WO2016121875A1 - Film protecteur de surface optique ayant un séparateur - Google Patents

Film protecteur de surface optique ayant un séparateur Download PDF

Info

Publication number
WO2016121875A1
WO2016121875A1 PCT/JP2016/052501 JP2016052501W WO2016121875A1 WO 2016121875 A1 WO2016121875 A1 WO 2016121875A1 JP 2016052501 W JP2016052501 W JP 2016052501W WO 2016121875 A1 WO2016121875 A1 WO 2016121875A1
Authority
WO
WIPO (PCT)
Prior art keywords
separator
meth
protective film
surface protective
sensitive adhesive
Prior art date
Application number
PCT/JP2016/052501
Other languages
English (en)
Japanese (ja)
Inventor
数馬 三井
崇弘 野中
林　圭治
Original Assignee
日東電工株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from JP2016012609A external-priority patent/JP6804843B2/ja
Application filed by 日東電工株式会社 filed Critical 日東電工株式会社
Priority to CN201680005154.7A priority Critical patent/CN107107597B/zh
Priority to KR1020177020419A priority patent/KR102428190B1/ko
Publication of WO2016121875A1 publication Critical patent/WO2016121875A1/fr

Abstract

L'invention concerne un film protecteur de surface optique ayant un séparateur et comprenant : un film de polyester sur une surface d'une couche adhésive ; le séparateur sur la surface opposée au film de polyester de la couche adhésive ; une force de rayons X Si-K alpha dans un rayon X fluorescent de la surface de la couche adhésive après décollage du séparateur étant de 2,5 kcps au plus ; une force de décollage du séparateur par rapport au film protecteur de surface optique étant de 0,5 N/50 mm au plus à une vitesse de tension de 0,3 m/minute. Le film de protection de surface optique ayant le séparateur peut empêcher le phénomène de décollage facile d'autres couches disposées sur la surface de la partie à coller, telles qu'un (une couche de) remplissage entre couches, après le décollage du film protecteur de surface de la partie à coller.
PCT/JP2016/052501 2015-01-30 2016-01-28 Film protecteur de surface optique ayant un séparateur WO2016121875A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
CN201680005154.7A CN107107597B (zh) 2015-01-30 2016-01-28 带间隔件的光学用表面保护膜
KR1020177020419A KR102428190B1 (ko) 2015-01-30 2016-01-28 세퍼레이터 부착형 광학용 표면 보호 필름

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2015016368 2015-01-30
JP2015-016368 2015-01-30
JP2016012609A JP6804843B2 (ja) 2015-01-30 2016-01-26 セパレータ付き光学用表面保護フィルム
JP2016-012609 2016-01-26

Publications (1)

Publication Number Publication Date
WO2016121875A1 true WO2016121875A1 (fr) 2016-08-04

Family

ID=56543480

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/052501 WO2016121875A1 (fr) 2015-01-30 2016-01-28 Film protecteur de surface optique ayant un séparateur

Country Status (1)

Country Link
WO (1) WO2016121875A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2020122048A (ja) * 2019-01-29 2020-08-13 大日精化工業株式会社 接着剤組成物及び積層体

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0732551A (ja) * 1993-07-21 1995-02-03 Dainippon Printing Co Ltd 剥離シート
JP2003240951A (ja) * 2002-02-15 2003-08-27 Oji Paper Co Ltd 偏光板保護用透明粘着フィルム
JP2010155976A (ja) * 2008-12-03 2010-07-15 Sumitomo Chemical Co Ltd 表面保護フィルム
JP2013227472A (ja) * 2011-07-12 2013-11-07 Mitsubishi Chemicals Corp 樹脂組成物及び離型フィルム
JP2014001332A (ja) * 2012-06-20 2014-01-09 Fujimori Kogyo Co Ltd 粘着剤組成物及び表面保護フィルム

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH0732551A (ja) * 1993-07-21 1995-02-03 Dainippon Printing Co Ltd 剥離シート
JP2003240951A (ja) * 2002-02-15 2003-08-27 Oji Paper Co Ltd 偏光板保護用透明粘着フィルム
JP2010155976A (ja) * 2008-12-03 2010-07-15 Sumitomo Chemical Co Ltd 表面保護フィルム
JP2013227472A (ja) * 2011-07-12 2013-11-07 Mitsubishi Chemicals Corp 樹脂組成物及び離型フィルム
JP2014001332A (ja) * 2012-06-20 2014-01-09 Fujimori Kogyo Co Ltd 粘着剤組成物及び表面保護フィルム

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2020122048A (ja) * 2019-01-29 2020-08-13 大日精化工業株式会社 接着剤組成物及び積層体

Similar Documents

Publication Publication Date Title
JP6804843B2 (ja) セパレータ付き光学用表面保護フィルム
JP6856394B2 (ja) 粘着剤組成物、粘着剤層、表面保護フィルム、及び、光学部材
KR20120137288A (ko) 박층 기재용 캐리어재
JP6546806B2 (ja) セパレータ付き光学用表面保護フィルム
JP2015212362A (ja) 粘着シート、及び、光学部材
KR102158128B1 (ko) 편광판용 표면 보호 필름, 편광판 및 편광판의 제조 방법
WO2018123694A1 (fr) Film de protection de surface
JP6898732B2 (ja) 粘着剤組成物、粘着シート、及び、光学部材
JP6931534B2 (ja) 表面保護フィルム、及び、光学部材
JP7010846B2 (ja) 表面保護フィルム
WO2016121875A1 (fr) Film protecteur de surface optique ayant un séparateur
JP6594636B2 (ja) 粘着シート、及び、光学部材
JP2019137831A (ja) 粘着シート、光学部材、及び、表示装置
JP2016011363A (ja) 粘着剤組成物、粘着シート、及び、光学部材
JP6692968B2 (ja) セパレータ付き光学用表面保護フィルム
JP2018106137A (ja) 表面保護フィルム付偏光フィルム、及び、表面保護フィルム付光学部材
KR102544536B1 (ko) 점착제 조성물, 점착 시트 및 광학 부재
WO2018123693A1 (fr) Film protecteur de surface
WO2019155939A1 (fr) Feuille adhésive, élément optique et dispositif d'affichage

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16743478

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20177020419

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase