WO2020113903A1 - Agent de finition de microcapsules antibactériennes et de soin de la peau, son procédé de préparation et son application - Google Patents
Agent de finition de microcapsules antibactériennes et de soin de la peau, son procédé de préparation et son application Download PDFInfo
- Publication number
- WO2020113903A1 WO2020113903A1 PCT/CN2019/086093 CN2019086093W WO2020113903A1 WO 2020113903 A1 WO2020113903 A1 WO 2020113903A1 CN 2019086093 W CN2019086093 W CN 2019086093W WO 2020113903 A1 WO2020113903 A1 WO 2020113903A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- microcapsule
- finishing agent
- skin care
- preparation
- organosilicon
- Prior art date
Abstract
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
AU2019394038A AU2019394038A1 (en) | 2018-12-04 | 2019-05-09 | Skincare and antibacterial microcapsule finishing agent, and preparation method therefor and application thereof |
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
CN201811474192.4 | 2018-12-04 | ||
CN201811474192.4A CN109554919A (zh) | 2018-12-04 | 2018-12-04 | 一种护肤抗菌微胶囊整理剂及其制备方法和应用 |
Publications (1)
Publication Number | Publication Date |
---|---|
WO2020113903A1 true WO2020113903A1 (fr) | 2020-06-11 |
Family
ID=65868869
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/CN2019/086093 WO2020113903A1 (fr) | 2018-12-04 | 2019-05-09 | Agent de finition de microcapsules antibactériennes et de soin de la peau, son procédé de préparation et son application |
Country Status (3)
Country | Link |
---|---|
CN (1) | CN109554919A (fr) |
AU (2) | AU2019394038A1 (fr) |
WO (1) | WO2020113903A1 (fr) |
Cited By (11)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN112411192A (zh) * | 2020-11-18 | 2021-02-26 | 肇庆乐印新材料有限公司 | 一种调湿抗紫外织物表面处理剂及其制备方法与应用 |
CN113235298A (zh) * | 2021-06-15 | 2021-08-10 | 吴江市南麻恒兴丝织厂 | 一种亲肤型涤棉乱麻面料的制备方法 |
CN113463380A (zh) * | 2021-07-26 | 2021-10-01 | 河南迪怡疗护科技开发有限公司 | 抗菌面料及生产方法 |
CN113511821A (zh) * | 2021-08-02 | 2021-10-19 | 四川四众玄武岩纤维技术研发有限公司 | 一种电子织物用玄武岩纤维浸润剂及其制备方法 |
CN113652861A (zh) * | 2021-08-31 | 2021-11-16 | 河南迪怡疗护科技开发有限公司 | 一种具有抗菌抗静电功能的面料 |
CN114431689A (zh) * | 2021-11-24 | 2022-05-06 | 吉祥三宝高科纺织有限公司 | 一种对婴童头部和颈部具有防护功能的护型枕 |
CN114469893A (zh) * | 2022-01-25 | 2022-05-13 | 东南大学 | 一种季铵盐化二氧化硅纳米颗粒及制备方法与应用 |
CN114917402A (zh) * | 2022-04-21 | 2022-08-19 | 江西省科学院应用化学研究所 | 单组分光固化型抗菌硅凝胶医用材料及其制备方法和应用 |
CN115341395A (zh) * | 2022-09-15 | 2022-11-15 | 上海安踏体育用品有限公司 | 一种纺织品的整理方法 |
CN115387128A (zh) * | 2022-07-08 | 2022-11-25 | 杭州英诺克新材料有限公司 | 一种基于双相微胶囊的护肤保湿整理剂 |
CN115747992A (zh) * | 2022-11-21 | 2023-03-07 | 江苏康溢臣生命科技有限公司 | 一种含高蛋白抗菌调温纤维素纤维及其制备方法 |
Families Citing this family (10)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN109554919A (zh) * | 2018-12-04 | 2019-04-02 | 江苏金太阳纺织科技股份有限公司 | 一种护肤抗菌微胶囊整理剂及其制备方法和应用 |
