Classifications

• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J11/00—Features of adhesives not provided for in group C09J9/00, e.g. additives
  • C09J11/02—Non-macromolecular additives
  • C09J11/06—Non-macromolecular additives organic
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08G—MACROMOLECULAR COMPOUNDS OBTAINED OTHERWISE THAN BY REACTIONS ONLY INVOLVING UNSATURATED CARBON-TO-CARBON BONDS
  • C08G59/00—Polycondensates containing more than one epoxy group per molecule; Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups
  • C08G59/18—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing
  • C08G59/68—Macromolecules obtained by polymerising compounds containing more than one epoxy group per molecule using curing agents or catalysts which react with the epoxy groups ; e.g. general methods of curing characterised by the catalysts used
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J11/00—Features of adhesives not provided for in group C09J9/00, e.g. additives
  • C09J11/02—Non-macromolecular additives
  • C09J11/04—Non-macromolecular additives inorganic
• • C—CHEMISTRY; METALLURGY
  • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
  • C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
  • C09J163/00—Adhesives based on epoxy resins; Adhesives based on derivatives of epoxy resins
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B6/00—Light guides; Structural details of arrangements comprising light guides and other optical elements, e.g. couplings
  • G02B6/24—Coupling light guides
  • G02B6/26—Optical coupling means
  • G02B6/264—Optical coupling means with optical elements between opposed fibre ends which perform a function other than beam splitting
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K3/00—Use of inorganic substances as compounding ingredients
  • C08K3/34—Silicon-containing compounds
  • C08K3/36—Silica
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/01—Hydrocarbons
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/02—Halogenated hydrocarbons
  • C08K5/03—Halogenated hydrocarbons aromatic, e.g. C6H5-CH2-Cl
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/04—Oxygen-containing compounds
  • C08K5/07—Aldehydes; Ketones
  • C08K5/08—Quinones
• • G—PHYSICS
  • G02—OPTICS
  • G02B—OPTICAL ELEMENTS, SYSTEMS OR APPARATUS
  • G02B6/00—Light guides; Structural details of arrangements comprising light guides and other optical elements, e.g. couplings
  • G02B6/24—Coupling light guides
  • G02B6/255—Splicing of light guides, e.g. by fusion or bonding

