチルプロパン－１－オン－２－イミン、Ｎ－アセチルオキシ－１－（４－フェニルスルファニルフェニル）－３－シクロヘキシルプロパン－１－オン－２－イミン等のジフェニルスルフィド骨格を有するＯ－アシルオキシム化合物；Ｎ－アセトキシ－１－［９－エチル－６－（２－メチルベンゾイル）－９Ｈ－カルバゾール－３－イル］エタン－１－イミン、Ｎ－アセトキシ－１－［９－エチル－６－｛２－メチル－４－（３，３－ジメチル－２，４－ジオキサシクロペンタニルメチルオキシ）ベンゾイル｝－９Ｈ－カルバゾール－３－イル］エタン－１－イミン、Ｎ－アセトキシ－１－［９－エチル－６－（２－メチルベンゾイル）－９Ｈ－カルバゾール－３－イル］－３－シクロペンチルプロパン－１－イミン、Ｎ－ベンゾイルオキシ－１－［９－エチル－６－（２－メチルベンゾイル）－９Ｈ－カルバゾール－３－イル］－３－シクロペンチルプロパン－１－オン－２－イミン等のカルバゾール骨格を有するＯ－アシルオキシム化合物；１－［７－（２－メチルベンゾイル）－９，９－ジプロピル－９Ｈ－フルオレン－２－イル］エタノン　Ｏ－アセチルオキシム等のフルオレン骨格を有するＯ－アシルオキシム化合物；等が挙げられる。イルガキュア（登録商標）ＯＸＥ０１、ＯＸＥ０２（以上、ＢＡＳＦ社製）、Ｎ－１９１９（ＡＤＥＫＡ社製）、ＤＦＩ－０９１（ダイトーケミックス株式会社製）等の市販品を用いてもよい。中でも、Ｏ－アシルオキシム化合物は、Ｎ－ベンゾイルオキシ－１－（４－フェニルスルファニルフェニル）オクタン－１－オン－２－イミン、Ｎ－アセチルオキシ－１－（４－フェニルスルファニルフェニル）－３－シクロヘキシルプロパン－１－オン－２－イミン、Ｎ－アセトキシ－１－［９－エチル－６－｛２－メチル－４－（３，３－ジメチル－２，４－ジオキサシクロペンタニルメチルオキシ）ベンゾイル｝－９Ｈ－カルバゾール－３－イル］エタン－１－イミン及び１－［７－（２－メチルベンゾイル）－９，９－ジプロピル－９Ｈ－フルオレン－２－イル］エタノン　Ｏ－アセチルオキシムからなる群から選ばれる少なくとも１種が好ましい。これらのＯ－アシルオキシム化合物であると、高明度なカラーフィルタが得られる傾向にある。
　前記アルキルフェノン化合物としては、例えば、２－メチル－２－モルホリノ－１－（４－メチルスルファニルフェニル）プロパン－１－オン、２－ジメチルアミノ－１－（４－モルホリノフェニル）－２－ベンジルブタン－１－オン、２－（ジメチルアミノ）－２－［（４－メチルフェニル）メチル］－１－［４－（４－モルホリニル）フェニル］ブタン－１－オン、２－ヒドロキシ－２－メチル－１－フェニルプロパン－１－オン、２－ヒドロキシ－２－メチル－１－〔４－（２－ヒドロキシエトキシ）フェニル〕プロパン－１－オン、１－ヒドロキシシクロヘキシルフェニルケトン、２－ヒドロキシ－２－メチル－１－（４－イソプロペニルフェニル）プロパン－１－オンのオリゴマー、α，α－ジエトキシアセトフェノン、ベンジルジメチルケタール等が挙げられる。イルガキュア（登録商標）３６９、９０７、３７９（以上、ＢＡＳＦ社製）等の市販品を用いてもよい。
　前記トリアジン化合物としては、例えば、２，４－ビス（トリクロロメチル）－６－（４－メトキシフェニル）－１，３，５－トリアジン、２，４－ビス（トリクロロメチル）－６－（４－メトキシナフチル）－１，３，５－トリアジン、２，４－ビス（トリクロロメチル）－６－ピペロニル－１，３，５－トリアジン、２，４－ビス（トリクロロメチル）－６－(４－メトキシスチリル)－１，３，５－トリアジン、２，４－ビス（トリクロロメチル）－６－〔２－（５－メチルフラン－２－イル）エテニル〕－１，３，５－トリアジン、２，４－ビス（トリクロロメチル）－６－〔２－（フラン－２－イル）エテニル〕－１，３，５－トリアジン、２，４－ビス（トリクロロメチル）－６－〔２－（４－ジエチルアミノ－２－メチルフェニル）エテニル〕－１，３，５－トリアジン、２，４－ビス（トリクロロメチル）－６－〔２－（３，４－ジメトキシフェニル）エテニル〕－１，３，５－トリアジン等が挙げられる。
　前記アシルホスフィンオキサイド化合物としては、２，４，６－トリメチルベンゾイルジフェニルホスフィンオキサイド等が挙げられる。イルガキュア（登録商標）８１９（ＢＡＳＦ社製）等の市販品を用いてもよい。
　前記ビイミダゾール化合物としては、例えば、２，２’－ビス（２－クロロフェニル）－４，４’，５，５’－テトラフェニルビイミダゾール、２，２’－ビス（２，３－ジクロロフェニル）－４，４’，５，５’－テトラフェニルビイミダゾール（例えば、特開平６－７５３７２号公報、特開平６－７５３７３号公報等参照。）、２，２’－ビス（２－クロロフェニル）－４，４’，５，５’－テトラフェニルビイミダゾール、２，２’－ビス（２－クロロフェニル）－４，４’，５，５’－テトラ（アルコキシフェニル）ビイミダゾール、２，２’－ビス（２－クロロフェニル）－４，４’，５，５’－テトラ（ジアルコキシフェニル）ビイミダゾール、２，２’－ビス（２－クロロフェニル）－４，４’，５，５’－テトラ（トリアルコキシフェニル）ビイミダゾール（例えば、特公昭４８－３８４０３号公報、特開昭６２－１７４２０４号公報等参照。）、４，４’，５，５’－位のフェニル基がカルボアルコキシ基により置換されているビイミダゾール化合物（例えば、特開平７－１０９１３号公報等参照）等が挙げられる。
　酸を発生する重合開始剤としては、例えば、４－ヒドロキシフェニルジメチルスルホニウムｐ－トルエンスルホナート、４－ヒドロキシフェニルジメチルスルホニウムヘキサフルオロアンチモネート、４－アセトキシフェニルジメチルスルホニウムｐ－トルエンスルホナート、４－アセトキシフェニル・メチル・ベンジルスルホニウムヘキサフルオロアンチモネート、トリフェニルスルホニウムｐ－トルエンスルホナート、トリフェニルスルホニウムヘキサフルオロアンチモネート、ジフェニルヨードニウムｐ－トルエンスルホナート、ジフェニルヨードニウムヘキサフルオロアンチモネート等のオニウム塩類や、ニトロベンジルトシレート類、ベンゾイントシレート類等が挙げられる。
