Classifications

• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
  • A61K8/00—Cosmetics or similar toiletry preparations
  • A61K8/18—Cosmetics or similar toiletry preparations characterised by the composition
  • A61K8/30—Cosmetics or similar toiletry preparations characterised by the composition containing organic compounds
  • A61K8/33—Cosmetics or similar toiletry preparations characterised by the composition containing organic compounds containing oxygen
  • A61K8/35—Ketones, e.g. benzophenone
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
  • A61K8/00—Cosmetics or similar toiletry preparations
  • A61K8/18—Cosmetics or similar toiletry preparations characterised by the composition
  • A61K8/30—Cosmetics or similar toiletry preparations characterised by the composition containing organic compounds
  • A61K8/33—Cosmetics or similar toiletry preparations characterised by the composition containing organic compounds containing oxygen
  • A61K8/37—Esters of carboxylic acids
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
  • A61K8/00—Cosmetics or similar toiletry preparations
  • A61K8/18—Cosmetics or similar toiletry preparations characterised by the composition
  • A61K8/72—Cosmetics or similar toiletry preparations characterised by the composition containing organic macromolecular compounds
  • A61K8/81—Cosmetics or similar toiletry preparations characterised by the composition containing organic macromolecular compounds obtained by reactions involving only carbon-to-carbon unsaturated bonds
  • A61K8/8141—Compositions of homopolymers or copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by only one carboxyl radical, or of salts, anhydrides, esters, amides, imides or nitriles thereof; Compositions of derivatives of such polymers
  • A61K8/8152—Homopolymers or copolymers of esters, e.g. (meth)acrylic acid esters; Compositions of derivatives of such polymers
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61Q—SPECIFIC USE OF COSMETICS OR SIMILAR TOILETRY PREPARATIONS
  • A61Q17/00—Barrier preparations; Preparations brought into direct contact with the skin for affording protection against external influences, e.g. sunlight, X-rays or other harmful rays, corrosive materials, bacteria or insect stings
  • A61Q17/04—Topical preparations for affording protection against sunlight or other radiation; Topical sun tanning preparations
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/12—Esters of monohydric alcohols or phenols
  • C08F220/14—Methyl esters, e.g. methyl (meth)acrylate
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/12—Esters of monohydric alcohols or phenols
  • C08F220/16—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms
  • C08F220/18—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms with acrylic or methacrylic acids
  • C08F220/1808—C8-(meth)acrylate, e.g. isooctyl (meth)acrylate or 2-ethylhexyl (meth)acrylate
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/12—Esters of monohydric alcohols or phenols
  • C08F220/16—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms
  • C08F220/18—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms with acrylic or methacrylic acids
  • C08F220/1818—C13or longer chain (meth)acrylate, e.g. stearyl (meth)acrylate
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/62—Monocarboxylic acids having ten or more carbon atoms; Derivatives thereof
  • C08F220/68—Esters
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
  • A61K2800/00—Properties of cosmetic compositions or active ingredients thereof or formulation aids used therein and process related aspects
  • A61K2800/40—Chemical, physico-chemical or functional or structural properties of particular ingredients
  • A61K2800/48—Thickener, Thickening system
• • A—HUMAN NECESSITIES
  • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
  • A61K—PREPARATIONS FOR MEDICAL, DENTAL OR TOILETRY PURPOSES
  • A61K2800/00—Properties of cosmetic compositions or active ingredients thereof or formulation aids used therein and process related aspects
  • A61K2800/40—Chemical, physico-chemical or functional or structural properties of particular ingredients
  • A61K2800/59—Mixtures
  • A61K2800/594—Mixtures of polymers
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/04—Acids; Metal salts or ammonium salts thereof
  • C08F220/06—Acrylic acid; Methacrylic acid; Metal salts or ammonium salts thereof
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/12—Esters of monohydric alcohols or phenols
  • C08F220/16—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms
  • C08F220/18—Esters of monohydric alcohols or phenols of phenols or of alcohols containing two or more carbon atoms with acrylic or methacrylic acids
  • C08F220/1804—C4-(meth)acrylate, e.g. butyl (meth)acrylate, isobutyl (meth)acrylate or tert-butyl (meth)acrylate
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
  • C08F220/00—Copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and only one being terminated by only one carboxyl radical or a salt, anhydride ester, amide, imide or nitrile thereof
  • C08F220/02—Monocarboxylic acids having less than ten carbon atoms; Derivatives thereof
  • C08F220/10—Esters
  • C08F220/40—Esters of unsaturated alcohols, e.g. allyl (meth)acrylate

