WO2006051188A2 - Bande d’alliage fer-nickel pour la fabrication de grilles support de circuits integres - Google Patents
Bande d’alliage fer-nickel pour la fabrication de grilles support de circuits integres Download PDFInfo
- Publication number
- WO2006051188A2 WO2006051188A2 PCT/FR2005/002741 FR2005002741W WO2006051188A2 WO 2006051188 A2 WO2006051188 A2 WO 2006051188A2 FR 2005002741 W FR2005002741 W FR 2005002741W WO 2006051188 A2 WO2006051188 A2 WO 2006051188A2
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- strip
- iron
- heat treatment
- nickel alloy
- recrystallized
- Prior art date
Abstract
Description
Claims