WO2014209074A1 - 광학용 점착 필름, 광학용 점착 필름의 제조 방법 및 이를 포함하는 터치 스크린 패널 - Google Patents

광학용 점착 필름, 광학용 점착 필름의 제조 방법 및 이를 포함하는 터치 스크린 패널 Download PDF

Info

Publication number
WO2014209074A1
WO2014209074A1 PCT/KR2014/005770 KR2014005770W WO2014209074A1 WO 2014209074 A1 WO2014209074 A1 WO 2014209074A1 KR 2014005770 W KR2014005770 W KR 2014005770W WO 2014209074 A1 WO2014209074 A1 WO 2014209074A1
Authority
WO
WIPO (PCT)
Prior art keywords
adhesive film
optical adhesive
layered clay
plate
clay compound
Prior art date
Application number
PCT/KR2014/005770
Other languages
English (en)
French (fr)
Inventor
윤찬오
박성찬
김장순
박은경
정부기
김원호
Original Assignee
(주)엘지하우시스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)엘지하우시스 filed Critical (주)엘지하우시스
Priority to JP2016523654A priority Critical patent/JP6523270B2/ja
Priority to EP14818577.0A priority patent/EP3015518B1/en
Priority to US14/899,122 priority patent/US10227510B2/en
Priority to CN201480037210.6A priority patent/CN105378012B/zh
Publication of WO2014209074A1 publication Critical patent/WO2014209074A1/ko

Abstract

판상형 무기 나노입자 및 경화성 수지를 포함하는 광학용 점착 필름을 제공한다. 상기 광학용 점착 필름은 수분 및 가스에 대한 배리어 특성 및 광 투과율이 향상되고, 내구성 및 박리 특성이 우수하다.

Description

광학용 점착 필름, 광학용 점착 필름의 제조 방법 및 이를 포함하는 터치 스크린 패널
광학용 점착 필름, 광학용 점착 필름의 제조 방법 및 이를 포함하는 터치 스크린 패널에 관한 것이다.
근래, PDA, 이동통신 단말기 또는 차량용 네비게이션 등과 같은 전자 기기가 큰 시장을 형성하고 있다. 이러한 전자 기기는 입력 조작부에 터치스크린 또는 터치패널 스위치가 설치되는 경우, 경량화 및 깨짐 방지 등을 위하여, 투명 도전성 플라스틱 필름이 사용되고 있다. 그 예로는, 폴리에틸렌테레프탈레이트 (PET) 필름을 기재로 하고, 그 일면에 인듐 주석 산화물 (Indium Tin Oxide, ITO) 등의 도전층을 형성한 투명 도전성 필름이 있으며, 상기 투명 도전성 필름은 점착제층에 의해 전도성 유리, 보강재 또는 데코 필름 등에 적층된다.
본 발명의 일 구현예는 수분 및 가스에 대한 배리어 특성을 향상시킨 광학용 점착 필름을 제공한다.
본 발명의 다른 구현예는 상기 광학용 점착 필름을 제조하는 방법을 제공한다.
본 발명의 또 다른 구현예는 상기 광학용 점착 필름을 포함하는 터치 스크린 패널을 제공한다.
본 발명의 일 구현예에서, 판상형 무기 나노입자 및 경화성 수지를 포함하는 광학용 점착 필름을 제공한다.
상기 판상형 무기 나노입자는 두께 약 1 nm 내지 약 100 nm의 판상 형태일 수 있다.
상기 판상형 무기 나노입자는 두께 대 판상의 장경의 비가 약 1 : 50 내지 약 1 : 200일 수 있다.
상기 판상형 무기 나노입자는 층상 점토 화합물을 구성하는 적어도 하나의 층을 포함할 수 있다.
상기 층상 점토 화합물은 친수성 작용기가 C12-C18 알킬기로 치환된 것일 수 있다.
상기 층상 점토 화합물은 마이카(Mica), 스멕타이트(Smectite), 버미큘라이트(Virmiculite), 클로라이트(Clorite), 몬모릴로나이트(Montmorillonite, MMT), 논트로나이트(Nontronite), 사포나이트(saponite), 헥토나이트(Hectorite), 벤토나이트(Bentonite) 및 이들의 조합으로 이루어진 군으로부터 선택된 하나를 포함할 수 있다.
상기 경화성 수지는 2-에틸헥실아크릴레이트(2-EHA, ethyl hexyl acylate), 이소보닐아크릴레이트(IBOA, isobonyl acrylate), 히드록시에틸아크릴레이트(HEA, hydroxy ethyl acrylate), 히드록시부틸아크릴레이트(HBA, hydroxyl butyl acrylate), 히드록시프로필아크릴레이트(HPA, hydroxyl propyl acryalte), 헥실메타크릴레이트(HMA, Hexyl methacrylate) 및 이들의 조합으로 이루어진 군으로부터 선택된 하나를 포함하는 모노머가 중합된 아크릴계 광경화성 수지일 수 있다.