Definitions

• the present invention relates to a blue light curing optical adhesive having a cure time less than 60 seconds.
• the exemplary optical adhesive can be used in the signal transmission path of an optical fiber network.
• optical fibers As the world demand for data continues to increase, more data is transmitted optically through indoor/outdoor cables using optical fibers, to deliver fiber to the home (FTTH), within the data center, central office or enterprise environments, as well as in fiber fed backhaul applications for wireless transmission or fiber to the antenna (FTTA) applications.
• FTTH fiber to the home
• FTTA fiber fed backhaul applications for wireless transmission or fiber to the antenna
• ferrule based connectors such as SC, LC, MT format optical fiber connectors will be used, due to their durable construction.
• permanent joints or splices are used to join optical fibers where the lowest optical loss is required.
• Conventional optical fiber splicing technologies include fusion splicing and mechanical splicing.
• Fusion splicing utilizes an arc to fuse or melt the ends of two optical fibers together.
• the splicing machines are expensive ($3,000-$10,000), fragile instruments, operated by specially trained technicians. Proper use, results in a reliable low optical loss joint. Fusion splicing is especially attractive where large numbers of fibers need to be spliced at a given location.
• Mechanical splice uses a mechanical structure to align and clamp two optical fiber ends, resulting in a low-cost installed splice. It can be challenging to prepare and mate optical fiber ends in a mechanical splice and have intimate glass to glass contact every time.
• industry standard cleavers deliver +/-1 degree cleave angle on the end face of an optical fiber.
• a small air gap can occur between the active portions of the optical fibers.
• an index match gel is used at the fiber joint to enhance the optical performance of mechanical splices.
• Common mechanical splices use substrate materials with a higher coefficient of thermal expansion (CTE) greater than the glass (silica) in the optical fibers core and cladding.
• Substrate examples are polyether imide materials and aluminum. CTE mismatch during thermal loading can cause the gap between the fiber tips to change with temperature, which can place demand on the index matching gel to flow and fill this variable gap.
• Typical index matching gels are a thixotropic blend of silicone oil loaded with micron sized fumed silica particles.
• the index matching gel is selected to match the index of refraction of silica at room temperatures. Their thixotropic nature allows the index matching gels to be sheared so that the can be dispensed into the mechanical splice, but prevent the gels flowing or wicking out of the gap between the ends of the optical fibers.
• the index matching gels have a higher dn/dT (i.e. the change of refractive index with temperature) than silica resulting in refractive index mismatch at temperature extremes. This index of refraction mismatch at the fiber to gel interface, causes a predictable, repeatable, slight reflection signal response that varies with temperature.
• an adhesive composition for joining optical components comprises at least one epoxy resin, a visible light photoinitiating system, a polyol and at least 50 wt.% of a nanoparticle filler.
• the visible light photoinitiating system includes at least one of a cationic photoinitiator and a sensitizer and the nanoparticle filler comprises a first nanoparticle having a first nominal size and a second nanoparticle having a second size.
• the adhesive composition has a refractive index between 1.44 and 1.485 and a dn/dT of less than -2E-4 when cured.
• an adhesive composition for joining optical components comprises 5 wt.% - 49.9 wt.% of at least one epoxy resin, 0.1 wt.% - 30 wt.% of a polyol, a visible light photoinitiating system
• the adhesive composition has a refractive index between 1.44 and 1.485 and a dn/dT of less than -2E-4 when cured.
• the exemplary adhesive may be used to join at least one optical fiber to a second optical signal transfer media.
• the second signal transfer media may be a second optical fiber, an optical wave guide, a lens and/or an opto-electric transceiver.
• the interconnection point between the at least one optical fiber to a second optical signal transfer media may be used in either an indoor or an outdoor environment.
• the exemplary adhesive When the exemplary adhesive is used to interconnect two optical fibers it will result in a permanent optical fiber splice. In this configuration, some of the adhesive may be disposed in the optical signal path.
• the exemplary adhesive should have high optical transmission (>98%) at the wavelength of the signal to be carried by the optical fiber and should be index matched to core of the optical fiber +/- 0.5%, preferably +/- 0.1% of the index of the core of the fiber to reduce signal losses due to back reflection.
• the telecommunication wavelengths are 850 nm and 1300 nm, and for single mode optical fiber, the telecommunication wavelength band about is 1250 nm - 1675 nm.
• the adhesive bond is desirably thermally stable.
• the adhesive bond desirably does not allow movement of the optical fibers under a mechanical load.
• the fiber retention of the adhesive should be at least 1.5 lbs.
• the exemplary adhesive should have a low dn/dT so that adhesive remains index matched to the optical fibers over the outside plant temperature conditions.
• the adhesive should have a low thermal expansion (i.e. less than 45 ppm, preferably less than 35 ppm) and a glass transition temperature of at least 50°C, preferably greater than about 70°C, more preferably greater than about 90°C.
• the exemplary adhesive will be used to join two optical fibers in a splice device.
• An exemplary splice device may include an alignment element having a base plate and a clamp plate, wherein at least one of the base plate and clamp plate having an alignment groove configured to receive the first and second optical fibers in an end-to-end manner, as described in copending US Patent Application No. 15/695842, herein incorporated by reference in its entirety.
• the exemplary adhesive can be disposed in at least a portion of the alignment groove.
