WO2020158140A1 - Feuille de cuivre traitée en surface, carte stratifiée cuivrée, et carte de circuit imprimé - Google Patents

Feuille de cuivre traitée en surface, carte stratifiée cuivrée, et carte de circuit imprimé Download PDF

Info

Publication number
WO2020158140A1
WO2020158140A1 PCT/JP2019/046454 JP2019046454W WO2020158140A1 WO 2020158140 A1 WO2020158140 A1 WO 2020158140A1 JP 2019046454 W JP2019046454 W JP 2019046454W WO 2020158140 A1 WO2020158140 A1 WO 2020158140A1
Authority
WO
WIPO (PCT)
Prior art keywords
copper foil
treated
layer
treatment layer
treated copper
Prior art date
Application number
PCT/JP2019/046454
Other languages
English (en)
Japanese (ja)
Inventor
郁浩 五刀
敦史 三木
宣明 宮本
Original Assignee
Ｊｘ金属株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ｊｘ金属株式会社 filed Critical Ｊｘ金属株式会社
Publication of WO2020158140A1 publication Critical patent/WO2020158140A1/fr

Abstract

L'invention concerne une feuille de cuivre traitée en surface qui possède une feuille de cuivre, et une couche traitée en surface formée sur au moins une face de cette feuille de cuivre. Cette feuille de cuivre traitée en surface présente une longueur moyenne (ＲＳｍ) de la couche traitée en surface comprise entre ３,３ et ５,２μｍ. Enfin, l'invention concerne une carte stratifiée cuivrée qui est équipée de la feuille de cuivre traitée en surface, et d'un substrat de résine en adhésion sur la couche traitée en surface de cette feuille de cuivre traitée en surface.
PCT/JP2019/046454 2019-01-30 2019-11-27 Feuille de cuivre traitée en surface, carte stratifiée cuivrée, et carte de circuit imprimé WO2020158140A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019014795A JP7114499B2 (ja) 2019-01-30 2019-01-30 表面処理銅箔、銅張積層板及びプリント配線板
JP2019-014795 2019-01-30

Publications (1)

Publication Number Publication Date
WO2020158140A1 true WO2020158140A1 (fr) 2020-08-06

Family

ID=71842054

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/046454 WO2020158140A1 (fr) 2019-01-30 2019-11-27 Feuille de cuivre traitée en surface, carte stratifiée cuivrée, et carte de circuit imprimé

Country Status (3)

Country Link
JP (1) JP7114499B2 (fr)
TW (1) TWI716210B (fr)
WO (1) WO2020158140A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115812109A (zh) * 2020-12-24 2023-03-17 日本制铁株式会社 钛材

Families Citing this family (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP7114500B2 (ja) * 2019-01-30 2022-08-08 Ｊｘ金属株式会社 表面処理銅箔、銅張積層板及びプリント配線板
KR20230159392A (ko) * 2021-03-26 2023-11-21 미쓰이금속광업주식회사 조화 처리 구리박, 캐리어를 구비한 구리박, 동장 적층판 및 프린트 배선판
WO2022202541A1 (fr) * 2021-03-26 2022-09-29 三井金属鉱業株式会社 Feuille de cuivre rugueuse, feuille de cuivre comprenant un support, carte stratifiée plaquée de cuivre et carte de circuit imprimé
KR20240017840A (ko) * 2021-06-03 2024-02-08 미쓰이금속광업주식회사 조화 처리 구리박, 동장 적층판 및 프린트 배선판
WO2023281775A1 (fr) * 2021-07-09 2023-01-12 Ｊｘ金属株式会社 Feuille de cuivre traitée en surface, stratifié cuivré et carte de circuit imprimé
CN117769491A (zh) 2021-08-06 2024-03-26 索尼集团公司 铜箔层压板及印刷线路板

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017051898A1 (fr) * 2015-09-24 2017-03-30 Ｊｘ金属株式会社 Feuille métallique, feuille métallique pourvue d'une couche de séparation, corps stratifié, carte de circuit imprimé, boîtier de semi-conducteur, appareil électronique, et procédé de production d'une carte de circuit imprimé
WO2017051906A1 (fr) * 2015-09-24 2017-03-30 Ｊｘ金属株式会社 Feuille métallique, feuille métallique comportant une couche antiadhésive, corps stratifié, carte de circuit imprimé, boîtier de semi-conducteur, appareil électronique et procédé de production de carte de circuit imprimé

