WO2013038672A1 - Pile secondaire à électrolyte non aqueux - Google Patents

Pile secondaire à électrolyte non aqueux Download PDF

Info

Publication number
WO2013038672A1
WO2013038672A1 PCT/JP2012/005835 JP2012005835W WO2013038672A1 WO 2013038672 A1 WO2013038672 A1 WO 2013038672A1 JP 2012005835 W JP2012005835 W JP 2012005835W WO 2013038672 A1 WO2013038672 A1 WO 2013038672A1
Authority
WO
WIPO (PCT)
Prior art keywords
negative electrode
active material
lithium
electrode active
layer
Prior art date
Application number
PCT/JP2012/005835
Other languages
English (en)
Japanese (ja)
Inventor
佐藤　俊忠
古結　康隆
本田　和義
Original Assignee
パナソニック株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by パナソニック株式会社 filed Critical パナソニック株式会社
Publication of WO2013038672A1 publication Critical patent/WO2013038672A1/fr

Abstract

La présente invention concerne une pile secondaire à électrolyte non aqueux dotée d'une capacité et d'une densité énergétique élevées, et possédant en outre un cycle de vie amélioré. La pile secondaire à électrolyte non aqueux est pourvue des éléments suivants : un groupe d'électrodes dans lequel une électrode positive, une électrode négative et un séparateur intercalé entre l'électrode positive et l'électrode négative sont enroulés ou empilés ; et un électrolyte non aqueux. L'électrode positive comprend un collecteur de courant d'électrode positive et, déposée à la surface du collecteur de courant de l'électrode positive, une couche de matériau actif d'électrode positive d'un matériau actif d'électrode positive apte à capter et à libérer des ions lithium. L'électrode négative comprend un collecteur de courant d'électrode négative et, déposée à la surface du collecteur de courant de l'électrode négative, une couche de matériau actif d'électrode négative d'un matériau actif d'électrode négative apte à capter et à libérer des ions lithium. La couche de matériau actif de l'électrode négative comprend un film formé à la surface du matériau actif de l'électrode négative, au moins une partie dudit film comprenant un composé de lithium inorganique. Lorsque la couche de matériau actif de l'électrode négative est divisée selon un rapport d'épaisseur de 7:3 en une couche (A) proche du collecteur de courant de l'électrode négative et une couche (B) proche de la surface de la couche de matériau actif de l'électrode négative, la teneur en composé de lithium inorganique comprise dans la couche (B) est supérieure à la teneur en composé de lithium inorganique comprise dans la couche (A).
PCT/JP2012/005835 2011-09-13 2012-09-13 Pile secondaire à électrolyte non aqueux WO2013038672A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2011199297A JP2014225324A (ja) 2011-09-13 2011-09-13 非水電解質二次電池
JP2011-199297 2011-09-13

Publications (1)

Publication Number Publication Date
WO2013038672A1 true WO2013038672A1 (fr) 2013-03-21

Family

ID=47882921

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2012/005835 WO2013038672A1 (fr) 2011-09-13 2012-09-13 Pile secondaire à électrolyte non aqueux

Country Status (2)

Country Link
JP (1) JP2014225324A (fr)
WO (1) WO2013038672A1 (fr)

Cited By (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015198038A (ja) * 2014-04-02 2015-11-09 信越化学工業株式会社 非水電解質二次電池用負極及び非水電解質二次電池
CN110556590A (zh) * 2018-05-31 2019-12-10 松下知识产权经营株式会社 锂二次电池
WO2020017515A1 (fr) 2018-07-18 2020-01-23 旭化成株式会社 Accumulateur au lithium-ion
CN111755664A (zh) * 2020-06-30 2020-10-09 蜂巢能源科技有限公司 一种锂离子电池的电极及锂离子电池
CN113380989A (zh) * 2020-02-25 2021-09-10 广州天赐高新材料股份有限公司 一种钝化锂粉及其制备方法和用途
US20210305633A1 (en) * 2018-12-12 2021-09-30 Contemporary Amperex Technology Co., Limited Wound electrode assembly, lithium-ion secondary battery and negative electrode plate
CN113614969A (zh) * 2020-03-04 2021-11-05 宁德新能源科技有限公司 电化学装置和包含其的电子装置
CN113646921A (zh) * 2019-03-29 2021-11-12 松下知识产权经营株式会社 非水电解质二次电池
CN116103614A (zh) * 2022-11-24 2023-05-12 广东金晟新能源股份有限公司 一种氟化锌改性多孔锂金属复合负极材料及其制备方法与应用

