WO2016208312A1 - リンス液、パターン形成方法、及び電子デバイスの製造方法 - Google Patents

リンス液、パターン形成方法、及び電子デバイスの製造方法 Download PDF

Info

Publication number
WO2016208312A1
WO2016208312A1 PCT/JP2016/065353 JP2016065353W WO2016208312A1 WO 2016208312 A1 WO2016208312 A1 WO 2016208312A1 JP 2016065353 W JP2016065353 W JP 2016065353W WO 2016208312 A1 WO2016208312 A1 WO 2016208312A1
Authority
WO
WIPO (PCT)
Prior art keywords
group
alkyl group
solvent
acetate
carbon atoms
Prior art date
Application number
PCT/JP2016/065353
Other languages
English (en)
French (fr)
Inventor
英明 椿
徹 土橋
亘 二橋
Original Assignee
富士フイルム株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 富士フイルム株式会社 filed Critical 富士フイルム株式会社
Priority to KR1020177036858A priority Critical patent/KR102061566B1/ko
Priority to JP2017524760A priority patent/JP6379292B2/ja
Publication of WO2016208312A1 publication Critical patent/WO2016208312A1/ja
Priority to US15/849,689 priority patent/US10599038B2/en

Abstract

高精度の微細パターンにおける、パターン倒れ性能とブリッジ性能を非常に高い次元で両立するために、感活性光線性又は感放射線性組成物から得られるレジスト膜に用いられるリンス液であって、分岐アルキル基を有する炭化水素系溶剤を含むリンス液、このリンス液を用いるパターン形成方法、及びこのパターン形成方法を含む電子デバイスの製造方法を提供する。

Description

リンス液、パターン形成方法、及び電子デバイスの製造方法
　本発明は、リンス液、パターン形成方法、及び電子デバイスの製造方法に関する。
　より詳細には、本発明は、ＩＣ等の半導体製造工程、液晶及びサーマルヘッド等の回路基板の製造、更にはその他のフォトファブリケーションのリソグラフィー工程などに使用される、レジスト膜パターニング用のリンス液、このリンス液を用いるパターン形成方法、及びこのパターン形成方法を含む電子デバイスの製造方法に関する。
　従来、ＩＣ（Ｉｎｔｅｇｒａｔｅｄ　Ｃｉｒｃｕｉｔ、集積回路）やＬＳＩ（Ｌａｒｇｅ　Ｓｃａｌｅ　Ｉｎｔｅｇｒａｔｅｄ　ｃｉｒｃｕｉｔ、大規模集積回路）などの半導体デバイスの製造プロセスにおいては、フォトレジスト組成物を用いたリソグラフィーによる微細加工が行われている。近年、集積回路の高集積化に伴い、サブミクロン領域やクオーターミクロン領域の超微細パターン形成が要求されるようになってきている。それに伴い、露光波長もｇ線からｉ線に、更にＫｒＦエキシマレーザー光に、というように短波長化の傾向が見られる。更には、現在では、エキシマレーザー光以外にも、電子線やＸ線、あるいはＥＵＶ光（Ｅｘｔｒｅｍｅ　Ｕｌｔｒａ　Ｖｉｏｌｅｔ、極紫外線）を用いたリソグラフィーも開発が進んでいる。
　このようなリソグラフィーにおいては、フォトレジスト組成物（感活性光線又は感放射線性組成物とも呼ばれる）により膜を形成した後、得られた膜を現像液により現像したり、現像後の膜をリンス液で洗浄することが行われている。
　例えば、特許文献１には、有機溶剤を含むリンス液を用いてリンスする工程を含むパターン形成方法が開示されている。
日本国特開２０１０－２１７８８４号公報
　近年、高集積かつ高精度な電子デバイスを製造するために、高精度（例えば、線幅２０ｎｍ以下）の微細パターンを安定的に形成する方法が求められている。
　本発明は、高精度（例えば、線幅２０ｎｍ以下）の微細パターンにおける、パターン倒れ性能とブリッジ性能を非常に高い次元で両立するためにレジスト膜に用いられるリンス液、このリンス液を用いるパターン形成方法、及びこのパターン形成方法を含む電子デバイスの製造方法を提供することを目的とする。
　パターン形成方法におけるリンス工程は、現像工程で生じた現像残渣をリンス液で洗い流すために行われるが、高精度（例えば、線幅２０ｎｍ以下）の微細パターンの形成においては、パターン倒れ性能とブリッジ性能の両立のために、現像残渣の洗浄に加えて、パターンにわずかに染込んだ現像液を取り除くことで、パターンの膨潤を抑制することも重要であることが分かった。そして、分岐アルキル基を有する炭化水素系溶剤を含むリンス液を用いることにより、現像残渣の洗浄とパターンの膨潤抑制の両方を達成することができることを見出した。
　詳細な理由は定かではないが、本発明者らは以下のように推定している。分岐アルキル基を有する炭化水素系溶剤を含むリンス液により、現像後にわずかにレジスト膜に染み込んでいた現像液が、疎水的なリンス液中へと洗い流されて、膜の膨潤が抑制されることに加えて、分岐型構造による立体障壁により、リンス液自体のレジスト膜への浸透が抑制され、より膨潤抑止効果が発揮されたものと考えられる。膨潤抑制により、パターン間の距離の減少が抑制されることで、隣接パターン同士の接着に起因したブリッジと、毛管力に起因したパターン倒れを抑制できたものと考えられる。
　すなわち、以下の手段により上記課題を解決できる。
＜１＞
　感活性光線性又は感放射線性組成物から得られるレジスト膜に用いられるリンス液であって、分岐アルキル基を有する炭化水素系溶剤を含むリンス液。
＜２＞
　上記分岐アルキル基を有する炭化水素系溶剤の炭素原子数が１０以上である、＜１＞に記載のリンス液。
＜３＞
　上記分岐アルキル基を有する炭化水素系溶剤が、イソデカン及びイソドデカンの少なくとも１種を含む、＜１＞又は＜２＞に記載のリンス液。
＜４＞
　感活性光線性又は感放射線性組成物を用いてレジスト膜を形成するレジスト膜形成工程と、
　上記レジスト膜を露光する露光工程と、
　露光された上記レジスト膜を有機溶剤を含む現像液を用いて現像する工程と、
　上記現像されたレジスト膜を＜１＞～＜３＞のいずれか１項に記載のリンス液を用いてリンスする工程と、をこの順で有する、パターン形成方法。
＜５＞
　上記現像液に含まれる有機溶剤がエステル系溶剤である、＜４＞に記載のパターン形成方法。
＜６＞
　上記現像液に含まれる有機溶剤が、酢酸ブチル、酢酸ペンチル、及び酢酸イソアミルからなる群より選ばれる１種以上を含む、＜４＞又は＜５＞に記載のパターン形成方法。
＜７＞
　上記感活性光線性又は感放射線性組成物が、下記一般式（１）で表される繰り返し単位を含有する樹脂を含有する、＜４＞～＜６＞のいずれか１項に記載のパターン形成方法。
Figure JPOXMLDOC01-appb-C000002
　一般式（１）中、
　Ａは水素原子、アルキル基、シクロアルキル基、ハロゲン原子、又はシアノ基を表す。
　Ｒは、ハロゲン原子、アルキル基、シクロアルキル基、アリール基、アルケニル基、アラルキル基、アルコキシ基、アルキルカルボニルオキシ基、アルキルスルホニルオキシ基、アルキルオキシカルボニル基又はアリールオキシカルボニル基を表し、複数個ある場合には同じであっても異なっていてもよい。複数のＲを有する場合には、互いに共同して環を形成していてもよい。
　ａは１～３の整数を表す。
　ｂは０～（３－ａ）の整数を表す。
＜８＞
　上記露光が、電子線又は極紫外線を用いて行われる、＜４＞～＜７＞のいずれか１項に記載のパターン形成方法。
＜９＞
　＜４＞～＜８＞のいずれか１項に記載のパターン形成方法を含む、電子デバイスの製造方法。
　高精度（例えば、線幅２０ｎｍ以下）の微細パターンにおける、パターン倒れ性能とブリッジ性能を非常に高い次元で両立するためにレジスト膜に用いられるリンス液、このリンス液を用いるパターン形成方法、及びこのパターン形成方法を含む電子デバイスの製造方法を提供することができる。
　以下に、本発明を実施するための形態の一例を説明する。
　なお、本明細書において「～」を用いて表される数値範囲は、「～」の前後に記載される数値を下限値及び上限値として含む範囲を意味する。
　本発明において「活性光線」又は「放射線」とは、例えば、水銀灯の輝線スペクトル、エキシマレーザーに代表される遠紫外線、極紫外線、Ｘ線、電子線等を意味する。また、本発明において「光」とは、活性光線又は放射線を意味する。本明細書中における「露光」とは、特に断らない限り、水銀灯、エキシマレーザーに代表される遠紫外線、Ｘ線、極紫外線（ＥＵＶ光）等による露光のみならず、ＥＢ（電子線）及びイオンビーム等の粒子線による描画も露光に含める。
　なお、本明細書に於ける基（原子団）の表記において、置換又は無置換を記していない表記は、置換基を有していないものと共に置換基を有するものをも包含するものである。例えば、「アルキル基」とは、置換基を有さないアルキル基（無置換アルキル基）のみならず、置換基を有するアルキル基（置換アルキル基）をも包含するものである。
　本明細書では、「（メタ）アクリル系モノマー」とは、「ＣＨ２＝ＣＨ－ＣＯ－」又は「ＣＨ２＝Ｃ（ＣＨ３）－ＣＯ－」の構造を有するモノマーの少なくとも１種を意味する。同様に「（メタ）アクリレート」及び「（メタ）アクリル酸」とは、それぞれ「アクリレート及びメタクリレートの少なくとも１種」並びに「アクリル酸及びメタクリル酸の少なくとも１種」を意味する。
　本明細書において、樹脂の重量平均分子量は、ＧＰＣ（ゲルパーミエーションクロマトグラフィー）法により測定したポリスチレン換算値である。ＧＰＣは、ＨＬＣ－８１２０（東ソー（株）製）を用い、カラムとしてＴＳＫ　ｇｅｌ　Ｍｕｌｔｉｐｏｒｅ　ＨＸＬ－Ｍ　（東ソー（株）製、７．８ｍｍＩＤ×３０．０ｃｍ）を、溶離液としてＴＨＦ（テトラヒドロフラン）を用いた方法に準ずる事ができる。
　＜リンス液＞
　本発明のリンス液は、感活性光線性又は感放射線性組成物から得られるレジスト膜に用いられるリンス液であって、分岐アルキル基を有する炭化水素系溶剤を含むリンス液である。
　本発明のリンス液は、後述するパターン形成方法におけるリンス工程で用いることができる。
　分岐アルキル基を有する炭化水素系溶剤としては、例えば、２，２，４－トリメチルペンタン、２，２，３－トリメチルヘキサン、イソヘキサン、イソヘプタン、イソオクタン、イソデカン、イソドデカン、イソウンデカン、イソヘキサデカン、イソテトラデカン、イソペンタデカン、リモネン、イソプロピルシクロペンタン、ｔｅｒｔ－ブチルシクロヘキサンが挙げられる。
　分岐アルキル基を有する炭化水素系溶剤としては、分岐鎖状脂肪族炭化水素系溶剤が好ましく、２，２，４－トリメチルペンタン、２，２，３－トリメチルヘキサン、イソヘキサン、イソヘプタン、イソオクタン、イソデカン、イソドデカン、イソウンデカン、イソヘキサデカン、イソテトラデカン、イソペンタデカンが好ましい。
　分岐アルキル基を有する炭化水素系溶剤は、好ましくは、炭素原子数が１０以上であることが好ましい。例えば、イソデカン、イソドデカン、イソウンデカン、イソヘキサデカン、イソテトラデカン、イソペンタデカンが好ましく、特に好ましくは、イソデカン、イソドデカンである。本発明のリンス液は、イソデカン及びイソドデカンの少なくとも１種を含むことが特に好ましい。炭素原子数が１０以上の分岐アルキル基を有する炭化水素系溶剤とすることで、良好なパターン倒れ特性と良好なブリッジ特性を両立することができる。
　分岐アルキル基を有する炭化水素系溶剤の炭素原子数の上限値は特に限定されないが、例えば、１６以下が挙げられ、１４以下が好ましく、１２以下がより好ましい。これにより、スピンドライ時の乾燥効率が向上し、ウエハ面内での欠陥発生を抑制できる。
　リンス液は、分岐アルキル基を有する炭化水素系溶剤を１種のみ含んでいてもよいし、２種以上を含んでいてもよい。
　なお、分岐アルキル基を有する炭化水素系溶剤は、同じ炭素数で異なる構造の化合物の混合物であってもよい。例えば、分岐アルキル基を有する炭化水素系溶剤としてデカンを使用した場合、同じ炭素数で異なる構造の化合物である２－メチルノナン、２，２－ジメチルオクタン、４－エチルオクタン、イソデカンなどが分岐アルキル基を有する炭化水素系溶剤に含まれていてもよい。
　また、上記同じ炭素数で異なる構造の化合物は、１種のみが含まれていてもよいし、上記のように複数種含まれていてもよい。
　リンス液の蒸気圧は、２０℃において０．０５ｋＰａ以上、５ｋＰａ以下が好ましく、０．１ｋＰａ以上、５ｋＰａ以下が更に好ましく、０．１２ｋＰａ以上、３ｋＰａ以下が最も好ましい。リンス液が複数の溶剤の混合溶剤である場合は全体としての蒸気圧が上記範囲であることが好ましい。リンス液の蒸気圧を０．０５ｋＰａ以上、５ｋＰａ以下にすることにより、ウエハ面内の温度均一性が向上し、更にはリンス液の浸透に起因した膨潤が抑制され、ウエハ面内の寸法均一性が良化する。
　リンス液のＳＰ値（Ｓｏｌｕｂｉｌｉｔｙ　Ｐａｒａｍｅｔｅｒ）の極性項δｐは、０～３が好ましく、０～２がより好ましく、０～１が更に好ましい。リンス液のＳＰ値の極性項δｐが０～３であると、パターンの膨潤抑制の観点から好ましく、現像残渣の洗浄とパターンの膨潤抑制の両方を達成することができる。ＳＰ値の極性項δｐは、以下の文献に記載の値を用いる：Ｈａｎｓｅｎ，Ｃｈａｒｌｅｓ（２００７）．Ｈａｎｓｅｎ　Ｓｏｌｕｂｉｌｉｔｙ　Ｐａｒａｍｅｔｅｒｓ：Ａ　ｕｓｅｒ’ｓ　ｈａｎｄｂｏｏｋ，Ｓｅｃｏｎｄ　Ｅｄｉｔｉｏｎ．Ｂｏｃａ　Ｒａｔｏｎ，Ｆｌａ：ＣＲＣ　Ｐｒｅｓｓ．
　リンス液において、硫黄原子を含む成分は１０ｍｍｏｌ／Ｌ以下であることが好ましい。
　リンス液における分岐アルキル基を有する炭化水素系溶剤の含有量は、リンス液の全質量に対して６０質量％以上であることが好ましく、８０質量％以上であることがより好ましく、９０質量％以上であることが更に好ましく、９５質量％以上であることが特に好ましい。リンス液における分岐アルキル基を有する炭化水素系溶剤の含有量を６０質量％以上にすることで、パターン倒れ性能が更に良化する。
　リンス液は、分岐アルキル基を有する炭化水素系溶剤以外の溶剤を含んでいてもよい。
　リンス液が含んでもよい分岐アルキル基を有する炭化水素系溶剤以外の溶剤としては、種々の有機溶剤が挙げられ、分岐アルキル基を有する炭化水素系溶剤以外の炭化水素系溶剤、ケトン系溶剤、エステル系溶剤、アルコール系溶剤、アミド系溶剤及びエーテル系溶剤からなる群より選択される少なくとも１種の有機溶剤を用いることが好ましい。
　エステル系溶剤とは分子内にエステル結合を有する溶剤のことであり、ケトン系溶剤とは分子内にケトン基を有する溶剤のことであり、アルコール系溶剤とは分子内にアルコール性水酸基を有する溶剤のことであり、アミド系溶剤とは分子内にアミド結合を有する溶剤のことであり、エーテル系溶剤とは分子内にエーテル結合を有する溶剤のことである。これらの中には、１分子内に上記官能基を複数種有する溶剤も存在するが、その場合は、その溶剤の有する官能基を含むいずれの溶剤種にも当てはまるものとする。例えば、ジエチレングリコールモノメチルエーテルは、上記分類中の、アルコール系溶剤、エーテル系溶剤いずれにも当てはまるものとする。
　エステル系溶剤としては、例えば、酢酸メチル、酢酸エチル、酢酸ブチル、酢酸イソブチル、酢酸ペンチル、酢酸プロピル、酢酸イソプロピル、酢酸アミル（酢酸ペンチル）、酢酸イソアミル（酢酸イソペンチル、酢酸３－メチルブチル）、酢酸２－メチルブチル、酢酸１－メチルブチル、酢酸ヘキシル、酢酸イソヘキシル、酢酸ヘプチル、酢酸オクチル、メトキシ酢酸エチル、エトキシ酢酸エチル、プロピレングリコールモノメチルエーテルアセテート（ＰＧＭＥＡ；別名１－メトキシ－２－アセトキシプロパン）、エチレングリコールモノエチルエーテルアセテート、エチレングリコールモノプロピルエーテルアセテート、エチレングリコールモノブチルエーテルアセテート、エチレングリコールモノフェニルエーテルアセテート、ジエチレングリコールモノメチルエーテルアセテート、ジエチレングリコールモノプロピルエーテルアセテート、ジエチレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノフェニルエーテルアセテート、ジエチレングリコールモノブチルエーテルアセテート、ジエチレングリコールモノエチルエーテルアセテート、２－メトキシブチルアセテート、３－メトキシブチルアセテート、４－メトキシブチルアセテート、３－メチル－３－メトキシブチルアセテート、３－エチル－３－メトキシブチルアセテート、プロピレングリコールモノエチルエーテルアセテート、プロピレングリコールモノプロピルエーテルアセテート、２－エトキシブチルアセテート、４－エトキシブチルアセテート、４－プロポキシブチルアセテート、２－メトキシペンチルアセテート、３－メトキシペンチルアセテート、４－メトキシペンチルアセテート、２－メチル－３－メトキシペンチルアセテート、３－メチル－３－メトキシペンチルアセテート、３－メチル－４－メトキシペンチルアセテート、４－メチル－４－メトキシペンチルアセテート、プロピレングリコールジアセテート、蟻酸メチル、蟻酸エチル、蟻酸ブチル、蟻酸プロピル、乳酸エチル、乳酸ブチル、乳酸プロピル、炭酸エチル、炭酸プロピル、炭酸ブチル、ピルビン酸メチル、ピルビン酸エチル、ピルビン酸プロピル、ピルビン酸ブチル、アセト酢酸メチル、アセト酢酸エチル、プロピオン酸メチル、プロピオン酸エチル、プロピオン酸プロピル、プロピオン酸イソプロピル、プロピオン酸ブチル、プロピオン酸ペンチル、プロピオン酸ヘキシル、プロピオン酸ヘプチル、ブタン酸ブチル、ブタン酸イソブチル、ブタン酸ペンチル、ブタン酸ヘキシル、イソブタン酸イソブチル、ペンタン酸プロピル、ペンタン酸イソプロピル、ペンタン酸ブチル、ペンタン酸ペンチル、ヘキサン酸エチル、ヘキサン酸プロピル、ヘキサン酸ブチル、ヘキサン酸イソブチル、ヘプタン酸メチル、ヘプタン酸エチル、ヘプタン酸プロピル、酢酸シクロヘキシル、酢酸シクロヘプチル、酢酸２－エチルヘキシル、プロピオン酸シクロペンチル、２－ヒドロキシプロピオン酸メチル、２－ヒドロキシプロピオン酸エチル、メチル－３－メトキシプロピオネート、エチル－３－メトキシプロピオネート、エチル－３－エトキシプロピオネート、プロピル－３－メトキシプロピオネート等を挙げることができる。これらの中でも、酢酸ブチル、酢酸アミル、酢酸イソアミル、酢酸２－メチルブチル、酢酸１－メチルブチル、酢酸ヘキシル、プロピオン酸ペンチル、プロピオン酸ヘキシル、プロピオン酸ヘプチル、ブタン酸ブチルが好ましく用いられ、酢酸イソアミルが特に好ましく用いられる。
