WO2011071975A2 - Moulage de précision à modèles perdus pour composants creux - Google Patents
Moulage de précision à modèles perdus pour composants creux Download PDFInfo
- Publication number
- WO2011071975A2 WO2011071975A2 PCT/US2010/059380 US2010059380W WO2011071975A2 WO 2011071975 A2 WO2011071975 A2 WO 2011071975A2 US 2010059380 W US2010059380 W US 2010059380W WO 2011071975 A2 WO2011071975 A2 WO 2011071975A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- ceramic core
- casting
- ceramic
- flexible
- mold
- Prior art date
Abstract
Priority Applications (4)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
KR1020127017689A KR101440872B1 (ko) | 2009-12-08 | 2010-12-08 | 중공 구성 요소용 인베스트먼트 주조 프로세스 |
JP2012543226A JP5693607B2 (ja) | 2009-12-08 | 2010-12-08 | 中空部品のためのインベストメント鋳造プロセス |
CN201080055307.1A CN102753284B (zh) | 2009-12-08 | 2010-12-08 | 用于中空部件的熔模铸造过程 |
EP10796523.8A EP2509728B1 (fr) | 2009-12-08 | 2010-12-08 | Procédé de coulée à la cire perdue pour la fabrication de composants creux |
Applications Claiming Priority (6)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
US26751909P | 2009-12-08 | 2009-12-08 | |
US61/267,519 | 2009-12-08 | ||
US12/961,740 US20110132564A1 (en) | 2009-12-08 | 2010-12-07 | Investment casting utilizing flexible wax pattern tool |
US12/961,720 US9272324B2 (en) | 2009-12-08 | 2010-12-07 | Investment casting process for hollow components |
US12/961,720 | 2010-12-07 | ||
US12/961,740 | 2010-12-07 |
Publications (2)
Publication Number | Publication Date |
---|---|
WO2011071975A2 true WO2011071975A2 (fr) | 2011-06-16 |
WO2011071975A3 WO2011071975A3 (fr) | 2011-10-06 |
Family
ID=44080864
Family Applications (2)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/US2010/059380 WO2011071975A2 (fr) | 2009-12-08 | 2010-12-08 | Moulage de précision à modèles perdus pour composants creux |
PCT/IB2011/000225 WO2011070557A2 (fr) | 2009-12-08 | 2011-02-08 | Coulée à cire perdue utilisant un outil de motif de cire souple |
Family Applications After (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
PCT/IB2011/000225 WO2011070557A2 (fr) | 2009-12-08 | 2011-02-08 | Coulée à cire perdue utilisant un outil de motif de cire souple |
Country Status (6)
Country | Link |
---|---|
US (3) | US20110132564A1 (fr) |
EP (2) | EP2509728B1 (fr) |
JP (1) | JP5693607B2 (fr) |
KR (1) | KR101440872B1 (fr) |
CN (1) | CN102753284B (fr) |
WO (2) | WO2011071975A2 (fr) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN112123662A (zh) * | 2020-09-08 | 2020-12-25 | 哈尔滨工业大学 | 一种复杂构型空腔水下吸声板的制备方法 |
Families Citing this family (52)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US9056795B2 (en) * | 2009-08-09 | 2015-06-16 | Rolls-Royce Corporation | Support for a fired article |
DE102009043555B4 (de) * | 2009-09-30 | 2013-09-12 | Ksb Aktiengesellschaft | Kastenlose Gießform |
US20130333855A1 (en) * | 2010-12-07 | 2013-12-19 | Gary B. Merrill | Investment casting utilizing flexible wax pattern tool for supporting a ceramic core along its length during wax injection |
US9017027B2 (en) | 2011-01-06 | 2015-04-28 | Siemens Energy, Inc. | Component having cooling channel with hourglass cross section |
US8764394B2 (en) | 2011-01-06 | 2014-07-01 | Siemens Energy, Inc. | Component cooling channel |
EP2592174A1 (fr) | 2011-11-14 | 2013-05-15 | Siemens Aktiengesellschaft | Système de couche doté d'une surface de substrat structurée et son procédé de fabrication |
