WO2015096549A1 - Procédé et appareil pour extraire du lithium de qualité pour batterie à partir de saumure - Google Patents

Procédé et appareil pour extraire du lithium de qualité pour batterie à partir de saumure Download PDF

Info

Publication number
WO2015096549A1
WO2015096549A1 PCT/CN2014/089736 CN2014089736W WO2015096549A1 WO 2015096549 A1 WO2015096549 A1 WO 2015096549A1 CN 2014089736 W CN2014089736 W CN 2014089736W WO 2015096549 A1 WO2015096549 A1 WO 2015096549A1
Authority
WO
WIPO (PCT)
Prior art keywords
brine
lithium
membrane
concentration
battery grade
Prior art date
Application number
PCT/CN2014/089736
Other languages
English (en)
Chinese (zh)
Inventor
彭文博
王肖虎
熊福军
张桂花
曹恒霞
项娟
张宏
Original Assignee
江苏久吾高科技股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from CN201310731430.6A external-priority patent/CN103738984B/zh
Priority claimed from CN201410353274.9A external-priority patent/CN104313348B/zh
Priority claimed from CN201410555213.0A external-priority patent/CN104310446B/zh
Application filed by 江苏久吾高科技股份有限公司 filed Critical 江苏久吾高科技股份有限公司
Publication of WO2015096549A1 publication Critical patent/WO2015096549A1/fr

Abstract

La présente invention concerne un procédé et un appareil pour extraire du lithium de qualité pour batterie à partir de saumure. Le procédé comprend les étapes suivantes : étape 1, absorption de la saumure avec un agent d'adsorption de lithium et ensuite, désorption de l'agent d'adsorption de lithium avec un éluant pour obtenir une solution de désorption ; étape 2, élimination du magnésium de la solution de désorption pour obtenir la solution de désorption avec le magnésium éliminé ; étape 3, concentration de la solution de désorption avec le magnésium éliminé, pour obtenir une saumure concentrée contenant du lithium. L'appareil comprend un dispositif d'adsorption-désorption (1), un dispositif d'élimination de magnésium (2), et un dispositif de concentration (3), une sortie de la solution de désorption du dispositif d'adsorption-désorption (1) étant raccordée à une entrée du dispositif d'élimination de magnésium (2), une sortie du dispositif d'élimination de magnésium (2) étant raccordée à une entrée du dispositif de concentration (3), et une sortie de la solution concentrée du dispositif de concentration (3) étant raccordée à une première cuve de précipitation (4) ; la première cuve de précipitation (4) étant également pourvue d'une première cuve de carbonate de sodium (5), et une sortie de la première cuve de précipitation (4) étant également raccordée à un deuxième séparateur solide-liquide (6).
PCT/CN2014/089736 2013-12-26 2014-10-28 Procédé et appareil pour extraire du lithium de qualité pour batterie à partir de saumure WO2015096549A1 (fr)

Applications Claiming Priority (6)

Application Number Priority Date Filing Date Title
CN201310731430.6A CN103738984B (zh) 2013-12-26 2013-12-26 一种盐卤氯化锂的提取方法及装置
CN201310731430.6 2013-12-26
CN201410353274.9A CN104313348B (zh) 2014-07-23 2014-07-23 一种吸附法提取盐湖卤水中锂的方法
CN201410353274.9 2014-07-23
CN201410555213.0 2014-10-17
CN201410555213.0A CN104310446B (zh) 2014-10-17 2014-10-17 一种由卤水提取电池级锂的工艺及装置

Publications (1)

Publication Number Publication Date
WO2015096549A1 true WO2015096549A1 (fr) 2015-07-02

Family

ID=53477498

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/CN2014/089736 WO2015096549A1 (fr) 2013-12-26 2014-10-28 Procédé et appareil pour extraire du lithium de qualité pour batterie à partir de saumure

Country Status (1)

Country Link
WO (1) WO2015096549A1 (fr)