• the exemplary adhesive should meet the fiber pullout strength requirements of the outside plant optical fiber splice standard, without requiring a long-term external mechanical clamp to hold the splice plates of the exemplary splice device.
• the adhesive can be preloaded into the splice device at the factory, eliminating need for field craft to mix or dispense.
• the rheology of the uncured exemplary adhesive should be such that the adhesive does not migrate prior to the creation of the optical fiber splice and curing of the adhesive. Because the exemplary device may be made in the field, the tools requires to activate the cure of the adhesive must be simple and safe to use in the field. As a result, UV curable and thermally curable adhesive formulations are undesirable.
• the adhesive is curable by light of wavelengths from about 400 nm to about 700 nm, preferably from about 400 nm to about 600 nm, which includes a portion of the blue and green area of the spectrum, most preferably more preferably between 430 nm to about 480 nm.
• adhesive compositions of the current disclosure can be epoxy based adhesives that utilize a blue light curing mechanism to cure the adhesive.
• These exemplary adhesives offer the advantages of rapid cure (less than 60 seconds, preferably less than 45 seconds, more preferably less than 30 seconds) while avoiding the mixing, dispensing and heating required by
• the exemplary adhesives described herein can be used to make a splice connection that meet standard indoor performance requirements, such as TIA 568.3-D.
• Exemplary light sources for curing the adhesive compositions described herein can have an output density from about 500 mW/cm 2 to about 3000 mW/cm 2 and may include a
• the LED light source provides not only the photonic initiation of the polymerization reaction, but can also have sufficient energy to photonically heat the bonding area, enabling the adhesive to achieve a higher glass transition temperature (Tg) than can be generated by the photonic initiation alone.
• Tg glass transition temperature
• the higher Tg of the adhesive can create more stable optical splices when used to bond optical fibers in an optical splice device, allowing the resulting splice connections to pass more rigorous environmental stress tests.
• the LED array will have a wavelength that is optimized for material curing and modification.
• Various form factors and features may include an LED array curing device designed to be a portable, hand held unit, for example, an LED light pen, an LED array, etc. to cover a targeted area (e.g. radial, segmented, and organic shapes). Selective control of particular LEDs in the array permits smaller material regions to be exposed.
• the thermal flux can be managed by a large surface area heat sink and/or forced air flow through the array.
• the LEDs can be arranged in a one-dimensional array, while in other aspects, the LEDs can be arranged in a two-dimensional array. In an exemplary aspect, the LEDs can be arranged in a plurality of banks or strips that are then configured into a two- dimensional array to allow selective exposure over a given cure region. LEDs can be arranged in a regular array with uniform spacing, for example with linear, hexagonal or other geometric placement to maximize light uniformity, minimize number of LEDs used, or for other reasons.
• an array of LEDs may be configured to be evenly distributed over the area intended to be cured, plus a reasonable perimeter, from a small fraction of the total area, to several times the total area, to insure uniform curing of a sample from center to edges.
• the exemplary adhesive can be cured using an LED array curing source after about a 60 second exposure, preferably after about a 30 second exposure.
• the exemplary adhesives are highly filled to reduce the thermal expansion of the cured adhesive and lower the dn/dT of the adhesives.
• adhesives that have a low coefficient of thermal expansion which incorporate conventional fillers such as alumina, quartz or other inorganic particles. These conventional fillers are unacceptable for applications where optical transmission through the adhesive is required. Because the average size of these fillers is generally larger than optical wavelengths (e.g., wavelengths in the visible or infrared regions of the electromagnetic spectrum), the fillers scatter the light and prevent the transmission of the light through the adhesive.
• optical wavelengths e.g., wavelengths in the visible or infrared regions of the electromagnetic spectrum
• the need for a low refractive index can preclude the use of common phenol based epoxy materials such diglycidyl ethers of bisphenol A, diglycidyl ethers of bisphenol F, novolac epoxy resins, resorcinol based epoxy resins, etc.
• Suitable epoxy resins for use in the exemplary adhesive should have a refractive index less than about 1.53 and can include monomeric or oligomeric epoxy compounds that can be aliphatic, alicyclic, or heterocyclic.
• the mixture of resins should have a refractive index less than 1.50.
• the terms "epoxy resin” and "epoxide” and "epoxy-containing material” are used interchangeably.
• epoxy-containing materials generally have, on the average, more than 1 polymerizable epoxy group per molecule. Some epoxy resins have at least 1.5 or at least 2 polymerizable epoxy groups per molecule.
• the average molecular weight of the epoxy-containing materials can vary from about 58 g/mole to about 1000 g/mole or more.
• epoxy resins include vinylcyclohexene dioxide; 3,4- epoxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate; bis(3,4-epoxy-6- methylcyclohexylmethyl) adipate; bis(2,3-epoxycyclopentyl) ether; aliphatic epoxy modified from polypropylene glycol; dipentene dioxide; epoxy functional silicone containing resins; bis(3,4-epoxycyclohexyl)adipate; 2-(3,4-epoxycyclohexyl-5,5-spiro-3,4-epoxy) cyclohexane- meta-dioxane; vinylcyclohexene monoxide; polyfunctional glycidyl ethers such as diglycidyl ether of 1,4-butanediol; diglycidyl ether of neopentyl glycol; diglycidyl ether of
• Still other useful epoxy resins include epoxy -functional silicones such as those described in U.S. Patent No. 4,279,717 (Eckberg et al.), which are commercially available from the
• epoxy resins are polydimethylsiloxanes in which 1 to 20 mole percent of the silicon atoms have been substituted with epoxyalkyl groups (preferably, epoxy cyclohexylethyl, as described in U.S. Patent No. 5,753,346 (Leir et al.)).
• epoxyalkyl groups preferably, epoxy cyclohexylethyl, as described in U.S. Patent No. 5,753,346 (Leir et al.)
