WO2009043818A1 - Hilfsmittel zur elektrischen kontaktierung von hochtemperatur-brennstoffzellen und verfahren zu dessen herstellung - Google Patents
Hilfsmittel zur elektrischen kontaktierung von hochtemperatur-brennstoffzellen und verfahren zu dessen herstellung Download PDFInfo
- Publication number
- WO2009043818A1 WO2009043818A1 PCT/EP2008/062925 EP2008062925W WO2009043818A1 WO 2009043818 A1 WO2009043818 A1 WO 2009043818A1 EP 2008062925 W EP2008062925 W EP 2008062925W WO 2009043818 A1 WO2009043818 A1 WO 2009043818A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- metal
- adhesive tape
- aid
- cell
- nickel
- Prior art date
Abstract
Description
Claims