Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F2/00—Processes of polymerisation
  • C08F2/38—Polymerisation using regulators, e.g. chain terminating agents, e.g. telomerisation
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F10/00—Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F210/00—Copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
  • C08F210/14—Monomers containing five or more carbon atoms
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F210/00—Copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
  • C08F210/16—Copolymers of ethene with alpha-alkenes, e.g. EP rubbers
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F4/00—Polymerisation catalysts
  • C08F4/42—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors
  • C08F4/44—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides
  • C08F4/60—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with refractory metals, iron group metals, platinum group metals, manganese, rhenium technetium or compounds thereof
  • C08F4/62—Refractory metals or compounds thereof
  • C08F4/64—Titanium, zirconium, hafnium or compounds thereof
  • C08F4/659—Component covered by group C08F4/64 containing a transition metal-carbon bond
  • C08F4/6592—Component covered by group C08F4/64 containing a transition metal-carbon bond containing at least one cyclopentadienyl ring, condensed or not, e.g. an indenyl or a fluorenyl ring
  • C08F4/65922—Component covered by group C08F4/64 containing a transition metal-carbon bond containing at least one cyclopentadienyl ring, condensed or not, e.g. an indenyl or a fluorenyl ring containing at least two cyclopentadienyl rings, fused or not
  • C08F4/65927—Component covered by group C08F4/64 containing a transition metal-carbon bond containing at least one cyclopentadienyl ring, condensed or not, e.g. an indenyl or a fluorenyl ring containing at least two cyclopentadienyl rings, fused or not two cyclopentadienyl rings being mutually bridged
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F2500/00—Characteristics or properties of obtained polyolefins; Use thereof
  • C08F2500/09—Long chain branches