　ケトン系溶剤としては、例えば、１－オクタノン、２－オクタノン、１－ノナノン、２－ノナノン、アセトン、２－ヘプタノン、４－ヘプタノン、１－ヘキサノン、２－ヘキサノン、ジイソブチルケトン、シクロヘキサノン、メチルシクロヘキサノン、フェニルアセトン、メチルエチルケトン、メチルイソブチルケトン、アセチルアセトン、アセトニルアセトン、イオノン、ジアセトニルアルコール、アセチルカービノール、アセトフェノン、メチルナフチルケトン、イソホロン、プロピレンカーボネート、γ－ブチロラクトン等を挙げることができ、中でも２－ヘプタノンが好ましい。
　アルコール系溶剤としては、例えば、メタノール、エタノール、１－プロパノール、イソプロパノール、１－ブタノール、２－ブタノール、３－メチル－１－ブタノール、ｔｅｒｔ―ブチルアルコール、１－ペンタノール、２－ペンタノール、１－ヘキサノール、１－ヘプタノール、１－オクタノール、１－デカノール、２－ヘキサノール、２－ヘプタノール、２－オクタノール、３－ヘキサノール、３－ヘプタノール、３－オクタノール、４－オクタノール、３－メチル－３－ペンタノール、シクロペンタノール、２，３－ジメチル－２－ブタノール、３，３－ジメチル－２－ブタノール、２－メチル－２－ペンタノール、２－メチル－３－ペンタノール、３－メチル－２－ペンタノール、３－メチル－３－ペンタノール、４－メチル－２－ペンタノール、４－メチル－３－ペンタノール、シクロヘキサノール、５－メチル－２－ヘキサノール、４－メチル－２－ヘキサノール、４，５－ジチル－２－ヘキサール、６－メチル－２－ヘプタノール、７－メチル－２－オクタノール、８－メチル－２－ノナール、９－メチル－２－デカノール、３－メトキシ－１－ブタノール等のアルコール（１価のアルコール）や、エチレングリコール、ジエチレングリコール、トリエチレングリコール等のグリコール系溶剤や、エチレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテル（ＰＧＭＥ；別名１－メトキシ－２－プロパノール）、ジエチレングリコールモノメチルエーテル、トリエチレングリコールモノエチルエーテル、メトキシメチルブタノール、エチレングリコールモノエチルエーテル、エチレングリコールモノプロピルエーテル、エチレングリコールモノブチルエーテル、プロピレングリコールモノエチルエーテル、プロピレングリコールモノプロピルエーテル、プロピレングリコールモノブチルエーテル、プロピレングリコールモノフェニルエーテル等の水酸基を含有するグリコールエーテル系溶剤等を挙げることができる。これらの中でもグリコールエーテル系溶剤を用いることが好ましい。
　エーテル系溶剤としては、例えば、上記水酸基を含有するグリコールエーテル系溶剤の他、プロピレングリコールジメチルエーテル、プロピレングリコールジエチルエーテル、ジエチレングリコールジメチルエーテル、ジエチレングリコールジエチルエーテル等の水酸基を含有しないグリコールエーテル系溶剤、アニソール、フェネトール等の芳香族エーテル溶剤、ジオキサン、テトラヒドロフラン、テトラヒドロピラン、パーフルオロ－２－ブチルテトラヒドロフラン、パーフルオロテトラヒドロフラン、１，４－ジオキサン、イソプロピルエーテル等が挙げられる。好ましくは、グリコールエーテル系溶剤、又はアニソールなどの芳香族エーテル溶剤を用いる。
　アミド系溶剤としては、例えば、Ｎ－メチル－２－ピロリドン、Ｎ，Ｎ－ジメチルアセトアミド、Ｎ，Ｎ－ジメチルホルムアミド、ヘキサメチルホスホリックトリアミド、１，３－ジメチル－２－イミダゾリジノン等が使用できる。
　分岐アルキル基を有する炭化水素系溶剤以外の炭化水素系溶剤としては、例えば、ペンタン、ヘキサン、オクタン、ノナン、デカン、ドデカン、ウンデカン、ヘキサデカン、パーフルオロヘキサン、パーフルオロヘプタン等の脂肪族炭化水素系溶剤、トルエン、キシレン、エチルベンゼン、プロピルベンゼン、１－メチルプロピルベンゼン、２－メチルプロピルベンゼン、ジメチルベンゼン、ジエチルベンゼン、エチルメチルベンゼン、トリメチルベンゼン、エチルジメチルベンゼン、ジプロピルベンゼンなどの芳香族炭化水素系溶剤、オクテン、ノネン、デセン、ウンデセン、ドデセン、ヘキサデセン、などの不飽和炭化水素系溶剤が挙げられる。
　不飽和炭化水素系溶剤が有する二重結合、三重結合は複数でもよく、炭化水素鎖のどの位置に有しても良い。二重結合を有することによるＣｉｓ、ｔｒａｎｓ体が混合しても良い。
　リンス液に、分岐アルキル基を有する炭化水素系溶剤以外の溶剤を含有する場合、分岐アルキル基を有する炭化水素系溶剤以外の溶剤の含有量はリンス液の全質量に対して４０質量％以下であることが好ましく、より好ましくは２０質量％以下であり、更に好ましくは１０質量％以下であり、特に好ましくは５質量％以下である。分岐アルキル基を有する炭化水素系溶剤以外の溶剤の含有量を４０質量％以下にすることで、パターン倒れ性能を更に良化することができる。
　リンス液は、界面活性剤を含有しても良い。リンス液が界面活性剤を含有することにより、レジスト膜に対する濡れ性が向上して、リンス性が向上し、異物の発生が抑制される傾向にある。
　界面活性剤としては、後述する感活性光線又は感放射線性組成物に用いられる界面活性剤と同様のものを用いることができる。
　リンス液が界面活性剤を含有する場合、界面活性剤の含有量は、リンス液の全質量に対して、０．００１～５質量％が好ましく、より好ましくは０．００５～２質量％であり、更に好ましくは０．０１～０．５質量％である。
　リンス液は、酸化防止剤を含有することが好ましい。リンス液が酸化防止剤を含有することにより、経時的な酸化剤の発生を抑制でき、経時での液の劣化を抑止することができる。
　酸化防止剤としては、公知のものが使用できるが、半導体用途に用いる場合、アミン系酸化防止剤、フェノール系酸化防止剤が好ましく用いられる。
　アミン系酸化防止剤としては、例えば、１－ナフチルアミン、フェニル－１－ナフチルアミン、ｐ－オクチルフェニル－１－ナフチルアミン、ｐ－ノニルフェニル－１－ナフチルアミン、ｐ－ドデシルフェニル－１－ナフチルアミン、フェニル－２－ナフチルアミン等のナフチルアミン系酸化防止剤；Ｎ，Ｎ'－ジイソプロピル－ｐ－フェニレンジアミン、Ｎ，Ｎ'－ジイソブチル－ｐ－フェニレンジアミン、Ｎ，Ｎ'－ジフェニル－ｐ－フェニレンジアミン、Ｎ，Ｎ'－ジ－β－ナフチル－ｐ－フェニレンジアミン、Ｎ－フェニル－Ｎ'－イソプロピル－ｐ－フェニレンジアミン、Ｎ－シクロヘキシル－Ｎ'－フェニル－ｐ－フェニレンジアミン、Ｎ－１，３－ジメチルブチル－Ｎ'－フェニル－ｐ－フェニレンジアミン、ジオクチル－ｐ－フェニレンジアミン、フェニルヘキシル－ｐ－フェニレンジアミン、フェニルオクチル－ｐ－フェニレンジアミン等のフェニレンジアミン系酸化防止剤；ジピリジルアミン、ジフェニルアミン、ｐ，ｐ'－ジ－ｎ－ブチルジフェニルアミン、ｐ，ｐ'－ジ－ｔ－ブチルジフェニルアミン、ｐ，ｐ'－ジ－ｔ－ペンチルジフェニルアミン、ｐ，ｐ'－ジオクチルジフェニルアミン、ｐ，ｐ'－ジノニルジフェニルアミン、ｐ，ｐ'－ジデシルジフェニルアミン、ｐ，ｐ'－ジドデシルジフェニルアミン、ｐ，ｐ'－ジスチリルジフェニルアミン、ｐ，ｐ'－ジメトキシジフェニルアミン、４，４'－ビス（４－α，α－ジメチルベンゾイル）ジフェニルアミン、ｐ－イソプロポキシジフェニルアミン、ジピリジルアミン等のジフェニルアミン系酸化防止剤；フェノチアジン、Ｎ－メチルフェノチアジン、Ｎ－エチルフェノチアジン、３，７－ジオクチルフェノチアジン、フェノチアジンカルボン酸エステル、フェノセレナジン等のフェノチアジン系酸化防止剤が挙げられる。
　フェノール系酸化防止剤としては、例えば、例えば、２，６－ジ－ターシャリブチルフェノール（以下、ターシャリブチルをｔ－ブチルと略記する。）、２，６－ジ－ｔ－ブチル－ｐ－クレゾール、２，６－ジ－ｔ－ブチル－４－メチルフェノール、２，６－ジ－ｔ－ブチル－４－エチルフェノール、２，４－ジメチル－６－ｔ－ブチルフェノール、４，４’－メチレンビス（２，６－ジ－ｔ－ブチルフェノール）、４，４’－ビス（２，６－ジ－ｔ－ブチルフェノール）、４，４’－ビス（２－メチル－６－ｔ－ブチルフェノール）、２，２’－メチレンビス（４－メチル－６－ｔ－ブチルフェノール）、２，２’－メチレンビス（４－エチル－６－ｔ－ブチルフェノール）、４，４’－ブチリデンビス（３－メチル－６－ｔ－ブチルフェノール）、４，４’－イソプロピリデンビス（２，６－ジ－ｔ－ブチルフェノール）、２，２’－メチレンビス（４－メチル－６－シクロヘキシルフェノール）、２，２’－メチレンビス（４－メチル－６－ノニルフェノール）、２，２’－イソブチリデンビス（４，６－ジメチルフェノール）、２，６－ビス（２’－ヒドロキシ－３’－ｔ－ブチル－５’－メチルベンジル）－４－メチルフェノール、３－ｔ－ブチル－４－ヒドロキシアニソール、２－ｔ－ブチル－４－ヒドロキシアニソール、３－（４－ヒドロキシ－３，５－ジ－ｔ－ブチルフェニル）プロピオン酸オクチル、３－（４－ヒドロキシ－３，５－ジ－ｔ－ブチルフェニル）プロピオン酸ステアリル、３－（４－ヒドロキシ－３，５－ジ－ｔ－ブチルフェニル）プロピオン酸オレイル、３－（４－ヒドロキシ－３，５－ジ－ｔ－ブチルフェニル）プロピオン酸ドデシル、３－（４－ヒドロキシ－３，５－ジ－ｔ－ブチルフェニル）プロピオン酸デシル、３－（４－ヒドロキシ－３，５－ジ－ｔ－ブチルフェニル）プロピオン酸オクチル、テトラキス｛３－（４－ヒドロキシ－３，５－ジ－ｔ－ブチルフェニル）プロピオニルオキシメチル｝メタン、３－（４－ヒドロキシ－３，５－ジ－ｔ－ブチルフェニル）プロピオン酸グリセリンモノエステル、３－（４－ヒドロキシ－３，５－ジ－ｔ－ブチルフェニル）プロピオン酸とグリセリンモノオレイルエーテルとのエステル、３－（４－ヒドロキシ－３，５－ジ－ｔ－ブチルフェニル）プロピオン酸ブチレングリコールジエステル、３－（４－ヒドロキシ－３，５－ジ－ｔ－ブチルフェニル）プロピオン酸チオジグリコールジエステル、４，４’－チオビス（３－メチル－６－ｔ－ブチルフェノール）、４，４’－チオビス（２－メチル－６－ｔ－ブチルフェノール）、２，２’－チオビス（４－メチル－６－ｔ－ブチルフェノール）、２，６－ジ－ｔ－ブチル－α－ジメチルアミノ－ｐ－クレゾール、２，６－ジ－ｔ－ブチル－４－（Ｎ，Ｎ’－ジメチルアミノメチルフェノール）、ビス（３，５－ジ－ｔ－ブチル－４－ヒドロキシベンジル）サルファイド、トリス｛（３，５－ジ－ｔ－ブチル－４－ヒドロキシフェニル）プロピオニル―オキシエチル｝イソシアヌレート、トリス（３，５－ジ－ｔ－ブチル－４－ヒドロキシフェニル）イソシアヌレート、１，３，５－トリス（３，５－ジ－ｔ－ブチル－４－ヒドロキシベンジル）イソシアヌレート、ビス｛２－メチル－４－（３－ｎ－アルキルチオプロピオニルオキシ）－５－ｔ－ブチルフェニル｝サルファイド、１，３，５－トリス（４－ｔ－ブチル－３－ヒドロキシ－２，６―ジメチルベンジル）イソシアヌレート、テトラフタロイル―ジ（２，６－ジメチル－４－ｔ－ブチル－３－ヒドロキシベンジルサルファイド）、６－（４－ヒドロキシ－３，５－ジ－ｔ－ブチルアニリノ）－２，４－ビス（オクチルチオ）－１，３，５―トリアジン、２，２－チオ－｛ジエチル－ビス－３－（３，５－ジ－ｔ－ブチル－４－ヒドロキシフェニル）｝プロピオネート、Ｎ，Ｎ’－ヘキサメチレンビス（３，５－ジ－ｔ－ブチル－４－ヒドロキシ－ヒドロシナミド）、３，９－ビス〔１，１－ジメチル－２－｛β－（３－ｔ－ブチル－４－ヒドロキシ－５－メチルフェニル）プロピオニルオキシ｝エチル〕－２，４，８，１０－テトラオキサスピロ［５，５］ウンデカン、１，１，３－トリス（２－メチル－４－ヒドロキシ－５－ｔ－ブチルフェニル）ブタン、１，３，５－トリメチル－２，４，６－トリス（３，５－ジ－ｔ－ブチル－４－ヒドロキシベンジル）ベンゼン、ビス｛３，３’－ビス－（４’－ヒドロキシ－３’－ｔ－ブチルフェニル）ブチリックアシッド｝グリコールエステル等が挙げられる。
　リンス液が酸化防止剤を含有する場合、酸化防止剤の含有量は、特に限定されないが、リンス液の全質量に対して、０．０００１～１質量％が好ましく、０．０００１～０．１質量％がより好ましく、０．０００１～０．０１質量％が更に好ましい。
＜パターン形成方法＞
　本発明のパターン形成方法は、
　感活性光線性又は感放射線性組成物を用いてレジスト膜を形成するレジスト膜形成工程と、
　レジスト膜を露光する露光工程と、
　露光されたレジスト膜を有機溶剤を含む現像液を用いて現像する工程と、
　現像されたレジスト膜を分岐アルキル基を有する炭化水素系溶剤を含むリンス液を用いてリンスする工程と、をこの順で有する、パターン形成方法である。
　以下、本発明のパターン形成方法が有する各工程について説明する。
　＜レジスト膜形成工程＞
　レジスト膜形成工程は、感活性光線性又は感放射線性組成物（「レジスト組成物」ともいう）を用いてレジスト膜を形成する工程であり、例えば次の方法により行うことができる。なお、レジスト組成物については後述する。
　レジスト組成物を用いて基板上にレジスト膜（感活性光線性又は感放射線性組成物膜）を形成するためには、後述する各成分を溶剤に溶解してレジスト組成物を調製し、必要に応じてフィルター濾過した後、基板上に塗布する。フィルターとしては、ポアサイズ０．１μｍ以下、より好ましくは０．０５μｍ以下、更に好ましくは０．０３μｍ以下のポリテトラフロロエチレン製、ポリエチレン製、ナイロン製のものが好ましい。
　レジスト組成物は、集積回路素子の製造に使用されるような基板（例：シリコン、二酸化シリコン被覆）上に、スピナー等の適当な塗布方法により塗布される。その後、乾燥し、レジスト膜を形成する。必要により、レジスト膜の下層に、各種下地膜（無機膜、有機膜、反射防止膜）を形成してもよい。
　乾燥方法としては、加熱して乾燥する方法が一般的に用いられる。加熱は通常の露光・現像機に備わっている手段で行うことができ、ホットプレート等を用いて行ってもよい。加熱温度は８０～１５０℃で行うことが好ましく、８０～１４０℃で行うことがより好ましく、８０～１３０℃で行うことが更に好ましい。加熱時間は３０～１０００秒が好ましく、６０～８００秒がより好ましく、６０～６００秒が更に好ましい。
　レジスト膜の膜厚は、一般的には２００ｎｍ以下であり、好ましくは１００ｎｍ以下である。
　例えば線幅２０ｎｍ以下の１：１ラインアンドスペースパターンを解像させるためには、形成されるレジスト膜の膜厚が５０ｎｍ以下であることが好ましい。膜厚が５０ｎｍ以下であれば、後述する現像工程を適用した際に、パターン倒れがより起こりにくくなり、より優れた解像性能が得られる。
　膜厚の範囲としてより好ましくは、１５ｎｍから４５ｎｍの範囲である。膜厚が１５ｎｍ以上であれば、十分なエッチング耐性が得られる。膜厚の範囲として更に好ましくは、１５ｎｍから４０ｎｍである。膜厚がこの範囲にあると、エッチング耐性とより優れた解像性能とを同時に満足させることができる。
　なお、本発明のパターン形成方法においては、レジスト膜の上層にトップコートを形成してもよい。トップコートは、レジスト膜と混合せず、更にレジスト膜上層に均一に塗布できることが好ましい。
　トップコートについては、特に限定されず、従来公知のトップコートを、従来公知の方法によって形成でき、例えば、特開２０１４－０５９５４３号公報の段落００７２～００８２の記載に基づいてトップコートを形成できる。
　現像工程において、有機溶剤を含有する現像液を使用する場合は、例えば、特開２０１３－６１６４８号公報に記載されたような塩基性化合物を含有するトップコートをレジスト膜上に形成することが好ましい。トップコートが含み得る塩基性化合物の具体的な例は、塩基性化合物（Ｅ）として後述する。
　また、トップコートは、エーテル結合、チオエーテル結合、ヒドロキシル基、チオール基、カルボニル結合及びエステル結合からなる群より選択される基又は結合を少なくとも一つ含む化合物を含むことが好ましい。
　＜露光工程＞
　露光工程は、レジスト膜を露光する工程であり、例えば次の方法により行うことができる。
　上記のようにして形成したレジスト膜に、所定のマスクを通して活性光線又は放射線を照射する。なお、電子ビームの照射では、マスクを介さない描画（直描）が一般的である。
　活性光線又は放射線としては特に限定されないが、例えばＫｒＦエキシマレーザー、ＡｒＦエキシマレーザー、極紫外線（ＥＵＶ、Ｅｘｔｒｅｍｅ　Ｕｌｔｒａ　Ｖｉｏｌｅｔ）、電子線（ＥＢ、Ｅｌｅｃｔｒｏｎ　Ｂｅａｍ）等であり、極紫外線又は電子線が特に好ましい。露光は液浸露光であってもよい。
