WO2017018392A1 - Composition de résine, film, élément de conversion de longueur d'onde et procédé de formation de film - Google Patents

Composition de résine, film, élément de conversion de longueur d'onde et procédé de formation de film Download PDF

Info

Publication number
WO2017018392A1
WO2017018392A1 PCT/JP2016/071779 JP2016071779W WO2017018392A1 WO 2017018392 A1 WO2017018392 A1 WO 2017018392A1 JP 2016071779 W JP2016071779 W JP 2016071779W WO 2017018392 A1 WO2017018392 A1 WO 2017018392A1
Authority
WO
WIPO (PCT)
Prior art keywords
compound
resin composition
film
wavelength conversion
group
Prior art date
Application number
PCT/JP2016/071779
Other languages
English (en)
Japanese (ja)
Inventor
英行 神井
Original Assignee
Jsr株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2016142846A external-priority patent/JP6834213B2/ja
Application filed by Jsr株式会社 filed Critical Jsr株式会社
Priority to KR1020177033673A priority Critical patent/KR20180035732A/ko
Publication of WO2017018392A1 publication Critical patent/WO2017018392A1/fr

Abstract

La présente invention concerne : une composition de formation d'élément de conversion de longueur d'onde qui peut supprimer une réduction du rendement quantique de fluorescence d'un point quantique à semi-conducteur suite au traitement thermique; un film durci obtenu à partir de la composition de formation d'élément de conversion de longueur d'onde; un élément de conversion de longueur d'onde qui utilise le film durci; et un procédé de formation d'un film durci à l'aide de la composition de formation d'élément de conversion de longueur d'onde. Cette composition de formation d'élément de conversion de longueur d'onde contient une résine liante, des points quantiques à semi-conducteur et au moins un type de composé sélectionné dans le groupe constitué d'un composé ayant une structure phénylphosphine, d'un composé ayant une structure cycloalkylphosphine, d'un composé ayant une structure thiobisphénol, d'un composé ayant une structure dialkylthiodipropionate et d'un composé ayant une structure benzothiazole. De préférence, la composition de formation d'élément de conversion de longueur d'onde contient en outre un piégeur de radicaux. De préférence, la composition de formation d'élément de conversion de longueur d'onde contient en outre un composé polymérisable. De préférence, la résine liante possède une structure alicyclique dans une chaîne latérale.
PCT/JP2016/071779 2015-07-29 2016-07-25 Composition de résine, film, élément de conversion de longueur d'onde et procédé de formation de film WO2017018392A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
KR1020177033673A KR20180035732A (ko) 2015-07-29 2016-07-25 수지 조성물, 막, 파장 변환 부재 및 막의 형성 방법

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2015-149643 2015-07-29
JP2015149643 2015-07-29
JP2016142846A JP6834213B2 (ja) 2015-07-29 2016-07-20 樹脂組成物、膜、波長変換部材、及び膜の形成方法
JP2016-142846 2016-07-20

Publications (1)

Publication Number Publication Date
WO2017018392A1 true WO2017018392A1 (fr) 2017-02-02

Family

ID=57884390

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/071779 WO2017018392A1 (fr) 2015-07-29 2016-07-25 Composition de résine, film, élément de conversion de longueur d'onde et procédé de formation de film

Country Status (1)

Country Link
WO (1) WO2017018392A1 (fr)

