Classifications

• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
  • C08J9/0014—Use of organic additives
  • C08J9/0023—Use of organic additives containing oxygen
• • C—CHEMISTRY; METALLURGY
  • C07—ORGANIC CHEMISTRY
  • C07D—HETEROCYCLIC COMPOUNDS
  • C07D307/00—Heterocyclic compounds containing five-membered rings having one oxygen atom as the only ring hetero atom
  • C07D307/77—Heterocyclic compounds containing five-membered rings having one oxygen atom as the only ring hetero atom ortho- or peri-condensed with carbocyclic rings or ring systems
  • C07D307/78—Benzo [b] furans; Hydrogenated benzo [b] furans
  • C07D307/82—Benzo [b] furans; Hydrogenated benzo [b] furans with hetero atoms or with carbon atoms having three bonds to hetero atoms with at the most one bond to halogen, e.g. ester or nitrile radicals, directly attached to carbon atoms of the hetero ring
  • C07D307/83—Oxygen atoms
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
  • C08K5/00—Use of organic ingredients
  • C08K5/04—Oxygen-containing compounds
  • C08K5/15—Heterocyclic compounds having oxygen in the ring
  • C08K5/151—Heterocyclic compounds having oxygen in the ring having one oxygen atom in the ring
  • C08K5/1535—Five-membered rings
• • C—CHEMISTRY; METALLURGY
  • C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
  • C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
  • C08J2375/00—Characterised by the use of polyureas or polyurethanes; Derivatives of such polymers
  • C08J2375/04—Polyurethanes