Definitions

• the present invention relates to compositions for imparting water resistance and aiding retention of active ingredients in personal care compositions.
• compositions for imparting water resistance and aiding retention of active ingredients in personal care compositions are well known. Without them, personal care actives, such as sun care actives, may wash off, wear off, be re-emulsified, or otherwise lose their efficacy.
• personal care actives such as sun care actives
• the problem with current water resistance imparting polymers is they are typically very tacky and impart bad aesthetic feel to consumers when formulated in sunscreen formulations.
• aesthetics is one of the most important considerations in a consumer's selection of, or at least loyalty to, a personal care composition.
• the present invention provides personal care compositions comprising a polymer comprising: (a) one or more polymer comprising, as polymerized units, (i) 75% to 35% by weight, based on the weight of said polymer, one or more (meth)acrylate monomer selected from at least one of C1-C4 (meth)acrylate, (meth)acrylic acid, styrene, or substituted styrene, and (ii) 25% to 65% by weight, based on the weight of said polymer, one or more hydrophobic monomer, including hydrophobically substituted (meth)acrylate monomers, with alkyl chain length from C8 to C22 and, (iii) optionally crosslinker, and, (b) at least one suncare active.
• the resulting polymer shows superior aesthetic feel, great film formation, and has excellent retention of active ingredients in the presence of water.
• (meth)acrylic means acrylic or methacrylic
• (meth)acrylate means acrylate or methacrylate
• (meth)acrylamide means acrylamide or methacrylamide.
• Substituted means having at least one attached chemical group such as, for example, alkyl group, alkenyl group, vinyl group, hydroxyl group, carboxylic acid group, other functional groups, and combinations thereof.
• Styrene and substituted Styrene monomers have one ethylenically unsaturated group per molecule.
• Styrene and substituted Styrene monomers include 4-methylstyrene, 2- methylstyrene, 3-methylstyrene, 4-methoxystyrene, 2-hydroxymethylstyrene, 4-ethylstyrene, 4- ethoxystyrene, 3,4-dimethylstyrene, 2-chlorostyrene, 3-chlorostyrene, 4-chloro-3-methylstyrene, 4-t- butylstyrene, 2,4-dichlorostyrene, 2,6-dichlorostyrene.
• Preferred Styrene and substituted Styrene monomers include styrene (Sty) and 4-methylstyrene (vinyl toluene).
• Prefered (meth)acrylate monomer containing acid functional group include acrylic acid, methacrylic acid, itaconic acid, crotonic acid. More preferred (meth)acrylate monomer scontaining acid functional group are acrylic acid, methacrylic acid.
• monomer (i) is present in a range of 75% to 35% by weight.
• Preferred monomer (i) are (meth) acrylate monomer with alkyl chain length of C4 and less, styrene, substituted styrene, More preferred monomer (i) are butyl acrylate, ethyl acrylate, acrylic acid, methyl methacrylate, ethyl methacrylate, butyl methacrylate, methacrylic acid, styrene. Most preferred monomer (i) are butyl acrylate, methyl methacrylate, methacrylic acid, styrene.
• monomer (ii) is one or more hydrophobic monomer, including hydrophobically substituted (meth) acrylate monomers, with alkyl chain length from C8 to C22.
• Prefered monomers (ii) are one or two monomer selected from ethylhexyl methacrylate, lauryl methacrylate, stearyl methacrylate, and cetyl-eicosyl methacrylate, behenyl methacrylate, ethylhexyl acrylate, lauryl acrylate, stearyl acrylate, and cetyl-eicosyl acrylate, behenyl acrylate.
• Most preferred monomer (ii) are one or two monomer selected from ethylhexyl acrylate, lauryl methacrylate, stearyl methacrylate.
• the polymer further comprising a cross-linker.
• Crosslinkers are monomers having two or more ethylenically unsaturated groups, and may include, e.g.,
• divinylaromatic compounds di-, tri- and tetra-(meth)acrylate esters, di-, tri- and tetra-allyl ether or ester compounds and allyl (meth)acrylate.
• Preferred examples of such monomers include divinylbenzene (DVB), trimethylolpropane diallyl ether, tetraallyl pentaerythritol, triallyl pentaerythritol, diallyl pentaerythritol, diallyl phthalate, diallyl maleate, triallyl cyanurate, Bisphenol A diallyl ether, allyl sucroses, methylene bisacrylamide, trimethylolpropane triacrylate, allyl methacrylate (ALMA), ethylene glycol dimethacrylate (EGDMA), hexane-l,6-diol diacrylate (HDD A) and butylene glycol dimethacrylate (BGDMA).
• AMA
• crosslinkers include DVB, ALMA, EGDMA, HDDA and BGDMA.
• Most preferred crosslinker is ALMA.
• the amount of polymerized crosslinker residue in the polymer is at least 0.01%, alternatively at least 0.02%, alternatively at least 0.05%.
• the amount of crosslinker residue in the polymer is no more than 0.3%, alternatively no more than 0.2%, alternatively no more than 0.15% .
• Polymers usefully employed according to the invention can be prepared by conventional emulsion, solution or suspension polymerization.
• Emulsion polymerization is preferred. Monomers used to prepare the polymers are added in a sequential process or randomly to afford non-random or random polymers using a free-radical initiator such as peroxygen compounds or diazo compounds and, optionally, chain transfer agents.
