WO2012142348A2

WO2012142348A2 - Refractory object including beta alumina and processes of making and using the same

Info

Publication number: WO2012142348A2
Application number: PCT/US2012/033409
Authority: WO
Inventors: Olivier Citti
Original assignee: Saint-Gobain Ceramics & Plastics, Inc.
Priority date: 2011-04-13
Filing date: 2012-04-13
Publication date: 2012-10-18
Also published as: RU2656647C1; KR101929733B1; CN108726849A; CN108726849B; TW201240941A; EP2697177A4; JP2014515721A; EP2697177A2; WO2012142348A3; KR20140018965A; US20120263929A1; EP2697177B1; US9216928B2; JP5762623B2; CN103492327A; WO2012142348A4; TWI572579B; MY185000A; RU2013148633A

Abstract

A refractory object can include a beta alumina. In an embodiment, the refractory object is capable of being used in a glass fusion process. In another embodiment, the refractory object can have a total Al2O3 content of at least 10 % by weight. Additionally, a Mg-Al oxide may not form along a surface of the refractory object when the surface is exposed to a molten glass including an Al-Si-Mg oxide. In a particular embodiment, a refractory object can be in the form of a glass overflow forming block used to form a glass object that includes an Al-Si-Mg oxide. When forming the glass object, the glass material contacts the beta alumina, and during the flowing of the glass material, a Mg-Al oxide does not form along the beta alumina at the surface.

Description

REFRACTORY OBJECT INCLUDING BETA ALUMINA AND PROCESSES OF

MAKING AND USING THE SAME

FIELD OF THE DISCLOSURE

This disclosure, in general, relates to a refractory object including beta alumina and processes of making and using the same.

BACKGROUND

Alkali alumino-silicate glasses that contain magnesium oxide are being used in applications where mechanical performance is more important. These glasses can be formed using a fusion draw process, where liquid glass flows over the lips of a glass overflow forming block made of zircon material and fuses at the bottom of the glass overflow forming block to form a glass sheet. In contact with alkali alumino-silicate glasses, zircon (ZrSiO₄) dissociates into ZrO₂ and SiO₂ at temperatures close to the glass forming temperature. The higher SiO₂ content may lead to formation of gas bubbles as it dissolves into the glass. ZrO₂ can create ZrO₂ solid nodules at the interface that can then be released into the glass forming defects. Accordingly, the glass overflow forming block has a reduced lifetime as zircon material erodes from the body of the glass overflow forming block while the glass that is manufactured is contaminated with an undesired element that disadvantageously affects its properties.

BRIEF DESCRIPTION OF THE DRAWINGS The present disclosure may be better understood, and its numerous features and advantages made apparent to those skilled in the art by referencing the accompanying drawings.

FIG. 1 is a diagram illustrating a particular embodiment of a refractory object.

FIG. 2 is a diagram illustrating a particular embodiment of a glass overflow forming block. FIG. 3 is a diagram illustrating a particular set of various cross-sectional perspectives of glass overflow forming blocks.

FIG. 4 is an illustration of a refractory object including a body.

FIG. 5 is an illustration of a refractory object including a coating over a body.

FIG. 6 is an illustration of a refractory object including a coating over a body, wherein the coating includes discrete layers.

FIG. 7 is a diagram illustrating the formation of a particular glass sheet from the glass overflow forming blocks.

FIG. 8 is a diagram illustrating the cross-sectional setup of a glass overflow trough during glass production.

FIGs. 9 to 11 are SEM images of a cross-sectional portion of different beta alumina- containing refractory materials after exposure to a molten alkali Al-Mg-Si glass.

FIG. 12 is a table that includes data on composition, physical properties and corrosion properties for refractory objects formed using different milling and sintering conditions.

FIG. 13 is an X-ray diffraction image illustrating a cross-sectional view of an interface between a portion of a sample of a beta alumina-containing refractory material and an alkali Al-Mg-Si glass.

FIG. 14 is an X-ray diffraction image illustrating a cross-sectional view of a portion of the body of the sample of FIG. 13 that is removed from the interface.

The use of the same reference symbols in different drawings indicates similar or identical items.

DETAILED DESCRIPTION

The following description in combination with the figures is provided to assist in understanding the teachings disclosed herein. The following discussion will focus on specific implementations and embodiments of the teachings. This focus is provided to assist in describing the teachings and should not be interpreted as a limitation on the scope or applicability of the teachings.

As used herein, the terms "comprises," "comprising," "includes," "including," "has," "having," or any other variation thereof, are intended to cover a non-exclusive inclusion. For example, a process, method, article, or apparatus that comprises a list of features is not necessarily limited only to those features but may include other features not expressly listed or inherent to such process, method, article, or apparatus. Further, unless expressly stated to the contrary, "or" refers to an inclusive-or and not to an exclusive-or. For example, a condition A or B is satisfied by any one of the following: A is true (or present) and B is false (or not present), A is false (or not present) and B is true (or present), and both A and B are true (or present).

The use of "a" or "an" is employed to describe elements and components described herein. This is done merely for convenience and to give a general sense of the scope of the invention. This description should be read to include one or at least one and the singular also includes the plural, or vice versa, unless it is clear that it is meant otherwise. For example, when a single device is described herein, more than one device may be used in place of a single device. Similarly, where more than one device is described herein, a single device may be substituted for that one device. The term "alumina" is intended to mean A1₂0₃, a compound that can be expressed as having A1₂0₃ as a constituent group within the molecular formula of such compound, or any combination thereof. An example of alumina includes alpha- A1₂0₃, beta alumina, mullite, sodium aluminate, another suitable Al₂0₃-based compound, or any combination thereof. Unless explicitly stated to the contrary, the term "beta alumina" refers to any individual beta alumina compound, all or any subset of individual beta alumina compounds, or any combination of beta alumina compounds (for example, a mixture of beta alumina compounds). Exemplary beta alumina compounds are described later in this specification. The term "averaged," when referring to a value, is intended to mean an average, a geometric mean, or a median value.

Group numbers corresponding to columns within the Periodic Table of the elements use the "New Notation" convention as seen in the CRC Handbook of Chemistry and Physics, 81^st Edition (2000-2001).

Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the features described herein belong. The materials, methods, and examples are illustrative only and not intended to be limiting. To the extent not described herein, many details regarding specific materials and processing acts are conventional and may be found in textbooks and other sources within the field of ceramic materials used as refractories.

In accordance with embodiments described herein, a refractory object can include beta alumina and have one or more properties that are better tailored to forming glass that includes aluminum, silicon, and magnesium ("Al-Si-Mg glass"). In an embodiment, beta alumina is less likely to form a Mg-Al oxide layer when the beta alumina is exposed to a molten alkali Al-Si-Mg glass, and thus, the beta alumina substantially prevents Mg-Al particles from being entrained into the glass being formed. After reading this specification, skilled artisans will appreciate that not all of the properties are required in all embodiments, and therefore, the description of properties is meant to illustrate, and not limit, concepts as described herein.

The refractory object can have a body or a coating overlying the body, wherein the body or coating includes a ceramic material that includes beta alumina. The ceramic material can contain at least 10 wt of the total A1₂0₃ content, whether in the form of alpha- A1₂0₃, beta alumina, another alumina compound, or any combination thereof. The sintered ceramic material can have at least approximately 50 wt , approximately 60 wt , approximately 70 wt , approximately 80 wt , approximately 85 wt , approximately 90 wt , approximately 93 wt , approximately 95 wt , or

approximately 97 wt of the total A1₂0₃ content, whether in the form of alpha- A1₂0₃, beta alumina, another alumina compound, or any combination thereof. In the ceramic material, at least approximately 40 %, at least approximately 50 %, at least

approximately 75%, at least approximately 90%, or at least 95% of the total AI₂O₃ content is from beta alumina.

The beta alumina can include a Group 1 element, a Group 2 element, a rare earth element, Pb, or any combination thereof. For the purposes of this specification, rare earth elements include Sc and the Lanthanoid elements. In an embodiment, the dopant can include Na₂0, K₂0, Li₂0, Cs₂0, MgO, BaO, SrO, PbO, Sc₂0₃, La₂0₃, Pr₂0₃, Nd₂0_3> ZnO, or any combination thereof. The dopant can be added to alpha- A1₂0₃ and help to convert the alpha- A1₂0₃ into beta alumina, and therefore, the dopant may be referred to as a beta conversion material. In another embodiment, the dopant can be added to beta alumina to modify the properties of the beta alumina, such as mechanical strength, diffusion, or the like.

In an embodiment, beta alumina includes beta' alumina having a molecular formula of 11 A1₂0₃ ^' X A₂0 wherein A is a Group 1 element, and X is in a range of 1 to 1.6. In another embodiment, beta alumina includes beta' ' alumina having a molecular formula of 5 A1₂0₃ ^' 1 Z, wherein Z is A₂0 and A is an element in a monovalent state, or Z is MO and M is an element in a divalent state. In a further embodiment, beta alumina includes beta' " alumina having a molecular formula of 15 A1₂0₃ 4 MgO 1 A₂0, wherein A is a Group 1 element. Beta' alumina has a total A1₂0₃ content in a range of approximately 87 mol% to approximately 92 mol%, beta" alumina has a total A1₂0₃ content of approximately 83 mol%, and beta" ' alumina has a total A1₂0₃ content of approximately 75 mol%.

The ceramic material can include another dopant, such as a sintering agent. In a particular example, the sintering agent can help to reduce porosity, which can help to improve resistance to corrosion if the refractory object is later exposed to a corrosive environment. An exemplary sintering agent can include Ta₂0₅, Nb₂0₃, Nb₂0₅, Ti0₂, Fe₂0₃, MnO, CuO, another suitable sintering agent, or any combination thereof. In a particular embodiment, a separate sintering agent is not used when the particular dopant as previously described can also act as a sintering agent, such as Ta₂0₅, Nb₂0₃, or Nb₂0₅.

The ceramic material can include yet another dopant that may help to keep the grain size within the ceramic material from becoming too large. Such a dopant can include an oxide of a rare earth element, Ta₂0₅, Nb₂0₃, Nb₂0₅, ZnO, MgO, Zr0₂, Hf0₂, or any combination thereof. In a particular embodiment, the rare earth oxide can include Y₂0₃, Sc₂0₃, Yb₂0₃, Pr₂0₃, Sm₂0₃, Gd₂0₃, La₂0₃, Ce₂0₃, Dy₂0₃, or any combination thereof.

In an embodiment, the amount of beta conversion material or its corresponding dopant or combination of dopants, when expressed as a metal oxide (e.g., Na₂0, BaO) within the ceramic material of the body or the coating can be at least approximately 2.1 mol , at least approximately 2.5 mol , or at least approximately 4.5 mol . In another embodiment, the amount may be no greater than approximately 26 mol , no greater than approximately 17 mol , or no greater than approximately 13 mol . In another embodiment, the content of the metal oxide can be expressed as a mol as compared to alpha- A1₂0₃. In particular, when any one or more of Na₂0, K₂0, La₂0₃, and Sc₂0₃ are used, the beta alumina can include at least approximately 2.1 mol of these metal oxides.

For the other dopants, the amount of any such dopant, when expressed as a metal oxide, within the ceramic material of the body or the coating can be at least approximately

0.02 wt , at least approximately 0.11 wt , at least approximately 0.2 wt , or at least approximately 0.5 wt . In another embodiment, the amount may be no greater than approximately 5 wt , no greater than approximately 4 wt , no greater than

approximately 3 wt , no greater than approximately 2 wt , or no greater than approximately 1.5 wt .

In a particular embodiment, some impurities may not be present or kept at a relatively low amount, as such impurities may allow grain sizes of sintered ceramics to become unacceptably large. Ti0₂, CaO, Si0₂, Fe₂0₃, Na₂0, or any combination thereof may be at a concentration of no greater than approximately 2 wt , no greater than approximately 1.5 wt , no greater than approximately 0.9 wt , or no greater than approximately 0.5 wt %.

The dopant starting materials may have any oxidation state, e.g., M²⁺, M³⁺, M⁴⁺, M⁵⁺, or any combination thereof, wherein M is a metal element within the dopant. The dopant may be introduced as an oxide of any of the foregoing. For example, the dopant can be Na₂0, K₂0, Li₂0, MgO, BaO, SrO, La₂0₃, Sc₂0₃, etc. Alternatively, any of the foregoing elements may be added as a boride, carbide, carbonate, nitrate, halide, phosphate, sulfate, or the like, as opposed to a metal oxide. In addition, one or more dopants can be added as an oxide in combination with a boride, carbide, carbonate, nitrate, halide, phosphate, sulfate, or any combination thereof. In yet another embodiment, the dopant can be in the form of a metal aluminate, such as sodium aluminate, potassium aluminate, or the like. In an embodiment, the dopant starting material can be powder that is in the form of particles having an averaged particle size no greater than approximately 30 μιη, in another embodiment, the averaged particle size is no greater than approximately 20 μιη, and in a further embodiment, the averaged particle size is no greater than approximately 15 μιη. In an embodiment, the averaged particle size is at least approximately 0.1 μιη, in another embodiment, the averaged particle size is at least approximately 0.5 μιη, and in a further embodiment, the averaged particle size is at least approximately 1 μιη. The ceramic material can be formed from alpha- A1₂0₃, beta alumina, a sodium aluminate, another alumina compound, a beta conversion material, or any combination thereof. When the starting material includes alpha- A1₂0₃, a beta conversion material (e.g., Na₂0) can be added in an amount sufficient to convert the alpha-Al₂0₃ to beta alumina. When the starting material includes beta alumina, a beta conversion material may not be used.

The process and starting materials may depend on whether the ceramic material is being used for the body or coating of the refractory object and whether a sintering technique, a casting technique, or a combination thereof is used. In an embodiment, a body of the refractory object can include the ceramic material formed using a sintering technique. In a particular embodiment, a green body can be formed and then sintered to form the refractory object. Starting materials can include powders of the metal oxides. The alumina powder can be in the form of particles having an averaged particle size no greater than approximately 50 μιη. In an embodiment, the averaged particle size is no greater than approximately 20 μιη, in another embodiment, the averaged particle size is no greater than approximately 12 μιη, and in a further embodiment, the averaged particle size is no greater than approximately 9 μιη or no greater than approximately 3 μιη. In an embodiment, the averaged particle size is at least approximately 0.1 μιη, in another embodiment, the averaged particle size is at least approximately 0.5 μιη, and in a further embodiment, the averaged particle size is at least approximately 0.9 μιη.

In an embodiment, the powders may be dry milled or wet milled to achieve a desired particle size. A planetary mill or rollers may be used. AI₂O₃ dry milling ("AI₂O₃ Dry") can include milling pieces of a refractory material in a planetary mill with an alpha- AI₂O₃ jar and an alpha-Al₂0₃ grinding medium. Zr0₂ dry milling ("Zr0₂ Dry") is the same as AI₂O₃ dry milling except the alpha- AI₂O₃ jar and an alpha- AI₂O₃ grinding medium are replaced with a Zr0₂ jar and a Zr0₂ grinding medium. AI₂O₃ wet milling ("AI₂O₃ Wet") can include milling pieces of a refractory material using an alpha- AI₂O₃ jar on rollers and an alpha- AI₂O₃ grinding medium or a Zr0₂ grinding medium and water. A ball mill process to crush coarser powders, and an extra step of fine milling using an attrition mill or a ball mill with finer media can also be used to reduce the particle size of the powder to the required size. In another embodiment, one or more of the powders can be jet milled. Any combination of milling techniques may also be used. After reading this specification, skilled artisans will appreciate that other materials can be used without departing from the concepts described herein.

After milling, particle distribution data can be collected on the milled powder. The particle distribution can include 10^th percentile, 50^th percentile, and 90^th percentile particle sizes. As used herein, a D10 value represents the 10^th percentile, a D50 value represents the 50^th percentile, and a D90 value represents the 90^th percentile. Thus, D50 corresponds to the median value. In an embodiment, the D10 value of a particle size of the milled powder is no greater than approximately 9 microns, no greater than approximately 3 microns, no greater than approximately 2 microns, or no greater than approximately 0.9 microns. In another embodiment, the D50 value of the particle size of the milled powder is no greater than approximately 20 microns, no greater than approximately 12 microns, no greater than approximately 9 microns, no greater than approximately 3 microns, no greater than approximately 2 microns, or no greater than approximately 0.9 microns. In a further embodiment, the D90 value of the particle size of the milled powder is no greater than approximately 90 microns, no greater than approximately 40 microns, no greater than approximately 30 microns, no greater than approximately 9 microns, or no greater than approximately 2 microns. The powder can have a specific surface area of at least approximately 0.5 m /g, at least approximately

0.9 m 2 /g, at least approximately 1.1 m 2 /g, or at least approximately 1.5 m 2 /g.

If needed or desired, an additional material that can be used and include a binder, a solvent, a dispersant, a thickener, a deflocculant, another suitable ingredient, or any combination thereof. In an embodiment, the additional material may include non- metallic compounds. In another embodiment, the additional material can include an organic compound, water, or the like.

The powders and additional material are combined and shaped to form a green body into a desired shape. In one embodiment, the powders and additional materials can be combined with water to form a slurry. Shaping can be performed using a technique, such as slip casting, uniaxial pressing, isostatic pressing, casting of a gel, vibro-casting, or any combination thereof. The shape can be rectilinear, cylindrical, spherical, ellipsoidal or nearly any other shape. In a particular embodiment, the body can be in the shape of a rectilinear block referred to as a blank that can subsequently be machined to form a glass overflow forming block. In another embodiment, the green body can be structured in such a fashion to more closely match the final refractory object to reduce the extent of any further machine processing. For example, when the refractory object includes a glass overflow forming block, the shape of the green body may more closely resemble the glass overflow forming block to reduce the amount of subsequent machining and ceramic material that would be discarded. More particularly, the green body may have a rectilinear portion adjacent to a tapered portion. The rectilinear portion corresponds to a region where a glass overflow trough will be formed. In another embodiment, the green body may be shaped to have the glass overflow trough adjacent to the tapered portion.

After the green body is formed, the green body is heated in an oven, heater, furnace, or the like to form the refractory object that includes a sintered ceramic material. The heating process can include an initial heating where moisture, a solvent, or another volatile component is evaporated, organic material is vaporized, or any combination thereof. The initial heating can be conducted at a temperature in a range of

approximately 100 °C to approximately 300 °C for a time period in a range of approximately 2 hours to approximately 400 hours. Following the initial heating, the sintering can be performed at a temperature in a range of approximately 1400 °C to approximately 1700 C for a time period in a range of approximately 10 hours to approximately 100 hours to form the body of the refractory object. In a particular embodiment, the sintering can be performed at a temperature no greater than approximately 1650 °C or no greater than approximately 1600 °C. During sintering, some shrinkage may occur, and the body may be smaller than the green body.

The sintering may be performed in an open container, such as an open muffle, or a closed container, such as a closed muffle. A closed container may help to keep the beta alumina from changing to alpha- AI₂O₃. Some of the dopants used in beta alumina, such as Na₂0 may be volatilized during the relatively high temperatures for sintering. As the dopant is lost, the beta alumina may change to alpha- A1₂0₃. When a closed container is used, the ambient may include a source separate from the refractory object that provides an additional amount of the metal element that can help to reduce the amount of beta alumina that changes to alpha- A1₂0₃ during sintering of the refractory object. For example, when the beta alumina includes Na, the closed container can include a source that provides an additional amount of Na to help reduce volatile losses of Na₂0 when the beta alumina is sintered. The additional amount of Na can be provided in the form of a saturated atmosphere of NaOH, a Na salt, a sodium aluminate, beta alumina (located outside the body), or the like.

If the body of the refractory object was sintered, a surface portion of the body may have some of the beta alumina converted to alpha- A1₂0₃, or may have a lower beta alumina content as compared to the beta alumina content at the center of the body. The surface portion may be at least approximately 2 μιη thick, at least approximately 20 μιη thick, at least approximately 50 μιη thick, or at least approximately 110 μιη thick, or even thicker, such as up to 4 mm thick. The surface portion can be removed, so that an exposed surface of the body has relatively higher beta alumina than if the surface portion was not removed.

The body of the refractory object may be formed using a casting technique, such as fusion casting. Alpha-Al₂0₃, beta alumina, sodium aluminate, another alumina compound, another source of a beta conversion material (e.g., Na₂0) or any

combination thereof, may be used. The starting materials are combined and heated to form a molten composition. In an embodiment, the heating can be performed as electrical arc heating. The molten composition is then cast into a mold and the molten composition is allowed to cool to form the body. The body can then be removed from the mold and can be machined down to form the isopipe.

In an embodiment as illustrated in FIG. 1, a body of a refractory object 100 can be a refractory block 102 having a rectilinear shape having a length (1), width (w), and height (h). In an embodiment, any of the dimensions 1, w, or h can be at least approximately 0.02 m, at least approximately 0.05 m, at least approximately 0.11 m, at least approximately 0.5 m, at least approximately 1.1 m, at least approximately 2.0 m, at least approximately 4.0 m, at least approximately 5.0 m, at least approximately 6.0 m, or more. In the embodiment as illustrated in FIG. 1, the refractory block 102 can be a blank from which a glass overflow forming block can be formed.

The refractory block 102 can be machined to produce a different shape, a smoother surface, or both. The refractory block 102 can be machined to form a glass overflow forming block 200, as illustrated in FIG. 2. The glass overflow forming block 200, which is also a refractory object, includes a glass overflow trough portion 202 and a tapered portion 204. The glass overflow trough portion 202 includes a trough that has a depth that decreases along a length of the glass overflow forming block 200. FIG. 3 includes a cross-sectional view of exemplary shapes of the tapered portion 204. More particularly, the tapered portion can include a wedge shape 2042, a concave shape

2044, or a convex shape 2046. Other shapes may be used to meet the needs or desires for a particular application.

In an embodiment, a refractory object 400 that includes a body 420 without any coating, is illustrated in FIG. 4. In yet another embodiment, the refractory object may include a coating that includes beta alumina that covers a body having a different composition. FIG. 5 includes an illustration of a refractory object 500 that includes a body 520 and a coating 540. The body 520 can include substantially no or a lower content of beta alumina than the coating. The composition of the body 520 may be selected on the basis of a lower creep rate, better mechanical integrity at temperatures used for molten glass, a coefficient of thermal expansion ("CTE") closer to beta alumina as compared to other compositions that can be used, another suitable characteristic, or any combination thereof. The body 520 can include alpha-Al₂0₃, a mixture of alpha- A1₂0₃ and beta alumina, a zircon, a mullite, SiC, or any combination thereof. In a particular embodiment, the body 520 can include at least approximately 50 wt , at least approximately 75 wt , at least approximately 85 wt , at

approximately least 90 wt , or at least approximately 95 wt alpha- A1₂0₃. Any of the foregoing materials for the body 520 may include one or more dopants for a sintering agent, particle size control, another desirable characteristic, or any combination thereof.

The coating 540 may be formed by vapor deposition (chemical or physical), plasma spray, flame spray of a beta alumina powder, formed from the deposition of a slurry, another suitable coating technique, or the like. The coating 540 can be annealed if needed or desired. In an embodiment, the coating 540 can have a thickness of at least approximately 100 μιη, at least approximately 250 μιη, or at least approximately 500 μιη. In another embodiment, the coating 540 can have a thickness no greater than approximately 5000 μιη, no greater than approximately 1500 μιη, or no greater than approximately 900 μιη.

In an embodiment, the coating can be a single layer having a substantially uniform composition, such as the coating 540 in FIG. 5. In another embodiment, the coating can include a plurality of layers having different compositions. FIG. 6 includes an illustration of a portion of a refractory object 600 that includes the body 520 and a coating 640. The coating 640 includes layers 642, 644, and 646. The number of layers within the plurality of layers can include 2, 3, 4, 5, 9, 11, or even more. The plurality of layers may help to accommodate a CTE mismatch between the composition of the body 520 and beta alumina. More particularly, the layer 642 may have a CTE closer to the CTE of the body 520 than the CTE of the layer 646, and the layer 644 may have a CTE closer to the CTE of the layer 646 than the CTE of the body 520.

