WO2017014131A1 - 非フッ素系ポリマー、撥水剤組成物、撥水性繊維製品及び撥水性繊維製品の製造方法 - Google Patents
非フッ素系ポリマー、撥水剤組成物、撥水性繊維製品及び撥水性繊維製品の製造方法 Download PDFInfo
- Publication number
- WO2017014131A1 WO2017014131A1 PCT/JP2016/070727 JP2016070727W WO2017014131A1 WO 2017014131 A1 WO2017014131 A1 WO 2017014131A1 JP 2016070727 W JP2016070727 W JP 2016070727W WO 2017014131 A1 WO2017014131 A1 WO 2017014131A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- group
- carbon atoms
- fiber product
- water
- meth
- Prior art date
Abstract
Description
表1~6に示される組成(表中、数値は(g)を示す)を有する混合液を、以下に示す手順により重合して、ポリマー分散液を得た。
500mLフラスコに、アクリル酸ステアリル20g、メタクリル酸ステアリル20g、塩化ビニル20g、ノイゲンXL-100(第一工業製薬株式会社製、ポリオキシアルキレン分岐デシルエーテル、HLB=14.7)2g、ノイゲンXL-60(第一工業製薬株式会社製、ポリオキシアルキレン分岐デシルエーテル、HLB=12.5)2g、ステアリルジメチルアミン塩酸塩3g、トリプロピレングリコール25g及び水207.70gを入れ、45℃にて混合攪拌し混合液とした。この混合液に超音波を照射して全単量体を乳化分散させた。次いで、アゾビス(イソブチルアミジン)二塩酸塩0.3gを混合液に添加し、窒素雰囲気下で60℃にて6時間ラジカル重合させて、ポリマー濃度20質量%の非フッ素系ポリマー分散液を得た。
表1~6に記載の材料を用いた以外は、実施例1と同様に重合を行い、表7~10に示すポリマー濃度の非フッ素系ポリマー分散液をそれぞれ得た。
ラテムルPD-420(花王株式会社製、ポリオキシアルキレンアルケニルエーテル、HLB=12.6)
ラテムルPD-430(花王株式会社製、ポリオキシアルキレンアルケニルエーテル、HLB=14.4)
カルダノールのエチレンオキサイド12.5モル付加物(HLB=12.9、表中、「カルダノール12.5EO」と示す)
カルダノールのエチレンオキサイド8.3モル付加物(HLB=11.0、表中、「カルダノール8.3EO」と示す)
ヒマシ油のエチレンオキサイド42モル付加物(HLB=13.3、表中、「ヒマシ油42EO」と示す)
ヒマシ油のエチレンオキサイド30モル付加物(HLB=11.7、表中、「ヒマシ油30EO」と示す)
実施例1~24及び比較例1~4で得られたポリマー分散液50gにアセトン500mLを加えることによりポリマーと乳化剤を分離させポリマーを濾取し、このポリマーを25℃にて24時間減圧乾燥させた。得られたポリマーを以下のように評価した。結果を表7~10に示す。
上記で得られた実施例及び比較例のポリマーについて、高架式フローテスターCFT-500((株)島津製作所製)を用い、ダイ(長さ10mm、直径1mm)を取り付けたシリンダー内にポリマーを1g入れ、105℃6分間保持し、プランジャーにより100kg・f/cm2の荷重を加えて105℃における溶融粘度を測定した。
上記で得られた実施例及び比較例のポリマーについて、GPC装置(東ソー(株)製GPC「HLC-8020」)により、カラム温度40℃、流量1.0ml/分の条件下で、溶離液にテトラヒドロフランを用いて測定し、標準ポリスチレン換算で重量平均分子量を測定した。なお、カラムは、東ソー(株)製の商品名TSK-GEL G5000HHR、G4000HHR、G3000HHRの3本を接続して装着した。
実施例及び比較例で得られたポリマー分散液を45℃で2週間保存した時の安定性を、以下の基準で評価した。結果を表7~10に示す。
A:外観変化のないもの
B:液面付近に油状物、容器壁面にポリマー析出物が僅かに認められるもの
C:ポリマーの沈降物、分離、ゲル化が認められるもの