Cited By (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN104961143A (zh) * 2015-07-03 2015-10-07 青海恒信融锂业科技有限公司 从盐湖卤水中提取锂的方法
CN109607578A (zh) * 2019-01-03 2019-04-12 青海中信国安锂业发展有限公司 一种从硫酸镁亚型盐湖卤水中提取电池级碳酸锂的方法
CN111268702A (zh) * 2019-12-30 2020-06-12 江苏久吾高科技股份有限公司 一种利用膜分离技术制备电池级碳酸锂的方法及装置
CN112079368A (zh) * 2019-06-12 2020-12-15 中能实用小微科学科技有限公司 多级回收的低能耗高纯度提取锂的方法
CN112142076A (zh) * 2020-09-08 2020-12-29 中国科学院青海盐湖研究所 一种吸附法从卤水中提取锂的方法
WO2020257937A1 (fr) * 2019-06-27 2020-12-30 Summit Nanotech Corporation Système et procédé de traitement et de concentration d'ions sélectionnés dans des solutions de saumure
WO2021053514A1 (fr) 2019-09-16 2021-03-25 InCoR Lithium Extraction sélective de lithium à partir de saumures
CN112919505A (zh) * 2021-03-03 2021-06-08 中国恩菲工程技术有限公司 盐湖富锂卤水连续生产氢氧化锂的装置及方法
CN113501587A (zh) * 2021-07-29 2021-10-15 德兰梅勒（北京）分离技术股份有限公司 一种吸附剂解析液的处理方法及处理系统
CN113577799A (zh) * 2021-07-20 2021-11-02 山东菜央子盐场有限公司 Mvr热泵蒸发制盐在多效真空制盐工艺技术中的运用方法
US11174532B1 (en) 2018-03-09 2021-11-16 Terralithium Llc Processes for producing lithium compounds using reverse osmosis
WO2021248221A1 (fr) * 2020-06-08 2021-12-16 Standard Lithium Ltd. Procédé de récupération de lithium à partir de saumure
US11235282B2 (en) * 2018-03-09 2022-02-01 Terralithium Llc Processes for producing lithium compounds using forward osmosis
CN114752785A (zh) * 2022-04-12 2022-07-15 厦门世达膜科技有限公司 一种无机吸附剂与连续流体分离组合工艺技术在卤水提锂中的应用
CN115161497A (zh) * 2022-07-11 2022-10-11 西宁永正锂业有限公司 一种高硫酸盐原卤的铝系吸附剂提锂方法
CN115490246A (zh) * 2022-09-22 2022-12-20 青海锂业有限公司 一种盐湖卤水制备高端锂电正极材料的除杂设备及方法
CN115558798A (zh) * 2021-07-02 2023-01-03 浙江新化化工股份有限公司 锂化合物的制备方法
CN115595455A (zh) * 2021-06-28 2023-01-13 中石化南京化工研究院有限公司（Cn） 一种用于低品位卤水提锂的系统及方法、应用
US11578414B2 (en) 2019-09-25 2023-02-14 Ecostar-Nautech Co., Ltd. Method for producing lithium hydroxide monohydrate from brines
CN115786732A (zh) * 2022-11-11 2023-03-14 湖北金泉新材料有限公司 一种从黏土型锂矿中提取锂资源的方法
CN115784271A (zh) * 2022-12-01 2023-03-14 紫金矿业集团股份有限公司 一种高钙镁型卤水浓缩结晶盐夹带锂的回收方法
CN116282087A (zh) * 2023-01-13 2023-06-23 格尔木藏格锂业有限公司 一种硫酸盐型盐湖卤水制备电池级碳酸锂的工艺方法

Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1425610A (zh) * 2003-01-13 2003-06-25 化学工业部连云港设计研究院 一种降低高镁锂比卤水镁锂比值的方法
CN1511963A (zh) * 2002-12-27 2004-07-14 中国科学院青海盐湖研究所 二氧化锰法从盐湖卤水中提锂的方法
CN1511964A (zh) * 2002-12-27 2004-07-14 中国科学院青海盐湖研究所 吸附法从盐湖卤水中提取锂的方法
CN101928828A (zh) * 2010-09-25 2010-12-29 西安蓝晓科技有限公司 一种吸附法从盐湖卤水中提取锂的方法
CN102432044A (zh) * 2011-09-26 2012-05-02 江苏海龙锂业科技有限公司 从高镁锂比盐湖卤水中提取超高纯度碳酸锂的方法