In another embodiment, when the body 520 comprises alpha- AI₂O₃, the opposing surfaces of the coating 640 can have a higher alpha- Al₂0₃:beta alumina ratio near the surface closer to the body 520 and a lower alpha- Al₂0₃:beta alumina ratio near the opposing surface. In the embodiment as illustrated in FIG. 6, the layers 642, 644, and 646 can have different alpha- Al₂0₃:beta alumina ratios, such that the alpha- Al₂0₃:beta alumina ratio of the layer 644 is less than the alpha- Al₂0₃:beta alumina ratio of the layer 642 and greater than the alpha- Al₂0₃:beta alumina ratio of the layer 646. In a particular embodiment, the body can include at least 80 wt alpha- AI₂O₃, and the layer 646, which is at the exposed surface of the refractory object 600, can include at least 80 wt beta alumina. In a particular embodiment, the layer 646 is substantially at least approximately 95 wt beta alumina and includes substantially no alpha- AI₂O₃. The layer 644 can have a lower beta alumina content as compared to the layer 646, and the layer 642 can have a lower beta alumina content and a higher alpha- AI₂O₃ content as compared to the layer 644. In another embodiment, a layer can have a composition that changes continuously as a function of thickness, such that beta alumina content increases with increasing thickness. When the body 520 is mostly a non-alumina material, the coating can include beta alumina and the material of the body or yet another material that is compatible (i.e., does not adversely interact) with beta alumina and the body 520

In a finished refractory object, an exposed surface, whether the body (without a coating) or the coating, can include alumina, wherein the beta alumina makes up at least approximately 50%, at least approximately 75%, at least approximately 85%, at approximately least 90%, at least approximately 95% of the total AI₂O₃ content within the refractory object.

The refractory object may have one or more properties that are particularly noteworthy. Such properties can include little or no significant formation of a Mg-Al oxide layer between the body or coating of the refractory object and an Al-Si-Mg glass. Other properties, such as density and porosity, are also addressed.

When a molten alkali Al-Si-Mg glass comes in contact with beta alumina, no significant amount of a Mg-Al oxide layer forms. Thus, beta alumina can be compared to alpha- AI₂O₃ in which a Mg-Al oxide layer can form when a molten alkali Al-Si-Mg glass is exposed to alpha- A1₂0₃. The formation of the Mg-Al oxide layer may subsequently lead to a part of the Mg-Al oxide layer entering the molten glass and cause a defect in a glass sheet being formed. Thus, the beta alumina and glass can form a relatively clean interface without an intermediate layer forming between the two.

Density and porosity of the refractory object can be determined using ASTM C20-00 Standard Test Method (reapproved 2005). The density of beta alumina depends in part on the dopant in the beta alumina. For example, a beta alumina that includes Na may have a lower density than a beta alumina that includes a rare earth element, such as Sc, La or the like. In an embodiment, the density can be at least approximately 2.50 g/cc, at least approximately 2.60 g/cc, at least approximately 2.80 g/cc, or at least approximately 3.00 g/cc. In another embodiment, the density may be no greater than approximately 3.90 g/cc, no greater than approximately 3.70 g/cc, or no greater than approximately 3.50 g/cc. In an embodiment, the porosity is expressed as a volume percent ("vol%"). In an embodiment, the porosity of the refractory object is at least approximately 0.1 vol%, at least approximately 1 vol%, or at least approximately 5 vol . In another embodiment, the porosity is no greater than approximately 20 vol , no greater than approximately 10 vol , no greater than approximately 7 vol , no greater than approximately 2 vol .

The refractory object, when in the form of a glass overflow forming block, can be useful in forming a glass sheet by a fusion process. FIGs. 7 and 8 include a perspective view and a cross-sectional view, respectively, of the glass overflow forming block during the formation of a glass sheet 302. The glass overflow forming block is heated to a temperature in a range of approximately 1050 °C to approximately 1300 °C. The glass overflow forming block includes the glass overflow trough portion 202 and the tapered portion 204, as previously described. In the embodiment as illustrated, the glass overflow forming block also includes end guards 206 that generally define the width of the glass sheet 302 to be formed. The glass overflow forming block further includes an inlet port 208 that receives a molten glass composition. A trough within the glass overflow trough portion 202 receives the molten glass composition until the trough fills up. Thereafter, the molten glass composition flows over opposing lips of the glass overflow trough portion 202. The molten glass composition then flows along opposite outer surfaces of the glass overflow trough portion 202 and the tapered portion 204. At the end of the tapered portion 204 that is opposite the glass overflow trough potion 202, the molten glass composition along the opposite outer surfaces fuse together to form the glass sheet 302. In another embodiment, another type of glass object may be formed.

In an embodiment, the glass sheet 302 can have a thickness of at least approximately 20 μιη, at least approximately 30 μιη, or at least approximately 50 μιη. In another embodiment, the glass sheet 302 may have a thickness no greater than approximately 5 mm, no greater than approximately 3 mm, or no greater than approximately 1.1 mm.

With respect to the width, the process allows the end guards 206 to be set to permit any desired width of the glass sheet 302. For example, the glass sheet 302 can have a width of at least approximately 0.5 m, at least approximately 1.1 m, at least approximately 2.0 m, at least approximately 4.0 m, or larger. In a particular embodiment, the molten glass composition includes an Al-Mg-Si glass. In a more particular embodiment, the molten glass composition is substantially the same as described. Referring to FIG. 8, a Mg-Al oxide does not form along a surface of the refractory object when the surface is exposed to a molten glass including an Al- Si-Mg oxide.

Many different aspects and embodiments are possible. Some of those aspects and embodiments are described herein. After reading this specification, skilled artisans will appreciate that those aspects and embodiments are only illustrative and do not limit the scope of the present invention. In a first aspect, a refractory object can comprise AI₂O₃, and at least approximately

50% of the AI₂O₃ includes a beta alumina, wherein the refractory object can be used in a glass fusion process.

In a second aspect, a refractory object can have a total AI₂O₃ content of at least 10 % by weight. A Mg-Al oxide may not form along a surface of the refractory object when the surface is exposed to a molten glass that includes an Al-Si-Mg oxide. The refractory object can be used in a glass fusion process.

In a third aspect, a process of forming a refractory object can include preparing a body that includes AI₂O₃ and at least approximately 50% of the AI₂O₃ includes a beta alumina. The process can also include sintering the body to form the refractory object. The refractory object can be used in a glass fusion process.

In an embodiment of the third aspect, sintering is performed at a temperature no greater than approximately 1700 °C, no greater than approximately 1650°C, or no greater than approximately 1600 °C. In a particular embodiment, sintering is performed in an open container or a closed container. In a more particular embodiment, sintering is performed in an ambient including a vapor that includes a Group 1 element, a Group 2 element, a rare earth element, Pb, or any combination thereof provided by a source separate from the refractory object. In still another embodiment of the third aspect, the process further includes milling a number of powders that are provided to form the refractory object. Milling the number of powders can produce a milled powder that includes each of the number of powders. In a particular embodiment, milling is performed as dry milling, wet milling, or any combination thereof. In another particular embodiment, a D10 value of a particle size of the milled powder is no greater than approximately 9 microns, no greater than approximately 3 microns, no greater than approximately 2 microns, or no greater than approximately 0.9 microns. In addition, a D50 value of the particle size of the milled powder is no greater than approximately 20 microns, no greater than approximately 12 microns, no greater than approximately 9 microns, no greater than approximately 3 microns no greater than approximately 2 microns, or no greater than approximately 0.9 microns. Further, a D90 value of the particle size of the milled powder is no greater than approximately 90 microns, no greater than approximately 40 microns, no greater than approximately 30 microns, no greater than approximately 9 microns, or no greater than approximately 2 microns. In a further particular embodiment, the milled powder includes alpha- A1₂0₃, beta alumina, or any combination thereof. In yet a further particular embodiment, after milling, the milled powder has a specific surface area of at least approximately 0.5 m 2 /g, at least approximately 0.9 m 2 /g, at least approximately

1.1 m 2 /g, or at least approximately 1.5 m 2 /g. In a fourth aspect, a process of forming a refractory object can include melting a powder to form a molten composition, wherein the powder includes an alpha- A1₂0₃ and a beta conversion material; a beta alumina; or any combination thereof. The process can also include filling a mold with the molten composition, wherein the mold has a pattern corresponding to the refractory object, and cooling the refractory object, wherein the refractory object includes a beta alumina and is capable of being used in a glass fusion process.