Definitions

• the present invention relates to a process for the preparation of a branched polyolefins via the polymerization of an olefin monomer and an alpha-olefin containing main group metal, preferably aluminum, hydrocarbyl chain transfer agent.
• the invention relates furthermore to a process for the preparation of branched polyolefins having end-functionalized branches.
• the invention moreover relates to branched polyolefins obtained by said process.
• the present invention relates to the preparation of a branched polyolefins, the intermediate products and the processes to obtain these products.
• linear polyolefins have many desirable physical properties, they show a variety of melt processing shortcomings, especially the metallocene prepared ones having narrow molecular weight distributions, which typically have a low melt strength. Low melt strength is a problem because it causes local thinning in melt thermoforming, relative weakness in large-part blow molding and flow instabilities in co-extrusion of laminates.
• branching viz. the provision of polymer side chains extending from the polyolefin backbone.
• polyolefins such as polyethylene and polypropylene are not appropriate for several applications as a consequence of their inherently nonpolar character.
• This nonpolar character is the reason for the poor adhesion, printability and compatibility that can restrict their efficacy.
• This invention is directed towards an improved process for the preparation of branched polyolefins and branched polyolefins having end functionalized branches.
• One or more of these aims are obtained by the catalyst system according to the present invention.
• the present invention relates to the novel and inventive process using chain transfer to prepare a main group metal, preferably aluminum, -terminated hydrocarbyl chain growth product and a subsequent quenching reaction to provide branched polyolefins.
• the present invention relates to both the novel and inventive process and to the products thus obtained.
• the present invention relates to a process for the preparation of a branched polyolefin, comprising the steps of:
• A) a polymerization step comprising copolymerizing at least one first type of olefin monomer and at least one second type of olefin monomer containing a main group metal hydrocarbyl chain transfer agent functionality according to Formula 1 a: R 100 ( n - 2)R 101 M n+ R 102 using a catalyst system to obtain a polyolefin having one or multiple main group metal end-functionalized branches; wherein said catalyst system comprises:
• a metal catalyst or catalyst precursor comprising a metal from Group 3- 10 of the lUPAC Periodic Table of elements
• R 100 , R 101 and R 102 of Formula 1 a are each independently selected from the group consisting of a hydride, a C1 -C18 hydrocarbyl group, or a hydrocarbyl group Q on the proviso that at least one of R 100 , R 101 and R 102 is a hydrocarbyl group Q, wherein hydrocarbyl group Q is according to Formula 1 b:
• Z is bonded to M and Z is a C1 -C18 hydrocarbyl group;
• R 105 optionally forms a cyclic group with Z; wherein R 103 and R 104 and R 105 are each independently selected from hydrogen or a hydrocarbyl group;
• step B) contacting said main group metal hydrocarbyt functionalized branched growth product obtained in step A) with a quenching agent to obtain a branched polyolefin.
• the chain transfer agent functionality can also be a chain shuttling agent functionality.
• the quenching agent used in step B) is a protic reagent resulting in hydrolysis and formation of the branched polyolefin.
• R 100 , R 101 and R 102 are hydrocarbyl group Q or wherein R 100 is a C2-C4 hydrocarbyl group and R 101 and R 102 are hydrocarbyl group Q or wherein R 100 and R 101 are a C2-C4 hydrocarbyl group and R 102 is hydrocarbyl group Q, preferably R 100 and R 101 are a C2-C4 hydrocarbyl group and R 102 is hydrocarbyl group Q, preferably the C2-C4 hydrocarbyl group is a branched or unbranched C4 hydrocarbyl, preferably branched, preferably isobutyl.
• the hydrocarbyl group Q according to Formula 1 b is a linear a- olefin group or a cyclic unsaturated hydrocarbyl group, preferably oct-7-en-1 -yl, 5- alkylenebicyclo[2.2.1 ]hept-2-ene or 5-alkylene-2-norbornene.
• an olefin monomer comprising a main group metal hydrocarbyl chain transfer agent can be selected from the group consisting of bis(isobutyl)(5- ethylen-yl-2-norbornene) aluminum, di(isobutyl)(7-octen-1 -yl) aluminum, di(isobutyl)(5-hexen-1 -yl) aluminum, di(isobutyl)(3-buten-1 -yl) aluminum, tris(5- ethylen-yl-2-norbornene) aluminum, tris(7-octen-1 -yl) aluminum, tris(5-hexen-1 -yl) aluminum, or tris(3-buten-1 -yl) aluminum, ethyl(5-ethylen-yl-2-norbornene) zinc, ethyl(7-octen-1 -yl) zinc, ethyl(5-
• a cyclic unsaturated hydrocarbyl group can thereby lead for example to a high reactivity.
• the co-catalyst is selected from the group consisting of MAO, DMAO, MMAO, SMAO and fluorinated aryl borane or fluorinated aryl borate.
• the metal catalyst or metal catalyst precursor used in step A) comprises a metal from Group 3-8 of the lUPAC Periodic Table of elements, more preferably from Group 3-6 and/or wherein the metal catalyst or metal catalyst precursor used in step A) comprises a metal selected from the group consisting of Ti, Zr, Hf, V, Cr, Fe, Co, Ni, Pd, preferably Ti, Zr or Hf.
• said metal catalyst is a Group 4 single-site catalyst, which can be a metallocene or a post-metallocene.
• said catalyst precursor is a C 3 -, Ci- or C2- symmetric zirconium metallocene, preferably an indenyl substituted zirconium dihalide, more preferably a bridged bis-indenyl zirconium dihalide, even more preferably rac-dimethyl silyl bis- indenyl zirconium dichloride (rac-Me 2 Si(lnd)2ZrCl2) or rac-dimethylsilyl bis-(2-methyl- 4-phenyl-indenyl) zirconium dichloride (rac-Me2Si(2-Me-4-Ph-lnd)2ZrCl2).
• said metal catalyst precursor is [Me2Si(C5Me4)N(tBu)]TiCl2.
• said metal catalyst precursor is [N-(2,6-di(l- methylethyl)phenyl)amido)(2-isopropylphenyl)(a-naphthalen-2-diyl(6-pyridin-2- diyl)methane)]hafnium dimethyl.
• the catalyst system used in step A) further comprises an additional main group metal hydrocarbyl chain transfer agent or main group metal hydrocarbyl chain shuttling agent, selected from the group consisting of hydrocarbyl aluminum, hydrocarbyl magnesium, hydrocarbyl zinc, hydrocarbyl gallium, hydrocarbyl boron, hydrocarbyl calcium, aluminum hydride, magnesium hydride, zinc hydride, gallium hydride, boron hydride, calcium hydride and a combination thereof.
• An additional main group metal hydrocarbyl chain transfer agent can also be a chain shuttling agent.
• the at least one olefin monomer used in step A) is selected from the group consisting of ethylene, propylene, 1 -butene, 4-methyl-1 -pentene, 1 -pentene, 1 -hexene, 1 -heptene, 1 -octene, 1 -nonene, 1 -decene, 1 -undecene, 1 -dodecene, 1 - tridecene, 1 -tetradecene, 1 -pentadecene, 1 -hexadecene, 1 -heptadecene, 1 - octadecene, 1 -cyclopentene, cyclopentene, cyclohexene, norbornene, ethylidene- norbornene, and vinylidene-norbornene and one or more combinations thereof.
• said metal catalyst is a group 4 single-site catalyst, which can be a metallocene or a post-metallocene.
• said catalyst precursor is a C 3 -, Ci- or C2- symmetric zirconium metallocene, preferably an indenyl substituted zirconium dihalide, more preferably a bridged bis-indenyl zirconium dihalide, even more preferably rac-dimethyl silyl bis- indenyl zirconium dichloride (rac-Me2Si(lnd)2ZrCl2) or rac-dimethylsilyl bis-(2-methyl- 4-phenyl-indenyl) zirconium dichloride (rac-Me2Si(2-Me-4Ph-lnd)2ZrCl2).
• said catalyst precursor is [N-(2,6-di(l-methylethyl)phenyl)amido )(2- isopropylphenyl)(a-naphthalen-2-diyl(6-pyridin-2-diyl)methane)]hafnium dimethyl.
• X is CI, Br, F or I ,
• X is O or S
• X is C, then Y is NR 2 or O
• the end-functionalized polyolefin has formula Pol-XYZ 1 R 1 (Formula ll-D), then:
• R 1 , R 2 , R 3 , R 4 , R 5 , R 6 are each independently selected from the group consisting of H, SiR 7 3 , SnR 7 3 or a C1 -C10 hydrocarbyl, preferably a C1 -C4 hydrocarbyl, where R 7 is selected from the group consisting of C1 -C10 hydrocarbyl, hydride, halide and silylhydrocarbyl.
• a quenching agent is used to remove the main group metal from the oxidized branch ends to obtain a branched polymer, preferably with polar functions at the chain ends.
• the quenching agent is a protic reagent.
• the protic agent is water or an alcohol or a mixture thereof, preferably water.
• said quenching agent is typically a halogen-containing agent releasing a metal-halide or an anhydride releasing a metal-carboxylate.
• Typical examples are alkyl halides and anhydrides.
• the main group metal(s) to be used according to the present invention can be selected for example from: lithium (Li), sodium (Na), potassium (K), beryllium (Be), magnesium (Mg), calcium (Ca), boron (B), aluminum (Al), gallium (Ga), indium (In), germanium (Ge), and tin (Sn), antimony (Sb), and bismuth (Bi) and/or zinc (Zn), preferably from lithium (Li), sodium (Na), potassium (K), beryllium (Be), magnesium (Mg), calcium (Ca), aluminum (Al), gallium (Ga), indium (In), germanium (Ge), and tin (Sn), antimony (Sb), and bismuth (Bi) and/or zinc (Zn) or further preferred from aluminum (Al) and/or zinc (Zn) and/or magnesium (Mg).
• the catalyst to main group metal mole ratio can be for example ⁇ 10, between 5 and 45, preferably between 15 and 35
• a branched polymer obtained according to the present invention can be especially for example a branched polymer with long chain branches (LCB) or a hyper branched polymer.
• LCB long chain branches
• chain-end-functionalized polyolefin or “end group-functionalized polyolefin” as used in the present description means: a polyolefin having a functional group on one or both of the ends of the polymer main chain.
• main chain as used in the present description means: the linear polymer chain to which all other chains may be regarded as being pendant. The main chain is preferably also the polymer chain starting from which other chains/side chains may be obtained. The main chain is thus obtained in step A).
• side chain or “branch” or “polymer branch” or “polymer side chain” as used in the present description means: an offshoot from a polymer main chain. These terms can be used interchangeably.
• This offshoot may be oligomer or polymeric and might be similar or different in nature compared to the polymer main chain.
• a "side chain” or “branch” or “polymer branches” or “polymer side chains” can thereby also be a random or block copolymer comprising at least two different monomers.
• “Side-chains” can be obtained starting from the main chain, especially starting from the monomers comprising an main group metal hydrocarbyl chain transfer agent functionality. “Side- chains” can thereby be obtained together with the main chain in step A).
• long chain branch as used in the present description means side chain with a length resembling the length of the main chain, that can mean that a long chain branch can have a length corresponding at least to 20 % of the length of the backbone in terms of monomer units and/or average molecular weight (Mn or Mw).
• a long chain branch can also preferably for example comprise > 100 carbon atoms in the backbone of the long chain branch. ).
• a long chain branch can also preferably for example long enough for entanglement phenomena, preferably involving the branch , to occur.
• each branch coming from the main chain of the polymer also comprises at least 1 , at least 2 and/or more branches.
• olefin monomer or “olefin” as used in the present description means: an a hydrocarbon compound having a carbon-carbon double bond that can be used serves as a building block for a polyolefin.
• a-olefin or alpha-olefin as used in the present description means: an olefin having a double bond at the a position.
• polyolefin as used in the present description means: a polymer obtained by the polymerization of olefin monomer.