Family Cites Families (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2007268596A (ja) * 2006-03-31 2007-10-18 Nikko Kinzoku Kk 粗化処理用銅合金箔
JP5416037B2 (ja) * 2009-05-29 2014-02-12 Ｊｘ日鉱日石金属株式会社 リチウム電池集電体用圧延銅箔
JP5871426B2 (ja) 2012-01-31 2016-03-01 古河電気工業株式会社 高周波伝送用表面処理銅箔、高周波伝送用積層板及び高周波伝送用プリント配線板
JP2016036829A (ja) * 2014-08-07 2016-03-22 Jx日鉱日石金属株式会社 圧延銅箔及びそれを用いた二次電池用集電体
JP2018122590A (ja) * 2017-02-02 2018-08-09 Ｊｘ金属株式会社 離型層付き金属箔、金属箔、積層体、プリント配線板、半導体パッケージ、電子機器及びプリント配線板の製造方法

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2017051898A1 (fr) * 2015-09-24 2017-03-30 Ｊｘ金属株式会社 Feuille métallique, feuille métallique pourvue d'une couche de séparation, corps stratifié, carte de circuit imprimé, boîtier de semi-conducteur, appareil électronique, et procédé de production d'une carte de circuit imprimé
WO2017051906A1 (fr) * 2015-09-24 2017-03-30 Ｊｘ金属株式会社 Feuille métallique, feuille métallique comportant une couche antiadhésive, corps stratifié, carte de circuit imprimé, boîtier de semi-conducteur, appareil électronique et procédé de production de carte de circuit imprimé

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN115812109A (zh) * 2020-12-24 2023-03-17 日本制铁株式会社 钛材
CN115812109B (zh) * 2020-12-24 2024-05-28 日本制铁株式会社 钛材

Also Published As

Publication number Publication date
TW202028484A (zh) 2020-08-01
JP2020122189A (ja) 2020-08-13
TWI716210B (zh) 2021-01-11
JP7114499B2 (ja) 2022-08-08

Similar Documents

Publication Publication Date Title
WO2020158140A1 (fr) Feuille de cuivre traitée en surface, carte stratifiée cuivrée, et carte de circuit imprimé
KR101920976B1 (ko) 구리박, 캐리어박 부착 구리박, 및 구리 피복 적층판
CN114761622B (zh) 表面处理铜箔、覆铜积层板及印刷配线板
TWI747088B (zh) 表面處理銅箔、覆銅積層板及印刷配線板
KR20100076055A (ko) 프린트 배선판용 동박
WO2021117338A1 (fr) Feuille de cuivre traitée en surface, carte stratifiée cuivrée, et carte de circuit imprimé
WO2022154102A1 (fr) Feuille de cuivre traitée en surface, plaque stratifiée plaquée de cuivre et carte de circuit imprimé
WO2023281777A1 (fr) Feuille de cuivre traitée en surface, plaque stratifiée plaquée de cuivre et carte de circuit imprimé
WO2024070245A1 (fr) Feuille de cuivre traitée en surface, plaque de stratifié revêtue de cuivre et carte de circuit imprimé
WO2024070246A1 (fr) Feuille de cuivre traitée en surface, plaque stratifiée plaquée de cuivre et carte de circuit imprimé
WO2024070247A1 (fr) Feuille de cuivre traitée en surface, plaque stratifiée plaquée de cuivre et carte de circuit imprimé
WO2024070248A1 (fr) Feuille de cuivre traitée en surface, stratifié plaqué cuivre et carte de circuit imprimé
WO2023281759A1 (fr) Feuille de cuivre traitée en surface, stratifié cuivré et carte de circuit imprimé
WO2023281778A1 (fr) Feuille de cuivre traitée en surface, carte stratifiée plaquée de cuivre et carte de circuit imprimé
WO2023281776A1 (fr) Feuille de cuivre traitée en surface, plaque stratifiée plaquée de cuivre et carte de circuit imprimé
WO2023281774A1 (fr) Feuille de cuivre traitée en surface, stratifié cuivré et carte de circuit imprimé
WO2023281775A1 (fr) Feuille de cuivre traitée en surface, stratifié cuivré et carte de circuit imprimé
WO2022202540A1 (fr) Feuille de cuivre rugosifiée, feuille de cuivre pourvue d'un support, carte stratifiée recouverte de cuivre et carte de circuit imprimé
WO2022202541A1 (fr) Feuille de cuivre rugueuse, feuille de cuivre comprenant un support, carte stratifiée plaquée de cuivre et carte de circuit imprimé
TW202413724A (zh) 表面處理銅箔、覆銅積層板及印刷配線板
TW202415155A (zh) 表面處理銅箔、覆銅積層板及印刷配線板

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19913768

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19913768

Country of ref document: EP

Kind code of ref document: A1