In an embodiment of the foregoing aspects and embodiments, the beta conversion material includes a Group 1 element, a Group 2 element, a rare earth element, Pb, or any combination thereof. In another embodiment, the process further includes sintering the refractory object. In a further embodiment of any of the foregoing aspects and embodiments, the process further includes shaping the refractory object into a glass overflow forming block.

In a fifth aspect, a process for forming a refractory object used in forming a glass object can include forming a body that includes a refractory material and forming a coating over the body. The coating can include a beta alumina, and the coating and refractory material have different compositions.

In a sixth aspect, a process of forming a glass object can include providing a refractory object that includes a glass overflow forming block that includes a beta alumina at a surface of the glass overflow forming block, and flowing a glass material including an Al-Si-Mg oxide into the glass overflow forming block and over a lip of the glass overflow forming block. The glass material can contact the beta alumina. During the flowing of the glass material, a Mg-Al oxide may not form along the beta alumina at the surface of the glass overflow forming block.

In an embodiment of the sixth aspect, the glass object is in a form of a glass sheet. In a particular embodiment, the glass sheet has a thickness of at least approximately 20 μιη, at least approximately 30 μιη, or at least approximately 50 μιη. In another particular embodiment, the glass sheet has a thickness no greater than approximately 5 mm, no greater than approximately 3 mm, or no greater than approximately 1.1 mm. In still another particular embodiment, the glass sheet has a width of at least approximately 0.2 m, at least approximately 0.5 m, at least approximately 0.7 m, at least approximately 1.1 m, at least approximately 2.0 m, at least approximately 2.4 m, or at least approximately 2.8 m. In another embodiment, the glass object includes an alkali glass.

In a particular embodiment of any of the embodiments or aspects described herein, a Mg-Al oxide does not form along a surface of the refractory object when the surface is exposed to a molten glass that includes an Al-Si-Mg oxide. In another embodiment, the refractory object includes a glass overflow forming block. In still another embodiment, the glass overflow forming block has a cross section in a shape that is tapered from the bottom of the glass overflow forming block. In a particular embodiment, the glass overflow forming block has a cross section in a shape of a wedge. In yet another embodiment, the refractory object can have a total AI₂O₃ content of at least

approximately 80%, at least approximately 90%, or at least approximately 95%. In a further embodiment, the beta alumina makes up at least approximately 50%, at least approximately 70%, at approximately least 90%, at least approximately 95% of the total alumina content within the refractory object.

In a particular embodiment of any of the embodiments or aspects described herein, the refractory object includes a body and a coating along at least a portion of the body, wherein the coating includes the beta alumina. In a more particular embodiment, the coating has a thickness no greater than approximately 5000 μιη, no greater than approximately 1500 μιη, or no greater than approximately 900 μιη. In another more particular embodiment, the coating has a thickness of at least approximately 100 μιη, at least approximately 250 μιη, or at least approximately 500 μιη.

In a particular embodiment of any of the embodiments or aspects described herein, the coating includes a single layer or a plurality of layers. In a more particular

embodiment, the coating has a substantially uniform composition. In another more particular embodiment, the plurality of layers includes an inner layer and outer layer, wherein the inner layer is disposed between the body and the outer layer, and the coefficient of thermal expansion of the inner layer is between the coefficients of thermal expansion of the body and the outer layer. In a further more particular embodiment, the coating has a first surface and a second surface opposite the first surface, where the first surface is closer to the body than the second surface. The coating can have a first alpha- Al₂0₃:beta alumina ratio near the first surface and a second alpha- Al₂0₃:beta alumina ratio near the second surface. In an embodiment, the first alpha- Al₂0₃:beta alumina ratio is greater than the second alpha- Al₂0₃:beta alumina ratio. In an even more particular embodiment, the coating has an intermediate region spaced apart from the first surface and the second surface, where the intermediate region has an intermediate alpha- Al₂0₃:beta alumina ratio that is less than the first alpha- Al₂0₃:beta alumina ratio and greater than the second alpha- Al₂0₃:beta alumina ratio. In a particular embodiment of any of the embodiments or aspects described herein, the body includes zircon, mullite, SiC, alpha- AI₂O₃, beta alumina, or any combination thereof. In a more particular embodiment, the body includes at least approximately 40 wt , at least approximately 50 wt , at least approximately 70 wt , at approximately least 90 wt , or at least 95 wt alpha-Al₂0₃. In another particular embodiment, the refractory object includes a first dopant that includes a Group 1 element, a Group 2 element, a rare earth element, Pb, or any combination thereof. In a more particular embodiment, the first dopant includes Na, K, Li, Cs, Mg, Ba, Sr, Pb, Sc, La, Pr, Nd, or any combination thereof. In another more particular embodiment, the refractory object includes no greater than approximately 26 mol , no greater than approximately 17 mol , or no greater than approximately 13 mol of the first dopant. In a further more particular embodiment, the refractory object includes at least approximately 2.1 mol , at least approximately 2.5 mol , or at least approximately 4.5 mol of the first dopant.

In a particular embodiment of any of the embodiments or aspects described herein, the refractory object includes a sintering agent. In a more particular embodiment, the sintering agent includes Ta, Nb, Ti, Fe, Mn, Cu, or any combination thereof. In another particular embodiment, the refractory object includes a second dopant that includes a rare earth element, Ta, Nb, Mg, Zr, Hf, Zn, or any combination thereof. In a more particular embodiment, the rare earth element includes Y, Sc, Yb, Pr, Sm, Gd, La, Ce, Dy, or any combination thereof. In a further particular embodiment, the sintering agent is different from the second dopant.

In a particular embodiment of any of the embodiments or aspects described herein, the refractory object has a density of at least approximately 2.50 g/cc, at least

approximately 2.60 g/cc, at least approximately 2.80 g/cc, or at least approximately 3.00 g/cc. In another particular embodiment, the refractory object has a density no greater than approximately 3.90 g/cc, no greater than approximately 3.70 g/cc, or no greater than approximately 3.50 g/cc. In still another particular embodiment, the refractory object has a porosity of at least approximately 0.1 vol , at least

approximately 1 vol , or at least approximately 5 vol . In yet another particular embodiment, the refractory object has a porosity no greater than approximately 20 vol , no greater than approximately 10 vol , no greater than approximately 7 vol , no greater than approximately 2 vol .

In a particular embodiment of any of the embodiments or aspects described herein, the refractory object includes Ti0₂, CaO, Si0₂, Fe₂0₃, Na₂0, or any combination thereof, at a concentration of no greater than approximately 2 wt , no greater than

approximately 1.5 wt , no greater than approximately 0.9 wt , or no greater than approximately 0.5 wt %. In another particular embodiment, the refractory object has no coating. In a further particular embodiment, the refractory object has a length of at least approximately 0.5 m, at least approximately 1.1 m, at least approximately 2.0 m, at least approximately 4.0 m, at least approximately 5.0 m, or at least approximately 6 m.

EXAMPLES

The concepts described herein will be further described in the following examples, which do not limit the scope of the features described in the claims. Numerical values in this Examples section may be approximated or rounded off for convenience.

Refractory objects including a variety of different sintered ceramic materials are prepared using the following process and following raw materials. Table 1 includes the compositions of samples, all of which are principally alumina containing. Trace levels of impurities may be present but are not reported, as such impurities typically do not significantly affect the performance of such samples.

The samples of different beta alumina refractories materials have compositions and properties as set forth in Table 1. Table 1

The samples are put in contact with a molten glass composition at 1150 °C for 120 hours without any significant relative motion between the samples and the molten glass composition (static test). The molten glass composition includes 61.9 wt% Si0₂, 17.5 wt% A1₂0₃, 12.6 wt% Na₂0, 3.5 wt% K₂0, and 3.5 wt% MgO.

FIG. 9 includes a scanning electron microscope ("SEM") image of the Jargal-M™- brand refractory and the glass after the static test. Where the glass 92 contacts the beta alumina 94, there is no layer between the glass 92 and beta alumina 94. At locations wherein beta alumina 94 does not lie between the portions of the alpha- A1₂0₃ 96, a spinel layer 98 (within the oval as illustrated in FIG. 9) is formed between the alpha- A1₂0₃ 96 and glass 92.

