WO2012053036A1 - 床材 - Google Patents

床材 Download PDF

Info

Publication number
WO2012053036A1
WO2012053036A1 PCT/JP2010/006248 JP2010006248W WO2012053036A1 WO 2012053036 A1 WO2012053036 A1 WO 2012053036A1 JP 2010006248 W JP2010006248 W JP 2010006248W WO 2012053036 A1 WO2012053036 A1 WO 2012053036A1
Authority
WO
WIPO (PCT)
Prior art keywords
layer
vinyl chloride
wpc
floor material
base material
Prior art date
Application number
PCT/JP2010/006248
Other languages
English (en)
French (fr)
Inventor
農野昇一
森本晃徳
Original Assignee
大建工業株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 大建工業株式会社 filed Critical 大建工業株式会社
Priority to PCT/JP2010/006248 priority Critical patent/WO2012053036A1/ja
Publication of WO2012053036A1 publication Critical patent/WO2012053036A1/ja

Abstract

　床材（１００）は、表層に設けられた塩化ビニル樹脂シートで構成された塩化ビニル層（１２１）を有する基材層（１２０）と、その基材層（１２０）の塩化ビニル層（１２１）上に積層されるように設けられたＷＰＣ単板で構成されたＷＰＣ層（１１２）と、それらの間に設けられた接着層（１３０）とを備える。接着層（１３０）には不織布（１３１）が埋設されている。