　さらに重合開始剤（Ｄ）としては、ベンゾイン、ベンゾインメチルエーテル、ベンゾインエチルエーテル、ベンゾインイソプロピルエーテル、ベンゾインイソブチルエーテル等のベンゾイン化合物；ベンゾフェノン、ｏ－ベンゾイル安息香酸メチル、４－フェニルベンゾフェノン、４－ベンゾイル－４’－メチルジフェニルサルファイド、３，３’，４，４’－テトラ（ｔｅｒｔ－ブチルパーオキシカルボニル）ベンゾフェノン、２，４，６－トリメチルベンゾフェノン等のベンゾフェノン化合物；９，１０－フェナンスレンキノン、２－エチルアントラキノン、カンファーキノン等のキノン化合物；１０－ブチル－２－クロロアクリドン、ベンジル、フェニルグリオキシル酸メチル、チタノセン化合物等が挙げられる。
　重合開始剤（Ｄ）としては、Ｏ－アシルオキシム化合物、アルキルフェノン化合物、トリアジン化合物、アシルホスフィンオキサイド化合物及びビイミダゾール化合物からなる群から選ばれる少なくとも１種を含む重合開始剤が好ましく、Ｏ－アシルオキシム化合物を含む重合開始剤がより好ましい。
　重合開始剤（Ｄ）の含有量は、樹脂（Ｂ）及び重合性化合物（Ｃ）の合計量１００質量部に対して、好ましくは０．１～３０質量部であり、より好ましくは１～２０質量部である。重合開始剤（Ｄ）の含有量が、前記の範囲内にあると、高感度化して露光時間が短縮される傾向があるためカラーフィルタの生産性が向上する。
＜溶剤（Ｅ）＞
　溶剤（Ｅ）は、特に限定されず、当該分野で通常使用される溶剤を用いることができる。例えば、エステル溶剤（分子内に－ＣＯＯ－を含み、－Ｏ－を含まない溶剤）、エーテル溶剤（分子内に－Ｏ－を含み、－ＣＯＯ－を含まない溶剤）、エーテルエステル溶剤（分子内に－ＣＯＯ－と－Ｏ－とを含む溶剤）、ケトン溶剤（分子内に－ＣＯ－を含み、－ＣＯＯ－を含まない溶剤）、アルコール溶剤（分子内にＯＨを含み、－Ｏ－、－ＣＯ－及び－ＣＯＯ－を含まない溶剤）、芳香族炭化水素溶剤、アミド溶剤、ジメチルスルホキシドが挙げられる。
　エステル溶剤としては、乳酸メチル、乳酸エチル、乳酸ブチル、２－ヒドロキシイソブタン酸メチル、酢酸エチル、酢酸ｎ－ブチル、酢酸イソブチル、ギ酸ペンチル、酢酸イソペンチル、プロピオン酸ブチル、酪酸イソプロピル、酪酸エチル、酪酸ブチル、ピルビン酸メチル、ピルビン酸エチル、ピルビン酸プロピル、アセト酢酸メチル、アセト酢酸エチル、シクロヘキサノールアセテート及びγ－ブチロラクトンなどが挙げられる。
　エーテル溶剤としては、エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、エチレングリコールモノプロピルエーテル、エチレングリコールモノブチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノブチルエーテル、プロピレングリコールモノメチルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノプロピルエーテル、プロピレングリコールモノブチルエーテル、３－メトキシ－１－ブタノール、３－メトキシ－３－メチルブタノール、テトラヒドロフラン、テトラヒドロピラン、１，４－ジオキサン、ジエチレングリコールジメチルエーテル、ジエチレングリコールジエチルエーテル、ジエチレングリコールメチルエチルエーテル、ジエチレングリコールジプロピルエーテル、ジエチレングリコールジブチルエーテル、アニソール、フェネトール及びメチルアニソールなどが挙げられる。
　エーテルエステル溶剤としては、メトキシ酢酸メチル、メトキシ酢酸エチル、メトキシ酢酸ブチル、エトキシ酢酸メチル、エトキシ酢酸エチル、３－メトキシプロピオン酸メチル、３－メトキシプロピオン酸エチル、３－エトキシプロピオン酸メチル、３－エトキシプロピオン酸エチル、２－メトキシプロピオン酸メチル、２－メトキシプロピオン酸エチル、２－メトキシプロピオン酸プロピル、２－エトキシプロピオン酸メチル、２－エトキシプロピオン酸エチル、２－メトキシ－２－メチルプロピオン酸メチル、２－エトキシ－２－メチルプロピオン酸エチル、３－メトキシブチルアセテート、３－メチル－３－メトキシブチルアセテート、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート、プロピレングリコールモノプロピルエーテルアセテート、エチレングリコールモノメチルエーテルアセテート、エチレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノエチルエーテルアセテート及びジエチレングリコールモノブチルエーテルアセテートなどが挙げられる。
　ケトン溶剤としては、４－ヒドロキシ－４－メチル－２－ペンタノン、アセトン、２－ブタノン、２－ヘプタノン、３－ヘプタノン、４－ヘプタノン、４－メチル－２－ペンタノン、シクロペンタノン、シクロヘキサノン及びイソホロンなどが挙げられる。
　アルコール溶剤としては、メタノール、エタノール、プロパノール、ブタノール、ヘキサノール、シクロヘキサノール、エチレングリコール、プロピレングリコール及びグリセリンなどが挙げられる。
　芳香族炭化水素溶剤としては、ベンゼン、トルエン、キシレン及びメシチレンなどが挙げられる。
　アミド溶剤としては、Ｎ，Ｎ－ジメチルホルムアミド、Ｎ，Ｎ－ジメチルアセトアミド及びＮ－メチルピロリドンなどが挙げられる。
　上記の溶剤のうち、塗布性、乾燥性の点から、１ａｔｍにおける沸点が１２０℃以上１８０℃以下である有機溶剤が好ましい。溶剤としては、プロピレングリコールモノメチルエーテルアセテート、乳酸エチル、プロピレングリコールモノメチルエーテル、３－エトキシプロピオン酸エチル、エチレングリコールモノメチルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノエチルエーテル、４－ヒドロキシ－４－メチル－２－ペンタノン及びＮ，Ｎ－ジメチルホルムアミドが好ましく、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノメチルエーテル、４－ヒドロキシ－４－メチル－２－ペンタノン、乳酸エチル及び３－エトキシプロピオン酸エチルがより好ましい。
　溶剤（Ｅ）の含有率は、本発明の着色硬化性樹脂組成物の総量に対して、好ましくは７０～９５質量％であり、より好ましくは７５～９２質量％である。言い換えると、着色硬化性樹脂組成物の固形分の総含有率は、好ましくは５～３０質量％、より好ましくは８～２５質量％である。溶剤（Ｅ）の含有率が前記の範囲内にあると、塗布時の平坦性が良好になり、またカラーフィルタを形成した際に色濃度が不足しないために表示特性が良好となる傾向がある。