FIG. 10 includes a SEM image of the Jargal H™-brand refractory 101 and the glass 103 after the static test. As illustrated in FIG. 10, the glass 103 contacts the beta alumina 101 and there is no layer between the glass 103 and beta alumina 101. Neither a separate alpha- A1₂0₃ phase nor a spinel layer is present in the SEM image. FIG. 11 includes a SEM image of the beta alumina with MgO refractory 111 and the glass 113 after the static test. As illustrated in FIG. 11, the glass 113 contacts the refractory 111 and there is no layer between the glass 113 and the refractory 111.

Neither a separate alpha- A1₂0₃ phase nor a spinel layer is present in the SEM image.

Unlike alpha- A1₂0₃, a spinel layer does not form between the beta alumina and the molten glass composition during static tests. Therefore, the glass formed using beta alumina refractory will not have defects from a spinel layer because a spinel layer is not formed.

Further samples are formed using different preparation and sintering conditions. Three different milling conditions are used. A1₂0₃ dry milling ("A1₂0₃ Dry") includes milling pieces of a refractory material for 30 minutes in a planetary mill with an alpha- A1₂0₃ jar and an alpha-Al₂0₃ grinding medium. Zr0₂ dry milling ("Zr0₂ Dry") is the same as A1₂0₃ dry milling except the alpha- A1₂0₃ jar and an alpha- A1₂0₃ grinding medium are replaced with a Zr0₂ jar and a Zr0₂ grinding medium. Both A1₂0₃ and Zr0₂ dry milling are performed without a liquid, such as water. A1₂0₃ wet milling ("A1₂0₃ Wet") includes milling pieces of a refractory material using alpha- A1₂0₃ jar on rollers and an alpha- A1₂0₃ grinding medium and water. Table 2 includes particle distribution data for the powders after milling.

Table 2

The wet milling provides smaller particles and a more tightly distributed particle size, as 90% of all particles have a particle size of 1.39 microns or smaller. After milling, of the alumina within the milled powder, 41% is alpha-Al₂0₃ and 59% is beta alumina. The samples are made using powders from different milling conditions and using different sintering conditions. Some samples are subject to x-ray diffraction analysis and chemistry to obtain the information for determining how much of the AI₂O₃ within the sintered material is alpha- AI₂O₃ and beta alumina.

After milling, the powders are isopressed to form pellets having an average mass of approximately 25 g. The pellets are sintered using one of four different sintering conditions as listed below:

1600 °C for 10 hours in an open container, wherein the ambient is air;

1600 °C for 10 hours in a closed container, wherein the ambient is air and filled with pieces of Jargal-M™-brand refractory to saturate the atmosphere with NaOH;

1700 °C for 10 hours in an open container, wherein the ambient is air;

1700 °C for 10 hours in a closed container, wherein the ambient is air and filled with pieces of Jargal- M™-brand refractory ("JM") to saturate the atmosphere with NaOH. FIG. 12 includes a table for a set of samples that are formed from pieces of Jargal-M™- brand or Jargal-H™-brand refractory. Samples 1 to 20 are formed from fuse-cast pieces of Jargal-M™-brand that is milled into a powder, and Samples 21 to 23 are formed from fuse-cast pieces of Jargal-H™-brand refractory that is milled into a powder. For the Jargal-M™-brand refractory samples, some of the samples are only AI₂O₃ dry milled (Samples 1 and 2), other samples are AI₂O₃ dry milled and Zr0₂ dry milled (Samples 3 to 8), and further samples are A1₂0₃ dry milled, Zr0₂ dry milled, and A1₂0₃ wet milled (Samples 9 to 20). Some of the samples include approximately 1 wt% ZnO (Samples 7, 8, and 17 to 20) or approximately 1 wt% MgO (Samples 5, 6, and 13 to 16). Samples 13 and 14 are re-tested for porosity and density. Samples 21 to 23 (Jargal-H™-brand refractory) are wet milled. Sample 21 does not include any added ZnO or MgO, Sample 22 includes approximately 1 wt% MgO, and Sample 23 includes approximately 1 wt% ZnO.

Some observations are made in view of the data within the table in FIG. 12. The observations with respect to Jargal-M™-brand refractory are presented before the observations with respect Jargal-H™-brand refractory ("JH").

For the Jargal-M™-brand refractory, unexpectedly, the wet-milled samples retain significantly more beta alumina as compared to the dry-milled samples. The unmilled powders have approximately 59% beta alumina. The MgO-containing wet-milled sample has the lowest beta alumina loss where the beta alumina is approximately 57%. The ZnO-containing wet-milled samples have lower beta alumina loss as compared to the wet-milled samples without any Mg or Zn. The dry-milled sample lost more than twice as much A1₂0₃ as compared to the wet-milled samples.

For the Jargal-M™-brand refractory, the porosity is higher and the density is lower for the samples that are only dry milled, as compared to samples that are wet milled. The samples that are wet milled have a smaller particle size as compared to the samples that are dry milled, due to the different milling conditions. When comparing the dry-milled samples between one another, the samples that are only A1₂0₃ dry milled have about the same porosity and density as compared to samples that are AI₂O₃ dry milled and Zr0₂ dry milled.

For the Jargal-M™-brand refractory, the addition of MgO helps to reduce porosity for samples that are wet milled. The porosity for the MgO-containing, wet-milled samples is no greater than approximately 0.04 vol when sintered at approximately 1600 °C and no greater than approximately 1.75 vol when sintered at approximately 1700 °C. Compare the MgO-containing, wet-milled samples with the other wet milled samples, in which porosity is at least approximately 0.36 vol when sintered at approximately 1600 °C and at least approximately 4.95 vol when sintered at approximately 1700 °C. The data is insufficient to make any observations of the density between the different wet-milled samples. The addition of MgO or ZnO does not appear to have a significant effect on the porosity and density for the dry- milled samples.

For the wet-milled samples using the Jargal-M™-brand refractory, samples sintered at the lower sintering temperature (approximately 1600 °C) have a lower porosity and a higher density as compared to samples sintered at the higher sintering temperature

(approximately 1700 °C). The porosity for the wet samples sintered at approximately 1700 °C have a porosity that is at least 5 times higher than the wet samples sintered at approximately 1600 °C. In particular, Sample 12 has a porosity that is approximately 7.8 times higher than the porosity of Sample 10, both of which do not include any added ZnO or MgO and are sintered in a closed container with Jargal-M™-brand refractory. For the MgO-containing wet-milled samples, Sample 15 has a porosity that is approximately 39 times higher than the porosity of Sample 13 ((Retest of density and porosity). For the ZnO-containing wet-milled samples, Sample 19 has a porosity that is approximately 12 times higher than the porosity of Sample 17. Note that other samples within each of the three different groups have an even greater difference in porosity at the different sintering temperatures, when all other parameters are held constant. With respect to density, the difference between sintering at approximately 1600 °C and approximately 1700 °C is seen with the data; however, the difference is not as large as it is for the porosity. For the dry-milled samples using the Jargal-M™-brand refractory, the sintering temperature does not appear to have a significant effect on the porosity or density.

The addition of Jargal-M™-brand refractory to the closed sintering environment appears to have a small effect on the porosity. For the wet-milled samples, the addition of Jargal-M™-brand refractory appears to have lower porosity as compared to the samples having the same composition and sintering conditions. For example, Sample 9 has a porosity of approximately 0.36 vol , and Sample 10 has a porosity of approximately 0.72 vol , and Sample 15 has a porosity of approximately 1.54 vol , and Sample 16 has a porosity of approximately 1.75 vol . The data for the dry-milled samples do not appear to have any correlation between the addition of Jargal-M™- brand refractory and porosity.

The addition of Jargal-M™-brand refractory does not appear to have a correlation to the density for both the dry-milled and wet-milled samples.