상기 층상 점토 화합물은 상기한 예시의 층상 점토 화합물의 친수성 작용기가 C12-C18 알킬기로 치환된 것일 수 있다.
상기 경화성 수지 100 중량부 및 상기 층상 점토 화합물 약 1 내지 약 20 중량부 포함할 수 있다.
상기 경화성 수지의 매트릭스 내에 상기 층상 점토 화합물이 상기 광학용 점착 필름의 면과 평행한 방향으로 배치되도록 배향성을 갖도록 분산될 수 있다.
CuKα선을 사용한 X선 회절(XRD) 패턴을 측정한 결과 약 2 내지 약 10도의 2θ 값에서 피크가 존재하지 않을 수 있다.
상기 광학용 점착 필름은 투과율이 약 91 내지 약 93%이고, 수분 투습도 (WVTR) 값이 약 50℃에서 약 24hr 동안 방치한 후 측정시 약 10gmm/m2 내지 80gmm/m2일 수 있다.
상기 광학용 점착 필름은 인성이 약 2.0 Kg/mm2 내지 약 5.0 Kg/mm2이고, 상온에서 측정한 모듈러스(modulus, Pa) 약 0.5 × 105 Pa 내지 약 1.3 × 105 Pa 및 박리 강도 약 2.0 kg/in 내지 약 3.5 kg/in일 수 있다.
본 발명의 다른 구현예에서, 유기 치환된 소수성의 층상 점토 화합물과 광학용 점착 필름 형성용 경화성 모노머를 혼합하여 상기 층상 점토 화합물의 층간에 상기 경화성 모노머가 개재되도록 혼합된 점착제 조성물을 준비하는 단계; 및 상기 점착제 조성물을 경화시켜 상기 층상 점토 화합물의 층간에 개재된 상기 경화성 모노머가 경화성 수지로 중합되면서 상기 층상 점토 화합물의 각 층을 형성하는 판상형 무기 나노입자를 박리하여, 상기 경화성 수지의 매트릭스 내에 상기 판상형 무기 나노입자가 분산된 광학용 점착 필름을 얻는 단계;를 포함하는 광학용 점착 필름의 제조 방법을 제공한다.
상기 층상 점토 화합물과 상기 경화성 모노머를 약 500 내지 약 10,000 rpm에서 약 5 내지 약 60분 동안 교반하여 혼합시킬 수 있다.
상기 유기 치환된 소수성의 층상 점토 화합물은 마이카(Mica), 스멕타이트(Smectite), 버미큘라이트(Virmiculite), 클로라이트(Clorite), 몬모릴로나이트(Montmorillonite, MMT), 논트로나이트(Nontronite), 사포나이트(saponite), 헥토나이트(Hectorite), 벤토나이트(Bentonite) 및 이들의 조합으로 이루어진 군으로부터 선택된 하나를 포함하고, 상기 층상 점토 화합물의 친수성 작용기가 C12-C18 알킬기로 치환된 것일 수 있다.
본 발명의 또 다른 구현예에서, 일면에 도전층이 형성된 전도성 플라스틱 필름; 및 상기 전도성 플라스틱 필름에 적층된, 상기 광학용 점착 필름;을 포함하는 터치 스크린 패널을 제공한다.
상기 전도성 플라스틱 필름이 ITO(도전성 금속 산화물)층이 일면에 형성된 폴리에틸렌테레프탈레이트 필름일 수 있다.
상기 광학용 점착 필름은 수분 및 가스에 대한 배리어 특성 및 광 투과율이 향상되고, 내구성 및 박리 특성이 우수하다.
도 1a와 1b는 본 발명의 일 구현예에 따른 광학용 점착 필름 및 판상형 무기 나노입자를 포함하지 않는 광학용 점착 필름의 각 단면을 나타내는 모식도이다.
도 2는 본 발명의 다른 구현예에 따른 광학용 점착 필름의 제조 방법의 모식적인 흐름도이다.
도 3은 실시예 1에서 제조된 광학용 점착 필름의 TEM 사진이다.
이하, 본 발명의 구현예를 상세히 설명하기로 한다. 다만, 이는 예시로서 제시되는 것으로, 이에 의해 본 발명이 제한되지는 않으며 본 발명은 후술할 청구항의 범주에 의해 정의될 뿐이다.
본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 동일 또는 유사한 구성요소에 대해서는 동일한 참조 부호를 붙이도록 한다.
도면에서 여러 층 및 영역을 명확하게 표현하기 위하여 두께를 확대하여 나타내었다. 그리고 도면에서, 설명의 편의를 위해, 일부 층 및 영역의 두께를 과장되게 나타내었다.
이하에서 기재의 “상부 (또는 하부)” 또는 기재의 “상 (또는 하)”에 임의의 구성이 형성된다는 것은, 임의의 구성이 상기 기재의 상면 (또는 하면)에 접하여 형성되는 것을 의미할 뿐만 아니라, 상기 기재와 기재 상에 (또는 하에) 형성된 임의의 구성 사이에 다른 구성을 포함하지 않는 것으로 한정하는 것은 아니다.
본 발명의 일 구현예에서, 판상형 무기 나노입자 및 경화성 수지를 포함하는 광학용 점착 필름을 제공한다.
상기 판상형 무기 나노입자는 약 1nm 내지 약 100nm의 판상 형태 나노 입자로서, 상기 광학용 점착 필름에 포함되어 물성을 보강할 수 있다.
상기 판상형 무기 나노입자는 두께 대 판상의 장경의 비가 약 1 : 50 내지 약 1 : 200일 수 있다. 상기 광학용 점착 필름은 상기 범위 내의 형태비를 갖는 판상형 무기 나노입자를 포함하여 적정한 길이의 수분 침투 유로를 확보할 수 있게 되어 우수한 가스 배리어 특성을 부여하고, 또한 우수한 분산성을 가지게 할 수 있다.
상기 광학용 점착 필름은 수분 및 가스에 대한 배리어 특성이 향상된다. 일 구현예에서, 상기 판상형 무기 나노입자는 상기 광학용 점착 필름의 면과 평행한 방향으로 배치되도록 배향성을 갖도록 분산되어 이러한 배리어 특성이 보다 향상될 수 있다. 이는 후술되는 제조 방법에 의해 구현될 수 있다.
도 1은 상기 광학용 점착 필름의 단면을 나타내는 모식도이다. 도 1(a)에서 상기 광학용 점착 필름(100)은 상기 판상형 무기 나노입자(20)가 포함되어 수분 및 가스의 침투 유로 (A)가 도 1(b)의 판상형 무기 나노입자를 포함하지 않는 광학용 점착 필름(200)의 침투 유로(B)보다 길어지기 때문에, 수분 및 가스에 대한 배리어 특성을 향상시킬 수 있다.
일 구현예에서, 상기 광학용 점착 필름은 수분 투습도 (WVTR) 값이 약 50℃에서 약 24hr 동안 방치한 후 측정시 약 10 gmm/m2 내지 80gmm/m2 일 수 있다.
상기 광학용 점착 필름은 터치 스크린 패널에 적용시 전도성 플라스틱 필름이 함께 적층되는데 침투된 수분 및 가스에 의해 전도성 물질, 예를 들어 ITO가 산화 될 수 있다. 상기 광학용 점착 필름은 이와 같이 수분 및 가스에 대한 배리어 특성이 향상되기 때문에 터치 스크린 패널에 적용시 함께 적층되는 전도성 플라스틱 필름 중의 전도성 물질, 예를 들어 ITO의 산화반응을 억제할 수 있다.
상기 판상형 무기 나노입자는 상기 광학용 점착 필름에 포함시 경화성 수지의 경화 특성을 저해하지 않으며, 또한, 상기 판상형 무기 나노입자의 판상의 두께가 나노 크기이어서 빛의 투과율을 감소시키지 않으면서도 빛의 보강 간섭을 유도하여 반사율을 감소시킴으로써 투과율 향상을 유도할 수 있다. 일 구현예에서, 상기 광학용 점착 필름은 투과율이 약 91 내지 93%를 유지할 수 있다.
상기 광학용 점착 필름은 상기 판상형 무기 나노입자를 포함함으로써 나노 입자가 분산되어 연신 특성이 우수하고, 응집력이 높아서 제거시 잔사가 남지 않는 광학용 점착 필름을 구현할 수 있다. 즉, 상기 광학용 점착 필름은 강도, 모듈러스 등의 기계적 강도가 상승하고, 열안정성이 향상되어, 박리력이 향상된다. 일 구현예에서, 상기 광학용 점착 필름은 인성이 약 2.0 Kg/mm2 내지 5.0 Kg/mm2, 상온 측정 모듈러스(modulus) 약 0.5 × 105 Pa 내지 약 1.3 × 105 Pa 및 박리 강도 약 2.0 kg/in 내지 약 3.5 kg/in 일 수 있다.
상기 광학용 점착 필름은 상기 경화성 수지 100 중량부 및 상기 층상 점토 화합물 약 0.1 내지 약 20 중량부, 구체적으로 약 0.1 내지 약 10 중량부 포함할 수 있다. 상기 함량비를 갖도록 하여 전술한 광학용 점착 필름의 물성 밸런스를 얻을 수 있다.
상기 판상형 무기 나노입자는 층상 점토 화합물을 구성하는 적어도 하나의 층으로부터 형성될 수 있다.