• Some exemplary materials can include l,3-di[2-(3,4-epoxycyclohexyl)ethyl]-l, l,3,3-tetramethyldisiloxane and epoxypropoxypropyl terminated polydimethysiloxane.
• the adhesive composition contains at least 25 wt.%, at least 30 wt.%, at least 35 wt.% or at least 40 weight percent epoxy resin based on the weight of the adhesive composition.
• Some adhesive compositions contain, up to 45 wt.%, or up to 40 wt.% epoxy resin.
• the adhesive compositions can contain 25 wt.% to 45 wt.%, 30 wt.% to 45 wt.%, 25 wt.% to 40 wt.%, or 30 wt.% to 40 wt.% epoxy resin based on the weight of the adhesive composition.
• the adhesive composition can further include a polyol in addition to the epoxy resin.
• a polyol refers to an organic compound having two or more hydroxy groups.
• the polyol can be added as a chain extender for the epoxy resin and can be a source of protons for the cationic polymerization reaction.
• any process used to remove water and the optional water-miscible solvent is conducted either prior to the addition of the polyol or under conditions that do not remove the polyol.
• Suitable diols include, but are not limited to, 1,2- ethanediol, 1,2-propanediol, 1,3-propanediol, 1,4-butanediol, 1,3-butanediol, 2-methyl-l,3- propanediol, 2,2-dimethyl- 1,3 -propanediol, 2-ethyl-l,6-hexanediol, 1,5-pentanediol, 1,6- hexanediol, 1,8-octanediol, neopentyl glycol, glycerol, trimethylolpropane, 1,2,6-hexanetriol, trimethylolethane, pentaerythritol, quinitol, mannitol, sorbitol, diethylene glycol, triethylene glycol, tetraethylene
• the polyol When a polyol is present in the adhesive composition, the polyol is typically present in an amount, up to 30 wt.%, up to 20 wt.%, up to 10 wt.%, or up to 5 wt.% based on the weight of the adhesive composition.
• the polyol can be present in an amount of at least 0.5 wt.%, at least 1 wt.%), at least 2 wt.%>, or at least 3 wt.%> based on the weight of the adhesive composition.
• the polyol is often present in an amount of 0.5 wt.%> to 10 wt.%>, 1 wt.%> to 10 wt.%>, 0.5 wt.%> to 5 wt.%), or 1 wt.%) to 5 wt.%) based on the weight of the adhesive composition.
• the adhesive composition contains surface-modified nanoparticles, in particular surface- modified silica nanoparticles.
• the surface-modified nanoparticles are added to the exemplary adhesive to modify the adhesive' s mechanical, thermal and optical properties.
• the surface-modified nanoparticles can be added to the adhesive to reduce the coefficient of thermal expansion (CTE) of the adhesive.
• CTE coefficient of thermal expansion
• the CTE of an unfilled epoxy can be greater than
• the CTE of the adhesive should be as low as possible so that the adhesive does not exert undue forces on the fiber due to changing temperature which could result in signal loss or breakage of the optical fiber.
• the adhesive needs to be highly loaded with a filler having a low CTE.
• the addition of high levels of nanoparticles can have a detrimental effect on the rheology of the particle-loaded adhesive which can make it difficult to dispense or complicate insertion of the fiber into the adhesive.
• the viscosity of a resin system can become excessively high, even to the point of becoming gel- like. It is well-known that the smaller the nanoparticle size, the lower the particle loading must be to avoid excessive viscosity build.
• the presence of nanoparticles can lead to viscosity increases with increases in temperature, shear rate, or both.
• some embodiments of the exemplary adhesive composition may contain a combination of two different sized, surface-modified silica nanoparticles, or in other words comprises a bimodal distribution of surface-modified silica nanoparticles.
• surface modified nanoparticles refer to the attachment of surface treatment agents into the surface of the nanoparticle.
• nanoparticles used in the present adhesive formulations refer to particles having an average diameter no greater than 500 nm.
• the term “diameter” refers not only to the diameter of substantially spherical particles but also to the longest dimension of non-spherical particles. Note that the particle sizes referred to herein are the nominal sizes provided by the vendor.
• the term "bimodal distribution of surface-modified silica nanoparticles” refers to a collection of particles having particles with two primary sizes.
• the bimodal distribution of the surface-modified nanoparticles can have first particles having a first average particle size, Dl, between 70 nm and 200 nm, inclusive.
• the first average particle size of the first particles is at least 70 nm, at least 80 nm, or even at least 90 nm.
• the first average particle size of the first particles is no greater than 200 nm, or no greater than 150 nm.
• the bimodal distribution of the surface-modified nanoparticles of the present disclosure also includes second particles having a second average particle size.
• the second average diameter, D2, of the second particles is less than the first average diameter of the first particles (i.e. D2 ⁇ D1).
• the second average particle size of the second particles is no greater than 60 nm, e.g., no greater than 50 nm, or no greater than 30 nm.
• D2 is at least 5 nm, e.g., at least 10 nm. In some embodiments, D2 is between 15 and 60 nm, inclusive.
• the sizes of the first and second particles are defined relative to each other such that the first average particle size of the first particles, Dl, is greater than the second average particle size of the second particles, D2.
• the ratio of the first average particle size of the first particles to the second average particle size of the second particles, D1 :D2 is at least 2: 1.
• the ratio of D1 :D2 is no greater than 30: 1, preferably 7: 1.
• the ratio of Dl :D2 is between 2: 1 and 7: 1.
• the weight percent of nanoparticles in the adhesive composition is based on all nanoparticles present in the adhesive composition. Generally, the percent by weight of nanoparticles is based on the combined weight of the resin component and the nanoparticles in the adhesive composition, and is no greater than 80 wt.%. In some embodiments, the adhesive composition contains at least at least 40 wt.% of nanoparticles.
