WO2005089943A1 - Procédure de production d’un catalyseur à oxydes composite - Google Patents

Procédure de production d’un catalyseur à oxydes composite Download PDF

Info

Publication number
WO2005089943A1
WO2005089943A1 PCT/JP2004/014379 JP2004014379W WO2005089943A1 WO 2005089943 A1 WO2005089943 A1 WO 2005089943A1 JP 2004014379 W JP2004014379 W JP 2004014379W WO 2005089943 A1 WO2005089943 A1 WO 2005089943A1
Authority
WO
WIPO (PCT)
Prior art keywords
composite oxide
oxide catalyst
acid
producing
catalyst
Prior art date
Application number
PCT/JP2004/014379
Other languages
English (en)
Japanese (ja)
Inventor
Yoshimune Abe
Isao Teshigahara
Original Assignee
Mitsubishi Chemical Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Mitsubishi Chemical Corporation filed Critical Mitsubishi Chemical Corporation
Publication of WO2005089943A1 publication Critical patent/WO2005089943A1/fr

Abstract

Procédure de production d’un catalyseur à oxydes composite avec lequel un aldéhyde insaturé est oxydé par catalyse dans une phase vapeur avec un carburant contenant de l’oxygène moléculaire, pour produire de manière stable l'acide carboxylique insaturé correspondant à haute dose et sur le long terme. La procédure, qui consiste à produire le catalyseur à oxydes composite représenté par la formule Mo12VaXbCucYdCeSifOg (où X représente au moins un élément sélectionné entre le niobium et le tungstène ; Y représente au moins un élément sélectionné dans le groupe comprenant l’antimoine, le magnésium, le calcium, le strontium, le baryum, et le zinc ; et où a, b, c, d, e, f, et g, indiquent les proportions atomiques des éléments respectifs qui sont les suivantes : 0<a≤12, 0≤b≤12, 0<c≤12, 0≤d≤8, 0≤e≤1,000, et 0≤f≤1,000 quand le nombre d’atomes de molybdène est de 12, et g est le nombre d’atomes d’oxygène satisfaisant les états oxydés des éléments de constitution hors silicone et carbone dans la formule), comprend l’unification des éléments source dans un milieu aqueux en présence d’un acide organique, l’assèchement de la solution aqueuse résultante ou la dispersion de la matière unifiée pour préparer une poudre, le moulage de la poudre, et l’incinération de la poudre.
PCT/JP2004/014379 2004-03-23 2004-09-30 Procédure de production d’un catalyseur à oxydes composite WO2005089943A1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2004085297 2004-03-23
JP2004-085297 2004-03-23

Publications (1)

Publication Number Publication Date
WO2005089943A1 true WO2005089943A1 (fr) 2005-09-29

Family

ID=34993493

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2004/014379 WO2005089943A1 (fr) 2004-03-23 2004-09-30 Procédure de production d’un catalyseur à oxydes composite

Country Status (2)

Country Link
CN (1) CN100430141C (fr)
WO (1) WO2005089943A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1997554A1 (fr) * 2006-03-20 2008-12-03 Asahi Kasei Chemicals Corporation Catalyseur d'oxydation ou d'ammoxydation et procédé de synthèse dudit catalyseur

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR102418676B1 (ko) * 2017-03-31 2022-07-07 미쯔비시 케미컬 주식회사 불포화 카복실산 제조용 촉매, 불포화 카복실산의 제조 방법, 및 불포화 카복실산 에스터의 제조 방법
JP2021122819A (ja) * 2020-01-31 2021-08-30 三菱ケミカル株式会社 触媒の製造方法及びアクリル酸の製造方法

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS49169B1 (fr) * 1970-12-28 1974-01-05
JPS5025914B1 (fr) * 1970-12-28 1975-08-27
US3959182A (en) * 1969-08-19 1976-05-25 Rohm And Haas Company Catalyst compositions and process for producing acrylic acid or methacrylic acid utilizing such catalyst
JPS5295609A (en) * 1976-02-09 1977-08-11 Toyo Soda Mfg Co Ltd Preparation of methacrylic acid
JP2000317309A (ja) * 1999-05-17 2000-11-21 Toagosei Co Ltd アクリル酸製造用触媒の製造方法
JP2003200055A (ja) * 2002-01-09 2003-07-15 Mitsubishi Chemicals Corp 複合酸化物触媒の製造方法

Family Cites Families (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
DE69518547T2 (de) * 1994-11-14 2001-01-11 Nippon Catalytic Chem Ind Verfahren zur Herstellung von Acrylsäure
DE10046928A1 (de) * 2000-09-21 2002-04-11 Basf Ag Verfahren zur Herstellung von Multimetalloxidmassen