상기 광학용 점착 필름은 먼저 유기 치환된 소수성의 층상 점토 화합물과 광학용 점착 필름 형성용 경화성 모노머를 혼합하여 상기 층상 점토 화합물의 층간에 상기 경화성 모노머가 개재되도록 혼합하여 점착제 조성물을 준비한 다음, 상기 점착제 조성물을 경화시키면, 상기 층상 점토 화합물의 층간에 개재된 상기 경화성 모노머가 경화성 수지로 중합되면서 그 부피가 커지게 되어서 상기 층상 점토 화합물의 층이 박리되게 된다. 이로써 상기 층상 점토 화합물의 박리된 층이 상기 경화성 수지의 매트릭스에 분산되어 상기 광학용 점착 필름을 형성할 수 있다.
상기 층상 점토 화합물의 박리된 층이 상기 판상형 무기 나노입자이므로, 상기 경화성 수지의 매트릭스에 상기 판상형 무기 나노입자가 분산된 형태로 상기 광학용 점착 필름이 형성된다. 따라서, 상기 판상형 무기 나노입자는 층상 점토 화합물을 구성하는 적어도 하나의 층을 포함할 수 있다.
본 발명의 다른 구현예에서, 유기 치환된 소수성의 층상 점토 화합물과 광학용 점착 필름 형성용 경화성 모노머를 혼합하여 상기 층상 점토 화합물의 층간에 상기 경화성 모노머가 개재되도록 혼합된 점착제 조성물을 준비하는 단계; 및 상기 점착제 조성물을 경화시켜 상기 층상 점토 화합물의 층간에 개재된 상기 경화성 모노머가 경화성 수지로 중합되면서 상기 층상 점토 화합물의 각 층을 형성하는 판상형 무기 나노입자를 박리하여, 상기 경화성 수지의 매트릭스 내에 상기 판상형 무기 나노입자가 분산된 광학용 점착 필름을 얻는 단계;를 포함하는 상기 광학용 점착 필름의 제조 방법을 제공한다.
전술한 상기 광학용 점착 필름의 물성, 즉, 강도, 모듈러스 등의 기계적 강도,, 열안정성, 박리력 등을 우수하게 구현하기 위해서, 층상 점토 화합물의 층간이 박리된 판상형 무기 나노입자를 경화성 수지의 매트릭스 내에 잘 분산되게 하여야 한다.
경화성 수지의 매트릭스 내에 층상 점토 화합물의 층간이 박리된 판상형 무기 나노입자를 잘 분산시키기 위해서는 층상 점토 화합물의 층간에 경화성 모노머를 잘 혼합하여야 한다. 예를 들어, 상기 층상 점토 화합물과 상기 경화성 모노머를 약 500 내지 약 10,000 rpm에서 약 5 내지 약 60분 동안 교반하여 혼합시킬 수 있다.
상기 층상 점토 화합물은, 예를 들어, 마이카(Mica), 스멕타이트(Smectite), 버미큘라이트(Virmiculite), 클로라이트(Clorite), 몬모릴로나이트(Montmorillonite, MMT), 논트로나이트(Nontronite), 사포나이트(saponite), 헥토나이트(Hectorite), 벤토나이트(Bentonite) 및 이들의 조합으로 이루어진 군으로부터 선택된 하나를 사용할 수 있다.
상기 층상 점토 화합물은 소수성으로 개질하기 위하여 함유된 친수성 작용기를 소수성 부여 치환기, 예를 들어, C12-C18 알킬기로 치환하여 유기 치환된 소수성의 층상 점토 화합물을 얻을 수 있다.
이어서, 상기 유기 치환된 소수성의 층상 점토 화합물을 경화성 모노머와 혼합하게 되면, 층상 점토 화합물의 층간에 경화성 모노머가 개재된다. 이후, 층상 점토 화합물의 층간에 개재된 경화성 모노머를 경화시키면 전술한 바와 같이 상기 경화성 모노머가 3차원 망목 구조의 경화성 수지로 중합되기 때문에 그 부피가 커지게 되면서 상기 층상 점토 화합물의 층 간을 벌어지게 하고 그에 따라 층이 박리되게 된다.
상기 박리된 층 간의 간격에 따라서 점착물성, 광학물성, 기계적 물성 등이 향상되거나, 변하는 것을 볼수 있다. 완전히 분리된 상태를 박리 상태(exfoliation state)라고 칭하는데, 이때 투명한 광학적 특성을 얻을 수 있으며, 형상비에 따라 보강재 효과를 얻을 수 있어 점착필름의 인장강도를 비롯한 기계적 물성이 약 5 내지 약 20% 이상 향상되는 결과를 얻을 수 있다. 또한, 형상비가 높을수록 가스 입자의 통과 유로가 길어져 배리어 특성이 향상되는 효과를 얻을 수 있다.
