WO2016042992A1 - Film réfléchissant, et unité de rétroéclairage à éclairage périphérique utilisant celui-ci - Google Patents

Film réfléchissant, et unité de rétroéclairage à éclairage périphérique utilisant celui-ci Download PDF

Info

Publication number
WO2016042992A1
WO2016042992A1 PCT/JP2015/073964 JP2015073964W WO2016042992A1 WO 2016042992 A1 WO2016042992 A1 WO 2016042992A1 JP 2015073964 W JP2015073964 W JP 2015073964W WO 2016042992 A1 WO2016042992 A1 WO 2016042992A1
Authority
WO
WIPO (PCT)
Prior art keywords
particles
reflective film
mass
layer
resin layer
Prior art date
Application number
PCT/JP2015/073964
Other languages
English (en)
Japanese (ja)
Inventor
田中正太郎
若原隆一
塚村裕介
Original Assignee
東レ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 東レ株式会社 filed Critical 東レ株式会社
Priority to JP2015542499A priority Critical patent/JP6641627B2/ja
Publication of WO2016042992A1 publication Critical patent/WO2016042992A1/fr

Abstract

L'invention concerne un film réfléchissant qui est caractérisé par le fait qu'il présente, sur au moins une surface d'un film de base, une couche de résine qui contient des particules de polyéthylène ayant un poids moléculaire moyen en viscosité de 10 000 ou plus et un point de fusion de 115 °C ou plus. La présente invention est en mesure de mettre en œuvre un film réfléchissant qui est supprimé par adhérence à un élément (par exemple, une plaque de guidage de lumière) qui vient en contact avec le film réfléchissant, tout en étant en mesure de supprimer les dommages (tels que des rayures et une contamination) sur l'élément de contact (par exemple, une plaque de guidage de lumière) et la contamination de l'élément de contact par la chaleur en même temps, et qui présente une bonne résistance à la chaleur (et subit peu de décoloration due à la chaleur).
PCT/JP2015/073964 2014-09-17 2015-08-26 Film réfléchissant, et unité de rétroéclairage à éclairage périphérique utilisant celui-ci WO2016042992A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
JP2015542499A JP6641627B2 (ja) 2014-09-17 2015-08-26 反射フィルムおよびそれを用いたエッジライト型バックライトユニット

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2014188733 2014-09-17
JP2014-188733 2014-09-17

Publications (1)

Publication Number Publication Date
WO2016042992A1 true WO2016042992A1 (fr) 2016-03-24

Family

ID=55533034

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2015/073964 WO2016042992A1 (fr) 2014-09-17 2015-08-26 Film réfléchissant, et unité de rétroéclairage à éclairage périphérique utilisant celui-ci

Country Status (3)

Country Link
JP (1) JP6641627B2 (fr)
TW (1) TW201614276A (fr)
WO (1) WO2016042992A1 (fr)

Cited By (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019093217A1 (fr) * 2017-11-08 2019-05-16 東洋紡株式会社 Film de résine de polyéthylène
JPWO2021193789A1 (fr) * 2020-03-26 2021-09-30
JP7323266B2 (ja) 2017-11-30 2023-08-08 大日本印刷株式会社 波長変換シート用のバリアフィルム、波長変換シートおよびそれに用いられる表示装置

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2007229943A (ja) * 2006-02-27 2007-09-13 Nitto Denko Corp 多孔質シートの製造方法及びその製造方法により得られる多孔質シート
JP2007321143A (ja) * 2006-05-01 2007-12-13 Fujifilm Corp 水中油（ｏ／ｗ）型エマルション塗布組成物、積層体、偏光板、画像表示装置、及び積層体の製造方法
WO2010101214A1 (fr) * 2009-03-06 2010-09-10 国立大学法人 群馬大学 Procédé de production d'un film en polyéthylène de poids moléculaire extrêmement élevé
WO2011105294A1 (fr) * 2010-02-24 2011-09-01 東レ株式会社 Film réfléchissant blanc pour rétroéclairage à éclairage latéral et rétroéclairage utilisant le film précité
JP2012159610A (ja) * 2011-01-31 2012-08-23 Teijin Dupont Films Japan Ltd 反射フィルム
JP2013205599A (ja) * 2012-03-28 2013-10-07 Panasonic Corp 映写用スクリーン及びこれを用いたホワイトボード装置

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP5255287B2 (ja) * 2008-01-30 2013-08-07 帝人株式会社 多孔膜の製造方法