• a free-radical initiator such as peroxygen compounds or diazo compounds and, optionally, chain transfer agents.
• the length of the primary polymer chains is typically such that, if any crosslinks were removed, the molecular weight (Mw) would be in the range of about 50,000 to 10,000,000, alternatively from 100,000 to 5,000,000, alternatively from 200,000 to 2,000,000.
• a free radical initiator is utilized in solution and emulsion polymerizations.
• Suitable free radical initiators include hydrogen peroxide; tert-butyl hydroperoxide; sodium, potassium, lithium and ammonium persulfate and the like.
• a reducing agent such as a bisulfite, including an alkali metal metabisulfite, hydrosulfite, and hyposulfite; and sodium formaldehyde sulfoxylate or a reducing sugar such as ascorbic acid or isoascorbic acid, may be used in combination with the initiator to form a redox system.
• Initiators usefully employed for suspension polymerization include oil soluble peroxides, hydroperoxides and azo compounds such as AIBN.
• the amount of initiator may be from 0.01% by weight to about 2% by weight of the monomer charged and in a redox system, a corresponding range of 0.01 % by weight to about 2% by weight of reducing agent may be used.
• Transition metal catalysts such as iron and copper salts, may be used.
• the polymerization temperature may be in the range of about 10° C. to 120° C. in the aqueous emulsion, suspension and solution polymerizations. In the case of the persulfate systems, the temperature is preferably in the range of 60° C. to 90° C. In the redox system, the temperature is preferably in the range of 20° C. to 70° C.
• any emulsifiers or dispersing agents optionally employed for preparing the monomer emulsions or polymer emulsions may be anionic, cationic or non-ionic types. Also a mixture of any two or more types may be used.
• Suitable nonionic emulsifiers include, but are not limited to, ethoxylated octylphenols, ethoxylated nonylphenols, ethoxylated fatty alcohols and the like.
• Suitable anionic emulsifiers include, but are not limited to, sodium lauryl sulfate, sodium dodecylbenzene sulfonate, sulfated and ethoxylated derivatives of nonylphenols, octylphenols and fatty alcohols, esterified sulfosuccinates and the like.
• Suitable cationic emulsifiers include, but are not limited to, laurylpyridinium chlorides, cetyldimethyl amine acetate, (C 8 -C is )
• alkyldimethylbenzylammonium chlorides and the like The level of emulsifier may be from about 0.1 % to about 10% by weight, based on total monomer charged.
• monomer (i) is at least two of butyl acrylate, methyl methacrylate, methacrylic acid, or styrene.
• monomer (ii) is at leastone of ethylhexyl acrylate, lauryl methacrylate, stearyl methacrylate, and cetyl-eicosyl methacrylate, behenyl methacrylate, lauryl acrylate, stearyl acrylate, and cetyl-eicosyl acrylate, behenyl acrylate.
• monomer (ii) is at least two of ethylhexyl acrylate, lauryl methacrylate, stearyl methacrylate, and cetyl-eicosyl methacrylate, behenyl methacrylate, lauryl acrylate, stearyl acrylate, and cetyl-eicosyl acrylate, behenyl acrylate.
• the polymer is formed in a single stage.
• the polymer is formed in a two stage reaction.
• the stage 2 polymer comprises, as polymerized units, (i) 10-99% of one or more monomer which has a Tg of more than 80 °C after polymer formation, (ii) 1- 10% of one or more (meth)acrylate monomer containing acid functional group, and (iii) optionally, a crosslinker.
• the stage 1 and stage 2 ratio ranges from 60:40 to 99 to 1.
• Tg glass transition temperatures
• the Tg of the second stage polymer is in the range of about 50 to 200 °C, alternatively from 75 to 150 °C, alternatively from 80 to 120 °C.
• the stage 1 and stage 2 ratio is more than 50:50, preferably more than 60: 40. In some embodiments of the invention, the stage 1 and stage 2 ratio is less than 99: 1, preferably, less than 90 to 10.
• a suitable oil base includes any oil or mixture of oils which are conventionally used in the personal care products. Examples include saturated fatty esters and diesters, such as isopropyl palmitate, octyl palmitate, butyl stearate, isocetyl stearate, octadodecyl stearoyl stearate, diisopropyl adipate, dioctyl sebacate, paraffin oils, paraffin waxes, animal oils and vegetable oils such as mink oil, coconut oil, soybean oil, palm oil, corn oil, cocoa butter, sesame oil, lanolin oil, fatty alcohols such as stearyl alcohol, isostearyl alcohol, isocetyl alcohol.
• the oils listed are merely examples are not intended to limit the invention in any way. In general, any hydrophobic material or mixtures thereof which are toxicologically safe for human or animal use may constitute the oil base
• the personal care compositions and formulations containing the water resistance polymers are of four basic compositions: oil dispersions, oil-in-water emulsions, water-in-oil emulsions and solutions from one or more organic solvents.
• the oil dispersions are prepared by dispersing the water resistance polymers in the oil base with one or more active ingredients.