Definitions

• the present invention relates to compositions comprising an organic material, such as a polymer, and an oligomeric lactone for use as a stabilizers.
• the inventive compositions may be employed for stabilization of organic materials against oxidative, thermal, or light-induced degradation.
• the invention is directed to novel oligomeric lactones.
• compositions that function to stabilize organic materials against oxidative, thermal or light-induced degradation.
• Such stabilization compositions may have broad applications in thermoplastics such as polyolefin, thermoset resins such as polyurethanes, and coating formulations.
• thermoplastics such as polyolefin
• thermoset resins such as polyurethanes
• coating formulations One problem with polyurethane foams, for example, is that such foams tend to yellow after a certain period of time. Yellowing of foam products is undesirable. Such yellowing may be caused by NOx gas fading or UV radiation.
• the compositions may comprise polymeric or oligomeric lactone antioxidants, such as poly(oxyalkylene) chain(s) substituted 3-arylbenzofuranones or poly(caprolactone) chain(s) substituted 3-arylbenzofuranones.
• the inventive lactone antioxidants may be polymeric or oligomeric, which may be liquid or pastes in nature at room temperature. In many applications, liquid or paste forms of such compounds provide a remarkable and surprising advantage.
• the compositions may bear one or more reactive primary -OH groups on the polymer chains.
• the terminal group(s) of the polymer chain(s) is not believed to be critical with regard to the functioning of the polymeric lactones in stabilizer compositions.
• the chain(s) may also contain oxyalkylene ether and aliphatic ester functional groups or radicals.
• the inventive liquid lacones polymeric/oligomeric chains may contain oxyalkylene segments (such as ethylene oxide and/or propylene oxide, etc, and the EO/PO ratio can be designed as such to achieve desired hydrophilic and/or hydrophobic properties) and/or aliphatic ester segments (hydrophobic).
• oxyalkylene segments such as ethylene oxide and/or propylene oxide, etc
• aliphatic ester segments hydrophobic
• Lactones bearing unique polymeric/oligomeric chains may also be comprised of specific combination of EO/PO/aliphatic esters that are compatible with most of the above-mentioned applications.
• the liquid nature of the inventive polymeric lactones provides ease of handling during the application process. That is, the compositions may desirably be liquids or pastes at room temperature, making it much easier to apply the compositions in manufacturing processes.
• the polymeric/oligomeric nature of the inventive lactones provides higher molecular weight and better compatibility with application media, thus is less volatile, and less prone to migrate, bloom and plate-out.
• inventive lactone molecules are present on the inventive lactone molecules. These structures offer superior reactivity in polyurethane, PET and coating systems. Thus the polymeric lactone molecules may be chemically attached on to the application media if such is desirable.
• inventive polymeric UV absorbers may solve or mitigate migration, leaching, fogging, plate-out, and extraction problems, each of which is highly undesirable.
• inventive polymeric lactone antioxidants 3- arylbenzofuranones when used along with other additives such as UV absorbers, other antioxidants, and light stabilizers, may significantly reduce the gas fading (NOx) and UV radiation induced yellowing of white polyurethane foam.
• the compositions may be provided in liquid form, and are reactive into the foam, which is a significant advantage. That is, these compositions are truly polymeric or oligomeric, having in some applications polyoxyalkylene and aliphatic polyester block copolymer/oligomer chains.
• the inventive lactone stabilizers may be liquid and polymeric. They may provide ease of handling, processing and metering.
• the inventive lactone stabilizers may bear primary -OH groups at the end of polymer chains. They may be completely reactive in polyurethane, coatings, PET, and polycarbonate applications if such is desirable. They may provide antioxidant functions to resist undesirable extraction, migration, fogging, and leaching out of the polymer matrix.
• the compounds of the invention may be described as follows:
• A comprises a C 2 -C 2O alkyl group or a divalent oligomeric oxyalkylene radical
• Z comprises a C 2 - C 20 alkyl or a divalent oligomeric ester radical
• G is an end group and is selected from the group consisting of: H, C 1 -C 10 alkyls, alkyl carbonyls and aryl carbonyls.
• R 9 comprises a divalent C-i - C20 alkyl radical; x, y and w are independently selected from the group consisting of: zero and positive integers or fractions between 1 and 20; wherein x+y+w is equal or greater than 1 ; and wherein
• R 10 comprises H or a Ci - C20 alkyl group.
• the Z group may be comprised of a divalent oligomeric ester radical, having the structure:
• R 11 and R 12 are independently selected from H or Ci - C 10 alkyl groups; n comprises an integer between 1 and 10; and m comprises any positive integer or fraction between 1 and 20.
• R1 , R3, R5 - R8, A, Z and G are as defined above.
• Ri, and R 3 are as defined above, and q is a positive integer between 1 and 20, and t is a positive integer between 0 and 20, and wherein q+t is equal to or greater than 3.
• inventive compounds can be used with the following classes of additives:
• Class A Benzotriazoles are (in general) those compounds that conform to the structure represented as the following:
• R 13 , Ri 4 , and R 15 are independently selected from hydrogen, a group having a formula C a H b N c OdS e wherein a, b, c, d, and e are from 0 to 30, and halogen.
• Class B Hindered phenols or BHT derivatives, and related compounds typically conform to the structure of the following:
• Ri 6 is selected from the group consisting of hydrogen, a group having a formula C a H b NcOdSe wherein a, b, c, d, and e may be from 0 to 30, and halogen.
• Class C Secondary diphenylamines may conform to the structure of the following
• Ri 7 and Ria are individually selected from the group consisting of hydrogen, a group having a formula C a H b N c O d S e wherein a, b, c, d, and e are from 0 to 30, and halogen.
• Class D other conventional Lactone-based antioxidants may include those compounds that conform to the structure of the following:
• R 19 to R 27 are individually selected from the group consisting of hydrogen, a group having a formula CaH b N c OdS e wherein a, b, c, d, and e are from 0 to 30, and halogen.
• the foams produced exhibited good resiliency and densities measured at about 1.5 pounds per cubit foot.
• the inventive polymeric lactone antioxidants provide acceptable polyurethane foam articles as compared with control samples.
• the polyurethane foams produced in above Section b) were analyzed for extraction levels using the following method.
• the extraction test involved cutting 1 gram of the cured foam from the center of the sample and post- curing the cut foam for another 20 minutes at 160 0 C in a glass jar. After cooling to room temperature, 75 grams of methanol were then added to the glass jar that was then capped for 1 hour. The foam was then removed and the extract solution was analyzed to detect the percentages of the lactone antioxidants being extracted out. The results are summarized in Table 2.
• Liquid polymeric colorant Reactint® Blue X3LV (available from Milliken Chemical) is widely used for the coloration of polyurethane foam, and is known to be prone to thermal discoloration during foam article formulation.
• the blue foams were made in the presence of 1 php Blue X3LV with or without inventive and comparative lactone antioxidants, in accordance with formulation and process similar to those as described Section a), with the exception that after the reaction created a "health" bubble (indicating gelation and blowing balance), the vessel was then exposed to 185 0 C (generated within a microwave oven to simulate actual heat history encountered on a large industrial production environment) for about 10 min before it was exposed to 160 0 C (generated by a conventional oven) for 3 minutes to cure the foam bun.
• Polyols are known to be very prone to oxidation. In order to retain the physical and chemical properties, almost all commercial polyols are protected with conventional hindered phenol antioxidants for storage and transportation.
• One major side effect of the hindered phenols is that they cause discoloration/yellowing during polyurethane article formation and when exposed to exhaust gas (NOx).
• An antioxidant which can effectively protect the intergraty of polyols without causing polymers such as polyurethane foam yellowing and compatible with polyols is highly desired.
• the white foams (without adding any colorant) were made using pure polyol (no conventional antioxidant package presence) with or without inventive and comparative lactone antioxidants, in accordance with formulation and process similar to those as described Section a), with the exception that after the reaction created a "health" bubble (indicating gelation and blowing balance), the vessel was then exposed to 185 0 C (generated within a microwave oven to simulate actual heat history encountered on a large industrial production environment) for about 10 min before it was exposed to 160 0 C (generated by a conventional oven) for 3 minutes to cure the foam bun.
• inventive polymeric liquid lactone antioxidants are very effective in stabilizing pure polyols from thermal degradation.
• the white foams (without adding any colorant) were made using pure polyol (no conventional antioxidant package presence), as well as regular polyols (with the conventional stabilizer package presences) with or without inventive and comparative lactone antioxidants, in accordance with formulation and process similar to those as described in Section a).
• the foam buns were sliced in half, and small pieces of foam samples (diameters of 10cm x 5cm x 2cm) were cut from the center of each foam bun.
• inventive additive packages containing the inventive liquid polymeric lactone antioxidants exhibited among the best overall performance against discoloration of UV exposure and gas fade, comparing to state-of-the-art commercial additive packages such as GG, HH and JJ.

