WO2005068181A1 - Photocatalytic particles in floor laminates - Google Patents

Photocatalytic particles in floor laminates Download PDF

Info

Publication number
WO2005068181A1
WO2005068181A1 PCT/EP2005/000354 EP2005000354W WO2005068181A1 WO 2005068181 A1 WO2005068181 A1 WO 2005068181A1 EP 2005000354 W EP2005000354 W EP 2005000354W WO 2005068181 A1 WO2005068181 A1 WO 2005068181A1
Authority
WO
WIPO (PCT)
Prior art keywords
resins
photocatalyst
particles
formaldehyde
finishing composition
Prior art date
Application number
PCT/EP2005/000354
Other languages
English (en)
French (fr)
Inventor
Jan De Clerck
Original Assignee
Domo Oudenaarde Nv
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Domo Oudenaarde Nv filed Critical Domo Oudenaarde Nv
Priority to EP05706894A priority Critical patent/EP1715995A1/de
Publication of WO2005068181A1 publication Critical patent/WO2005068181A1/en

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/18—Layered products comprising a layer of synthetic resin characterised by the use of special additives
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B27/00—Layered products comprising a layer of synthetic resin
    • B32B27/12—Layered products comprising a layer of synthetic resin next to a fibrous or filamentary layer
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M11/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising
    • D06M11/32—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with oxygen, ozone, ozonides, oxides, hydroxides or percompounds; Salts derived from anions with an amphoteric element-oxygen bond
    • D06M11/36—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with oxygen, ozone, ozonides, oxides, hydroxides or percompounds; Salts derived from anions with an amphoteric element-oxygen bond with oxides, hydroxides or mixed oxides; with salts derived from anions with an amphoteric element-oxygen bond
    • D06M11/44—Oxides or hydroxides of elements of Groups 2 or 12 of the Periodic Table; Zincates; Cadmates
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M11/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising
    • D06M11/32—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with oxygen, ozone, ozonides, oxides, hydroxides or percompounds; Salts derived from anions with an amphoteric element-oxygen bond
    • D06M11/36—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with oxygen, ozone, ozonides, oxides, hydroxides or percompounds; Salts derived from anions with an amphoteric element-oxygen bond with oxides, hydroxides or mixed oxides; with salts derived from anions with an amphoteric element-oxygen bond
    • D06M11/46—Oxides or hydroxides of elements of Groups 4 or 14 of the Periodic Table; Titanates; Zirconates; Stannates; Plumbates
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M11/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising
    • D06M11/32—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with oxygen, ozone, ozonides, oxides, hydroxides or percompounds; Salts derived from anions with an amphoteric element-oxygen bond
    • D06M11/36—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with oxygen, ozone, ozonides, oxides, hydroxides or percompounds; Salts derived from anions with an amphoteric element-oxygen bond with oxides, hydroxides or mixed oxides; with salts derived from anions with an amphoteric element-oxygen bond
    • D06M11/48—Oxides or hydroxides of chromium, molybdenum or tungsten; Chromates; Dichromates; Molybdates; Tungstates
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M11/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising
    • D06M11/32—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with oxygen, ozone, ozonides, oxides, hydroxides or percompounds; Salts derived from anions with an amphoteric element-oxygen bond
    • D06M11/36—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with oxygen, ozone, ozonides, oxides, hydroxides or percompounds; Salts derived from anions with an amphoteric element-oxygen bond with oxides, hydroxides or mixed oxides; with salts derived from anions with an amphoteric element-oxygen bond
    • D06M11/49—Oxides or hydroxides of elements of Groups 8, 9,10 or 18 of the Periodic Table; Ferrates; Cobaltates; Nickelates; Ruthenates; Osmates; Rhodates; Iridates; Palladates; Platinates
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M11/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising
    • D06M11/51—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with sulfur, selenium, tellurium, polonium or compounds thereof
    • D06M11/52—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with sulfur, selenium, tellurium, polonium or compounds thereof with selenium, tellurium, polonium or their compounds; with sulfur, dithionites or compounds containing sulfur and halogens, with or without oxygen; by sulfohalogenation with chlorosulfonic acid; by sulfohalogenation with a mixture of sulfur dioxide and free halogens
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M11/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising
    • D06M11/51—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with sulfur, selenium, tellurium, polonium or compounds thereof
    • D06M11/53—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with sulfur, selenium, tellurium, polonium or compounds thereof with hydrogen sulfide or its salts; with polysulfides
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M11/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising
    • D06M11/77—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with silicon or compounds thereof
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M11/00—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising
    • D06M11/77—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with silicon or compounds thereof
    • D06M11/79—Treating fibres, threads, yarns, fabrics or fibrous goods made from such materials, with inorganic substances or complexes thereof; Such treatment combined with mechanical treatment, e.g. mercerising with silicon or compounds thereof with silicon dioxide, silicic acids or their salts
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06M—TREATMENT, NOT PROVIDED FOR ELSEWHERE IN CLASS D06, OF FIBRES, THREADS, YARNS, FABRICS, FEATHERS OR FIBROUS GOODS MADE FROM SUCH MATERIALS
    • D06M23/00—Treatment of fibres, threads, yarns, fabrics or fibrous goods made from such materials, characterised by the process
    • D06M23/08—Processes in which the treating agent is applied in powder or granular form
    • D—TEXTILES; PAPER
    • D06—TREATMENT OF TEXTILES OR THE LIKE; LAUNDERING; FLEXIBLE MATERIALS NOT OTHERWISE PROVIDED FOR
    • D06N—WALL, FLOOR, OR LIKE COVERING MATERIALS, e.g. LINOLEUM, OILCLOTH, ARTIFICIAL LEATHER, ROOFING FELT, CONSISTING OF A FIBROUS WEB COATED WITH A LAYER OF MACROMOLECULAR MATERIAL; FLEXIBLE SHEET MATERIAL NOT OTHERWISE PROVIDED FOR
    • D06N7/00—Flexible sheet materials not otherwise provided for, e.g. textile threads, filaments, yarns or tow, glued on macromolecular material
    • D06N7/0005—Floor covering on textile basis comprising a fibrous substrate being coated with at least one layer of a polymer on the top surface
    • D06N7/0039—Floor covering on textile basis comprising a fibrous substrate being coated with at least one layer of a polymer on the top surface characterised by the physical or chemical aspects of the layers
    • D06N7/0052—Compounding ingredients, e.g. rigid elements
    • D06N7/0055—Particulate material such as cork, rubber particles, reclaimed resin particles, magnetic particles, metal particles, glass beads
    • E—FIXED CONSTRUCTIONS
    • E04—BUILDING
    • E04F—FINISHING WORK ON BUILDINGS, e.g. STAIRS, FLOORS
    • E04F15/00—Flooring
    • E04F15/02—Flooring or floor layers composed of a number of similar elements
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01D—SEPARATION
    • B01D2259/00—Type of treatment
    • B01D2259/45—Gas separation or purification devices adapted for specific applications
    • B01D2259/4591—Construction elements containing cleaning material, e.g. catalysts
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B01—PHYSICAL OR CHEMICAL PROCESSES OR APPARATUS IN GENERAL
    • B01J—CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
    • B01J35/00—Catalysts, in general, characterised by their form or physical properties
    • B01J35/30—Catalysts, in general, characterised by their form or physical properties characterised by their physical properties
    • B01J35/39—Photocatalytic properties
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2262/00—Composition or structural features of fibres which form a fibrous or filamentary layer or are present as additives
    • B32B2262/06—Vegetal fibres
    • B32B2262/062—Cellulose fibres, e.g. cotton
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B2471/00—Floor coverings
    • B32B2471/02—Carpets