상기 박리된 층 간의 간격은 상기 광학용 점착 필름 내의 상기 판상형 무기 나노입자의 분산의 정도와 관계되고, 이는 XRD 측정시 피크의 위치 값에 영향의 준다. 일 구현예에서, 상기 광학용 점착 필름에 대한 CuKα선을 사용한 X선 회절(XRD) 패턴에서 약 2 내지 약 10도의 2θ 값에서 피크값이 사라지는 것을 볼 수 있다. 이는 분산이 잘 이루어짐을 의미한다.
상기와 같이 제조된 광학용 점착 필름은 상기 경화성 수지의 매트릭스 내에 상기 층상 점토 화합물이 배향성을 가지면서 분산될 수 있다.
도 2는 전술한 광학용 점착 필름을 제조하는 방법의 모식적인 흐름도이다.
상기 광학용 점착 필름은 표시 장치의 스크린 또는 패널 등에 유용하게 적용될 수 있고, 상기 경화성 모노머는 광학적으로 투명한 점착제층 (OCA, optically clear adhesive layer)으로 형성되도록 공지된 조성을 사용할 수 있다.
구체적으로, 상기 경화성 수지는 2-에틸헥실아크릴레이트(2-EHA, ethyl hexyl acylate), 이소보닐아크릴레이트(IBOA, isobonyl acrylate), 히드록시에틸아크릴레이트(HEA, hydroxy ethyl acrylate), 히드록시부틸아크릴레이트(HBA, hydroxyl butyl acrylate), 히드록시프로필아크릴레이트(HPA, hydroxyl propyl acryalte), 헥실메타크릴레이트(HMA, Hexyl methacrylate), 메틸아크릴레이트(Methyl acrylate), 부틸아크릴레이트(Butyl acrylate), 메틸메타아크릴레이트(Methyl metacylate) 및 이들의 조합으로 이루어진 군으로부터 선택된 하나를 포함하는 모노머가 중합된 아크릴계 광경화성 수지일 수 있고, 중합시 상기 모노머를 포함하는 점착제 조성물에, 광개시제, 경화제, 기타 첨가제 등을 더 포함시켜 중합할 수 있다.
상기와 같이 점착제 조성물을, 예를 들어 UV와 같은 광 조사에 의한 광경화에 의해 상기 경화성 수지의 매트릭스를 형성할 수 있다. 상기 광경화성 모노머 대신 열경화성 모노머를 사용하여 열경화시켜 열경화성 수지의 매트릭스를 형성할 수도 있다.
상기 광학용 점착 필름은 점착력을 갖는 점착제층으로 형성된 것이기 때문에 상기 광학용 점착 필름의 표면에 히드록시기, 카르보닐기, 알데하이드기, 할로포르밀기, 카르보네이트 에스터기, 카르복실레이트기, 카르복실기, 에스터기, 하이드로퍼옥시기, 퍼옥시기, 에테르기, 헤미케탈기, 아세탈기, 오르소에스테르기, 오르소카르보네이트 에스터기, 카르복실릭 엑시드기, 아마이드기, 아민기, 이민기, 아지드기, 아조컴파운드기, 시아네이트기, 니트레이트기, 니트릴기, 니트로컴파운드기, 니트로소컴파운드기, 싸이올기, 술폰산기 등 또는 이들의 조합의 관능기가 존재할 수 있다.
광경화는 통상 이중결합의 개환에 의해 반응이 발생하므로, 대다수 관능기는 미반응상태로 자연히 존재하는 경우가 대부분이며, 열경화의 경우 관능기가 경화반응에 참여하는 경우가 많고, 이때 관능기를 남기기 위해 경화제 함량을 상대적으로 적게 하는 경우가 있다.
본 발명의 또 다른 구현예에서, 일면에 도전층이 형성된 전도성 플라스틱 필름; 및 상기 전도성 플라스틱 필름에 적층된 전술한 바와 같은 상기 광학용 점착 필름;을 포함하는 터치 스크린 패널을 제공한다.
상기 터치 스크린 패널은, 예를 들면, 정전용량 방식의 터치 패널일 수 있다. 또한, 상기 터치 스크린 패널의 구체적인 구조 또는 그 형성 방법은, 전술한 상기 광학용 점착 필름이 적용되는 한, 특별히 제한되지 않고, 이 분야의 일반적인 다층구조의 적층체 구성이 채용될 수 있다.
상기 광학용 점착 필름은 전술한 광학용 점착 필름이 사용되고, 상세한 설명은 전술한 바와 같다.
일구현예에서, 상기 광학용 점착 필름은 약 91 내지 약 93%의 투과율을 가지면서 수분 투습도 (WVTR) 값이 약 50℃에서 약 24hr 동안 방치한 후 측정시 약 10 gmm/m2 내지 80gmm/m2이 되도록 전술한 바와 같이 제조된 광학용 점착 필름을 사용한다.