• polymer chain as used in the present description means: a chain having a number average molecular weight (Mn) of at least 500 g/mol.
• copolymer as used in the present description means: a polymer derived from more than one type of monomer.
• main group metal hydrocarbyl functionalized branched growth product or “main group metal hydrocarbyl growth product” as used in the present description means: main group metal omprising as a ligand a hydrocarbyl chain obtained by chain transfer polymerization (in this case the polyolefin). Said hydrocarbyl chain is a polyolefin chain.
• main group metal hydrocarbyl branched growth product or “main group metal hydrocarbyl growth product” can have a main group metal at at least one of its chain ends and can be considered synonymous to "main group metal -terminated polyolefin” and "main group metal -functionalized polyolefin.”
• copolymerization as used in the present description means: a process to produce a copolymer wherein at least two different types of monomers are used.
• Poly as used in the present description means: polyolefin.
• PE polyethylene
• LDPE low density polyethylene
• LDPE low density polyethylene
• LLDPE linear low density polyethylene
• LDPE and LLDPE thereby encompass polyethylene with a density for example between 0.85 and 0.95 kg/m 3 , that can thus also includes especially for example VLDPE and MDPE.
• iPP as used in the present description means: isotactic polypropylene.
• P4M1 P as used in the present description means: poly-4-methyl-1 -pentene
• HT SEC as used in the present description means: high temperature size exclusion chromatography. Size exclusion chromatography can be used as a measure of both the size and the polydispersity of a polymer.
• polydispersity index (D) as used in the present description means: a value that indicates the distribution of the sizes of polymer molecules (Mw/Mn). The method of measuring the D is explained below.
• main group metal hydrocarbyl chain transfer agent or “chain transfer agent” as used in the present description means: a compound that is capable of reversibly or irreversibly interchanging hydrocarbyls and/or hydrocarbyl chains with the active catalyst or other chain transfer agents. It may be a metal compound with at least one ligand with a weak chemical bond, preferably a chain transfer agent based on a main group metal having at least one hydrocarbyl as ligand. If talking about an olefin or olefin monomer comprising a chain transfer agent, a corresponding functionality can be meant.
• chain transfer agent as used in the present description means: a compound that is capable of reversibly or irreversibly interchanging hydrocarbyls and/or hydrocarbyl chains with the active catalyst. It is a metal compound comprising at least one ligand with a weak chemical bond.
• chain transfer polymerization as used in the present description can mean: a polymerization reaction by which the growing polymer chain is transferred to another molecule, being the chain transfer agent. During this process a hydrocarbyl group is transferred back to the active catalyst. This process can be either reversible or irreversible. When reversible, the chain transfer agents can create a controlled, livinglike system.
• chain shuttling agent as used in the present description means: a compound that is capable of reversibly interchanging hydrocarbyls and/or hydrocarbyl chains with catalysts or other chain transfer agents. It is a metal compound comprising at least one ligand with a weak chemical bond. A chain shuttling agent can thus be a chain transfer agent.
• hydrocarbyl chain transfer agent as used in the present description means: a chain transfer agent having at least one hydrocarbyl as ligand.
• additional chain transfer agent as used in the present description means: a chain transfer agent that is present in addition to another chain transfer agent and/or to an olefin monomer comprising a chain transfer agent functionality.
• catalyst system means: a combination of at least two components selected from the group consisting of: a metal catalyst or a catalyst precursor, a co-catalyst, one or more types of chain transfer agents, etc.
• a catalyst system always includes a metal catalyst or a catalyst precursor.
• catalystst as used in the present description means: a species providing the catalytic reaction.
• a "metal catalyst” wherein said catalyst comprises at least one metal center that forms the active site is the same as a “transition metal catalyst” wherein the metal is a transition metal.
• catalyst precursor as used in the present description means: a compound that upon activation forms the active catalyst.
• single-site catalyst as used in the present description means: a metal catalyst that consists of solely one type of catalytically active site.
• metal catalyst as used in the present description means: a metal catalyst or catalyst precursor typically consisting of two substituted cyclopentadienyl (Cp) ligands bound to a metal active site.
• half-metallocene as used in the present description means: a metal catalyst or catalyst precursor consisting one substituted cyclopentadienyl (Cp) ligand bound to a metal active site and one or more anions bound to the metal, typically via a hetero atom.
• Cp substituted cyclopentadienyl
• post-metallocene as used in the present description means: a metal catalyst or catalyst precursor containing one or more anions bound to the metal active site, typically via a hetero atom, that are not substituted cyclopentadienyl (Cp) ligands.
• transition metal as used in the present description means: a metal from any of the Groups 3-10 of the lUPAC Periodic Table of elements or in other words a Group 3 metal, a Group 4 metal, a Group 5 metal, a Group 6 metal, a Group 7 metal, a Group 8 metal, a Group 9 metal or a Group 10 metal.
• Group 3 metal as used in the present description means: a metal selected from Group 3 of the lUPAC Periodic Table of elements, being scandium (Sc), yttrium (Y), lanthanum (La) and other lanthanides (Ce-Lu), and actinium (Ac) and other actinides (Th-Lr).
• Group 4 metal as used in the present description means: a metal selected from Group
• Group 5 metal as used in the present description means: a metal selected from Group
• V vanadium
• Nb niobium
• Ta tantalum
• Group 6 metal as used in the present description means: a metal selected from Group 6 of the Periodic Table of elements, being chromium (Cr), molybdenum (Mb) and tungsten (W).
• Group 7 metal as used in the present description means: a metal selected from Group
• Group 8 metal as used in the present description means: a metal selected from Group
• Group 9 metal as used in the present description means: a metal selected from Group
• Group 10 metal as used in the present description means: a metal selected from Group 10 of the Periodic Table of elements, being nickel (Ni), palladium (Pd) and platinum (Pt).
• Group X metal (half/post) metallocene catalyst or “Group X (half/post) metallocene catalyst” as used in the present description means: a metal catalyst constituted of a Group X metal (half/post) metallocene.
• any element of the Groups 3, 4, 5, 6, 7, 8, 9 and 10 of the lUPAC Periodic Table of elements may be substituted on X.
• An example is "Group 4 metal catalyst” being a catalyst constituted of a Group 4 metal.
• Group X metal single-site catalyst or “Group X single-site catalyst” as used in the present description means: a catalyst constituted of a Group X metal single-site catalyst.
• any element of the Groups 3, 4, 5, 6, 7, 8, 9 and 10 of the lUPAC Periodic Table of elements may be substituted on X.
• co-catalyst as used in the present description means a compound that activates the catalyst precursor to obtain the active catalyst. In the present description these two terms are used interchangeable.
• main group metal or “main group” as used in the present description refers to/means: a metal that is an element of Groups 1 , 2, and 13-15 of the period table. In other words, metals of:
• Group 13 boron (B), aluminum (Al), gallium (Ga), and indium (In)
• main group metals also include for the context of the present invention zinc (Zn), of the lUPAC Periodic Table of elements.
• main group metal-polymer species as used in the present description means: a polymer produced during the chain transfer polymerization that contains a main group metal as chain end group.
• catalyzed chain growth process means: the use of a metal catalyst in the polymerization of olefins, characterized by fast and reversible chains transfer reactions between the active metal center and main group metal center.
• methylaluminoxane or “MAO” as used in the present description means: a compound that serves as an co-catalyst for catalytic olefin polymerization.
• methylaluminoxane or “SMAO” as used in the present description means: a methylaluminoxane bound to a solid support.
• depleted methylaluminoxane or “DMAO” as used in the present description means: a methylaluminoxane from which the free trimethyl aluminum has been removed.
• modified methylaluminoxane or “MMAO” as used in the present description means: a methylaluminoxane that has been reacted with a neutral Lewis acid or polymeric or oligomeric hydrocarbyl group.
• fluorinated aryl borates or fluorinated aryl boranes as used in the present description means: a borate compound having three or four fluorinated (preferably perfluorinated) aryl ligands or a borane compound having three fluorinated (preferably perfluorinated) aryl ligands.
• halide as used in the present description means: an ion selected from the group of: fluoride (F-), chloride (CI-), bromide (Br-) or iodide (I-).
• halogen as used in the present description means: an atom selected from the group of: fluorine (F), chlorine (CI), bromine (Br) or iodine (I).
• heteroatom as used in the present description means: an atom other than carbon or hydrogen. Heteroatom also includes halides.
• heteroatom selected from Group 14, 15, 16 or 17 of the lUPAC Periodic Table of the Elements as used in the present description means: a hetero atom selected from Si, Ge, Sn [Group 14], N, P, As, Sb, Bi [Group 15], O, S, Se, Te [Group 16], F, CI, Br, I [Group 17].
• hydrocarbyl as used in the present description means: a substituent containing hydrogen and carbon atoms; it is a linear, branched or cyclic saturated or unsaturated aliphatic substituent, such as alkyl, alkenyl, alkadienyl and alkynyl; alicyclic substituent, such as cycloalkyl, cycloalkadienyl cycloalkenyl; aromatic substituent, such as monocyclic or polycyclic aromatic substituent, as well as combinations thereof, such as alkyl-substituted aryls and aryl-substituted alkyls. It may be substituted with one or more non-hydrocarbyl substituents.
• hydrocarbyl When in the present description "hydrocarbyl” is used, it can also be “substituted hydrocarbyl", unless stated otherwise. Included in the term “hydrocarbyl” are also perfluorinated hydrocarbyls wherein all hydrogen atoms are replaced by fluorine atoms.
• a hydrocarbyl may be present as a group on a compound (hydrocarbyl group) or it may be present as a ligand on a metal (hydrocarbyl ligand). It is different from a hydrocarbyl chain, which is the product of a polymerization reaction according to the present invention.
• hydrocarbyl chain as used in the present description can mean: the hydrocarbyl product of a polymerization reaction according to step A) of the present invention. It may be a oligomeric polyolefin chain having e.g. between 2 and 20 olefin units or it may be a polyolefin chain, i.e. consisting of more than 20 olefin units. It should be noted that “hydrocarbyl chain” and “hydrocarbyl” are not used as synonyms.
• alkyl as used in the present description means: a group consisting of carbon and hydrogen atoms having only single carbon-carbon bonds. An alkyl group may be straight or branched, un-substituted or substituted.
• It may contain aryl substituents. It may or may not contain one or more heteroatoms, such as for example oxygen (O), nitrogen (N), phosphorus (P), silicon (Si), tin (Sn) or sulfur (S) or halogens (i.e. F, CI, Br, I).