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US10128529B2 (en) * 2015-11-13 2018-11-13 Semiconductor Energy Laboratory Co., Ltd. Lithium-ion secondary battery, fabricating method therof, and electronic device
KR20210063129A (ko) * 2019-11-22 2021-06-01 주식회사 엘지에너지솔루션 플렉서블 이차전지

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH09161779A (ja) * 1995-12-13 1997-06-20 Japan Storage Battery Co Ltd 非水電解液リチウム二次電池の製造方法
JPH10284053A (ja) * 1997-04-10 1998-10-23 Matsushita Electric Ind Co Ltd 二次電池用電極およびそれを用いた二次電池、並びに二次電池用電極の製造方法
JP2005038720A (ja) * 2003-07-15 2005-02-10 Sony Corp 負極の製造方法および電池の製造方法
JP2005166469A (ja) * 2003-12-03 2005-06-23 Sanyo Electric Co Ltd リチウム二次電池およびその製造方法
JP2008117785A (ja) * 2005-08-02 2008-05-22 Matsushita Electric Ind Co Ltd リチウム二次電池用負極およびその製造方法
JP2009076372A (ja) * 2007-09-21 2009-04-09 Shin Etsu Chem Co Ltd 非水系二次電池

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH09161779A (ja) * 1995-12-13 1997-06-20 Japan Storage Battery Co Ltd 非水電解液リチウム二次電池の製造方法
JPH10284053A (ja) * 1997-04-10 1998-10-23 Matsushita Electric Ind Co Ltd 二次電池用電極およびそれを用いた二次電池、並びに二次電池用電極の製造方法
JP2005038720A (ja) * 2003-07-15 2005-02-10 Sony Corp 負極の製造方法および電池の製造方法
JP2005166469A (ja) * 2003-12-03 2005-06-23 Sanyo Electric Co Ltd リチウム二次電池およびその製造方法
JP2008117785A (ja) * 2005-08-02 2008-05-22 Matsushita Electric Ind Co Ltd リチウム二次電池用負極およびその製造方法
JP2009076372A (ja) * 2007-09-21 2009-04-09 Shin Etsu Chem Co Ltd 非水系二次電池