Cited By (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016108548A (ja) * 2014-12-02 2016-06-20 東友ファインケム株式会社Dongwoo Fine−Chem Co., Ltd. 自発光感光性樹脂組成物、これから製造されたカラーフィルタおよび前記カラーフィルタを含む画像表示装置
WO2018180445A1 (fr) * 2017-03-30 2018-10-04 住友化学株式会社 Polymère et composition
WO2019021813A1 (fr) * 2017-07-28 2019-01-31 東レ株式会社 Composition de conversion de couleur et film de conversion de couleur, et unité de source de lumière, unité d'affichage et éclairage la comprenant
WO2019181698A1 (fr) * 2018-03-23 2019-09-26 東レ株式会社 Composition de résine photosensible, film durci, carte de conversion de couleur, appareil d'affichage d'image et procédé de fabrication de film durci
JP2019532346A (ja) * 2016-11-15 2019-11-07 東友ファインケム株式会社Ｄｏｎｇｗｏｏ Ｆｉｎｅ−Ｃｈｅｍ Ｃｏ．， Ｌｔｄ． 感光性樹脂組成物、カラーフィルタ、及び画像表示装置
WO2020217700A1 (fr) * 2019-04-25 2020-10-29 Jsr株式会社 Composition de résine photosensible
TWI840326B (zh) 2017-02-15 2024-05-01 日商東京應化工業股份有限公司 間隔壁用圖案的形成方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010277069A (ja) * 2009-04-27 2010-12-09 Jsr Corp 感放射線性樹脂組成物、硬化膜及びその形成方法
JP2015018131A (ja) * 2013-07-11 2015-01-29 Jsr株式会社 感放射線性樹脂組成物、硬化膜、発光素子、波長変換フィルムおよび発光層の形成方法
JP2015121702A (ja) * 2013-12-24 2015-07-02 Jsr株式会社 硬化性樹脂組成物、硬化膜、発光素子、波長変換フィルムおよび発光層の形成方法
WO2016035602A1 (fr) * 2014-09-05 2016-03-10 住友化学株式会社 Composition durcissable
JP2016108548A (ja) * 2014-12-02 2016-06-20 東友ファインケム株式会社Dongwoo Fine−Chem Co., Ltd. 自発光感光性樹脂組成物、これから製造されたカラーフィルタおよび前記カラーフィルタを含む画像表示装置

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2010277069A (ja) * 2009-04-27 2010-12-09 Jsr Corp 感放射線性樹脂組成物、硬化膜及びその形成方法
JP2015018131A (ja) * 2013-07-11 2015-01-29 Jsr株式会社 感放射線性樹脂組成物、硬化膜、発光素子、波長変換フィルムおよび発光層の形成方法
JP2015121702A (ja) * 2013-12-24 2015-07-02 Jsr株式会社 硬化性樹脂組成物、硬化膜、発光素子、波長変換フィルムおよび発光層の形成方法
WO2016035602A1 (fr) * 2014-09-05 2016-03-10 住友化学株式会社 Composition durcissable
JP2016108548A (ja) * 2014-12-02 2016-06-20 東友ファインケム株式会社Dongwoo Fine−Chem Co., Ltd. 自発光感光性樹脂組成物、これから製造されたカラーフィルタおよび前記カラーフィルタを含む画像表示装置