＜レベリング剤（Ｆ）＞
　レベリング剤（Ｆ）としては、シリコーン系界面活性剤、フッ素系界面活性剤及びフッ素原子を有するシリコーン系界面活性剤等が挙げられる。これらは、側鎖に重合性基を有していてもよい。
　シリコーン系界面活性剤としては、分子内にシロキサン結合を有する界面活性剤等が挙げられる。具体的には、トーレシリコーンＤＣ３ＰＡ、同ＳＨ７ＰＡ、同ＤＣ１１ＰＡ、同ＳＨ２１ＰＡ、同ＳＨ２８ＰＡ、同ＳＨ２９ＰＡ、同ＳＨ３０ＰＡ、同ＳＨ８４００（東レ・ダウコーニング（株）製）、ＫＰ３２１、ＫＰ３２２、ＫＰ３２３、ＫＰ３２４、ＫＰ３２６、ＫＰ３４０、ＫＰ３４１（信越化学工業（株）製）、ＴＳＦ４００、ＴＳＦ４０１、ＴＳＦ４１０、ＴＳＦ４３００、ＴＳＦ４４４０、ＴＳＦ４４４５、ＴＳＦ４４４６、ＴＳＦ４４５２及びＴＳＦ４４６０（モメンティブ・パフォーマンス・マテリアルズ・ジャパン合同会社製）等が挙げられる。
　前記のフッ素系界面活性剤としては、分子内にフルオロカーボン鎖を有する界面活性剤等が挙げられる。具体的には、フロラード（登録商標）ＦＣ４３０、同ＦＣ４３１（住友スリーエム（株）製）、メガファック（登録商標）Ｆ１４２Ｄ、同Ｆ１７１、同Ｆ１７２、同Ｆ１７３、同Ｆ１７７、同Ｆ１８３、同Ｆ５５４、同Ｒ３０、同ＲＳ－７１８－Ｋ（ＤＩＣ（株）製）、エフトップ（登録商標）ＥＦ３０１、同ＥＦ３０３、同ＥＦ３５１、同ＥＦ３５２（三菱マテリアル電子化成（株）製）、サーフロン（登録商標）Ｓ３８１、同Ｓ３８２、同ＳＣ１０１、同ＳＣ１０５（旭硝子（株）製）及びＥ５８４４（（株）ダイキンファインケミカル研究所製）等が挙げられる。
　前記のフッ素原子を有するシリコーン系界面活性剤としては、分子内にシロキサン結合及びフルオロカーボン鎖を有する界面活性剤等が挙げられる。具体的には、メガファック（登録商標）Ｒ０８、同ＢＬ２０、同Ｆ４７５、同Ｆ４７７及び同Ｆ４４３（ＤＩＣ（株）製）等が挙げられる。
　レベリング剤（Ｆ）の含有率は、着色硬化性樹脂組成物の総量に対して、好ましくは０．００１質量％以上０.２質量％以下であり、より好ましくは０.００２質量％以上０．２質量％以下、さらに好ましくは０.００５質量％以上０．２質量％以下である。尚、この含有率に、前記分散剤の含有率は含まれない。レベリング剤（Ｆ）の含有率が前記の範囲内にあると、カラーフィルタの平坦性を良好にすることができる。
　＜その他の成分＞
　本発明の着色硬化性樹脂組成物は、必要に応じて、重合開始助剤、充填剤、他の高分子化合物、密着促進剤、光安定剤、連鎖移動剤等、当該技術分野で公知の添加剤を含んでもよい。
　密着促進剤としては、ビニルトリメトキシシラン、ビニルトリエトキシシラン、ビニルトリス（２－メトキシエトキシ）シラン、３－グリシジルオキシプロピルトリメトキシシラン、３－グリシジルオキシプロピルメチルジメトキシシラン、３－グリシジルオキシプロピルメチルジエトキシシラン、２－（３，４－エポキシシクロヘキシル）エチルトリメトキシシラン、３－クロロプロピルメチルジメトキシシラン、３－クロロプロピルトリメトキシシラン、３－メタクリロイルオキシプロピルトリメトキシシラン、３－スルファニルプロピルトリメトキシシラン、３－イソシアナトプロピルトリエトキシシラン、Ｎ－２－（アミノエチル）－３－アミノプロピルメチルジメトキシシラン、Ｎ－２－（アミノエチル）－３－アミノプロピルメチルジエトキシシラン、Ｎ－２－（アミノエチル）－３－アミノプロピルトリメトキシシラン、３－アミノプロピルトリメトキシシラン、３－アミノプロピルトリエトキシシラン、Ｎ－フェニル－３－アミノプロピルトリメトキシシラン及びＮ－フェニル－３－アミノプロピルトリエトキシシラン等が挙げられる。
＜着色硬化性樹脂組成物の製造方法＞
　本発明の着色硬化性樹脂組成物は、例えば、着色剤（Ａ）、樹脂（Ｂ）、重合性化合物（Ｃ）、及び重合開始剤（Ｄ）並びに必要に応じて用いられる溶剤（Ｅ）、レベリング剤（Ｆ）及びその他の成分を混合することにより調製できる。
＜カラーフィルタの製造方法＞
　本発明の着色硬化性樹脂組成物から着色パターンを製造する方法としては、フォトリソグラフ法、インクジェット法、印刷法等が挙げられる。中でも、フォトリソグラフ法が好ましい。フォトリソグラフ法は、前記着色硬化性樹脂組成物を基板に塗布し、乾燥させて着色組成物層を形成し、フォトマスクを介して該着色組成物層を露光して、現像する方法である。フォトリソグラフ法において、露光の際にフォトマスクを用いないこと、及び／又は現像しないことにより、上記着色組成物層の硬化物である着色塗膜を形成することができる。このように形成した着色パターンや着色塗膜が本発明のカラーフィルタである。
　作製するカラーフィルタの膜厚は、特に限定されず、目的や用途等に応じて適宜調整することができ、例えば、０．１～３０μｍ、好ましくは０．１～２０μｍ、さらに好ましくは０．５～６μｍである。
　基板としては、石英ガラス、ホウケイ酸ガラス、アルミナケイ酸塩ガラス、表面をシリカコートしたソーダライムガラスなどのガラス板や、ポリカーボネート、ポリメタクリル酸メチル、ポリエチレンテレフタレートなどの樹脂板、シリコン、前記基板上にアルミニウム、銀、銀／銅／パラジウム合金薄膜などを形成したものが用いられる。これらの基板上には、別のカラーフィルタ層、樹脂層、トランジスタ、回路等が形成されていてもよい。
　フォトリソグラフ法による各色画素の形成は、公知又は慣用の装置や条件で行うことができる。例えば、下記のようにして作製することができる。
　まず、着色硬化性樹脂組成物を基板上に塗布し、加熱乾燥（プリベーク）及び／又は減圧乾燥することにより溶剤等の揮発成分を除去して乾燥させ、平滑な着色組成物層を得る。
　塗布方法としては、スピンコート法、スリットコート法、スリット　アンド　スピンコート法等が挙げられる。
　加熱乾燥を行う場合の温度は、３０～１２０℃が好ましく、５０～１１０℃がより好ましい。また加熱時間としては、１０秒間～６０分間であることが好ましく、３０秒間～３０分間であることがより好ましい。
　減圧乾燥を行う場合は、５０～１５０Ｐａの圧力下、２０～２５℃の温度範囲で行うことが好ましい。
　着色組成物層の膜厚は、特に限定されず、目的とするカラーフィルタの膜厚に応じて適宜選択すればよい。
