WO2010071298A2 - 난연성 접착제 조성물 및 그 제조방법 - Google Patents

난연성 접착제 조성물 및 그 제조방법 Download PDF

Info

Publication number
WO2010071298A2
WO2010071298A2 PCT/KR2009/006326 KR2009006326W WO2010071298A2 WO 2010071298 A2 WO2010071298 A2 WO 2010071298A2 KR 2009006326 W KR2009006326 W KR 2009006326W WO 2010071298 A2 WO2010071298 A2 WO 2010071298A2
Authority
WO
WIPO (PCT)
Prior art keywords
weight
flame
flame retardant
parts
retardant
Prior art date
Application number
PCT/KR2009/006326
Other languages
English (en)
French (fr)
Other versions
WO2010071298A3 (ko
Inventor
이한민
Original Assignee
(주)선만
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by (주)선만 filed Critical (주)선만
Publication of WO2010071298A2 publication Critical patent/WO2010071298A2/ko
Publication of WO2010071298A3 publication Critical patent/WO2010071298A3/ko

Abstract

본 발명은 난연성 접착제의 조성물에 관한 것으로 보다 상세하게는 멜라민 시아누레이트(melamine cyanurate) 0.1~5 중량부, 수산화마그네슘 0.5~5 중량부, 납석 7~15 중량부, 비석 15~30 중량부 및 규산소다 60~75 중량부를 포함하는 것을 특징으로 하는 난연성 접착제 조성물 및 그의 제조방법에 관한 것으로서, 유기계 난연제, 무기계 난연제 및 규산소다를 혼용하여 환경 친화적이면서도 난연성, 차열성, 접착성, 내수성이 우수한 난연제 접착제의 조성물 및 그 제조방법에 관한 것이다.

Description

난연성 접착제 조성물 및 그 제조방법
본 발명은 난연성 접착제의 조성물에 관한 것으로 보다 상세하게는 멜라민 시아누레이트(melamine cyanurate) 0.1~5 중량부, 수산화마그네슘 0.5~5 중량부, 납석 7~15 중량부, 비석 15~30 중량부 및 규산소다 60~75 중량부를 포함하는 것을 특징으로 하는 난연성 접착제 조성물 및 그의 제조방법에 관한 것으로서, 유기계 난연제, 무기계 난연제 및 규산소다를 혼용하여 환경 친화적이면서도 난연성, 차열성, 접착성, 내수성이 우수한 난연제 접착제의 조성물 및 그 제조방법에 관한 것이다.
연소하기 쉬운 성질을 가지고 있는 대부분의 종이, 헝겊, 플라스틱류 및 목재 등의 연소성 재질을 물리적 또는 화학적으로 개선시켜 잘 타지 못하도록 첨가하는 물질을 난연제라고 한다. 일반적으로 널리 사용되고 있는 난연제는 연소성 소재에 적용하는 방법에 따라 크게 첨가형과 반응형으로 나뉘고, 첨가형은 구성 성분에 따라 다시 유기계와 무기계 난연제로 구분된다. 첨가형 난연제는 물리적으로 난연제를 첨가해서 난연성을 향상시키는 것이고, 반응형 난연제는 화학반응을 일으켜 난연성을 향상시키는 것이다.
유기계는 주로 인계, 질소계를 포함하는 비할로겐계 난연제와 브롬계, 염소계를 포함하는 할로겐계 등으로 분류되고 무기계는 금속 수산화물계인 수산화알루미늄 및 수산화마그네슘과 안티몬계 제품등으로 분류된다.
현재 가장 많이 사용되고 있는 할로겐계 난연제 중, 브롬계 난연제는 난연화 효과가 뛰어나며, 비용대비 성능면에서 뛰어난 난연제로, 전기기기나 사무용기기의 하우징 재료, ABS(acrylonitrile butadiene styrene copolymer)수지나 PS(polystyrene), PBT(poly butylene terephthalate), PET(poly ethylene terephthalate), 에폭시 수지 등의 주요 난연제로서 사용되고 있으나 연소시 다이옥신이 발생하는 심각한 문제점이 지적되고 있으며, 특히 브롬계 난연제 제조에 사용되는 화합물인 데카브로모페닐 다이옥사이드(decabromophenyl dioxide), 옥타브로모페닐에테르(octabromophenylether) 등의 사용규제가 유럽 각국을 중심으로 검토 중인 것으로 알려져 있다. 또한, 무기계 난연제 중, 안티몬계 화합물 역시 인체 유해성 시비가 끊이지 않고 있다.
