WO2018066633A1 - Oxyde composite de lithium manganèse substitué par du titane et/ou du germanium et son procédé de production - Google Patents

Oxyde composite de lithium manganèse substitué par du titane et/ou du germanium et son procédé de production Download PDF

Info

Publication number
WO2018066633A1
WO2018066633A1 PCT/JP2017/036223 JP2017036223W WO2018066633A1 WO 2018066633 A1 WO2018066633 A1 WO 2018066633A1 JP 2017036223 W JP2017036223 W JP 2017036223W WO 2018066633 A1 WO2018066633 A1 WO 2018066633A1
Authority
WO
WIPO (PCT)
Prior art keywords
lithium
compound
composite oxide
discharge
charge
Prior art date
Application number
PCT/JP2017/036223
Other languages
English (en)
Japanese (ja)
Inventor
田渕　光春
京介 堂前
英香 渋谷
田村　宜之
亮太 弓削
直樹 河野
Original Assignee
国立研究開発法人産業技術総合研究所
株式会社田中化学研究所
日本電気株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 国立研究開発法人産業技術総合研究所, 株式会社田中化学研究所, 日本電気株式会社 filed Critical 国立研究開発法人産業技術総合研究所
Priority to JP2018543956A priority Critical patent/JP7048944B2/ja
Publication of WO2018066633A1 publication Critical patent/WO2018066633A1/fr

Abstract

Un oxyde composite de lithium manganèse représenté par la formule générale (1) Li1+x(M1 yM2 zMn1-y-z)1-xO2 (dans laquelle M1 représente Fe et/ou Ni; M2 représente Ti et/ou Ge; et x, y et z satisfont 0 < x < 1/3, 0 ≤ y ≤ 0,4 et 0 < z ≤ 0,3) et contenant une phase cristalline ayant une structure de sel gemme stratifiée monoclinique ou une structure de sel gemme stratifiée hexagonale, est un nouveau matériau qui a peu de contraintes de ressources et utilise des éléments à faible coût, tout en obtenant une haute capacité et une haute tension de décharge et présentant d'excellentes caractéristiques de cycle à long terme pour maintenir la similarité des formes des courbes de charge/décharge pendant les cycles de charge/décharge s'il est utilisé pour un matériau d'électrode positive pour batteries secondaires au lithium-ion.
PCT/JP2017/036223 2016-10-07 2017-10-05 Oxyde composite de lithium manganèse substitué par du titane et/ou du germanium et son procédé de production WO2018066633A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2018543956A JP7048944B2 (ja) 2016-10-07 2017-10-05 チタン及び／又はゲルマニウム置換リチウムマンガン系複合酸化物及びその製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2016-199187 2016-10-07
JP2016199187 2016-10-07

Publications (1)

Publication Number Publication Date
WO2018066633A1 true WO2018066633A1 (fr) 2018-04-12

Family

ID=61831375

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2017/036223 WO2018066633A1 (fr) 2016-10-07 2017-10-05 Oxyde composite de lithium manganèse substitué par du titane et/ou du germanium et son procédé de production

Country Status (2)

Country Link
JP (1) JP7048944B2 (fr)
WO (1) WO2018066633A1 (fr)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2018085311A (ja) * 2016-11-25 2018-05-31 日立造船株式会社 全固体電池用正極活物質およびこれを具備する正極の製造方法ならびに全固体電池用正極およびこれを具備する全固体電池
WO2019235573A1 (fr) * 2018-06-06 2019-12-12 国立研究開発法人産業技術総合研究所 Oxyde composite à base de lithium-manganèse et son procédé de production

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2009274940A (ja) * 2008-05-19 2009-11-26 National Institute Of Advanced Industrial & Technology 陽イオン規則構造を有する単斜晶系リチウムマンガン系複合酸化物およびその製造方法
WO2015025844A1 (fr) * 2013-08-23 2015-02-26 日本電気株式会社 Oxyde composite à base de lithium-fer-manganèse et cellule secondaire au lithium-ion l'utilisant
WO2015025721A1 (fr) * 2013-08-23 2015-02-26 日本電気株式会社 Matériau d'électrode positive pour batterie au lithium-ion, son procédé de fabrication et batterie au lithium-ion l'utilisant