　＜ベーク＞
　本発明のパターン形成方法においては、露光後、現像を行う前にベーク（加熱）を行うことが好ましい。ベークにより露光部の反応が促進され、感度やパターン形状がより良好となる。
　加熱温度は８０～１５０℃が好ましく、８０～１４０℃がより好ましく、８０～１３０℃が更に好ましい。
　加熱時間は３０～１０００秒が好ましく、６０～８００秒がより好ましく、６０～６００秒が更に好ましい。
　加熱は通常の露光・現像機に備わっている手段で行うことができ、ホットプレート等を用いて行ってもよい。
　＜現像工程＞
　現像工程は、露光されたレジスト膜を現像液によって現像する工程である。
　現像方法としては、たとえば、現像液が満たされた槽中に基板を一定時間浸漬する方法（ディップ法）、基板表面に現像液を表面張力によって盛り上げて一定時間静止することで現像する方法（パドル法）、基板表面に現像液を噴霧する方法（スプレー法）、一定速度で回転している基板上に一定速度で現像液吐出ノズルをスキャンしながら現像液を吐出しつづける方法（ダイナミックディスペンス法）などを適用することができる。
　また、現像を行う工程の後に、他の溶媒に置換しながら、現像を停止する工程を実施してもよい。
　現像時間は未露光部の樹脂が十分に溶解する時間であれば特に制限はなく、通常は１０～３００秒であり、好ましくは２０～１２０秒である。
　現像液の温度は０～５０℃が好ましく、１５～３５℃がより好ましい。
　現像液は有機溶剤を含むことが好ましく、有機溶剤としては、前述のリンス液が含み得る有機溶剤（炭化水素系溶剤、ケトン系溶剤、エステル系溶剤、アルコール系溶剤、アミド系溶剤及びエーテル系溶剤からなる群より選択される少なくとも１種の有機溶剤）と同様である。なお、炭化水素系溶剤は、分岐アルキル基を有する炭化水素系溶剤であっても、分岐アルキル基を有する炭化水素系溶剤以外の炭化水素系溶剤であってもよい。
　現像液が含む有機溶剤は、エステル系溶剤が好ましく、分岐炭化水素骨格を有するエステル系溶剤がより好ましい。
　現像液が含む有機溶剤の蒸気圧は、２０℃に於いて、５ｋＰａ以下が好ましく、３ｋＰａ以下が更に好ましく、２ｋＰａ以下が特に好ましい。現像液の蒸気圧を５ｋＰａ以下にすることにより、現像液の基板上あるいは現像カップ内での蒸発が抑制され、ウエハ面内の温度均一性が向上し、結果としてウエハ面内の寸法均一性が良化する。
　現像液が含む有機溶剤の好ましい例としては、例えば、酢酸メチル、酢酸ブチル、酢酸エチル、酢酸イソプロピル、酢酸アミル、酢酸イソアミル、蟻酸メチル、蟻酸エチル、蟻酸ブチル、蟻酸プロピル、乳酸エチル、乳酸ブチル、乳酸プロピル、炭酸エチル、炭酸プロピル、炭酸ブチル、ピルビン酸メチル、ピルビン酸エチル、ピルビン酸プロピル、ピルビン酸ブチル、アセト酢酸メチル、アセト酢酸エチル、プロピオン酸メチル、プロピオン酸エチル、プロピオン酸プロピル、プロピオン酸イソプロピル、２－ヒドロキシプロピオン酸メチル、２－ヒドロキシプロピオン酸エチル等を挙げることができる。
　これらの中でも、酢酸ブチル、酢酸アミル（酢酸ペンチル）、酢酸イソアミル（酢酸イソペンチル）であることがより好ましく、酢酸イソアミルであることが更に好ましい。
　現像液は、界面活性剤を含有することが好ましい。これにより、レジスト膜に対する濡れ性が向上して、現像がより効果的に進行する。
　界面活性剤としては、後述する感活性光線又は感放射線性組成物に用いられる界面活性剤と同様のものを用いることができる。
　現像液が界面活性剤を含有する場合、界面活性剤の含有量は、現像液の全質量に対して、０．００１～５質量％であることが好ましく、より好ましくは０．００５～２質量％であり、更に好ましくは０．０１～０．５質量％である。
　現像液は、酸化防止剤を含有することが好ましい。これにより、経時的な酸化剤の発生を抑制でき、酸化剤の含有量をより低下できる。
　現像液が含有してもよい酸化防止剤としては、前述のリンス液が含有してもよい酸化防止剤と同様である。
　酸化防止剤の含有量は、特に限定されないが、現像液の全質量に対して、０．０００１～１質量％が好ましく、０．０００１～０．１質量％がより好ましく、０．０００１～０．０１質量％が更に好ましい。０．０００１質量％以上であるとより優れた酸化防止効果が得られ、１質量％以下であることで、現像残渣を抑制できる傾向にある。
　現像液は、塩基性化合物を含有することが好ましい。塩基性化合物の具体例としては、後に述べる感活性光線性又は感放射線性組成物が含み得る塩基性化合物として例示する化合物が挙げられる。
　現像液に含まれ得る塩基性化合物の中でも、含窒素化合物を好ましく用いることができる。
　現像工程で用いられる現像液としては、有機溶剤を含有する現像液を用いた現像に加えて、アルカリ現像液による現像（いわゆる二重現像）を行ってもよい。
　＜リンス工程＞
　リンス工程は、現像工程の後にリンス液によって洗浄（リンス）する工程である。
　リンス工程においては、現像を行ったウエハを前述のリンス液を用いて洗浄処理する。
　洗浄処理の方法は特に限定されないが、たとえば、一定速度で回転している基板上にリンス液を吐出しつづける方法（回転吐出法）、リンス液が満たされた槽中に基板を一定時間浸漬する方法（ディップ法）、基板表面にリンス液を噴霧する方法（スプレー法）、などを適用することができ、この中でも回転吐出方法で洗浄処理を行い、洗浄後に基板を２０００ｒｐｍ～４０００ｒｐｍの回転数で回転させ、リンス液を基板上から除去することが好ましい。
　リンス時間には特に制限はないが、好ましくは１０秒～３００秒であり、より好ましくは１０秒～１８０秒であり、最も好ましくは２０秒～１２０秒である。
　リンス液の温度は０～５０℃が好ましく、１５～３５℃が更に好ましい。
　また、現像処理又はリンス処理の後に、パターン上に付着している現像液又はリンス液を超臨界流体により除去する処理を行うことができる。
　更に、現像処理又はリンス処理又は超臨界流体による処理の後、パターン中に残存する溶剤を除去するために加熱処理を行うことができる。加熱温度は、良好なレジストパターンが得られる限り特に限定されるものではなく、通常４０～１６０℃である。加熱温度は５０～１５０℃が好ましく、５０～１１０℃が最も好ましい。加熱時間に関しては良好なレジストパターンが得られる限り特に限定されないが、通常１５～３００秒であり、好ましくは、１５～１８０秒である。
　リンス液としては、上述したリンス液を用いることが好ましい。
　＜感活性光線又は感放射線性組成物＞
　次に、本発明のパターン形成方法で用いられる感活性光線性又は感放射線性組成物について説明する。
　本発明のパターン形成方法において、感活性光線性又は感放射線性組成物は、有機溶剤を含む現像液を使用する有機溶剤現像用の感活性光線性又は感放射線性組成物であることが好ましい。ここで、有機溶剤現像用とは、少なくとも、有機溶剤を含む現像液を用いて現像する工程に供される用途を意味する。本発明における感活性光線性又は感放射線性組成物は化学増幅型レジスト組成物であっても、非化学増幅型レジスト組成物であってもよいが、化学増幅型レジスト組成物であることが好ましい。また、本発明における感活性光線性又は感放射線性組成物はポジ型レジスト組成物であってもネガ型レジスト組成物であってもよい。
　本発明における感放射線性又は感活性光線性組成物は、電子線又は極紫外線露光用であることが好ましい。
＜樹脂（Ａ）＞
　レジスト組成物は、樹脂（Ａ）を含有することが好ましい。樹脂（Ａ）は、少なくとも（ｉ）酸の作用により分解してカルボキシル基を生じる基を有する繰り返し単位（更に、フェノール性水酸基を有する繰り返し単位を有してもよい）、又は、少なくとも（ｉｉ）フェノール性水酸基を有する繰り返し単位を有する。
　なお、酸の作用により分解してカルボキシル基を有する繰り返し単位を有すると、酸の作用によりアルカリ現像液に対する溶解度が増大し、有機溶剤に対する溶解度が減少する。
　樹脂（Ａ）が有するフェノール性水酸基を有する繰り返し単位としては、例えば、下記一般式（Ｉ）で表される繰り返し単位が挙げられる。
Figure JPOXMLDOC01-appb-C000003
　一般式（Ｉ）中、
　Ｒ４１、Ｒ４２及びＲ４３は、各々独立に、水素原子、アルキル基、シクロアルキル基、ハロゲン原子、シアノ基又はアルコキシカルボニル基を表す。但し、Ｒ４２はＡｒ４と結合して環を形成していてもよく、その場合のＲ４２は単結合又はアルキレン基を表す。
　Ｘ４は、単結合、－ＣＯＯ－、又は－ＣＯＮＲ６４－を表し、Ｒ６４は、水素原子又はアルキル基を表す。
　Ｌ４は、単結合又はアルキレン基を表す。
　Ａｒ４は、（ｎ＋１）価の芳香環基を表し、Ｒ４２と結合して環を形成する場合には（ｎ＋２）価の芳香環基を表す。
　ｎは、１～５の整数を表す。
　一般式（Ｉ）におけるＲ４１、Ｒ４２、Ｒ４３のアルキル基としては、好ましくは置換基を有していても良いメチル基、エチル基、プロピル基、イソプロピル基、ｎ－ブチル基、ｓｅｃ－ブチル基、ヘキシル基、２－エチルヘキシル基、オクチル基、ドデシル基など炭素数２０以下のアルキル基が挙げられ、より好ましくは炭素数８以下のアルキル基、特に好ましくは炭素数３以下のアルキル基が挙げられる。
　一般式（Ｉ）におけるＲ４１、Ｒ４２、Ｒ４３のシクロアルキル基としては、単環型でも、多環型でもよい。好ましくは置換基を有していてもよいシクロプロピル基、シクロペンチル基、シクロヘキシル基などの炭素数３～８個で単環型のシクロアルキル基が挙げられる。
　一般式（Ｉ）におけるＲ４１、Ｒ４２、Ｒ４３のハロゲン原子としては、フッ素原子、塩素原子、臭素原子及びヨウ素原子が挙げられ、フッ素原子が特に好ましい。
　一般式（Ｉ）におけるＲ４１、Ｒ４２、Ｒ４３のアルコキシカルボニル基に含まれるアルキル基としては、上記Ｒ４１、Ｒ４２、Ｒ４３におけるアルキル基と同様のものが好ましい。
　上記各基における好ましい置換基としては、例えば、アルキル基、シクロアルキル基、アリール基、アミノ基、アミド基、ウレイド基、ウレタン基、ヒドロキシル基、カルボキシル基、ハロゲン原子、アルコキシ基、チオエーテル基、アシル基、アシロキシ基、アルコキシカルボニル基、シアノ基、ニトロ基等を挙げることができ、置換基の炭素数は８以下が好ましい。
　Ａｒ４は、（ｎ＋１）価の芳香環基を表す。ｎが１である場合における２価の芳香環基は、置換基を有していてもよく、例えば、フェニレン基、トリレン基、ナフチレン基、アントラセニレン基などの炭素数６～１８のアリーレン基、あるいは、例えば、チオフェン、フラン、ピロール、ベンゾチオフェン、ベンゾフラン、ベンゾピロール、トリアジン、イミダゾール、ベンゾイミダゾール、トリアゾール、チアジアゾール、チアゾール等のヘテロ環を含む芳香環基を好ましい例として挙げることができる。
　ｎが２以上の整数である場合における（ｎ＋１）価の芳香環基の具体例としては、２価の芳香環基の上記した具体例から、（ｎ－１）個の任意の水素原子を除してなる基を好適に挙げることができる。
　（ｎ＋１）価の芳香環基は、更に置換基を有していてもよい。
　上述したアルキル基、シクロアルキル基、アルコキシカルボニル基、アルキレン基及び（ｎ＋１）価の芳香環基が有し得る置換基としては、例えば、一般式（Ｉ）におけるＲ４１、Ｒ４２、Ｒ４３で挙げたアルキル基、メトキシ基、エトキシ基、ヒドロキシエトキシ基、プロポキシ基、ヒドロキシプロポキシ基、ブトキシ基などのアルコキシ基；フェニル基などのアリール基；等が挙げられる。
　Ｘ４により表わされる－ＣＯＮＲ６４－（Ｒ６４は、水素原子、アルキル基を表す）におけるＲ６４のアルキル基としては、好ましくは置換基を有していてもよいメチル基、エチル基、プロピル基、イソプロピル基、ｎ－ブチル基、ｓｅｃ－ブチル基、ヘキシル基、２－エチルヘキシル基、オクチル基、ドデシル基など炭素数２０以下のアルキル基が挙げられ、より好ましくは炭素数８以下のアルキル基が挙げられる。
　Ｘ４としては、単結合、－ＣＯＯ－、－ＣＯＮＨ－が好ましく、単結合、－ＣＯＯ－がより好ましい。
　Ｌ４におけるアルキレン基としては、好ましくは置換基を有していてもよいメチレン基、エチレン基、プロピレン基、ブチレン基、ヘキシレン基、オクチレン基等の炭素数１～８個のものが挙げられる。
　Ａｒ４としては、置換基を有していてもよい炭素数６～１８の芳香環基がより好ましく、ベンゼン環基、ナフタレン環基、ビフェニレン環基が特に好ましい。
　一般式（Ｉ）で表される繰り返し単位は、ヒドロキシスチレン構造を備えていることが好ましい。即ち、Ａｒ４は、ベンゼン環基であることが好ましい。
　樹脂（Ａ）が有するフェノール性水酸基を有する繰り返し単位としては、下記一般式（１）で表される繰り返し単位が好ましい。
Figure JPOXMLDOC01-appb-C000004
　一般式（１）中、
　Ａは水素原子、アルキル基、シクロアルキル基、ハロゲン原子、又はシアノ基を表す。
　Ｒは、ハロゲン原子、アルキル基、シクロアルキル基、アリール基、アルケニル基、アラルキル基、アルコキシ基、アルキルカルボニルオキシ基、アルキルスルホニルオキシ基、アルキルオキシカルボニル基又はアリールオキシカルボニル基を表し、複数個ある場合には同じであっても異なっていてもよい。複数のＲを有する場合には、互いに共同して環を形成していてもよい。Ｒとしては水素原子が好ましい。
　ａは１～３の整数を表し、好ましくは１である。
　ｂは０～（３－ａ）の整数を表す。
　樹脂（Ａ）が有するフェノール性水酸基を有する繰り返し単位としては、好ましくは、下記一般式（ｐ１）で表される繰り返し単位が挙げられる。
Figure JPOXMLDOC01-appb-C000005
　一般式（ｐ１）におけるＲは、水素原子、ハロゲン原子又は１～４個の炭素原子を有する直鎖若しくは分岐のアルキル基を表す。複数のＲは、各々同じでも異なっていてもよい。一般式（ｐ１）中のＲとしては水素原子が特に好ましい。
　一般式（ｐ１）におけるＡｒは芳香族環を表し、例えば、ベンゼン環、ナフタレン環、アントラセン環、フルオレン環、フェナントレン環などの炭素数６～１８の置換基を有していてもよい芳香族炭化水素環、又は、例えば、チオフェン環、フラン環、ピロール環、ベンゾチオフェン環、ベンゾフラン環、ベンゾピロール環、トリアジン環、イミダゾール環、ベンゾイミダゾール環、トリアゾール環、チアジアゾール環、チアゾール環等のヘテロ環を含む芳香環ヘテロ環を挙げることができる。中でも、ベンゼン環が最も好ましい。
　一般式（ｐ１）におけるｍは、１～５の整数を表し、好ましくは１である。
　以下、樹脂（Ａ）が有するフェノール性水酸基を有する繰り返し単位の具体例を示すが、本発明は、これに限定されるものではない。式中、ａは１又は２を表す。
Figure JPOXMLDOC01-appb-C000006
Figure JPOXMLDOC01-appb-C000007
Figure JPOXMLDOC01-appb-C000008
　フェノール性水酸基を有する繰り返し単位の含有量は、樹脂（Ａ）中の全繰り返し単位に対し、０～５０モル％が好ましく、より好ましくは０～４５モル％、更に好ましくは０～４０モル％である。
　樹脂（Ａ）が有する酸の作用により分解してカルボキシル基を生じる基を有する繰り返し単位は、カルボキシル基の水素原子が酸の作用により分解して脱離する基で置換された基を有する繰り返し単位である。
　酸で脱離する基としては、例えば、－Ｃ（Ｒ３６）（Ｒ３７）（Ｒ３８）、－Ｃ（Ｒ３６）（Ｒ３７）（ＯＲ３９）、－Ｃ（Ｒ０１）（Ｒ０２）（ＯＲ３９）等を挙げることができる。
　式中、Ｒ３６～Ｒ３９は、各々独立に、アルキル基、シクロアルキル基、アリール基、アラルキル基又はアルケニル基を表す。Ｒ３６とＲ３７とは、互いに結合して環を形成してもよい。
　Ｒ０１及びＲ０２は、各々独立に、水素原子、アルキル基、シクロアルキル基、アリール基、アラルキル基又はアルケニル基を表す。
　樹脂（Ａ）が有する、酸の作用により分解してカルボキシル基を生じる基を有する繰り返し単位としては、下記一般式（ＡＩ）で表される繰り返し単位が好ましい。
Figure JPOXMLDOC01-appb-C000009
　一般式（ＡＩ）において、
　Ｘａ１は、水素原子、又は置換基を有していてもよいアルキル基を表す。
　Ｔは、単結合又は２価の連結基を表す。
　Ｒｘ１～Ｒｘ３は、各々独立に、アルキル基（直鎖若しくは分岐）又はシクロアルキル基（単環若しくは多環）を表す。ただし、Ｒｘ１～Ｒｘ３の全てがアルキル基（直鎖若しくは分岐）である場合、Ｒｘ１～Ｒｘ３のうち少なくとも２つはメチル基であることが好ましい。
　Ｒｘ１～Ｒｘ３の２つが結合して、シクロアルキル基（単環若しくは多環）を形成してもよい。
　Ｘａ１により表される、置換基を有していてもよいアルキル基としては、例えば、メチル基又は－ＣＨ２－Ｒ１１で表される基が挙げられる。Ｒ１１は、ハロゲン原子（フッ素原子など）、ヒドロキシル基又は１価の有機基を表し、例えば、炭素数５以下のアルキル基、炭素数５以下のアシル基が挙げられ、好ましくは炭素数３以下のアルキル基であり、更に好ましくはメチル基である。Ｘａ１は、一態様において、好ましくは水素原子、メチル基、トリフルオロメチル基又はヒドロキシメチル基等である。
　Ｔの２価の連結基としては、アルキレン基、－ＣＯＯ－Ｒｔ－基、－Ｏ－Ｒｔ－基等が挙げられる。式中、Ｒｔは、アルキレン基又はシクロアルキレン基を表す。
　Ｔは、単結合又は－ＣＯＯ－Ｒｔ－基が好ましい。Ｒｔは、炭素数１～５のアルキレン基が好ましく、－ＣＨ２－基、－（ＣＨ２）２－基、－（ＣＨ２）３－基がより好ましい。
　Ｒｘ１～Ｒｘ３のアルキル基としては、メチル基、エチル基、ｎ－プロピル基、イソプロピル基、ｎ－ブチル基、イソブチル基、ｔ－ブチル基などの炭素数１～４のものが好ましい。
