WO2007034672A1 - 防音材 - Google Patents

防音材 Download PDF

Info

Publication number
WO2007034672A1
WO2007034672A1 PCT/JP2006/317566 JP2006317566W WO2007034672A1 WO 2007034672 A1 WO2007034672 A1 WO 2007034672A1 JP 2006317566 W JP2006317566 W JP 2006317566W WO 2007034672 A1 WO2007034672 A1 WO 2007034672A1
Authority
WO
WIPO (PCT)
Prior art keywords
thermoplastic resin
weight
soundproofing
sound
soundproofing material
Prior art date
Application number
PCT/JP2006/317566
Other languages
English (en)
French (fr)
Inventor
Nobuhiko Inui
Joji Yamada
Eduard Karel Offermanns
Armand Alphons Duijsens
Laurens Petrus Vogels
Original Assignee
Sekisui Chemical Co., Ltd.
Alveo Ag
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sekisui Chemical Co., Ltd., Alveo Ag filed Critical Sekisui Chemical Co., Ltd.
Priority to US11/991,554 priority Critical patent/US20090272932A1/en
Priority to EP06797466A priority patent/EP1923421A4/en
Priority to JP2007536439A priority patent/JPWO2007034672A1/ja
Publication of WO2007034672A1 publication Critical patent/WO2007034672A1/ja

Abstract

　本発明は、優れた防音性及び成形性を有する防音材を提供する。本発明の防音材は、熱可塑性樹脂発泡体中に無機化合物を含有させてなり、熱可塑性樹脂発泡体を構成している熱可塑性樹脂１００重量部に対して無機化合物を３０～３００重量部含有していることを特徴とするので、優れた防音性及び成形性を有しており、防音処理を施したい被防音部材の形状に沿った形態に公知の成形方法を用いて精度良く成形することができるので、自動車の床材や、エンジンルームと車室とを仕切る隔壁などの被防音部材上に防音材を被防音部材との間に殆ど隙間を生じさせることなく安定的に貼着させることができ、防音処理を確実に施すことができる。

Description

明 細 書
防音材
技術分野
[0001] 本発明は、優れた防音性及び成形性を有する防音材に関する。
背景技術
[0002] 従来から、多種多様な防音材が自動車や鉄道などの車輛の他にエレベーターなど の乗り物に多く使用されている。特に、自動車用途では、エンジン力も発生する音の 車室内への侵入が室内音環境を悪ィ匕させる要因となっており、そのために、エンジン 、フロアシート、トランクなどに防音材を使用している。
[0003] このような防音材としては、特許文献 1に、ゴム成分を 90重量％以上含有するバイ ンダ一成分、充填材成分及び添加材類などを混練、圧延し、 20°Cにおける弾性率を 5 X 107 Pa以下としてなる遮音性シートが提案されて 、る。