이에 유럽에서는 최근에 할로겐 및 안티몬이 함유된 난연제에는 '에코라벨'을 부여하고 있지 않는 등 규제를 가하고 있는 실정이어서, 최근의 난연제 개발의 동향은 단순히 난연성만 우수한 것이 아니라, 저유해성, 저발연성, 저부식성, 내열성을 겸비한 비할로겐계, 비안티몬계 난연제의 개발로 모아지고 있다.
무기계 난연제는 광범위하게 사용되는 난연제로서 고온에서 탈수되어 소화작용을 일으켜 난연제 역할을 하나 난연 지속이 어려운 단점이 있고, 비할로겐 난연제 중 인계 난연제는 연소되면서 인산이 발생하면서 탈수 반응이 일어나 고분자화되어 폴리인산막을 형성하여 산소를 차단해서 난연효과를 발현하나 인산이 되면 액상이 되어 잘 흘러내리는 단점이 있다. 또한, 인계 난연제는 저독성 및 고성능의 두 가지 측면을 만족시키면서 할로겐계 난연제의 대체품으로 각광받고 있지만 기존 제품에서 인계 난연제로 교체하는 프로세스 비용이 많이 들고, 비교적 고가라는 점이 단점으로 작용한다.
이에 본 발명은 난연성이 우수하면서도, 저독성, 저유해성을 가지고, 또한, 접착성능이 우수한 난연성 접착제 조성물 및 저장성이 우수한 난연성 접착제 조성물 제조방법에 관한 것이다.
본 발명은 상기의 목적을 달성하고자 멜라민 시아누레이트(melamine cyanurate) 0.1~5 중량부, 수산화마그네슘 0.5~5 중량부, 납석 7~15 중량부, 비석 15~30 중량부 및 규산소다 60~75 중량부을 포함하는 것을 특징으로 하는 난연성 접착제 조성물 및 그 제조방법을 제공한다.
본 발명은 난연성 접착제의 조성물로 멜라민 시아누레이트(melamine cyanurate) 0.1~5 중량부, 수산화마그네슘 0.5~5 중량부, 납석 7~15 중량부, 비석 15~30 중량부 및 규산소다 60~75 중량부를 포함하여 사용함으로 인하여 환경 친화적이면서도 난연성, 차열성, 접착성, 내수성이 우수한 효과가 있으며, 또한 본 발명의 난연성 접착제 제조방법은 먼저 규산소다에 무기계 난연제를 첨가하여 교반 혼합한 후 유기계 난연제를 첨가하여 교반 혼합하여 사용함으로 인하여 저장 안정성이 우수한 효과가 있다.
또한 본 발명의 난연성 접착제는 합판, 집성목 등의 목재류, 플라스틱, 부직포, 유기섬유펠트 등에 적용되어 우수한 난연성과 차열성을 부여할 수 있게 된다.
본 발명은 난연성 접착제의 조성물에 관한 것으로 보다 상세하게는 멜라민 시아누레이트(melamine cyanurate) 0.1~5 중량부, 수산화마그네슘 0.5~5 중량부, 납석 7~15 중량부, 비석 15~30 중량부 및 규산소다 60~75 중량부을 포함하는 것을 특징으로 하는 난연성 접착제 조성물 및 그의 제조방법에 관한 것으로서, 유기계 난연제, 무기계 난연제 및 규산소다를 혼용하여 환경 친화적이면서도 난연성, 차열성, 접착성, 내수성이 우수한 난연제 접착제의 조성물 및 그 제조방법에 관한 것이다.
더욱 자세히 설명하면, 본 발명은 유기계 난연제로 멜라민 시아누레이트(melamine cyanurate)를 사용하고, 여기에 무기계 난연제로 납석, 수산화마그네슘, 비석을 첨가하여 차열 효과 및 난연 상승효과를 부여하였으며, 접착성 물질로 규산소다를 사용한 것을 특징으로 한다.