상기 전도성 플라스틱 필름의 구체적인 종류는 특별히 제한되지 않고, 이 분야의 공지의 전도성 필름을 사용할 수 있다. 예를 들어, 상기 전도성 필름으로, 일면에 ITO 전극층이 형성된 투명 플라스틱 필름일 수 있다. 구체적으로, 상기 플라스틱 기재층을 형성하는 상기 투명 플라스틱 필름으로는, 폴리에틸렌테레프탈레이트 필름, 폴리테트라플로오루에틸렌 필름, 폴리에틸렌 필름, 폴리프로필렌 필름, 폴리부텐 필름, 폴리부타디엔 필름, 염화비닐 공중합체 필름, 폴리우레탄 필름, 에틸렌-비닐 아세테이트 필름, 에틸렌-프로필렌 공중합체 필름, 에틸렌-아크릴산 에틸 공중합체 필름, 에틸렌-아크릴산 메틸 공중합체 필름 또는 폴리이미드 필름 등을 사용할 수 있고, 이에 제한되지 않는다. 보다 구체적으로, 상기 플라스틱 기재층은 폴리에틸렌테레프탈레이트(PET) 필름일 수 있다.
이하 본 발명의 실시예 및 비교예를 기재한다. 그러한 하기한 실시예는 본 발명의 일 실시예일뿐 본 발명이 하기한 실시예에 한정되는 것은 아니다.
(실시예)
실시예 1
2-EHA(에틸헥실아크릴레이트) 100 중량부, IBOA(이소보닐아크릴레이트) 50 중량부 및 HEA(히드록시에틸아크릴레이트) 40 중량부의 함량비로 혼합하고, 여기에 광개시제로서 1-히드록시 시클로헥실 페닐 케톤(Irgacure 184, HCPK) 및 기타 첨가제로 커플링제를 포함하는 점착제 조성물을 제조한 다음, 상기 점착제 조성물에 유기치환된 오가노클레이 (organoclay, Southern Clay(USA)사 Cloisite 10A, 두께: 1 nm, 두께 대 판상의 장경의 비가 1 : 100임) 1 중량부를 혼합하여 CAT社 제조 Homogenizer X360 믹서를 사용하여 10,000 rpm으로 30 분 동안 잘 혼합하여 점착제 조성물의 코팅액을 준비하였다. 이형처리된 폴리에틸렌테레프탈레이트 필름 (두께: 75 ㎛)에 점착제층의 두께가 100㎛가 되도록 바코터를 이용하여 코팅한 후 UV 램프를 이용하여 자외선을 10 분 동안 조사하여 경화시킴으로써 점착 필름을 제조하였다.
상기 점착 필름에 대하여 CuKα선을 사용한 X선 회절(XRD) 패턴을 측정한 결과 약 2 내지 약 10도의 2θ 값에서 피크값이 사라졌다.
실시예 2
상기 실시예 1에서 오가노클레이 함량을 3 중량부를 삽입한 것을 제외하고는 실시예 1과 동일한 방법으로 점착 필름을 제조하였다.
상기 점착 필름에 대하여 CuKα선을 사용한 X선 회절(XRD) 패턴을 측정한 결과 약 2 내지 약 10도의 2θ 값에서 피크값이 사라졌다.
실시예 3
상기 실시예 1에서 오가노클레이 함량을 5 중량부를 삽입한 것을 제외하고는 실시예 1과 동일한 방법으로 점착 필름을 제조하였다.
상기 점착 필름에 대하여 CuKα선을 사용한 X선 회절(XRD) 패턴을 측정한 결과 약 2 내지 약 10도의 2θ 값에서 피크값이 사라졌다.
실시예 4
실시예 1에서와 동일하게 코팅액을 제조한 다음, CAT社 제조 Homogenizer X360 믹서를 사용하여 10,000rpm으로 5분 동안 혼합한 점을 제외하고 실시예 2와 동일한 방법으로 점착 필름을 제조하였다.
실시예 5
실시예 1에서와 동일하게 코팅액을 제조한 다음, CAT社 제조 Homogenizer X360 믹서를 사용하여 1,000rpm으로 30분 동안 혼합한 점을 제외하고 실시예 3과 동일한 방법으로 점착 필름을 제조하였다.
비교예 1
비교예 1은 실시예 1에서 판상형 무기 나노입자인 오가노클레이를 포함하지 않는 것을 제외하고는 실시예 1과 동일한 방법으로 점착 필름을 제조하였다.
하기 표 1에 실시예 1-3 및 비교예 1-3에서 점착 필름을 구성하는 주요 조성을 정리하여 나타내었다.
