WO2019031564A1 - Procédé de production de nanofils d'argent, nanofils d'argent, encre à nanofils d'argent et film conducteur transparent - Google Patents

Procédé de production de nanofils d'argent, nanofils d'argent, encre à nanofils d'argent et film conducteur transparent Download PDF

Info

Publication number
WO2019031564A1
WO2019031564A1 PCT/JP2018/029841 JP2018029841W WO2019031564A1 WO 2019031564 A1 WO2019031564 A1 WO 2019031564A1 JP 2018029841 W JP2018029841 W JP 2018029841W WO 2019031564 A1 WO2019031564 A1 WO 2019031564A1
Authority
WO
WIPO (PCT)
Prior art keywords
silver
silver nanowires
polymer
producing
protective agent
Prior art date
Application number
PCT/JP2018/029841
Other languages
English (en)
Japanese (ja)
Inventor
王高 佐藤
Original Assignee
Ｄｏｗａエレクトロニクス株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ｄｏｗａエレクトロニクス株式会社 filed Critical Ｄｏｗａエレクトロニクス株式会社
Priority to CN201880051097.5A priority Critical patent/CN111032257A/zh
Publication of WO2019031564A1 publication Critical patent/WO2019031564A1/fr

Abstract

Le problème décrit par la présente invention est de produire de manière stable des fils particulièrement fins lors de la fabrication de nanofils d'argent par un procédé de réduction utilisant un solvant alcoolique. À cet effet, l'invention concerne un procédé de production de nanofils d'argent qui comprend une étape au cours de laquelle de l'argent est réduit et précipité sous la forme de fils dans un solvant alcoolique, dans lequel sont dissous un composé d'argent et un agent de protection organique. Ce procédé de production de nanofils d'argent est configuré de telle sorte qu'une poudre, qui est principalement composée d'un polymère ayant un motif structural vinylyrrolidone et contient un ester d'acide acétique en une quantité de 0,002 à 0,040 mole pour 1 mole du polymère, est utilisée comme source d'alimentation en agent de protection organique ; et les nanofils d'argent ont un diamètre moyen DM de 30 nm ou moins.
PCT/JP2018/029841 2017-08-09 2018-08-08 Procédé de production de nanofils d'argent, nanofils d'argent, encre à nanofils d'argent et film conducteur transparent WO2019031564A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
CN201880051097.5A CN111032257A (zh) 2017-08-09 2018-08-08 银纳米线的制造方法以及银纳米线、银纳米线墨及透明导电膜

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2017-154737 2017-08-09
JP2017154737A JP6539315B2 (ja) 2017-08-09 2017-08-09 銀ナノワイヤの製造法並びに銀ナノワイヤインクおよび透明導電膜の製造法

Publications (1)

Publication Number Publication Date
WO2019031564A1 true WO2019031564A1 (fr) 2019-02-14

Family

ID=65272006

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2018/029841 WO2019031564A1 (fr) 2017-08-09 2018-08-08 Procédé de production de nanofils d'argent, nanofils d'argent, encre à nanofils d'argent et film conducteur transparent

Country Status (4)

Country Link
JP (1) JP6539315B2 (fr)
CN (1) CN111032257A (fr)
TW (1) TWI686484B (fr)
WO (1) WO2019031564A1 (fr)

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111069626A (zh) * 2020-01-07 2020-04-28 南京信息职业技术学院 一种绿色环保的银纳米线的制备方法及银纳米线薄膜的后处理方法
CN112768113B (zh) * 2020-12-31 2023-06-27 合肥工业大学 一种响应性纳米复合聚合物导电薄膜的制备方法

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016114370A1 (fr) * 2015-01-15 2016-07-21 公立大学法人滋賀県立大学 Nanofil d'argent, procédé de fabrication de celui-ci et encre
JP2016138313A (ja) * 2015-01-27 2016-08-04 星光Pmc株式会社 金属ナノワイヤ成長制御剤、該金属ナノワイヤ成長制御剤を用いて合成された金属ナノワイヤ及び金属ナノワイヤ分散液、並びに金属ナノワイヤ分散液の製造方法