본 발명에서는 유기계 난연제로 비할로겐계인 멜라민 시아누레이트를 사용하였다. 멜라민 시아누레이트는 할로겐계보다 독성이 적고, 취급이 용이한 특성이 있다. 특히 멜라민을 함유한 연질 폴리우레탄 폼 제품의 열분해시 독성기체의 발생이 없으며, 다른 난연제보다 연기의 발생이 적은 장점이 있다. 미국 환경청(United states Environmental Protection Agency)에서는 멜라민은 환경에 대한 독성의 위험 정도가 낮으며, 인간의 건강 및 환경에 악영향을 주는 증거가 없다는 연구결과를 발표한 바 있다. 본 발명에서 멜라민 시아누레이트의 사용량은 전체 중량의 0.1~5 중량부를 사용하였다. 0.1 중량부 미만일 경우에는 난연 효과가 저하되며 5 중량부 이상일 경우에는 난연효과는 우수하나 유기계 난연제가 고가이므로 원재료비가 올라가는 단점이 있다.
또한, 본 발명에서는 유기계 난연제와 함께 혼합사용되어 난연 상승 효과를 부여하기 위한 무기계 난연제로 비안티몬계인 납석, 수산화마그네슘, 비석을 혼합 사용하였으며, 특히 수산화마그네슘으로 인하여 차열성까지 부여하였다. 수산화마그네슘은 배합량당 난연효과가 다른 무기계 난연제인 수산화알루미늄보다 우수하며, 가격이 싸고 유독가스 및 연기발생을 억지하는 등의 장점이 있다. 납석과 비석은 내열성과 내화성이 우수하여, 상기 난연제와 혼합하여 사용할 경우 난연 효과 및 차열효과가 상승된다. 종래에는 난연효과를 상승시키기 위하여 유기계 난연제에 무기계 난연제로 안티몬계 물질(삼산화안티몬 등)을 사용하였으나, 상기한 바와 같이 삼산화안티몬은 인체유해성 물질에 해당하여, 본 발명에서는 수산화알루미늄, 납석, 비석 등을 혼합 사용하여 환경 친화적이면서도 난연성이 우수하도록 하였다.
무기계 난연제의 사용량은 전체 중량의 22~50 중량부를 사용하는 것이 바람직하다.
22 중량부 미만 사용시에는 난연 상승효과가 미미하였으며, 50 중량부 이상 사용시에는 비중이 높아져 저장성이 불량한 결과를 보인다. 특히 무기계 난연제 중 수산화마그네슘을 전체 중량부의 0.5~5 중량부를 사용함으로써 차열성을 부여할 수 있었다. 이것은 수산화마그네슘이 열이 가해졌을 경우 탈수 반응이 일어나는 성질을 이용한 것이다. 또한, 본 발명은 납석, 비석을 더 첨가함으로 인해 난연성 및 차열성을 상승시킬 수 있었다. 바람직하게는 수산화마그네슘 0.5~5 중량부, 납석 7~15 중량부 , 비석 15~30 중량부를 사용하는 것이 바람직하다.
또한, 접착성을 부여하기 위한 무기계 접착제로서는 규산소다, 규산칼륨, 실라카졸, 알루미나 졸 등이 있을 수 있으나, 이들 중 가장 저렴한 규산소다를 사용하는 것이 바람직하며, 대량생산을 고려하여 점도가 가장 낮은 3종 규산소다를 사용하는 것이 바람직하다. 규산소다의 사용량은 전체 중량부의 60~75 중량부를 사용하였다. 60 중량부 미만에서는 접착성이 불량하였으며, 75 중량부 이상에서는 수분에 민감하게 반응하여 접착성이 불량하였으며, 건조시간이 길어지는 결과를 보였다. 또한 규산소다는 화염에 접촉되었을 때 발포되어 미세한 공기층을 형성하게 되므로 난연 및 차열효과를 가져오게 된다.
이하 본 발명을 실시예에 의해 상세히 설명한다. 하기 실시예는 본 발명을 예시하는 것일 뿐, 본 발명의 범위가 하기 실시예에 한정되는 것은 아니다.