[0004] この遮音性シートは、密度を増加させて遮音性を付与するために、バインダー成分 中に充填材成分を含有させてあり、そのために、遮音性シートは、高比重なものとな つており硬くて切断加工が困難であると共に、折り曲げなどの成形性にも乏しいとい つた問題点を有していた。
[0005] 更に、上記遮音性シートは伸び性にも乏しぐ金型を用いて遮音性シートを成形し ようとしても、遮音性シートに亀裂を生じ或いは切断してしまい、所望形状を有する成 形品に成形することができな力つた。
[0006] 従って、自動車の床鋼板などの複雑な形状を有する振動金属板に、遮音性シート を振動金属板の形状に沿った状態に成形した上で貼着しょうとしても、遮音性シート を振動金属板の形状に沿った形状に正確に成形することができな!/、ことから、遮音 性シートと振動金属板との間に隙間を生じ、この隙間を埋める作業を別途要するなど の問題点を生じていた。
[0007] 特許文献 1 :特開平 6— 301385号公報
発明の開示
発明が解決しょうとする課題 [0008] 本発明は、優れた防音性及び成形性を有する防音材を提供する。
課題を解決するための手段
[0009] 本発明の防音材は、熱可塑性榭脂発泡体と、この熱可塑性榭脂発泡体を構成して いる熱可塑性榭脂 100重量部に対して 30〜300重量部の割合で熱可塑性榭脂発 泡体中に含有されて 、る無機化合物とからなることを特徴とする。
[0010] 即ち、本発明の防音材は、熱可塑性榭脂発泡体中に無機化合物を含有させてなり 、熱可塑性榭脂発泡体を構成している熱可塑性榭脂 100重量部に対して無機化合 物を 30〜300重量部含有して 、ることを特徴とする。
[0011] 上記熱可塑性榭脂発泡体を構成している熱可塑性榭脂としては、特に限定されず 、例えば、高密度ポリエチレン、中密度ポリエチレン、低密度ポリエチレン、直鎖状低 密度ポリエチレン、エチレン 酢酸ビニル共重合体などのポリエチレン系榭脂や、プ ロピレン単独重合体、プロピレンと他のォレフィンとの共重合体などのポリプロピレン 系榭脂などのポリオレフイン系榭脂；ポリスチレン系榭脂；ポリエステル系榭脂；ポリア ミド系榭脂;ポリイミド系榭脂;石油榭脂などの有機材料などが挙げられ、防音材が剛 性に優れており、防音材の取扱中に橈みや反りが発生しにくく作業性に優れている 点で、ポリオレフイン系榭脂が好ましぐポリエチレン系榭脂とエチレン 酢酸ビュル 共重合体とを併用することがより好ましい。
[0012] そして、上記熱可塑性榭脂発泡体中に無機化合物を所定割合でもって含有させる ことによって防音材が構成されている。このような無機化合物としては、例えば、硫酸 ノリウム、硫酸マグネシウムなどの無機酸の金属塩の他に、水酸ィ匕アルミニウム、水 酸ィ匕マグネシウムなどの金属水酸ィ匕物が挙げられるが、防音材は成形時に加熱され るので、この加熱によって分解する虞れのない、無機酸の金属塩が好ましぐ硫酸バ リウムがより好ましい。
[0013] 更に、防音材中における無機化合物の含有量は、少ないと、防音材の防音性が低 下する一方、多いと、防音材の成形性が低下するので、熱可塑性榭脂発泡体を構成 している熱可塑性榭脂 100重量部に対して 30〜300重量部に限定され、 75〜250 重量部が好ましい。
[0014] このように、本発明の防音材は、熱可塑性榭脂発泡体中に無機化合物を所定割合 で充填することによって優れた防音性能を付与している。ここで、熱可塑性榭脂中に 無機充填材、特に、硫酸バリウムなどの比重の大きな無機化合物を高充填させると、 一般的に熱可塑性榭脂は、その伸び性が低下して成形性が低下し、真空成形など の成形方法を適用し難くなる。
