Classifications

• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
  • C01B3/00—Hydrogen; Gaseous mixtures containing hydrogen; Separation of hydrogen from mixtures containing it; Purification of hydrogen
  • C01B3/02—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen
  • C01B3/32—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen by reaction of gaseous or liquid organic compounds with gasifying agents, e.g. water, carbon dioxide, air
  • C01B3/323—Catalytic reaction of gaseous or liquid organic compounds other than hydrocarbons with gasifying agents
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
  • C01B3/00—Hydrogen; Gaseous mixtures containing hydrogen; Separation of hydrogen from mixtures containing it; Purification of hydrogen
  • C01B3/02—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen
  • C01B3/06—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen by reaction of inorganic compounds containing electro-positively bound hydrogen, e.g. water, acids, bases, ammonia, with inorganic reducing agents
  • C01B3/12—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen by reaction of inorganic compounds containing electro-positively bound hydrogen, e.g. water, acids, bases, ammonia, with inorganic reducing agents by reaction of water vapour with carbon monoxide
  • C01B3/16—Production of hydrogen or of gaseous mixtures containing a substantial proportion of hydrogen by reaction of inorganic compounds containing electro-positively bound hydrogen, e.g. water, acids, bases, ammonia, with inorganic reducing agents by reaction of water vapour with carbon monoxide using catalysts
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
  • C01B2203/00—Integrated processes for the production of hydrogen or synthesis gas
  • C01B2203/02—Processes for making hydrogen or synthesis gas
  • C01B2203/0283—Processes for making hydrogen or synthesis gas containing a CO-shift step, i.e. a water gas shift step
• • C—CHEMISTRY; METALLURGY
  • C01—INORGANIC CHEMISTRY
  • C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
  • C01B2203/00—Integrated processes for the production of hydrogen or synthesis gas
  • C01B2203/14—Details of the flowsheet
  • C01B2203/148—Details of the flowsheet involving a recycle stream to the feed of the process for making hydrogen or synthesis gas

