Classifications

• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61L—METHODS OR APPARATUS FOR STERILISING MATERIALS OR OBJECTS IN GENERAL; DISINFECTION, STERILISATION OR DEODORISATION OF AIR; CHEMICAL ASPECTS OF BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES; MATERIALS FOR BANDAGES, DRESSINGS, ABSORBENT PADS OR SURGICAL ARTICLES
  • A61L15/00—Chemical aspects of, or use of materials for, bandages, dressings or absorbent pads
  • A61L15/07—Stiffening bandages
  • A61L15/12—Stiffening bandages containing macromolecular materials
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F13/00—Bandages or dressings; Absorbent pads
  • A61F13/02—Adhesive bandages or dressings
  • A61F13/0273—Adhesive bandages for winding around limb, trunk or head, e.g. cohesive
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F13/00—Bandages or dressings; Absorbent pads
  • A61F13/02—Adhesive bandages or dressings
  • A61F13/0276—Apparatus or processes for manufacturing adhesive dressings or bandages
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F13/00—Bandages or dressings; Absorbent pads
  • A61F13/02—Adhesive bandages or dressings
  • A61F13/0276—Apparatus or processes for manufacturing adhesive dressings or bandages
  • A61F13/0283—Apparatus or processes for manufacturing adhesive dressings or bandages for making adhesive or cohesive tape or fabrics therefor, e.g. coating or mechanical treatments
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F7/00—Heating or cooling appliances for medical or therapeutic treatment of the human body
  • A61F7/02—Compresses or poultices for effecting heating or cooling
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F7/00—Heating or cooling appliances for medical or therapeutic treatment of the human body
  • A61F7/10—Cooling bags, e.g. ice-bags
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61P—SPECIFIC THERAPEUTIC ACTIVITY OF CHEMICAL COMPOUNDS OR MEDICINAL PREPARATIONS
  • A61P17/00—Drugs for dermatological disorders
  • A61P17/04—Antipruritics
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61P—SPECIFIC THERAPEUTIC ACTIVITY OF CHEMICAL COMPOUNDS OR MEDICINAL PREPARATIONS
  • A61P29/00—Non-central analgesic, antipyretic or antiinflammatory agents, e.g. antirheumatic agents; Non-steroidal antiinflammatory drugs [NSAID]
  • A61P29/02—Non-central analgesic, antipyretic or antiinflammatory agents, e.g. antirheumatic agents; Non-steroidal antiinflammatory drugs [NSAID] without antiinflammatory effect
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61P—SPECIFIC THERAPEUTIC ACTIVITY OF CHEMICAL COMPOUNDS OR MEDICINAL PREPARATIONS
  • A61P43/00—Drugs for specific purposes, not provided for in groups A61P1/00-A61P41/00
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F7/00—Heating or cooling appliances for medical or therapeutic treatment of the human body
  • A61F2007/0059—Heating or cooling appliances for medical or therapeutic treatment of the human body with an open fluid circuit
  • A61F2007/0063—Heating or cooling appliances for medical or therapeutic treatment of the human body with an open fluid circuit for cooling
  • A61F2007/0068—Heating or cooling appliances for medical or therapeutic treatment of the human body with an open fluid circuit for cooling evaporating on the spot to be cooled
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F7/00—Heating or cooling appliances for medical or therapeutic treatment of the human body
  • A61F7/02—Compresses or poultices for effecting heating or cooling
  • A61F2007/0203—Cataplasms, poultices or compresses, characterised by their contents; Bags therefor
  • A61F2007/0215—Cataplasms, poultices or compresses, characterised by their contents; Bags therefor containing liquids other than water
  • A61F2007/0219—Gels
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F7/00—Heating or cooling appliances for medical or therapeutic treatment of the human body
  • A61F7/02—Compresses or poultices for effecting heating or cooling
  • A61F2007/0225—Compresses or poultices for effecting heating or cooling connected to the body or a part thereof
  • A61F2007/0226—Compresses or poultices for effecting heating or cooling connected to the body or a part thereof adhesive, self-sticking
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F7/00—Heating or cooling appliances for medical or therapeutic treatment of the human body
  • A61F7/02—Compresses or poultices for effecting heating or cooling
  • A61F2007/0244—Compresses or poultices for effecting heating or cooling with layers
  • A61F2007/026—Compresses or poultices for effecting heating or cooling with layers with a fluid absorbing layer
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F13/00—Bandages or dressings; Absorbent pads
  • A61F2013/00089—Wound bandages
  • A61F2013/00187—Wound bandages insulating; warmth or cold applying
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61F—FILTERS IMPLANTABLE INTO BLOOD VESSELS; PROSTHESES; DEVICES PROVIDING PATENCY TO, OR PREVENTING COLLAPSING OF, TUBULAR STRUCTURES OF THE BODY, e.g. STENTS; ORTHOPAEDIC, NURSING OR CONTRACEPTIVE DEVICES; FOMENTATION; TREATMENT OR PROTECTION OF EYES OR EARS; BANDAGES, DRESSINGS OR ABSORBENT PADS; FIRST-AID KITS
  • A61F13/00—Bandages or dressings; Absorbent pads
  • A61F2013/00361—Plasters
  • A61F2013/00655—Plasters adhesive
  • A61F2013/00697—Plasters adhesive elastomer-, e.g. rubber- based