[0015] そこで、本発明の防音材では、無機化合物を含有させることによる熱可塑性榭脂の 伸び性の低下を補完すベぐ熱可塑性榭脂を発泡させて熱可塑性榭脂発泡体とし、 この熱可塑性榭脂発泡体中に無機化合物を含有させている。このように、熱可塑性 榭脂を発泡させて熱可塑性榭脂発泡体とすることによって、熱可塑性榭脂の引張り 時の破断点の伸び率を向上させることができ、その結果、熱可塑性榭脂発泡体、即 ち、防音材の成形性を向上させることができ、防音材を真空成形などの公知の成形 方法を用いて所望形状に精度良く成形することができる。
[0016] 即ち、本発明の防音材は、熱可塑性榭脂を発泡させて熱可塑性榭脂発泡体とし、 伸び性を向上させていることから、この熱可塑性榭脂発泡体中に無機化合物を高充 填させることが可能となり、その結果、本発明の防音材は優れた防音性を備えている 上に成形性にも優れたものとなっている。
[0017] そして、無機化合物を含有させた熱可塑性榭脂発泡体、即ち、防音材の見掛け密 度は、小さいと、防音材の防音性が低下することがある一方、大きいと、防音材の成 形性が低下することがあるので、 0. 1〜0. 8gZcm3が好ましぐ 0. 25-0. 7g/cm 3がより好ましい。なお、防音材の見掛け密度は、 JIS Z6767に準拠して測定された ものをいう。
[0018] 又、熱可塑性榭脂発泡体を構成して!/ヽる熱可塑性榭脂の樹脂倍率は、小さ ヽと、 熱可塑性榭脂発泡体を構成して！/ヽる熱可塑性榭脂の伸び性が低下して、防音材の 成形性が低下することがあるので、 300%以上が好ましぐ 500%以上がより好ましく 、大き過ぎると、防音材の成形時に防音材に破れや亀裂を生じることがあるので、 15 00%以下が好ましぐ 1000%以下がより好ましい。
[0019] なお、熱可塑性榭脂発泡体を構成して!/ヽる熱可塑性榭脂の樹脂倍率は、熱可塑 性榭脂自体の発泡前後における体積膨張率を示す指標であり、具体的には、下記 式 1で算出されたものをいう。なお、無機化合物の密度を AgZcm3と、熱可塑性榭 脂発泡体を構成している熱可塑性榭脂の密度を BgZcm3とする。熱可塑性榭脂発 泡体中に含有されている無機化合物の重量を Xgと、熱可塑性榭脂の重量を Ygとす る。無機化合物を含有する熱可塑性榭脂発泡体全体の見掛け密度を CgZcm3とす る。なお、熱可塑性榭脂発泡体を構成している熱可塑性榭脂が二種以上の熱可塑 性榭脂の混合物である場合、熱可塑性榭脂の密度とは、熱可塑性榭脂の混合物の 密度をいう。
[0020] [数 1]
樹脂倍率（％) X100 ■ ■ ■ 式 1
Figure imgf000006_0001
[0021] そして、防音材の厚みは、薄いと、防音材の防音性が低下し或いは防音材の機械 的強度が低下することがある一方、厚いと、防音材の成形性が低下することがあるの で、 2〜6mmが好ましい。防音材の遮音性は、 5dB以上が好ましぐ 10dB以上がよ り好ましい。
[0022] 次に、本発明の防音材の製造方法を説明する。この防音材の製造方法としては特 に限定されず、例えば、（1)熱可塑性榭脂、無機化合物及び熱分解型発泡剤からな る発泡性榭脂組成物をラボプラストミルなどの汎用の攪拌装置に供給して溶融混練 した上でプレス成形などの汎用の成形方法によって発泡性榭脂シートを作製し、この 発泡性榭脂シートを、必要に応じて電子線、 α線、 |8線などの電離性放射線を照射 することによって架橋した後、発泡性榭脂シートを熱分解型発泡剤の分解温度以上 の温度に加熱して発泡させて防音材を製造する方法、（2)熱可塑性榭脂、無機化合 物及び熱分解型発泡剤からなる発泡性榭脂組成物を押出機に供給して溶融混練し て押出機力 発泡性榭脂シートを連続的に押出し、この発泡性榭脂シートを必要に 応じて電子線、 α線、 j8線などの電離性放射線を照射することによって架橋した後、 発泡性榭脂シートを熱分解型発泡剤の分解温度以上の温度に加熱して発泡させて 防音材を連続的に製造する方法などが挙げられる。
