WO2005116337A1 - Procede de fabrication de papier decoratif et stratifie decoratif comportant un tel papier decoratif - Google Patents
Procede de fabrication de papier decoratif et stratifie decoratif comportant un tel papier decoratif Download PDFInfo
- Publication number
- WO2005116337A1 WO2005116337A1 PCT/FR2005/001203 FR2005001203W WO2005116337A1 WO 2005116337 A1 WO2005116337 A1 WO 2005116337A1 FR 2005001203 W FR2005001203 W FR 2005001203W WO 2005116337 A1 WO2005116337 A1 WO 2005116337A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- paper
- decorative
- resin
- ink
- sheet
- Prior art date
Abstract
Description
Claims