Patent Citations (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN1511963A (zh) * 2002-12-27 2004-07-14 中国科学院青海盐湖研究所 二氧化锰法从盐湖卤水中提锂的方法
CN1511964A (zh) * 2002-12-27 2004-07-14 中国科学院青海盐湖研究所 吸附法从盐湖卤水中提取锂的方法
CN1425610A (zh) * 2003-01-13 2003-06-25 化学工业部连云港设计研究院 一种降低高镁锂比卤水镁锂比值的方法
CN101928828A (zh) * 2010-09-25 2010-12-29 西安蓝晓科技有限公司 一种吸附法从盐湖卤水中提取锂的方法
CN102432044A (zh) * 2011-09-26 2012-05-02 江苏海龙锂业科技有限公司 从高镁锂比盐湖卤水中提取超高纯度碳酸锂的方法

Cited By (29)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN104961143A (zh) * 2015-07-03 2015-10-07 青海恒信融锂业科技有限公司 从盐湖卤水中提取锂的方法
US11174532B1 (en) 2018-03-09 2021-11-16 Terralithium Llc Processes for producing lithium compounds using reverse osmosis
US11235282B2 (en) * 2018-03-09 2022-02-01 Terralithium Llc Processes for producing lithium compounds using forward osmosis
CN109607578A (zh) * 2019-01-03 2019-04-12 青海中信国安锂业发展有限公司 一种从硫酸镁亚型盐湖卤水中提取电池级碳酸锂的方法
CN112079368A (zh) * 2019-06-12 2020-12-15 中能实用小微科学科技有限公司 多级回收的低能耗高纯度提取锂的方法
WO2020257937A1 (fr) * 2019-06-27 2020-12-30 Summit Nanotech Corporation Système et procédé de traitement et de concentration d'ions sélectionnés dans des solutions de saumure
WO2021053514A1 (fr) 2019-09-16 2021-03-25 InCoR Lithium Extraction sélective de lithium à partir de saumures
US11634789B2 (en) 2019-09-16 2023-04-25 InCoR Lithium Selective lithium extraction from brines
US11578414B2 (en) 2019-09-25 2023-02-14 Ecostar-Nautech Co., Ltd. Method for producing lithium hydroxide monohydrate from brines
CN111268702A (zh) * 2019-12-30 2020-06-12 江苏久吾高科技股份有限公司 一种利用膜分离技术制备电池级碳酸锂的方法及装置
WO2021248221A1 (fr) * 2020-06-08 2021-12-16 Standard Lithium Ltd. Procédé de récupération de lithium à partir de saumure
CN112142076A (zh) * 2020-09-08 2020-12-29 中国科学院青海盐湖研究所 一种吸附法从卤水中提取锂的方法
CN112142076B (zh) * 2020-09-08 2022-06-24 中国科学院青海盐湖研究所 一种吸附法从卤水中提取锂的方法
CN112919505A (zh) * 2021-03-03 2021-06-08 中国恩菲工程技术有限公司 盐湖富锂卤水连续生产氢氧化锂的装置及方法
CN112919505B (zh) * 2021-03-03 2022-12-06 中国恩菲工程技术有限公司 盐湖富锂卤水连续生产氢氧化锂的装置及方法
CN115595455B (zh) * 2021-06-28 2023-12-19 中国石油化工股份有限公司 一种用于低品位卤水提锂的系统及方法、应用
CN115595455A (zh) * 2021-06-28 2023-01-13 中石化南京化工研究院有限公司（Cn） 一种用于低品位卤水提锂的系统及方法、应用
CN115558798B (zh) * 2021-07-02 2023-12-01 浙江新化化工股份有限公司 锂化合物的制备方法
CN115558798A (zh) * 2021-07-02 2023-01-03 浙江新化化工股份有限公司 锂化合物的制备方法
CN113577799A (zh) * 2021-07-20 2021-11-02 山东菜央子盐场有限公司 Mvr热泵蒸发制盐在多效真空制盐工艺技术中的运用方法
CN113501587A (zh) * 2021-07-29 2021-10-15 德兰梅勒（北京）分离技术股份有限公司 一种吸附剂解析液的处理方法及处理系统
CN114752785A (zh) * 2022-04-12 2022-07-15 厦门世达膜科技有限公司 一种无机吸附剂与连续流体分离组合工艺技术在卤水提锂中的应用
CN114752785B (zh) * 2022-04-12 2023-09-29 厦门世达膜科技有限公司 一种无机吸附剂与连续流体分离组合工艺在卤水提锂中的应用
CN115161497A (zh) * 2022-07-11 2022-10-11 西宁永正锂业有限公司 一种高硫酸盐原卤的铝系吸附剂提锂方法
CN115161497B (zh) * 2022-07-11 2024-02-13 衢州永正锂业科技有限公司 一种高硫酸盐原卤的铝系吸附剂提锂方法
CN115490246A (zh) * 2022-09-22 2022-12-20 青海锂业有限公司 一种盐湖卤水制备高端锂电正极材料的除杂设备及方法
CN115786732A (zh) * 2022-11-11 2023-03-14 湖北金泉新材料有限公司 一种从黏土型锂矿中提取锂资源的方法
CN115784271A (zh) * 2022-12-01 2023-03-14 紫金矿业集团股份有限公司 一种高钙镁型卤水浓缩结晶盐夹带锂的回收方法
CN116282087A (zh) * 2023-01-13 2023-06-23 格尔木藏格锂业有限公司 一种硫酸盐型盐湖卤水制备电池级碳酸锂的工艺方法