　次に、着色組成物層は、目的の着色パターンを形成するためのフォトマスクを介して露光される。該フォトマスク上のパターンは特に限定されず、目的とする用途に応じたパターンが用いられる。
　露光に用いられる光源としては、２５０～４５０ｎｍの波長の光を発生する光源が好ましい。例えば、３５０ｎｍ未満の光を、この波長域をカットするフィルタを用いてカットしたり、４３６ｎｍ付近、４０８ｎｍ付近、３６５ｎｍ付近の光を、これらの波長域を取り出すバンドパスフィルタを用いて選択的に取り出したりしてもよい。具体的には、水銀灯、発光ダイオード、メタルハライドランプ、ハロゲンランプ等が挙げられる。
　露光面全体に均一に平行光線を照射したり、フォトマスクと着色組成物層が形成された基板との正確な位置合わせを行うことができるため、マスクアライナ及びステッパ等の露光装置を使用することが好ましい。
　露光後の着色組成物層を現像液に接触させて現像することにより、基板上に着色パターンが形成される。現像により、着色組成物層の未露光部が現像液に溶解して除去される。
現像液としては、例えば、水酸化カリウム、炭酸水素ナトリウム、炭酸ナトリウム、水酸化テトラメチルアンモニウム等のアルカリ性化合物の水溶液が好ましい。これらのアルカリ性化合物の水溶液中の濃度は、好ましくは０．０１～１０質量％であり、より好ましくは０．０３～５質量％である。さらに、現像液は、界面活性剤を含んでいてもよい。
　現像方法は、パドル法、ディッピング法及びスプレー法等のいずれでもよい。さらに現像時に基板を任意の角度に傾けてもよい。
　現像後は、水洗することが好ましい。
　さらに、得られた着色パターンに、ポストベークを行うことが好ましい。ポストベーク温度は、１５０～２５０℃が好ましく、１６０～２３５℃がより好ましい。ポストベーク時間は、１～１２０分間が好ましく、１０～６０分間がより好ましい。
　以下、実施例によって本発明をより詳細に説明するが、本発明はこれらの実施例によって限定されるものではない。例中、含有量ないし使用量を表す％及び部は、特に断らな
い限り質量基準である。
　以下の合成例において、化合物は、ＮＭＲ（JNM-EX-270；（日本電子(株)製））で同定した。
（着色剤合成例１）
　２，４－ジメチルアニリン（東京化成工業（株）製）１０．０部、２－エチルヘキサンブロミド（東京化成工業（株）製）１７．０部、及びテトラブチルアンモニウムブロミ
ド（和光化学工業（株）製）４４．０部を混合した。得られた混合物を、９０℃で８時間撹拌した。反応終了後、５０部の１０％重曹水を加えた後、酢酸エチル１００部を加えて水層を廃棄した。水、１０％塩酸で洗う操作を２回繰り返した後、溶剤を溜去した。得られたオイルを６０℃で２４時間減圧乾燥し、下記式（ａ－１）で表される化合物９．３部を得た。
Figure JPOXMLDOC01-appb-C000019
　式（ａ－１）で示される化合物の1Ｈ－ＮＭＲ（２７０ＭＨｚ、δ値（ｐｐｍ、ＴＭＳ基準）、ＤＭＳＯ－ｄ６）
δ　０．８５（ｍ，６Ｈ）、１．２３－１．４２（ｂｒ，８Ｈ）、１．５９（ｂｒ，１Ｈ）、２．０４（ｓ，３Ｈ）、２．１２（ｓ，３Ｈ）、２．９１（ｄ，２Ｈ）、４．３７（ｂｒ，１Ｈ）、６．３８（ｄ，１Ｈ）、６．７５（ｓ，１Ｈ）、６．７７（ｄ，１Ｈ）
　上記で得られた式（ａ－１）で表される化合物３．０部、３－ブロモフェノール（東京化成工業（株）製）２．２部、酢酸パラジウム０．０１５部、ｔｅｒｔ－ブトキシナトリウム（東京化成工業（株）製）３．２部、トリｔｅｒｔ－ブチルホスフィン（東京化成工業（株）製）０．０５５部、及びトルエン２５．６部を混合し、１００℃で１５時間撹
拌した。得られた混合物に、酢酸エチル３０部、水１００部を加えて水層を廃棄した。水で洗う操作を２回繰り返した後、溶剤を溜去した。残渣をシリカゲルクロマトグラフィー（クロロホルム／ヘキサン＝１／１）で精製し、得られたオイルを６０℃で２４時間減圧乾燥し、下記式（ａ－２）で表される化合物で示される化合物１．９部を得た。
Figure JPOXMLDOC01-appb-C000020
　式（ａ－２）で示される化合物の1Ｈ－ＮＭＲ（２７０ＭＨｚ、δ値（ｐｐｍ、ＴＭＳ基準）、ＤＭＳＯ－ｄ６）
δ　０．８５（ｍ，６Ｈ）、１．２３－１．４２（ｂｒ，８Ｈ）、１．５５（ｂｒ，１Ｈ）、１．９４（ｓ，３Ｈ）、２．２７（ｓ，３Ｈ）、２．９０（ｄ，２Ｈ）、６．３７（ｄ，１Ｈ）、６．７５（ｓ，１Ｈ）、６．７６（ｄ，１Ｈ）、６．９２－７．１４（ｍ，４Ｈ）、８．９３（ｓ，１Ｈ）
　上記で得られた式（ａ－２）で示される化合物４．４部、３，４－ジヒドロキシ－３－シクロブテン－１，２－ジオン（東京化成工業（株）製）０．８部、１－ブタノール９０．０部及びトルエン６０．０部を混合した。得られた混合物を、Ｄｅａｎ－Ｓｔａｒｋ
管を用いて生成した水を除きながら１２５℃で３時間撹拌した。反応終了後、溶剤を溜去し、酢酸を１５部加えた後、１８％食塩水１００部に滴下し、析出した固体を濾取した。
濾取した固体をヘキサンで洗浄した。得られた固体を６０℃で２４時間減圧乾燥し、式（ＡＩＩ－１０）で示される化合物４．９部を得た。
Figure JPOXMLDOC01-appb-C000021
　式（ＡＩＩ－１０）で示される化合物の1Ｈ－ＮＭＲ（２７０ＭＨｚ、δ値（ｐｐｍ、ＴＭＳ基準）、ＤＭＳＯ－ｄ６）
δ　０．８７（ｍ，１２Ｈ）、１．２１－１．５７（ｍ，１６Ｈ）、１．７２（ｂｒ，２Ｈ）、２．０５（ｓ，６Ｈ）、２．３６（ｓ，６Ｈ）、３．３７（ｂｒ，２Ｈ）、３．７８（ｂｒ，２Ｈ）、６．００（ｂｒ，４Ｈ）、６．９７－７．１２（ｍ，６Ｈ）、７．７７－７．９５（ｍ，２Ｈ）、１１．３５（ｓ，１Ｈ）、１２．０６（ｓ，１Ｈ）
　以下において、化合物の構造は質量分析（ＬＣ；Ａｇｉｌｅｎｔ製１２００型、ＭＡＳＳ；Ａｇｉｌｅｎｔ製ＬＣ／ＭＳＤ型）で確認した。
（着色剤合成例２）
　ｍ－ブロモフェノール（東京化成工業（株）製）５０部及びイミダゾール（東京化成工業（株）製）３０部をジクロロメタン（関東化学（株）製）５００部に溶解させ０℃に冷却後、ｔｅｒｔ－ブチルジメチルクロロシラン（東京化成工業（株）製）４８部を滴下した。滴下終了後２３℃へ昇温し１６時間撹拌した。反応終了後水を加えて有機層を抽出し、溶剤を濃縮後シリカゲルカラムクロマトグラフィーで分離精製を行い、式（ａ－３）で表される化合物を７４部得た。