• the water resistance polymers can be dispersed in an oil phase or are prepared as an aqueous suspension prior to preparing the final oil-in-water or water-in-oil emulsion.
• the polymers can be added in either phase at any stage in preparing the composition or formulation.
• Personal care formulations are prepared by combining water resistance polymers, an oil base, optionally including an aqueous phase, one or more active ingredients and optional additives by warming the mixture with slow agitation.
• the oil based personal care compositions and formulations include from 0.01 to 10% by weight of at least one water resistance polymer based on the total weight of the formulation.
• the cosmetically acceptable base of the compositions and formulations may be solid or liquid, but the entire formulation is preferably fluid at skin temperatures for ease of application.
• Suitable solvents for preparing a solution of the polymer are typically those used in the art and include alcohols such as ethyl alcohol and volatile silicones such as cyclomethicone.
• Suitable additives include fragrances, fillers, dyes, colorants, preservatives, biocides, antioxidants, other such additives conventionally used in personal care products without negatively impacting substantivity and combinations thereof.
• the invention provides dermally applied personal care compositions and formulations including water resistance polymers dispersed in an oil base and one or more active ingredients.
• active ingredients include but are not limited to sunscreening actives, moisturising actives such as moisturizing oils, cleansing actives for personal care, detergent actives for personal care, vitamins, folic acid derivatives, exfoliating agents, deodorising actives, fragrance actives, skin exfoliating actives, topical medicament actives for personal care, cosmetic agents for personal care, hair conditioners, facial care products, body washes, topical preparations, infrared (IR)-absorbing materials for personal care, acne medications and combinations thereof.
• Cosmetic agents include for example mascaras, eyeliners, lipsticks, powders, paints, foundations and masks.
• Suitable sunscreen actives include inorganic oxides such as titanium dioxide and zinc oxide, cinoxate(2-ethoxyethyl-p-methoxy-cinnamate) ; diethanolamine-p-methoxycinnamate; digalloyl trioleate ethyl 4-bis(hydroxypropyl)aminobenzoate; ethylhexyl-p-methoxy-cinnamate; 2-ethylhexyl salicylate; glyceryl aminobenzoate; homosalate(3,3,5-trimethylcyclohexyl salicylate); triethanolamine salicylate; 2-phenyl-benzimidazole-5-sulfonic acid; sulisobenzone(2-hydroxy-4-methoxy- benzophenone-5- sulfonic acid); Padimate A (amyl p-dimethylaminobenzoate); Padimate O (octyl dimethyl para aminobenzoate); Octocrylene, Avo
• the sunscreen compositions and formulations also may include a sunscreen material particularly suitable for ultraviolet-A (320-400 nm) protection.
• a sunscreen material particularly suitable for ultraviolet-A (320-400 nm) protection suitably is selected from oxybenzone, dioxybenzone; 2-ethylhexyl-2-cyano-3,3 diphenylacrylate; methyl benzilidine camphor; 4-t-butyl-4'-methoxydibenzoyl-methane and mixtures thereof.
• Sunscreen compositions and formulations of the invention may be formed using conventional emulsion techniques and inexpensive agitation equipment.
• the sunscreen compositions and formulations thus formed are stable emulsions, the polymers effectively retaining active ingredients at low polymer concentrations, ranging from 0.01 to 10% by polymer weight based on the total weight of the composition in the oil phase; the formulation having an oil phase viscosity of at least 10 poise under a shear stress up to 1000 dynes/cm 2 . It is preferred that the formulation consists of an oil-in- water emulsion.
• compositions and formulations of the present invention When applied to mammalian skin, these personal care compositions and formulations of the present invention form an oil film on the skin surface. This film gives the skin a moist, glossy appearance which provides cosmetic elegance.
• the films helps protect the skin from the drying, oxidizing effects of the environment, and the ultraviolet light-absorber protects the skin from the damaging rays of the sun.
• the polymer retains the ultraviolet light-absorber onto the skin so that a significantly greater percentage of sunscreen protection is provided at lower polymer concentrations after than with compositions not containing one or more active retaining polymers.
• the compositions and formulations remain substantive for extended periods of time and prolonged exposure to aqueous environments such as water, humidity or perspiration.
• Oil-in-water emulsions are generally prepared by heating the oil and water phases, and slowly adding the water phase to the oil phase with good agitation. Homogenization may be helpful, but it is not necessary. The addition of low levels of stabilizing ingredients in the water phase has been shown to be helpful. Salts such as magnesium sulfate have proven to be useful emulsion stabilizers, and they do not significantly affect the water resistance of the formulations. The addition of water soluble gums such as guar derivatives, xanthan gum, and aloe vera and thickeners such as hydroxyethyl cellulose, hydroxymethyl cellulose and carboxyvinyl polymers have been found to be helpful in stabilizing the emulsions.