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2009274940A (ja) * 2008-05-19 2009-11-26 National Institute Of Advanced Industrial & Technology 陽イオン規則構造を有する単斜晶系リチウムマンガン系複合酸化物およびその製造方法
WO2015025844A1 (fr) * 2013-08-23 2015-02-26 日本電気株式会社 Oxyde composite à base de lithium-fer-manganèse et cellule secondaire au lithium-ion l'utilisant
WO2015025721A1 (fr) * 2013-08-23 2015-02-26 日本電気株式会社 Matériau d'électrode positive pour batterie au lithium-ion, son procédé de fabrication et batterie au lithium-ion l'utilisant

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
TABUCHI, M. ET AL.: "Stepwise charging and calcination atmosphere effects for iron and nickel substituted lithium manganese oxide positive electrode material", JOURNAL OF POWER SOURCES, vol. 313, 4 March 2016 (2016-03-04), pages 120 - 127, XP029474017, DOI: doi:10.1016/j.jpowsour.2015.12.008 *

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2018085311A (ja) * 2016-11-25 2018-05-31 日立造船株式会社 全固体電池用正極活物質およびこれを具備する正極の製造方法ならびに全固体電池用正極およびこれを具備する全固体電池
WO2019235573A1 (fr) * 2018-06-06 2019-12-12 国立研究開発法人産業技術総合研究所 Oxyde composite à base de lithium-manganèse et son procédé de production
JPWO2019235573A1 (ja) * 2018-06-06 2021-07-08 国立研究開発法人産業技術総合研究所 リチウムマンガン系複合酸化物及びその製造方法
JP7302826B2 (ja) 2018-06-06 2023-07-04 国立研究開発法人産業技術総合研究所 リチウムマンガン系複合酸化物及びその製造方法

Also Published As

Publication number Publication date
JPWO2018066633A1 (ja) 2019-07-25
JP7048944B2 (ja) 2022-04-06

Similar Documents

Publication Publication Date Title
JP4963059B2 (ja) チタン及びニッケル含有リチウムマンガン系複合酸化物
JP5263761B2 (ja) 陽イオン規則構造を有する単斜晶系リチウムマンガン系複合酸化物およびその製造方法
JP5158787B2 (ja) 新規チタン酸化物及びその製造方法、並びにそれを活物質として用いたリチウム二次電池
EP1837937B1 (fr) Oxyde composite à base de manganèse au lithium et son procédé de préparation
JP6119003B2 (ja) リチウムマンガン系複合酸化物およびその製造方法
WO2012132155A1 (fr) Poudre de particules d&#39;oxyde composite à base de manganèse-nickel, procédé de production associé, poudre de particules de matériau actif d&#39;électrode positive destinée à des batteries secondaires à électrolyte non aqueux, procédé de production associé, et batterie secondaire à électrolyte non aqueux
JP5516926B2 (ja) 規則構造を有する単斜晶系リチウムマンガン系複合酸化物およびその製造方法
JP5958926B2 (ja) リチウムマンガン系複合酸化物およびその製造方法
JP3922040B2 (ja) リチウムマンガン複合酸化物とその製造方法並びにその用途
JP5673932B2 (ja) 立方晶岩塩型構造を有するリチウムマンガン系複合酸化物およびその製造方法
JP4997609B2 (ja) リチウムマンガン系複合酸化物の製造方法
JP6872816B2 (ja) ニッケルマンガン系複合酸化物及びその製造方法
WO2018096999A1 (fr) Oxyde complexe de lithium-manganèse et son procédé de production
JP4457213B2 (ja) リチウムフェライト系複合酸化物の製造方法
WO2018066633A1 (fr) Oxyde composite de lithium manganèse substitué par du titane et/ou du germanium et son procédé de production
KR20080088177A (ko) 리튬 이차전지용 스피넬형 양극 활물질 및 그 제조방법
JP7128475B2 (ja) リチウムマンガン系複合酸化物及びその製造方法
JP4734672B2 (ja) リチウム−鉄−マンガン複合酸化物の製造方法
KR20050047291A (ko) 리튬이차전지용 양극 활물질 및 그 제조방법
KR101383681B1 (ko) 리튬망간산화물 전극재료 제조방법, 그 방법으로 제조된 리튬망간산화물 전극재료, 및 상기 전극재료를 포함하는 2차 전지
JP7192397B2 (ja) リチウム－コバルト－マンガン系複合酸化物及びこれを含むリチウム二次電池
JP7133215B2 (ja) ニッケルマンガン系複合酸化物及びその製造方法
JP3968420B2 (ja) 立方晶岩塩型リチウムフェライト系複合酸化物およびその製造方法

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2018543956

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 17858469

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 17858469

Country of ref document: EP

Kind code of ref document: A1