JIS L 1092(1998)のスプレー法に準じてシャワー水温を27℃として試験をした。本試験においては、染色を行ったポリエステル100%布又はナイロン100%布を、実施例及び比較例のポリマー分散液をポリマーの含有量が3質量%となるように水で希釈した処理液に浸漬処理(ピックアップ率60質量%)した後、130℃で2分間乾燥し、更に表7~10に示すような条件で熱処理して、得られた布の撥水性を評価した。結果は目視にて下記の等級で評価した。なお、特性がわずかに良好な場合は等級に「+」をつけ、特性がわずかに劣る場合は等級に「-」をつけた。結果を表7~10に示す。
撥水性:状態
5:表面に付着湿潤のないもの
4:表面にわずかに付着湿潤を示すもの
3:表面に部分的湿潤を示すもの
2:表面に湿潤を示すもの
1:表面全体に湿潤を示すもの
0:表裏両面が完全に湿潤を示すもの
風合は、染色を行ったポリエステル100%布を、実施例及び比較例のポリマー分散液をポリマーの含有量が3質量%となるように水で希釈した処理液に浸漬処理(ピックアップ率60質量%)した後、130℃で2分間乾燥し、更に170℃で30秒間熱処理したものを用いて評価した。結果はハンドリングにて下記に示す5段階で評価した。結果を表7~10に示す。
1:硬い ~ 5:柔らかい
JIS L 1092(1998)のスプレー法に準じてシャワー水温を27℃として試験をした。本試験においては、染色を行ったポリエステル100%布を、ポリマーの含有量が3質量%、UNIKA RESIN 380-K(架橋剤、ユニオン化学工業株式会社製、トリメチロールメラミン樹脂)の含有量が0.3質量%及びUNIKA CATALYST 3-P(界面活性剤、ユニオン化学工業株式会社製、アミノアルコール塩酸塩)の含有量が0.2質量%となるように、実施例及び比較例のポリマー分散液及び上記各薬剤を水で希釈した処理液に浸漬処理(ピックアップ率60質量%)した後、130℃で2分間乾燥し、更に170℃で60秒間熱処理して得られた布(L-0)、及びJIS L 0217(1995)の103法による洗濯を10回(L-10)行った後の布の撥水性を上記撥水性評価方法と同様に評価した。また、ナイロン100%布の場合も、熱処理温度を170℃から160℃に変えたこと以外は、ポリエステル100%布の場合と同様に評価した。結果を表7~10に示す。
JIS K 6404-5(1999)に準拠して試験を行った。本試験においては、染色を行ったナイロン100%布を、実施例及び比較例のポリマー分散液をポリマー含有量が3質量%となるように水で希釈した処理液に、浸漬処理(ピックアップ率60質量%)した後、130℃で2分間乾燥し、更に160℃で30秒熱処理して得られたものを基布とした。その得られた基布に、熱圧着装置を用いて、ホットメルト接着テープ(サン化成株式会社製「MELCOテープ」)を150℃で1分間熱接着させ、基布とシームテープとの層間の剥離強度をオートグラフ(AG-IS、島津製作所(株)製)にて測定した。掴み具の移動速度を100mm/minで引っ張り、応力の平均値を剥離強度[N/inch]とした。結果を表7~10に示す。
Claims (8)
- (B1)HLBが7~18である下記一般式(I-1)で表される化合物、(B2)HLBが7~18である下記一般式(II-1)で表される化合物、及び(B3)HLBが7~18である、ヒドロキシル基及び重合性不飽和基を有する油脂に炭素数2~4のアルキレンオキサイドを付加した化合物のうちから選ばれる少なくとも1種の反応性乳化剤(B)に由来する構成単位を更に含有する、請求項1に記載の非フッ素系ポリマー。
- 前記乳化物又は前記分散物が、(B1)HLBが7~18である下記一般式(I-1)で表される化合物、(B2)HLBが7~18である下記一般式(II-1)で表される化合物、及び(B3)HLBが7~18である、ヒドロキシル基及び重合性不飽和基を有する油脂に炭素数2~4のアルキレンオキサイドを付加した化合物のうちから選ばれる少なくとも1種の反応性乳化剤(B)を更に含む、請求項3に記載の非フッ素系ポリマー。
- 前記(メタ)アクリル酸エステル単量体(A)が、アクリル酸エステル単量体(a1)とメタクリル酸エステル単量体(a2)とを含み、
前記(メタ)アクリル酸エステル単量体(A)に含まれる前記アクリル酸エステル単量体(a1)の質量と前記メタクリル酸エステル単量体(a2)の質量との比(a1)/(a2)が30/70~90/10である、請求項1~4のいずれか一項に記載の非フッ素系ポリマー。 - 請求項1~5のいずれか一項に記載の非フッ素系ポリマーを含む、撥水剤組成物。
- 請求項1~5のいずれか一項に記載の非フッ素系ポリマーが付着した繊維製品からなる、撥水性繊維製品。
- 繊維製品を、請求項6に記載の撥水剤組成物が含まれる処理液で処理する工程、を備える、撥水性繊維製品の製造方法。