Description

床材
　本発明は床材に関する。
　高い耐傷性を有する床材として、樹脂含浸処理（ＷＰＣ（Wood Plastic Combination）処理）を施したものが知られている。
　特許文献１には、樹脂含浸処理した厚さ１．５～２．０ｍｍのＷＰＣ単板と、その裏面に接着された厚さ１．０～２．０ｍｍの軟性を有する合成樹脂製シートとからなる床材が開示されている。
　特許文献２には、木質化粧単板と合板とを貼り合わせ且つ樹脂含浸処理したＷＰＣ板と、その裏面に貼り合わされた樹脂含浸処理しない基材とからなる建材が開示されている。
特開２００９－２９３３２９号公報 特開昭６３－１０７５０１号公報
　本発明の床材は、表層に設けられた塩化ビニル樹脂シートで構成された塩化ビニル層を有する基材層と、
　上記基材層の上記塩化ビニル層上に積層されるように設けられたＷＰＣ単板で構成されたＷＰＣ層と、
　上記塩化ビニル層と上記ＷＰＣ層との間に設けられた接着層と、
を備え、
　上記接着層には不織布が埋設されている。
　上記構成によれば、基材層の表層の塩化ビニル層上にＷＰＣ層が積層されるように設けられ、そして、それらの間の接着層に不織布が埋設されていることにより、接着層として少なくとも不織布の厚さが確保され、それによって可塑剤がＷＰＣ層まで達するのを有効に阻止することができる。それに加え、表面層が表面塗装層及びＷＰＣ単板で構成されたＷＰＣ層を有するので、高い耐傷性と共に高い耐摩耗性を得ることができ、また、基材層が反り防止材層を有しているので、形状が安定で優れた耐反り変形性を得ることができ、このような特性を有することから床材の薄型化を図ることができる。
　本発明の床材は、上記基材層が、上記塩化ビニル層の下層側に設けられた反り防止層を有していてもよい。
　上記構成によれば、塩化ビニル層の下層側に反り防止層が設けられていることにより、反りの少ない床材を得ることができる。
　その場合、本発明の床材は、上記反り防止層が寒冷紗で構成されていることが好ましい。
　上記構成によれば、反り防止層が寒冷紗で構成されていることにより、床材全体の剛性を上げることなく、反りの少ない床材を高い生産性で得ることができる。
　本発明の床材は、上記反り防止層が、上記基材層における中央よりも下層側に設けられていることが好ましい。
　上記構成によれば、反り防止層が基材層における中央よりも下層側に設けられていることにより、表面層の寸法変形に対するバランスを有効にとることができる。
　本発明の床材は、上記基材層が、上記塩化ビニル層と上記反り防止層との間に設けられた上側弾性樹脂層を有していてもよい。
　上記の構成によれば、塩化ビニル層と上記反り防止層との間に上側弾性樹脂層が設けられていることにより、ＷＰＣ層を構成するＷＰＣ単板のような材料を使用した場合においても、ＷＰＣ層と基材層との界面剥離が発生しにくいものとすることができる。
　本発明の床材は、上記基材層が、上記反り防止層の下層側に設けられた下側弾性樹脂層を有していてもよい。
　上記の構成によれば、反り防止層の下層側に下側弾性樹脂層が設けられていることにより、反り防止材層による突出物を有さない切断面を得ることができる。
実施形態に係る床材の断面図である。 （ａ）～（ｃ）は床材の製造方法を示す説明図である。
　以下、実施形態について詳細に説明する。
　図１は本実施形態に係る床材１００を示す。本実施形態に係る床材１００は、例えば商業施設の木質フロア等に用いられるものである。
　本実施形態に係る床材１００は、長尺の矩形板状に形成されており、側面同士や端面同士或いは側面と端面とを当接させて敷設することにより床面を形成するように構成されている。本実施形態に係る床材１００は、床面にＶ溝等が形成されるように、上縁に面取り加工が施されていてもよい。本実施形態に係る床材１００は、例えば、長さが８００～１３００ｍｍ、幅が３０３～７５０ｍｍ、及び厚さが２．２～４．０ｍｍである。
　本実施形態に係る床材１００は、木質の表面層１１０が樹脂製の基材層１２０に接着層１３０を介して積層された構造を有する。
　表面層１１０は、厚さ方向に、上から順に、表面塗装層１１１、及びＷＰＣ層１１２が積層された構造を有する。表面層１１０の厚さは例えば０．２～０．８ｍｍである。
　表面塗装層１１１の構成材料としては、特に限定されるものではないが、例えば、透明なＵＶ硬化型ウレタン樹脂などの硬化型樹脂が挙げられる。表面塗装層１１１の厚さは例えば５０～１５０μｍであり、５０～８０μｍであることが好ましい。
　ＷＰＣ層１１２はＷＰＣ単板で構成されている。ＷＰＣ単板は、木質材料の組織に液状の樹脂材料を含浸させて充填した後に硬化させるという公知の方法により作製することができる。ＷＰＣ単板を構成する木質材料としては、特に限定されるものではないが、例えば、ナラ、ブナ、タモ、シナ、カバ、ナット、ヒノキ、スギ等が挙げられる。樹脂含浸処理に用いられる樹脂材料としては、特に限定されるものではないが、例えば、不飽和ポリエステル樹脂やビニルエステル樹脂などの熱硬化型樹脂等が挙げられる。ＷＰＣ層１１２の厚さは例えば０．４～３．０ｍｍである。
　接着層１３０は、硬化した樹脂接着剤１３１のマトリクスに不織布１３２が埋設され、その不織布１３２に樹脂接着剤１３１が含浸して硬化した構成を有する。接着層１３０の厚さは例えば２０～１００μｍである。
　接着層１３０のマトリクスを形成する樹脂接着剤１３１としては、特に限定されるものではないが、例えばコールドプレス加工での硬化が可能な２液混合反応型ウレタン接着剤が好適なものとして挙げられる。後述の塩化ビニル層１２１は耐熱性が劣るため、基材層１２０にＷＰＣ層１１２を積層する加工として熱プレスは不向きである。また、ＷＰＣ層１１２及び塩化ビニル層１２１共に通気性を有さないことから、樹脂接着剤１３１として、硬化して接着層１３０を形成する際にガスが生成するものや水分の蒸発が必要なものは好ましくない。但し、樹脂接着剤１３１としては、塩化ビニル層１２１の劣化を招かない程度の短時間の加熱による接着加工が可能であれば、ホットメルト接着剤等も使用することができる。樹脂接着剤１３１は、表面層１１０が薄く、表面層１１０を透過して基材層１２０が視認されるような場合には、ＷＰＣ層１１２を構成するＷＰＣ単板と同系色に着色されていてもよい。
　不織布１３２の材質としては、特に限定されるものではないが、例えば、ポリエステル等が挙げられる。不織布１３２の厚さは例えば０．０５～０．２０ｍｍである。不織布１３２の目付は例えば５～５０ｇ／ｍ２である。