同定：（質量分析）イオン化モード＝ＥＳＩ＋：m/z=[M+H]+ ２８７．０
Ｅｘａｃｔ　Ｍａｓｓ：＋２８６．０
Figure JPOXMLDOC01-appb-C000022
　２，４－ジメチルアニリン（東京化成工業（株）製）１５部、式（ａ－３）で表される化合物３５部、水酸化カリウム（和光純薬工業（株）製）１４部、テトラブチルアンモニウムブロミド（東京化成工業（株）製）２部及びビス（トリ－ｔｅｒｔ－ブチルホスフィン）パラジウム（０）（アルドリッチ（株）製）０．６部をトルエン（関東化学（株）製）２５０部及び水１５部に溶解させ、９０℃に加熱して３０分撹拌した。反応終了後有機層を抽出して濃縮し、シリカゲルカラムクロマトグラフィーで分離精製を行い式（ａ－４）で表される化合物を１４部得た。
同定：（質量分析）イオン化モード＝ＥＳＩ＋：m/z=[M+H]+ ３２８．３
Ｅｘａｃｔ　Ｍａｓｓ：＋３２７．２
Figure JPOXMLDOC01-appb-C000023
　式（ａ－４）で表される化合物１４部及び４－クロロ－４－オキソ酪酸メチル１０部（東京化成工業（株）製）をトルエン（関東化学（株）製）２５５部に溶解させ、９０℃に昇温して１時間撹拌した。反応終了後、水を加えて有機層を抽出し、溶剤を濃縮後シリカゲルクロマトグラフィーで分離精製を行い、式（ａ－５）で表される化合物を１５部得た。
同定：（質量分析）イオン化モード＝ＥＳＩ＋：m/z=[M+H]+ ４４２．３
Ｅｘａｃｔ　Ｍａｓｓ：＋４４１．２
Figure JPOXMLDOC01-appb-C000024
　式（ａ－５）で表される化合物１５部をテトラヒドロフラン（関東化学（株）製）１５０部に溶解させ、０℃に冷却後にフッ化テトラ－ｎ－ブチルアンモニウム１Ｍテトラヒドロフラン溶液（東京化成工業（株）製）１５部を滴下した。滴下終了後２３℃に昇温し、２時間撹拌した。反応終了後、溶剤を濃縮し、シリカゲルカラムクロマトグラフィーで分離精製を行い、式（ａ－６）で表される化合物を１２部得た。
同定：（質量分析）イオン化モード＝ＥＳＩ＋：m/z=[M+H]+ ３２８．２
Ｅｘａｃｔ　Ｍａｓｓ：＋３２７．２
Figure JPOXMLDOC01-appb-C000025
　式（ａ－６）で表される化合物１２部をテトラヒドロフラン（関東化学（株）製）２４０部に溶解させ０℃に冷却後、ボラン－１Ｍテトラヒドロフラン溶液（関東化学（株）製）１８０部を滴下した。滴下終了後３０分撹拌し、水を加えたのちテトラヒドロフランを濃縮し、酢酸エチルで有機層を抽出した。溶剤を濃縮後シリカゲルカラムクロマトグラフィーで分離精製を行い、式（ａ－７）で表される化合物を６部得た。
同定：（質量分析）イオン化モード＝ＥＳＩ＋：m/z=[M+H]+ ３１４．２
Ｅｘａｃｔ　Ｍａｓｓ：＋３１３．２
Figure JPOXMLDOC01-appb-C000026
　式（ａ－７）で表される化合物６部及び水酸化リチウムー水和物（和光純薬工業（株））０．２部をメタノール（関東化学（株）製）２０部、テトラヒドロフラン（関東化学（株）製）２０部、水１０部に溶解させ、２３℃で１時間撹拌した。反応終了後、有機溶剤を濃縮し、酢酸エチルで有機層を抽出し、シリカゲルカラムクロマトグラフィーで分離精製を行って式（ａ－８）で表される化合物を４部得た。
同定：（質量分析）イオン化モード＝ＥＳＩ＋：m/z=[M+H]+ ３００．２
Ｅｘａｃｔ　Ｍａｓｓ：＋２９９．２
Figure JPOXMLDOC01-appb-C000027
　式（ａ－８）で表される化合物４部及び３，４－ジヒドロキシ－３－シクロブテン－１，２－ジオン（和光純薬工業（株）製）０．８部をトルエン（関東化学（株）製）４０部、ｎ－ブタノール（関東化学（株）製）１０部に溶解させ、１４０℃に昇温し、２時間撹拌した。溶剤を濃縮後、シリカゲルカラムクロマトグラフィーで分離精製を行い、式（ＡＩＩ－１７）で表される化合物を１．６部得た。
同定：（質量分析）イオン化モード＝ＥＳＩ＋：m/z=[M+H]+ ６７７．３
Ｅｘａｃｔ　Ｍａｓｓ：＋６７６．３
Figure JPOXMLDOC01-appb-C000028
（着色剤合成例３）
　３－ブロモアニソール（東京化成工業（株）製）５０部を２，４，６－トリメチルアニリン（東京化成工業（株）製）３６．１部とトルエン（関東化学（株）製）４３４部に溶解させ、この溶液に水酸化カリウム（関東化学（株）製）３０部、水２５部、テトラブチルアンモニウムブロミド（東京化成工業（株）製）２部、ビス(トリ－ｔｅｒｔ－ブチルホスフィン)パラジウム（０）（東京化成工業（株）製）１．４部を混合した。９０℃に昇温して５時間撹拌した後、有機層を抽出により取得し、溶剤を留去し粗生成物を５２．１部得た。得られた粗生成物をカラムクロマトグラフィーで分離精製を行って式（ａ－９）で表される化合物を５０．２部得た。
同定：（質量分析）イオン化モード＝ＥＳＩ＋：m/z=[M+H]+ ２４２．３
Ｅｘａｃｔ　Ｍａｓｓ：＋２４１．２
Figure JPOXMLDOC01-appb-C000029
　式（ａ－９）で表される化合物３３部、４－クロロ－４－オキソ酪酸メチル（東京化成工業（株）製）２６．８部及びトルエン（関東化学（株）製）２８６部を混合し、１００℃で１６時間撹拌しながら加熱した。反応終了後溶剤を留去し、得られた粗生成物をカラムクロマトグラフィーで分離精製を行って式（ａ－１０）で表される化合物を３０．７部得た。
同定：（質量分析）イオン化モード＝ＥＳＩ＋：m/z=[M+H]+ ３５６．２
Ｅｘａｃｔ　Ｍａｓｓ：＋３５５．２
Figure JPOXMLDOC01-appb-C000030
　式（ａ－１０）で表される化合物１０部を塩化メチレン（関東化学（株）製）９５部に溶解させ撹拌しながら０℃に冷却した。撹拌しながら三臭化ホウ素（富士フイルム和光純薬（株）製）２８．２部を滴下投入した。滴下終了後、徐々に昇温し１０℃で４時間撹拌した。反応終了後溶剤を減圧留去し、水－有機溶剤抽出操作を施し、溶剤を留去して９．１部の粗生成物を得た。この中に式（ａ－１１）で表される化合物が４８％、式（ａ－１２）で表される化合物が３６％含まれていた。
Figure JPOXMLDOC01-appb-C000031
 同定：（質量分析）イオン化モード＝ＥＳＩ＋：m/z=[M+H]+ ３４２．２
Ｅｘａｃｔ　Ｍａｓｓ：＋３４１．２
