WO2012053058A1 - Procédé de fabrication de scories de ciment - Google Patents

Procédé de fabrication de scories de ciment Download PDF

Info

Publication number
WO2012053058A1
WO2012053058A1 PCT/JP2010/068376 JP2010068376W WO2012053058A1 WO 2012053058 A1 WO2012053058 A1 WO 2012053058A1 JP 2010068376 W JP2010068376 W JP 2010068376W WO 2012053058 A1 WO2012053058 A1 WO 2012053058A1
Authority
WO
WIPO (PCT)
Prior art keywords
slaked lime
cement clinker
exhaust gas
raw material
cement
Prior art date
Application number
PCT/JP2010/068376
Other languages
English (en)
Japanese (ja)
Inventor
朝明 西岡
亮悦 吉野
松尾　靖史
一平 中島
智己 斉藤
大森　博昭
Original Assignee
電気化学工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 電気化学工業株式会社 filed Critical 電気化学工業株式会社
Priority to JP2012539498A priority Critical patent/JP5738882B2/ja
Priority to PCT/JP2010/068376 priority patent/WO2012053058A1/fr
Priority to CN201080068686.8A priority patent/CN103068765B/zh
Publication of WO2012053058A1 publication Critical patent/WO2012053058A1/fr

Abstract

La présente invention concerne un procédé de fabrication de scories de ciment capable de supprimer efficacement la concentration de dioxines dans le gaz d'échappement sans modifier significativement le procédé. Le procédé de fabrication de scories de ciment comprend une étape de fabrication d'un mélange de matières premières de scories de ciment modifié par ajout de chaux hydratée ayant une vitesse de sédimentation terminale de 0,5 à 10 cm/s à un mélange de matières premières de scories de ciment, et une étape d'introduction du mélange de matières premières de scories de ciment modifié dans le préchauffeur d'une unité de fabrication de scories de ciment équipée d'un préchauffeur et d'un four.
PCT/JP2010/068376 2010-10-19 2010-10-19 Procédé de fabrication de scories de ciment WO2012053058A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
JP2012539498A JP5738882B2 (ja) 2010-10-19 2010-10-19 セメントクリンカーの製造方法
PCT/JP2010/068376 WO2012053058A1 (fr) 2010-10-19 2010-10-19 Procédé de fabrication de scories de ciment
CN201080068686.8A CN103068765B (zh) 2010-10-19 2010-10-19 水泥熟料的制造方法

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2010/068376 WO2012053058A1 (fr) 2010-10-19 2010-10-19 Procédé de fabrication de scories de ciment

Publications (1)

Publication Number Publication Date
WO2012053058A1 true WO2012053058A1 (fr) 2012-04-26

Family

ID=45974795

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2010/068376 WO2012053058A1 (fr) 2010-10-19 2010-10-19 Procédé de fabrication de scories de ciment

Country Status (3)

Country Link
JP (1) JP5738882B2 (fr)
CN (1) CN103068765B (fr)
WO (1) WO2012053058A1 (fr)

Families Citing this family (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111442651B (zh) * 2020-04-03 2022-03-25 北京四方联新技术开发有限公司 一种基于水泥窑的飞灰二噁英去除系统及方法

Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002321957A (ja) * 2001-04-25 2002-11-08 Denki Kagaku Kogyo Kk 急硬性セメントコンクリート及びトンネル覆工工法
JP2007062263A (ja) * 2005-09-01 2007-03-15 Tekken Constr Co Ltd コンクリートの凝結時間制御方法及び該コンクリートの凝結時間制御方法を使用したコンクリート構造物の築造・補強工法
JP2007090261A (ja) * 2005-09-29 2007-04-12 Taiheiyo Cement Corp セメント製造装置の排ガス処理方法及び処理システム

Family Cites Families (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP4230371B2 (ja) * 2003-01-22 2009-02-25 太平洋セメント株式会社 セメント製造装置の排ガスの処理方法
DK176268B1 (da) * 2006-05-10 2007-05-21 Smidth As F L Fremgangsmåde og anlæg til fremstilling af cementklinker
CN101475324A (zh) * 2009-01-31 2009-07-08 合肥水泥研究设计院 电石渣干烧制水泥熟料的工艺方法

Patent Citations (3)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2002321957A (ja) * 2001-04-25 2002-11-08 Denki Kagaku Kogyo Kk 急硬性セメントコンクリート及びトンネル覆工工法
JP2007062263A (ja) * 2005-09-01 2007-03-15 Tekken Constr Co Ltd コンクリートの凝結時間制御方法及び該コンクリートの凝結時間制御方法を使用したコンクリート構造物の築造・補強工法
JP2007090261A (ja) * 2005-09-29 2007-04-12 Taiheiyo Cement Corp セメント製造装置の排ガス処理方法及び処理システム

Also Published As

Publication number Publication date
JPWO2012053058A1 (ja) 2014-02-24
CN103068765B (zh) 2014-12-10
JP5738882B2 (ja) 2015-06-24
CN103068765A (zh) 2013-04-24

Similar Documents

Publication Publication Date Title
CN111233356B (zh) 一种铝灰预处理的全固废制备硫铝酸盐水泥的方法及系统
JP4350765B2 (ja) セメント焼成設備の二酸化炭素の回収方法及び回収装置
US20130125799A1 (en) Systems and methods for comminuting and recirculating coal combustion products
MXPA06008163A (es) Produccion de cemento clinker que comprende la remocion parcial de un flujo de gases perdidos de horno rotatorio que contienen sustancias nocivas.
CN107235647A (zh) 应用于水泥熟料生产工艺的氧气/二氧化碳燃烧技术
JP4483946B2 (ja) セメントの製造方法
JP2012506990A5 (fr)
JP2007126328A (ja) セメント製造装置及びセメント製造方法
JP2011168445A (ja) 粉体状炭酸カルシウムの焼成方法
CN103922624B (zh) 以电石渣为钙质原料并处理垃圾焚烧烟气的熟料烧成系统
JP2006035189A (ja) セメント製造プロセスを利用した有機性汚泥の処理方法
JP5738882B2 (ja) セメントクリンカーの製造方法
RU2552277C1 (ru) Способ получения низкотемпературного портландцементного клинкера
CN106006643A (zh) 一种利用黄磷尾气和磷石膏制备电石的方法
JP5092211B2 (ja) セメント製造設備
JP2007090261A (ja) セメント製造装置の排ガス処理方法及び処理システム
JP5091084B2 (ja) 石炭灰の処理方法
JP5303716B2 (ja) 改質灰、改質灰の製造方法及びセメント組成物
JP6260404B2 (ja) 排ガス処理方法及び処理装置
JP2022149127A (ja) セメントクリンカ製造システム及びセメントクリンカ製造方法
JP2007098343A (ja) セメント製造装置の排ガス処理方法及び処理システム
JPWO2019193938A1 (ja) 有機汚泥の処理装置及び処理方法
RU2547195C1 (ru) Способ получения портландцементного клинкера (варианты)
JP2023116231A (ja) セメントクリンカ製造システム及びセメントクリンカ製造方法
JP6287477B2 (ja) 排ガス処理方法及び処理装置

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 201080068686.8

Country of ref document: CN

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 10858614

Country of ref document: EP

Kind code of ref document: A1

WWE Wipo information: entry into national phase

Ref document number: 2012539498

Country of ref document: JP

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 10858614

Country of ref document: EP

Kind code of ref document: A1