• heteroatoms such as for example oxygen (O), nitrogen (N), phosphorus (P), silicon (Si), tin (Sn) or sulfur (S) or halogens (i.e. F, CI, Br, I).
• aryl as used in the present description means: a substituent derived from an aromatic ring.
• An aryl group may or may not contain one or more heteroatoms, such as for example oxygen (O), nitrogen (N), phosphorus (P), silicon (Si), tin (Sn), sulfur (S) or halogen (i.e. F, CI, Br, I).
• An aryl group also encloses substituted aryl groups wherein one or more hydrogen atoms on the aromatic ring have been replaced by hydrocarbyl groups.
• alkoxide or "alkoxy” as used in the present description means: a substituent obtained from an aliphatic alcohol. It consists of an alkyl group bonded to an oxygen atom.
• aryloxide or "aryloxy” or “phenoxide” as used in the present description means: a substituent obtained from an aromatic alcohol. It consists of an aryl group bonded to an oxygen atom.
• silyl group as used in the present description means: a linear, branched or cyclic substituent containing 1 -20 silicon atoms. Said silyl group may consist of Si-Si single or double bonds.
• hydroide as used in the present description means a hydrogen anion bonded to a metal.
• quenching agent as used in the present description means: an agent to remove the main group metal from the polyolefin having one or multiple main group metal end- functionalized oxidized branches to obtain a polyolefin having one or multiple main group metal end-functionalized oxidized branches.
• Expressions like for example "C1 -C16" and similar formulations may refer to a range regarding a number of carbon atoms, here for example from 1 to 16 carbon atoms.
• the key of the present invention is the copolymerization of an olefin monomer, preferably a a-olefin, and at least one type olefin monomer, preferably a a-olefin, containing a main group metal chain transfer agent functionality.
• the resultant main group metal hydrocarbyl growth product (for example aluminum-PE) of the present invention can be used in several processes. It can for example be used for the preparation of polyolefins and of end-functionalized polyolefins.
• the end product that is desired in the present invention can be a polyolefin.
• An intermediate product for polyolefins is a so-called chain growth product, more specifically according to the present invention a main group metal hydrocarbyl chain growth product or main group metal-terminated polymer. Said main group metal stabilizes said polymer chain.
• the end product that is desired in the present invention is a branched polyolefin.
• the end product that is desired in the present invention is a branched polyolefin having end-functionalized branches.
• An intermediate product for end-functionalized polyolefins is a so-called chain growth product, more specifically according to the present invention an main group metal hydrocarbyl chain growth product or main group metall-terminated polymer.
• the present invention relates to the process to prepare the intermediate species, said intermediate species, the process to prepare the end product using said intermediate species and said end product. All of these are inventive by the use of an inventive catalyst system. These are all different aspects of the same invention that are linked by the same catalyst system.
• the present invention uses an olefin-containing main group metal hydrocarbyl as chain transfer agents.
• the olefin comprising a main group metal hydrocarbyl can be an alkene containing main group metal hydrocarbyl.
• the first step in the process according to the present invention is the preparation of an main group metal, preferably aluminum, hydrocarbyl chain growth product by polymerizing at least one first type of olefin monomer, preferably an a-olefin, and at least one second type of olefin monomer, preferably an a-olefin, comprising a main group metal hydrocarbyl chain transfer agent functionality.
• Said main group metal hydrocarbyl chain growth product has a reactive electrophilic end group.
• said main group metal, preferably aluminum, hydrocarbyl chain growth product is a branched polyolefin that is functionalized on at least one of its branch ends with a main group metal .
• step A an olefin monomer comprising an main group metal I hydrocarbyl chain transfer agent (being for example an aluminum atom bearing one or more hydrocarbyl comprising an olefin and/or hydride groups) is used.
• the product obtained in step A) is then an main group metal-functionalized chain growth product (being a branched polyolefin that is functionalized on at least one of its branch ends with a main group metal ). This is considered to be the main product of step A), which is an intermediate product in the process according to the present invention.
• Chain transfer polymerization is a specific type of polymerization reaction.
• a polymer chain grows on a catalytically active site. Said grown polymer chain is then transferred from the catalytically active site to another molecule, viz. a so-called chain transfer agent.
• Chain transfer to boron is known for ethylene and propylene polymerization using a variety of catalysts including metallocenes.
• Examples of documents disclosing chain transfer to boron are the publications of Xu, G. et al, J. Am. Chem. Soc. 1999, (121 ), 6763; Chung, T. C. et al, Macromolecules 2001 , (34), 8040; Lin, W. et al, J. Polym. Sci. Part A Polym. Chem. 2010, (48), 3534; Y. Lu, Y. Hu, Z. M. Wang, E. Manias, T. C. Chung, J. Polym. Sci. Part A 2002, (40), 3416; G. Xu, T. C. Chung, Macromolecules 1999, (32), 8689.
• the disadvantage of borane end-functionalized polymers is the relatively low reactivity of the B-C bond, which requires harsh oxidizing conditions (H202 NaOH) to functionalize
• Polymerization/copolymerization in step A) can preferably for example been carried out using by chain transfer polymerization.
• the catalyst system used in step A) comprises: i) a Group 3-10, preferably Group 3- 8, metal catalyst or catalyst precursor; ii) optionally a co-catalyst and iii) optionally additional chain transfer agents or chain shuttling agents. Each of these discussed separately below.
• Suitable monomers include linear or branched a-olefins.
• Said olefins preferably have between 2 and 30 carbon atoms, more preferably between 2 and 20 carbon atoms.
• one or more of the following are used: ethylene, propylene, 1 -butene, 4-methyl-1 -pentene, 1 -pentene, 1 -hexene, 1 -heptene, 1 -octene, 1 -nonene, 1 -decene, 1 -undecene, 1 -dodecene, 1 -tridecene, 1 -tetradecene, 1 -pentadecene, 1 - hexadecene, 1 -heptadecene, 1 -octadecene, 1 -cyclopentene, cyclohexene, norbornene, ethylidene-norbornene, and
• a combination of ethylene and/or propylene on the one and one or more other olefins on the other hand is also possible.
• Substituted analogues of the monomers discussed above may also be used, e.g. substituted by one or more halogens.
• aromatic monomers can be used according to the present invention. It is also possible to use a combination of two or more olefins, such as a combination of ethylene with a-olefins to arrive at an LLDPE-block.
• the present invention comprises at least one olefin monomer comprising an main group metal, preferably aluminum, hydrocarbyl chain transfer agent.
• the present invention may also use main group metal, preferably aluminum, chain transfer agent in combination with other main group metal hydrocarbyl chain transfer agents, for example, zinc, magnesium and/or calcium and/or boron and/or gallium hydrocarbyl/hydride chain transfer agents.
• the olefin monomer comprising a main group hydrocarbyl chain transfer agent used in the present invention has a structure according to Formula 1 a:
• Formula 1 a wherein: M is a main group metal; n is the oxidation state of M; R 100 , R 101 and R 102 are each independently selected from the group consisting of a hydride, a C1 -C18 hydrocarbyl group, or a hydrocarbyl group Q on the proviso that at least one of R 100 , R 101 and R 102 is hydrocarbyl group Q.
• hydrocarbyl group Q is according to Formula 1 b:
• Formula 1 b wherein Z is bonded to M and is a C1 -C18 hydrocarbyl group; R 105 optionally forms a cyclic group with Z; wherein R 103 and R 104 and R 105 are each independently selected from hydrogen or hydrocarbyl;
• hydrocarbyl group Q is an a-olefin wherein Z is bonded to the main group metal, Z is a C1 -C18 hydrocarbyl spacer group, R 103 R 104 and R 105 are each hydrogen, said hydrocarbyl group Q being according to Formula 1 c:
• hydrocarbyl group Q is an alkene wherein Z is bonded to the main group metal, Z is a C1 -C18 hydrocarbyl spacer group, R 103 and R 104 are independently hydrogen or hydrocarbyl and R105 is a C1 -18 hydrocarbyl, said R 105 group forming a cyclic structure with Z, said hydrocarbyl group Q being according to Formula 1 d:
• said hydrocarbyl group Q can be an a-olefin according to Formula 1 c or an unsaturated cyclic hydrocarbyl group according to Formula 1 d.
• hydrocarbyl group Q is an a-olefin or an unsaturated cyclic hydrocarbyl group.
• Z is a branched or unbranched hydrocarbyl spacer group consisting of between 1 and 18 carbon atoms, preferably 2 and 8 carbon atoms, more preferably 4 and 7 carbon atoms, even more preferably 5 or 6 carbon atoms. Z is optionally substituted with hydrogen, carbon, heteroatoms or halides.
• hydrocarbyl group Q is an ⁇ -olefin according to Formula 1 c.
• Said ⁇ -olefin has up to and including 30 carbon atoms, such as up to and including 20 carbon atoms, preferably up to and including 10 carbon atoms, such as ethenyl, propenyl, butenyl, heptenyl, hexenyl, septenyl, octenyl, nonenyl or decenyl and can be unbranched or branched.
• said ⁇ -olefin is an unbranched ⁇ -olefin according to Formula 1 e.
• the main group metal preferably aluminium, hydrocarbyl chain transfer agent comprises at least one hydrocarbyl chain bearing an ⁇ -olefin (i.e. hydrocarbyl group Q).
• Said hydrocarbyl group Q is an a-olefin-comprising a main group metal.
• hydrocarbyl group Q is an ⁇ -olefin according to Formula 1 e where n is 1 -5.
• the hydrocarbyl group Q is 3-buten-1 -yl, 4-penten-1 -yl, 5-hexen-1 -yl, 6-hepten-1 -yl or 7-octen-1 yl.
• the hydrocarbyl group Q is an unsaturated cyclic hydrocarbyl group according to Formula 1 d.
• the alkene is situated between substituents R 105 and Z and R 105 forms at least one a ring with Z.
• R 105 can be a C1 - C18 hydrocarbyl, which forms one or more bonds with Z to form a cyclic group.
• hydrocarbyl group Q comprises a norbornene group.
• R 105 provides carbons at positions 1 , 6 and 7
• Z provides carbons at positions 4 and 5, and the substituents at carbon 5.
• Suitable norbornene groups which can be used in the present invention can be, for example but not limited to, 5-ethylenebicyclo[2.2.1 ]hept-2-ene, 5-propylenebicyclo[2.2.1 ]hept-2-ene.
• the number of R groups around the main group metal is dependent on the oxidization state of the metal. For example, when the main group metal is zinc or magnesium or calcium, the oxidation state is +2, and the formula is R 100 MR 101 .
• the oxidation state is +3, and the formula is R 100 R 101 MR 102 .
• At least one olefin comprising main group metal hydrocarbyl chain transfer agent can be for example ethyl(5-ethylene-2-norbornene) zinc, ethyl(7-octen1 -yl) zinc, bis(5-ethylene-2-norbornene) zinc, or bis(7-octen-1 -yl) zinc.
• the olefin comprising at least one main group metal hydrocarbyl chain transfer agent can be for example bis(isobutyl)(5-ethylen-yl-2- norbornene) aluminum, di(isobutyl)(7-octen-1 -yl) aluminum, di(isobutyl)(5-hexen-1 -yl) aluminum, di(isobutyl)(3-buten-1 -yl) aluminum, tris(5-ethylen-yl-2-norbornene) aluminum, tris(7-octen-1 -yl) aluminum, tris(5-hexen-1 -yl) aluminum, or tris(3-buten-1 - yl) aluminum.
• the copolymerization of at least one olefin comprising main group metal hydrocarbyl chain transfer agent and a-olefin monomer may be carried out in the presence of an additional and/or other chain transfer reagent. From the prior art chain transfer reactions are known using several different chain transfer agents.