Family Cites Families (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2011140609A (ja) * 2009-04-07 2011-07-21 Seiko Epson Corp 耐水化アルミニウム顔料および耐水化アルミニウム顔料分散液、それらを含有する水性インク組成物、ならびに耐水化アルミニウム顔料分散液の製造方法
GB2486190A (en) * 2010-12-06 2012-06-13 P V Nano Cell Ltd Concentrated dispersion of nanometric silver particles
CN106068166B (zh) * 2014-03-07 2018-10-09 同和控股（集团）有限公司 银纳米线的制造方法和银纳米线及使用该银纳米线的油墨
CN110666154B (zh) * 2014-04-11 2022-02-22 凯姆控股有限公司 控制纳米线形态的方法
CN104874813A (zh) * 2015-05-28 2015-09-02 东华大学 一种超细超长银纳米线的制备方法
JP2017078207A (ja) * 2015-10-20 2017-04-27 公立大学法人 滋賀県立大学 銀ナノワイヤおよびその製造方法並びに分散液およびインク

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2016114370A1 (fr) * 2015-01-15 2016-07-21 公立大学法人滋賀県立大学 Nanofil d'argent, procédé de fabrication de celui-ci et encre
JP2016138313A (ja) * 2015-01-27 2016-08-04 星光Pmc株式会社 金属ナノワイヤ成長制御剤、該金属ナノワイヤ成長制御剤を用いて合成された金属ナノワイヤ及び金属ナノワイヤ分散液、並びに金属ナノワイヤ分散液の製造方法

Also Published As

Publication number Publication date
JP6539315B2 (ja) 2019-07-03
CN111032257A (zh) 2020-04-17
TW201917220A (zh) 2019-05-01
JP2019031726A (ja) 2019-02-28
TWI686484B (zh) 2020-03-01

Similar Documents

Publication Publication Date Title
JP6703802B2 (ja) 銀ナノワイヤおよびその製造方法並びにインク
JP6526739B2 (ja) 銀ナノワイヤおよびその製造法並びに銀ナノワイヤインクおよび透明導電膜
JP2017078207A (ja) 銀ナノワイヤおよびその製造方法並びに分散液およびインク
KR20160129895A (ko) 은나노 와이어의 제조 방법 및 은나노 와이어 및 이를 사용한 잉크
TWI665037B (zh) 銀奈米線及該銀奈米線之製造方法，以及銀奈米線墨水
JP2017082305A (ja) 銀ナノワイヤおよびその製造方法並びに分散液
JP6539315B2 (ja) 銀ナノワイヤの製造法並びに銀ナノワイヤインクおよび透明導電膜の製造法
KR20190128670A (ko) 은 나노와이어 잉크의 제조 방법 및 은 나노와이어 잉크 및 투명 도전 도막
JP2019147983A (ja) 銀ナノワイヤ合成用有機保護剤並びに銀ナノワイヤおよびその製造方法
TWI696669B (zh) 銀奈米線的製造法和銀奈米線、銀奈米線印墨及透明導電膜
JP2020158857A (ja) 銀ナノワイヤの製造法
JP2020158858A (ja) 銀ナノワイヤの製造法
TWI697526B (zh) 銀奈米線的製造法和銀奈米線、銀奈米線印墨及透明導電膜
JP2018070946A (ja) 銀ナノワイヤ合成用有機保護剤並びに銀ナノワイヤおよびその製造方法
WO2020175255A1 (fr) Nanofils d'argent, leur procédé de production, solution réactionnelle contenant des nanofils d'argent et dispersion de nanofils d'argent
JP2010260994A (ja) 金属含有ブロック共重合体及びその製造方法

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 18845107

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 18845107

Country of ref document: EP

Kind code of ref document: A1