Definitions

• This invention relates to water-gas shift processes.
• the water gas shift process is well established as a means to increase the hydrogen content and/or reduce the carbon monoxide content of synthesis gases produced by steam reforming, partial oxidation and gasification of hydrocarbon and carbonaceous feedstocks.
• the reaction may be depicted as follows. H 2 0 + CO ⁇ H 2 + C0 2
• HTS high-temperature-shift
• cobalt- molybdenum catalysts which can be used in so-called "sour shift” processes, may be operated with inlet temperatures above 220°C.
• synthesis gases derived from partial oxidation and in particular gasification of carbonaceous feedstocks.
• Such synthesis gases contain hydrogen, carbon oxides and a small amount of steam but have a relatively high carbon monoxide contents, typically > 45 mole% CO on a dry gas basis.
• Such "reactive" synthesis gases can, as a result of the increased amount of shifting required to generate acceptably low CO-containing product gases, cause overheating and deterioration of the shift catalyst if operated conventionally.
• GB1302135 describes a multi-stage shift process wherein a gaseous feed stream comprising CO and H 2 0 is passed over a first catalyst bed of water-gas shift catalyst at 350-1050°F and 1- 250 atm to produce a partially shifted gas mixture, a portion of which is recycled to the feed stream and the remainder cooled and passed over a second water gas shift catalyst bed disposed in the same vessel.
• the complicated use of multiple beds with inter-bed cooling was performed to maximise conversion of conventional synthesis gas mixtures at low steam:dry gas ratios and is not suited to reactive synthesis gases.
• US4161393 describes a multi-stage sour shift process wherein a raw gas produced by the gasification of a solid fuel is split; one portion is fed to a saturator where it is saturated with water vapour and fed to a shift vessel containing a sour shift catalyst at an inlet temperature in the range 280-450°C, to produce a shifted gas mixture which is combined with a further portion of the raw gas and fed to further shift vessels at an inlet temperature in the range 300-500°C. There is no recycle of the shifted gas mixture to the inlet of the shift vessels. Accordingly the invention provides a process for increasing the hydrogen content of a synthesis gas comprising hydrogen and carbon oxides having a carbon monoxide content > 45 mole% on a dry-gas basis, comprising the steps of:
• dry gas basis we mean the composition of the gas mixture disregarding the steam content. It will be understood that the synthesis gas, which may also be termed “dry gas” may contain relatively small amounts of steam.
• the process may be operated adiabatically at a suitably high inlet temperature, without the exotherm from the high CO in the synthesis gas feed causing deterioration of the shift catalyst towards the exit of the shift converter.
• the process of the aforesaid GB1302135 was exemplified with a synthesis gas feed having 48.71 % volume CO on a dry gas basis and because the conversions over the first shift catalyst were incomplete, the CO contents of the recycled gases were >10 mole%.
• GB1302135 does not consider the problem of using a high C0 2 -containing recycle stream to moderate the temperature through a single bed of high temperature shift catalyst fed with a reactive synthesis gas.
• the synthesis gas in the present invention may be any synthesis gas having a CO content > 45 mole % on a dry-gas basis, preferably > 55 mole % on a dry-gas basis ,but is preferably one derived from the gasification of coal, petroleum coke or biomass.
• the synthesis gas preferably has a carbon monoxide content > 60 mole % on a dry-gas basis.
• the synthesis gas requires sufficient steam to allow the water-gas shift reaction to proceed.
• synthesis gases derived from processes such as steam reforming may contain sufficient steam
• reactive synthesis gases generally are deficient in steam and steam must be added.
• the steam may be added by direct injection or by another means such as a saturator or steam stripper.
• a saturator or steam stripper In the present invention, because steam is present in the recycled shifted gas mixture the amount of fresh steam required is reduced over a non-recycle process.
• the amount of steam should desirably be controlled such that the total steam: synthesis gas volume ratio in the steam-enriched synthesis gas mixture fed to the catalyst, including the steam from the recycle stream, is in the range 0.5:1 to 4: 1 , preferably in the range 1 :1 to 2.5: 1.
• the inlet temperature of the shift process may be in the range 220-370°C, but is preferably in the range 240-350°C.
• the inlet temperature is preferably in the range 300-360°C and more preferably 310-330°C so that the performance of the catalyst over an extended period is maximised.
• the shift process is preferably operated adiabatically without cooling of the catalyst bed, although if desired some cooling may be applied for example by passing cooling water under pressure through tubes disposed in the catalyst bed.
• the exit temperature from the shift vessel is preferably ⁇ 500°C, more preferably ⁇ 475°C to maximise the life and performance of the catalyst.
• the process is preferably operated at elevated pressure in the range 1-100 bar abs, more preferably 15-50 bar abs.
• the water gas shift is a high-temperature shift catalyst comprising one or more iron oxides stabilised with chromia and/or alumina and which may optionally contain zinc oxide and one or more copper compounds.
• Iron oxide/chromia shift catalysts are conventionally made by precipitation of iron and chromium compounds (that decompose to the oxides upon heating) from a solution of iron and chromium salts by the addition of a suitable alkaline reactant, e.g. sodium hydroxide or carbonate. The resulting precipitate is then washed, dried, and calcined and tableted to form catalyst precursor pellets.
• the precursor preferably has an iron oxide content (expressed as Fe 2 0 3 ) of 60 to 95% by weight.
• the iron to chromium atomic ratio in the precursor is in the range 6 to 20, particularly 8 to 12.
• the precursor may contain oxides of other metals, e.g. aluminium, manganese, or, especially, copper. Particularly preferred precursors have an iron to copper atomic ratio of 10:1 to 100:1 .
• the pellets Prior to use for the shift reaction, the pellets are subjected to reduction conditions wherein the iron oxide is reduced to magnetite (Fe 3 0 4 ) and any chromium trioxide present reduced to the sesquioxide, chromia (Cr 2 0 3 ). This reduction is often carried out in the reactor wherein the shift reaction is to be effected.
• the activity of the catalyst may be significantly increased by incorporating into the catalyst precursor particles of aspect ratio of at least 2 and a maximum dimension of at least 5000A (500nm), and preferably less than 15000A (1500nm) into the catalyst precursor pellets.
• the chromia-promoted magnetite catalyst comprises acicular iron oxide particles.
• Such catalysts are described in US 5656566.
• a particularly suitable commercially available high temperature water gas shift catalyst is KATALCO JM TM 71-5 available from Johnson Matthey PLC.
• Zinc oxide and copper may desirably also be present.
• Such catalysts are described for example in WO2009078979.
• the water gas shift catalyst is a sour shift catalyst comprising 1-5% wt cobalt and 5-15% molybdenum, optionally with additional oxides such as magnesia and/or titanium dioxide, on a suitable support such as alumina or calcium aluminate.
• a suitable support such as alumina or calcium aluminate.
• Such catalysts are often made by impregnating an oxidic support composition with cobalt and molybdenum compounds and heating the resulting composition to convert the cobalt and molybdenum compounds to their respective oxides.
• the cobalt and molybdenum oxides may be sulphided with a suitable sulphur compound such as hydrogen sulphide.
• a suitable sulphur compound such as hydrogen sulphide.
• the water-gas shift reaction converts the majority of the CO in the feed gas to C0 2 such that the product gas mixture has a CO content ⁇ 10% by volume on a dry gas basis.
• the temperature, pressure and flowrates are set such that the hydrogen-enriched shifted gas mixture has a carbon monoxide content ⁇ 7.5% by volume on a dry gas basis.
• it is a portion of the product gas stream containing a low level of CO that is recycled. 20 to 80% by volume, preferably 30 to 45% by volume of the hydrogen- enriched shifted gas mixture is recycled to the feed gas mixture.
• the recycle may be controlled by conventional valve means.
• the recycle stream is fed through an injector.
• the synthesis gas, fresh steam and recycle stream may be combined in any order to form the mixed gas feed.
• the recycle stream may be mixed with steam in an injector and the mixed recycle stream/steam mixture combined with the synthesis gas to form the mixed feed stream.
• the product gas stream that is not recycled may be used in conventional downstream processes.
• the product gas stream may be fed, optionally with a part of the synthesis gas, to one or more further sour shift vessels containing a sour shift catalyst, for example as described in the aforesaid US 4161393.
• the product gas stream may be subjected to one or more further shift stages, such as medium temperature shift and/or low-temperature shift over one or more copper catalysts in separate vessels, but generally this is not required.
• the hydrogen enriched shifted gas without further shifting, may be cooled to a temperature below the dew point so that the steam condenses.
• the de-watered shifted gas mixture may be fed to methanol, dimethyl ether, Fischer-Tropsch wax, olefin and other chemical syntheses processes or may be subjected to a stage of C0 2 - removal to generate hydrogen for ammonia synthesis or the generation of electrical power as part of an IGCC process.
• FIG. 1 depicts a flowsheet of one embodiment of the present invention.
• a synthesis gas stream 10 comprising hydrogen and carbon oxides and having a carbon monoxide content > 55 mole % on a dry-gas basis, is mixed with a steam stream 12 and a compressed recycle stream 14 to form a steam-enriched feed gas mixture 16 which is heated in heat exchanger 18 to a temperature in the range 300-360°C and then fed via line 20 to the inlet of a shift converter 22 containing a fixed bed 24 of a particulate iron-containing water-gas shift catalyst.
• the water gas shift reaction occurs adiabatically over the catalyst 24 in the shift converter 22 thereby increasing the hydrogen content of the gas mixture and reducing the carbon monoxide content to ⁇ 10 mole% on a dry gas basis.
• the product hydrogen-enriched shifted gas mixture is recovered from the converter 22 via line 26.
• a portion of the product gas mixture is taken from line 26 via line 28 for recycle.
• the recycle stream is compressed in compressor 30 from which line 14 conveys the compressed recycle stream to form the feed gas mixture.
• the non-recycle product stream is recovered from line 26 via line 32.
• the steam stream 12 is liquid (and the mixed stream 16 partially liquid) in order to simplify its combination with the synthesis gas and recycle stream and allow a single heat exchanger to bring the feed mixture to the inlet temperature.
• variation in the flowsheet in order to efficiently combine gaseous steam, recycle stream and synthesis gas (dry gas) stream may be performed by the skilled person using conventional techniques and are within the scope of the present invention.
• the model shows that the exotherm across the catalyst is controlled to ⁇ 470°C using the recycle of H 2 /C0 2 -rich product gas.
• the catalyst is predicted to remain effective under these conditions for 3 or more years, while without a product gas recycle, the exotherm would cause rapid deactivation of the catalyst.
• the methane, air, nitrogen and methanol contents of the synthesis gas do not materially affect the performance of the catalyst under the conditions. Catalyst over-reduction is also not expected to occur under these conditions.