US8813824B2 (en) | 2011-12-06 | 2014-08-26 | Mikro Systems, Inc. | Systems, devices, and/or methods for producing holes |
US20130280093A1 (en) | 2012-04-24 | 2013-10-24 | Mark F. Zelesky | Gas turbine engine core providing exterior airfoil portion |
KR101960715B1 (ko) * | 2012-08-02 | 2019-03-22 | 한화파워시스템 주식회사 | 임펠러 또는 터빈 휠의 제조 방법 |
CN103433431B (zh) * | 2013-09-06 | 2016-08-31 | 安徽应流集团霍山铸造有限公司 | 气缸盖内腔的陶瓷芯 |
US20150122450A1 (en) * | 2013-11-07 | 2015-05-07 | Ching-Pang Lee | Ceramic casting core having an integral vane internal core and shroud backside shell for vane segment casting |
US9061349B2 (en) * | 2013-11-07 | 2015-06-23 | Siemens Aktiengesellschaft | Investment casting method for gas turbine engine vane segment |
EP3086893B1 (fr) | 2013-12-23 | 2019-07-24 | United Technologies Corporation | Cadre structural d'un noyau perdu |
US9669458B2 (en) * | 2014-02-06 | 2017-06-06 | General Electric Company | Micro channel and methods of manufacturing a micro channel |
US20150239043A1 (en) * | 2014-02-21 | 2015-08-27 | Siemens Energy, Inc. | Cast Features for Location and Inspection |
WO2016133987A2 (fr) | 2015-02-18 | 2016-08-25 | Siemens Aktiengesellschaft | Formation de passages de refroidissement dans des pièces coulées en superalliage d'une turbine à combustion |
WO2015130528A1 (fr) * | 2014-02-25 | 2015-09-03 | Siemens Aktiengesellschaft | Revêtement de barrière thermique de composant de turbine avec éléments de surface usinés d'isolation contre les fissures |
CN104493081B (zh) * | 2014-12-09 | 2016-07-06 | 南京航空航天大学 | 用于空心涡轮叶片熔模铸造的注蜡模具及其快速制造方法 |
US10029299B2 (en) * | 2015-07-09 | 2018-07-24 | General Electric Company | Three-dimensional manufacturing methods and systems for turbine components |
US9987677B2 (en) | 2015-12-17 | 2018-06-05 | General Electric Company | Method and assembly for forming components having internal passages using a jacketed core |
US10118217B2 (en) | 2015-12-17 | 2018-11-06 | General Electric Company | Method and assembly for forming components having internal passages using a jacketed core |
US10150158B2 (en) | 2015-12-17 | 2018-12-11 | General Electric Company | Method and assembly for forming components having internal passages using a jacketed core |
US9968991B2 (en) | 2015-12-17 | 2018-05-15 | General Electric Company | Method and assembly for forming components having internal passages using a lattice structure |
US10099284B2 (en) | 2015-12-17 | 2018-10-16 | General Electric Company | Method and assembly for forming components having a catalyzed internal passage defined therein |
US9579714B1 (en) | 2015-12-17 | 2017-02-28 | General Electric Company | Method and assembly for forming components having internal passages using a lattice structure |
US10046389B2 (en) | 2015-12-17 | 2018-08-14 | General Electric Company | Method and assembly for forming components having internal passages using a jacketed core |
US10099276B2 (en) | 2015-12-17 | 2018-10-16 | General Electric Company | Method and assembly for forming components having an internal passage defined therein |
US10137499B2 (en) | 2015-12-17 | 2018-11-27 | General Electric Company | Method and assembly for forming components having an internal passage defined therein |
US10099283B2 (en) | 2015-12-17 | 2018-10-16 | General Electric Company | Method and assembly for forming components having an internal passage defined therein |
