CN101694058A - 一种用于纺织品功能整理的硅溶胶的制备方法 - Google Patents
一种用于纺织品功能整理的硅溶胶的制备方法 Download PDFInfo
- Publication number
- CN101694058A CN101694058A CN200910197291A CN200910197291A CN101694058A CN 101694058 A CN101694058 A CN 101694058A CN 200910197291 A CN200910197291 A CN 200910197291A CN 200910197291 A CN200910197291 A CN 200910197291A CN 101694058 A CN101694058 A CN 101694058A
- Authority
- CN
- China
- Prior art keywords
- finishing
- finishing agent
- agent
- functions
- textile fabrics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种用于纺织品功能整理的硅溶胶的制备方法,包括:配制钠、钾或锂水玻璃与纺织品功能整理剂的混合溶液,其中钠、钾或锂水玻璃质量百分比浓度为1~15%,模数范围为1~3.5,功能整理剂质量百分比浓度为0.01~4%;向该混合溶液中添加有机酯使溶液中有机酯质量百分比浓度为0.5~10%,得到用于纺织品功能整理的硅溶胶。该制备方法简单、成本低、来源广,易产业化。
Description
技术领域
本发明属纺织品整理剂的制备技术领域,特别涉及一种使用水玻璃为原料,有机酯为催化剂,采用溶胶-凝胶技术制备用于纺织品功能整理的硅溶胶的方法。
背景技术
硅溶胶是二氧化硅高分子无定形微粒分散在溶剂中的胶体溶液。纺织领域中硅溶胶的浓度一般为1~20%,其粒径大小为5~100nm。硅溶胶可以由工业生产的水玻璃水解制备得到。对于纺织工业而言,由水玻璃制备得到的二氧化硅水溶胶成本低廉,且便于与前后道的含水整理连续加工,在印染行业有广阔的应用空间。然而,溶剂水在一定程度上也影响到了这类二氧化硅溶胶的应用,如很多不溶于水的有机功能整理剂,由于无法与二氧化硅水溶胶形成均一稳定的体系,使二氧化硅溶胶的应用受到限制。
发明内容
本发明所要解决的技术问题是提供一种用于纺织品功能整理的硅溶胶的制备方法,制备工艺简单,成本低廉,功能整理剂在溶胶体系中溶解分散效果好。
本发明提供一种用于纺织品功能整理的硅溶胶的制备方法,包括如下步骤:配制钠、钾或锂水玻璃与纺织品功能整理剂的混合溶液,其中钠、钾或锂水玻璃模数范围为1~3.5,质量百分比浓度为1~15%,功能整理剂质量百分比浓度为0.01~4%;向该混合溶液中添加有机酯使溶液中有机酯质量百分比浓度为0.5~10%,pH达到10.8~10.2后得到用于纺织品功能整理的硅溶胶。
所述的有机酯为有机酸A和醇B反应形成的单酯、二酯或多元酯中的一种或几种:其中,酸A为H-(CH2)n-COOH,n=0~3、HOOC-(CH2)n-COOH,n=0~3或柠檬酸中的一种;醇B为H-(CH2)m-OH,m=1~5、HO-(CH2)m-OH,m=2~5、H-(O-CH2CH2)m-OH,m=1~20、H-(O-CH2CH2CH2)m-OH,m=1~20、甘油或季戊四醇中的一种或几种。
所述的功能整理剂是水溶性功能整理剂或溶解于所用有机酯水解后产生的有机酸A或醇B中的有机功能整理剂。具体地,所述的功能整理剂是防紫外线整理剂、抗菌防臭整理剂、抗静电剂、防电磁波辐射整理剂、远红外发射材料、拒水整理剂、拒油整理剂、负氧离子释放材料、脱味剂、阻燃剂、香味剂或药物。