Landscapes

• Chemical & Material Sciences (AREA)
• Organic Chemistry (AREA)
• Health & Medical Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Medicinal Chemistry (AREA)
• Polymers & Plastics (AREA)
• Emergency Medicine (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Compositions Of Macromolecular Compounds (AREA)
• Anti-Oxidant Or Stabilizer Compositions (AREA)
• Furan Compounds (AREA)
• Cosmetics (AREA)
• Polyurethanes Or Polyureas (AREA)

Priority Applications (5)

Applications Claiming Priority (2)

Publications (1)

Family

ID=36061423

Family Applications (1)

Country Status (8)

Cited By (3)

Families Citing this family (11)

Citations (3)

Family Cites Families (12)

• 2004
  • 2004-12-17 US US11/016,171 patent/US7390912B2/en active Active
• 2005
  • 2005-12-12 WO PCT/US2005/045100 patent/WO2006065829A1/en not_active Ceased
  • 2005-12-12 BR BRPI0519524A patent/BRPI0519524B1/pt active IP Right Grant
  • 2005-12-12 AT AT05853912T patent/ATE423811T1/de not_active IP Right Cessation
  • 2005-12-12 EP EP05853912A patent/EP1824921B1/en not_active Expired - Lifetime
  • 2005-12-12 CN CN2005800435229A patent/CN101080451B/zh not_active Expired - Lifetime
  • 2005-12-12 JP JP2007546833A patent/JP5010480B2/ja not_active Expired - Lifetime
  • 2005-12-12 DE DE602005012985T patent/DE602005012985D1/de not_active Expired - Lifetime
• 2008
  • 2008-05-19 US US12/122,961 patent/US7601853B2/en not_active Expired - Lifetime
• 2009
  • 2009-09-18 US US12/562,456 patent/US8653284B2/en active Active

Patent Citations (3)

Also Published As

Similar Documents

Legal Events