난연성 접착제의 제조
표 1에 나타난 중량부 배합량으로 난연성 접착제를 제조하였다.
표 1
구성성분 실시예 1 실시예 2 실시예 3 실시예 4 실시예 5 실시예 6 실시예 7
수산화마그네슘 3 0.5 0.5 0.5 0 0.5 3
납석 10 10 10 10 10 10 7
비석 18 18 13.5 18 18 18 18
규산소다 70 70 70 56 70 70 70
멜라민시아누레이트 2 2 2 2 2 0.1 2
난연성, 차열성, 접착성의 시험
상기 표 1의 배합량으로 제조된 난연성 접착제의 접착성, 난연성, 차열성을 측정하기 위한 시험방법은 다음과 같다.
접착성 시험을 위한 시편을 위해 상기 난연성 접착제 조성물을 5mm 두께의 합판에 일정량 (200~300 g/㎡) 도포하여 5매의 합판을 적층시켜 건조시킨 후 제조된 25mm 두께의 합판을 바닥에 던졌을 때 합판의 탈락에 의해 접착성을 시험하였다.
난연성 시험을 위한 시편은 상기의 접착성 시편제작방법과 동일한 방법으로 제작한 후, 간이 내화시험로에서 KS F2257-1(건축 구조 부재의 내화 시험방법)에 명시된 로내 온도 조건을 맞추면서 화염을 가하여 시편에 구멍이 생겨 화염통과가 된 시간을 측정하여 시험하였다. 화염통과 시험기준은 60분을 기준으로 하였으며, 이것을 난연성 평가기준으로 하여, 60분 이상의 경우 난연효과가 우수한 것으로, 60분 이하인 경우 난연효과가 불량한 것으로 하였다.
차열성 시험을 위한 시편은 상기의 접착성 시편제작방법과 동일한 방법으로 제작한 후, 간이 내화시험로에서 KS F2257-1(건축 구조 부재의 내화 시험방법)에 명시된 로내 온도 조건을 맞추면서 화염을 가하여 화염통과가 될 때까지의 이면의 온도를 온도기록계를 사용하여 측정하였다. 이면온도의 평가기준은 KS F2257-1에 명시된 이면온도 기준(비가열면의 평균 상승온도가 140 ℃ 이상이거나 최고 상승온도가 180℃이상인 경우 차열성에 실패한 것으로 규정되어 있다)에 의하여 평가하였다.
아래 표 2는 표1의 배합량으로 제조된 난연성 접착제 실시예의 접착성, 난연성, 차열성 시험결과이다.
표 2
실시예 1 실시예 2 실시예 3 실시예 4 실시예 5 실시예 6 실시예 7
접착성 양호 양호 양호 불량 양호 양호 양호
화염통과 72분 65분 51분 67분 67분 47분 56분
이면온도(℃) 89 142 146 150 215 152 114
상기의 표 2의 시험결과를 분석하면, 멜라민시아누레이트와 수산화마그네슘, 비석, 납석, 규산소다를 일정 중량부로 사용한 경우, 즉, 멜라민시아누레이트 2 중량부, 수산화마그네슘 3 중량부, 납석 10 중량부, 비석 18 중량부, 규산소다 70 중량부를 사용한 실시예 1의 경우가 접착성(양호) 및 난연성(72분), 차열성(이면온도 89℃)로 가장 우수한 결과를 나타내었다.
실시예 2는 실시예 1과 비교시 수산화마그네슘 중량부를 감소시킨 경우 화염통과 시간이 65분으로 단축된 결과를 나타내였으며, 이면온도도 142℃로 상승되었는바, 수산화마그네슘이 일정 중량비 이상 사용되는 것아 바람직함을 알 수 있다.
특히 실시예 5의 경우 실시예 1과 비교하여 난연성 접착제 조성물 내에 수산화마그네슘만 첨가하지 않은 경우로서, 시험결과 이면온도가 215℃도로 급격히 상승하는 것을 알 수 있어, 수산화마그네슘이 본 발명에 차열효과에 주도적으로 역할을 하는 것을 알 수 있고, 또한, 난연 상승효과에도 부수적으로 영향을 미친다는 것을 알 수 있다. 따라서 본 발명에서는 난연성 접착제 조성물 내에 수산화마그네슘의 중량부는 0.5 ~ 5 중량부를 사용하는 것이 바람직하다.