• compositions and formulations are usefully employed in accordance with the present invention as creams, lotions, gels, towelettes, wipes, masks, adhesive pads, sprays delivered from solvent and any conventional means used in personal care art.
• MMA methyl methacrylate
• a standard emulsion polymerization method is used. For example, to a 2-liter round-bottom flask equipped with a overhead stirrer, thermocouple, condenser and inlets for the addition of monomer and initiators is charged 183.5 g of deionized water, 26.6 g of 50% CAVASOLTM W7 M TL (cyclodextrin from Wacker Fine Chemicals), 6.1 g of a 30% DISPONIL® FES 32 (Cognis) surfactant and 1.8 g of sodium carbonate. The flask is stirred and heated to 92°C.
• a monomer emulsion is prepared by charging 363 g of deionized water and 13.6 g of DISPONIL® FES 32 surfactant to an appropriate container and set to stir. After the surfactant is incorporated into the water, 175 g of BA, 203 g of Styrene, 105 g of MAA and 217 g of SMA is added slowly to the stirring mixture.
• a cofeed catalyst solution is also prepared by charging 0.69 g of sodium persulfate and 96 g of deionized water.
• reaction temperature of 92°C 25 g of the above prepared monomer emulsion is charged to the kettle with a l l gram deionized water rinse, followed by an initiator solution of 2.11 g sodium persulfate and 12 g water.
• the monomer emulsion cofeed is begun at a rate of 6.33 g per minute for 10 minutes and 12.7 g per minute for 75 minutes.
• the catalyst cofeed is begun at a rate of 1.1 g per minute for 88 minutes.
• the reaction mixture is chased to reduce the amount of residual monomers.
• the resulting Polymer 1 latex has the following characteristics. Solids is the weight of solid material left when the latex is evaporated to dryness, as a percentage of the total weight of latex. Grit is the amount of material retained in the mesh bags. Mean particle size was measured with a Brookhaven Instruments Corp. BI-90 device. Residual Monomer amounts were measured by head space gas chromatography.
• Polymer 2 is made substantially as described above, the appropriate changes being made.
• Example 3 The comparative polymer is made substantially as described in Example 1, the appropriate changes being made.
• a standard emulsion polymerization method is used. For example, for Polymer 9, 252 g of deionized water, 8 g of a 23% sodium dodecyl benzene sulfonate and 2 g of sodium carbonate are charged to a 2-liter round-bottom flask equipped with a overhead stirrer, thermocouple, condenser and inlets for the addition of monomer and initiators. The flask is stirred and heated to 92°C.
• a monomer emulsion (stage 1) is prepared by charging 146 g of deionized water and 5.6 g of sodium dodecyl benzene sulfonate (23%) to an appropriate container and set to stir.
• a cofeed catalyst solution is also prepared by charging 0.86 g of sodium persulfate and 50 g of deionized water.
• reaction temperature of 88°C 19 g of the above prepared monomer emulsion is charged to the kettle with 5 g of deionized water rinse, followed by an initiator solution of 1.9 g sodium persulfate and 15 g water.
• the stage 1 monomer emulsion cofeed is begun at a rate of 4.72 g per minute for 15 minutes and 10.1 g per minute for 83 minutes.
• the stagel catalyst cofeed is begun at a rate of 0.61 g per minute for 88 minutes.
• the reaction mixture is held for 10 minutes.
• stage 2 monomer emulsion and catalyst are prepared.
• Stage 2 monomer emulsion is prepared by charging 52 g of deionized water and 2 g of sodium dodecyl benzene sulfonate (23%) to an appropriate container and set to stir. After the surfactant is incorporated into the water, 112 g of MMA, 1.1 g of g of MAA, and 0.09 g of ALMA is added slowly to the stirring mixture.
• a stage 2 cofeed catalyst solution is also prepared by charging 0.12 g of sodium persulfate and 14 g of deionized water. Upon the completion of stage 1 hold, the stage 2 monomer emulsion cofeed is begun at a rate of 6.55 g per minute for 29 minutes.
• the reaction mixture is chased to reduce the amount of residual monomers.
• the resulting latex has the following characteristics.
• Polymers 3-8 are made substantially as described above, the appropriate changes being made.
• a sunscreen base (1) and a nonionic sunscreen base (2) are prepared with the components listed in TABLE 4 in weight percent.
• the sunscreen formulations are prepared by adding all phase A ingredients into a container and heating to 75 °C. All phase B ingredients are added to another container and heated to 75°C to ensure oxybenzone well dissolved. Then phases A and B are combined with high sheer. The solution is cooled to 55-60 °C and phase D ingredients are added. When temperature reaches 45 °C, phase C ingredients are added. Add phase E when the temperature is below 40 °C. Adjust pH to 6.0-7.0.
• Tackiness Score ranges between most tacky (5) and least tacky (1).