• the present invention can use for example main group metal hydrocarbyls and/or main group metal hydrides as chain transfer agents.
• main group metal hydrocarbyl or hydride the following can for example be used: one or more hydrocarbyl or hydride groups attached to a main group metal selected from aluminum, magnesium, calcium, zinc, gallium or boron. Of these several specific examples are specified below.
• the additional chain transfer agent may be selected from the group specified above having a general structure:
• M is a main group metal
• R is a hydride or hydrocarbyl group
• p is the oxidation state of the metal
• X is a heteroatom or heteroatom-bonded ligand
• q is an integer between 0 and p-1
• At least one hydrocarbyl or hydride group should be present.
• at least one R group is alkyl.
• R is an alkyl this group has up to and including 30 carbon atoms, such as up to and including 20 carbon atoms, preferably up to and including 10 carbon atoms, such as methyl, ethyl, propyl, butyl, heptyl, hexyl, septyl, octyl, nonyl or decyl and can be unbranched or branched.
• R is an alkenyl this group has up to and including 30 carbon atoms, such as up to and including 20 carbon atoms, preferably up to and including 10 carbon atoms, such as ethenyl, propenyl, butenyl, heptenyl, hexenyl, septenyl, octenyl, nonenyl or decenyl and can be unbranched or branched.
• R is an alkynyl this group has up to and including 30 carbon atoms, such as up to and including 20 carbon atoms, preferably up to and including 10 carbon atoms, such as vinyl, propynyl, butynyl, heptynyl, hexynyl, septynyl, octynyl, nonynyl or decynyl and can be unbranched or branched.
• carbon atoms such as up to and including 20 carbon atoms, preferably up to and including 10 carbon atoms, such as vinyl, propynyl, butynyl, heptynyl, hexynyl, septynyl, octynyl, nonynyl or decynyl and can be unbranched or branched.
• R is aryl it can be selected from mono cyclic or bicyclic groups or groups having more than two rings. These rings may be fused together or linked by a spacer. The aryl might be substituted on any ring position with a hydrocarbyl or heteroatom- containing group.
• aryl moieties include, but are not limited to, chemical structures such as phenyl, 1 -naphthyl, 2-naphthyl, dihydronaphthyl, tetrahydronaphthyl, biphenyl, anthryl, phenanthryl, biphenylenyl, acenaphthenyl, acenaphthylenyl, tolyl, xylyl, mesityl, 2-methoxy-phenyl, 2,6-dimethoxy-phenyl, 2-N,N- dimethylaminomethyl-phenyl, 2-N,N-dimethylamino-phenyl.
• R is an aryl-substituted alkyi this group consists of an alkyi containing an aryl that might be substituted on any ring position with a hydrocarbyl.
• Non-limiting examples are: benzyl, 1 -phenylethyl, 2-phenylethyl, diphenylmethyl, 3-phenylpropyl, and 2-phenylpropyl, o-methoxy-phenyl-methyl, o-N,N-dimethylamino-phenyl-methyl.
• main group metal hydrocarbyls containing hydrocarbyldiyl groups e.g. cyclic or oligomeric main group metal hydrocarbyls or alkoxyhydrocarbyl or amidohydrocarbyl groups may be used in order to obtain telechelic polymer blocks, which can be used to prepare triblock copolymers.
• the heteroatom-containing ligand X can be selected from the group consisting of: halide, oxide (-0-), carboxylate (-0 2 CR 40 ), alkoxide (-OR 40 ; i.e. O-alkyl), aryloxide (- OAr), thiolate (-SR 40 ), amide (-NR 40 R 41 ), phosphide (-PR 40 R 41 ), mercaptanate (-SAr), siloxide (-OSiR 40 R 41 R 42 ), stannate (-OSnR 40 R 41 R 42 ). Wherein R' independently a hydrocarbyl.
• an additional chain transfer agent may be selected from the group consisting of trialkyl boron, dialkyl boron halide, dialkyl boron hydride, diaryl boron hydride, dialkyl boron alkoxide, dialkyl boron aryloxide, dialkyl boron amide, dialkyl boron thiolate, dialkyl boron carboxylate, dialkyl boron phosphide, dialkyl boron mercaptanate, dialkyl boron siloxide, dialkyl boron stannate, alkyi boron dialkoxide, alkyi boron diaryloxide, alkyi boron dicarboxylate, alkyi boron diphosphide, alkyi boron dimercaptanate, alkyi boron disiloxide, alkyi boron distannate, boron hydride dialkoxide, boron hydride diaryloxide, boro
• tri-isobutyl aluminum trimethyl aluminum, triethyl aluminum, tri(i- propyl) aluminum, tri(n-butyl) aluminum, tri(t-butyl) aluminum, tri(n-hexyl) aluminum, tri(n-octyl) aluminum, di-isobutyl aluminum hydride, dimethyl aluminum 2,6-di(t-butyl)- 4-methyl-phenoxide, diethyl aluminum 2,6-di(t-butyl)-4-methyl-phenoxide, di-isobutyl aluminum 2,6-di(t-butyl)-4-methyl-phenoxide, iso-butyl aluminum-bis(di- trimethylsilyl)amide), n-octyl aluminum-di(pyridine-2-methoxide), bis(n-octadecyl)- isobutyl aluminum, isobutyl aluminum-bis(di(n-pentyl)amide), n-oct
• a main group metal especially for example aluminum
• a combination of for example a magnesium hydrocarbyl and an aluminum hydrocarbyl as the chain transfer agents for example a ternary system (TM + Al + Zn, where TM is transition metal of the catalyst) may be formed. Doing so can lead to reversible transfer reactions.
• hydrocarbyl zinc, hydrocarbyl gallium, hydrocarbyl boron or hydrocarbyl calcium can be used.
• a catalyst system for use in step a) comprises the following components:
• a metal catalyst or catalyst precursor comprising a metal from Group 3- 10 of the lUPAC Periodic Table of elements
• Suitable chain transfer agents have been discussed above. Suitable catalysts and/or catalyst precursors are discussed in this section as well as suitable co-catalysts, which are optional.
• a catalyst for step A) can preferably be used for example without co- catalyst.
• a catalyst precursor for step A) can preferably be used with aa co-catalyst to obtain the actual active catalyst.
• Metal catalysts that are suitable for use in step A) of the present invention may be obtained by reaction the metal catalyst precursors with a co-catalyst either prior to use in step A) or by reaction in situ.
• the metal catalyst has a metal center selected from a Group 3 metal, a Group 4 metal, a Group 5 metal, a Group 6 metal, a Group 7 metal, a Group 8 metal, a Group 9 metal or a Group 10 metal, preferably Y, Sm, Ti, Zr, Hf, V, Cr, Fe, Co, Ni, Pd.
• a metal catalyst or a metal catalyst precursor according to the invention may be for example a single-site catalyst or Ziegler-Natta catalyst.
• a transition metal- containing solid catalyst compound comprises a transition metal halide selected from titanium halide, chromium halide, hafnium halide, zirconium halide, and vanadium halide, supported on a metal or metalloid compound (e.g. a magnesium compound or a silica compound).
• a metal or metalloid compound e.g. a magnesium compound or a silica compound.
• Ziegler- Natta catalysts as reported in US2009/0048399, US2014/0350200, W096/32427, WO01 /23441 , WO2007/134851 , US4978648, EP1283 222A1 , US5556820; US4414132; US5106806 and US5077357 may also be suitable to use as metal catalyst precursors in the present invention.
• the metal catalysts or metal catalyst precursors may for example be a C 3 -, Ci- or C2- symmetric zirconium or hafnium metallocene, preferably an indenyl substituted zirconium or hafnium dihalide, more preferably a bridged bis-indenyl zirconium or hafnium dihalide, even more preferably rac-dimethylsilyl bis-indenyl zirconium or hafnium dichloride (rac-Me2Si(lnd)2ZrCl2 and rac-Me2Si(lnd)2HfCl2, respectively), or rac-dimethylsilyl bis-(2-methyl-4-phenyl-indenyl) zirconium or hafnium dichloride (rac- Me 2 Si(2-Me-4-Ph-lnd) 2 ZrCl2 and rac-Me 2 Si(2-Me-4-Ph-l nd)2HfCl2, respectively).
• said catalyst can be for example a so-called post- metallocene, preferably [Et 2 NC(N(2,6-iPr2-C6H 3 )]TiCl3 or [N-(2,6-di(l- methylethyl)phenyl)amido)(2-isopropylphenyl)(a-naphthalen-2-diyl(6-pyridin-2- diyl)methane)]hafnium dimethyl.
• post- metallocene preferably [Et 2 NC(N(2,6-iPr2-C6H 3 )]TiCl3 or [N-(2,6-di(l- methylethyl)phenyl)amido)(2-isopropylphenyl)(a-naphthalen-2-diyl(6-pyridin-2- diyl)methane)]hafnium dimethyl.
• the metal catalyst or metal catalyst precursor can also be for example a preferably C s or Ci symmetric compound according to the formula (C5R 8 4)R 9 (Ci3R 8 8)ML 1 n , where C 5 R 8 4 is an unsubstituted or substituted cyclopentadienyl, and Ci3R 1 1 e is an unsubstituted fluorenyl group or a substituted fluorenyl group; and the bridging R 9 group is selected from the group consisting of -Si(Me)2-, -Si(Ph) 2 - -C(Me)2- or - C(Ph)2- thus producing Ci- and Cs-symmetric metallocenes.
• zirconocene dichloride metal catalyst precursors suitable for use in the present invention include: bis(cyclopentadienyl) zirconium dichloride, bis(methyl-cyclopentadienyl) zirconium dichloride, bis(n-propyl-cyclopentadienyl) zirconium dichloride, bis(n-butyl-cyclopentadienyl) zirconium dichloride, bis(1 ,3- dimethyl-cyclopentadienyl) zirconium dichloride, bis(1 ,3-di-t-butyl-cyclopentadienyl) zirconium dichloride, bis(1 ,3-ditrimethylsilyl-cyclopentadienyl) zirconium dichloride, bis(1 ,2,4-trimethyl-cyclopentadienyl) zirconium dichloride, bis(1 ,2,3,4-tetramethyl- cyclopent
• the metal catalyst or metal catalyst precursor can be for example: [[2,2'-[[[2-(dimethylamino-KN)ethyl]imino-KN]bis(methylene)]bis[4,6-bis(1 , 1 - dimethylethyl) phenolato- ⁇ ]] zirconium dibenzyl, (phenylmethyl)[[2,2'-[(propylimino- KN)bis(methylene)]bis[4,6-bis(1 , 1 -dimethylethyl)phenolato-KO]] zirconium dibenzyl or (phenylmethyl)[[2,2'-[[[(2-pyridinyl-KN)methyl]imino-KN]bis(methylene)]bis[4,6-bis(1 , 1 - dimethylethyl)phenolato-KO]] zirconium dibenzyl.
• complexes as reported in WO 00/43426, WO 2004/081064, US 2014/0039138 Al, US 2014/0039139 Al and US 2014/0039140 Al are suitable to use as metal catalyst precursors for the processes of the present invention.
• hafnocenes may also be used according to the as catalyst precursors present invention.
• the metal catalysts or metal catalyst precursors for use in the present invention may also be from post-metallocene catalysts or catalyst precursors.
• the metal catalyst or metal catalyst precursor may be : [HN(CH2CH2N-2,4,6-Me3-C6H2)2]Hf(CH2Ph)2 or bis[N,N'-(2,4,6- trimethylphenyl)amido)ethylenediamine]hafnium dibenzyl.
• the metal catalyst or metal catalyst precursor may be 2,6-diisopropylphenyl-N-(2-methyl-3-(octylimino)butan-2) hafnium trimethyl, 2,4,6- trimethylphenyl-N-(2-methyl-3-(octylimino)butan-2) hafnium trimethyl.
• the metal catalyst or metal catalyst precursor may be [2,6- iPr2C6H3NC(2-iPr-C6H4)-2-(6-C5H6)]HfMe2 — [N-(2,6-di(1 - methylethyl)phenyl)amido)(2-isopropylphenyl) ( -naphthalen-2-diyl(6-pyridin-2- diyl)methane)]hafnium dimethyl.
• metal catalyst precursors according to the present invention are: [N-(2,6-di(1 -methylethyl)phenyl)amido)(o-tolyl)(a-naphthalen-2-diyl(6- pyridin-2-diyl)methane)] hafnium dimethyl, [N-(2,6-di(1 -methylethyl)phenyl)amido)(o- tolyl)(a,a-naphthalen-2-diyl(6-pyridin-2-diyl)methane)] hafnium di(N, N- dimethylamido), [N-(2,6-di(l-methylethyl)phenyl)amido)(o-tolyl)(a,a-naphthalen-2- diyl(6-pyridin-2-diyl)methane)] hafnium dichloride, [N-(2,6-di(1 -methyle
• Non-limiting examples include the family of pyridyl diamide metal dichloride complexes such as: [N-[2,6-bis( 1 -methylethyl)phenyl]- 6-[2-[phenyl(phenylamino-KN)methyl]phenyl]-2-pyridinemethanaminato(2-)- KN 1 , KN2]hafnium dichloride, [N-[2,6-bis( 1 -methylethyl)phenyl]-6-[2-[(phenylamino- KN)methyl]- 1 -naphthalenyl]-2-pyridinemethanaminato(2-)-KN 1 , KN2] hafnium dichloride, [N-[2,6-bis( 1 -methylethyl)phenyl]-a-[2-( 1 -methylethyl)phenyl]-6-[2- [(phenylamino-KN)methyl]phenyl]-2-pyridinemethanamin
• Non-limiting examples of titanium dichloride metal catalyst precursors suitable for use in the present invention include: cyclopentadienyl(P,P,P-tri-t-butylphosphine imidato) titanium dichloride, pentafluorophenylcyclopentadienyl(P,P,P-tri-t-butylphosphine imidato) titanium dichloride, pentamethylcyclopentadienyl(P,P,P-tri-t-butylphosphine imidato) titanium dichloride, 1 ,2 ,3,4-tetraphenyl-cyclopentadienyl(P,P-tri-t- butylphosphine imidato) titanium dichloride, cyclopentadienyl(P,P,P- tricyclohexylphosphine imidato) titanium dichloride, pentafluorophenyl cyclopentadienyl(P, P,