실시예 2와 실시예 3을 비교시 난연성 접착제 조성물 내에 비석의 중량부를 18 중량부에서 13.5 중량부로 감소하였을 경우 화염통과 시간이 65분에서 51분으로 단축되어 난연성이 급격히 저하됨을 알 수 있으며, 이면온도도 142℃에서 146℃로 상승되어 차열효과도 감소됨을 알 수 있다. 따라서 난연성 접착제 조성물 내에 비석의 중량부는 18 중량부 이상을 사용하는 것이 바람직하다.
실시예 2와 실시예 4를 비교시 난연성 접착제 조성물 내에 규산소다의 중량부를 70 중량부에서 56 중량부로 감소시켰을 경우 접착성이 불량한 결과를 보였으며, 이면온도도 142℃에서 150℃로 상승되어 차열효과도 감소됨을 알 수 있다. 따라서 난연성 접착제 조성물 내에 규석의 중량부는 60~75 중량부를 사용하는 것이 바람직하다. 75 중량부 이상 사용할 경우는 접착성이 불량하였으며, 건조시간이 길어지는 바 바람직하지 못하다.
실시예 2와 실시예 6을 비교시 난연성 접착제 조성물 내에 멜라민 시아누레이트 중량부를 2에서 0.1로 감소하였을 경우, 화염통과 시간이 65분에서 47분으로 급격히 감소하여 난연효과가 불량한 결과를 보였으며, 또한, 이면온도도 142℃에서 152℃로 상승되어 차열효과도 감소됨을 알 수 있다. 따라서 난연성 접착제 조성물 내에 멜라민 시아누레이트는 0.1 중량부 이상 사용하는 것이 바람직하고, 비용이 고가인 관계로 5 중량부 이하로 사용하는 것이 바람직하다.
실시예 7은 실시예 1과 비교시 난연성 접착제 조성물 내에 납석 중량비를 10중량부에서 7중량부로 감소하였을 경우 화염통과 시간이 72분에서 56분으로 감소하여 난연효과가 불량한 결과를 보였으며, 이면온도도 89℃에서 114℃로 상승되어 차열효과도 감소됨을 알 수 있다. 따라서 난연성 접착제 조성물 내에 납석의 중량부는 7 중량부 이상 사용하는 것이 바람직하다.
아래 표 3은 본 발명의 최적의 실시예 1과 비교예의 중량부 배합량과 그에 따른 접착성, 난연성, 차열성 시험결과를 나타낸 표이다.
표 3
실시예 1 비교예 1 비교예 2 비교예 3 비교예 4 비교예 5 비교예 6
수산화 마그네슘 3 - 30 - 3 3 -
납석 10 30 - - 10 10 -
비석 18 - - 30 18 18 -
규산소다 70 56 70 70 70 70 70
멜라민 시아누레이트 2 2 2 2 - - 2
트리페닐포스페이트 - - - - - 2 -
접착성 양호 불량 양호 양호 양호 양호 양호
화염통과 72분 65분 43분 71분 45분 54분 40분
이면온도(℃) 89 225 159 268 160 154 300
표 3을 보면 본 발명의 난연성 접착제 조성물 중 수산화마그네슘, 납석, 비석 중 어느 하나만 사용하였을 경우(비교예 1, 2 ,3), 비록 그 중량비을 늘린다 하더라도 수산화마그네슘, 납석, 비석 모두를 사용한 경우에 비하여 난연효과 및 차열효과가 크게 감소하는 결과를 보였다. 다만 비교예 3의 경우 난연효과는 실시예 1에 비해 큰 차이가 없는 것으로 나왔지만 차열효과가 크게 떨어져, 수산화마그네슘 및 납석이 큰 차열효과를 가져옴을 알 수 있다.
