WO2019185697A1 - Revêtement à base d'acrylate avec ajout de thiol - Google Patents

Revêtement à base d'acrylate avec ajout de thiol Download PDF

Info

Publication number
WO2019185697A1
WO2019185697A1 PCT/EP2019/057700 EP2019057700W WO2019185697A1 WO 2019185697 A1 WO2019185697 A1 WO 2019185697A1 EP 2019057700 W EP2019057700 W EP 2019057700W WO 2019185697 A1 WO2019185697 A1 WO 2019185697A1
Authority
WO
WIPO (PCT)
Prior art keywords
coating
composition
coating composition
compound
meth
Prior art date
Application number
PCT/EP2019/057700
Other languages
English (en)
Inventor
Tommy Haraldsson
Henrik MIKAELSSON
Carl Fredrik Carlborg
Original Assignee
Mercene Labs Ab
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mercene Labs Ab filed Critical Mercene Labs Ab
Publication of WO2019185697A1 publication Critical patent/WO2019185697A1/fr

Abstract

L'invention concerne un revêtement d'apprêt à base d'acrylate comportant un ajout d'une petite quantité de thiol. Plus particulièrement, la composition de revêtement comprend au moins un composé comprenant au moins un groupe (méth)acrylate et ladite composition de revêtement comprenant au moins un composé comprenant au moins un groupe thiol. Les avantages de l'invention incluent le fait que la résistance à l'usure liée aux impacts à cisaillement élevé est améliorée. En outre, la durée de conservation de la composition de revêtement est améliorée.
PCT/EP2019/057700 2018-03-27 2019-03-27 Revêtement à base d'acrylate avec ajout de thiol WO2019185697A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
SE1850340-9 2018-03-27
SE1850340 2018-03-27

Publications (1)

Publication Number Publication Date
WO2019185697A1 true WO2019185697A1 (fr) 2019-10-03

Family

ID=65991813

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2019/057700 WO2019185697A1 (fr) 2018-03-27 2019-03-27 Revêtement à base d'acrylate avec ajout de thiol

Country Status (1)

Country Link
WO (1) WO2019185697A1 (fr)

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20070021521A1 (en) 2005-07-22 2007-01-25 3M Innovative Properties Company Curable thiol-ene compositions for optical articles
WO2012126695A1 (fr) * 2011-03-23 2012-09-27 Huntsman Advanced Materials (Switzerland) Gmbh Composition thiol-ène durcissable stable
US20160168416A1 (en) 2013-09-06 2016-06-16 Dow Global Technologies Llc Coating composition
US20160222217A1 (en) 2013-09-13 2016-08-04 Basf Se Scratch-resistant radiation-cured coatings
US20160230014A1 (en) * 2013-09-13 2016-08-11 Basf Se Scratch-resistant radiation-cured coatings
WO2017157711A1 (fr) * 2016-03-15 2017-09-21 Arkema France Compositions de revêtement et d'étanchéité durcissables par radicaux libres ayant des propriétés de durcissement de surface améliorées

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US20070021521A1 (en) 2005-07-22 2007-01-25 3M Innovative Properties Company Curable thiol-ene compositions for optical articles
WO2012126695A1 (fr) * 2011-03-23 2012-09-27 Huntsman Advanced Materials (Switzerland) Gmbh Composition thiol-ène durcissable stable
US20160168416A1 (en) 2013-09-06 2016-06-16 Dow Global Technologies Llc Coating composition
US20160222217A1 (en) 2013-09-13 2016-08-04 Basf Se Scratch-resistant radiation-cured coatings
US20160230014A1 (en) * 2013-09-13 2016-08-11 Basf Se Scratch-resistant radiation-cured coatings
WO2017157711A1 (fr) * 2016-03-15 2017-09-21 Arkema France Compositions de revêtement et d'étanchéité durcissables par radicaux libres ayant des propriétés de durcissement de surface améliorées

Similar Documents

Publication Publication Date Title
KR101891835B1 (ko) 저 고스팅 건식 소거 용품 및 그의 사용
TWI568588B (zh) Hard coat film
JP2008516121A (ja) 保護用フィルム磨耗層
JP2009541033A (ja) 耐久性疎水性表面を有する物品
US20190308398A1 (en) Self-healing surface protective film with an acrylate-functional topcoat
KR20070084125A (ko) 보호용 필름 접착제
US20070166536A1 (en) Composite sheet
CA2572279A1 (fr) Substrats souples avec revetements antitache souples et leurs methodes de fabrication et d'utilisation
JP6245705B2 (ja) ハードコート膜形成用組成物、硬化膜、及び帯電防止性物品
JP2010143153A (ja) 木質建材
US10981352B2 (en) Method for producing optical member, and optical member
JP6381354B2 (ja) 活性エネルギー線硬化性樹脂組成物及びコーティング剤組成物
JP6481565B2 (ja) 加飾フィルム用ハードコーティング剤、硬化膜、プラスチックフィルム、及び、成型物
KR102100028B1 (ko) 자외선 경화형 무광 도료 조성물 및 이를 이용한 코팅 필름
WO2019185697A1 (fr) Revêtement à base d'acrylate avec ajout de thiol
JP5057547B2 (ja) 内装材及びその製造方法
JP5902953B2 (ja) 活性エネルギー線硬化型樹脂組成物
JP2006257289A (ja) 樹脂組成物、同樹脂組成物を用いた化粧合板およびその製造方法
JP7223746B2 (ja) 膜形成用の塗布液および膜付基材の製造方法
KR101829714B1 (ko) 표면보호용 열전사필름 및 그 제조방법
JP2007106927A (ja) 床用塗料組成物及びこの塗料にて被覆された床材
CN110325604B (zh) 地板涂料组合物和地板材料
KR20190017130A (ko) 바이오 원료를 사용한 내스팀성이 향상된 자외선 또는 전자빔 경화용 조성물 및 이를 이용한 시트
JP5014634B2 (ja) 帯電防止コーティング剤組成物及びそれを硬化させた被膜
JP5014625B2 (ja) 帯電防止コーティング組成物及びそれを硬化させた被膜

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 19714394

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 19714394

Country of ref document: EP

Kind code of ref document: A1