Cited By (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2015198038A (ja) * 2014-04-02 2015-11-09 信越化学工業株式会社 非水電解質二次電池用負極及び非水電解質二次電池
CN110556590A (zh) * 2018-05-31 2019-12-10 松下知识产权经营株式会社 锂二次电池
WO2020017515A1 (fr) 2018-07-18 2020-01-23 旭化成株式会社 Accumulateur au lithium-ion
KR20200039742A (ko) 2018-07-18 2020-04-16 아사히 가세이 가부시키가이샤 리튬 이온 2 차 전지
US11923541B2 (en) 2018-07-18 2024-03-05 Asahi Kasei Kabushiki Kaisha Lithium ion secondary battery
US20210305633A1 (en) * 2018-12-12 2021-09-30 Contemporary Amperex Technology Co., Limited Wound electrode assembly, lithium-ion secondary battery and negative electrode plate
US11824167B2 (en) * 2018-12-12 2023-11-21 Contemporary Amperex Technology Co., Limited Wound electrode assembly, lithium-ion secondary battery and negative electrode plate
CN113646921A (zh) * 2019-03-29 2021-11-12 松下知识产权经营株式会社 非水电解质二次电池
CN113380989A (zh) * 2020-02-25 2021-09-10 广州天赐高新材料股份有限公司 一种钝化锂粉及其制备方法和用途
CN113614969A (zh) * 2020-03-04 2021-11-05 宁德新能源科技有限公司 电化学装置和包含其的电子装置
EP4102609A4 (fr) * 2020-03-04 2023-04-05 Ningde Amperex Technology Limited Dispositif électrochimique et dispositif électronique le comprenant
CN111755664A (zh) * 2020-06-30 2020-10-09 蜂巢能源科技有限公司 一种锂离子电池的电极及锂离子电池
CN116103614A (zh) * 2022-11-24 2023-05-12 广东金晟新能源股份有限公司 一种氟化锌改性多孔锂金属复合负极材料及其制备方法与应用
CN116103614B (zh) * 2022-11-24 2023-09-15 广东金晟新能源股份有限公司 一种氟化锌改性多孔锂金属复合负极材料及其制备方法与应用

Also Published As

Publication number Publication date
JP2014225324A (ja) 2014-12-04

Similar Documents

Publication Publication Date Title
JP5313761B2 (ja) リチウムイオン電池
WO2013038672A1 (fr) Pile secondaire à électrolyte non aqueux
JP5173181B2 (ja) リチウムイオン二次電池及びリチウムイオン二次電池用負極板の製造方法
JP5219387B2 (ja) 非水電解質二次電池
JP6258641B2 (ja) 非水電解液二次電池
US11824185B2 (en) Negative electrode for nonaqueous electrolyte secondary battery and nonaqueous electrolyte secondary battery
JP5226128B2 (ja) 非水電解質二次電池用負極及びその製造方法並びに非水電解質二次電池
WO2010131401A1 (fr) Electrode pour une batterie secondaire au lithium, et batterie secondaire au lithium
JP2007220452A (ja) 非水電解液二次電池用セパレータおよび非水電解液二次電池
WO2010134258A1 (fr) Electrode plane pour accumulateur à électrolyte non aqueux et accumulateur à électrolyte non aqueux
JP2008300302A (ja) 非水電解質二次電池及び非水電解質二次電池用正極の製造方法
JPWO2016098708A1 (ja) リチウムイオン二次電池
JP6917907B2 (ja) リチウムイオン二次電池用正極及びリチウムイオン二次電池、並びにリチウムイオン二次電池用正極の製造方法及び評価方法、及びリチウムイオン二次電池の製造方法
JP2009266761A (ja) 非水電解質二次電池及びその製造方法
WO2015083262A1 (fr) Matériau d'électrode négative pour des batteries rechargeables au lithium-ion, procédé permettant de produire ce dernier, électrode négative pour des batteries rechargeables au lithium-ion, procédé permettant de produire une électrode négative pour des batteries rechargeables au lithium-ion et batterie rechargeable au lithium-ion
JPWO2017217407A1 (ja) リチウムイオン二次電池
JP2016076342A (ja) 非水系二次電池用電極及び非水系二次電池
JP2011100694A (ja) 非水電解質二次電池
JP2010287470A (ja) 非水二次電池およびその製造方法
JP2013131427A (ja) ラミネート電池
WO2015162885A1 (fr) Pile rechargeable à électrolyte non aqueux
KR20180083432A (ko) Li 이온 2차 전지용 부극 재료 및 그의 제조 방법, Li 이온 2차 전지용 부극 그리고 Li 이온 2차 전지
JP6627708B2 (ja) リチウムイオン二次電池、及び、リチウムイオン二次電池の製造方法
US11600825B2 (en) Positive electrode for secondary lithium metal battery and method of making
JP5662746B2 (ja) リチウムイオン二次電池

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 12831874

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 12831874

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: JP