WO2017127043A1 (fr) * | 2016-01-18 | 2017-07-27 | Siemens Aktiengesellschaft | Procédé pour réguler une orientation de profil aérodynamique à l'intérieur d'aubes à double moulage de section de turbine |
US20170246677A1 (en) * | 2016-02-29 | 2017-08-31 | General Electric Company | Casting with metal components and metal skin layers |
US20210205876A1 (en) * | 2016-03-18 | 2021-07-08 | Siemens Aktiengesellschaft | Manufacturing method and tooling for ceramic cores |
US10807153B2 (en) | 2016-03-18 | 2020-10-20 | Siemens Aktiengesellschaft | Method of manufacturing advanced features in a core for casting |
US10286450B2 (en) | 2016-04-27 | 2019-05-14 | General Electric Company | Method and assembly for forming components using a jacketed core |
US10335853B2 (en) | 2016-04-27 | 2019-07-02 | General Electric Company | Method and assembly for forming components using a jacketed core |
US10683762B2 (en) | 2016-07-12 | 2020-06-16 | Rolls-Royce North American Technologies Inc. | Gas engine component with cooling passages in wall |
CN106392010B (zh) * | 2016-11-18 | 2018-05-18 | 绥阳县海红铸造有限责任公司 | 消失模铸造的工艺 |
US20180161866A1 (en) | 2016-12-13 | 2018-06-14 | General Electric Company | Multi-piece integrated core-shell structure for making cast component |
US11813669B2 (en) | 2016-12-13 | 2023-11-14 | General Electric Company | Method for making an integrated core-shell structure |
US20180161855A1 (en) * | 2016-12-13 | 2018-06-14 | General Electric Company | Multi-piece integrated core-shell structure with standoff and/or bumper for making cast component |
US20180238175A1 (en) * | 2017-02-21 | 2018-08-23 | General Electric Company | Method and Device for Retaining Position of a Consumable Core |
US10556269B1 (en) | 2017-03-29 | 2020-02-11 | United Technologies Corporation | Apparatus for and method of making multi-walled passages in components |
US10596621B1 (en) | 2017-03-29 | 2020-03-24 | United Technologies Corporation | Method of making complex internal passages in turbine airfoils |
CN107570662B (zh) * | 2017-09-20 | 2020-02-21 | 北京星航机电装备有限公司 | 一种中间带隔层腔体的压蜡模具 |
US10913106B2 (en) | 2018-09-14 | 2021-02-09 | Raytheon Technologies Corporation | Cast-in film cooling hole structures |
DE102018215966A1 (de) * | 2018-09-19 | 2020-03-19 | Fraunhofer-Gesellschaft zur Förderung der angewandten Forschung e.V. | Gießform zum Gießen von Bauteilen sowie Verfahren zu deren Herstellung |
EP4003622A1 (fr) * | 2019-09-19 | 2022-06-01 | Adultimum AG | Procédé de fabrication d'un motif de cire, motif de cire |
EP4037850B1 (fr) | 2019-11-01 | 2024-01-03 | Siemens Energy Global GmbH & Co. KG | Procédé de fabrication d'outillage souple pour la coulée d'un noyau céramique |
WO2021134248A1 (fr) * | 2019-12-30 | 2021-07-08 | 泰州鑫宇精工股份有限公司 | Matériau de moulage de moule en céramique et son procédé de coulée |
WO2021145850A1 (fr) * | 2020-01-13 | 2021-07-22 | Siemens Aktiengesellschaft | Procédé de fabrication rapide pour noyau en céramique haute définition utilisé pour des applications de moulage à la cire perdue |
CN113636858B (zh) * | 2021-08-25 | 2022-09-09 | 佛山市非特新材料有限公司 | 一种具有曲面流道的叶轮陶瓷型芯的制备方法 |
EP4343116A3 (fr) | 2022-09-26 | 2024-04-17 | RTX Corporation | Profils aérodynamiques à cavités de refroidissement à lobes |
Citations (4)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US958220A (en) | 1909-07-26 | 1910-05-17 | Edwin J Blood | Cannon. |