[0023] なお、上記熱分解型発泡剤としては、従来力 発泡体の製造に用いられているもの であれば、特に限定されず、例えば、ァゾジカルボンアミド、ベンゼンスルホ-ルヒドラ ジド、ジニトロソペンタメチレンテトラミン、トルエンスルホ-ルヒドラジド、 4, 4 ォキシ ビス（ベンゼンスルホ-ルヒドラジド）などが挙げられ、これらは単独で用いられても二 種類以上が併用されてもよい。
[0024] 得られた防音材は、自動車の床鋼板などの防音処理を施した!/ヽ部材 (以下「被防 音部材」 t 、うことがある)の形状に沿った形状に成形された上で、被防音部材に接 着剤などを用いて貼着されて用いられる。なお、防音材を成形する成形方法としては 、従来力も公知の成形方法を用いることができ、例えば、真空成形、圧空成形などが 挙げられる。
[0025] この際、防音材は、被防音部材の形状に沿って精度良く成形されていることから、 防音材を被防音部材に該被防音部材との間に隙間を殆ど生じさせることなく貼着さ せることができ、防音処理を容易に行うことができる。
発明の効果
[0026] 本発明の防音材は、熱可塑性榭脂発泡体と、この熱可塑性榭脂発泡体を構成して いる熱可塑性榭脂 100重量部に対して 30〜300重量部の割合で熱可塑性榭脂発 泡体中に含有されている無機化合物とからなることを特徴とするので、優れた防音性 、特に遮音性を有して 、ると共に成形性にも優れて！/、る。
[0027] 従って、本発明の防音材は、防音処理を施した!/、被防音部材の形状に沿った形態 に公知の成形方法を用いて精度良く成形することができるので、自動車の床材や、 エンジンルームと車室とを仕切る隔壁などの被防音部材上に防音材を被防音部材と の間に殆ど隙間を生じさせることなく安定的に貼着させることができ、防音処理を確 実に施すことができる。
[0028] 更に、本発明の防音材において、熱可塑性榭脂発泡シートを構成している熱可塑 性榭脂がポリオレフイン系榭脂である場合には、剛性に優れており、防音材の取り扱 Vヽ中に橈みや反りが発生しにくく、作業性にも優れて!/、る。
[0029] そして、本発明の防音材において、無機化合物が、無機酸の金属塩である場合に は、防音材を成形する際に加えられる熱にもかかわらず安定的に熱可塑性榭脂発泡 体中に存在し、防音材をその防音性能を損なうことなく所望形状に成形させることが できる。
[0030] 又、本発明の防音材において、見掛け密度が 0. 1〜0. 8g/cm3である場合には 、防音材は、より優れた防音性及び成形性を有する。
図面の簡単な説明
[0031] [図 1]防音材の成形性の測定要領を示した模式断面図である。
符号の説明
[0032] 1 雌金型
2 成形品
21 底面部
22 周壁部
発明を実施するための最良の形態
[0033] (実施例 1)
低密度ポリエチレン (三井住友ポリオレフイン社製商品名「LE520」）65重量部、ェ チレン 酢酸ビュル共重合体 (三井デュポンポリケミカル社製 商品名「エバフレック ス EV460」、酢酸ビニル含有量： 19重量％) 35重量部、硫酸バリウム (竹原化学社 製 商品名「W—1」） 150重量部、ァゾジカルボンアミド (大塚ィ匕学社製 商品名「ュ 二フォーム AZ SO— 40」 ) 4重量部及び発泡助剤としてステアリン酸亜鉛 (堺化学社 製 商品名「SZ— 2000」） 1重量部力 なる発泡性榭脂組成物をラボプラストミルに 供給して 110°Cにて 15分間に亘つて混練して均一に混合した後、発泡性榭脂組成 物を 110°Cにてプレス成形して厚みが 2. 5mmの発泡性榭脂シートを作製した。