표 1
구분 EHA 함량(중량부) IBOA 함량(중량부) HEA 함량(중량부) 판상형 무기 나노입자(오가노클레이) 함량(중량부)
실시예 1 100 50 40 1
실시예 2 100 50 40 3
실시예 3 100 50 40 5
실시예 4 100 50 40 3
실시예 5 100 50 40 5
비교예 1 100 50 40 0
평가
실험예 1
상기 실시예 1에서 제조된 광학용 점착 필름에 대하여 TEM 사진을 찍었다. 도 3은 실시예 1에서 제조된 광학용 점착 필름의 TEM 사진이다. 광학용 점착 필름 내에 판상형 무기 나노입자가 배향성을 가지고 정렬되어 있음을 확인할 수 있다.
실험예 2: 광학적 특성 평가
실시예 1-5 및 비교예 1의 광학용 점착 필름에 대하여 전광선 투과율(Total Transmittance) 및 헤이즈를 ASTM D 1003 Modified 법으로 CM-5 (Konica Minolt社 제조)를 이용하여 측정하고, 그 결과를 하기 표 1에 기재하였다.
전광선 투과율(Total Transmittance)은 입사광의 직진광선과 산란광선을 모두 포함하는 전광선 투과율을 의미하고, 실시예 1-5 및 비교예 1의 광학용 점착 필름을 글래스에 부착한 후 이를 측정하였으며, 베이스라인(baseline)은 공기(air)로 설정한 뒤 100% 기준의 코렉션 데이터(Correction data)로 하기 식 1에 따라 나타내었다.
[식 1]
(유리/OCA의 적층체의 투과율) / 공기의 투과율 * 100
- Glass 및 OCA 계면에서의 반사율은 보정 안 함
실시예 1-3의 광학용 점착 필름에서 매우 우수한 투과율 및 헤이즈 특성을 나타내었다.
실험예 3: 수분 투습도 (WVTR)
수분 투습도는 ASTM E96법에 의해 측정하며, 측정 기기는 MOCON社 제조 Model: PERMATRAN_W 3/33 MA를 사용하였다.
실험예 4: 내구성 측정
ASTM D3759 의 기준을 적용하여, Texture Analyzer社 제조, TA Plus를 이용하여 인장강도를 측정하였다.
실험예 5: 박리강도 측정
실시예 1-3의 광학용 점착 필름에 대하여 인치(inch) 폭에 대한 약 300mm/min 속도로 박리 강도를 측정하였다.
ASTM D3330 의 기준을 적용하여, Texture Analyzer社 제조 TA Plus를 이용하여 박리강도를 측정하였다.
상기 측정한 물성을 하기 표 2에 나타내었다.
표 2
투과율(%) 수분 투습도(g/(m2·day) 인성(kg) 모듈러스(Pa,상온) 박리강도(kg/in) 헤이즈
실시예 1 92.5 70 3.0 1.10×105 2.5 0.4
실시예 2 92.0 50 3.5 1.15×105 3.0 0.5
실시예 3 91.5 30 4.0 1.20×105 3.5 0.6
실시예 4 90.0 90 3.1 1.1×105 2.4 1.0
실시예 5 89.0 80 3.5 1.15×105 2.7 1.3
비교예 1 92.5 100 2.6 1.0×105 2.1 0.3
상기 표 1의 결과 실시예 1-5는 적합한 광학적 용도에 적합한 광학 특성 및 물성을 갖는 것으로 확인되었다.
[부호의 설명]
1: 경화성 수지 매트릭스
2: 판상형 무기 나노입자
10, 20: 광학용 점착 필름

Claims (19)

  1. 판상형 무기 나노입자 및 경화성 수지를 포함하는 광학용 점착 필름.
  2. 제1항에 있어서,
    상기 판상형 무기 나노입자는 두께 1 nm 내지 100 nm의 판상 형태인
    광학용 점착 필름.
  3. 제1항에 있어서,
    상기 판상형 무기 나노입자는 두께 대 판상의 장경의 비가 1 : 50 내지 1 : 200인
    광학용 점착 필름.
  4. 제1항에 있어서,
    상기 판상형 무기 나노입자는 층상 점토 화합물을 구성하는 적어도 하나의 층을 포함하는
    광학용 점착 필름.
  5. 제1항에 있어서,
    상기 층상 점토 화합물은 마이카(Mica), 스멕타이트(Smectite), 버미큘라이트(Virmiculite), 클로라이트(Clorite), 몬모릴로나이트(Montmorillonite, MMT), 논트로나이트(Nontronite), 사포나이트(saponite), 헥토나이트(Hectorite), 벤토나이트(Bentonite) 및 이들의 조합으로 이루어진 군으로부터 선택된 하나를 포함하는
    광학용 점착 필름.
  6. 제5항에 있어서,
    상기 층상 점토 화합물은 친수성 작용기가 C12-C18 알킬기로 치환된
    광학용 점착 필름.