　Ｒｘ１～Ｒｘ３のシクロアルキル基としては、シクロペンチル基、シクロヘキシル基などの単環のシクロアルキル基、ノルボルニル基、テトラシクロデカニル基、テトラシクロドデカニル基、アダマンチル基などの多環のシクロアルキル基が好ましい。
　Ｒｘ１～Ｒｘ３の２つが結合して形成されるシクロアルキル基としては、シクロペンチル基、シクロヘキシル基などの単環のシクロアルキル基、ノルボルニル基、テトラシクロデカニル基、テトラシクロドデカニル基、アダマンチル基などの多環のシクロアルキル基が好ましい。炭素数５～６の単環のシクロアルキル基が特に好ましい。
　Ｒｘ１～Ｒｘ３の２つが結合して形成されるシクロアルキル基は、例えば、環を構成するメチレン基の１つが、酸素原子等のヘテロ原子、又は、カルボニル基等のヘテロ原子を有する基で置き換わっていてもよい。
　一般式（ＡＩ）で表される繰り返し単位は、例えば、Ｒｘ１がメチル基又はエチル基であり、Ｒｘ２とＲｘ３とが結合して上述のシクロアルキル基を形成している態様が好ましい。
　上記各基は置換基を有していてもよく、置換基としては、例えば、アルキル基（炭素数１～４）、ハロゲン原子、水酸基、アルコキシ基（炭素数１～４）、カルボキシル基、アルコキシカルボニル基（炭素数２～６）などが挙げられ、炭素数８以下が好ましい。
　一般式（ＡＩ）で表される繰り返し単位としては、好ましくは、酸分解性（メタ）アクリル酸３級アルキルエステル系繰り返し単位（Ｘａ１が水素原子又はメチル基を表し、かつ、Ｔが単結合を表す繰り返し単位）である。より好ましくは、Ｒｘ１～Ｒｘ３が各々独立に、直鎖又は分岐のアルキル基を表す繰り返し単位であり、更に好ましくは、Ｒｘ１～Ｒｘ３が各々独立に、直鎖のアルキル基を表す繰り返し単位である。
　樹脂（Ａ）が有する、酸の作用により分解してカルボキシル基を生じる基を有する繰り返し単位の具体例を以下に示すが、本発明は、これに限定されるものではない。
　具体例中、Ｒｘ、Ｘａ１は、水素原子、ＣＨ３、ＣＦ３、又はＣＨ２ＯＨを表す。Ｒｘａ、Ｒｘｂは各々炭素数１～４のアルキル基を表す。Ｚは、極性基を含む置換基を表し、複数存在する場合は各々独立である。ｐは０又は正の整数を表す。Ｚにより表される極性基を含む置換基としては、例えば、水酸基、シアノ基、アミノ基、アルキルアミド基又はスルホンアミド基を有する、直鎖又は分岐のアルキル基、シクロアルキル基が挙げられ、好ましくは、水酸基を有するアルキル基である。分岐状アルキル基としてはイソプロピル基が特に好ましい。
Figure JPOXMLDOC01-appb-C000010
　酸の作用により分解してカルボキシル基を生じる基を有する繰り返し単位の含有量は、樹脂（Ａ）中の全繰り返し単位に対し、２０～９０モル％が好ましく、より好ましくは２５～８０モル％、更に好ましくは３０～７０モル％である。
　樹脂（Ａ）は、更にラクトン基を有する繰り返し単位を含有することが好ましい。
　ラクトン基としては、ラクトン構造を含有していればいずれの基でも用いることができるが、好ましくは５～７員環ラクトン構造を含有する基であり、５～７員環ラクトン構造にビシクロ構造、スピロ構造を形成する形で他の環構造が縮環しているものが好ましい。下記一般式（ＬＣ１－１）～（ＬＣ１－１７）のいずれかで表されるラクトン構造を有する基を有する繰り返し単位を有することがより好ましい。また、ラクトン構造を有する基が主鎖に直接結合していてもよい。好ましいラクトン構造としては一般式（ＬＣ１－１）、（ＬＣ１－４）、（ＬＣ１－５）、（ＬＣ１－６）、（ＬＣ１－１３）、（ＬＣ１－１４）で表される基である。
Figure JPOXMLDOC01-appb-C000011
　ラクトン構造部分は、置換基（Ｒｂ２）を有していても有していなくてもよい。好ましい置換基（Ｒｂ２）としては、炭素数１～８のアルキル基、炭素数４～７のシクロアルキル基、炭素数１～８のアルコキシ基、炭素数１～８のアルコキシカルボニル基、カルボキシル基、ハロゲン原子、水酸基、シアノ基、酸分解性基などが挙げられる。ｎ２は、０～４の整数を表す。ｎ２が２以上の時、複数存在するＲｂ２は、同一でも異なっていてもよく、また、複数存在するＲｂ２同士が結合して環を形成してもよい。
　一般式（ＬＣ１－１）～（ＬＣ１－１７）のいずれかで表されるラクトン構造を有する基を有する繰り返し単位としては、例えば、下記一般式（ＡＩ）で表される繰り返し単位等を挙げることができる。
Figure JPOXMLDOC01-appb-C000012
　一般式（ＡＩ）中、Ｒｂ０は、水素原子、ハロゲン原子、又は炭素数１～４のアルキル基を表す。
　Ｒｂ０のアルキル基が有していてもよい好ましい置換基としては、水酸基、ハロゲン原子が挙げられる。
　Ｒｂ０のハロゲン原子としては、フッ素原子、塩素原子、臭素原子、沃素原子を挙げることができる。Ｒｂ０は、水素原子又はメチル基が好ましい。
　Ａｂは、単結合、アルキレン基、単環又は多環の脂環炭化水素構造を有する２価の連結基、エーテル基、エステル基、カルボニル基、カルボキシル基、又はこれらを組み合わせた２価の基を表す。好ましくは、単結合、－Ａｂ１－ＣＯ２－で表される連結基である。Ａｂ１は、直鎖、分岐アルキレン基、単環又は多環のシクロアルキレン基であり、好ましくは、メチレン基、エチレン基、シクロヘキシレン基、アダマンチレン基、ノルボルニレン基である。
　Ｖは、一般式（ＬＣ１－１）～（ＬＣ１－１７）のうちのいずれかで示される基を表す。
　ラクトン構造を有する基を有する繰り返し単位は、通常、光学異性体が存在するが、いずれの光学異性体を用いてもよい。また、１種の光学異性体を単独で用いても、複数の光学異性体を混合して用いてもよい。１種の光学異性体を主に用いる場合、その光学純度（ｅｅ）が９０以上のものが好ましく、より好ましくは９５以上である。
　ラクトン構造を有する基を有する繰り返し単位の具体例を以下に挙げるが、本発明はこれらに限定されない。
Figure JPOXMLDOC01-appb-C000013
　ラクトン基を有する繰り返し単位の含有量は、樹脂（Ａ）中の全繰り返し単位に対し、１～３０モル％が好ましく、より好ましくは５～２５モル％、更に好ましくは５～２０モル％である。
　樹脂（Ａ）は、極性基を有する有機基を含有する繰り返し単位、特に、極性基で置換された脂環炭化水素構造を有する繰り返し単位を更に有することができる。
　これにより基板密着性、現像液親和性が向上する。極性基で置換された脂環炭化水素構造の脂環炭化水素構造としてはアダマンチル基、ジアマンチル基、ノルボルナン基が好ましい。極性基としては水酸基、シアノ基が好ましい。
　極性基を有する繰り返し単位の具体例を以下に挙げるが、本発明はこれらに限定されない。
Figure JPOXMLDOC01-appb-C000014
　樹脂（Ａ）が、極性基を有する有機基を含有する繰り返し単位を有する場合、その含有量は、樹脂（Ａ）中の全繰り返し単位に対し、１～３０モル％が好ましく、より好ましくは５～２５モル％、更に好ましくは５～２０モル％である。
　更に、上記以外の繰り返し単位として、活性光線又は放射線の照射により酸を発生する基（光酸発生基）を有する繰り返し単位を含むこともできる。この場合、この光酸発生基を有する繰り返し単位が、後述する活性光線又は放射線の照射により酸を発生する化合物（Ｂ）にあたると考えることができる。
　このような繰り返し単位としては、例えば、下記一般式（４）で表される繰り返し単位が挙げられる。
Figure JPOXMLDOC01-appb-C000015
　Ｒ４１は、水素原子又はメチル基を表す。Ｌ４１は、単結合又は２価の連結基を表す。Ｌ４２は、２価の連結基を表す。Ｒ４０は、活性光線又は放射線の照射により分解して側鎖に酸を発生させる構造部位を表す。
　以下に、一般式（４）で表される繰り返し単位の具体例を示すが、本発明がこれに限定されるものではない。
Figure JPOXMLDOC01-appb-C000016
　そのほか、一般式（４）で表される繰り返し単位としては、例えば、特開２０１４－０４１３２７号公報の段落［００９４］～［０１０５］に記載された繰り返し単位が挙げられる。
　樹脂（Ａ）が光酸発生基を有する繰り返し単位を含有する場合、光酸発生基を有する繰り返し単位の含有量は、樹脂（Ａ）中の全繰り返し単位に対し、１～４０モル％が好ましく、より好ましくは５～３５モル％、更に好ましくは５～３０モル％である。
　樹脂（Ａ）は、常法に従って（例えばラジカル重合）合成することができる。例えば、一般的合成方法としては、モノマー種及び開始剤を溶剤に溶解させ、加熱することにより重合を行う一括重合法、加熱溶剤にモノマー種と開始剤の溶液を１～１０時間かけて滴下して加える滴下重合法などが挙げられ、滴下重合法が好ましい。
　反応溶媒としては、例えば、テトラヒドロフラン、１，４－ジオキサン、ジイソプロピルエーテルなどのエーテル類；メチルエチルケトン、メチルイソブチルケトンなどのケトン類；酢酸エチルなどのエステル溶媒；ジメチルホルムアミド、ジメチルアセトアミドなどのアミド溶剤；後述のプロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノメチルエーテル、シクロヘキサノンなどの本発明のレジスト組成物を溶解する溶媒；等が挙げられる。より好ましくは本発明のレジスト組成物に用いられる溶剤と同一の溶剤を用いて重合することが好ましい。これにより保存時のパーティクルの発生が抑制できる。
　重合反応は窒素やアルゴンなど不活性ガス雰囲気下で行われることが好ましい。重合開始剤としては市販のラジカル開始剤（アゾ系開始剤、パーオキサイドなど）を用いて重合を開始させる。ラジカル開始剤としてはアゾ系開始剤が好ましく、エステル基、シアノ基、カルボキシル基を有するアゾ系開始剤が好ましい。好ましい開始剤としては、アゾビスイソブチロニトリル、アゾビスジメチルバレロニトリル、ジメチル２，２’－アゾビス（２－メチルプロピオネート）などが挙げられる。所望により開始剤を追加、あるいは分割で添加し、反応終了後、溶剤に投入して粉体あるいは固形回収等の方法で所望のポリマーを回収する。反応の濃度は５～５０質量％であり、好ましくは１０～３０質量％である。反応温度は、通常１０℃～１５０℃であり、好ましくは３０℃～１２０℃、更に好ましくは６０～１００℃である。
　精製は、水洗や適切な溶媒を組み合わせることにより残留単量体やオリゴマー成分を除去する液液抽出法、特定の分子量以下のもののみを抽出除去する限外ろ過等の溶液状態での精製方法や、樹脂溶液を貧溶媒へ滴下することで樹脂を貧溶媒中に凝固させることにより残留単量体等を除去する再沈殿法や、濾別した樹脂スラリーを貧溶媒で洗浄する等の固体状態での精製方法等の通常の方法を適用できる。
　樹脂（Ａ）の重量平均分子量は、ＧＰＣ法によりポリスチレン換算値として、好ましくは１，０００～２００，０００であり、更に好ましくは３，０００～２０，０００、最も好ましくは５，０００～１５，０００である。重量平均分子量を、１，０００～２００，０００とすることにより、耐熱性やドライエッチング耐性の劣化を防ぐことができ、かつ現像性が劣化したり、粘度が高くなって製膜性が劣化したりすることを防ぐことができる。
　樹脂（Ａ）の重量平均分子量の特に好ましい別の形態は、ＧＰＣ法によるポリスチレン換算値で３，０００～９，５００である。重量平均分子量を３，０００～９，５００にすることにより、特にレジスト残渣（以降、「スカム」ともいう）が抑制され、より良好なパターンを形成することができる。
　分散度（分子量分布）は、通常１～５であり、好ましくは１～３、更に好ましくは１．２～３．０、特に好ましくは１．２～２．０の範囲のものが使用される。分散度の小さいものほど、解像度、レジスト形状が優れ、かつレジストパターンの側壁がスムーズであり、ラフネス性に優れる。
　本発明のレジスト組成物において、樹脂（Ａ）の含有量は、全固形分中５０～９９．９質量％が好ましく、より好ましくは６０～９９．０質量％である。
　また、本発明のレジスト組成物において、樹脂（Ａ）は、１種で使用してもよいし、複数併用してもよい。
　また、樹脂（Ａ）は、下記一般式（ＶＩ）で表される繰り返し単位を含んでいてもよい。
Figure JPOXMLDOC01-appb-C000017
　一般式（ＶＩ）中、
　Ｒ６１、Ｒ６２及びＲ６３は、各々独立に、水素原子、アルキル基、シクロアルキル基、ハロゲン原子、シアノ基、又はアルコキシカルボニル基を表す。但し、Ｒ６２はＡｒ６と結合して環を形成していてもよく、その場合のＲ６２は単結合又はアルキレン基を表す。
　Ｘ６は、単結合、－ＣＯＯ－、又は－ＣＯＮＲ６４－を表す。Ｒ６４は、水素原子又はアルキル基を表す。
　Ｌ６は、単結合又はアルキレン基を表す。
　Ａｒ６は、（ｎ＋１）価の芳香環基を表し、Ｒ６２と結合して環を形成する場合には（ｎ＋２）価の芳香環基を表す。
　Ｙ２は、ｎ≧２の場合には各々独立に、水素原子又は酸の作用により脱離する基を表す。但し、Ｙ２の少なくとも１つは、酸の作用により脱離する基を表す。
　ｎは、１～４の整数を表す。
　酸の作用により脱離する基Ｙ２としては、下記一般式（ＶＩ－Ａ）で表される構造がより好ましい。
Figure JPOXMLDOC01-appb-C000018
　ここで、Ｌ１及びＬ２は、各々独立に、水素原子、アルキル基、シクロアルキル基、アリール基、又はアルキレン基とアリール基とを組み合わせた基を表す。
　Ｍは、単結合又は２価の連結基を表す。
　Ｑは、アルキル基、ヘテロ原子を含んでいてもよいシクロアルキル基、ヘテロ原子を含んでいてもよいアリール基、アミノ基、アンモニウム基、メルカプト基、シアノ基又はアルデヒド基を表す。
　Ｑ、Ｍ、Ｌ１の少なくとも２つが結合して環（好ましくは、５員若しくは６員環）を形成してもよい。
　上記一般式（ＶＩ）で表される繰り返し単位は、下記一般式（３）で表される繰り返し単位であることが好ましい。
Figure JPOXMLDOC01-appb-C000019
　一般式（３）において、
　Ａｒ３は、芳香環基を表す。
　Ｒ３は、水素原子、アルキル基、シクロアルキル基、アリール基、アラルキル基、アルコキシ基、アシル基又はヘテロ環基を表す。
　Ｍ３は、単結合又は２価の連結基を表す。
　Ｑ３は、アルキル基、シクロアルキル基、アリール基又はヘテロ環基を表す。
　Ｑ３、Ｍ３及びＲ３の少なくとも二つが結合して環を形成してもよい。
　Ａｒ３が表す芳香環基は、上記一般式（ＶＩ）におけるｎが１である場合の、上記一般式（ＶＩ）におけるＡｒ６と同様であり、より好ましくはフェニレン基、ナフチレン基であり、更に好ましくはフェニレン基である。
　以下に一般式（ＶＩ）で表される繰り返し単位の具体例を示すが、本発明はこれに限定されるものではない。
Figure JPOXMLDOC01-appb-C000020
　樹脂（Ａ）は、下記一般式（５）で表される繰り返し単位を含むことも好ましい。
Figure JPOXMLDOC01-appb-C000021
　一般式（５）中、
　Ｒ４１、Ｒ４２及びＲ４３は、各々独立に、水素原子、アルキル基、シクロアルキル基、ハロゲン原子、シアノ基又はアルコキシカルボニル基を表す。Ｒ４２はＬ４と結合して環を形成していてもよく、その場合のＲ４２はアルキレン基を表す。
　Ｌ４は、単結合又は２価の連結基を表し、Ｒ４２と環を形成する場合には３価の連結基を表す。
　Ｒ４４及びＲ４５は、水素原子、アルキル基、シクロアルキル基、アリール基、アラルキル基、アルコキシ基、アシル基又はヘテロ環基を表す。
　Ｍ４は、単結合又は２価の連結基を表す。
　Ｑ４は、アルキル基、シクロアルキル基、アリール基又はヘテロ環基を表す。
　Ｑ４、Ｍ４及びＲ４４の少なくとも二つが結合して環を形成してもよい。
　Ｒ４１、Ｒ４２及びＲ４３は、各々独立に、水素原子、アルキル基、シクロアルキル基、ハロゲン原子、シアノ基、又はアルコキシカルボニル基を表す。Ｒ４２はＬ４と結合して環を形成していてもよく、その場合のＲ４２はアルキレン基を表す。
　Ｌ４は、単結合又は２価の連結基を表し、Ｒ４２と環を形成する場合には３価の連結基を表す。
　Ｒ４４及びＲ４５は、前述の一般式（３）中のＲ３と同義であり、また好ましい範囲も同様である。
　Ｍ４は、前述の一般式（３）中のＭ３と同義であり、また好ましい範囲も同様である。
　Ｑ４は、前述の一般式（３）中のＱ３と同義であり、また好ましい範囲も同様である。Ｑ４、Ｍ４及びＲ４４の少なくとも二つが結合して形成される環としては、Ｑ３、Ｍ３及びＲ３の少なくとも二つが結合して形成される環があげられ、また好ましい範囲も同様である。
　一般式（５）におけるＲ４１～Ｒ４３のアルキル基としては、好ましくは置換基を有していても良いメチル基、エチル基、プロピル基、イソプロピル基、ｎ－ブチル基、ｓｅｃ－ブチル基、ヘキシル基、２－エチルヘキシル基、オクチル基、ドデシル基など炭素数２０以下のアルキル基が挙げられ、より好ましくは炭素数８以下のアルキル基、特に好ましくは炭素数３以下のアルキル基が挙げられる。
　アルコキシカルボニル基に含まれるアルキル基としては、上記Ｒ４１～Ｒ４３におけるアルキル基と同様のものが好ましい。
　シクロアルキル基としては、単環型でも、多環型でもよい。好ましくは置換基を有していても良いシクロプロピル基、シクロペンチル基、シクロヘキシル基のような炭素数３～１０個で単環型のシクロアルキル基が挙げられる。
　ハロゲン原子としては、フッ素原子、塩素原子、臭素原子及びヨウ素原子が挙げられ、フッ素原子が特に好ましい。
　上記各基における好ましい置換基としては、例えば、アルキル基、シクロアルキル基、アリール基、アミノ基、アミド基、ウレイド基、ウレタン基、ヒドロキシル基、カルボキシル基、ハロゲン原子、アルコキシ基、チオエーテル基、アシル基、アシルオキシ基、アルコキシカルボニル基、シアノ基、ニトロ基等を挙げることができ、置換基の炭素数は８以下が好ましい。