For the wet-milled samples using the Jargal-M™-brand refractory, samples sintered at the lower sintering temperature (approximately 1600 °C) have a lower porosity and a higher density as compared to samples sintered at the higher sintering temperature (approximately 1700 °C). The porosity for the wet samples sintered at approximately 1700 °C have a porosity that is at least 5 times higher than the wet samples sintered at approximately 1600 °C. In particular, Sample 11 has a porosity that is approximately 6.9 times higher than the porosity of Sample 10, both of which did not include any added ZnO or MgO. For the MgO-containing wet-milled samples, Sample 15 has a porosity that is approximately 39 times higher than the porosity of Sample 13 (Retest). For the ZnO-containing wet-milled samples, Sample 19 has a porosity that is approximately 39 times higher than the porosity of Sample 18. Note that other samples within each of the three different groups have an even greater difference in porosity at the different sintering temperatures. Dry- milled samples are not sintered at different temperatures, and therefore, the effect of sintering temperature on porosity and density is unknown. The observations for the Jargal-H™-brand refractory are quite different as compared to the Jargal-M™-brand refractory. The shrinkage during sintering is approximately 16 %. Whereas the addition of MgO to the Jargal-M™-brand refractory has lower porosity and higher density, for the Jargal-H™-brand refractory, the opposite effect is seen. In particular, Sample 22 (approximately 1 wt MgO) has a porosity of approximately 4.00 vol and a density of 3.05 g/cc. Sample 21 (undoped) has a porosity of approximately 0.39 vol and a density of 3.23 g/cc. With respect to porosity and density, Sample 23 (approximately 2 wt ZnO) is between but much closer to Sample 21 as compared to Sample 22. Sample 23 has a porosity of approximately 0.67 vol and a density of 3.19 g/cc. More samples with Jargal-H™- brand refractory may be tested to determine the effect of sintering temperature (e.g., 1700°C) and sintering environment (e.g., closed with pieces of Jargal-M™-brand or Jargal-M™-brand refractory) on the porosity and density.

Additional samples 24-27 are formed according to techniques described herein. In particular, samples are prepared by combining powders having the compositions indicated in Table 3. The samples are formed by mixing the beta- alumina powder and the powders of any dopants, such as Ta₂0₅, Y₂0₃, or ZnO, with water to form a slurry. The beta-alumina powder is previously jet milled, such that the particles have a D50 within a range of approximately 2.9 microns and approximately 3.8 microns. In the case of sample 31, the beta-alumina powder is also wet milled. The slurry is then spray dried with binders and other additives and used to form a green body by isostatic pressing having dimensions of 2x2x5 inches. The green body is then fired in air for approximately 15 days on a suitable cycle and then sintered at a temperature within a range of 1560°C to 1640°C for a period within a range of 29 hours to 31 hours. The beta-alumina powder comprising samples 24-27 includes A1₂0₃ within a range of approximately 93.2 wt and approximately 94.4 wt , Na₂0 within a range of approximately 5.3 wt and approximately 6.5 wt , Si0₂ within a range of

approximately 0.07 wt and approximately 0.13 wt . In addition, the beta- alumina of samples 24-27 includes a combined content of CaO, MgO, and Fe₂0₃ within a range of approximately 1.6 wt and 2.4 wt . Table 3

Table 4 indicates density and porosity data of the samples 24-27 and Table 5 indicates the composition of crystalline phases of portions of samples 24 and 27. The crystalline phase data is obtained using X-ray diffraction techniques. Table 4 indicates that Sample 24, which is prepared with Ta^s_, is more dense and less porous than samples 25, 26, and 27. Additionally, the data in Table 5 indicates that a reaction layer forms on portions of the respective samples where a portion of the beta-alumina converts to corundum during preparation of the respective samples. The reaction layer is less than approximately 4 mm deep in the portions of samples 24 and 27 being measured. Below the reaction layer, the A1₂0₃ of the samples remains in the beta-alumina phase.

FIG. 13 is an X-ray diffraction image illustrating a cross-sectional view of an interface between a portion of a sample having the composition of sample 24 and a portion of an alkali Al-Mg-Si glass 131. Ta₂0₅ is illustrated in FIG. 13 as white segments, such as exemplary white segment 133. In the view of the sample shown in FIG. 13, the beta alumina phase 135 did not convert to corundum when exposed to molten alkali Al-Mg- Si glass. Further, a Mg-Al oxide layer is absent from the portion of the sample illustrated in FIG. 13. In addition, FIG. 13 illustrates a number of pores, such as exemplary pore 137. FIG. 14 is an X-ray diffraction image illustrating a cross-sectional view of a portion of the body of the sample of FIG. 13. The view of FIG. 14 illustrates a portion of the sample that is set apart from the interface with the Al-Mg-Si glass. The portion of the sample illustrated in FIG. 14 includes segments of Ta₂0₅, such as exemplary segment 141, and a beta-alumina phase 143. Additionally, the portion of the sample illustrated in FIG. 14 includes a number of pores, such as exemplary pore 145.

Table 4

Table 5

Note that not all of the activities described above in the general description or the examples are required, that a portion of a specific activity may not be required, and that one or more further activities may be performed in addition to those described. Still further, the order in which activities are listed is not necessarily the order in which they are performed.

Benefits, other advantages, and solutions to problems have been described above with regard to specific embodiments. However, the benefits, advantages, solutions to problems, and any feature(s) that may cause any benefit, advantage, or solution to occur or become more pronounced are not to be construed as a critical, required, or essential feature of any or all the claims.

The specification and illustrations of the embodiments described herein are intended to provide a general understanding of the structure of the various embodiments. The specification and illustrations are not intended to serve as an exhaustive and

comprehensive description of all of the elements and features of apparatus and systems that use the structures or methods described herein. Separate embodiments may also be provided in combination in a single embodiment, and conversely, various features that are, for brevity, described in the context of a single embodiment, may also be provided separately or in any subcombination. Further, reference to values stated in ranges includes each and every value within that range. Many other embodiments may be apparent to skilled artisans only after reading this specification. Other embodiments may be used and derived from the disclosure, such that a structural substitution, logical substitution, or another change may be made without departing from the scope of the disclosure. Accordingly, the disclosure is to be regarded as illustrative rather than restrictive.

Claims

WHAT IS CLAIMED IS:

1. A refractory object comprising AI₂O₃, wherein at least approximately 50% of the

AI₂O₃ comprises a beta alumina, and wherein the refractory object is capable of being used in a glass fusion process.

2. A refractory object comprising a total AI₂O₃ content of at least 10 % by weight,

wherein:

a Mg-Al oxide does not form along a surface of the refractory object when the surface is exposed to a molten glass including an Al-Si-Mg oxide; and the refractory object is capable of being used in a glass fusion process.

3. A process of forming a refractory object comprising:

preparing a body including AI₂O₃, wherein at least approximately 50% of the

AI₂O₃ comprises a beta alumina; and

sintering the body to form the refractory object,

wherein the refractory object is capable of being used in a glass fusion process.

4. The process according to claims 3, wherein sintering is performed at a temperature no greater than approximately 1700 °C, no greater than approximately 1650°C, or no greater than approximately 1600 °C.

5. The process according to claim 4, wherein sintering is performed in an open container.

6. The process according to claim 4, wherein sintering is performed in a closed

container.

7. The process according to claim 6, wherein sintering is performed in an ambient

including a vapor that includes a Group 1 element, a Group 2 element, a rare earth element, Pb, or any combination thereof provided by a source separate from the refractory object.

8. The process according to any one of claims 3 to 7, further comprising milling a number of powders to form a milled powder, wherein the body comprises the milled powder.

9. The process according to claim 8, wherein the milling is performed as dry milling, wet milling, or any combination thereof.

10. The process according to claim 8 or 9, wherein:

a D10 value of a particle size of the milled powder is no greater than

approximately 9 microns, no greater than approximately 3 microns, no greater than approximately 2 microns, or no greater than approximately 0.9 microns;

a D50 value of the particle size of the milled powder is no greater than

approximately 20 microns, no greater than approximately 12 microns, no greater than approximately 9 microns, no greater than approximately 3 microns, no greater than approximately 2 microns, or no greater than approximately 0.9 microns;

a D90 value of the particle size of the milled powder is no greater than

approximately 90 microns, no greater than approximately 40 microns, no greater than approximately 30 microns, or no greater than approximately 9 microns, no greater than approximately 2 microns; or

any combination thereof.

11. The process according to claim 8, 9, or 10, wherein the milled powder includes

alpha- AI2O3, beta alumina, or any combination thereof.

12. The process according to claim 8, 9, 10, or 11, wherein the milled powder has a

specific surface area of at least 0.5 m 2 /g, at least approximately 0.9 m 2 /g, at least approximately 1.1 m 2 /g, or at least approximately 1.5 m 2 /g.

