WO2008133320A1 - ノズルベーン式ターボチャージャーの排気ガイド部品 - Google Patents
ノズルベーン式ターボチャージャーの排気ガイド部品 Download PDFInfo
- Publication number
- WO2008133320A1 WO2008133320A1 PCT/JP2008/058002 JP2008058002W WO2008133320A1 WO 2008133320 A1 WO2008133320 A1 WO 2008133320A1 JP 2008058002 W JP2008058002 W JP 2008058002W WO 2008133320 A1 WO2008133320 A1 WO 2008133320A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- nozzle vane
- exhaust
- exhaust guide
- turbocharger
- mass
- Prior art date
Abstract
Description
Claims