CN110344257A (zh) * | 2019-07-29 | 2019-10-18 | 苏州经贸职业技术学院 | 一种微胶囊抑菌功能整理剂的制备方法 |
CN110804871A (zh) * | 2019-09-27 | 2020-02-18 | 嘉兴市民华纺织有限公司 | 一种长丝人棉竹节面料的生产工艺 |
CN110804861A (zh) * | 2019-09-29 | 2020-02-18 | 嘉兴市恒悦纺织有限公司 | 一种涤纶耐久性抗静电面料的生产工艺 |
CN110804864A (zh) * | 2019-09-29 | 2020-02-18 | 嘉兴市恒悦纺织有限公司 | 一种涤纶阻燃抗菌面料加工工艺 |
CN110747651A (zh) * | 2019-10-25 | 2020-02-04 | 嘉兴市秀洲恒丰纺织有限公司 | 一种纯棉面料保湿微胶囊整理工艺 |
CN111455675A (zh) * | 2020-04-23 | 2020-07-28 | 罗莱生活科技股份有限公司 | 一种护肤微胶囊及其制备方法和用途 |
CN114431229A (zh) * | 2020-11-06 | 2022-05-06 | 深圳先进技术研究院 | 一种抗菌抗病毒微胶囊及其制备方法和应用 |
CN112760989A (zh) * | 2020-12-02 | 2021-05-07 | 江苏汇鸿国际集团中锦控股有限公司 | 一种段染石墨烯加缓释微胶囊式空气层面料制作方法 |
CN112726212A (zh) * | 2020-12-24 | 2021-04-30 | 罗莱生活科技股份有限公司 | 一种烟酰胺护肤纺织品及其制备方法 |
Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102677453A (zh) * | 2012-05-25 | 2012-09-19 | 浙江理工大学 | 负载有机硅季铵盐和纳米二氧化钛复合抗菌剂的棉织物制备方法 |
CN102677471A (zh) * | 2012-05-29 | 2012-09-19 | 东华大学 | 一种溶胶-凝胶技术制备调温织物的方法 |
CN106567149A (zh) * | 2016-10-26 | 2017-04-19 | 帛方纺织有限公司 | 一种功能性植物芳香、抗菌纤维素纤维及其制备方法 |
CN107213080A (zh) * | 2016-12-20 | 2017-09-29 | 林彩霞 | 一种芦荟添加物及其制备方法 |
CN107326660A (zh) * | 2017-06-26 | 2017-11-07 | 苏州威尔德工贸有限公司 | 一种抗菌织物整理剂的制备方法 |
CN107694522A (zh) * | 2017-10-16 | 2018-02-16 | 广州中国科学院工业技术研究院 | 含有有机硅季铵盐的纳米粒子及其制备方法和用途 |
CN109554919A (zh) * | 2018-12-04 | 2019-04-02 | 江苏金太阳纺织科技股份有限公司 | 一种护肤抗菌微胶囊整理剂及其制备方法和应用 |
-
2018
- 2018-12-04 CN CN201811474192.4A patent/CN109554919A/zh active Pending
-
2019
- 2019-05-09 AU AU2019394038A patent/AU2019394038A1/en active Pending
- 2019-05-09 WO PCT/CN2019/086093 patent/WO2020113903A1/fr active Application Filing
- 2019-05-09 AU AU2019101766A patent/AU2019101766A4/en active Active
Patent Citations (7)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN102677453A (zh) * | 2012-05-25 | 2012-09-19 | 浙江理工大学 | 负载有机硅季铵盐和纳米二氧化钛复合抗菌剂的棉织物制备方法 |
CN102677471A (zh) * | 2012-05-29 | 2012-09-19 | 东华大学 | 一种溶胶-凝胶技术制备调温织物的方法 |
CN106567149A (zh) * | 2016-10-26 | 2017-04-19 | 帛方纺织有限公司 | 一种功能性植物芳香、抗菌纤维素纤维及其制备方法 |
CN107213080A (zh) * | 2016-12-20 | 2017-09-29 | 林彩霞 | 一种芦荟添加物及其制备方法 |
CN107326660A (zh) * | 2017-06-26 | 2017-11-07 | 苏州威尔德工贸有限公司 | 一种抗菌织物整理剂的制备方法 |
CN107694522A (zh) * | 2017-10-16 | 2018-02-16 | 广州中国科学院工业技术研究院 | 含有有机硅季铵盐的纳米粒子及其制备方法和用途 |
CN109554919A (zh) * | 2018-12-04 | 2019-04-02 | 江苏金太阳纺织科技股份有限公司 | 一种护肤抗菌微胶囊整理剂及其制备方法和应用 |
Cited By (15)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN112411192A (zh) * | 2020-11-18 | 2021-02-26 | 肇庆乐印新材料有限公司 | 一种调湿抗紫外织物表面处理剂及其制备方法与应用 |
CN113235298A (zh) * | 2021-06-15 | 2021-08-10 | 吴江市南麻恒兴丝织厂 | 一种亲肤型涤棉乱麻面料的制备方法 |
CN113463380A (zh) * | 2021-07-26 | 2021-10-01 | 河南迪怡疗护科技开发有限公司 | 抗菌面料及生产方法 |
CN113511821A (zh) * | 2021-08-02 | 2021-10-19 | 四川四众玄武岩纤维技术研发有限公司 | 一种电子织物用玄武岩纤维浸润剂及其制备方法 |
CN113511821B (zh) * | 2021-08-02 | 2022-10-25 | 四川四众玄武岩纤维技术研发有限公司 | 一种电子织物用玄武岩纤维浸润剂及其制备方法 |