　基材層１２０は、表層に塩化ビニル層１２１が設けられ、その下層側に、厚さ方向に上から順に、上側弾性樹脂層１２２、反り防止材層１２３、及び下側弾性樹脂層１２４が積層されて設けられた構造を有する。基材層１２０の厚さは例えば２．０～３．０ｍｍである。
　塩化ビニル層１２１は塩化ビニル樹脂シートで構成されている。塩化ビニル層１２１を構成する塩化ビニル樹脂シートには可塑剤が配合されている。可塑剤としては、例えば、ＤＯＰなどのフタル酸エステル類；ＤＯＡなどのアジピン酸エステル類；ＴＯＴＭなどのトリメリット酸エステル類；ピロメリット酸エステル類；エポキシ化動植物油類；エポキシ化脂肪酸エステル類；塩素化パラフィン類；リン酸エステル類等が挙げられる。可塑剤は、単一種が配合されているだけであってもよく、また、複数種が配合されていてもよい。塩化ビニル樹脂シートには可塑剤の他に安定剤、充填材、及び顔料等が配合されていてもよい。塩化ビニル層１２１は、表面層１１０が薄く、表面層１１０を透過して基材層１２０が視認されるような場合には、ＷＰＣ層１１２を構成するＷＰＣ単板と同系色に着色されていてもよい。塩化ビニル層１２１の厚さは例えば０．３～１．０ｍｍである。
　上側弾性樹脂層１２２の構成材料としては、特に限定されるものではないが、例えば塩化ビニル樹脂シート等が挙げられる。上側弾性樹脂層１２２の厚さは例えば０．３～１．０ｍｍである。この上側弾性樹脂層１２２により、ＷＰＣ層１１２を構成するＷＰＣ単板のような材料を使用した場合においても、ＷＰＣ層１１２と基材層１２０との界面剥離が発生しにくい。
　反り防止材層１２３の構成材料としては、特に限定されるものではないが、例えば、ポリエステル製、ポリエチレン製、ポリプロピレン製、或いはビニロン製の寒冷紗、ガラス繊維製の不織布等のシート材が挙げられる。反り防止材層１２３の厚さは例えば０．１～０．５ｍｍである。この反り防止材層１２３により反りの少ない床材１００を得ることができる。特に、寒冷紗を反り防止材層１２３の構成材料として用いれば、床材１００全体の剛性を上げることなく、反りの少ない床材１００を高い生産性で得ることができる。かかる寒冷紗としては、経糸及び緯糸がポリエステル繊維及びレーヨンからなる太さ１８～２２番手の混紡糸で構成された平織り組織を有し、経糸及び緯糸の糸密度が２．５４ｃｍ当たり１６～１８本、目付が４４～５０ｇ／ｍ２、並びに厚さが０．３～０．４ｍｍであるものが好ましい。反り防止材層１２３は、表面層１１０の寸法変形に対するバランスを有効にとるという観点から、基材層１２０における中央よりも下層側に設けられていることが好ましい。
　下側弾性樹脂層１２４の構成材料としては、特に限定されるものではないが、例えば塩化ビニル樹脂シート等が挙げられる。下側弾性樹脂層１２４の厚さは例えば０．３～１．０ｍｍである。なお、下側弾性樹脂層１２４が設けられずに反り防止材層１２３が基材層１２０の最下層に設けられた構成であってもよい。但し、かかる構成では、反り防止材層１２３が例えば寒冷紗であって、それが最下層に配置された場合、床材１００を切断したとき、その切断面から寒冷紗の糸が切断しきれずに突出した形態となることがある。従って、反り防止材層１２３による突出物を有さない切断面を得る観点から、本実施形態に係る床材１００のように、下側弾性樹脂層１２４により反り防止材層１２３が基材層１２０の中間層に位置付けられた構成であることが好ましい。
　ところで、基材層の表層の塩化ビニル層上に接着層を介してＷＰＣ層が積層された従来の床材では、ＷＰＣ層に含まれる可塑剤が接着層側にブリードする場合があり、かかる場合に、接着層の厚さが薄いと可塑剤がＷＰＣ層まで達して変色等を生じることがある。しかしながら、上記構成の本実施形態に係る床材によれば、基材層１２０の表層の塩化ビニル層１２１上にＷＰＣ層１１２が積層されるように設けられ、そして、それらの間の接着層１３０に不織布１３２が埋設されているので、接着層１３０として少なくとも不織布１３２の厚さが確保され、それによって可塑剤がＷＰＣ層１１２まで達するのを有効に阻止することができる。
　また、表面層１１０が表面塗装層１１１及びＷＰＣ単板で構成されたＷＰＣ層１１２を有するので、高い耐傷性と共に高い耐摩耗性を得ることができ、また、基材層１２０が反り防止材層１２３を有しているので、形状が安定で優れた耐反り変形性を得ることができる。このような特性を有することから床材１００の薄型化を図ることができる。
　次に、本実施形態に係る床材の製造方法について説明する。
　まず、塩化ビニル層１２１を構成する塩化ビニル樹脂シート、上側弾性樹脂層１２２を構成する樹脂シート、反り防止材層１２３を構成するシート材、及び下側弾性樹脂層１２４を構成する樹脂シートを、それぞれのロール状巻物から引き出し、それらを積層してカレンダ加工を施し、熱融着で一体化させることにより基材層１２０を作製する。カレンダ加工温度は例えば１３０～１６０℃である。
　次いで、図２（ａ）に示すように、基材層１２０の表層の塩化ビニル層１２１上に不織布１３２を接着する。この接着には次工程でＷＰＣ単板の接着に用いる樹脂接着剤１３１を使用することが好ましい。
　続いて、基材層１２０上に接着した不織布１３２が埋設されるようにスプレッター等を用いて樹脂接着剤１３１を塗布した後、図２（ｂ）に示すように、その上にＷＰＣ層１１２を構成するＷＰＣ単板を積層し、それらをプレス板Ｐ間で挟んでプレス加工する。このとき、樹脂接着剤１３１は不織布１３２に含浸して硬化する。プレス圧力は例えば１～５Ｐａである。プレス時間は例えば４～８時間である。プレス温度は常温であることが好ましい。なお、予め基材層１２０上への不織布１３２の接着を行わず、この工程において、基材層１２０上への不織布１３２の接着を併せて行ってもよい。
　そして、プレス圧力を解除した後、例えば１～７日間程度無負荷状態で放置し、小分割すると共に必要に応じてテノーナー等を用いて上縁に面取り加工を施す。
　最後に、図２（ｃ）に示すように、ＷＰＣ層１１２上に表面塗装層１１１を構成する塗料１１１’を塗布して硬化させる。
　本発明は床材について有用である。
１００　床材
１１０　表面層
１１１　表面塗装層
１１１’　塗料
１１２　ＷＰＣ層
１２０　基材層
１２１　塩化ビニル層
１２２　上側弾性樹脂層
１２３　反り防止材層
１２４　下側弾性樹脂層
１３０　接着層
１３１　樹脂接着剤
１３２　不織布