　またＲ４２がアルキレン基でありＬ４と環を形成する場合、アルキレン基としては、好ましくはメチレン基、エチレン基、プロピレン基、ブチレン基、ヘキシレン基、オクチレン基等の炭素数１～８のアルキレン基が挙げられる。炭素数１～４のアルキレン基がより好ましく、炭素数１～２のアルキレン基が特に好ましい。Ｒ４２とＬ４とが結合して形成する環は、５又は６員環であることが特に好ましい。
　Ｒ４１及びＲ４３としては、水素原子、アルキル基、ハロゲン原子がより好ましく、水素原子、メチル基、エチル基、トリフルオロメチル基（－ＣＦ３）、ヒドロキシメチル基（－ＣＨ２－ＯＨ）、クロロメチル基（－ＣＨ２－Ｃｌ）、フッ素原子（－Ｆ）が特に好ましい。Ｒ４２としては、水素原子、アルキル基、ハロゲン原子、アルキレン基（Ｌ４と環を形成）がより好ましく、水素原子、メチル基、エチル基、トリフルオロメチル基（－ＣＦ３）、ヒドロキシメチル基（－ＣＨ２－ＯＨ）、クロロメチル基（－ＣＨ２－Ｃｌ）、フッ素原子（－Ｆ）、メチレン基（Ｌ４と環を形成）、エチレン基（Ｌ４と環を形成）が特に好ましい。
　Ｌ４で表される２価の連結基としては、アルキレン基、２価の芳香環基、－ＣＯＯ－Ｌ１－、－Ｏ－Ｌ１－、これらの２つ以上を組み合わせて形成される基等が挙げられる。ここで、Ｌ１はアルキレン基、シクロアルキレン基、２価の芳香環基、アルキレン基と２価の芳香環基を組み合わせた基を表す。
　Ｌ４は、単結合、－ＣＯＯ－Ｌ１－で表される基又は２価の芳香環基が好ましい。Ｌ１は炭素数１～５のアルキレン基が好ましく、メチレン、プロピレン基がより好ましい。２価の芳香環基としては、１，４－フェニレン基、１，３－フェニレン基、１，２－フェニレン基、１，４－ナフチレン基が好ましく、１，４－フェニレン基がより好ましい。
　Ｌ４がＲ４２と結合して環を形成する場合における、Ｌ４で表される３価の連結基としては、Ｌ４で表される２価の連結基の上記した具体例から１個の任意の水素原子を除してなる基を好適に挙げることができる。
　以下に一般式（５）で表される繰り返し単位の具体例を示すが、本発明はこれに限定されるものではない。
Figure JPOXMLDOC01-appb-C000022
　また、樹脂（Ａ）は、下記一般式（ＢＺ）で表される繰り返し単位を含んでいてもよい。
Figure JPOXMLDOC01-appb-C000023
　一般式（ＢＺ）中、ＡＲは、アリール基を表す。Ｒｎは、アルキル基、シクロアルキル基又はアリール基を表す。ＲｎとＡＲとは互いに結合して非芳香族環を形成してもよい。
　Ｒ１は、水素原子、アルキル基、シクロアルキル基、ハロゲン原子、シアノ基又はアルキルオキシカルボニル基を表す。
　以下に、一般式（ＢＺ）により表される繰り返し単位の具体例を示すが、これらに限定されるものではない。
Figure JPOXMLDOC01-appb-C000024
Figure JPOXMLDOC01-appb-C000025
　上記酸分解性基を有する繰り返し単位は、１種類であってもよいし、２種以上を併用してもよい。
　樹脂（Ａ）における酸分解性基を有する繰り返し単位の含有量（複数種類含有する場合はその合計）は、上記樹脂（Ａ）中の全繰り返し単位に対して５モル％以上８０モル％以下であることが好ましく、５モル％以上７５モル％以下であることがより好ましく、１０モル％以上６５モル％以下であることが更に好ましい。
　樹脂（Ａ）は、下記一般式（Ｖ－１）又は下記一般式（Ｖ－２）で表される繰り返し単位を含有してもよい。
Figure JPOXMLDOC01-appb-C000026
　式中、
　Ｒ６及びＲ7は、それぞれ独立に、水素原子、ヒドロキシ基、炭素数１～１０の直鎖状、分岐状又は環状のアルキル基、アルコキシ基又はアシロキシ基、シアノ基、ニトロ基、アミノ基、ハロゲン原子、エステル基（－ＯＣＯＲ又は－ＣＯＯＲ：Ｒは炭素数１～６のアルキル基又はフッ素化アルキル基）、又はカルボキシル基を表す。　
　ｎ３は０～６の整数を表す。
　ｎ４は０～４の整数を表す。
　Ｘ４はメチレン基、酸素原子又は硫黄原子である。　
　一般式（Ｖ－１）又は（Ｖ－２）で表される繰り返し単位の具体例を下記に示すが、これらに限定されない。
Figure JPOXMLDOC01-appb-C000027
　〔（Ｂ）活性光線又は放射線により酸を発生する化合物〕
　感活性光線性又は感放射線性組成物は、活性光線又は放射線により酸を発生する化合物（「光酸発生剤《ＰＡＧ：Ｐｈｏｔｏ　Ａｃｉｄ　Ｇｅｎｅｒａｔｏｒ》」、又は「化合物（Ｂ）」ともいう）を含有することが好ましい。
　光酸発生剤は、低分子化合物の形態であっても良く、重合体の一部に組み込まれた形態であっても良い。また、低分子化合物の形態と重合体の一部に組み込まれた形態を併用しても良い。
　光酸発生剤が、低分子化合物の形態である場合、分子量が３０００以下であることが好ましく、２０００以下であることがより好ましく、１０００以下であることが更に好ましい。
　光酸発生剤が、重合体の一部に組み込まれた形態である場合、樹脂（Ａ）の一部に組み込まれても良く、樹脂（Ａ）とは異なる樹脂に組み込まれても良い。
　本発明において、光酸発生剤が、低分子化合物の形態であることが好ましい。
　光酸発生剤としては、公知のものであれば特に限定されないが、活性光線又は放射線、好ましくは電子線又は極紫外線の照射により、有機酸、例えば、スルホン酸、ビス（アルキルスルホニル）イミド、又はトリス（アルキルスルホニル）メチドの少なくともいずれかを発生する化合物が好ましい。
　より好ましくは下記一般式（ＺＩ）、（ＺＩＩ）、（ＺＩＩＩ）で表される化合物を挙げることができる。
Figure JPOXMLDOC01-appb-C000028
　上記一般式（ＺＩ）において、
　Ｒ２０１、Ｒ２０２及びＲ２０３は、各々独立に、有機基を表す。
　Ｒ２０１、Ｒ２０２及びＲ２０３としての有機基の炭素数は、一般的に１～３０、好ましくは１～２０である。
　また、Ｒ２０１～Ｒ２０３のうち２つが結合して環構造を形成してもよく、環内に酸素原子、硫黄原子、エステル結合、アミド結合、カルボニル基を含んでいてもよい。Ｒ２０１～Ｒ２０３の内の２つが結合して形成する基としては、アルキレン基（例えば、ブチレン基、ペンチレン基）を挙げることができる。
　Ｚ－は、非求核性アニオン（求核反応を起こす能力が著しく低いアニオン）を表す。
　非求核性アニオンとしては、例えば、スルホン酸アニオン（脂肪族スルホン酸アニオン、芳香族スルホン酸アニオン、カンファースルホン酸アニオンなど）、カルボン酸アニオン（脂肪族カルボン酸アニオン、芳香族カルボン酸アニオン、アラルキルカルボン酸アニオンなど）、スルホニルイミドアニオン、ビス（アルキルスルホニル）イミドアニオン、トリス（アルキルスルホニル）メチドアニオン等を挙げられる。
　脂肪族スルホン酸アニオン及び脂肪族カルボン酸アニオンにおける脂肪族部位は、アルキル基であってもシクロアルキル基であってもよく、好ましくは炭素数１～３０の直鎖又は分岐のアルキル基及び炭素数３～３０のシクロアルキル基が挙げられる。
　芳香族スルホン酸アニオン及び芳香族カルボン酸アニオンにおける芳香族基としては、好ましくは炭素数６～１４のアリール基、例えば、フェニル基、トリル基、ナフチル基等を挙げることができる。
　上記で挙げたアルキル基、シクロアルキル基及びアリール基は、置換基を有していてもよい。この具体例としては、ニトロ基、フッ素原子などのハロゲン原子、カルボキシル基、水酸基、アミノ基、シアノ基、アルコキシ基（好ましくは炭素数１～１５）、シクロアルキル基（好ましくは炭素数３～１５）、アリール基（好ましくは炭素数６～１４）、アルコキシカルボニル基（好ましくは炭素数２～７）、アシル基（好ましくは炭素数２～１２）、アルコキシカルボニルオキシ基（好ましくは炭素数２～７）、アルキルチオ基（好ましくは炭素数１～１５）、アルキルスルホニル基（好ましくは炭素数１～１５）、アルキルイミノスルホニル基（好ましくは炭素数１～１５）、アリールオキシスルホニル基（好ましくは炭素数６～２０）、アルキルアリールオキシスルホニル基（好ましくは炭素数７～２０）、シクロアルキルアリールオキシスルホニル基（好ましくは炭素数１０～２０）、アルキルオキシアルキルオキシ基（好ましくは炭素数５～２０）、シクロアルキルアルキルオキシアルキルオキシ基（好ましくは炭素数８～２０）等を挙げることができる。各基が有するアリール基及び環構造については、置換基として更にアルキル基（好ましくは炭素数１～１５）を挙げることができる。
　アラルキルカルボン酸アニオンにおけるアラルキル基としては、好ましくは炭素数７～１２のアラルキル基、例えば、ベンジル基、フェネチル基、ナフチルメチル基、ナフチルエチル基、ナフチルブチル基等を挙げることができる。
　スルホニルイミドアニオンとしては、例えば、サッカリンアニオンを挙げることができる。
　ビス（アルキルスルホニル）イミドアニオン、トリス（アルキルスルホニル）メチドアニオンにおけるアルキル基は、炭素数１～５のアルキル基が好ましい。これらのアルキル基の置換基としてはハロゲン原子、ハロゲン原子で置換されたアルキル基、アルコキシ基、アルキルチオ基、アルキルオキシスルホニル基、アリールオキシスルホニル基、シクロアルキルアリールオキシスルホニル基等を挙げることができ、フッ素原子又はフッ素原子で置換されたアルキル基が好ましい。
　また、ビス（アルキルスルホニル）イミドアニオンにおけるアルキル基は、互いに結合して環構造を形成してもよい。これにより、酸強度が増加する。
　その他の非求核性アニオンとしては、例えば、弗素化燐（例えば、ＰＦ６ －）、弗素化硼素（例えば、ＢＦ４ －）、弗素化アンチモン（例えば、ＳｂＦ６ －）等を挙げることができる。
　非求核性アニオンとしては、スルホン酸の少なくともα位がフッ素原子で置換された脂肪族スルホン酸アニオン、フッ素原子又はフッ素原子を有する基で置換された芳香族スルホン酸アニオン、アルキル基がフッ素原子で置換されたビス（アルキルスルホニル）イミドアニオン、アルキル基がフッ素原子で置換されたトリス（アルキルスルホニル）メチドアニオンが好ましい。非求核性アニオンとして、より好ましくはパーフロロ脂肪族スルホン酸アニオン（更に好ましくは炭素数４～８）、フッ素原子を有するベンゼンスルホン酸アニオン、更により好ましくはノナフロロブタンスルホン酸アニオン、パーフロロオクタンスルホン酸アニオン、ペンタフロロベンゼンスルホン酸アニオン、３，５－ビス（トリフロロメチル）ベンゼンスルホン酸アニオンである。
　酸強度の観点からは、発生酸のｐＫａが－１以下であることが、感度向上のために好ましい。
　また、非求核性アニオンとしては、以下の一般式（ＡＮ１）で表されるアニオンも好ましい態様として挙げられる。
Figure JPOXMLDOC01-appb-C000029
　式中、
　Ｘｆは、それぞれ独立に、フッ素原子、又は少なくとも１つのフッ素原子で置換されたアルキル基を表す。
　Ｒ１、Ｒ２は、それぞれ独立に、水素原子、フッ素原子、又は、アルキル基を表し、複数存在する場合のＲ１、Ｒ２は、それぞれ同一でも異なっていてもよい。
　Ｌは、二価の連結基を表し、複数存在する場合のＬは同一でも異なっていてもよい。
　Ａは、環状の有機基を表す。
　ｘは１～２０の整数を表し、ｙは０～１０の整数を表し、ｚは０～１０の整数を表す。
　一般式（ＡＮ１）について、更に詳細に説明する。
　Ｘｆのフッ素原子で置換されたアルキル基におけるアルキル基としては、好ましくは炭素数１～１０であり、より好ましくは炭素数１～４である。また、Ｘｆのフッ素原子で置換されたアルキル基は、パーフルオロアルキル基であることが好ましい。
　Ｘｆとして好ましくは、フッ素原子又は炭素数１～４のパーフルオロアルキル基である。Ｘｆの具体的としては、フッ素原子、ＣＦ３、Ｃ２Ｆ５、Ｃ３Ｆ７、Ｃ４Ｆ９、ＣＨ２ＣＦ３、ＣＨ２ＣＨ２ＣＦ３、ＣＨ２Ｃ２Ｆ５、ＣＨ２ＣＨ２Ｃ２Ｆ５、ＣＨ２Ｃ３Ｆ７、ＣＨ２ＣＨ２Ｃ３Ｆ７、ＣＨ２Ｃ４Ｆ９、ＣＨ２ＣＨ２Ｃ４Ｆ９が挙げられ、中でもフッ素原子、ＣＦ３が好ましい。特に、双方のＸｆがフッ素原子であることが好ましい。
　Ｒ１、Ｒ２のアルキル基は、置換基（好ましくはフッ素原子）を有していてもよく、炭素数１～４のものが好ましい。更に好ましくは炭素数１～４のパーフルオロアルキル基である。Ｒ１、Ｒ２の置換基を有するアルキル基の具体例としては、ＣＦ３、Ｃ２Ｆ５、Ｃ３Ｆ７、Ｃ４Ｆ９、Ｃ５Ｆ１１、Ｃ６Ｆ１３、Ｃ７Ｆ１５、Ｃ８Ｆ１７、ＣＨ２ＣＦ３、ＣＨ２ＣＨ２ＣＦ３、ＣＨ２Ｃ２Ｆ５、ＣＨ２ＣＨ２Ｃ２Ｆ５、ＣＨ２Ｃ３Ｆ７、ＣＨ２ＣＨ２Ｃ３Ｆ７、ＣＨ２Ｃ４Ｆ９、ＣＨ２ＣＨ２Ｃ４Ｆ９が挙げられ、中でもＣＦ３が好ましい。
　Ｒ１、Ｒ２としては、好ましくはフッ素原子又はＣＦ３である。
　ｘは１～１０が好ましく、１～５がより好ましい。
　ｙは０～４が好ましく、０がより好ましい。
　ｚは０～５が好ましく、０～３がより好ましい。
　Ｌの２価の連結基としては特に限定されず、―ＣＯＯ－、－ＯＣＯ－、－ＣＯ－、－Ｏ－、－Ｓ―、－ＳＯ―、―ＳＯ２－、アルキレン基、シクロアルキレン基、アルケニレン基又はこれらの複数が連結した連結基などを挙げることができ、総炭素数１２以下の連結基が好ましい。このなかでも―ＣＯＯ－、－ＯＣＯ－、－ＣＯ－、－Ｏ－が好ましく、―ＣＯＯ－、－ＯＣＯ－がより好ましい。
　Ａの環状の有機基としては、環状構造を有するものであれば特に限定されず、脂環基、アリール基、複素環基（芳香族性を有するものだけでなく、芳香族性を有さないものも含む）等が挙げられる。
　脂環基としては、単環でも多環でもよく、シクロペンチル基、シクロヘキシル基、シクロオクチル基などの単環のシクロアルキル基、ノルボルニル基、トリシクロデカニル基、テトラシクロデカニル基、テトラシクロドデカニル基、アダマンチル基などの多環のシクロアルキル基が好ましい。中でも、ノルボルニル基、トリシクロデカニル基、テトラシクロデカニル基、テトラシクロドデカニル基、アダマンチル基等の炭素数７以上のかさ高い構造を有する脂環基が、露光後加熱工程での膜中拡散性を抑制でき、ＭＥＥＦ向上の観点から好ましい。
　アリール基としては、ベンゼン環、ナフタレン環、フェナンスレン環、アントラセン環が挙げられる。
　複素環基としては、フラン環、チオフェン環、ベンゾフラン環、ベンゾチオフェン環、ジベンゾフラン環、ジベンゾチオフェン環、ピリジン環由来のものが挙げられる。中でもフラン環、チオフェン環、ピリジン環由来のものが好ましい。
　また、環状の有機基としては、ラクトン構造も挙げることができ、具体例としては、前述の一般式（ＬＣ１－１）～（ＬＣ１－１７）で表されるラクトン構造を挙げることができる。
　上記環状の有機基は、置換基を有していてもよく、上記置換基としては、アルキル基（直鎖、分岐、環状のいずれであっても良く、炭素数１～１２が好ましい）、シクロアルキル基（単環、多環、スピロ環のいずれであっても良く、炭素数３～２０が好ましい）、アリール基（炭素数６～１４が好ましい）、ヒドロキシ基、アルコキシ基、エステル基、アミド基、ウレタン基、ウレイド基、チオエーテル基、スルホンアミド基、スルホン酸エステル基等が挙げられる。なお、環状の有機基を構成する炭素（環形成に寄与する炭素）はカルボニル炭素であっても良い。
　Ｒ２０１、Ｒ２０２及びＲ２０３の有機基としては、アリール基、アルキル基、シクロアルキル基などが挙げられる。
　Ｒ２０１、Ｒ２０２及びＲ２０３のうち、少なくとも１つがアリール基であることが好ましく、三つ全てがアリール基であることがより好ましい。アリール基としては、フェニル基、ナフチル基などの他に、インドール残基、ピロール残基などのヘテロアリール基も可能である。Ｒ２０１～Ｒ２０３のアルキル基及びシクロアルキル基としては、好ましくは、炭素数１～１０の直鎖又は分岐アルキル基、炭素数３～１０のシクロアルキル基を挙げることができる。アルキル基として、より好ましくはメチル基、エチル基、ｎ－プロピル基、ｉ－プロピル基、ｎ－ブチル基等を挙げることができる。シクロアルキル基として、より好ましくは、シクロプロピル基、シクロブチル基、シクロペンチル基、シクロヘキシル基、シクロへプチル基等を挙げることができる。これらの基は更に置換基を有していてもよい。その置換基としては、ニトロ基、フッ素原子などのハロゲン原子、カルボキシル基、水酸基、アミノ基、シアノ基、アルコキシ基（好ましくは炭素数１～１５）、シクロアルキル基（好ましくは炭素数３～１５）、アリール基（好ましくは炭素数６～１４）、アルコキシカルボニル基（好ましくは炭素数２～７）、アシル基（好ましくは炭素数２～１２）、アルコキシカルボニルオキシ基（好ましくは炭素数２～７）等が挙げられるが、これらに限定されるものではない。
　一般式（ＺＩＩ）、（ＺＩＩＩ）中、
　Ｒ２０４～Ｒ２０７は、各々独立に、アリール基、アルキル基又はシクロアルキル基を表す。
　Ｒ２０４～Ｒ２０７のアリール基、アルキル基、シクロアルキル基としては、前述の化合物（ＺＩ）におけるＲ２０１～Ｒ２０３のアリール基、アルキル基、シクロアルキル基として説明したアリール基と同様である。
　Ｒ２０４～Ｒ２０７のアリール基、アルキル基、シクロアルキル基は、置換基を有していてもよい。この置換基としても、前述の化合物（ＺＩ）におけるＲ２０１～Ｒ２０３のアリール基、アルキル基、シクロアルキル基が有していてもよいものが挙げられる。
　Ｚ－は、非求核性アニオンを表し、一般式（ＺＩ）に於けるＺ－の非求核性アニオンと同様のものを挙げることができる。
