WO2020070933A1 - Batterie secondaire au lithium-ion et son procédé de fabrication - Google Patents

Batterie secondaire au lithium-ion et son procédé de fabrication

Info

Publication number
WO2020070933A1
WO2020070933A1 PCT/JP2019/026269 JP2019026269W WO2020070933A1 WO 2020070933 A1 WO2020070933 A1 WO 2020070933A1 JP 2019026269 W JP2019026269 W JP 2019026269W WO 2020070933 A1 WO2020070933 A1 WO 2020070933A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
substrate
ion secondary
secondary battery
lithium ion
Prior art date
Application number
PCT/JP2019/026269
Other languages
English (en)
Japanese (ja)
Inventor
安田　剛規
坂脇　彰
晴章 内田
恭成 渡邉
Original Assignee
昭和電工株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 昭和電工株式会社 filed Critical 昭和電工株式会社
Publication of WO2020070933A1 publication Critical patent/WO2020070933A1/fr

Abstract

L'invention concerne une batterie secondaire au lithium-ion (1) qui est constituée de couches dans l'ordre suivant : un substrat (10) qui sert de couche collectrice de courant d'électrode positive; une sous-couche (20); une couche d'électrode positive (30) contenant un matériau actif d'électrode positive; une couche d'électrolyte solide (40) contenant Li3PO4 mais ne contenant pas LiPON; une couche de rétention (50) composée d'un métal noble ou similaire; une couche de prévention de diffusion (60) composée d'un alliage amorphe; et une couche collectrice de courant d'électrode négative (70) composée d'un métal noble. Une surface (10a) du substrat (10) pour stratifier la sous-couche (20), etc. a une différence de hauteur maximale-minimale, qui est la différence de hauteur entre la hauteur maximale et la hauteur minimale obtenue par mesure d'une irrégularité dans une plage de 20 µm × 20 µm par microscope à force atomique (AFM), qui est établie à 78 nm ou moins. Ainsi, dans une batterie secondaire au lithium-ion stratifiée à film mince utilisant Li3PO4 en tant que électrolyte solide inorganique constituant une couche d'électrolyte solide, une augmentation de la résistance interne et une diminution du taux de rétention de capacité sont toutes deux supprimées.
PCT/JP2019/026269 2018-10-03 2019-07-02 Batterie secondaire au lithium-ion et son procédé de fabrication WO2020070933A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2018-188636 2018-10-03
JP2018188636A JP2020057561A (ja) 2018-10-03 2018-10-03 リチウムイオン二次電池、リチウムイオン二次電池の製造方法

Publications (1)

Publication Number Publication Date
WO2020070933A1 true WO2020070933A1 (fr) 2020-04-09

Family

ID=70055407

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2019/026269 WO2020070933A1 (fr) 2018-10-03 2019-07-02 Batterie secondaire au lithium-ion et son procédé de fabrication

Country Status (2)

Country Link
JP (1) JP2020057561A (fr)
WO (1) WO2020070933A1 (fr)

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07267800A (ja) * 1994-03-25 1995-10-17 Shinkosha:Kk 単結晶の表面処理方法
JPH08274195A (ja) * 1995-03-30 1996-10-18 Mitsubishi Chem Corp 強誘電体ｆｅｔ素子
JP2004063419A (ja) * 2002-07-31 2004-02-26 Matsushita Electric Ind Co Ltd 薄膜の製造方法と電池
JP2012256581A (ja) * 2010-12-02 2012-12-27 Sony Corp 固体電解質電池および正極活物質
JP2013058376A (ja) * 2011-09-08 2013-03-28 Toyota Motor Corp 固体電解質粒子、固体電解質膜、固体電解質粒子の製造方法
JP2016213124A (ja) * 2015-05-12 2016-12-15 トヨタ自動車株式会社 電極積層体
JP2016225281A (ja) * 2015-05-26 2016-12-28 パナソニックＩｐマネジメント株式会社 全固体リチウムイオン二次電池、および、その製造方法
JP2018029046A (ja) * 2016-08-19 2018-02-22 国立大学法人東北大学 全固体リチウム電池および全固体リチウム電池の製造方法
JP2018129159A (ja) * 2017-02-07 2018-08-16 三星電子株式会社Ｓａｍｓｕｎｇ Ｅｌｅｃｔｒｏｎｉｃｓ Ｃｏ．，Ｌｔｄ． 全固体型二次電池用負極及び全固体型二次電池