US7141812B2 (en) | 2002-06-05 | 2006-11-28 | Mikro Systems, Inc. | Devices, methods, and systems involving castings |
US7410606B2 (en) | 2001-06-05 | 2008-08-12 | Appleby Michael P | Methods for manufacturing three-dimensional devices and devices created thereby |
US7438527B2 (en) | 2005-04-22 | 2008-10-21 | United Technologies Corporation | Airfoil trailing edge cooling |
Family Cites Families (48)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US3850559A (en) * | 1973-04-18 | 1974-11-26 | Unisil Molds Inc | Apparatus for vulcanizing rubber molds |
FR2369072A1 (fr) * | 1976-11-02 | 1978-05-26 | Bradbury Farel | Procede et dispositif de moulage sous pression |
JPS60195141U (ja) | 1984-06-07 | 1985-12-26 | 本田技研工業株式会社 | 精密鋳造用金属鋳型のモデル |
JPS623909A (ja) * | 1985-06-28 | 1987-01-09 | Matsushita Electric Ind Co Ltd | ゴム型の加熱方法 |
FR2594727B1 (fr) * | 1986-02-27 | 1988-05-06 | Snecma | Procede de preparation de noyaux ceramiques |
JPS6331711A (ja) * | 1986-07-26 | 1988-02-10 | 東陶機器株式会社 | 陶磁器の加圧鋳込成形用型の製造方法 |
US4840764A (en) * | 1988-10-12 | 1989-06-20 | Cummins Richard F | Controlled wall casting process |
US5163499A (en) * | 1988-11-10 | 1992-11-17 | Lanxide Technology Company, Lp | Method of forming electronic packages |
US5066213A (en) * | 1989-04-03 | 1991-11-19 | John Ferincz | Wax-casting components |
JPH02303651A (ja) * | 1989-05-19 | 1990-12-17 | Komatsu Ltd | 中空セラミック中子の造型方法 |
JPH0813446B2 (ja) * | 1990-05-30 | 1996-02-14 | 株式会社日立製作所 | スリツプキヤステイング法 |
DE4022653A1 (de) * | 1990-07-17 | 1992-01-23 | Michael Haeusle | Verfahren zum giessen von praezisionsgussstuecken |
JP2725447B2 (ja) * | 1990-07-26 | 1998-03-11 | ブリヂストンスポーツ株式会社 | ゴルフボールの製造方法 |
US5258151A (en) * | 1991-06-01 | 1993-11-02 | Hoechst Aktiengesellschaft | Molding composition for the production of inorganic sintered products |
JPH06253443A (ja) * | 1993-02-26 | 1994-09-09 | Hitachi Cable Ltd | 電力ケーブル用プレハブ接続部 |
US5291654A (en) * | 1993-03-29 | 1994-03-08 | United Technologies Corporation | Method for producing hollow investment castings |
US5639416A (en) * | 1994-11-18 | 1997-06-17 | Motorola, Inc. | Method of molding precision parts |
US5651932A (en) * | 1995-04-14 | 1997-07-29 | Butler; Byron | Method for investment wax casting of golf club heads |
US5906234A (en) * | 1996-10-22 | 1999-05-25 | Johnson & Johnson Professional, Inc. | Investment casting |
US6019927A (en) * | 1997-03-27 | 2000-02-01 | Galliger; Nicholas | Method of casting a complex metal part |
US5976457A (en) * | 1997-08-19 | 1999-11-02 | Amaya; Herman E. | Method for fabrication of molds and mold components |
DE19821770C1 (de) | 1998-05-14 | 1999-04-15 | Siemens Ag | Verfahren und Vorrichtung zur Herstellung eines metallischen Hohlkörpers |
US6352101B1 (en) * | 1998-07-21 | 2002-03-05 | General Electric Company | Reinforced ceramic shell mold and related processes |
US6171093B1 (en) * | 1998-12-16 | 2001-01-09 | T. R. Hawkinson Ltd. | Process and apparatus for molding jewelry |
US6156250A (en) * | 1999-01-04 | 2000-12-05 | Mcp Metalspecialties, Inc. | Constructing fully dense composite accurate tooling |
JP2000301289A (ja) | 1999-04-22 | 2000-10-31 | Ebara Corp | 消失模型の製造方法 |
ATE350182T1 (de) * | 1999-10-26 | 2007-01-15 | Howmet Res Corp | Mehrwandiger kern und verfahren |
US6331267B1 (en) * | 1999-11-16 | 2001-12-18 | General Electric Company | Apparatus and method for molding a core for use in casting hollow parts |