　本発明においては、上記光酸発生剤は、露光で発生した酸の非露光部への拡散を抑制し解像性を良好にする観点から、電子線又は極紫外線の照射により、体積１３０Å３以上の大きさの酸（より好ましくはスルホン酸）を発生する化合物であることが好ましく、体積１９０Å３以上の大きさの酸（より好ましくはスルホン酸）を発生する化合物であることがより好ましく、体積２７０Å３以上の大きさの酸（より好ましくはスルホン酸）を発生する化合物であることが更に好ましく、体積４００Å３以上の大きさの酸（より好ましくはスルホン酸）を発生する化合物であることが特に好ましい。ただし、感度や塗布溶剤溶解性の観点から、上記体積は、２０００Å３以下であることが好ましく、１５００Å３以下であることが更に好ましい。上記体積の値は、富士通株式会社製の「ＷｉｎＭＯＰＡＣ」を用いて求めた。すなわち、まず、各例に係る酸の化学構造を入力し、次に、この構造を初期構造としてＭＭ３法を用いた分子力場計算により、各酸の最安定立体配座を決定し、その後、これら最安定立体配座についてＰＭ３法を用いた分子軌道計算を行うことにより、各酸の「ａｃｃｅｓｓｉｂｌｅ　ｖｏｌｕｍｅ」を計算することができる。
　本発明においては、活性光線又は放射線の照射により以下に例示する酸を発生する光酸発生剤が好ましい。なお、例の一部には、体積の計算値を付記している（単位Å３）。なお、ここで求めた計算値は、アニオン部にプロトンが結合した酸の体積値である。
　１Åは１×１０－１０ｍである。
Figure JPOXMLDOC01-appb-C000030
Figure JPOXMLDOC01-appb-C000031
Figure JPOXMLDOC01-appb-C000032
　光酸発生剤としては、特開２０１４－４１３２８号公報段落［０３６８］～［０３７７］、特開２０１３－２２８６８１号公報段落［０２４０］～［０２６２］（対応する米国特許出願公開第２０１５／００４５３３号明細書の［０３３９］）が援用でき、これらの内容は本願明細書に組み込まれる。また、好ましい具体例として以下の化合物が挙げられるが、これらに限定されるものではない。
Figure JPOXMLDOC01-appb-C000033
Figure JPOXMLDOC01-appb-C000034
Figure JPOXMLDOC01-appb-C000035
　光酸発生剤は、１種類単独で又は２種類以上を組み合わせて使用することができる。
　光酸発生剤の感活性光線性又は感放射線性組成物中の含有量は、組成物の全固形分を基準として、０．１～５０質量％が好ましく、より好ましくは５～５０質量％、更に好ましくは８～４０質量％である。特に、電子線や極紫外線露光の際に高感度化、高解像性を両立するには光酸発生剤の含有率は高いほうが好ましく、更に好ましくは１０～４０質量％、最も好ましくは１０～３５質量％である。
　（Ｃ）溶剤
　本発明において用いられる感活性光線性又は感放射線性組成物は、溶剤（「レジスト溶剤」ともいう）を含んでいることが好ましい。この溶剤は、（Ｍ１）プロピレングリコールモノアルキルエーテルカルボキシレートと、（Ｍ２）プロピレングリコールモノアルキルエーテル、乳酸エステル、酢酸エステル、アルコキシプロピオン酸エステル、鎖状ケトン、環状ケトン、ラクトン、及びアルキレンカーボネートからなる群より選択される少なくとも１つとの少なくとも一方を含んでいることが好ましい。なお、この溶剤は、成分（Ｍ１）及び（Ｍ２）以外の成分を更に含んでいてもよい。
　本発明者らは、このような溶剤と上述した樹脂とを組み合わせて用いると、組成物の塗布性が向上すると共に、現像欠陥数の少ないパターンが形成可能となることを見出している。その理由は必ずしも明らかではないが、本発明者らは、これら溶剤は、上述した樹脂の溶解性、沸点、及び粘度のバランスが良いため、組成物膜の膜厚のムラやスピンコート中の析出物の発生などを抑制できることに起因していると考えている。
　成分（Ｍ１）としては、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノメチルエーテルプロピオネート、及び、プロピレングリコールモノエチルエーテルアセテートからなる群より選択される少なくとも１つが好ましく、プロピレングリコールモノメチルエーテルアセテートが特に好ましい。
　成分（Ｍ２）としては、以下のものが好ましい。
　プロピレングリコールモノアルキルエーテルとしては、プロピレングリコールモノメチルエーテル又はプロピレングリコールモノエチルエーテルが好ましい。
　乳酸エステルとしては、乳酸エチル、乳酸ブチル、又は乳酸プロピルが好ましい。
　酢酸エステルとしては、酢酸メチル、酢酸エチル、酢酸ブチル、酢酸イソブチル、酢酸プロピル、酢酸イソアミル、蟻酸メチル、蟻酸エチル、蟻酸ブチル、蟻酸プロピル、又は酢酸３－メトキシブチルが好ましい。
　酪酸ブチルも好ましい。
　アルコキシプロピオン酸エステルとしては、３－メトキシプロピオン酸メチル（ＭＭＰ）、又は、３－エトキシプロピオン酸エチル（ＥＥＰ）が好ましい。
　鎖状ケトンとしては、１－オクタノン、２－オクタノン、１－ノナノン、２－ノナノン、アセトン、４－ヘプタノン、１－ヘキサノン、２－ヘキサノン、ジイソブチルケトン、フェニルアセトン、メチルエチルケトン、メチルイソブチルケトン、アセチルアセトン、アセトニルアセトン、イオノン、ジアセトニルアルコール、アセチルカービノール、アセトフェノン、メチルナフチルケトン、又はメチルアミルケトンが好ましい。
　環状ケトンとしては、メチルシクロヘキサノン、イソホロン、又はシクロヘキサノンが好ましい。
　ラクトンとしては、γ－ブチロラクトンが好ましい。
　アルキレンカーボネートとしては、プロピレンカーボネートが好ましい。
　成分（Ｍ２）としては、プロピレングリコールモノメチルエーテル、乳酸エチル、３－エトキシプロピオン酸エチル、メチルアミルケトン、シクロヘキサノン、酢酸ブチル、酢酸ペンチル、γ－ブチロラクトン又はプロピレンカーボネートがより好ましい。
　上記成分の他、炭素原子数が７以上（７～１４が好ましく、７～１２がより好ましく、７～１０が更に好ましい）、かつヘテロ原子数が２以下のエステル系溶剤を用いることが好ましい。
　炭素原子数が７以上かつヘテロ原子数が２以下のエステル系溶剤の好ましい例としては、酢酸アミル、酢酸２－メチルブチル、酢酸１-メチルブチル、酢酸ヘキシル、プロピオン酸ペンチル、プロピオン酸ヘキシル、プロピオン酸ブチル、イソ酪酸イソブチル、プロピオン酸ヘプチル、ブタン酸ブチルなどが挙げられ、酢酸イソアミルを用いることが特に好ましい。
　成分（Ｍ２）としては、引火点（以下、ｆｐともいう）が３７℃以上であるものを用いることが好ましい。このような成分（Ｍ２）としては、プロピレングリコールモノメチルエーテル（ｆｐ：４７℃）、乳酸エチル（ｆｐ：５３℃）、３－エトキシプロピオン酸エチル（ｆｐ：４９℃）、メチルアミルケトン（ｆｐ：４２℃）、シクロヘキサノン（ｆｐ：４４℃）、酢酸ペンチル（ｆｐ：４５℃）、２－ヒドロキシイソ酪酸メチル（ｆｐ：４５℃）、γ－ブチロラクトン（ｆｐ：１０１℃）又はプロピレンカーボネート（ｆｐ：１３２℃）が好ましい。これらのうち、プロピレングリコールモノエチルエーテル、乳酸エチル、酢酸ペンチル、又はシクロヘキサノンが更に好ましく、プロピレングリコールモノエチルエーテル又は乳酸エチルが特に好ましい。なお、ここで「引火点」とは、東京化成工業株式会社又はシグマアルドリッチ社の試薬カタログに記載されている値を意味している。
　溶剤は、成分（Ｍ１）を含んでいることが好ましい。溶剤は、実質的に成分（Ｍ１）のみからなるか、又は、成分（Ｍ１）と他の成分との混合溶剤であることがより好ましい。後者の場合、溶剤は、成分（Ｍ１）と成分（Ｍ２）との双方を含んでいることが更に好ましい。
　成分（Ｍ１）と成分（Ｍ２）との質量比は、１００：０乃至１５：８５の範囲内にあることが好ましく、１００：０乃至４０：６０の範囲内にあることがより好ましく、１００：０乃至６０：４０の範囲内にあることが更に好ましい。即ち、溶剤は、成分（Ｍ１）のみからなるか、又は、成分（Ｍ１）と成分（Ｍ２）との双方を含んでおりかつそれらの質量比が以下の通りであることが好ましい。即ち、後者の場合、成分（Ｍ２）に対する成分（Ｍ１）の質量比は、１５／８５以上であることが好ましく、４０／６０以上であることよりが好ましく、６０／４０以上であることが更に好ましい。このような構成を採用すると、現像欠陥数を更に減少させることが可能となる。
　なお、溶剤が成分（Ｍ１）と成分（Ｍ２）との双方を含んでいる場合、成分（Ｍ２）に対する成分（Ｍ１）の質量比は、例えば、９９／１以下とする。
　上述した通り、溶剤は、成分（Ｍ１）及び（Ｍ２）以外の成分を更に含んでいてもよい。この場合、成分（Ｍ１）及び（Ｍ２）以外の成分の含有量は、溶剤の全量に対して、５質量％乃至３０質量％の範囲内にあることが好ましい。
　感活性光線性又は感放射線性組成物に占める溶剤の含有量は、全成分の固形分濃度が０．５～３０質量％となるように定めることが好ましく、１～２０質量％となるように定めることがより好ましい。こうすると、感活性光線性又は感放射線性組成物の塗布性を更に向上させることができる。
（Ｅ）塩基性化合物
　本発明のレジスト組成物は、露光から加熱までの経時による性能変化を低減するために、（Ｅ）塩基性化合物を含有することが好ましい。
　塩基性化合物としては、好ましくは、下記式（Ａ）～（Ｅ）で示される構造を有する化合物を挙げることができる。
Figure JPOXMLDOC01-appb-C000036
　一般式（Ａ）及び（Ｅ）中、Ｒ２００、Ｒ２０１及びＲ２０２は、同一でも異なってもよく、水素原子、アルキル基（好ましくは炭素数１～２０）、シクロアルキル基（好ましくは炭素数３～２０）又はアリール基（好ましくは炭素数６～２０）を表し、ここで、Ｒ２０１とＲ２０２は、互いに結合して環を形成してもよい。
　上記アルキル基について、置換基を有するアルキル基としては、炭素数１～２０のアミノアルキル基、炭素数１～２０のヒドロキシアルキル基、又は炭素数１～２０のシアノアルキル基が好ましい。
　Ｒ２０３、Ｒ２０４、Ｒ２０５及びＲ２０６は、同一でも異なってもよく、炭素数１～２０個のアルキル基を表す。
　これら一般式（Ａ）及び（Ｅ）中のアルキル基は、無置換であることがより好ましい。
　好ましい化合物として、グアニジン、アミノピロリジン、ピラゾール、ピラゾリン、ピペラジン、アミノモルホリン、アミノアルキルモルフォリン、ピペリジン等を挙げることができ、更に好ましい化合物として、イミダゾール構造、ジアザビシクロ構造、オニウムヒドロキシド構造、オニウムカルボキシレート構造、トリアルキルアミン構造、アニリン構造又はピリジン構造を有する化合物、水酸基及び／又はエーテル結合を有するアルキルアミン誘導体、水酸基及び／又はエーテル結合を有するアニリン誘導体等を挙げることができる。
　イミダゾール構造を有する化合物としてはイミダゾール、２、４、５－トリフェニルイミダゾール、ベンズイミダゾール等が挙げられる。ジアザビシクロ構造を有する化合物としては１、４－ジアザビシクロ［２，２，２］オクタン、１、５－ジアザビシクロ［４，３，０］ノナ－５－エン、１、８－ジアザビシクロ［５，４，０］ウンデカ－７－エン等が挙げられる。オニウムヒドロキシド構造を有する化合物としてはトリアリールスルホニウムヒドロキシド、フェナシルスルホニウムヒドロキシド、２－オキソアルキル基を有するスルホニウムヒドロキシド、具体的にはトリフェニルスルホニウムヒドロキシド、トリス（ｔ－ブチルフェニル）スルホニウムヒドロキシド、ビス（ｔ－ブチルフェニル）ヨードニウムヒドロキシド、フェナシルチオフェニウムヒドロキシド、２－オキソプロピルチオフェニウムヒドロキシド等が挙げられる。オニウムカルボキシレート構造を有する化合物としてはオニウムヒドロキシド構造を有する化合物のアニオン部がカルボキシレートになったものであり、例えばアセテート、アダマンタン－１－カルボキシレート、パーフロロアルキルカルボキシレート等が挙げられる。トリアルキルアミン構造を有する化合物としては、トリ（ｎ－ブチル）アミン、トリ（ｎ－オクチル）アミン等を挙げることができる。アニリン化合物としては、２，６－ジイソプロピルアニリン、Ｎ，Ｎ－ジメチルアニリン、Ｎ，Ｎ－ジブチルアニリン、Ｎ，Ｎ－ジヘキシルアニリン等を挙げることができる。水酸基及び／又はエーテル結合を有するアルキルアミン誘導体としては、エタノールアミン、ジエタノールアミン、トリエタノールアミン、トリス（メトキシエトキシエチル）アミン等を挙げることができる。水酸基及び／又はエーテル結合を有するアニリン誘導体としては、Ｎ，Ｎ－ビス（ヒドロキシエチル）アニリン等を挙げることができる。
　好ましい塩基性化合物として、更に、フェノキシ基を有するアミン化合物、フェノキシ基を有するアンモニウム塩化合物を挙げることができる。
　アミン化合物は、１級、２級、３級のアミン化合物を使用することができ、少なくとも１つのアルキル基が窒素原子に結合しているアミン化合物が好ましい。アミン化合物は、３級アミン化合物であることがより好ましい。アミン化合物は、少なくとも１つのアルキル基（好ましくは炭素数１～２０）が窒素原子に結合していれば、アルキル基の他に、シクロアルキル基（好ましくは炭素数３～２０）又はアリール基（好ましくは炭素数６～１２）が窒素原子に結合していてもよい。
　また、アミン化合物は、アルキル鎖中に、酸素原子を有し、オキシアルキレン基が形成されていることが好ましい。オキシアルキレン基の数は、分子内に１つ以上、好ましくは３～９個、更に好ましくは４～６個である。オキシアルキレン基の中でもオキシエチレン基（－ＣＨ２ＣＨ２Ｏ－）若しくはオキシプロピレン基（－ＣＨ（ＣＨ３）ＣＨ２Ｏ－若しくは－ＣＨ２ＣＨ２ＣＨ２Ｏ－）が好ましく、更に好ましくはオキシエチレン基である。
　アンモニウム塩化合物は、１級、２級、３級、４級のアンモニウム塩化合物を使用することができ、少なくとも１つのアルキル基が窒素原子に結合しているアンモニウム塩化合物が好ましい。アンモニウム塩化合物は、少なくとも１つのアルキル基（好ましくは炭素数１～２０）が窒素原子に結合していれば、アルキル基の他に、シクロアルキル基（好ましくは炭素数３～２０）又はアリール基（好ましくは炭素数６～１２）が窒素原子に結合していてもよい。
　アンモニウム塩化合物は、アルキル鎖中に、酸素原子を有し、オキシアルキレン基が形成されていることが好ましい。オキシアルキレン基の数は、分子内に１つ以上、好ましくは３～９個、更に好ましくは４～６個である。オキシアルキレン基の中でもオキシエチレン基（－ＣＨ２ＣＨ２Ｏ－）若しくはオキシプロピレン基（－ＣＨ（ＣＨ３）ＣＨ２Ｏ－若しくは－ＣＨ２ＣＨ２ＣＨ２Ｏ－）が好ましく、更に好ましくはオキシエチレン基である。
　アンモニウム塩化合物のアニオンとしては、ハロゲン原子、スルホネート、ボレート、フォスフェート等が挙げられるが、中でもハロゲン原子、スルホネートが好ましい。ハロゲン原子としてはクロライド、ブロマイド、アイオダイドが特に好ましく、スルホネートとしては、炭素数１～２０の有機スルホネートが特に好ましい。有機スルホネートとしては、炭素数１～２０のアルキルスルホネート、アリールスルホネートが挙げられる。アルキルスルホネートのアルキル基は置換基を有していてもよく、置換基としては例えばフッ素、塩素、臭素、アルコキシ基、アシル基、アリール基等が挙げられる。アルキルスルホネートとして、具体的にはメタンスルホネート、エタンスルホネート、ブタンスルホネート、ヘキサンスルホネート、オクタンスルホネート、ベンジルスルホネート、トリフルオロメタンスルホネート、ペンタフルオロエタンスルホネート、ノナフルオロブタンスルホネート等が挙げられる。アリールスルホネートのアリール基としてはベンゼン環、ナフタレン環、アントラセン環が挙げられる。ベンゼン環、ナフタレン環、アントラセン環は置換基を有していてもよく、置換基としては炭素数１～６の直鎖若しくは分岐アルキル基、炭素数３～６のシクロアルキル基が好ましい。直鎖若しくは分岐アルキル基、シクロアルキル基として、具体的には、メチル、エチル、ｎ－プロピル、イソプロピル、ｎ－ブチル、ｉ－ブチル、ｔ－ブチル、ｎ－ヘキシル、シクロヘキシル等が挙げられる。他の置換基としては炭素数１～６のアルコキシ基、ハロゲン原子、シアノ、ニトロ、アシル基、アシルオキシ基等が挙げられる。
　フェノキシ基を有するアミン化合物、フェノキシ基を有するアンモニウム塩化合物とは、アミン化合物又はアンモニウム塩化合物のアルキル基の窒素原子と反対側の末端にフェノキシ基を有するものである。フェノキシ基は、置換基を有していてもよい。フェノキシ基の置換基としては、例えば、アルキル基、アルコキシ基、ハロゲン原子、シアノ基、ニトロ基、カルボキシル基、カルボン酸エステル基、スルホン酸エステル基、アリール基、アラルキル基、アシルオキシ基、アリールオキシ基等が挙げられる。置換基の置換位は、２～６位のいずれであってもよい。置換基の数は、１～５の範囲で何れであってもよい。
　フェノキシ基と窒素原子との間に、少なくとも１つのオキシアルキレン基を有することが好ましい。オキシアルキレン基の数は、分子内に１つ以上、好ましくは３～９個、更に好ましくは４～６個である。オキシアルキレン基の中でもオキシエチレン基（－ＣＨ２ＣＨ２Ｏ－）若しくはオキシプロピレン基（－ＣＨ（ＣＨ３）ＣＨ２Ｏ－若しくは－ＣＨ２ＣＨ２ＣＨ２Ｏ－）が好ましく、更に好ましくはオキシエチレン基である。
　フェノキシ基を有するアミン化合物は、フェノキシ基を有する１又は２級アミンとハロアルキルエーテルを加熱して反応させた後、水酸化ナトリウム、水酸化カリウム、テトラアルキルアンモニウム等の強塩基の水溶液を添加した後、酢酸エチル、クロロホルム等の有機溶剤で抽出することにより得ることができる。又は、１又は２級アミンと末端にフェノキシ基を有するハロアルキルエーテルを加熱して反応させた後、水酸化ナトリウム、水酸化カリウム、テトラアルキルアンモニウム等の強塩基の水溶液を添加した後、酢酸エチル、クロロホルム等の有機溶剤で抽出することにより得ることができる。
（プロトンアクセプター性官能基を有し、かつ、活性光線又は放射線の照射により分解してプロトンアクセプター性が低下、消失、又はプロトンアクセプター性から酸性に変化した化合物を発生する化合物（ＰＡ））