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH07267800A (ja) * 1994-03-25 1995-10-17 Shinkosha:Kk 単結晶の表面処理方法
JPH08274195A (ja) * 1995-03-30 1996-10-18 Mitsubishi Chem Corp 強誘電体ｆｅｔ素子
JP2004063419A (ja) * 2002-07-31 2004-02-26 Matsushita Electric Ind Co Ltd 薄膜の製造方法と電池
JP2012256581A (ja) * 2010-12-02 2012-12-27 Sony Corp 固体電解質電池および正極活物質
JP2013058376A (ja) * 2011-09-08 2013-03-28 Toyota Motor Corp 固体電解質粒子、固体電解質膜、固体電解質粒子の製造方法
JP2016213124A (ja) * 2015-05-12 2016-12-15 トヨタ自動車株式会社 電極積層体
JP2016225281A (ja) * 2015-05-26 2016-12-28 パナソニックＩｐマネジメント株式会社 全固体リチウムイオン二次電池、および、その製造方法
JP2018029046A (ja) * 2016-08-19 2018-02-22 国立大学法人東北大学 全固体リチウム電池および全固体リチウム電池の製造方法
JP2018129159A (ja) * 2017-02-07 2018-08-16 三星電子株式会社Ｓａｍｓｕｎｇ Ｅｌｅｃｔｒｏｎｉｃｓ Ｃｏ．，Ｌｔｄ． 全固体型二次電池用負極及び全固体型二次電池

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
"RECHARGEABLE LITHIUM BATTERIES. 1st ed.", 20 August 2010, OHMSHA, LTD., pages: 132 - 133 *

Also Published As

Publication number Publication date
JP2020057561A (ja) 2020-04-09

Similar Documents

Publication Publication Date Title
TWI720784B (zh) 電解銅箔、電極及包含其之鋰離子二次電池
JP5169156B2 (ja) 電気化学素子用電極
JP4642835B2 (ja) 電極用集電体
US7794878B2 (en) Negative electrode for lithium secondary battery and lithium secondary battery using the negative electrode
KR101916984B1 (ko) 리튬 이온 이차 전지의 부극재 제조 방법 및 리튬 이온 이차 전지용 부극재
JP4054868B2 (ja) リチウム電池用負極及び該リチウム電池用負極の製造方法
US7482095B2 (en) Anode and battery using the same
JP3922579B2 (ja) 負極および電池
WO2019123981A1 (fr) Procédé de fabrication d'une batterie secondaire au lithium-ion
WO2020137449A1 (fr) Batterie secondaire lithium-ion et procédé destiné à fabriquer une batterie secondaire lithium-ion
WO2019123980A1 (fr) Accumulateur au lithium-ion
WO2020070933A1 (fr) Batterie secondaire au lithium-ion et son procédé de fabrication
JP4329357B2 (ja) リチウム二次電池負極部材、及びその製造方法
WO2020070932A1 (fr) Batterie secondaire au lithium-ion et son procédé de fabrication
JP2019114529A (ja) リチウムイオン二次電池
US7524585B2 (en) Anode and battery using it
WO2020116004A1 (fr) Batterie secondaire au lithium-ion
WO2020012734A1 (fr) Batterie rechargeable au lithium-ion
JP2018181636A (ja) リチウムイオン二次電池およびリチウムイオン二次電池の製造方法
WO2020075352A1 (fr) Accumulateur au lithium-ion et procédé de fabrication d'accumulateur au lithium-ion
WO2019123951A1 (fr) Accumulateur au lithium-ion
JP2008010364A (ja) リチウムイオン二次電池用負極
CN111033856A (zh) 锂离子二次电池、锂离子二次电池的层叠结构、锂离子二次电池的制造方法
JP2005050806A (ja) 負極およびそれを用いた電池

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19869295

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19869295

Country of ref document: EP

Kind code of ref document: A1