US6364001B1 (en) * | 2000-08-15 | 2002-04-02 | Pcc Airfoils, Inc. | Method of casting an article |
US6403020B1 (en) * | 2001-08-07 | 2002-06-11 | Howmet Research Corporation | Method for firing ceramic cores |
US6634410B1 (en) * | 2001-08-28 | 2003-10-21 | John H. Wilson | Mold apparatus and method |
DE10332904B3 (de) * | 2003-07-21 | 2004-12-23 | Daimlerchrysler Ag | Verstärkte Formkerne für den Metallguss, Herstellung und Verwendung |
US6929054B2 (en) * | 2003-12-19 | 2005-08-16 | United Technologies Corporation | Investment casting cores |
US20050236729A1 (en) * | 2004-04-23 | 2005-10-27 | Arnott Robin A | Method and apparatus for vibrating melt in an injection molding machine using active material elements |
CA2511154C (fr) | 2004-07-06 | 2012-09-18 | General Electric Company | Coulage de modele synthetique |
US7448433B2 (en) * | 2004-09-24 | 2008-11-11 | Honeywell International Inc. | Rapid prototype casting |
US7134475B2 (en) * | 2004-10-29 | 2006-11-14 | United Technologies Corporation | Investment casting cores and methods |
US8906282B2 (en) * | 2005-07-06 | 2014-12-09 | Nanyang Technological University | Micro-structured and nano-structured surfaces on biodegradable polymers |
US7972129B2 (en) * | 2005-09-16 | 2011-07-05 | O'donoghue Joseph | Compound tooling system for molding applications |
EP1772210A3 (fr) | 2005-09-30 | 2008-05-28 | General Electric Company | Noyaux de fonderie et procédé pour leur fabrication |
US20100276829A1 (en) | 2006-02-13 | 2010-11-04 | Guohua Yang | High Aspect Ratio Microstructures and Method for Fabricating High Aspect Ratio Microstructures From Powder Composites |
US20080135721A1 (en) * | 2006-12-06 | 2008-06-12 | General Electric Company | Casting compositions for manufacturing metal casting and methods of manufacturing thereof |
US7624787B2 (en) * | 2006-12-06 | 2009-12-01 | General Electric Company | Disposable insert, and use thereof in a method for manufacturing an airfoil |
US7487819B2 (en) | 2006-12-11 | 2009-02-10 | General Electric Company | Disposable thin wall core die, methods of manufacture thereof and articles manufactured therefrom |
DE102007023152A1 (de) * | 2007-05-16 | 2008-11-20 | Mtu Aero Engines Gmbh | Verfahren zur Herstellung eines Gussteils, Gussform und damit hergestelltes Gussteil |
US7913743B2 (en) * | 2008-06-12 | 2011-03-29 | Pcc Airfoils, Inc. | Method of forming a pattern |
US20090308559A1 (en) * | 2008-06-13 | 2009-12-17 | Matthew Powell | Hollow articles and method of manufacture |
EP2559533B1 (fr) | 2008-09-26 | 2020-04-15 | United Technologies Corporation | Pièce coulée |
-
2010
- 2010-12-07 US US12/961,740 patent/US20110132564A1/en not_active Abandoned
- 2010-12-07 US US12/961,720 patent/US9272324B2/en active Active
- 2010-12-08 WO PCT/US2010/059380 patent/WO2011071975A2/fr active Application Filing
- 2010-12-08 CN CN201080055307.1A patent/CN102753284B/zh active Active
- 2010-12-08 JP JP2012543226A patent/JP5693607B2/ja not_active Expired - Fee Related
- 2010-12-08 EP EP10796523.8A patent/EP2509728B1/fr active Active
- 2010-12-08 KR KR1020127017689A patent/KR101440872B1/ko active IP Right Grant
-
2011
- 2011-02-08 WO PCT/IB2011/000225 patent/WO2011070557A2/fr active Application Filing
- 2011-02-08 EP EP11710560.1A patent/EP2509726B1/fr active Active
-
2016
- 2016-02-23 US US15/050,503 patent/US20160167115A1/en not_active Abandoned