　本発明に係る組成物は、塩基性化合物として、プロトンアクセプター性官能基を有し、かつ、活性光線又は放射線の照射により分解してプロトンアクセプター性が低下、消失、又はプロトンアクセプター性から酸性に変化した化合物を発生する化合物〔以下、化合物（ＰＡ）ともいう〕を更に含んでいてもよい。
　プロトンアクセプター性官能基とは、プロトンと静電的に相互作用し得る基或いは電子を有する官能基であって、例えば、環状ポリエーテル等のマクロサイクリック構造を有する官能基や、π共役に寄与しない非共有電子対をもった窒素原子を有する官能基を意味する。π共役に寄与しない非共有電子対を有する窒素原子とは、例えば、下記一般式に示す部分構造を有する窒素原子である。
Figure JPOXMLDOC01-appb-C000037
　プロトンアクセプター性官能基の好ましい部分構造として、例えば、クラウンエーテル、アザクラウンエーテル、１～３級アミン、ピリジン、イミダゾール、ピラジン構造などを挙げることができる。
　化合物（ＰＡ）は、活性光線又は放射線の照射により分解してプロトンアクセプター性が低下、消失、又はプロトンアクセプター性から酸性に変化した化合物を発生する。ここで、プロトンアクセプター性の低下、消失、又はプロトンアクセプター性から酸性への変化とは、プロトンアクセプター性官能基にプロトンが付加することに起因するプロトンアクセプター性の変化であり、具体的には、プロトンアクセプター性官能基を有する化合物（ＰＡ）とプロトンからプロトン付加体が生成する時、その化学平衡に於ける平衡定数が減少することを意味する。
　化合物（ＰＡ）の具体例としては、例えば、下記化合物を挙げることができる。更に、化合物（ＰＡ）の具体例としては、例えば、特開２０１４－４１３２８号公報の段落０４２１～０４２８、特開２０１４－１３４６８６号公報の段落０１０８～０１１６に記載されたものを援用することができ、これらの内容は本明細書に組み込まれる。
Figure JPOXMLDOC01-appb-C000038
Figure JPOXMLDOC01-appb-C000039
　これらの塩基性化合物は、単独であるいは２種以上一緒に用いられる。
　塩基性化合物の使用量は、レジスト組成物の固形分を基準として、通常、０．００１～１０質量％、好ましくは０．０１～５質量％である。
　酸発生剤と塩基性化合物の組成物中の使用割合は、酸発生剤／塩基性化合物（モル比）＝２．５～３００であることが好ましい。即ち、感度、解像度の点からモル比が２．５以上が好ましく、露光後加熱処理までの経時でのレジストパターンの太りによる解像度の低下抑制の点から３００以下が好ましい。酸発生剤／塩基性化合物（モル比）は、より好ましくは５．０～２００、更に好ましくは７．０～１５０である。
　塩基性化合物としては、例えば、特開２０１３－１１８３３号公報の段落０１４０～０１４４に記載の化合物（アミン化合物、アミド基含有化合物、ウレア化合物、含窒素複素環化合物等）を用いることができる。
　＜疎水性樹脂＞
　本発明における感活性光線性又は感放射線性組成物は、上記樹脂（Ａ）とは別に樹脂（Ａ）とは異なる疎水性樹脂を有していてもよい。
　疎水性樹脂はレジスト膜の表面に偏在するように設計されることが好ましいが、界面活性剤とは異なり、必ずしも分子内に親水基を有する必要はなく、極性／非極性物質を均一に混合することに寄与しなくてもよい。
　疎水性樹脂を添加することの効果として、水に対するレジスト膜表面の静的／動的な接触角の制御、アウトガスの抑制などを挙げることができる。
　疎水性樹脂は、膜表層への偏在化の観点から、“フッ素原子”、“珪素原子”、及び、 “樹脂の側鎖部分に含有されたＣＨ３部分構造”のいずれか１種以上を有することが好ましく、２種以上を有することが更に好ましい。また、上記疎水性樹脂は、炭素数５以上の炭化水素基を含有することが好ましい。これらの基は樹脂の主鎖中に有していても、側鎖に置換していてもよい。
　疎水性樹脂が、フッ素原子及び／又は珪素原子を含む場合、疎水性樹脂に於ける上記フッ素原子及び／又は珪素原子は、樹脂の主鎖中に含まれていてもよく、側鎖中に含まれていてもよい。
　疎水性樹脂がフッ素原子を含んでいる場合、フッ素原子を有する部分構造として、フッ素原子を有するアルキル基、フッ素原子を有するシクロアルキル基、又は、フッ素原子を有するアリール基を有する樹脂であることが好ましい。
　フッ素原子を有するアルキル基（好ましくは炭素数１～１０、より好ましくは炭素数１～４）は、少なくとも１つの水素原子がフッ素原子で置換された直鎖又は分岐アルキル基であり、更にフッ素原子以外の置換基を有していてもよい。
　フッ素原子を有するシクロアルキル基は、少なくとも１つの水素原子がフッ素原子で置換された単環又は多環のシクロアルキル基であり、更にフッ素原子以外の置換基を有していてもよい。
　フッ素原子を有するアリール基としては、フェニル基、ナフチル基などのアリール基の少なくとも１つの水素原子がフッ素原子で置換されたものが挙げられ、更にフッ素原子以外の置換基を有していてもよい。
　フッ素原子又は珪素原子を有する繰り返し単位の例としては、ＵＳ２０１２／０２５１９４８Ａ１の段落０５１９に例示されたものを挙げることが出来る。
　また、上記したように、疎水性樹脂は、側鎖部分にＣＨ３部分構造を含むことも好ましい。
　ここで、疎水性樹脂中の側鎖部分が有するＣＨ３部分構造には、エチル基、プロピル基等が有するＣＨ３部分構造を包含するものである。
　一方、疎水性樹脂の主鎖に直接結合しているメチル基（例えば、メタクリル酸構造を有する繰り返し単位のα－メチル基）は、主鎖の影響により疎水性樹脂の表面偏在化への寄与が小さいため、本発明におけるＣＨ３部分構造に包含されないものとする。
　疎水性樹脂に関しては、特開２０１４－０１０２４５号公報の［０３４８］～［０４１５］の記載を参酌でき、これらの内容は本願明細書に組み込まれる。
　なお、疎水性樹脂としてはこの他にも特開２０１１－２４８０１９号公報、特開２０１０－１７５８５９号公報、特開２０１２－０３２５４４号公報記載のものも好ましく用いることができる。
　本発明のパターン形成方法では、基板上に上記感活性光線性又は感放射線性組成物を用いてレジスト膜を形成し得、上記レジスト膜上に上記トップコート組成物を用いてトップコート層を形成し得る。このレジスト膜の膜厚は、好ましくは１０～１００ｎｍであり、トップコート層の膜厚は、好ましくは１０～２００ｎｍ、更に好ましくは２０～１００ｎｍ、特に好ましくは４０～８０ｎｍである。
　基板上に感活性光線性又は感放射線性組成物を塗布する方法としては、スピン塗布が好ましく、その回転数は１０００～３０００ｒｐｍが好ましい。
　例えば、感活性光線性又は感放射線性組成物を精密集積回路素子の製造に使用されるような基板（例：シリコン／二酸化シリコン被覆）上にスピナー、コーター等の適当な塗布方法により塗布、乾燥し、レジスト膜を形成する。なお、予め公知の反射防止膜を塗設することもできる。また、トップコート層の形成前にレジスト膜を乾燥することが好ましい。
　次いで、得られたレジスト膜上に、上記レジスト膜の形成方法と同様の手段によりトップコート組成物を塗布、乾燥し、トップコート層を形成することができる。
　トップコート層を上層に有するレジスト膜に、通常はマスクを通して、電子線（ＥＢ）、Ｘ線又はＥＵＶ光を照射し、好ましくはベーク（加熱）を行い、現像する。これにより良好なパターンを得ることができる。
　界面活性剤（Ｆ）
　本発明において用いられる感活性光線性又は感放射線性組成物は、界面活性剤（Ｆ）を更に含んでいてもよい。界面活性剤を含有することにより、波長が２５０ｎｍ以下、特には２２０ｎｍ以下の露光光源を使用した場合に、良好な感度及び解像度で、密着性及び現像欠陥のより少ないパターンを形成することが可能となる。
　界面活性剤としては、フッ素系及び／又はシリコン系界面活性剤を用いることが特に好ましい。
　フッ素系及び／又はシリコン系界面活性剤としては、例えば、米国特許出願公開第２００８／０２４８４２５号明細書の［０２７６］に記載の界面活性剤が挙げられる。また、エフトップＥＦ３０１若しくはＥＦ３０３（新秋田化成（株）製）；フロラードＦＣ４３０、４３１若しくは４４３０（住友スリーエム（株）製）；メガファックＦ１７１、Ｆ１７３、Ｆ１７６、Ｆ１８９、Ｆ１１３、Ｆ１１０、Ｆ１７７、Ｆ１２０若しくはＲ０８（ＤＩＣ（株）製）；サーフロンＳ－３８２、ＳＣ１０１、１０２、１０３、１０４、１０５若しくは１０６（旭硝子（株）製）；トロイゾルＳ－３６６（トロイケミカル（株）製）；ＧＦ－３００若しくはＧＦ－１５０（東亜合成化学（株）製）、サーフロンＳ－３９３（セイミケミカル（株）製）；エフトップＥＦ１２１、ＥＦ１２２Ａ、ＥＦ１２２Ｂ、ＲＦ１２２Ｃ、ＥＦ１２５Ｍ、ＥＦ１３５Ｍ、ＥＦ３５１、ＥＦ３５２、ＥＦ８０１、ＥＦ８０２若しくはＥＦ６０１（（株）ジェムコ製）；ＰＦ６３６、ＰＦ６５６、ＰＦ６３２０若しくはＰＦ６５２０（ＯＭＮＯＶＡ社製）；又は、ＦＴＸ－２０４Ｇ、２０８Ｇ、２１８Ｇ、２３０Ｇ、２０４Ｄ、２０８Ｄ、２１２Ｄ、２１８Ｄ若しくは２２２Ｄ（（株）ネオス製）を用いてもよい。なお、ポリシロキサンポリマーＫＰ－３４１（信越化学工業（株）製）も、シリコン系界面活性剤として用いることができる。
　また、界面活性剤は、上記に示すような公知のものの他に、テロメリゼーション法（テロマー法ともいわれる）又はオリゴメリゼーション法（オリゴマー法ともいわれる）により製造されたフルオロ脂肪族化合物を用いて合成してもよい。具体的には、このフルオロ脂肪族化合物から導かれたフルオロ脂肪族基を備えた重合体を、界面活性剤として用いてもよい。このフルオロ脂肪族化合物は、例えば、特開２００２－９０９９１号公報に記載された方法によって合成することができる。
　また、米国特許出願公開第２００８／０２４８４２５号明細書の［０２８０］に記載されているフッ素系及び／又はシリコン系以外の界面活性剤を使用してもよい。
　これら界面活性剤は、１種類を単独で用いてもよく、２種類以上を組み合わせて用いてもよい。
　本発明において用いられる感活性光線性又は感放射線性組成物が界面活性剤を含んでいる場合、その含有量は、組成物の全固形分を基準として、好ましくは０～２質量％、より好ましくは０．０００１～２質量％、更に好ましくは０．０００５～１質量％である。
　その他の添加剤（Ｇ）
　本発明において用いられる感活性光線性又は感放射線性組成物は、溶解阻止化合物、染料、可塑剤、光増感剤、光吸収剤、及び／又は現像液に対する溶解性を促進させる化合物（例えば、分子量１０００以下のフェノール化合物、又はカルボキシ基を含んだ脂環族若しくは脂肪族化合物）を更に含んでいてもよい。
　本発明において用いられる感活性光線性又は感放射線性組成物は、溶解阻止化合物を更に含んでいてもよい。ここで「溶解阻止化合物」とは、酸の作用により分解して有機系現像液中での溶解度が減少する、分子量３０００以下の化合物である。
　本発明のリンス液は、非化学増幅系のレジスト組成物にも好適に適用することができる。
　非化学増幅系のレジスト組成物としては、例えば、
　ｇ線、ｈ線、ｉ線、ＫｒＦ、ＡｒＦ、ＥＢあるいはＥＵＶ等の照射によって主鎖が切断し、分子量が低下することにより溶解性が変化するレジスト材料（例えば特開２０１３－２１０４１１号公報［００２５］～［００２９］、［００５６］や米国特許公報２０１５／０００８２１１［００３２］～［００３６］、［００６３］に記載のα－クロロアクリル酸エステル系化合物とα－メチルスチレン系化合物との共重合体を主成分とするレジスト材料等） 
　ｇ線、ｈ線、ｉ線、ＫｒＦ、ＡｒＦ、ＥＢあるいはＥＵＶ等によって生じたシラノール縮合反応を伴うハイドロゲンシルセスオキサン（ＨＳＱ）、塩素置換したカリックスアレーン、
　ｇ線、ｈ線、ｉ線、ＫｒＦ、ＡｒＦ、ＥＢあるいはＥＵＶ等の光に対して吸収を有する金属錯体（マグネシウム、クロム、マンガン、鉄、コバルト、ニッケル、銅、亜鉛、銀、カドミウム、インジウム、錫、アンチモン、セシウム、ジルコニウム、ハフニウム等の錯体であり、チタン、ジルコニウム、ハフニウムがパターン形成性の観点から好ましい）を含み、配位子脱離や酸発生剤と併用して配位子交換過程を伴うレジスト材料（特開２０１５－０７５５００［００１７］～［００３３］、［００３７］～［００４７］、特開２０１２－１８５４８５［００１７］～［００３２］、［００４３］～［００４４］、米国特許公報２０１２／０２０８１２５［００４２］～［００５１］、［００６６］等に記載のレジスト材料）等が挙げられる。
　また、レジスト組成物としては、特開２００８－８３３８４号公報に記載の［００１０］～［００６２］、［０１２９］～［０１６５］に記載のレジスト組成物も用いることができる。
　本発明における感活性光線性又は感放射線性組成物、及び、本発明のパターン形成方法において使用される各種材料（例えば、レジスト溶剤、現像液、リンス液、反射防止膜形成用組成物、トップコート形成用組成物など）は、金属、ハロゲンを含む金属塩、酸、アルカリ等の不純物を含まないことが好ましい。これら材料に含まれる不純物の含有量としては、１ｐｐｍ以下が好ましく、１ｐｐｂ以下がより好ましく、１００ｐｐｔ以下が更に好ましく、１０ｐｐｔ以下が特に好ましく、実質的に含まないこと（測定装置の検出限界以下であること）が最も好ましい。
　各種材料から金属等の不純物を除去する方法としては、例えば、フィルターを用いた濾過を挙げることができる。フィルター孔径としては、ポアサイズ１０ｎｍ以下が好ましく、５ｎｍ以下がより好ましく、３ｎｍ以下が更に好ましい。フィルターの材質としては、ポリテトラフロロエチレン製、ポリエチレン製、ナイロン製のフィルターが好ましい。フィルターは、これらの材質とイオン交換メディアを組み合わせた複合材料であってもよい。フィルターは、有機溶剤であらかじめ洗浄したものを用いてもよい。フィルター濾過工程では、複数種類のフィルターを直列又は並列に接続して用いてもよい。複数種類のフィルターを使用する場合は、孔径及び／又は材質が異なるフィルターを組み合わせて使用しても良い。また、各種材料を複数回濾過してもよく、複数回濾過する工程が循環濾過工程であっても良い。
　また、各種材料に含まれる金属等の不純物を低減する方法としては、各種材料を構成する原料として金属含有量が少ない原料を選択する、各種材料を構成する原料に対してフィルター濾過を行う、装置内をテフロン（登録商標）でライニングする等してコンタミネーションを可能な限り抑制した条件下で蒸留を行う等の方法を挙げることができる。各種材料を構成する原料に対して行うフィルター濾過における好ましい条件は、上記した条件と同様である。
　フィルター濾過の他、吸着材による不純物の除去を行っても良く、フィルター濾過と吸着材を組み合わせて使用しても良い。吸着材としては、公知の吸着材を用いることができ、例えば、シリカゲル、ゼオライトなどの無機系吸着材、活性炭などの有機系吸着材を使用することができる。
　＜収容容器＞
　現像液及びリンス液に使用し得る有機溶剤（「有機系処理液」ともいう）としては、収容部を有する、化学増幅型又は非化学増幅型レジスト膜のパターニング用有機系処理液の収容容器に保存されたものを使用することが好ましい。この収容容器としては、例えば、収容部の、有機系処理液に接触する内壁が、ポリエチレン樹脂、ポリプロピレン樹脂、及び、ポリエチレン－ポリプロピレン樹脂のいずれとも異なる樹脂、又は、防錆・金属溶出防止処理が施された金属から形成された、レジスト膜のパターニング用有機系処理液の収容容器であることが好ましい。この収容容器の上記収容部に、レジスト膜のパターニング用有機系処理液として使用される予定の有機溶剤を収容し、レジスト膜のパターニング時において、上記収容部から排出したものを使用することができる。
　上記の収容容器が、更に、上記の収容部を密閉するためのシール部を有している場合、このシール部も、ポリエチレン樹脂、ポリプロピレン樹脂、及び、ポリエチレン－ポリプロピレン樹脂からなる群より選択される１種以上の樹脂とは異なる樹脂、又は、防錆・金属溶出防止処理が施された金属から形成されることが好ましい。
　ここで、シール部とは、収容部と外気とを遮断可能な部材を意味し、パッキンやＯリングなどを好適に挙げることができる。
　ポリエチレン樹脂、ポリプロピレン樹脂、及び、ポリエチレン－ポリプロピレン樹脂からなる群より選択される１種以上の樹脂とは異なる樹脂は、パーフルオロ樹脂であることが好ましい。
　パーフルオロ樹脂としては、四フッ化エチレン樹脂（ＰＴＦＥ）、四フッ化エチレン・パーフルオロアルキルビニルエーテル共重合体（ＰＦＡ）、四フッ化エチレン－六フッ化プロピレン共重合樹脂（ＦＥＰ）、四フッ化エチレン－エチレン共重合体樹脂（ＥＴＦＥ）、三フッ化塩化エチレン－エチレン共重合樹脂（ＥＣＴＦＥ）、フッ化ビニリデン樹脂（ＰＶＤＦ）、三フッ化塩化エチレン共重合樹脂（ＰＣＴＦＥ）、フッ化ビニル樹脂（ＰＶＦ）等を挙げることができる。
　特に好ましいパーフルオロ樹脂としては、四フッ化エチレン樹脂、四フッ化エチレン・パーフルオロアルキルビニルエーテル共重合体、四フッ化エチレン－六フッ化プロピレン共重合樹脂を挙げることができる。
　防錆・金属溶出防止処理が施された金属における金属としては、炭素鋼、合金鋼、ニッケルクロム鋼、ニッケルクロムモリブデン鋼、クロム鋼、クロムモリブデン鋼、マンガン鋼等を挙げることができる。
　防錆・金属溶出防止処理としては、皮膜技術を適用することが好ましい。
　皮膜技術には、金属被覆（各種メッキ），無機被覆（各種化成処理，ガラス，コンクリート，セラミックスなど）及び有機被覆（さび止め油，塗料，ゴム，プラスチックス）の３種に大別されている。
　好ましい皮膜技術としては、錆止め油、錆止め剤、腐食抑制剤、キレート化合物、可剥性プラスチック、ライニング剤による表面処理が挙げられる。