Landscapes

• Chemical & Material Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Organic Chemistry (AREA)
• Health & Medical Sciences (AREA)
• General Health & Medical Sciences (AREA)
• Engineering & Computer Science (AREA)
• Combustion & Propulsion (AREA)
• Inorganic Chemistry (AREA)
• Organic Low-Molecular-Weight Compounds And Preparation Thereof (AREA)
• Catalysts (AREA)
• Hydrogen, Water And Hydrids (AREA)
• Industrial Gases (AREA)

Priority Applications (7)

Applications Claiming Priority (2)

Related Child Applications (2)

Publications (1)

Family

ID=41501932

Family Applications (1)

Country Status (9)

Cited By (9)

Families Citing this family (10)

Citations (10)

Family Cites Families (12)

• 2009
  • 2009-11-05 GB GBGB0919385.5A patent/GB0919385D0/en not_active Ceased
• 2010
  • 2010-10-14 US US13/508,483 patent/US8821833B2/en not_active Expired - Fee Related
  • 2010-10-14 JP JP2012537446A patent/JP5680658B2/ja not_active Expired - Fee Related
  • 2010-10-14 AU AU2010316873A patent/AU2010316873B2/en not_active Ceased
  • 2010-10-14 CA CA2778409A patent/CA2778409A1/en not_active Abandoned
  • 2010-10-14 PL PL10766327T patent/PL2496517T3/pl unknown
  • 2010-10-14 EP EP10766327.0A patent/EP2496517B1/en not_active Ceased
  • 2010-10-14 CN CN201080050300.0A patent/CN102695669B/zh not_active Expired - Fee Related
  • 2010-10-14 WO PCT/GB2010/051730 patent/WO2011055132A1/en not_active Ceased
• 2014
  • 2014-04-22 US US14/258,469 patent/US9365421B2/en not_active Expired - Fee Related

Patent Citations (10)

Also Published As

Similar Documents

Legal Events