• Non-limiting examples of titanium (IV) dichloride metal catalyst suitable for use in the present invention are: (N-t-butylamido)(dimethyl)(tetramethylcyclopentadienyl)silane titanium dichloride, (N phenylamido)(dimethyl)(tetramethylcyclopentadienyl) silane titanium dichloride, (N sec-butylamido)(dimethyl)(tetramethylcyclopentadienyl)silane titanium dichloride, (N sec-dodecylamido) (dimethyl)(fluorenyl)silane titanium dichloride, (3 phenylcyclopentadien-1 -yl) dimethyl(t-butylamido) silane titanium dichloride, (3 (pyrrol-l-yl)cyclopentadien-l -yl) dimethyl(t-butylamido)silane titanium dichloride, (3,4-diphenylcyclopent
• Ln is dimethyl, dibenzyl, diphenyl, 1 ,4-diphenyl-2-butene-1 ,4-diyl, 1 ,4-dimethyl-2-butene-1 ,4-diyl or 2,3- dimethyl-2-butene-1 ,4-diyl.
• Suitable metal catalyst precursors can be also the trivalent transition metal as those described in WO 9319104 (for example see especially example 1 , page 13, line 15).
• Suitable metal catalyst precursors can be also the trivalent transition metal as [C5Me4CH2CH2N(n-Bu)2]TiCI2 described in WO 9613529 (for example see especially example II I, page 20, line 10-13) or [C5H(iPr)3CH2CH2NMe2]TiCI2 described in WO 97142232 and WO 9742236 (for example see especially example 1 , page 26, line 14).
• the metal catalyst precursor is [C5H4CH2CH2NMe2]TiCI2;
• the metal catalyst or metal catalyst precursor may also be [C5Me4CH2CH2NMe2]TiCI2, [C5H4CH2CH2NiPr2]TiCI2, [C5Me4CH2CH2NiPr2]TiCI2, [C5H4C9H6N]TiCI2, [C5H4CH2CH2NMe2]CrCI2, [C5Me4CH2CH2NMe2]CrCI2; [C5H4CH2CH2NiPr2]CrCI2, [C5Me4CH2CH2NiPr2]CrCI2 or [C5H4C9H6N]CrCI2.
• metal catalyst precursors that would be suitable according to the present invention are: (N,N dimethylamino)methyl- tetramethylcyclopentadienyl titanium dichloride, (N,N dimethylamino)ethyl- tetramethylcyclopentadienyl titanium dichloride, (N,N dimethylamino)propyl- tetramethylcyclopentadienyl titanium dichloride, (N,N dibutylamino)ethyl- tetramethylcyclopentadienyl titanium dichloride, (pyrrolidinyl)ethyl- tetramethylcyclopentadienyl titanium dichloride, (N,N-dimethylamino)ethyl-fluorenyl titanium dichloride, (bis(1 -methyl-ethyl)phosphino)ethyl-tetramethylcyclopentadienyl titanium dichloride, (bis(2-methyl
• the catalyst precursor is: [2-(2,4,6-iPr3-C6H2)-6-(2,4,6- iPr3-C6H2)-C5H3N]Ti(CH2Ph)3 or [Et2NC(N-2,6-iPr2-C6H3)2]TiCI3
• metal catalyst precursors according to the present invention are: ⁇ N',N"-bis[2,6-di(1 -methylethyl)phenyl]-N,N-diethylguanidinato ⁇ titanium trichloride, ⁇ N',N"bis[2,6-di(1 -methylethyl)phenyl]-N-methyl-N-cyclohexylguanidinato ⁇ titanium trichloride, ⁇ N',N"-bis[2,6-di(1 -methylethyl)phenyl]-N,N- pentamethyleneguanidinato ⁇ titanium trichloride, ⁇ N',N"-bis[2,6-di(methyl)phenyl]-sec- butyl-aminidinato ⁇ titanium trichloride, ⁇ N-trimethylsilyl,N'-(N",N"- dimethylaminomethyl)benzamidinato ⁇ titanium dichloride THF complex,
• metal catalyst precursors according to the present invention can be for example: bis[2-[(2-pyridinylimino)methyl]phenolato] titanium dichloride, bis[2-(1 , 1 -dimethylethyl)-6-[(phenylimino)methyl]phenolato] titanium dichloride, bis[2-(1 , 1 -dimethylethyl)-6-[(1 - naphthalenylimino)methyl]phenolato] titanium dichloride, bis[3-
• the metal catalyst precursor cited in the list directly above wherein the dichloride can be replaced with dimethyl, dibenzyl, diphenyl, 1 ,4- diphenyl-2-butene-1 ,4-diyl, 1 ,4-dimethyl-2-butene-1 ,4-diyl or 2,3-dimethyl-2-butene- 1 ,4-diyl; and/or wherein the metal may be zirconium or hafnium.
• the catalyst precursor can be : [2-[[[2-[[[[3,5-bis(1 , 1 - dimethylethyl)-2-(hydroxy-KO)phenyl]methyl]amino-KN]ethyl]methylamino-KN]methyl]- 4,6-bis(1 , 1 -dimethylethyl)phenolato(2-)-KO] titanium bis(phenylmethyl), [2,4-dichloro- 6-[[[2-[[[[3,5-dichloro-2-(hydroxy-KO)phenyl]methyl]amino-KN]ethyl]methylamino-
• metal catalyst precursor cited in the list directly above wherein bis(phenylmethyl) can be replaced with dichloride, dimethyl, diphenyl, 1 ,4-diphenyl-2-butene-1 ,4-diyl, 1 ,4- dimethyl-2-butene-1 ,4-diyl or 2,3-dimethyl-2-butene-1 ,4-diyl; and/or wherein the metal may be zirconium or hafnium.
• chromium catalysts that would be suitable for use in to the present invention are:
• L1 is hydride, methyl, benzyl, phenyl, allyl, (2-N,N- dimethylaminomethyl)phenyl, (2-N,N-dimethylamino)benzyl; in other words chromium methyl, chromium benzyl, chromium allyl, chromium (2-N,N-dimethylamino)benzyl; and/or wherein the metal is trivalent yttrium or samarium;
• metal catalyst precursors as cited in the list directly above wherein Ln is chloride, bromide, hydride, methyl, benzyl, phenyl, allyl, (2-N,N-dimethylaminomethyl)phenyl, (2-N,N- dimethylamino)benzyl and/or wherein the metal is trivalent titanium or trivalent chromium.
• Non-limiting examples of metal catalyst precursors according to the present invention are: N,N'-1 ,2-acenaphthylenediylidenebis(2,6-bis(1 -methylethyl)benzenamine) nickel dibromide, N,N'-1 ,2-ethanediylidenebis(2,6-dimethylbenzenamine) nickel dibromide, N,N'-1 ,2-ethanediylidenebis(2,6-bis(1 -methyl-ethyl)benzenamine) nickel dibromide, N,N'-1 ,2-acenaphthylenediylidenebis(2,6-dimethylbenzenamine) nickel dibromide, N,N'-1 ,2-acenaphthylenediylidenebis(2,6-bis(1 -methylethyl)benzenamine) nickel dibromide, N,N'-1 ,2-acenaphthylenediylidenebis
• metal catalyst precursors according to the present invention are: [2-[[[2,6-bis(1 -methylethyl)phenyl]imino-KN]methyl]-6-(1 , 1 - dimethylethyl)phenolato-KO] nickel phenyl(triphenylphosphine), [2-[[[2,6-bis(1 - methylethyl)phenyl]imino-KN]methyl]-6-(1 , 1 -dimethylethyl)phenolato-KO] nickel phenyl(triphenylphosphine), [2-[[[2,6-bis(1 -methylethyl)phenyl]imino- KN]methyl]phenolato-KO] nickel phenyl(triphenylphosphine), [2-[[[2,6-bis(1 -methylethyl)phenyl]imino- KN]methyl]phenolato-KO] nickel phenyl(triphenylphos
• a co-catalyst can be used when a metal catalyst precursor is applied.
• the function of this co-catalyst is to activate the metal catalyst precursor.
• Co-catalysts may be selected for example from the group consisting of aluminum alkyls and aluminum alkyl halides, such as for example triethyl aluminum (TEA) or diethyl aluminum chloride (DEAC), MAO, DMAO, MMAO, SMAO, possibly in combination with aluminum alkyls, for example triisobutyl aluminum, and/or with a combination of an aluminum alkyl, for example triisobutyl aluminum, and a fluorinated aryl borane or fluorinated aryl borate (viz.
• Methylaluminoxane or MAO as used in the present description may mean: a compound derived from the partial hydrolysis of trimethyl aluminum that serves as a co-catalyst for catalytic olefin polymerization.
• Supported methylaluminoxane or SMAO as used in the present description may mean: a methylaluminoxane bound to a solid support.
• Depleted methylaluminoxane or DMAO as used in the present description may mean: a methylaluminoxane from which the free trimethyl aluminum has been removed.
• Modified methylaluminoxane or MMAO as used in the present description may mean: modified methylaluminoxane, viz. the product obtained after partial hydrolysis of trimethyl aluminum plus another trialkyl aluminum such as tri(isobutyl) aluminum or tri- n-octyl aluminum.
• Fluorinated aryl borates or fluorinated aryl boranes as used in the present description may mean: a borate compound having three or four fluorinated (preferably perfluorinated) aryl ligands or a borane compound having three fluorinated (preferably perfluorinated) aryl ligands.
• the co-catalyst can be an organometallic compound.
• the metal of the organometallic compound can be selected from Group 1 , 2, 12 or 13 of the lUPAC Periodic Table of Elements.
• the co-catalyst is an organoaluminum compound, more preferably an aluminoxane, said aluminoxane being generated by the reaction of a trialkyl aluminum compound with water to partially hydrolyze said aluminoxane.
• trimethyl aluminum can react with water (partial hydrolysis) to form methylaluminoxane (MAO).
• MAO has the general formula (AI(CH3)3- nOo.5n)x (AIMe3)y having an aluminum oxide framework with methyl groups on the aluminum atoms.
• MAO generally contains significant quantities of free trimethyl aluminum (TMA), which can be removed by drying the MAO to afford the so-called depleted MAO or DMAO.
• Supported MAO (SMAO) may also be used and may be generated by the treatment of an inorganic support material, typically silica, by MAO.
• SMAO free trimethyl aluminum
• a bulky phenol such as butylhydroxytoluene (BHT, 2,6-di-t-butyl-4- methylphenol) can be added which reacts with the free trimethyl aluminum.
• BHT butylhydroxytoluene
• Neutral Lewis acid modified polymeric or oligomeric aluminoxanes may also be used, such as alkylaluminoxanes modified by addition of a C1 -30 hydrocarbyl substituted Group 13 compound, especially a tri(hydrocarbyl) aluminum- or tri(hydrocarbyl) boron compounds, or a halogenated (including perhalogenated) derivatives thereof, having 1 to 10 carbons in each hydrocarbyl or halogenated hydrocarbyl group, more especially a trialkyl aluminum compound.
• alkylaluminoxanes modified by addition of a C1 -30 hydrocarbyl substituted Group 13 compound especially a tri(hydrocarbyl) aluminum- or tri(hydrocarbyl) boron compounds, or a halogenated (including perhalogenated) derivatives thereof, having 1 to 10 carbons in each hydrocarbyl or halogenated hydrocarbyl group, more especially a trialkyl aluminum compound.
• polymeric or oligomeric aluminoxanes are tri(isobutyl) aluminum- or tri(n-octyl) aluminum-modified methylaluminoxane, generally referred to as modified methylaluminoxane, or MMAO.
• MAO, DMAO, SMAO and MMAO may all be used as co-catalyst.
• the metal catalyst precursors may also be rendered catalytically active by a combination of an alkylating agent and a cation forming agent which together form the co-catalyst, or only a cation forming agent in the case the catalyst precursor is already alkylated, as exemplified in T. J. Marks et al. , Chem. Rev. 2000, (100), 1391 .
• Suitable alkylating agents are trialkyl aluminum compounds, preferably TIBA.
• Suitable cation forming agents for use herein include (i) neutral Lewis acids, such as C1 -30 hydrocarbyl substituted Group 13 compounds, preferably tri(hydrocarbyl)boron compounds and halogenated (including perhalogenated) derivatives thereof, having from 1 to 10 carbons in each hydrocarbyl or halogenated hydrocarbyl group, more preferably perfluorinated tri(aryl)boron compounds, and most preferably tris(pentafluorophenyl) borane, (ii) non polymeric, compatible, non-coordinating, ion forming compounds of the type [C] + [A] ⁇ where "C" is a cationic group such as ammonium, phosphonium, oxonium, , silylium or sulfonium groups and [A]- is an anion, especially for example a borate.
• neutral Lewis acids such as C1 -30 hydrocarbyl substituted Group 13 compounds, preferably tri(hydrocarbyl)boron compounds and
• Non-limiting examples of the anionic ["A"] are borate compounds such as C1 -30 hydrocarbyl substituted borate compounds, preferably tetra(hydrocarbyl)boron compounds and halogenated (including perhalogenated) derivatives thereof, having from 1 to 10 carbons in each hydrocarbyl or halogenated hydrocarbyl group, more preferably perfluorinated tetra(aryl)boron compounds, and most preferably tetrakis(pentafluorophenyl) borate.
• borate compounds such as C1 -30 hydrocarbyl substituted borate compounds, preferably tetra(hydrocarbyl)boron compounds and halogenated (including perhalogenated) derivatives thereof, having from 1 to 10 carbons in each hydrocarbyl or halogenated hydrocarbyl group, more preferably perfluorinated tetra(aryl)boron compounds, and most preferably tetrakis(pentafluorophenyl) borate.
• a supported catalyst may also be used, for example using SMAO as the co-catalyst.
• the support material can be an inorganic material. Suitable supports include solid and particulated high surface area, metal oxides, metalloid oxides, or mixtures thereof. Examples include: talc, silica, alumina, magnesia, titania, zirconia, tin oxide, aluminosilicates, borosilicates, clays, and mixtures thereof.