　中でも、各種のクロム酸塩、亜硝酸塩、ケイ酸塩、燐酸塩、オレイン酸、ダイマー酸、ナフテン酸等のカルボン酸、カルボン酸金属石鹸、スルホン酸塩、アミン塩、エステル（高級脂肪酸のグリセリンエステルや燐酸エステル）などの腐食抑制剤、エチレンジアンテトラ酢酸、グルコン酸、ニトリロトリ酢酸、ヒドロキシエチルエチオレンジアミン三作酸、ジエチレントリアミン五作酸などのキレート化合物及びフッ素樹脂ライニングが好ましい。特に好ましいのは、燐酸塩処理とフッ素樹脂ライニングである。
　また、直接的な被覆処理と比較して、直接、錆を防ぐわけではないが、被覆処理による防錆期間の延長につながる処理方法として、防錆処理にかかる前の段階である「前処理」を採用することも好ましい。
　このような前処理の具体例としては、金属表面に存在する塩化物や硫酸塩などの種々の腐食因子を、洗浄や研磨によって除去する処理を好適に挙げることができる。
　収容容器としては具体的に以下を挙げることができる。
　・Ｅｎｔｅｇｒｉｓ社製　ＦｌｕｏｒｏＰｕｒｅＰＦＡ複合ドラム（接液内面；ＰＦＡ樹脂ライニング）
　・ＪＦＥ社製　鋼製ドラム缶（接液内面；燐酸亜鉛皮膜）
　また、本発明において用いることができる収容容器としては、特開平１１－０２１３９３号公報［００１３］～［００３０］、及び特開平１０－４５９６１号公報［００１２］～［００２４］に記載の容器も挙げることができる。
　本発明の有機系処理液は、静電気の帯電、引き続き生じる静電気放電に伴う薬液配管や各種パーツ（フィルター、Ｏ－リング、チューブなど）の故障を防止する為、導電性の化合物を添加しても良い。導電性の化合物としては特に制限されないが、例えば、メタノールが挙げられる。添加良は特に制限されないが、好ましい現像特性を維持する観点で、１０質量％以下が好ましく、更に好ましくは、５質量％以下である。薬液配管の部材に関しては、ＳＵＳ（ステンレス鋼）、或いは帯電防止処理の施されたポリエチレン、ポリプロピレン、又はフッ素樹脂（ポリテトラフルオロエチレン、パーフロオロアルコキシ樹脂など）で被膜された各種配管を用いることができる。フィルターやＯ－リングに関しても同様に、帯電防止処理の施されたポリエチレン、ポリプロピレン、又はフッ素樹脂（ポリテトラフルオロエチレン、パーフロオロアルコキシ樹脂など）を用いることができる。
　なお、一般的に、現像液及びリンス液は、使用後に配管を通して廃液タンクに収容される。その際、リンス液として炭化水素系溶媒を使用すると、現像液中に溶解したレジストが析出し、ウエハ背面や、配管側面などに付着することを防ぐために、再度、レジストが溶解する溶媒を配管に通す方法がある。配管に通す方法としては、リンス液での洗浄後に基板の背面や側面などをレジストが溶解する溶媒で洗浄して流す方法や、レジストに接触させずにレジストが溶解する溶剤を配管を通るように流す方法が挙げられる。
　配管に通す溶剤としては、レジストを溶解し得るものであれば特に限定されず、例えば上述した有機溶媒が挙げられ、プロピレングリコールモノメチルエーテルアセテート（ＰＧＭＥＡ）、プロピレングリコールモノエチルエーテルアセテート、プロピレングリコールモノプロピルエーテルアセテート、プロピレングリコールモノブチルエーテルアセテート、プロピレングリコールモノメチルエーテルプロピオネート、プロピレングリコールモノエチルエーテルプロピオネート、エチレングリコールモノメチルエーテルアセテート、エチレングリコールモノエチルエーテルアセテート、プロピレングリコールモノメチルエーテル（ＰＧＭＥ）、プロピレングリコールモノエチルエーテル、プロピレングリコールモノプロピルエーテル、プロピレングリコールモノブチルエーテル、エチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、２－ヘプタノン、乳酸エチル、１－プロパノール、アセトン、等を用いることができる。中でも好ましくは、ＰＧＭＥＡ，ＰＧＭＥ，シクロヘキサノンを用いることができる。
　本発明のパターン形成方法により得られるパターンをマスクとして用い、適宜エッチング処理及びイオン注入などを行い、半導体微細回路、インプリント用モールド構造体、フォトマスク等を製造することができる。
　上記の方法によって形成されたパターンは、ＤＳＡ（Ｄｉｒｅｃｔｅｄ　Ｓｅｌｆ-Ａｓｓｅｍｂｌｙ）におけるガイドパターン形成（例えば、ＡＣＳ　Ｎａｎｏ　Ｖｏｌ．４　Ｎｏ．８　Ｐａｇｅ４８１５-４８２３参照）にも用いることができる。また、上記の方法によって形成されたパターンは、例えば特開平３－２７０２２７及び特開２０１３－１６４５０９号公報に開示されたスペーサープロセスの芯材（コア）として使用できる。
　なお、本発明の組成物を用いてインプリント用モールドを作成する場合のプロセスについては、例えば、特許第４１０９０８５号公報、特開２００８－１６２１０１号公報、及び「ナノインプリントの基礎と技術開発・応用展開―ナノインプリントの基板技術と最新の技術展開―編集：平井義彦（フロンティア出版）」に記載されている。
　本発明のパターン形成方法を用いて製造されるフォトマスクは、ＡｒＦエキシマレーザー等で用いられる光透過型マスクであっても、ＥＵＶ光を光源とする反射系リソグラフィーで用いられる光反射型マスクであってもよい。
　また、本発明は、上記した本発明のパターン形成方法を含む、電子デバイスの製造方法にも関する。
　本発明の電子デバイスの製造方法により製造される電子デバイスは、電気電子機器（家電、ＯＡ（Ｏｆｆｉｃｅ　Ａｐｐｌｉａｎｃｅ）・メディア関連機器、光学用機器及び通信機器等）に、好適に、搭載されるものである。
　以下、本発明を実施例により更に具体的に説明するが、本発明はその主旨を越えない限り、以下の実施例に限定されるものではない。なお、特に断りのない限り、「部」、「％」は質量基準である。
　＜樹脂（Ａ）＞
（合成例１）樹脂（Ａ－１）の合成
　２Ｌフラスコにシクロヘキサノン６００ｇを入れ、１００ｍＬ／ｍｉｎの流量で一時間窒素置換した。その後、重合開始剤Ｖ－６０１（和光純薬工業（株）製）４．６０ｇ（０．０２ｍｏｌ）を加え、内温が８０℃になるまで昇温した。次に、以下のモノマーと重合開始剤Ｖ－６０１（和光純薬工業（株）製）４．６０ｇ（０．０２ｍｏｌ）とを、シクロヘキサノン２００ｇに溶解し、モノマー溶液を調製した。モノマー溶液を上記８０℃に加熱したフラスコ中に６時間かけて滴下した。滴下終了後、更に８０℃で２時間反応させた。
　４－アセトキシスチレン　　　　　　　　　４８．６６ｇ（０．３ｍｏｌ）
　１－エチルシクロペンチルメタクリレート　１０９．４ｇ（０．６ｍｏｌ）
　モノマー１　　　　　　　　　　　　　　　２２．２ｇ（０．１ｍｏｌ）
Figure JPOXMLDOC01-appb-C000040
　反応溶液を室温まで冷却し、ヘキサン３Ｌ中に滴下しポリマーを沈殿させた。ろ過した固体をアセトン５００ｍＬに溶解し、再度ヘキサン３Ｌ中に滴下、ろ過した固体を減圧乾燥して、４－アセトキシスチレン／１－エチルシクロペンチルメタクリレート／モノマー１共重合体（Ａ－１ａ）１６０ｇを得た。
　反応容器中に上記で得られた重合体１０ｇ、メタノール４０ｍＬ、１－メトキシ－２－プロパノール２００ｍＬ、及び、濃塩酸１．５ｍＬを加え、８０℃に加熱して５時間攪拌した。反応溶液を室温まで放冷し、蒸留水３Ｌ中に滴下した。ろ過した固体をアセトン２００ｍＬに溶解し、再度蒸留水３Ｌ中に滴下、ろ過した固体を減圧乾燥して樹脂（Ａ－１）（８．５ｇ）を得た。ＧＰＣによる重量平均分子量は１０８００、分子量分散度（Ｍｗ／Ｍｎ）は１．５５であった。
　用いるモノマーを変更した以外は、上記合成例１と同様の方法で、下記表１に示す構造を有する樹脂（Ａ－２）～（Ａ－４）を合成した。樹脂の組成比（モル比）は、１Ｈ－ＮＭＲ測定により算出した。樹脂の重量平均分子量（Ｍｗ：ポリスチレン換算）、分散度（Ｍｗ／Ｍｎ）はＧＰＣ（溶媒：ＴＨＦ）測定により算出した。
Figure JPOXMLDOC01-appb-T000041
　用いるモノマーを変更した以外は、上記合成例１と同様の方法で、下記表２に示す構造を有する樹脂（Ａ－５）～（Ａ－７）を合成した。樹脂の組成比（モル比）は、１Ｈ－ＮＭＲ測定により算出した。樹脂の重量平均分子量（Ｍｗ：ポリスチレン換算）、分散度（Ｍｗ／Ｍｎ）はＧＰＣ（溶媒：ＴＨＦ）測定により算出した。
Figure JPOXMLDOC01-appb-T000042
　＜酸発生剤（Ｂ）＞
　酸発生剤としては、以下のものを用いた。
Figure JPOXMLDOC01-appb-C000043
　＜塩基性化合物（Ｅ）＞
　塩基性化合物としては、以下のものを用いた。
Figure JPOXMLDOC01-appb-C000044
Figure JPOXMLDOC01-appb-C000045
　＜溶剤（Ｃ）＞
　溶剤としては、以下のものを用いた。
　Ｃ－１：プロピレングリコールモノメチルエーテルアセテート
　Ｃ－２：プロピレングリコール
　Ｃ－３：乳酸エチル
　Ｃ－４：シクロヘキサノン
　＜レジスト組成物＞
　下記表３に示す各成分を、同表に示す溶剤に溶解させた。これを０．０３μｍのポアサイズを有するポリエチレンフィルターを用いてろ過して、レジスト組成物を得た。
Figure JPOXMLDOC01-appb-T000046
　＜ＥＵＶ露光評価＞
　表３に記載のレジスト組成物を用いて、以下の操作によりレジストパターンを形成した。
　〔レジスト組成物の塗布及び塗布後ベーク（ＰＢ）〕
　ＨＭＤＳ（ヘキサメチルジシラザン）処理を行った４インチシリコンウエハ上に、上記のようにして得られた各レジスト組成物を塗布し、表６に示す温度の条件で６０秒間ベークし、膜厚４０ｎｍのレジスト膜を形成した。
　１インチは２５．４ｍｍである。
　〔露光〕
　上記で作成したウエハに、ＮＡ（レンズ開口数、Ｎｕｍｅｒｉｃａｌ　Ａｐｅｒｔｕｒｅ）０．３、ダイポール照明でＥＵＶ露光を行った。具体的には、線幅１５～２０ｎｍの１：１ラインアンドスペースパターンを形成する為のパターンが含まれたマスクを介して、露光量を変えてＥＵＶ露光を行った。
　〔露光後ベーク（ＰＥＢ）〕
　照射後、ＥＵＶ露光装置から取り出したら、ただちに、表６に示す温度の条件で６０秒間ベークした。
　〔現像〕
　その後、シャワー型現像装置（ＡＣＴＥＳ（株）製ＡＤＥ３０００Ｓ）を用いて、５０回転（ｒｐｍ）でウエハを回転しながら表４に記載の現像液（２３℃）を、２００ｍＬ／分の流量で、所定時間スプレー吐出して現像を行った。
　Ｓ－９の酢酸ブチルと酢酸イソペンチルの含有比は、質量比である。
Figure JPOXMLDOC01-appb-T000047
　〔リンス〕
　その後、５０回転（ｒｐｍ）でウエハを回転しながら表５に記載のリンス液（２３℃）を、２００ｍＬ／分の流量で、所定時間スプレー吐出してリンス処理を行った。
　最後に、２５００回転（ｒｐｍ）で１２０秒間高速回転してウエハを乾燥させた。
　Ｒ－６のイソデカンとイソドデカンの含有比は、質量比である。
Figure JPOXMLDOC01-appb-T000048
　〔評価試験〕
　以下の項目について、レジストパターンの評価を行った。結果は表６に示す。
Figure JPOXMLDOC01-appb-T000049
　（パターン倒れ性能）
　２０ｎｍの線幅において、ラインとスペースとの比率が１：１で分離解像する照射エネルギーにて露光を行った。
　得られたレジストパターンを、走査型電子顕微鏡（（株）日立製作所製Ｓ－９３８０ＩＩ）を用いて観察した。倍率は２０万倍とした。
　上記の方法にて得られた線幅２０ｎｍの解像状況を、走査型電子顕微鏡によって観察して、パターン倒れの個数を求めた。観察箇所を１μｍずつずらしながら、１０００枚の写真撮影を行い、写真１視野中にパターン倒れが観察されたものをＮＧ，観察されなかったものをＯＫとし、カウントした。ＮＧの数により、以下のＡ～Ｄに分類した。ＮＧが少ないほど、パターン倒れ性能が良好であることを示す。
　Ａ：０個
　Ｂ：１～１０個
　Ｃ：１１～１００個
　Ｄ：１０１～１０００個
　（ブリッジ性能）
　２０ｎｍの線幅において、ラインとスペースとの比率が１：１で分離解像する照射エネルギーにて露光を行った。
　得られたレジストパターンを、走査型電子顕微鏡（（株）日立製作所製Ｓ－９３８０ＩＩ）を用いて観察した。倍率は２０万倍とした。
　上記の方法にて得られた線幅２０ｎｍの解像状況を、走査型電子顕微鏡によって観察して、ブリッジの個数を求めた。観察箇所を１μｍずつずらしながら、１０００枚の写真撮影を行い、写真１視野中にブリッジが観察されたものをＮＧ，観察されなかったものをＯＫとし、カウントした。ＮＧの数により、以下のＡ～Ｄに分類した。ＮＧが少ないほど、ブリッジ性能が良好であることを示す。
　Ａ：０個
　Ｂ：１～１０個
　Ｃ：１１～１００個
　Ｄ：１０１～１０００個
　＜ＥＢ露光評価＞
　上記表３に記載のレジスト組成物を用いて、以下の操作によりレジストパターンを形成した。
　〔レジスト組成物の塗布及び塗布後ベーク（ＰＢ）〕
　６インチシリコンウエハ上に有機膜ＤＵＶ４４（Ｂｒｅｗｅｒ　Ｓｃｉｅｎｃｅ社製）を塗布し、２００℃で６０秒間ベークして、膜厚６０ｎｍの有機膜を形成した。その上に表３に記載のレジスト組成物を塗布し、表７に示す温度で６０秒間ベークし、膜厚４０ｎｍのレジスト膜を形成した。
　〔露光〕
　上記で作製したウエハに、電子線照射装置（（株）ＪＥＯＬ製　ＪＢＸ６０００ＦＳ／Ｅ；加速電圧５０ｋｅＶ）を用いて、１．２５ｎｍ刻みで線幅２０ｎｍ～１７．５ｎｍの１：１ラインアンドスペースパターン（長さ方向０．１２ｍｍ、描画本数２０本）を、露光量を変えて露光した。
　〔露光後ベーク（ＰＥＢ）〕
　照射後、電子線照射装置から取り出したら、ただちに、表７に示す温度で６０秒の条件でホットプレート上にて加熱した。
　〔現像〕
　シャワー型現像装置（ＡＣＴＥＳ（株）製ＡＤＥ３０００Ｓ）を用いて、５０回転（ｒｐｍ）でウエハを回転しながら上記表４に記載の現像液（２３℃）を、２００ｍＬ／分の流量で、所定時間スプレー吐出して現像を行った。
　〔リンス〕
　その後、５０回転（ｒｐｍ）でウエハを回転しながら上記表５に記載のリンス液（２３℃）を、２００ｍＬ／分の流量で、所定時間スプレー吐出してリンス処理を行った。
　最後に、２５００回転（ｒｐｍ）で１２０秒間高速回転してウエハを乾燥させた。
　上述した「ＥＵＶ露光評価」と同様の方法でレジストパターンの評価を行った。結果は表７に示す。
Figure JPOXMLDOC01-appb-T000050
　上記表６及び表７に示す通り、いずれの露光光源を用いても、リンス液として、分岐鎖状脂肪族炭化水素系溶剤を含むリンス液を用いることで、パターン倒れ性能及びブリッジ性能の何れも非常に良好であることが分かった。
　本発明によれば、高精度（例えば、線幅２０ｎｍ以下）の微細パターンにおける、パターン倒れ性能とブリッジ性能を非常に高い次元で両立するためにレジスト膜に用いられるリンス液、このリンス液を用いるパターン形成方法、及びこのパターン形成方法を含む電子デバイスの製造方法を提供することができる。
　本発明を詳細にまた特定の実施態様を参照して説明したが、本発明の精神と範囲を逸脱することなく様々な変更や修正を加えることができることは当業者にとって明らかである。
　本出願は、２０１５年６月２３日出願の日本特許出願（特願２０１５－１２５６２２）に基づくものであり、その内容はここに参照として取り込まれる。
 

Claims (9)

  1. 　感活性光線性又は感放射線性組成物から得られるレジスト膜に用いられるリンス液であって、分岐アルキル基を有する炭化水素系溶剤を含むリンス液。
  2. 　前記分岐アルキル基を有する炭化水素系溶剤の炭素原子数が１０以上である、請求項１に記載のリンス液。
  3. 　前記分岐アルキル基を有する炭化水素系溶剤が、イソデカン及びイソドデカンの少なくとも１種を含む、請求項１又は２に記載のリンス液。
  4. 　感活性光線性又は感放射線性組成物を用いてレジスト膜を形成するレジスト膜形成工程と、
    　前記レジスト膜を露光する露光工程と、
    　露光された前記レジスト膜を有機溶剤を含む現像液を用いて現像する工程と、
    　前記現像されたレジスト膜を請求項１～３のいずれか１項に記載のリンス液を用いてリンスする工程と、をこの順で有する、パターン形成方法。
  5. 　前記現像液に含まれる有機溶剤がエステル系溶剤である、請求項４に記載のパターン形成方法。
  6. 　前記現像液に含まれる有機溶剤が、酢酸ブチル、酢酸ペンチル、及び酢酸イソアミルからなる群より選ばれる１種以上を含む、請求項４又は５に記載のパターン形成方法。
  7. 　前記感活性光線性又は感放射線性組成物が、下記一般式（１）で表される繰り返し単位を含有する樹脂を含有する、請求項４～６のいずれか１項に記載のパターン形成方法。
    Figure JPOXMLDOC01-appb-C000001
    　一般式（１）中、
    　Ａは水素原子、アルキル基、シクロアルキル基、ハロゲン原子、又はシアノ基を表す。
    　Ｒは、ハロゲン原子、アルキル基、シクロアルキル基、アリール基、アルケニル基、アラルキル基、アルコキシ基、アルキルカルボニルオキシ基、アルキルスルホニルオキシ基、アルキルオキシカルボニル基又はアリールオキシカルボニル基を表し、複数個ある場合には同じであっても異なっていてもよい。複数のＲを有する場合には、互いに共同して環を形成していてもよい。
    　ａは１～３の整数を表す。
    　ｂは０～（３－ａ）の整数を表す。
  8. 　前記露光が、電子線又は極紫外線を用いて行われる、請求項４～７のいずれか１項に記載のパターン形成方法。
  9. 　請求項４～８のいずれか１項に記載のパターン形成方法を含む、電子デバイスの製造方法。
PCT/JP2016/065353 2015-06-23 2016-05-24 リンス液、パターン形成方法、及び電子デバイスの製造方法 WO2016208312A1 (ja)