• nanoparticles in adhesive compositions are of particular interest when working in optical communication applications. Because the wavelengths of light used in optical communication applications are longer than the diameter of the silica nanoparticles (e.g., the wavelengths used are often about 10 to 20 times longer than the average diameter of the silica nanoparticles), the silica nanoparticles typically do not scatter the optical signal when it passes through an adhesive with nanoparticles. More particularly, the silica nanoparticles usually allow high transmission of visible and infrared wavelengths of light through the adhesive.
• Suitable silica nanoparticles are often available in the form of a sol, which is a colloidal dispersion of amorphous silica nanoparticles in a liquid medium.
• the liquid medium can be water, an organic solvent, or water/organic solvent mixture.
• the silica nanoparticles preferably have a relatively uniform size (i.e., diameter) and remain non-aggregated in the liquid medium, (i.e. less than 1 wt.%, less than 0.5 wt.%, or less than 0.2 wt.% of the silica nanoparticles in the adhesive composition are aggregated).
• non-aggregated means that the silica nanoparticles or the surface-modified silica nanoparticles are substantially free of aggregated nanoparticles, which refers to clusters or clumps or nanoparticles that are firmly associated with one another and that can typically only be separated with high shear. Particle aggregation can result in precipitation, gelation, a substantial viscosity increase, or light scattering in the final adhesive composition.
• Silica hydrosols having water as the liquid medium, are commercially available in a variety of particle sizes and concentrations from Nyacol Products, Inc. (Ashland, MD), Nalco Chemical Co. (Naperville, IL), and DuPont Chemical Co. (Wilmington, DE).
• the concentration of silica nanoparticles is often in the range of 10 to 50 wt.% based on the weight of the hydrosol. Concentrations of silica nanoparticles in the range of 30 to 50 wt.% based on the weight of the hydrosol are often preferred because less water needs to be removed after surface modification.
• the silica nanoparticles are surface modified using a surface modification mixture that contains (a) silica nanoparticles, (b) a silane surface modifying agent in a sufficient amount to form a monolayer on the surface of the silica nanoparticles, (c) an excess amount of water, and (d) an optional water-miscible solvent.
• a surface modification mixture that contains (a) silica nanoparticles, (b) a silane surface modifying agent in a sufficient amount to form a monolayer on the surface of the silica nanoparticles, (c) an excess amount of water, and (d) an optional water-miscible solvent.
• the silica nanoparticles are typically non-aggregated and usually have a monolayer of the surface- modifier covalently attached to the surface.
• Suitable silane surface modifying agents include, but are not limited to,
• alkyltrialkoxysilanes such as methyltrimethoxysilane, methyltriethoxysilane,
• ethyltrimethoxysilane ethyltriethoxysilane
• n-propyltrimethoxysilane n-propyltriethoxysilane
• iso-propyltrimethoxysilane iso-propyltriethoxysilane, butyltrimethoxysilane
• butyltriethoxysilane hexyltrimethoxysilane, n-octyltrimethoxysilane, n-octyltriethoxysilane, isooctyltrimethoxysilane, dodecyltrimethoxysilane, and octadecyltrimethoxysilane; aryltrialkoxysilanes such as styrylethyltrimethoxysilane, phenyltrimethoxysilane, phenyltriethoxysilane, and p-tolyltriethoxysilane; 3-glycidoxypropyltrialkoxysilane such as glycidoxypropyltrimethoxysilane; alkyltrichlorosilanes such as methyltrichlorosilane;
• aryltrichlorosilanes such as phenyltrichlorsilane, phenylethyltrichlorosilane,
• the surface modification mixture contains water and an optional water-miscible solvent.
• Suitable optional water-miscible solvents include, but are not limited to, alcohols (e.g., methanol, ethanol, n-propanol, isopropanol, l-methoxy-2-propanol, or butanol), ethers (e.g., diethyl ether or tetrahydrofuran), dimethylformamide, dimethylsulfoxide, acetonitrile, and the like.
• the optional water-miscible solvent is typically chosen to have a boiling point that allows removal at a temperature suitable for removal of the water.
• the volume ratio of water to water-miscible solvent is at least 99: 1 (i.e., 99 parts of water to 1 part water-miscible solvent), at least 98:2, at least 95:5, at least 90: 10, at least 85: 15, at least 80:20, at least 75:25, at least 70:30, at least
• the optional water-miscible solvent can be used to increase the solubility of the surface modifying agent.
• Suitable reaction conditions for covalently bonding the surface modification agent to the surface of the silica nanoparticles can vary depending on the presence or absence of a water-miscible solvent, the nature of the water-miscible solvent, and the presence or absence of a catalyst to accelerate the reaction.
• the catalyst can include, but is not limited to, ammonia, amines and fluoride ions.
• the surface-modified silica nanoparticles are dispersed in an epoxy resin. At least most of the water and optional water-miscible solvent in the surface-modification mixture is removed by evaporation or distillation. The removal of the water and optional water-miscible solvent can occur either before or after addition of the epoxy resin (i.e., either before or after formation of the dispersion). Suitable methods of removing the water and optional water-miscible solvent include, but are not limited to, rotary evaporation, thin film evaporation, simple distillation, azeotropic distillation, gap drying, or spray drying.
• the adhesive composition often contains at least 50 wt.%, at least 55 wt.%, at least 60 wt.%), or at least 65 wt.%> surface- modified silica nanoparticles based on the weight of the adhesive composition.
• Some adhesive compositions contain up to 75 wt.%, up to 70 wt.%, or up to 80 wt.%) surface-modified silica nanoparticles.
• the adhesive composition can contain 50 to 75 wt.%, 50 to 70 wt.%, 55 to 70 wt.%, 55 to 75 wt.%, 55 to 80 wt.%, 60 to 70 wt.%, 60 to 75 wt.%, 60 to 80 wt.%, 65 to 70 wt.%, 65 to 75wt.%, or 65 to 80 wt.% surface- modified silica nanoparticles.
• the photoinitiator system can initiate the cationic polymerization of the exemplary adhesive formulation and more preferably will accelerate the polymerization.
• the photoinitiator system is one which is capable of light absorption in the visible range, i.e., between about 400 nm and about 700 nm. In preferred assemblies of the invention, the photoinitiator system absorbs light between about 400 nm and about 600 nm, more preferably between 430 nm to about 480 nm, in the blue portion of the spectrum.