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2007229943A (ja) * 2006-02-27 2007-09-13 Nitto Denko Corp 多孔質シートの製造方法及びその製造方法により得られる多孔質シート
JP2007321143A (ja) * 2006-05-01 2007-12-13 Fujifilm Corp 水中油（ｏ／ｗ）型エマルション塗布組成物、積層体、偏光板、画像表示装置、及び積層体の製造方法
WO2010101214A1 (fr) * 2009-03-06 2010-09-10 国立大学法人 群馬大学 Procédé de production d'un film en polyéthylène de poids moléculaire extrêmement élevé
WO2011105294A1 (fr) * 2010-02-24 2011-09-01 東レ株式会社 Film réfléchissant blanc pour rétroéclairage à éclairage latéral et rétroéclairage utilisant le film précité
JP2012159610A (ja) * 2011-01-31 2012-08-23 Teijin Dupont Films Japan Ltd 反射フィルム
JP2013205599A (ja) * 2012-03-28 2013-10-07 Panasonic Corp 映写用スクリーン及びこれを用いたホワイトボード装置

Cited By (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019093217A1 (fr) * 2017-11-08 2019-05-16 東洋紡株式会社 Film de résine de polyéthylène
CN111315805A (zh) * 2017-11-08 2020-06-19 东洋纺株式会社 聚乙烯系树脂膜
JPWO2019093217A1 (ja) * 2017-11-08 2020-12-10 東洋紡株式会社 ポリエチレン系樹脂フィルム
JP7200943B2 (ja) 2017-11-08 2023-01-10 東洋紡株式会社 ポリエチレン系樹脂フィルム
CN111315805B (zh) * 2017-11-08 2023-04-11 东洋纺株式会社 聚乙烯系树脂膜
JP7323266B2 (ja) 2017-11-30 2023-08-08 大日本印刷株式会社 波長変換シート用のバリアフィルム、波長変換シートおよびそれに用いられる表示装置
JPWO2021193789A1 (fr) * 2020-03-26 2021-09-30
WO2021193789A1 (fr) * 2020-03-26 2021-09-30 日東電工株式会社 Élément optique, et unité de rétroéclairage et dispositif d'affichage d'image à l'aide dudit élément optique
JP7389228B2 (ja) 2020-03-26 2023-11-29 日東電工株式会社 光学部材ならびに該光学部材を用いたバックライトユニットおよび画像表示装置
US11994709B2 (en) 2020-03-26 2024-05-28 Nitto Denko Corporation Optical member, and backlight unit and image display device using said optical member

Also Published As

Publication number Publication date
TW201614276A (en) 2016-04-16
JPWO2016042992A1 (ja) 2017-06-29
JP6641627B2 (ja) 2020-02-05

Similar Documents

Publication Publication Date Title
JP6485758B2 (ja) 液晶ディスプレイのエッジライト型バックライト用白色反射フィルム及びそれを用いたバックライト
TW200829962A (en) White polyester film for light reflecting plate
JP2009210911A (ja) 光学用積層シート及び画像表示装置
TW200937044A (en) Anti-glare film, anti-glare polarizing plate, and image display device
JP2008074083A (ja) 光学用積層シート及び画像表示装置
WO2016042992A1 (fr) Film réfléchissant, et unité de rétroéclairage à éclairage périphérique utilisant celui-ci
TW201126242A (en) Viewing angle enhancement film for liquid crystal display device, protect film with function of viewing angle enhancement, and liquid crystal display device
JP5532799B2 (ja) 白色反射フィルム
WO2016204234A1 (fr) Film de réflexion et unité de réflexion pour dispositif de source de lumière de surface
JP6226024B2 (ja) 反射フィルムを用いたエッジライト型バックライトユニット
KR101580346B1 (ko) 광 확산 필름 및 그것을 구비한 장치
TWI676551B (zh) 積層薄膜
KR102590694B1 (ko) 백색 반사 필름
JP2017044718A (ja) 反射フィルムおよびそれを用いたエッジライト型バックライト
WO2010073611A1 (fr) Réflecteur de lumière et appareil superficiel pour source de lumière
JP2017090560A (ja) 反射フィルムおよびそれを用いたエッジライト型バックライトユニット
KR100744842B1 (ko) 액정 디스플레이의 백라이트 유니트용 고휘도 광확산 시트및 그 제조방법
JP2008282010A (ja) 光拡散板
TW202228998A (zh) 成形用膜
JP2020011430A (ja) 反射材
WO2015163363A1 (fr) Film de réflexion de rétro-éclairage du type à émission latérale et rétro-éclairage comprenant ce dernier
JP2017134146A (ja) エッジライト型バックライト用反射フィルム及びそれを用いた液晶ディスプレイ用バックライト

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2015542499

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 15842819

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 15842819

Country of ref document: EP

Kind code of ref document: A1