Claims (6)

  1. 　表層に設けられた塩化ビニル樹脂シートで構成された塩化ビニル層を有する基材層と、
    　上記基材層の上記塩化ビニル層上に積層されるように設けられたＷＰＣ単板で構成されたＷＰＣ層と、
    　上記塩化ビニル層と上記ＷＰＣ層との間に設けられた接着層と、
    を備え、
    　上記接着層には不織布が埋設されている床材。
  2. 　請求項１に記載された床材において、
    　上記基材層は、上記塩化ビニル層の下層側に設けられた反り防止層を有する床材。
  3. 　請求項２に記載された床材において、
    　上記反り防止層が寒冷紗で構成されている床材。
  4. 　請求項２又は３に記載された床材において、
    　上記反り防止層は、上記基材層における中央よりも下層側に設けられている床材。
  5. 　請求項２乃至４のいずれかに記載された床材において、
    　上記基材層は、上記塩化ビニル層と上記反り防止層との間に設けられた上側弾性樹脂層を有する床材。
  6. 　請求項２乃至５のいずれかに記載された床材において、
    　上記基材層は、上記反り防止層の下層側に設けられた下側弾性樹脂層を有する床材。
PCT/JP2010/006248 2010-10-21 2010-10-21 床材 WO2012053036A1 (ja)