Definitions

• the invention relates to a bandage comprising a
• a self-adhesive cohesive adhesive is at least partially applied and the
• Substrate is impregnated with a liquid preparation.
• the prior art has been cohesive for many years
• Bonding with liquid preparations z. B. known as cooling bandages Bonding with liquid preparations z. B. known as cooling bandages.
• a dry bandage with a cooling fluid for example based on water / ethanol or
• Such products are, for example, among the
• Such bandages are called compression and / or
• the cold and compression counteract swelling.
• WO 2005/007050 A1 describes a cooling bandage based on an elastic carrier material with a cooling liquid preparation based on ethanol, water, methanol and isoamyl acetate.
• Natural rubber latex are formed with respect to their cohesive adhesive forces is that during storage time the
• the invention therefore solves the problem by a bandage having the features of claim 1 and a method having the features of claim 10 wherein the bandage is formed so that the adhesive is anhydrous cohesive
• Adhesive comprising natural and / or synthetic rubber, in which the natural and / or synthetic rubber is dissolved for application in organic solvent or the pressure-sensitive adhesive for application is molten.
• cohesive properties can be used without having to resort to a latex material.
• Synthetic rubber is preferred, able to provide a cohesive coating composition for a binding, which surprisingly shows a different aging behavior than natural rubber latex and thus even after prolonged storage still a satisfactory adhesive force
• the adhesive force between the layers of a dry binding according to the invention corresponds almost identical to the adhesive force of bindings based on natural rubber latex. Become both the
• inventive bandage as well as the bandage of the prior art with a liquid preparation, eg. B. from 50% ethanol impregnated in water, adhere surprisingly the layers of the bandage invention still
• the bandage according to the invention therefore has the advantage that a secure ply adhesion of the wet bandage without the use of bandage clips over a wearing time of up to several days is given, even if the bandage since
• the natural rubber (polyisoprene) or preferably the
• Synthetic rubber (polyisoprene, -budadiene, -chloroprene) is designed as an open-cell coating, preferably only partially, in the form of fragments or patterns.
• a corresponding application can take place in various ways, namely, for example, a) in the form of a spray application of solutions of solid rubber in
• Hydrocarbons, ethers, esters or ketones can be used and beyond b) a spray application of hot melt adhesives.
• Rubber material in organic solvents are also processed in the context of a stencil printing, wherein alternatively, the hot melt adhesives in the
• Stencil printing can be applied.
• Hot melt adhesives also conceivable an anilox roll order.
• Rubber fragments in an application amount per surface of 2 to 20 g / m 2 is formed, wherein the rubber fragments are preferably arranged on the surface and may be adhesively bonded to the substrate, here
• the cohesive PSA ensures a non-slip fit when wound on the body part.
• the proportion of the rubber, if it is brought into solution with organic solvents, is 5 to 20% solids content.
• the applied rubber solution is then treated in a drying step so that the
• Drying process on the substrate surface remains a closed or open-pored rubber film. This is sealed when pressing with itself or adheres to each other, so that in this way the cohesive adhesive force is provided.
• the bandage can be elastic in the longitudinal and / or transverse direction. It can be provided in particular that the substrate is a woven, knitted fabric or knit fabric. The elasticity can be achieved by the incorporation of elastic threads, such as high-turned
• Cotton threads, as spun or Zwirnkreppfäden, by textured polyamide or polyester yarns and rubber or polyurethane threads or combinations thereof are caused.
• elasticity can be achieved by overstitching a rigid nonwoven fabric with permanently elastic elastane threads in the longitudinal direction using the MALIWATT sewing technique was obtained.
• the sewing technique MALIWATT is in Malimo sewing technology, Ploch, Böttcher, Scharch, VEB
• the liquid preparation according to the invention consists of a mono- or multiphase preparation based on water with additions of inorganic substances, such as, for example, salts, or organic substances, namely, for example, alcohols, esters, ethers, ketones or terpenes.
• inorganic substances such as, for example, salts, or organic substances, namely, for example, alcohols, esters, ethers, ketones or terpenes.
• preparations may also contain gels or foams
• the amount of fluid necessary for the intended effect is applied to the cohesive bandage after application of the adhesive by spraying, dipping, foulading, padding and / or pouring.
• the preparation may be distributed partially or over the entire bandage.
• the bandage can then be introduced into a hermetically sealed packaging, such as foil bags, peel packs, deep-drawn packs, cans, bottles, etc., thus achieving a storage time of up to 3 years.
• a hermetically sealed packaging such as foil bags, peel packs, deep-drawn packs, cans, bottles, etc.
• a bandage produced in this way which may alternatively also be referred to as a bandage, has a cohesive self-adhesion both in the wet and in the dried state, which is still present even after several years of storage.
• the invention will be explained in more detail below with reference to examples.
• Example 1 Cohesive nonwoven bandage with cooling fluid
• Nonwoven construction type 752 trade name NOWOPRESS 752, manufacturer Karl Otto Braun GmbH & Co., Wolfstein,
• This elastic base fabric is called the sheet goods
• the cohesive pressure-sensitive adhesive consists of the following components:
• Solid Rubber Ice 1. Solid Rubber Ice 1.4 Polyisoprene, Trade name NATSYN 2200, Manufacturer: GOODYEAR, Ohio, USA
• Hydrocarbon mixture of different isomers manufacturer: BIESTERFELD, Hamburg, Germany
• anti-aging agent 2,6-di-tert-butylpcresol
• the preparation is carried out according to the following procedure: 400 g of isohexane are placed in a stainless steel stirred tank
• Grain size about 4 mm added. Also be 1.21 g
• Anti-aging agent (component 3) added as a powder. At a stirring speed of 300 rpm, component 3 dissolves immediately in isohexane, while for complete solution of component 2 about 120 minutes are required. As a result, there is a grayish cloudy viscous adhesive mass with a solids content of 13.1%. The viscosity was measured using a Haake viscometer, type "Haake-Viscotester VT 2 plus, manufacturer: THERMO SCIENTIFIC
• the coating of the elastic nonwovens type 752 is done in such a way that the 10 cm wide web with the
• roller squeegee is supplied, with the lowest possible tensile forces are used to largely maintain the unstretched state of the type 752 web.
• Roller doctor blade is 15 cm.
• the web is over the Roll and performed under the doctor blade and the pasty adhesive before the doctor blade in portions, so that always a lot of about 100 g
• Adhesive rests on the web. The gap between doctor blade and roller is adjusted so that the
• Adhesive forms a microporous, open-pored film of rubber fragments.
• the web material leaves the dryer in the dried state and is wound low-tension into a roll.
• the web is now coated on one side with the dry adhesive, the order quantity is between 7.2 and 8.5 g dry weight.
• Basis weight of the one-side coated sheet goods is 50.2 to 51.5 g, the ductility about 190% (both parameters according to DIN 61632 at 3 N / cm). The role of
• One-side coated sheet goods now passes through the roll-doctoring unit and the second in a second pass
• the solid adhesive forms a
• a release paper or a release film as a spacer is used when winding the roll
• Application amount of the adhesive on the substrate is now total between 14.4 and 17.0 g dry weight.
• the weight per unit area of the two-side coated sheet material is 57.4 to 60.0 g, the extensibility at about 160% (both parameters according to DIN 61632 at 3 N / cm).
• a winding core e.g. Polypropylene plastic sleeve, inner diameter 28 mm, wall thickness 1 mm, height 10.0 cm then becomes a length of 1.75 m
• the net weight (sheet goods without sleeve) is 27.0 g.
• the bond diameter is 54 mm.
• the cooling fluid used is mixtures of ethanol / water with or without the addition of cooling auxiliaries:
• Cooling fluid KF1 Produced by mixing the following components:
• Coolant KF2 (with enhanced cooling effect): Mix / dissolve the following components
• Eumulgin HRE 40 emulsifier, manufacturer COGNIS, Dusseldorf, Germany
• the cooling temperature difference ⁇ is determined in a test subject application test as follows:
• the subject's forearm is 5 - 10 cm away from the elbow as a 2-ply edge-just overlapping ring wrapped and lightly pressed to connect the layers. Then a digital thermometer with metal sensor tip is immediately pushed under the dressing, so that the tip is placed in the middle.
• the starting temperature of the skin T (H) was previously determined with a dry ideal bandage according to DIN 61632.
• the cooling temperature difference ⁇ is calculated as the difference T (B) -T (H).
• AKTmax is the maximum Cooling temperature difference, ie the amount T (B) - T (H) is maximum.
• the bandages are wound on the lower leg with slight stretching of about 80% with 50% overlap as Spiraltouren claimed and pressed the layers by hand well.
• the layers enter into an adhesive bond, although the cooling fluid also covers the rubber fragments of the cohesive coating.
• the subject perceives the cooling effect immediately after applying the dressings, the peak of the cooling effect is reached after 30 - 60 minutes.
• the cooling effect lasts for a total of about 90 to 120 minutes. Subjectively, they feel
• the invention also relates to a method for producing a bandage comprising a
• Pressure-sensitive adhesive comprising natural and / or synthetic rubber takes place in which the natural and / or synthetic rubber is dissolved for application in organic solvent or molten for application and then either evaporates the solvent or the pressure-sensitive adhesive hardens and then coated with the cohesive adhesive substrate a liquid preparation is soaked.
• the coating of the elastic fabric type 199 is carried out using the adhesive described in Example 1 on the same roll doctor coating system, using a 10 cm wide web.
• the amount of glue applied to the substrate is now 13.0 g
• coated sheet is 108 g, the extensibility at 100% (both parameters according to DIN 61632 at 3 N / cm).
• a winding core e.g. Plastic sleeve made of polypropylene, inner diameter 28 mm, wall thickness 1 mm, height 10.0 cm, a length of 2.0 m webbing of the fabric type 199 in a tension-reduced state to a
• the net weight (sheet goods without sleeve) is 44.0 g.
• the bond diameter is 57 mm.
• the fluid is a dilute aqueous solution of
• Fluid KF3 By mixing the following components
• a wound body is placed in a plastic can with screw cap, inner diameter 67 mm, height 110 mm, and poured slowly with 44.0 g of fluid KF3 until the fluid is completely absorbed by the bandage.
• the fluid is distributed homogeneously in the bandage within one minute.
• the bandages are wound on the lower leg with slight elongation of about 60% with 50% overlap as Spiraltouren- bandage and pressed the layers by hand well.
• the layers enter into an adhesive bond, although the alumina-clay-alumina fluid forms an interface between the layers
• Rubber fragments of the cohesive coating forms.
• the subject feels the effect as pleasant cooling and skin-drying (astringent). Swellings form back.