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3959182A (en) * 1969-08-19 1976-05-25 Rohm And Haas Company Catalyst compositions and process for producing acrylic acid or methacrylic acid utilizing such catalyst
JPS49169B1 (fr) * 1970-12-28 1974-01-05
JPS5025914B1 (fr) * 1970-12-28 1975-08-27
JPS5295609A (en) * 1976-02-09 1977-08-11 Toyo Soda Mfg Co Ltd Preparation of methacrylic acid
JP2000317309A (ja) * 1999-05-17 2000-11-21 Toagosei Co Ltd アクリル酸製造用触媒の製造方法
JP2003200055A (ja) * 2002-01-09 2003-07-15 Mitsubishi Chemicals Corp 複合酸化物触媒の製造方法

Cited By (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP1997554A1 (fr) * 2006-03-20 2008-12-03 Asahi Kasei Chemicals Corporation Catalyseur d'oxydation ou d'ammoxydation et procédé de synthèse dudit catalyseur
EP1997554A4 (fr) * 2006-03-20 2011-02-23 Asahi Kasei Chemicals Corp Catalyseur d'oxydation ou d'ammoxydation et procédé de synthèse dudit catalyseur
US7919430B2 (en) 2006-03-20 2011-04-05 Asahi Kasei Chemicals Corporation Catalyst for oxidation or ammoxidation, and process for producing the same
EP2913104A1 (fr) * 2006-03-20 2015-09-02 Asahi Kasei Chemicals Corporation Catalyseur d'ammoxydation ou d'oxydation et son procédé de production

Also Published As

Publication number Publication date
CN1697702A (zh) 2005-11-16
CN100430141C (zh) 2008-11-05

Similar Documents

Publication Publication Date Title
JP3892244B2 (ja) 不飽和アルデヒドおよび不飽和カルボン酸製造用触媒の製造方法
US7414008B2 (en) Catalyst for synthesis of unsaturated aldehyde, production process for said catalyst, and production process for unsaturated aldehyde using said catalyst
TWI267402B (en) Catalyst for partial oxidation and preparation method thereof
KR100986898B1 (ko) 복합 금속 산화물 촉매 및 상기 촉매를 사용한(메타)아크릴산 제조 방법
JP2000325795A (ja) 複合酸化物触媒、並びに（メタ）アクロレインおよび（メタ）アクリル酸の製造方法
JP2001162173A (ja) 複合酸化物触媒およびアクリル酸の製造方法
KR20170125827A (ko) 불포화 알데히드 및/또는 불포화 카본산 제조용 촉매 및 그의 제조 방법 그리고 불포화 알데히드 및/또는 불포화 카본산의 제조 방법
JP2007520328A (ja) プロピレン気相部分酸化反応用触媒及びその製造方法
CS200497B2 (en) Catalyst for making the acrylic acid or methacrylic acid
JP4442317B2 (ja) 複合酸化物触媒の製造方法
JP2005305421A (ja) 複合酸化物触媒の製造方法
JP4863436B2 (ja) 不飽和アルデヒドおよび不飽和カルボン酸合成用触媒
JP4858266B2 (ja) 複合酸化物触媒の製造法
JP2008284416A (ja) 金属酸化物触媒の製造方法
JP2006007205A (ja) 複合酸化物触媒及びその製造方法
JP2005169311A (ja) 複合酸化物触媒の製造方法
WO2005089943A1 (fr) Procédure de production d’un catalyseur à oxydes composite
JP4285084B2 (ja) メタクリル酸製造用触媒の製造方法およびメタクリル酸の製造方法
JP6136436B2 (ja) 触媒の製造方法
JPH10258233A (ja) 不飽和アルデヒドおよび不飽和カルボン酸合成用触媒の製造法
WO2005113139A1 (fr) Catalyseur d&#39;oxyde composite et procédé de production de celui-ci
JP2005205263A (ja) 複合酸化物触媒の製造方法。
JP4273565B2 (ja) 不飽和アルデヒド及び不飽和カルボン酸合成用の複合酸化物触媒の製造法
JPH0597761A (ja) メタクロレイン製造方法及びメタクロレインの製造に用いる触媒の製造方法
JP2005186064A (ja) 不飽和アルデヒド及び不飽和カルボン酸の製造用触媒の製造方法

Legal Events

Date Code Title Description
WWE Wipo information: entry into national phase

Ref document number: 2004800370X

Country of ref document: CN

AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): BW GH GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
NENP Non-entry into the national phase

Ref country code: DE

WWW Wipo information: withdrawn in national office

Country of ref document: DE

122 Ep: pct application non-entry in european phase