• Components in the photoinitiator system include at least one initiator, at least one sensitizer, and optionally, an electron donor.
• Useful sensitizers should be soluble in the epoxy monomers, capable of light absorption in the appropriate wavelengths, and shelf stable for reasonable periods of time.
• Suitable sensitizers are believed to include compounds in the following categories:
• ketones coumarin dyes (e.g., keto-coumarins), xanthene dyes, acridine dyes, thiazole dyes, thiazine dyes, oxazine dyes, azine dyes, aminoketone dyes, porphyrins, aromatic polycyclic hydrocarbons, p-substituted aminostyryl ketone compounds, aminotriaryl methanes,
• Ketones e.g., monoketones or
• sensitizers are preferred sensitizers.
• a sensitizer containing a julolidinyl moiety For applications requiring deep cure (e.g., where the adhesive or the substrates attenuate radiation of similar wavelengths), it is preferred to employ sensitizers having an extinction coefficient below about 1000, more preferably below about 100, at the desired wavelength of irradiation for photopolymerization.
• Suitable ketones of the above formula include monoketones such as 2,2- dihydroxybenzophenone, 4,4-dihydroxybenzophenone, or 2,4-dihydroxybenzophenone, di-2- pyridyl ketone, di-2-furanyl ketone, di-2-thiophenyl ketone, benzoin, fluorenones, quinones, e.g., chloroquinone, 2-aza-3-carboxy-9-fluorenone, and the like, chalcone, Michler's ketone, 2-fluoro- 9-fluorenone, 2-chlorothioxanthone, 2-isopropylthioxanthone, acetophenone, benzophenone, 1- or 2-acetonaphthone, 9-acetylantracene, 2-acetylphenanthrene, 3-acetylphenanthrene or 9- acetylphenanthrene, 4-acetylbiphenyl, propioph
• Suitable diketones include aralkyldiketones such as anthraquinone, phenanthrenequinone, o-, m- and p- diacetylbenzene, 1,3-diacetylanthracene, 1,4-diacetylanthracene, 1,5-diacetylanthracene, 1,6- diacetylanthracene, 1,7-diacetylanthracene and 1,8-diacetylnaphthalene, 1,5- diacetylanthracene, 1,8-diacetylanthracene and 9, 10-diacetylanthracene, and the like.
• aralkyldiketones such as anthraquinone, phenanthrenequinone, o-, m- and p- diacetylbenzene, 1,3-diacetylanthracene, 1,4-diacety
• Suitable a-diketones include 2,3-butanedione, 2,3-pentanedione, 2,3-hexanedione, 3,4-hexanedionc, 2,3-heptanedione, 3,4- heptanedione, 2,3-octanedione, 4,5-octanedione, benzil, 2,2'-dihydroxylbenzil, 3,3'- dihydroxylbenzil and 4,4'-dihydroxylbenzil, furil, di-3,3'-indolylethanedione, 2,3-bornanedione (camphorquinone), 1,2-cyclohexanedione, 1,2-naphthaquinone, acenaphthaquinone, and the like.
• the sensitizer can be initially colored prior to curing of the adhesive composition, undergo a reaction when exposed to the activating light which results in a color change to indicate the onset of cure in the adhesive composition.
• Other sensitizers could optionally include Rose Bengal, Methylene Violet, Fluorescein, Eosin Yellow, Eosin Y, Ethyl Eosin, Fosin Bluish, Erythrosin Yellowish Blend, 4',5'-Dibromofluorescein.
• the photoinitiator system can also include an electron donor.
• an electron donor A wide variety of donors can be used; the donor should be soluble in the monomer, and have good shelf stability. Suitable donors are capable of increasing the speed of cure or depth of cure of a composition upon exposure to light of the desired wavelength.
• the optional electron donors can include amines (including aminoaldehydes and aminosilanes), amides (including phosphoramides), anthracenes, ethers (including thioether), ureas (including thioureas), ferrocene, sulfinic acids and their salts, salts of ferrocyanide, ascorbic acid and its salts, dithiocarbamic acid and its salts, salts of xanthates, salts of ethylene diamine tetraacetic acid, and salts of tetraphenylboronic acid.
• the donor can be unsubstituted or substituted with one or more non-interfering substituents.
• Particularly preferred donors contain an electron donor atom such as a nitrogen, oxygen, phosphorus, or sulfur atom, and an abstractable hydrogen atom bonded to a carbon or silicon atom alpha to the electron donor atom.
• Preferred amine donor compounds include alkyl-, aryl-, alkaryl- and aralkyl-amines such as methylamine, ethylamine, propylamine, butylamine, triethanolamine, amylamine, hexylamine, 2,4-dimethylaniline, 2,3-dimethylaniline, o-, m- and p-toluidine, benzylamine, aminopyridine, N,N'-dimethylethylenediamine, ⁇ , ⁇ '-diethylethylenediamine, N,N'-dibenzylethylenediamine, N,N'-diethyl-l,3-propanediamine, N,N'-diethyl-2-butene-l,4-diamine, N,N'-dimethyl- 1,6- hexanediamine, piperazine, 4,4'-trimethylenedipiperidine, 4,4'-ethylenedipiperidine, p-N,N- dimethyl-a
• trimethylsilylmorpholine trimethylsilylpiperidine, bis(dimethylamino)diphenylsilane, tris(dimethylamino)methylsilane, N,N-diethylaminotrimethylsilane,
• Tertiary aromatic alkylamines particularly those having at least one electron-withdrawing group on the aromatic ring, have been found to provide especially good shelf stability. Good shelf stability has also been obtained using amines that are solids at room temperature.
• Preferred amide donor compounds include ⁇ , ⁇ -dimethylacetamide, N,N- di ethyl acetami de, N-methy 1 -N-pheny 1 acetami de, hexamethy lphosphorami de,
• hexaethylphosphoramide hexapropylphosphoramide, trimorpholinophosphine oxide and tripiperidinophosphine oxide.
• the present invention features a photoinitiator for a cationically polymerizable adhesive composition.
• the system includes an onium salt such as an iodonium salt or a sulphonium salt.
• the iodonium salt for the photoinitiator system may be, for example, diaryliodonium hexafluorophosphate, diaryliodonium hexafluoroantimonate, diaryliodonium tetrakis(pentafluorophenyl)borate, 4-octyloxyphenyl phenyliodonium hexafluoroantimonate, 4- (2-hydroxytetradecyloxyphenyl)phenyliodonium hexafluoroantimonate, 4-(l -methylethyl)phenyl 4-methylphenyliodonium tetrakis(pentafluorophenyl)borate, or combinations thereof.
• the cationic photoinitiator could be a sulfonium salt.
• Useful sulfonium salt photoacid generators include a mixture of triarylsulfonium salts (diphenyl(4- phenylthio)phenylsulfonium hexafluoroantimonate and bis(4-(diphenylsulfonio)phenyl)sulfide hexafluoroantimonate) available as UVI-6976 from Synasia Metuchen, N.J., a mixture of diphenyl(4-phenylthio)phenylsulfonium hexafluorophosphate, bis(4-