Landscapes

• Health & Medical Sciences (AREA)
• Chemical & Material Sciences (AREA)
• Life Sciences & Earth Sciences (AREA)
• Organic Chemistry (AREA)
• Polymers & Plastics (AREA)
• Medicinal Chemistry (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Veterinary Medicine (AREA)
• Public Health (AREA)
• General Health & Medical Sciences (AREA)
• Animal Behavior & Ethology (AREA)
• Epidemiology (AREA)
• Birds (AREA)
• Emergency Medicine (AREA)
• Dermatology (AREA)
• Cosmetics (AREA)
• Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)

Priority Applications (6)

Applications Claiming Priority (2)

Related Child Applications (2)

Publications (2)

Family

ID=47470206

Family Applications (1)

Country Status (6)

Cited By (7)

Families Citing this family (10)

Family Cites Families (18)

• 2012
  • 2012-12-11 BR BR112014013682A patent/BR112014013682B8/pt active IP Right Grant
  • 2012-12-11 US US14/366,193 patent/US9486399B2/en active Active
  • 2012-12-11 CN CN201280060231.0A patent/CN103987373A/zh active Pending
  • 2012-12-11 CN CN201810890704.9A patent/CN108969401A/zh active Pending
  • 2012-12-11 EP EP12809032.1A patent/EP2776010B1/en active Active
  • 2012-12-11 WO PCT/US2012/068898 patent/WO2013095993A2/en not_active Ceased
  • 2012-12-11 JP JP2014549111A patent/JP6335789B2/ja active Active
• 2016
  • 2016-08-08 US US15/231,052 patent/US9789049B2/en active Active

Non-Patent Citations (1)

Also Published As

Similar Documents

Legal Events