Figure JPOXMLDOC01-appb-C000032
 同定：（質量分析）イオン化モード＝ＥＳＩ＋：m/z=[M+H]+ ３２８．１
Ｅｘａｃｔ　Ｍａｓｓ：＋３２７．２
　チオニルクロライド（東京化成工業（株）製）１３．２部を７２部のメタノール（関東化学（株）製）に溶かした溶液を０℃に冷却し撹拌しながら、上記で得られた式（ａ－１１）で表される化合物と式（ａ－１２）で表される化合物とを含む粗生成物９．１部を投入した。室温まで昇温し１６時間反応させた。溶剤を減圧留去し、式（ａ－１１）で表される化合物を含む８．３部の粗生成物を得た。得られた粗生成物をシリカゲルカラムクロマトグラフィーで精製し、式（ａ－１１）で表される化合物を７．４部得た。
同定：（質量分析）イオン化モード＝ＥＳＩ＋：m/z=[M+H]+ ３４２．２
Ｅｘａｃｔ　Ｍａｓｓ：＋３４１．２
　式（ａ－１１）で表される化合物２部、ボラン１Ｍテトラヒドロフラン溶液（関東化学（株）製）２６．３部、テトラヒドロフラン（関東化学（株）製）１８部を０℃で混合し１０℃まで昇温し５時間撹拌した。反応終了後、水を加えてクエンチし、有機溶剤で抽出した。溶剤を留去して得られた粗生成物をシリカゲルカラムクロマトグラフィーで精製し、式（ａ－１３）で表される化合物を１．６４部得た。
同定：（質量分析）イオン化モード＝ＥＳＩ＋：m/z=[M+H]+ ３００．２
Ｅｘａｃｔ　Ｍａｓｓ：＋２９９．２
Figure JPOXMLDOC01-appb-C000033
　式（ａ－１３）で表される化合物２．５部及び３，４－ジヒドロキシ－３－シクロブテン－１，２－ジオン（富士フイルム和光純薬（株）製）０．５５部をトルエン（関東化学（株）製）５０部、ｎ－ブタノール（関東化学（株）製）５０部に溶解させ、１１０℃で６時間撹拌しながら加熱した。反応終了後、溶剤を留去し得られた粗生成物をシリカゲルカラムクロマトグラフィーで分離精製を行い、式（ＡＩＩ－１８）で表される化合物を２．７部得た。
同定：（質量分析）イオン化モード＝ＥＳＩ＋：m/z=[M+H]+ ６７７．４
Ｅｘａｃｔ　Ｍａｓｓ：＋６７６．４
Figure JPOXMLDOC01-appb-C000034
（樹脂合成例１）
　還流冷却器、滴下ロート及び撹拌機を備えたフラスコ内に窒素を適量流して窒素雰囲気に置換し、乳酸エチル２８８部を入れ、撹拌しながら８５℃まで加熱した。次いで、該フラスコ内に、３，４－エポキシトリシクロ［５．２．１．０2,6］デカン－８－イルアクリレート及び３，４－エポキシトリシクロ［５．２．１．０2,6］デカン－９－イルアク
リレートの混合物（混合割合は１：１）２０８部、アクリル酸４２部、乳酸エチル２００部の混合溶液を滴下ポンプを用いて５時間かけて滴下した。
　一方、重合開始剤２，２’－アゾビス（２，４－ジメチルバレロニトリル）８部を乳酸エチル２５４部に溶解した混合溶液を別の滴下ポンプを用いて５時間かけてフラスコ内に滴下した。重合開始剤の滴下が終了した後、３時間同温度で保持した後、室温まで冷却して、Ｂ型粘度（２３℃）４４ｍＰａｓ、固形分２６．２％の共重合体（樹脂（Ｂ－１））の溶液を得た。生成した共重合体の重量平均分子量（Ｍｗ）は１０３００、固形分換算の酸価は１３４ｍｇ－ＫＯＨ／ｇ、分散度２．２７であった。樹脂（Ｂ－１）は下記構造単位を有する。
Figure JPOXMLDOC01-appb-C000035
　樹脂のポリスチレン換算の重量平均分子量（Ｍｗ）及び数平均分子量（Ｍｎ）の測定は、ＧＰＣ法により以下の条件で行った。
　　　装置　　　　　　；HLC-8120GPC（東ソー（株）製）
　　　カラム　　　　　；TSK-GELG2000HXL
　　　カラム温度　　　；40℃
　　　溶剤　　　　　　；THF
　　　流速　　　　　　；1.0mL/min
　　　被検液固形分濃度；0.001～0.01質量％
　　　注入量　　　　　；50μL
　　　検出器　　　　　；RI
　　　校正用標準物質　；TSK STANDARD POLYSTYRENE 
　　　　　　　　　　F-40、F-4、F-288、A-2500、A-500（東ソー（株）製）
　上記で得られたポリスチレン換算の重量平均分子量及び数平均分子量の比（Ｍｗ／Ｍｎ）を分散度とした。
（樹脂合成例２）
　還流冷却器、滴下ロート及び撹拌機を備えたフラスコ内に窒素を適量流して窒素雰囲気に置換し、プロピレングリコールモノメチルエーテルアセテート３２４部を入れ、撹拌しながら８０℃まで加熱した。次いで、該フラスコ内に、３，４－エポキシトリシクロ［５．２．１．０2,6］デカン－８－イルアクリレート及び３，４－エポキシトリシクロ［５．２．１．０2,6］デカン－９－イルアクリレートの混合物（混合割合は１：１）１３５
部、アクリル酸４５部、フェニルメタクリレート１２０部、並びにプロピレングリコールモノメチルエーテル２０３部の混合溶液を滴下ポンプを用いて５時間かけて滴下した。
　一方、重合開始剤２，２’－アゾビス（２，４－ジメチルバレロニトリル）１８部をプロピレングリコールモノメチルエーテルアセテート１５５部に溶解した混合溶液を別の滴下ポンプを用いて５時間かけてフラスコ内に滴下した。重合開始剤の滴下が終了した後、３時間同温度で保持した後、室温まで冷却して、Ｂ型粘度（２３℃）１４１ｍＰａｓ、固形分３１．６％の共重合体（樹脂（Ｂ－２））の溶液を得た。生成した共重合体の重量平均分子量（Ｍｗ）は１７３００、固形分換算の酸価は１１２ｍｇ－ＫＯＨ／ｇ、分散度２．４４であった。樹脂（Ｂ－２）は下記構造単位を有する。
Figure JPOXMLDOC01-appb-C000036
（樹脂合成例３）
　還流冷却器、滴下ロート及び撹拌機を備えたフラスコ内に窒素を適量流して窒素雰囲気に置換し、プロピレングリコールモノメチルエーテルアセテート２５０部、及びプロピレングリコールモノメチルエーテル１００部を入れ、撹拌しながら８０℃まで加熱した。次いで、該フラスコ内に、３，４－エポキシトリシクロ［５．２．１．０2,6］デカン－８－イルアクリレート及び３，４－エポキシトリシクロ［５．２．１．０2,6］デカン－９
－イルアクリレートの混合物（混合割合は１：１）２２５部、アクリル酸７５部、プロピレングリコールモノメチルエーテル１４５部の混合溶液を滴下ポンプを用いて４時間かけて滴下した。