또한, 실시예 1과 비교예 2를 비교할 때 납석과 비석을 사용하지 않은 경우 난연효과 및 차열효과가 크게 떨어지는 결과를 가져오므로, 납석과 비석이 난연 상승효과 및 차열효과에 중요한 역할을 함을 알 수 있다.
또한, 비교예 4의 경우 멜라민 시아누레이트를 사용하지 않은 경우 무기계 난연제와 혼합 사용한 경우에 비하여 난연효과 및 차열효과가 크게 감소하는 것으로 나타났으며, 비교예 6의 경우 멜라민 시아누레이트 단독으로 사용한 경우 무기계 난연제와 혼합 사용한 경우에 비하여 난연효과 및 차열효과가 크게 감소하는 것으로 나타나, 무기계 난연제 단독으로, 또는 유기계 난연제 단독으로 사용한 경우보다 이를 혼합하여 사용하는 것이 훨씬 더 우수한 난연효과 및 차열효과를 가져오는 것을 알 수 있다.
그리고, 실시예 1과 비교예 5를 비교시 유기계 난연제로 멜라민 시아누레이트를 사용하는 대신 인계 난연제인 트리페닐 포스페이트(triphenyl phosphate)를 사용한 경우 멜라닌 시아누레이트를 사용한 것에 비하여 난연효과 및 차열효과가 크게 감소하는 결과를 보였다.
그리고 규산소다의 함량을 60 중량부 이하로 사용한 경우 접착성이 불량한 결과를 보였다.
따라서, 본 발명은 유기계 난연제로 멜라민 시아누레이트(melamine cyanurate)를 사용하고, 무기계 난연제로 납석, 수산화마그네슘, 비석을 혼합하여 사용함으로 인하여 우수한 차열 효과 및 난연 상승효과를 가져올 수 있었으며, 비할로겐계, 비안티몬계 난연제를 사용함으로 인하여 환경 친화적인 효과를 가져올 수 있는 것이다.
또한 본 발명의 난연성 접착제 조성물 제조방법은 먼저 규산소다에 무기계 난연제를 첨가하여 교반 혼합한 후 유기계 난연제를 첨가하여 교반 혼합하는 것을 특징으로 한다. 이렇게 제조된 난연성 접착제는 교반 혼합 시 별다른 문제점을 발생시키지 않았으며 7일 이상의 저장 안정성을 보여주고 있다. 반면, 규산소다에 유기계 난연제를 첨가하여 교반 혼합한 후 무기계 난연제를 첨가하여 교반 혼합한 하여 난연성 접착제를 제조한 경우에는 제조된 난연성 접착제가 겔(gel)상태가 되어 유동성이 떨어져 믹싱 탱크에서의 난연성 접착제 이송시 이송이 어려운 문제점이 발생하였다. 따라서 본 발명의 난연성 접착제 조성물 제조방법은 규산소다에 무기계 난연제로 수산화마그네슘, 비석, 납석을 먼저 첨가하여 교반 혼합한 후 유기계 난연제로 멜라민 시아누레이트를 첨가하여 교반 혼합하여 제조된 것을 특징으로 한다.

Claims (3)

  1. 유기계 난연제로 멜라민 시아누레이트(melamine cyanurate) 0.1~5 중량부와 무기계 난연제로 수산화마그네슘, 납석 및 비석의 혼합물 22~50 중량부와 규산소다 60~75 중량부를 포함하는 것을 특징으로 하는 난연성 접착제 조성물.
  2. 유기계 난연제로 멜라민 시아누레이트(melamine cyanurate) 0.1~5 중량부와 무기계 난연제로 수산화마그네슘 0.5~5 중량부, 납석 7~15 중량부, 비석 15~30 중량부와 규산소다 60~75 중량부를 포함하는 것을 특징으로 하는 난연성 접착제 조성물.
  3. 제1항 또는 제2항에 기재된 난연성 접착제 조성물의 제조방법에 있어서, 먼저 규산소다에 무기계 난연제를 첨가하여 교반 혼합한 후 유기계 난연제를 첨가하여 교반 혼합하는 것을 특징으로하는 난연성 접착제 조성물 제조방법.
PCT/KR2009/006326 2008-12-15 2009-10-30 난연성 접착제 조성물 및 그 제조방법 WO2010071298A2 (ko)