[0034] この発泡性榭脂シートに 800KVの条件下にて電子線を 2. OMrad照射させること によって発泡性榭脂シートを架橋した。この発泡性榭脂シートをオーブンに供給して 、発泡性榭脂シートを 240°Cにて 80秒間に亘つて放置して発泡させて、低密度ポリ エチレン及びエチレン 酢酸ビュル共重合体力 なるポリオレフイン系榭脂よりなる 発泡シート中に硫酸バリウムが含有されてなる防音材を得た。なお、得られた防音材 は、その見掛け密度が 0. 33g/cm3で、厚みが 3. 7mmであった。又、熱可塑性榭 脂発泡シートを構成しているポリオレフイン系榭脂の榭脂倍率は、 650. 4%であった 。なお、低密度ポリエチレン及びエチレン 酢酸ビュル共重合体力 なるポリオレフィ ン系榭脂の密度は 0. 9gZcm3で、硫酸バリウムの密度は 4. 3gZcm3であった。
[0035] (実施例 2)
硫酸バリウムを 150重量部の代わりに 100重量部としたこと、ァゾジカルボンアミドを 4重量部の代わり 3重量部としたこと、ステアリン酸亜鉛を 1重量部の代わりに 0. 8重 量部としたこと以外は実施例 1と同様にして防音材を得た。なお、得られた防音材は 、その見掛け密度が 0. 31g/cm3で、厚みが 3. 6mmであった。又、熱可塑性榭脂 発泡シートを構成しているポリオレフイン系榭脂の榭脂倍率は、 559. 7%であった。
[0036] (実施例 3)
硫酸バリウムを 150重量部の代わりに 50重量部としたこと、ァゾジカルボンアミドを 4 重量部の代わり 2重量部としたこと、ステアリン酸亜鉛を 1重量部の代わりに 0. 6重量 部としたこと以外は実施例 1と同様にして防音材を得た。なお、得られた防音材は、 その見掛け密度が 0. 32g/cm3で、厚みが 3. 7mmであった。又、熱可塑性榭脂発 泡シートを構成しているポリオレフイン系榭脂の榭脂倍率は、 411. 4%であった。
[0037] (実施例 4)
硫酸バリウムを 150重量部の代わりに 50重量部としたこと、発泡性榭脂シートの厚 みを 2. 5mmの代わりに 2. Ommとしたこと以外は実施例 1と同様にして防音材を得 た。なお、得られた防音材は、その見掛け密度が 0. 16gZcm3で、厚みが 3. 7mm であった。又、熱可塑性榭脂発泡シートを構成しているポリオレフイン系榭脂の榭脂 倍率は、 833. 3%であった。
[0038] (比較例 1)
硫酸バリウムを用いな力つたこと、ァゾジカルボンアミドを 4重量部の代わり 1. 4重量 部としたこと、ステアリン酸亜鉛を 1重量部の代わりに 0. 4重量部としたこと以外は実 施例 1と同様にして防音材を得た。なお、得られた防音材は、その見掛け密度が 0. 4 Og/cm3で、厚みが 3. 7mmであった。又、熱可塑性榭脂発泡シートを構成している ポリオレフイン系榭脂の榭脂倍率は、 225. 0%であった。
[0039] (比較例 2)
硫酸バリウムを用いな力つたこと、発泡性榭脂シートの厚みを 2. 5mmの代わりに 2 . Ommとしたこと以外は実施例 1と同様にして防音材を得た。なお、得られた防音材 は、その見掛け密度が 0. l lg/cm3で、厚みが 3. 8mmであった。又、熱可塑性榭 脂発泡シートを構成しているポリオレフイン系榭脂の榭脂倍率は、 818. 2%であった
[0040] (比較例 3)
硫酸バリウムを 150重量部の代わりに 350重量部としたこと、ァゾジカルボンアミドを 4重量部の代わり 6重量部としたこと、ステアリン酸亜鉛を 1重量部の代わりに 1. 3重 量部としたこと、発泡性榭脂シートの厚みを 2. 5mmの代わりに 2. Ommとしたこと以 外は実施例 1と同様にして防音材を得た。なお、得られた防音材は、その見掛け密 度が 0. 61g/cm3で、厚みが 3. 6mmであった。又、熱可塑性榭脂発泡シートを構 成しているポリオレフイン系榭脂の榭脂倍率は、 590. 7%であった。
[0041] (比較例 4)
エチレン プロピレン ジェンゴム（EPDM)シート（見掛け密度： 2. 4gZcm3、厚 み： 1. 7mm)を防音材とした。
[0042] 得られた防音材の成形性及び防音性を下記の要領で測定し、その結果を表 1に示 した。