　一方、重合開始剤２，２’－アゾビス（２，４－ジメチルバレロニトリル）５部をプロピレングリコールモノメチルエーテルアセテート２００部に溶解した混合溶液を別の滴下ポンプを用いて５時間かけてフラスコ内に滴下した。重合開始剤の滴下が終了した後、３時間同温度で保持した後、室温まで冷却して、Ｂ型粘度（２３℃）１２２ｍＰａｓ、固形分３２．０％の共重合体（樹脂（Ｂ－３））の溶液を得た。生成した共重合体の重量平均分子量（Ｍｗ）は２１５００、固形分換算の酸価は１８７ｍｇ－ＫＯＨ／ｇ、分散度２．８５であった。樹脂（Ｂ－３）は樹脂（Ｂ－１）と同様の構造単位を有する。
（樹脂合成例４）
　還流冷却器、滴下ロート及び撹拌機を備えたフラスコ内に窒素を適量流して窒素雰囲気に置換し、プロピレングリコールモノメチルエーテルアセテート２３２部、及び乳酸エチル１６２部を入れ、撹拌しながら８５℃まで加熱した。次いで、該フラスコ内に、３，４－エポキシトリシクロ［５．２．１．０2,6］デカン－８－イルアクリレート及び３，４－エポキシトリシクロ［５．２．１．０2,6］デカン－９－イルアクリレートの混合物（
混合割合は１：１）１８０部、アクリル酸６０部、２－ヒドロキシエチルメタクリレート６０部、乳酸エチル１４８部並びにプロピレングリコールモノメチルエーテルアセテート５４部の混合溶液を滴下ポンプを用いて５時間かけて滴下した。
　一方、重合開始剤２，２’－アゾビス（２，４－ジメチルバレロニトリル）１０部をプロピレングリコールモノメチルエーテルアセテート１００部に溶解した混合溶液を別の滴下ポンプを用いて５時間かけてフラスコ内に滴下した。重合開始剤の滴下が終了した後、３時間同温度で保持した後、室温まで冷却して、Ｂ型粘度（２３℃）１０３ｍＰａｓ、固形分３１．０％の共重合体（樹脂（Ｂ－４））の溶液を得た。生成した共重合体の重量平均分子量（Ｍｗ）は９８００、固形分換算の酸価は１５３ｍｇ－ＫＯＨ／ｇ、分散度２．４３であった。樹脂（Ｂ－４）は下記構造単位を有する。
Figure JPOXMLDOC01-appb-C000037
（樹脂合成例５）
　還流冷却器、滴下ロート及び撹拌機を備えたフラスコ内に窒素を適量流して窒素雰囲気に置換し、プロピレングリコールモノメチルエーテルアセテート１００部を入れ、撹拌しながら８５℃まで加熱した。次いで、該フラスコ内に、メタクリル酸１９部、３，４－エポキシトリシクロ［５．２．１．０2,6］デカン－８－イルアクリレート及び３，４－エポキシトリシクロ［５．２．１．０2,6］デカン－９－イルアクリレートの混合物（混合
割合は１：１）１７１部をプロピレングリコールモノメチルエーテルアセテート４０部に溶解した溶液を滴下ポンプを用いて約５時間かけて滴下した。
　一方、重合開始剤２，２’－アゾビス（２，４－ジメチルバレロニトリル）２６部をプロピレングリコールモノメチルエーテルアセテート１２０部に溶解した溶液を別の滴下ポンプを用いて約５時間かけてフラスコ内に滴下した。重合開始剤の滴下が終了した後、約３時間同温度で保持した後、その後室温まで冷却して、固形分４３．５％の共重合体（樹脂（Ｂ－５））の溶液を得た。得られた樹脂（Ｂ－５）の重量平均分子量（Ｍｗ）は８０００、分散度は１．９８、固形分換算の酸価は５３ｍｇ－ＫＯＨ／ｇであった。樹脂（Ｂ－５）は下記構造単位を有する。
Figure JPOXMLDOC01-appb-C000038
（樹脂合成例６）
　還流冷却器、滴下ロート及び攪拌機を備えたフラスコ内に窒素を適量流し窒素雰囲気に置換し、プロピレングリコールモノメチルエーテルアセテート２８０部を入れ、攪拌しながら８０℃まで加熱した。次いで、アクリル酸３８部、３，４－エポキシトリシクロ［５．２．１．０2,6］デカン－８－イルアクリレート及び３，４－エポキシトリシクロ［５．２．１．０2,6］デカン－９－イルアクリレートの混合物（混合割合は１：１）２８９
部、プロピレングリコールモノメチルエーテルアセテート１２５部の混合溶液を滴下ポンプを用いて５時間かけて滴下した。
　一方、２，２’－アゾビス（２，４－ジメチルバレロニトリル）３３部をプロピレングリコールモノメチルエーテルアセテート２３５部に溶解した混合溶液を別の滴下ポンプを用いて６時間かけて滴下した。滴下終了後、フラスコ内を８０℃で４時間保持した後、室温で冷却して、Ｂ型粘度（２３℃）１０８ｍＰａｓ、固形分３５．０％の共重合体（樹脂（Ｂ－６））溶液を得た。生成した共重合体の重量平均分子量（Ｍｗ）は９１００、分散度２．１９、固形分換算の酸価８１ｍｇ－ＫＯＨ／ｇであった。樹脂（Ｂ－６）は樹脂（Ｂ－１）と同様の構造単位を有する。
（樹脂合成例７）
　還流冷却器、滴下ロート及び撹拌機を備えたフラスコ内に窒素を適量流して窒素雰囲気に置換し、プロピレングリコールモノメチルエーテルアセテート２４５部、及びプロピレングリコールモノメチルエーテル１７１部を入れ、撹拌しながら８５℃まで加熱した。次いで、該フラスコ内に、３，４－エポキシトリシクロ［５．２．１．０2,6］デカン－８－イルアクリレート及び３，４－エポキシトリシクロ［５．２．１．０2,6］デカン－９
－イルアクリレートの混合物（混合割合は１：１）２１０部、アクリル酸９０部、プロピレングリコールモノメチルエーテル６４部の混合溶液を滴下ポンプを用いて４時間かけて滴下した。
　一方、重合開始剤２，２’－アゾビス（２，４－ジメチルバレロニトリル）２０部をプロピレングリコールモノメチルエーテルアセテート２００部に溶解した混合溶液を別の滴下ポンプを用いて５時間かけてフラスコ内に滴下した。重合開始剤の滴下が終了した後、３時間同温度で保持した後、室温まで冷却して、Ｂ型粘度（２３℃）６９ｍＰａｓ、固形分３３．３％の共重合体（樹脂（Ｂ－７））の溶液を得た。生成した共重合体の重量平均分子量（Ｍｗ）は９２００、固形分換算の酸価は２１３ｍｇ－ＫＯＨ／ｇ、分散度２．２６であった。樹脂（Ｂ－７）は樹脂（Ｂ－１）と同様の構造単位を有する。
［実施例１～９、比較例１～４］
［着色硬化性樹脂組成物の調製］
　表２に示す組成となるように各成分を混合して着色硬化性樹脂組成物を得た。
Figure JPOXMLDOC01-appb-T000039
　表２中、各成分は以下の化合物を表す。
着色剤（Ａ－１）：式（ＡＩＩ－１０）で表される化合物
着色剤（Ａ－２）：式（ＡＩＩ－１７）で表される化合物
着色剤（Ａ－３）：式（ＡＩＩ－１８）で表される化合物
樹脂（Ｂ－１）：樹脂（Ｂ－１）（固形分換算）