本发明所制备的硅溶胶适用于任何天然纤维织物或合成纤维织物,并可通过浸渍、浸轧或浸轧堆置等工艺对织物进行功能整理。
有益效果
(1)扩展了由水玻璃制备得到的二氧化硅溶胶的使用性能,一方面以水为溶剂的溶胶易于产业化生产;另一方面溶胶体系中水解生成的有机溶剂弥补了水体系对于有机物溶解性较差的缺点,增加了溶胶对各类功能整理剂的溶解能力,扩大了溶胶的应用范围。
(2)制备方法简单、常温下即可进行,原料成本低、来源广,易产业化。
(3)用于织物整理的方法简便,可用于各类纺织品多种加工方式。
具体实施方式
下面结合具体实施例,进一步阐述本发明。应理解,这些实施例仅用于说明本发明而不用于限制本发明的范围。此外应理解,在阅读了本发明讲授的内容之后,本领域技术人员可以对本发明作各种改动或修改,这些等价形式同样落于本申请所附权利要求书所限定的范围。
实施例1
向50mL的质量百分比浓度为2%的水玻璃和质量百分比浓度为1%的十六烷基三甲氧基硅氧烷的混合体系中逐滴加入1.5mL乙酸乙酯,室温下搅拌30分钟后静置4小时,得到透明、均一的具有拒水功能的二氧化硅混合溶胶(pH=10.2)。
将棉纱卡(20s×16s,128×60)在得到的溶胶中二浸二轧,带液率80%,80℃预烘3分钟,得到具有拒水功能的棉织物。
实施例2
向50mL的质量百分比浓度为2%的水玻璃和质量百分比浓度为2%的维生素E醋酸酯的混合体系中逐滴加入1.5mL柠檬酸三乙酯,室温下搅拌30分钟后静置4小时,得到透明、均一的具有护肤功能的二氧化硅混合溶胶(pH=10.5)。
将棉纱卡(20s×16s,128×60)在得到的溶胶中二浸二轧,带液率80%,80℃预烘3分钟,得到具有护肤、保健功能的棉织物。
实施例3
向50mL的质量百分比浓度为2%的水玻璃和质量百分比浓度为1%的三氯生的混合体系中逐滴加入2mL三乙酸甘油酯,室温下搅拌30分钟后静置4小时,得到透明、均一的具有抗菌功能的二氧化硅溶胶(pH=10.8)。
将涤纶机织物(68D×68D,210T)在得到的溶胶中二浸二轧,带液率70%,80℃预烘3分钟,得到具有抗菌功能的涤纶织物。
Claims (4)
1.一种用于纺织品功能整理的硅溶胶的制备方法,包括如下步骤:配制钠、钾或锂水玻璃与纺织品功能整理剂的混合溶液,其中钠、钾或锂水玻璃模数范围为1~3.5,质量百分比浓度为1~15%,功能整理剂质量百分比浓度为0.01~4%;向该混合溶液中添加有机酯使溶液中有机酯质量百分比浓度为0.5~10%,pH达到10.8~10.2后得到用于纺织品功能整理的硅溶胶。
2.根据权利要求1所述的一种用于纺织品功能整理的硅溶胶的制备方法,其特征在于,所述的有机酯为有机酸A和醇B反应形成的单酯、二酯或多元酯中的一种或几种:其中,酸A为H-(CH2)n-COOH,n=0~3、HOOC-(CH2)n-COOH,n=0~3或柠檬酸中的一种;醇B为H-(CH2)m-OH,m=1~5、HO-(CH2)m-OH,m=2~5、H-(O-CH2CH2)m-OH,m=1~20、H-(O-CH2CH2CH2)m-OH,m=1~20、甘油或季戊四醇中的一种或几种。
3.根据权利要求1或2所述的一种用于纺织品功能整理的硅溶胶的制备方法,其特征在于,所述的功能整理剂是水溶性功能整理剂或溶解于所用有机酯水解后产生的有机酸A或醇B中的有机功能整理剂。
4.根据权利要求3所述的一种用于纺织品功能整理的硅溶胶的制备方法,其特征在于,所述的功能整理剂是防紫外线整理剂、抗菌防臭整理剂、抗静电剂、防电磁波辐射整理剂、远红外发射材料、拒水整理剂、拒油整理剂、负氧离子释放材料、脱味剂、阻燃剂、香味剂或药物。