Patent Citations (5)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US958220A (en) | 1909-07-26 | 1910-05-17 | Edwin J Blood | Cannon. |
US7410606B2 (en) | 2001-06-05 | 2008-08-12 | Appleby Michael P | Methods for manufacturing three-dimensional devices and devices created thereby |
US7141812B2 (en) | 2002-06-05 | 2006-11-28 | Mikro Systems, Inc. | Devices, methods, and systems involving castings |
US7411204B2 (en) | 2002-06-05 | 2008-08-12 | Michael Appleby | Devices, methods, and systems involving castings |
US7438527B2 (en) | 2005-04-22 | 2008-10-21 | United Technologies Corporation | Airfoil trailing edge cooling |
Cited By (2)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
CN112123662A (zh) * | 2020-09-08 | 2020-12-25 | 哈尔滨工业大学 | 一种复杂构型空腔水下吸声板的制备方法 |
CN112123662B (zh) * | 2020-09-08 | 2022-02-01 | 哈尔滨工业大学 | 一种复杂构型空腔水下吸声板的制备方法 |
Also Published As
Publication number | Publication date |
---|---|
US9272324B2 (en) | 2016-03-01 |
KR101440872B1 (ko) | 2014-09-17 |
WO2011070557A2 (fr) | 2011-06-16 |
EP2509728B1 (fr) | 2019-11-06 |
JP2013512783A (ja) | 2013-04-18 |
KR20120106790A (ko) | 2012-09-26 |
EP2509728A2 (fr) | 2012-10-17 |
WO2011070557A8 (fr) | 2012-01-12 |
WO2011071975A3 (fr) | 2011-10-06 |
US20160167115A1 (en) | 2016-06-16 |
JP5693607B2 (ja) | 2015-04-01 |
EP2509726B1 (fr) | 2019-11-06 |
CN102753284A (zh) | 2012-10-24 |
EP2509726A2 (fr) | 2012-10-17 |
CN102753284B (zh) | 2014-09-03 |
US20110132563A1 (en) | 2011-06-09 |
US20110132564A1 (en) | 2011-06-09 |
WO2011070557A3 (fr) | 2011-11-24 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
US9272324B2 (en) | Investment casting process for hollow components | |
EP2509727B1 (fr) | Procédé de coulée à la cire perdue sans cire | |
EP2991787B1 (fr) | Moulage à la cire perdue utilisant un outil de motif de cire souple servant à supporter un noyau en céramique le long de sa longueur pendant l'injection de cire | |
JP5518208B2 (ja) | 柔軟なワックスパターンツールを利用するインベストメント鋳造 | |
US8196640B1 (en) | Self supporting core-in-a-core for casting | |
EP1495820B1 (fr) | Procédé de coulée de précision | |
EP3429778B1 (fr) | Procédé de fabrication d'éléments caractéristiques perfectionnés dans un noyau pour la coulée | |
JP6556149B2 (ja) | 中空の部材の精密鋳造方法 | |
JP6918507B2 (ja) | 熱間等方圧加圧法により第1の金属部品の周囲に形成された第2の金属部品を用いた鋳造 | |
JP2010110795A (ja) | 一体型の使い捨て中子及びシェルダイを使用してガスタービン構成要素を製造する方法 | |
CN108367345B (zh) | 涡轮叶片制造方法 | |
EP3381582B1 (fr) | Procédé de fabrication de passages internes complexes dans des aubes de turbine | |
Magerramova et al. | Development of a method for manufacturing ceramic tooling for precision casting of blades made of heat-resistant alloys using additive technologies |
Legal Events
Date | Code | Title | Description |
---|---|---|---|
WWE | Wipo information: entry into national phase |
Ref document number: 201080055307.1 Country of ref document: CN |
|
121 | Ep: the epo has been informed by wipo that ep was designated in this application |
Ref document number: 10796523 Country of ref document: EP Kind code of ref document: A1 |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2010796523 Country of ref document: EP |
|
NENP | Non-entry into the national phase |
Ref country code: DE |
|
WWE | Wipo information: entry into national phase |
Ref document number: 2012543226 Country of ref document: JP |
|
ENP | Entry into the national phase |
Ref document number: 20127017689 Country of ref document: KR Kind code of ref document: A |