Landscapes

• Health & Medical Sciences (AREA)
• Engineering & Computer Science (AREA)
• Life Sciences & Earth Sciences (AREA)
• Animal Behavior & Ethology (AREA)
• General Health & Medical Sciences (AREA)
• Public Health (AREA)
• Veterinary Medicine (AREA)
• Biomedical Technology (AREA)
• Vascular Medicine (AREA)
• Heart & Thoracic Surgery (AREA)
• Chemical & Material Sciences (AREA)
• Physics & Mathematics (AREA)
• Thermal Sciences (AREA)
• Manufacturing & Machinery (AREA)
• Organic Chemistry (AREA)
• Pharmacology & Pharmacy (AREA)
• Chemical Kinetics & Catalysis (AREA)
• General Chemical & Material Sciences (AREA)
• Medicinal Chemistry (AREA)
• Nuclear Medicine, Radiotherapy & Molecular Imaging (AREA)
• Epidemiology (AREA)
• Materials Engineering (AREA)
• Bioinformatics & Cheminformatics (AREA)
• Dermatology (AREA)
• Pain & Pain Management (AREA)
• Rheumatology (AREA)
• Materials For Medical Uses (AREA)
• Medicinal Preparation (AREA)
• Acyclic And Carbocyclic Compounds In Medicinal Compositions (AREA)
• Adhesive Tapes (AREA)
• Adhesives Or Adhesive Processes (AREA)
• Pharmaceuticals Containing Other Organic And Inorganic Compounds (AREA)
• Prostheses (AREA)

Priority Applications (8)

Applications Claiming Priority (2)

Publications (1)

Family

ID=57794267

Family Applications (1)

Country Status (9)

Cited By (2)

Families Citing this family (4)

Citations (4)

Family Cites Families (20)

• 2015
  • 2015-12-23 DE DE102015226645.1A patent/DE102015226645A1/de not_active Withdrawn
• 2016
  • 2016-12-23 US US16/064,590 patent/US20190001016A1/en not_active Abandoned
  • 2016-12-23 PL PL16825781.4T patent/PL3393415T3/pl unknown
  • 2016-12-23 AU AU2016375185A patent/AU2016375185B2/en active Active
  • 2016-12-23 ES ES16825781T patent/ES2954124T3/es active Active
  • 2016-12-23 CN CN201680075422.2A patent/CN108430408A/zh active Pending
  • 2016-12-23 EP EP16825781.4A patent/EP3393415B1/de active Active
  • 2016-12-23 JP JP2018532210A patent/JP7270378B2/ja active Active
  • 2016-12-23 WO PCT/EP2016/082627 patent/WO2017109210A1/de not_active Ceased

Patent Citations (4)

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events