Similar Documents

Publication Publication Date Title
WO2015096549A1 (fr) Procédé et appareil pour extraire du lithium de qualité pour batterie à partir de saumure
CN104310446B (zh) 一种由卤水提取电池级锂的工艺及装置
CN204162442U (zh) 一种由卤水提取电池级锂的装置
CN104313348B (zh) 一种吸附法提取盐湖卤水中锂的方法
JP3883491B2 (ja) リチウム含有水溶液からのリチウム濃縮液の製造方法
KR101351223B1 (ko) 해수 중의 금속이온 회수 공정
CN103738984B (zh) 一种盐卤氯化锂的提取方法及装置
JP2021120350A (ja) 高不純度リチウム源からバッテリーグレード及び高純度グレードの水酸化リチウム及び炭酸リチウムを生成するシステム
CN109692581B (zh) 二维层状Ti3C2膜及其制备方法与应用
CN109368742B (zh) 剩余污泥中胞外聚合物回收以及重金属离子去除的方法
JP2013535573A (ja) リチウム含有溶液からリチウムを経済的に抽出する方法
CN105540970B (zh) 中水回用反渗透浓水近零排放膜法集成处理的工艺
CN111527046A (zh) 磷酸锂的制备方法、氢氧化锂的制备方法及碳酸锂的制备方法
CN103585896A (zh) 一种层状硫化钼纳米片分子分离膜的制备方法
US10273160B2 (en) Graphene oxide purification method and graphene oxide
CN111620458A (zh) 一种卤水浓缩和软化处理的方法及装置
CN113511663A (zh) 一种油田地下卤水提锂制备碳酸锂工艺
CN112593094A (zh) 一种盐湖提锂的工艺及装置
CN107010701B (zh) 利用电容去离子技术分离富集五价钒的方法
JP7128546B2 (ja) リチウム鉱石から炭酸リチウムを調製するための方法およびシステム
CN203741054U (zh) 一种盐卤氯化锂的提取装置
CN107416871A (zh) 一种基于二氧化碳二次碳化的电池级碳酸锂的制备方法
KR20130078174A (ko) 해수 내 리튬을 회수하는 방법
CN213652069U (zh) 一种卤水浓缩和软化处理的装置及盐湖卤水的提锂装置
CN212954669U (zh) 一种多级过滤净水系统及净水器

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 14873336

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 14873336

Country of ref document: EP

Kind code of ref document: A1