[0043] (成形性）
防音材をその両面温度が 140°Cとなるように遠赤外線ヒーターを用いて加熱した。 次に、図 1に示したような有底円筒状の雌金型 1を用意して、この雌金型 1を用いて 防音材を真空成形し、平面円形状の底面部 21と、この底面部 21に直交した状態に底 面部 21の外周縁に延設された円筒状の周壁部 22とからなる有底円筒状の成形品 2 を得た。なお、防音材の真空成形は、成形品 2の周壁部 22の厚みが均一であること、 底面部 21に亀裂ゃ孔が生じて 、な 、こと、底面部 21の厚みと周壁部 22の厚みとが略 同一であることの三条件を満たす範囲内において、防音材を最大限、深く真空成形 した。
[0044] そして、成形品の外底面の直径 Dと、雌金型 1内に防音材を真空吸引した深さ Hと 力も下記式 2に基づいて真空成形最大絞り比 (HZD)を算出し、これを成形性の指 標とした。真空成形最大絞り比が大きければ大きいほど防音材は成形性に優れてい る。 真空成形最大絞り比 (HZD) =深さ HZ直径 D， · ·式 2
[0045] 実施例 1〜3では、真空成形最大絞り比が 0. 8以上であり、防音材は何れも優れた 成形性を有していた。比較例 1は、真空成形最大絞り比が 0. 6であり、この程度の成 形性では防音材を金型形状に沿った形状に正確に成形することはできな!、。比較例 3の防音材は、成形性に劣り底面部に直ちに孔が生じて殆ど真空成形することがで きな力つた。比較例 4の防音材は、成形性に劣り底面部に直ちに孔が生じて全く真空 成形できなかった。
[0046] (防音性）
防音材の遮音性を JIS A1416に基づいて測定し、防音性の指標とした。具体的 には、音源室と残響室との仕切扉に開設された一辺が 600mmの正方形状の防音 材取付用の開口部に防音材を取り付けて開口部を全面的に閉止した。しかる後、音 源室の音源から 90dBの音を発生させ、残響室にて音の大きさ Aを騒音計 (RION社 製 商品名「精密騒音計 NA— 27」 )を用いて測定した。
[0047] 次に、防音材取付用の開口部に防音材を取り付けることなぐ開口部を全面的に開 放した状態にて、上述と同様の要領で音の大きさ Bを測定し、下記式 3に基づいて遮 音性を算出した。
遮音性 (dB) = (音の大きさ B)—（音の大きさ A) · · ·式 3
[0048] [表 1]
Figure imgf000012_0001
産業上の利用可能性
本発明の防音材は、優れた防音性及び成形性を有していることから、種々の形状 を有する被防音部材に適用することができ、自動車用途、鉄道用途、建築用途など の広範囲な用途に適用することができる。

Claims

請求の範囲
[1] 熱可塑性榭脂発泡体と、この熱可塑性榭脂発泡体を構成している熱可塑性榭脂 10
0重量部に対して 30〜300重量部の割合で熱可塑性榭脂発泡体中に含有されて 、 る無機化合物とからなることを特徴とする防音材。
[2] 熱可塑性榭脂発泡体を構成している熱可塑性榭脂がポリオレフイン系榭脂であるこ とを特徴とする請求項 1に記載の防音材。
[3] 無機化合物が、無機酸の金属塩であることを特徴とする請求項 1に記載の防音材。
[4] 見掛け密度が 0. 1〜0. 8gZcm3であることを特徴とする請求項 1に記載の防音材。
[5] 無機化合物が、熱可塑性榭脂発泡体を構成している熱可塑性榭脂 100重量部に対 して 75〜250重量部含有されて 、ることを特徴とする請求項 1に記載の防音材。
[6] 無機化合物が硫酸バリウムであることを特徴とする請求項 1に記載の防音材。
[7] 熱可塑性榭脂発泡体を構成している熱可塑性榭脂の樹脂倍率が 300%以上である ことを特徴とする請求項 1に記載の防音材。
PCT/JP2006/317566 2005-09-08 2006-09-05 防音材 WO2007034672A1 (ja)