• the visible light sensitizer is present at about 0.05-5.0 weight percent based on the reactive components of the adhesive composition (e.g. the total of the epoxy resin and the polyol in the adhesive composition), more preferably, at about 0.10-2.5 weight percent.
• the onium salt is preferably present at about 0.05-10.0 weight percent based on the reactive component of the adhesive composition, more preferably at about 0.10-5.0 weight percent, and most preferably at about 0.50-3.0 weight percent.
• the optional electron donor compound or compounds are preferably present at about 0.01-5.0 weight percent, based on the reactive component of the adhesive composition, more preferably about 0.05-1.0 weight percent, and most preferably about 0.05-0.50 weight percent when they are present in the adhesive composition.
• anthracene-based compounds include: 2-ethyl-9,10- dimethoxyanthracene (EDMOA), 9,10-dimethylanthracene, 9,10-diethoxyanthracene, 1,4- dimethoxyanthracene, 9-methylanthracene, 2-ethylanthracene, 2-tert-butylanthracene, 2,6-di- tert-butylanthracene, 9, 10-diphenyl-2,6-di-tert-butylanthracene, and combinations thereof.
• EDMOA 2-ethyl-9,10- dimethoxyanthracene
• 9,10-dimethylanthracene 9,10-diethoxyanthracene
• 1,4- dimethoxyanthracene 9-methylanthracene
• 2-ethylanthracene 2-tert-butylanthracene
• the anthracene-based compounds will absorb visible light and can be used as the sensitizer.
• Additional optional materials can be can be added to the adhesive composition such as rheological modifiers, and a colorant that signals when there has been sufficient exposure to a light source to cure the adhesive.
• the adhesive bond is desirably thermally stable.
• the adhesive bond desirably does not allow movement of the optical fibers under a mechanical load.
• the fiber retention of the adhesive should be at least 1.5 lbs.
• the cured adhesive composition should have Tg over 45°C, preferably over 50°C after blue light exposure, a refractive index between about 1.44 to about 1.485, preferably between about 1.44 to about 1.47, preferably about 1.45 at 1330 nm and a dn/dT less than -20E-5/°C, preferably less than less than -15E-5/°C, and more preferably less than -10E-5/°C.
• the exemplary adhesives can have a Tg of greater than about 70°C, preferably greater than about 90°C.
• An Abbe Refractometer (model No. IT available from Atago U.S.A., Inc) was used to measure the index of refraction of the uncured samples at the Sodium D-Line wavelength (589 nm).
• An Abbe Refractometer with a water bath was used to control the temperature for the uncured 589 nm dn/dT measurements.
• the end of a piece of SMF 28 single mode optical fiber is cleaved using a Cl-01 cleaver available from Ilsintech Company, Ltd. (Dallas, TX) to produce a perpendicular end face (i.e. the end face of the optical fiber varies less than 0.5° from perpendicular with respect to the axis of the optical fiber).
• the cleaved end of the optical fiber with adhesive disposed thereon is placed in a controlled temperature environment.
• a base scan of the light reflected by the cleaved end face is measured from 1250 nm to 1720 nm yielding a base spectra is saved.
• a drop of a sample adhesive is placed on the cleaved end face of the optical fiber and cured using a Paradigm DeepCure Curing Light available from 3M Company (St. Paul, MN) for 60 seconds.
• the cleaved end of the optical fiber with adhesive disposed thereon is placed in a controlled temperature environment.
• a test scan of the light reflected by the glass at cleaved end face with the cured sample adhesive is measured from 1250 nm to 1720 nm yielding a sample spectra. This process is repeated at 20°C, 40°C, 60°C, and 80°C.
• the base spectra is subtracted from the sample spectra for each temperature condition to give a test spectra.
• An average reflectance value is obtained from the test spectra at each temperature condition.
• the index of refraction was calculated for the material being analyzed using the Fresnel equation to provide measured reflection at 80°C.
• dn/dT is calculated from the slope of the line through the calculated index values when plotted against their corresponding temperature.
• the modulus and hardness of the adhesive samples was found using a G200 nanoindenter in GCM mode with a Berkovich diamond probe after curing the adhesive with a ParadigmTM DeepCure LED curing light available from 3M Company (St. Paul, MN) for the designated cure time. An approach velocity of 10 nm/sec was used.
• the terminal portion of an SMF 28 single mode optical fiber was stripped to remove the acrylic buffer coating and cleaned with isopropyl alcohol.
• the end of the bare glass portion of the optical fiber was cleaved to either a 2 mm cleave length, a 5 mm cleave length or a 10 mm cleave length.
• a drop of a sample adhesive was placed on a microscope slide and the stripped and cleaved bare glass portion of the optical fiber was placed in the adhesive drop. Another microscope slide was placed on top such that the bond thickness between the glass slides was 250 microns.
• the adhesive was cured with a ParadigmTM DeepCure curing light for 1 minute.
• the test sample was placed in an Instron 5966 Series Mechanical Testing System, available from (Norwood, MA), using a 500N load cell and the fiber was pulled at a 6 mm/min. crosshead speed.
• CTE Coefficient of Thermal Expansion
• silica sol having an initial pH between 8-10.5 was placed in a beaker and while stirring at low speed, the rinsed ion exchange resin (Amberlite IR- 120(H) ion exchange resin from Alfa Aesar) was added by small spoonfuls. About 3-5 minutes after each addition, the pH was measured. Once the pH had been reduced to about 2.5, no further ion exchange resin was added. The sol/ ion exchange resin mixture was stirred for 45-60 minutes, after which the ion exchange resin was filtered off.
• the rinsed ion exchange resin Amberlite IR- 120(H) ion exchange resin from Alfa Aesar
• the nanoparticles in the Filler 3 sol were surface modified with Silane 1
• the surface treatment agent (tnmethoxyphenylsilane) was added to the Filler 3 sol and stirred for 5 minutes at room temperature (23 deg. C).
• a co-solvent (l-methoxy-2-propanol) was added to the sol/silane mixture over a 5 minute period and the resulting dispersion was continuously stirred prior to delivery to the tubular reactor.