  7. 제1항에 있어서,
    상기 경화성 수지는 2-에틸헥실아크릴레이트(2-EHA, ethyl hexyl acylate), 이소보닐아크릴레이트(IBOA, isobonyl acrylate), 히드록시에틸아크릴레이트(HEA, hydroxy ethyl acrylate), 히드록시부틸아크릴레이트(HBA, hydroxyl butyl acrylate), 히드록시프로필아크릴레이트(HPA, hydroxyl propyl acryalte), 헥실메타크릴레이트(HMA, Hexyl methacrylate) 및 이들의 조합으로 이루어진 군으로부터 선택된 하나를 포함하는 모노머가 중합된 아크릴계 광경화성 수지인
    광학용 점착 필름.
  8. 제1항에 있어서,
    상기 경화성 수지 100 중량부 및 상기 층상 점토 화합물 1 내지 20 중량부 포함하는
    광학용 점착 필름.
  9. 제1항에 있어서,
    상기 경화성 수지의 매트릭스 내에 상기 층상 점토 화합물이 상기 광학용 점착 필름의 면과 평행한 방향으로 배치되도록 배향성을 갖도록 분산된
    광학용 점착 필름.
  10. 제1항에 있어서,
    CuKα선을 사용한 X선 회절(XRD) 패턴을 측정한 결과 2 내지 10도의 2θ 값에서 피크가 존재하지 않는
    광학용 점착 필름.
  11. 제1항에 있어서,
    투과율 91 내지 93% 및 수분 투습도 (WVTR) 값이 약 50℃에서 약 24hr 동안 방치한 후 측정시 약 10 gmm/m2 내지 80gmm/m2인
    광학용 점착 필름.
  12. 제1항에 있어서,
    인성 2.0 Kg/mm2 내지 5.0 Kg/mm2, 상온 측정 모듈러스 0.5 × 105 Pa 내지 1.3 × 105 Pa 및 박리 강도 2.0 kg/in 내지 3.5 kg/in인
    광학용 점착 필름.
  13. 유기 치환된 소수성의 층상 점토 화합물과 광학용 점착 필름 형성용 경화성 모노머를 혼합하여 상기 층상 점토 화합물의 층간에 상기 경화성 모노머가 개재되도록 혼합된 점착제 조성물을 준비하는 단계; 및
    상기 점착제 조성물을 경화시켜 상기 층상 점토 화합물의 층간에 개재된 상기 경화성 모노머가 경화성 수지로 중합되면서 상기 층상 점토 화합물의 각 층을 형성하는 판상형 무기 나노입자를 박리하여, 상기 경화성 수지의 매트릭스 내에 상기 판상형 무기 나노입자가 분산된 광학용 점착 필름을 얻는 단계
    를 포함하는 광학용 점착 필름의 제조 방법.
  14. 제13항에 있어서,
    상기 층상 점토 화합물과 상기 경화성 모노머를 500 내지 10,000 rpm에서 5 내지 60분 동안 교반하여 혼합시키는
    광학용 점착 필름의 제조 방법.
  15. 제13항에 있어서,
    상기 판상형 무기 나노입자는 두께 1nm 내지 100 nm의 판상 형태인
    광학용 점착 필름의 제조 방법.
  16. 제13항에 있어서,
    상기 판상형 무기 나노입자는 두께 대 판상의 장경의 비가 1 : 50 내지 1 : 200인
    광학용 점착 필름의 제조 방법.
  17. 제13항에 있어서,
    상기 유기 치환된 소수성의 층상 점토 화합물은 마이카(Mica), 스멕타이트(Smectite), 버미큘라이트(Virmiculite), 클로라이트(Clorite), 몬모릴로나이트(Montmorillonite, MMT), 논트로나이트(Nontronite), 사포나이트(saponite), 헥토나이트(Hectorite), 벤토나이트(Bentonite) 및 이들의 조합으로 이루어진 군으로부터 선택된 하나를 포함하고, 상기 층상 점토 화합물의 친수성 작용기가 C12-C18 알킬기로 치환된 것인
    광학용 점착 필름의 제조 방법.
  18. 일면에 도전층이 형성된 전도성 플라스틱 필름; 및
    상기 전도성 플라스틱 필름에 적층된, 제1항 내지 제12항 중 어느 한 항에 따른 광학용 점착 필름
    을 포함하는 터치 스크린 패널.
  19. 제18항에 있어서,
    상기 전도성 플라스틱 필름이 ITO(도전성 금속 산화물)층이 일면에 형성된 폴리에틸렌테레프탈레이트 필름인
    터치 스크린 패널.
PCT/KR2014/005770 2013-06-28 2014-06-27 광학용 점착 필름, 광학용 점착 필름의 제조 방법 및 이를 포함하는 터치 스크린 패널 WO2014209074A1 (ko)