樹脂（Ｂ－２）：樹脂（Ｂ－２）（固形分換算）
樹脂（Ｂ－３）：樹脂（Ｂ－３）（固形分換算）
樹脂（Ｂ－４）：樹脂（Ｂ－４）（固形分換算）
樹脂（Ｂ－５）：樹脂（Ｂ－５）（固形分換算）
樹脂（Ｂ－６）：樹脂（Ｂ－６）（固形分換算）
樹脂（Ｂ－７）：樹脂（Ｂ－７）（固形分換算）
重合性化合物（Ｃ－１）：ジペンタエリスリトールヘキサアクリレート（ＫＡＹＡＲＡＤ（登録商標）　ＤＰＨＡ；日本化薬（株）製）
重合開始剤（Ｄ－１）：Ｎ－ベンゾイルオキシ－１－（４－フェニルスルファニルフェニル）オクタン－１－オン－２－イミン（イルガキュア（登録商標）ＯＸＥ－０１；ＢＡＳＦ社製；Ｏ－アシルオキシム化合物）
重合開始剤（Ｄ－２）：ＤＦＩ－０９１（ダイトーケミックス社製；Ｏ－アシルオキシム化合物）
溶剤（Ｅ－１）：４－ヒドロキシ－４－メチル－２－ペンタノン
溶剤（Ｅ－２）：プロピレングリコールモノメチルエーテルアセテート
溶剤（Ｅ－３）：乳酸エチル
溶剤（Ｅ－４）：プロピレングリコールモノメチルエーテル
レベリング剤（Ｆ－１）：ポリエーテル変性シリコーンオイル（東レ・ダウコーニング（株）製「トーレシリコーンＳＨ８４００」）
［着色塗膜の作製］
　５ｃｍ角のガラス基板（イーグルＸＧ；コーニング社製）上に、着色硬化性樹脂組成物を、ポストベーク後の膜厚が２．０μｍになるようにスピンコート法で塗布したのち、１００℃で３分間プリベークして着色組成物層を形成した。放冷後、露光機（ＴＭＥ－１５０ＲＳＫ；トプコン（株）製）を用いて、大気雰囲気下、１００ｍＪ／ｃｍ2の露光量（３６５ｎｍ基準）で着色組成物層に光照射を行った。その後、オーブン中２３０℃で３０分間ポストベークを行い、着色塗膜を得た。
［工程性評価］
１．吸光度保持率
　プリベーク後及びポストベーク後に測定した分光から極大吸光度を求め、下記式に従
って極大吸光度の保持率を計算した。結果を表３～５に示す。
　吸光度保持率（ΔＡｂｓ.Ｍａｘ）＝ポストベーク後の極大吸光度／プリベーク後の極大吸光度
　吸光度保持率が高いほど、成膜工程における適性が高いことを意味する。
２．耐熱性（ΔＥａｂ＊）
　プリベーク後及びポストベーク後に色度の測定を行い、該測定値からＪＩＳ　Ｚ　８
７３０：２００９（７．色差の計算方法）に記載される方法で色差△Ｅａｂ＊を計算した。結果を表５に示す。△Ｅａｂ＊は小さいほど色変化が小さいことを意味する。
［パターンの作製］
　２インチ角のガラス基板（イーグルＸＧ；コーニング社製）上に、着色硬化性樹脂組成物を、プリベーク後の膜厚が２．０μｍになるように、スピンコート法で塗布した後、１００℃で３分間プリベークして組成物層を形成した。冷却後、組成物層を形成した基板と石英ガラス製フォトマスクとの間隔を１００μｍとして、露光機（ＴＭＥ－１５０ＲＳＫ；トプコン（株）製）を用いて、大気雰囲気下、６０ｍＪ／ｃｍ2の露光量（３６５ｎｍ基準）で光照射した。尚、フォトマスクとしては、１００μｍのラインアンドスペースパターンが形成されたものを使用した。光照射後の組成物層を、非イオン系界面活性剤０．１２％と水酸化カリウム０．０４％とを含む水溶液に２３℃で９０秒間浸漬させて現像した。
３．パターン現像性の評価
　現像後、水洗した基板を、顕微鏡（倍率５００倍；ＶＦ－７５１０；（株）キーエンス製）を用いて観察し、以下の評価基準に従って着色硬化性樹脂組成物層のパターニング性を評価した。結果を表５に示す。
○：所定の線幅のパターンが形成されている。
×：所定の線幅のパターンが形成されておらず、未露光部が現像液で溶解除去されていない、又は未露光部にパターンの一部が存在する。
　未露光部にパターンの一部が存在する状態として、現像液によって溶解除去された未露光部に、形成されたパターンの一部が現像液によって溶解し浸食され、
　ｉ）溶解したパターンが未露光部にまで広がっている状態
　ｉｉ）一度基板から剥離したパターンが未露光部に再び付着した状態
などが挙げられる。
Figure JPOXMLDOC01-appb-T000040
Figure JPOXMLDOC01-appb-T000041
Figure JPOXMLDOC01-appb-T000042
　本発明の着色樹脂組成物によれば、吸光度保持率に優れるカラーフィルタを形成することができる。

Claims (3)

  1. 　着色剤、樹脂、重合性化合物、及び重合開始剤を含み、
    　前記着色剤が、式（Ｉ）で表されるスクアリリウム染料を含む着色剤であり、
    　前記樹脂の固形分換算における酸価が、１００～２００ｍｇ－ＫＯＨ／ｇである着色硬化性樹脂組成物。
    Figure JPOXMLDOC01-appb-C000001
     ［式（Ｉ）中、
    　Ｒ1～Ｒ4は、それぞれ独立に、水素原子、ハロゲン原子、ヒドロキシ基又は置換基を有していてもよい炭素数１～２０の１価の飽和炭化水素基を表す。該１価の飽和炭化水素基を構成する炭素原子間に、酸素原子又は硫黄原子が挿入されていてもよい。
    　Ｒ5～Ｒ8は、それぞれ独立に、水素原子又はヒドロキシ基を表す。
    　Ａｒ1及びＡｒ2は、それぞれ独立に、置換基を有していてもよい炭素数１～２０の１価の飽和炭化水素基又は式（ｉ）で表される基を表す。
    Figure JPOXMLDOC01-appb-C000002
     ［式（ｉ）中、
    　Ｒ12は、置換基を有していてもよい炭素数１～２０の１価の飽和炭化水素基又は置換基を有していてもよい炭素数２～２０の１価の不飽和炭化水素基を表し、ｍは０～５の整数を表す。該１価の飽和炭化水素基を構成する炭素原子間に、酸素原子又は硫黄原子が挿入されていてもよい。ｍが２以上のとき、複数のＲ12は、それぞれ同一であっても異なっていてもよい。＊は、窒素原子との結合手を表す。］
    　Ｒ9及びＲ10は、それぞれ独立に、置換基を有していてもよい炭素数１～２０の１価の飽和炭化水素基又は式（ｉ）で表される基を表す。該１価の飽和炭化水素基を構成する炭素原子間に、酸素原子又は硫黄原子が挿入されていてもよい。］
  2. 　請求項１に記載の着色硬化性樹脂組成物から形成されるカラーフィルタ。
  3. 　請求項２に記載のカラーフィルタを含む表示装置。
PCT/JP2019/047176 2019-02-08 2019-12-03 着色硬化性樹脂組成物 WO2020162010A1 (ja)