• the resulting solution was 14.7% silica as determined by oven solids and thermogravimetric analysis.
• 140 nm phenylsilane modified silica 140 nm PsMS
• the nanoparticles in the Filler 2 sol were surface modified with Silane 1
• the surface treatment agent trimethoxyphenylsilane was added to the Filler 2 sol and stirred for 5 minutes at room temperature (23 deg. C).
• a co-solvent (l-methoxy-2-propanol) was added to the sol/silane mixture over a 5 minute period and the resulting dispersion was continuously stirred prior to delivery to the tubular reactor.
• the resulting solution was 14.7% silica as determined by oven solids and thermogravimetric analysis.
• the Filler 2 sol having an initial pH between 8-10.5 was placed in a beaker and while stirring at low speed, the rinsed ion exchange resin (Amberlite IR- 120(H) ion exchange resin from Alfa Aesar) was added by small spoonfuls. About 3-5 minutes after each addition, the pH was measured. Once the pH had been reduced to about 2.5, no further ion exchange resin was added. The sol/ ion exchange resin mixture was stirred for 45-60 minutes, after which the ion exchange resin was filtered off.
• the rinsed ion exchange resin Amberlite IR- 120(H) ion exchange resin from Alfa Aesar
• ion exchanged Filler 2 (lab ion exchanged Nalco TX 15827) was placed in a three-neck round bottom flask equipped with an overhead air stirrer, thermometer and condenser. While stirring at medium speed the solution was heated to 50°C and 250 g of l-methoxy-2-propanol was slowly added. This was followed by the addition of concentrated ammonium hydroxide - added by dropper to quickly adjust the pH from ⁇ 2.7 to >9.2.
• a premix was prepared containing 4.0 g Silane 1 (trimethoxyphenylsilane), 4.69 g Silane 4 (isooctyl silane), and 1250 g l-methoxy-2- propanol. This was poured into the stirred (50°C) pH adjusted silica solution over 5-10 minutes, then entire mixture was heated at 90-95°C for 18-20 hours. The resulting solution was 19.0% silica as determined by oven solids and thermogravimetric analysis.
• the Filler 3 sol having an initial pH between 8-10.5 was placed in a beaker and while stirring at low speed, the rinsed ion exchange resin (Amberlite IR- 120(H) ion exchange resin from Alfa Aesar) was added by small spoonfuls. About 3-5 minutes after each addition, the pH was measured. Once the pH had been reduced to about 2.5, no further ion exchange resin was added. The sol/ ion exchange resin mixture was stirred for 45-60 minutes, after which the ion exchange resin was filtered off.
• the rinsed ion exchange resin Amberlite IR- 120(H) ion exchange resin from Alfa Aesar
• ion exchanged Filler 3 750 g was placed in a three-neck round bottom flask equipped with an overhead air stirrer, thermometer and condenser. While stirring at medium speed the solution was heated to 50°C and 170 g of l-methoxy-2-propanol was slowly added. This was followed by the addition of concentrated ammonium hydroxide - added by dropper to quickly adjust the pH from ⁇ 2.7 to >9.2. Used a pH probe in the solution to monitor the pH change as the ammonium hydroxide was added.
• epoxy resins were purified to reduce/remove contaminants according to the process described in United States Patent 6,620,907, herein incorporated by reference.
• epoxy/diol/silica mix was added 0.64 g of a 54.1% solution of CXC 1612 in propylene carbonate. Both were speed mixed on a FlackTek 150FVZ speed mixer available from
• Epoxy 1A, 5.9 g 1,5 pentanediol, 300 g 90 nm PsCaEMS (21.5% solids in methoxypropanol/water) and 48.7 g 20nm PsMS (14.7% solids in methoxypropanol/water) were placed in a bottle, and shaken well until thoroughly mixed. The mixture was then placed on a roto-evaporator with the oil bath set at about 90°C and vacuum applied. After 1-2 hours, the temperature was increased to 125°C for 15 minute, followed by 145°C for 15 minutes to ensure the methoxypropanol and water were removed. The resulting epoxy/silica had 63.9% silica as determined by thermogravimetric analysis.
• Example 5 Adhesive Composition (Ex. 5)
• Comparative examples C2-C9 were cured per the manufacturer's recommended procedures.
• Example 6 Adhesive Composition (Ex. 6)
• Epoxy 1 A Epoxy 1 A (ERL 422 le)
• 9.75 g of 1,5-pentanediol, 87.75 g silica solids equivalents of 90nm PSMS and 9.75 g silica solids equivalents of 20 nm PSMS silica sol were placed in a bottle, and shaken well until thoroughly mixed. The mixture was then placed on a roto-evaporator with the oil bath set at 85-90°C and vacuum applied. Once most of the volatiles had been removed (roughly one hour) the temperature was increased to 150°C for 45 minutes as a final devolatilizing step. The resulting epoxy/silica had 59.2% silica as determined by thermogravimetric analysis.
• Example 7 Adhesive Composition (Ex. 7)
• Example 9 Adhesive Composition (Ex. 9)
• the LEDs were arranged in a 10x20 two- dimensional array with a 2.5 mm spacing.
• a finned anodized aluminum heat sink has been used, sized appropriately to dissipate the heat generated by the array used to cure our adhesives.
• the samples were then removed to DSC pans for evaluation of Tg. Results are shown in Tables 3 and 4. Table 3. The effect of current on the curing of select adhesive materials
• the preferred current settings are between 1.5 A to 3.0 A, preferably between to 2.0 A and 2.75 A, based on Tg and completeness of cure (residual cure less than 10 J/g, preferably 5 J/g, most preferable about 0 J/g).
• the samples were then removed to DSC pans for evaluation of Tg. Results are shown in Table 4.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Physics & Mathematics (AREA)
• Optics & Photonics (AREA)
• General Physics & Mathematics (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Inorganic Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Plasma & Fusion (AREA)
• Adhesives Or Adhesive Processes (AREA)
• Epoxy Resins (AREA)

Priority Applications (2)

Applications Claiming Priority (4)

Publications (1)

Family

ID=59895406

Family Applications (1)

Country Status (4)

Cited By (2)

Families Citing this family (10)

Citations (9)

Family Cites Families (27)

• 2017
  • 2017-09-06 JP JP2019535190A patent/JP2019532165A/ja active Pending
  • 2017-09-06 WO PCT/US2017/050255 patent/WO2018052777A1/en not_active Ceased
  • 2017-09-06 CN CN201780056253.2A patent/CN109689826B/zh not_active Expired - Fee Related
  • 2017-09-06 US US15/696,901 patent/US10329460B2/en not_active Expired - Fee Related