13. A process of forming a refractory object, wherein the process comprises:

melting a powder to form a molten composition, wherein the powder includes: an alpha- AI₂O₃ and a beta conversion material;

a beta alumina; or

any combination thereof;

filling a mold with the molten composition, wherein the mold has a pattern

corresponding to the refractory object; and

cooling the refractory object, wherein the refractory object comprises beta

alumina and is capable of being used in a glass fusion process, and wherein at least approximately 50% of the total AI₂O₃ content of the refractory object is a beta alumina.

14. The process according to claim 13, wherein the beta conversion material includes a

Group 1 element, a Group 2 element, a rare earth element, Pb, or any combination thereof.

15. The process according to any one of claims 3 to 14, further comprising shaping the refractory object into a glass overflow forming block.

16. A process for forming a refractory object used in forming a glass object comprising: forming a body that includes a refractory material; and

forming a coating over the body, wherein the coating comprises AI₂O₃ and at least approximately 50% of the A1₂0₃ includes a beta alumina, wherein the coating and refractory material have different compositions.

17. A process of forming a glass object comprising:

providing a refractory object that includes a glass overflow forming block

comprising a beta alumina at a surface of the glass overflow forming block; and

flowing a glass material including Al-Si-Mg oxide into the glass overflow

forming block and over a lip of the glass overflow forming block, wherein:

the glass material contacts the beta alumina during the flowing of the glass material; and

a Mg-Al oxide does not form along the beta alumina at the surface.

18. The process according to claim 17, wherein the glass object is in a form of a glass sheet.

19. The process according to claim 18, wherein the glass sheet has a thickness of at least approximately 20 μιη, at least approximately 30 μιη, or at least approximately 50

20. The process according to claim 18, wherein the glass sheet has a thickness no greater than approximately 5 mm, no greater than approximately 3 mm, or no greater than approximately 1.1 mm.

21. The process according to claim 18, wherein the glass sheet has a width of at least approximately 0.2 m, at least approximately 0.5 m, at least approximately 0.7 m, at least approximately 1.1 m, at least approximately 2.0 m, at least approximately 2.4 m, or at least approximately 2.8 m.

22. The process according to claim 17, wherein the glass object includes an alkali glass.

23. The refractory object or the process according to any one of claims 1 and 3 to 22, wherein a Mg-Al oxide does not form along a surface of the refractory object when the surface is exposed to a molten glass including an Al-Si-Mg oxide.

24. The refractory object or the process according to any one of claims 1 to 14 and 16 to

23, wherein the refractory object includes a glass overflow forming block.

25. The refractory object or the process according to any one of the preceding claims, wherein the glass overflow forming block has a cross section in a shape that is tapered from the bottom of the glass overflow forming block.

26. The refractory object or the process according to claim 25, wherein the glass

overflow forming block has a cross section in a shape of a wedge.

27. The refractory object or the process according to any one of the preceding claims, wherein the refractory object comprises a total AI₂O₃ content of at least

approximately 80%, at least approximately 90%, or at least approximately 95%.

28. The refractory object or the process according to any one of the claims 1 to 15 and 17 to 27, wherein the beta alumina makes up at least approximately 70%, at approximately least 90%, at least approximately 95% of the total AI₂O₃ content within the refractory object.

29. The refractory object or the process according to any one of claims 1, 2, and 17 to

27, wherein the refractory object comprises a body and a coating along at least a portion of the body, wherein the coating comprises the beta alumina.

30. The refractory object or the process according to claim 16 or 29, wherein the coating has a thickness no greater than approximately 5000 μιη, no greater than

approximately 1500 μιη, or no greater than approximately 900 μιη.

31. The refractory object or the process according to claim 16, 29, or 30, wherein the coating has a thickness of at least approximately 100 μιη, at least approximately 250 μιη, or at least approximately 500 μιη.

32. The process according to claim 16, 29, 30, or 31, wherein the coating includes a single layer or a plurality of layers.

33. The process according to claim 32, wherein the coating has a substantially uniform composition.

34. The process according to claim 16, 29, 30, or 31, wherein the plurality of layers comprises an inner layer and an outer layer, wherein the inner layer is disposed between the body and the outer layer, and the coefficient of thermal expansion of the inner layer is between the coefficients of thermal expansion of the body and the outer layer.

35. The refractory object or the process according to any one of claims 16 and 29 to 34, wherein:

the coating has a first surface and a second surface opposite the first surface; the first surface is closer to the body than the second surface;

the coating has a first alpha- Al₂0₃:beta alumina ratio near the first surface and a second first alpha- Al₂0₃:beta alumina ratio near the second surface; and the first alpha- Al₂0₃:beta alumina ratio is greater than the second

alpha- Al₂0₃:beta alumina ratio.

36. The refractory object or the process according to claim 35, wherein:

the coating has an intermediate region spaced apart from the first surface and the second surface; and

the intermediate region has an intermediate alpha- Al₂0₃:beta alumina ratio that less than the first alpha- Al₂0₃:beta alumina ratio and greater than the second alpha- Al₂0₃:beta alumina ratio.

37. The refractory object or the process according to any one of claims 1, 2, and 16 to

36, wherein the body comprises zircon, mullite, SiC, alpha-Al₂0₃, beta alumina, or any combination thereof.

38. The refractory object or the process according to any one of claims 1, 2, and 16 to 36, wherein the body comprises at least approximately 40 wt , at least approximately 50 wt , at least approximately 70 wt , at approximately least 90 wt%, or at least 95 wt% alpha- A1₂0₃.

39. The refractory object or the process according to any one of the preceding claims, wherein the refractory object includes a first dopant comprising a Group 1 element, a Group 2 element, a rare earth element, Pb, or any combination thereof.

40. The refractory object or the process according to claim 39, wherein the first dopant comprises Na, K, Li, Cs, Mg, Ba, Sr, Pb, Sc, La, Pr, Nd, or any combination thereof.

41. The refractory object or the process according to claim 39, wherein the refractory object comprises no greater than approximately 26 mol , no greater than approximately 17 mol , or no greater than approximately 13 mol of the first dopant.

42. The refractory object or the process according to claim 39, wherein the refractory object comprises at least approximately 2.1 mol , at least approximately 2.5 mol , or at least approximately 4.5 mol of the first dopant.

43. The refractory object or the process according to any one of the preceding claims, wherein the refractory object includes a sintering agent.

44. The refractory object or the process according to claim 43, wherein the sintering agent comprises Ta, Nb, Ti, Fe, Mn, Cu, or any combination thereof.

45. The refractory object or the process according to any one of the preceding claims, wherein the refractory object includes a second dopant that comprises a rare earth element, Ta, Nb, Mg, Zr, Hf, Zn, or any combination thereof.

46. The refractory object or the process according to claim 45, wherein the rare earth element includes Y, Sc, Yb, Pr, Sm, Gd, La, Ce, Dy, or any combination thereof.

47. The refractory object or the process according to any one of claims 43 to 46, wherein the sintering agent is different from the second dopant.

48. The refractory object or the process according to any one of the preceding claims, wherein the refractory object has a density of at least approximately 2.50 g/cc, at least approximately 2.60 g/cc, at least approximately 2.80 g/cc, or at least approximately 3.00 g/cc.

49. The refractory object or the process according to any one of the preceding claims, wherein the refractory object has a density no greater than approximately 3.90 g/cc, no greater than approximately 3.70 g/cc, or no greater than approximately 3.50 g/cc.

50. The refractory object or the process according to any one of the preceding claims, wherein the refractory object has a porosity of at least approximately 0.1 vol , at least approximately 1 vol , or at least approximately 5 vol .

51. The refractory object or the process according to any one of the preceding claims, wherein the refractory object has a porosity no greater than approximately 20 vol , no greater than approximately 10 vol , no greater than approximately 7 vol , no greater than approximately 2 vol .

52. The refractory object or the process according to any one of the preceding claims, wherein the refractory object includes Ti0₂, CaO, Si0₂, Fe₂0₃, Na₂0, or any combination thereof at a concentration of no greater than approximately 2 wt , no greater than approximately 1.5 wt , no greater than approximately 0.9 wt , or no greater than approximately 0.5 wt .

53. The refractory object or the process according to any one of claims 1 to 15, 17 to 28, and 39 to 53, wherein the refractory object has no coating.

54. The refractory object or the process according to any one of the preceding claims, wherein the refractory object has a length of at least approximately 0.5 m, approximately 1.1 m, at least approximately 2.0 m, at least approximately 4.0 m, at least approximately 5.0 m, or at least approximately 6 m.