• Preparation of a supported catalyst can be carried out using methods known in the art, for example i) a metal catalyst precursor can be reacted with supported MAO to produce a supported catalyst; ii) MAO can be reacted with a metal catalyst precursor and the resultant mixture can be added to silica to form the supported catalyst; iii) a metal catalyst precursor immobilized on a support can be reacted with soluble MAO.
• a scavenger can optionally be added in the catalyst system in order to react with impurities that are present in the polymerization reactor, and/or in the solvent and/or monomer feed. This scavenger prevents poisoning of the catalyst during the olefin polymerization process.
• the scavenger can be the same as the co-catalyst but can also independently be selected from the group consisting of aluminum hydrocarbyls (e.g. triisobutyl aluminum, trioctyl aluminum, trimethyl aluminum, MAO, MMAO, SMAO), zinc hydrocarbyls (e.g. diethyl zinc) or magnesium hydrocarbyls (e.g. dibutyl magnesium).
• Step A) is preferably carried out in an inert atmosphere.
• Step A) can be preferably for example carried out using chain transfer polymerization.
• Polymerization/copolymerization of the olefins can for example be carried out in the gas phase below the melting point of the polymer. Polymerization can also be carried out in the slurry phase below the melting point of the polymer. Moreover, polymerization can be carried out in solution at temperatures above the melting point of the polymer product. It is known to continuously polymerize one or more olefins, such as ethylene or propylene, in solution or in slurry, e.g.
• the polymer particles are kept in the fluidized and/or stirred state in a gaseous reaction mixture containing the olefin(s).
• the catalyst is introduced continuously or intermittently into the reactor while the polymer constituting the fluidized or mechanically stirred bed is withdrawn from the reactor, also continuously or intermittently.
• the heat of the polymerization reaction is essentially removed by the gaseous reaction mixture, which passes through heat transfer means before being recycled into the reactor.
• a liquid stream may be introduced into the gas- phase reactor to enhance heat removal.
• Slurry phase polymerization of olefins is very well known, wherein an olefin monomer and optionally olefin comonomer are polymerized in the presence of a catalyst in a diluent in which the solid polymer product is suspended and transported.
• Two or more reactors are typically used in such polymerizations when it is desired to produce a multimodal product, in which a polymer made in a first reactor is transferred to a second reactor, where a second polymer having different properties to the first polymer is made in the presence of the first.
• a slurry reactor may also be combined with a gas phase reactor.
• Slurry phase polymerizations are typically carried out at temperatures in the range 50- 125 °C and at pressures in the range 1 -40 bar.
• the catalyst used can be any catalyst typically used for olefin polymerization such as those according to the present invention.
• the product slurry, comprising polymer and diluent and in most cases also catalyst, olefin monomer and comonomer can be discharged from each reactor intermittently or continuously, optionally using concentrating devices such as hydrocyclones or settling legs to minimize the quantity of fluids withdrawn with the polymer.
• the present invention may also be carried out in a solution polymerization process.
• the monomer and polymer are dissolved in an inert solvent.
• Solution polymerization has some advantages over slurry processes.
• the molecular weight distribution and the process variables are more easily controlled because the polymerization occurs in a homogeneous phase using homogeneous single site catalysts.
• the high polymerization temperature typically above 150°C also leads to high reaction rates.
• the solution process is used primarily for the production of relatively low molecular weight and/or low density resins, which are difficult to manufacture by the liquid slurry or gas phase processes.
• the solution process is very well suited to produce low density products but it is thought much less satisfactory for higher molecular weight resins because of the excessive viscosity in the reactor as discussed by Choi and Ray, JMS Review Macromolecular Chemical Physics C25(l), 1 -55, pg. 10 (1985).
• the reaction temperature and the reaction pressure are higher than in gas phase or slurry process to maintain the polymer in solution.
• the solution process tends to use an inert solvent that dissolves the polymer as it is formed, subsequently the solvent is separated and the polymer is pelletized.
• the solution process is considered versatile in that a wide spectrum of product properties can be obtained by varying the catalyst composition, the pressure, the temperature and the comonomer employed.
• the second step of the process according to the present invention relates to contacting the main group metal hydrocarbyl branched growth product obtained in step A) with a quenching agent to obtain a branched polymer.
• the quenching agent is a protic reagent.
• the protic agent is water or an alcohol or a mixture thereof, preferably ethanol or methanol.
• the intermediate product according to the present invention viz. the main group metal chain growth product, is converted into the corresponding branched polyolefin.
• this can be done by a step to release the main group metal from the polymer chain (for example hydrolysis by water) using a quenching agent to replace the aluminum especially for example by H, a hydrocarbyl, a silyl group or a stannyl group.
• a quenching agent to replace the aluminum especially for example by H, a hydrocarbyl, a silyl group or a stannyl group.
• the quenching agent can be a hydrolyzing agent, wich can be a protic solvent, e.g. water or an alcohol, such as for example (acidified) methanol or ethanol, preferably water.
• said quenching agent is typically a halogen-containing agent releasing a metal-halide or an anhydride releasing a metal-carboxylate. Typical examples are alkyl halides and anhydrides.
• branched polyolefins can be obtained.
• the branched polyolefins and branched polyolefins having end functionalized branches have an average number molecular weight (M n ) between 500 and 1 ,000,000 g/mol, preferably between 1000 and 200.000 g/mol.
• M n average number molecular weight
• the branched polyolefins and branched polyolefins having end functionalized branches according to the present invention preferably have a polydispersity index (D) of between 1 .1 and 10.0, more preferably between 1 .1 and 5.0, more preferably between 1 .1 and 4.0, even more preferably between 1 .5 and 2.5.
• the branched polyolefins may be composed of polyolefin blocks, which blocks may be linear or branched (both branched and short chain branched), atactic or isotactic, preferably, isotactic polyolefins in the case of poly-alpha-olefins, wherein the isotactic polyolefin is preferably isotactic polypropylene.
• An advantage of the present invention is that branched polyolefins can be obtained with a simple process in one single series of connected reactors in a continuous matter.
• the branched polyolefins prepared according to the present invention may for example be used to introduce polar properties to enhance the interracial interactions in polyolefins blends with polar polymers or blends with different polyolefins with PEs.
• Beta-hydride (or ⁇ - ⁇ ) elimination is a reaction in which a polymeryl group containing ⁇ -hydrogens bonded to a metal center is converted into the corresponding macromolecular alkene and the corresponding metal-bonded hydride.
• Beta-hydride (or ⁇ - ⁇ ) transfer to monomer is a reaction in which a polymeryl group containing ⁇ -hydrogens bonded to a metal center is converted into a macromolecular alkene and the hydride is transferred to an olefin coordinated to the metal thus forming another alkyl group bonded to said metal center.
• ⁇ -alkyl transfer or elimination is also known.
• the polymeryl must have an alkyl group (typically a methyl) on the ⁇ -carbon.
• ⁇ -Alkyl transfer or elimination typically results in unsaturated macromolecules, containing an allyl chain end, and a new metal alkyl. These are undesired processes since they lead to non-end-functionalized polyolefins. Examples
• ODIBA is di(isobutyl)(7-octen-1 -yl)aluminum
• NDIBA is bis(isobutyl)(5-ethylen-yl-2-norbornene) aluminum
• TIBA is tri(isobutyl) aluminum (additional chain transfer agent).
• the products were removed from the reactor and purified by repeatedly washing with acidic ethanol (containing 5-10 % concentrated HCI) and dried under vacuum at 60 °C for 18 hours.
• Heteronuclear multiple-bond correlation spectra were recorded with pulse field gradients.
• the spectral windows for 1 H and 13C axes were 6075.3 and 21367.4 Hz, respectively.
• the data were collected in a 2560 x 210 matrix and processed in a 1 K x 1 K matrix.
• the spectra were recorded with the acquisition time 0.21 1 s, relaxation delay 1 .4 s and number of scans equal to 144 210 increments.
• the 13 C ⁇ 1 H ⁇ INEPT spectra were recorded using the refocused-INEPT sequence with a J-evolution period of either 1/3 JCH or 1/6 JCH assuming a 1 JCH of 150 Hz, i.e. for a J-evolution time of 1/3 JCH the signals from CH and CH3 groups are positive, while those of CH2 are negative.
• the 2D 1 H- 1 H double quantum-single quantum (DQ-SQ) correlation experiments and DQ build-up experiments were carried out on a Bruker AVANCE-II I 700 spectrometer using a 2.5 mm solid-state MAS double-resonance probe. These experiments employed a spinning frequency of 25.0 kHz. DQ excitation and reconversion was performed using the broadband back-to-back (BaBa) sequence. Chemical shifts for 1 H and 13C are reported relative to TMS using solid adamantane as an external.
• the molecular weight in kg/mol and the PDI were determined by means of high temperature size exclusion chromatography which was performed at 160 °C using a high speed GPC (Freeslate, Sunnyvale, USA). Detection: IR4 (PolymerChar, Valencia, Spain). Column set: three Polymer Laboratories 13 ⁇ PLgel Olexis, 300 x 7.5 mm. 1 ,2,4-Trichlorobenzene (TCB) was used as eluent at a flow rate of 1 mL min-1 . TCB was freshly distilled prior to use. The molecular weights and the corresponding PDI were calculated from HT SEC analysis with respect to narrow polyethylene standards (PSS, Mainz, Germany).
• DSC Differential scanning calorimetry
• Diisobutyl(oct-7-en-1-yl)aluminum and (2-(bicyclo[2.2.1]hept-5-en-2- yl)ethyl)diisobutylaluminum were synthesized by hydroalumination of excess 1 ,7- octadiene and 5-vinyl-2-norbornene using diisobutylaluminum hydride at 60 °C for 6 h in a 200 mL Schlenk flask equipped with a magnetic stirrer. The remaining reagents (1 ,7-octadiene and 5-vinyl-2-norbornene) after the hydroalumination reaction were removed by evacuation.
• Polymerization reactions were carried out in stainless steel Buchi reactors (300 mL). Prior to the polymerization, the reactor was dried in vacuo at 40 °C and flushed with dinitrogen. Toluene (70 mL) and ODIBA or NDIBA (second type of olefin monomer comprising a chain transfer agent functionality) solution in toluene (20 ml_, Al/Zr « 285) were added and stirred at 50 rpm for 30 min. Polymerization was staaddition of DEZ (1 .0 ml_, 1 .0 M solution in hexanes, Al/Zr « 50 equiv.), the zirconocene complex and optionally MAO or TIBA.
• the solutions were saturated with predefined amount of ethylene first type of olefin monomer).
• the reactors were then pressurized to the desired pressure (2 bars) with ethylene and the pressure was maintained for a predefined time (5 min).
• the ethylene feed was stopped and the residual ethylene was vented off.
• the resulting mixture was quenched directly with a diluted solution of hydrochloric acid in methanol, filtered and dried under reduced pressure at 60 °C for 18 h.
• the precipitated powder was filtered out and dried under vacuum at 60 °C for 18 h.