CN113652861B (zh) * | 2021-08-31 | 2023-07-11 | 宁波华鑫针织服装有限公司 | 一种具有抗菌抗静电功能的面料 |
CN113652861A (zh) * | 2021-08-31 | 2021-11-16 | 河南迪怡疗护科技开发有限公司 | 一种具有抗菌抗静电功能的面料 |
CN114431689A (zh) * | 2021-11-24 | 2022-05-06 | 吉祥三宝高科纺织有限公司 | 一种对婴童头部和颈部具有防护功能的护型枕 |
CN114431689B (zh) * | 2021-11-24 | 2023-07-21 | 吉祥三宝高科纺织有限公司 | 一种对婴童头部和颈部具有防护功能的护型枕 |
CN114469893A (zh) * | 2022-01-25 | 2022-05-13 | 东南大学 | 一种季铵盐化二氧化硅纳米颗粒及制备方法与应用 |
CN114917402A (zh) * | 2022-04-21 | 2022-08-19 | 江西省科学院应用化学研究所 | 单组分光固化型抗菌硅凝胶医用材料及其制备方法和应用 |
CN114917402B (zh) * | 2022-04-21 | 2023-08-15 | 江西省科学院应用化学研究所 | 单组分光固化型抗菌硅凝胶医用材料及其制备方法和应用 |
CN115387128A (zh) * | 2022-07-08 | 2022-11-25 | 杭州英诺克新材料有限公司 | 一种基于双相微胶囊的护肤保湿整理剂 |
CN115341395A (zh) * | 2022-09-15 | 2022-11-15 | 上海安踏体育用品有限公司 | 一种纺织品的整理方法 |
CN115747992A (zh) * | 2022-11-21 | 2023-03-07 | 江苏康溢臣生命科技有限公司 | 一种含高蛋白抗菌调温纤维素纤维及其制备方法 |
Also Published As
Publication number | Publication date |
---|---|
AU2019394038A1 (en) | 2020-12-03 |
AU2019101766A4 (en) | 2020-12-24 |
CN109554919A (zh) | 2019-04-02 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
WO2020113903A1 (fr) | Agent de finition de microcapsules antibactériennes et de soin de la peau, son procédé de préparation et son application | |
CN102002854B (zh) | 一种多功能织物整理剂及其制备方法和棉织物整理方法 | |
CN101591859B (zh) | 一种艾叶油微胶囊织物复合整理剂及其应用 | |
CN101709549B (zh) | 一种纤维素织物的耐久功能整理方法 | |
CN102995394B (zh) | 一种基于氧化石墨烯的染色、抗菌整理剂及其制备方法和应用 | |
CN105821660B (zh) | 一种高吸湿保湿性的改性蚕丝纤维及其制备方法 | |
CN102605619A (zh) | 一种棉织物的丝胶后整理方法 | |
CN104532596A (zh) | 一种肉桂油微胶囊织物整理液及其制备方法和应用 | |
CN105155278A (zh) | 一种抗皱整理液及真丝面料的抗皱整理方法 | |
CN103981701B (zh) | 一种壳聚糖/Ag+复合抗菌整理液及其制备方法和应用 | |
CN103643526B (zh) | 一种采用硅溶胶制备抗皱棉织物的方法 | |
CN103361966A (zh) | 一种活性负氧离子羊绒纱线后整理方法 | |
CN106592104B (zh) | 一种茶多酚纤维素纤维水刺无纺布及其生产方法 | |
CN105369628A (zh) | 一种涤纶织物整理工艺 | |
US20140304922A1 (en) | Fabric having ultraviolet radiation protection | |
CN105220481A (zh) | 一种婴儿服装专用的新型抗静电面料及其制备方法 | |
CN103924444A (zh) | 一种用于织物的亲水抗菌调理剂制备方法及其应用 | |
CN101418517B (zh) | 一种用于纺织品抗菌的季铵盐溶胶的应用 | |
CN107974831A (zh) | 一种海藻酸钙改性的丙纶非织造布及其制备方法 | |
CN114645453A (zh) | 一种耐久阻燃蛋白质纤维制品及其制备方法 | |
CN104988741A (zh) | 一种棉质衬衫的香薰免烫处理方法 | |
CN101694058A (zh) | 一种用于纺织品功能整理的硅溶胶的制备方法 | |
CN107475861A (zh) | 一种含有壳聚糖的抗拉伸面料的制备方法 | |
CN109303879A (zh) | 一种治疗湿疹的中药贴膏剂及其制备方法 | |
CN115094627B (zh) | 一种耐久疏水聚酯纤维制品的制备方法 |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 19894047 Country of ref document: EP Kind code of ref document: A1 |
|
ENP | Entry into the national phase |
Ref document number: 2019394038 Country of ref document: AU Date of ref document: 20190509 Kind code of ref document: A |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
122 | Ep: pct application non-entry in european phase |
Ref document number: 19894047 Country of ref document: EP Kind code of ref document: A1 |