Cited By (18)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2016108548A (ja) * 2014-12-02 2016-06-20 東友ファインケム株式会社Dongwoo Fine−Chem Co., Ltd. 自発光感光性樹脂組成物、これから製造されたカラーフィルタおよび前記カラーフィルタを含む画像表示装置
JP2019532346A (ja) * 2016-11-15 2019-11-07 東友ファインケム株式会社Ｄｏｎｇｗｏｏ Ｆｉｎｅ−Ｃｈｅｍ Ｃｏ．， Ｌｔｄ． 感光性樹脂組成物、カラーフィルタ、及び画像表示装置
TWI840326B (zh) 2017-02-15 2024-05-01 日商東京應化工業股份有限公司 間隔壁用圖案的形成方法
KR20190127938A (ko) * 2017-03-30 2019-11-13 스미또모 가가꾸 가부시키가이샤 중합체 및 조성물
WO2018180445A1 (fr) * 2017-03-30 2018-10-04 住友化学株式会社 Polymère et composition
JP2018172637A (ja) * 2017-03-30 2018-11-08 住友化学株式会社 重合体及び組成物
KR102461802B1 (ko) 2017-03-30 2022-11-01 스미또모 가가꾸 가부시키가이샤 중합체 및 조성물
CN110945389A (zh) * 2017-07-28 2020-03-31 东丽株式会社 颜色转换组合物、颜色转换膜以及包含其的光源单元、显示器及照明
CN110945389B (zh) * 2017-07-28 2021-08-03 东丽株式会社 颜色转换组合物、颜色转换膜以及包含其的装置
US11459504B2 (en) 2017-07-28 2022-10-04 Toray Industries, Inc. Color conversion composition and color conversion film, and light source unit, display, and lighting including same
JPWO2019021813A1 (ja) * 2017-07-28 2019-07-25 東レ株式会社 色変換組成物、色変換フィルムならびにそれを含む光源ユニット、ディスプレイおよび照明
WO2019021813A1 (fr) * 2017-07-28 2019-01-31 東レ株式会社 Composition de conversion de couleur et film de conversion de couleur, et unité de source de lumière, unité d'affichage et éclairage la comprenant
WO2019181698A1 (fr) * 2018-03-23 2019-09-26 東レ株式会社 Composition de résine photosensible, film durci, carte de conversion de couleur, appareil d'affichage d'image et procédé de fabrication de film durci
KR20200135942A (ko) * 2018-03-23 2020-12-04 도레이 카부시키가이샤 감광성 수지 조성물, 경화막, 색변환 기판, 화상 표시 장치, 및 경화막의 제조 방법
JPWO2019181698A1 (ja) * 2018-03-23 2021-02-04 東レ株式会社 感光性樹脂組成物、硬化膜、色変換基板、画像表示装置、および硬化膜の製造方法
JP7259741B2 (ja) 2018-03-23 2023-04-18 東レ株式会社 感光性樹脂組成物、硬化膜、色変換基板、画像表示装置、および硬化膜の製造方法
KR102599290B1 (ko) 2018-03-23 2023-11-07 도레이 카부시키가이샤 감광성 수지 조성물, 경화막, 색변환 기판, 화상 표시 장치, 및 경화막의 제조 방법
WO2020217700A1 (fr) * 2019-04-25 2020-10-29 Jsr株式会社 Composition de résine photosensible

Similar Documents

Publication Publication Date Title
JP6834213B2 (ja) 樹脂組成物、膜、波長変換部材、及び膜の形成方法
WO2017018392A1 (fr) Composition de résine, film, élément de conversion de longueur d'onde et procédé de formation de film
KR102325621B1 (ko) 경화성 수지 조성물, 경화막, 파장 변환 필름, 발광층의 형성 방법 및 발광 표시 소자
KR102276034B1 (ko) 경화성 수지 조성물, 경화막, 발광 소자, 파장 변환 필름 및 발광층의 형성 방법
CN108445715B (zh) 固化性树脂组合物、固化膜及显示装置
JP6171923B2 (ja) 硬化性樹脂組成物、硬化膜、発光素子、波長変換フィルムおよび発光層の形成方法
JP6497251B2 (ja) 硬化膜形成用組成物、硬化膜、発光表示素子、硬化膜の形成方法及び分散液
JP2021170137A (ja) 量子ドット含有組成物、量子ドット製造方法およびカラーフィルタ
JP6427876B2 (ja) 感放射線性樹脂組成物、硬化膜、発光素子および発光層の形成方法
CN108445714B (zh) 固化性树脂组合物、固化膜及显示装置
JP2017032918A (ja) 硬化膜形成用組成物、硬化膜、発光表示素子、フィルム及び硬化膜の形成方法
WO2016098570A1 (fr) Élément électroluminescent organique, composition de résine durcissable, procédé de formation d'unité de conversion de longueur d'onde, et dispositif électroluminescent organique
JP6065665B2 (ja) 感放射線性樹脂組成物、硬化膜、発光表示素子および発光層の形成方法
CN110119066B (zh) 感光性树脂组合物、使用其的感光性树脂层及彩色滤光片
KR102197936B1 (ko) 경화성 수지 조성물, 경화막, 발광 소자, 파장 변환 필름 및 발광층의 형성 방법
CN108445716B (zh) 固化性树脂组合物、固化膜及显示装置
KR102195513B1 (ko) 경화성 수지 조성물, 경화막, 발광 소자 및 발광층의 형성 방법
JP6657684B2 (ja) 硬化膜形成用組成物、硬化膜、発光表示素子及び硬化膜の形成方法
CN112724959A (zh) 量子点、包括其的可固化组合物、固化层以及彩色滤光器

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16830497

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20177033673

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16830497

Country of ref document: EP

Kind code of ref document: A1