Landscapes

• Chemical & Material Sciences (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Organic Chemistry (AREA)
• Crystallography & Structural Chemistry (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Transition And Organic Metals Composition Catalysts For Addition Polymerization (AREA)
• Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
• Polymerisation Methods In General (AREA)

Priority Applications (6)

Applications Claiming Priority (2)

Publications (1)

Family

ID=52130160

Family Applications (1)

Country Status (7)

Cited By (11)

Families Citing this family (8)

Citations (3)

Family Cites Families (34)

• 2014
  • 2014-12-23 EP EP14200125.4A patent/EP3037438A1/en not_active Withdrawn
• 2015
  • 2015-12-23 JP JP2017533760A patent/JP6770960B2/ja active Active
  • 2015-12-23 US US15/537,926 patent/US10450388B2/en active Active
  • 2015-12-23 EP EP15816486.3A patent/EP3237460A1/en active Pending
  • 2015-12-23 CN CN201580075828.6A patent/CN107207660B/zh active Active
  • 2015-12-23 WO PCT/EP2015/081203 patent/WO2016102690A1/en not_active Ceased
  • 2015-12-23 KR KR1020177020264A patent/KR102510436B1/ko active Active
• 2017
  • 2017-06-22 SA SA517381805A patent/SA517381805B1/ar unknown

Patent Citations (3)