Definitions

  • the present invention relates to improved floor covering.
  • the present invention relates to floor covering formed of laminated panels.
  • the present invention relates to carpet floor covering.
  • floor covering such as floor laminates or carpets comprising photocatalytic particles having many functions of antimicrobial, preventing smell or stainproof, or decomposition of harmful substances (NOx, and the like) based on the photocatalytic function.
  • carpets and laminates have been the floor coverings of choice for improving both the aesthetics and comfort in residential homes and commercial buildings.
  • Decorative laminates and carpet are well known and used for instance as covering material on walls, cupboard doors and desks, on tables and other furniture and as flooring material.
  • the laminates are often made of a base of particle board or fiber board provided with a monochromatic or patterned decor sheet impregnated with melamine-formaldehyde resin and a fine so-called overlay sheet of a-cellulose impregnated with melamine- formaldehyde resin. These sheets can be laminated to the base under heat and pressure.
  • the overlay sheet is intended to protect the decor sheet from abrasion. In certain cases the overlay sheet is omitted.
  • the decorative layer can be protected by either an overlay of paper saturated with melamine resins and a certain content of AIO 2 to make the product abrasive resistant, or by saturation of the decorative printed paper with a suspension of melamine urea formaldehyde resins and a certain amount of aluminum oxide.
  • Another method to treat and protect the decorative layer is the application of lacquers and hardening with electron beam curing.
  • floor coverings are susceptible to staining by foods and beverages and also discoloration due to soil pick-up caused by foot traffic.
  • floor coverings are usually strongly glued by synthetic adhesives. Synthetic adhesive having fungus resistance performance are often used.
  • Air pollution is an issue that has been discussed for many years. Pollutants in the air have been proved to affect human comfort and health. Relatively recently, it has been found that the quality of the air inside a home or business is frequently worse than the quality of the air outside that very same home or business.
  • VOC volatile organic compounds
  • surface treatments are often used in order to protect the floor coverings and/or to polish them.
  • synthetic resin for example, acryl resin emulsified polishing agent and a product filled in a synthetic resin bottle with a nozzle for spray is generally used.
  • polishing agents often contain solvents harmful for human body.
  • living spaces of residences and offices may carry airborne malodorous substances including sulfur compounds such as hydrogen sulfide and methyl mercaptan, nitrogen compounds such as ammonia, and other compounds such as fatty acid. To provide a comfort of living environment, it is desirable to treat the contaminated air for removal of the malodorous substances.
  • the present invention provides laminates comprising a decorative upper layer, optionally a protective overlay and optionally a base layer, wherein said decorative upper layer comprises a web of fibers having deposited therein and/or thereon photocatalyst particles embedded in a binder.
  • the present invention also provides laminates comprising a decorative upper layer, a protective overlay and optionally a base layer, wherein said protective overlay comprises a web of fibers having deposited therein and/or thereon photocatalyst particles embedded in a binder.
  • the present invention encompasses decorative layers for laminate comprising a web of fibers having deposited therein and/or thereon photocatalyst particles embedded in a binder.
  • the present invention also encompasses protective overlays, wherein said protective overlay comprises a web of fibers having deposited therein and/or thereon photocatalyst particles embedded in a binder.
  • the present invention also provides a process for the production of a decorative layer or a protective overlay according to the present invention, comprising the step of providing a fiber web layer, treating said fiber web layer with a photocatalyst composition comprising photocatalyst particles, a binder and a solvent, and hardening said treated fiber web to obtain a decorative layer or a protective overlay comprising a web of fibers having deposited therein and/or thereon photocatalyst particles embedded in a binder.
  • the present invention provides the advantage that the laminates, the decorative layer and the overlay according to the present invention are excellent in the points that they show a deodorant function, an antimicrobial function or an antistain function due to photocatalyst particles comprised in said laminates.
  • the laminates of the present invention have the advantages of being anti staining, selfcleaning, antimicrobial and desodorizing.
  • the photocatalyst particles comprised in said laminates will actively decompose toxic and non-biodegradable pollutants. Said photocatalysts will also mineralize any organic pollutants into CO 2 , H 2 O and inorganic compounds. These reactions can be activated by the sunlight, and when said photocatalysts are tuned by visible light.
  • the present invention further provides carpet having air clarifying properties which has undergone a post-treatment with a finishing composition comprising the photocatalyst composition described above, optionally in combination with stain blockers such as grease and water stain fluoride-based repellent.
  • the present invention also provides a finishing composition
  • a finishing composition comprising (a) a photocatalyst composition as defined herein, (b) a liquid carrier and (c) optionally a coacervate, wherein said photocatalyst composition comprises (i) photocatalyst particles, (ii) a binder and (iii) a solvent.
  • said photocatalyst particles are selected from the group comprising TiO 2 , ZnO, SiO 3 ; Ti ⁇ -x Sn x O 2 , SrTiO 3 , Fe 2 O 3 , CdS, CdSe, WO 3 , FeTiO 3 , GaP, GaAs, GeAs, RuO 2 , MoS 3 , LaRhO 3 , CdFeO 3 , Bi 2 O 3 , MoS 2l ln 2 O 3 , CdO, SnO 2 , SiC, InP and/or mixture thereof.
  • said photocatalyst particle is anatase TiO 2 .
  • the present invention also encompasses the use of a finishing composition according to the invention, for the treatment of carpets.
  • the present invention further encompasses a Method for the preparation of a carpet having air clarifying properties comprising the steps of: providing a finishing composition according to the invention, and applying said finishing composition onto a carpet thereby obtaining a carpet having air clarifying properties.
  • the present invention also encompasses carpet having air clarifying properties obtained by a method according to the invention.
  • the object of the present invention is to provide a photocatalytic process for treating an indoor environment contaminated by bacteria and airborne particulate or volatile substances which may be carried out without resort to a light source which is harmful to human being.
  • the laminates, overlay, decorative layers or carpets having air clarifying properties according to the invention do not necessitate the use of a special light source for excitation of the photocatalyst particles. They permit to photocatalytically treat an indoor environment or air. When bacteria and/or airborne substances are brought in contact with the photocatalyst particles comprised in said laminates, they are photodecomposed in situ.
  • FIG 1 illustrates the experimental arrangement for the assessment of degradation of volatile organic compound (VOC) by the floor covering according to the invention.
  • Figure 2 illustrates the results of an experiment measuring the catalytic activity of TiO2 coated carpet by the analysis of the effect of the coated carpets on formaldehyde degradation under continuous aeration.
  • Figure 3 illustrates the results of an experiment measuring the catalytic activity of TiO2 coated carpet by the analysis of the effect of the coated carpets on benzene degradation under continuous aeration.
  • Figure 4 illustrates the results of olfactory evaluation of the tobacco odor deodorant property of the carpets according to the invention.
  • Figure 5 illustrates the results of olfactory evaluation of the tobacco odor deodorant property of the carpets according to the invention.
  • Figure 6 illustrates determination of the catalytic degradation of total volatile organic compound (TVOC) by the carpets according to the invention under continuous aeration.
  • TVOC total volatile organic compound
  • Figure 7 illustrates the results of an experiment measuring the effect of the duration of U V light illumination on the catalytic formaldehyde degradation property of the carpets according to the invention under continuous aeration.
  • Figure 8 illustrates the results of an experiment determining the air cleaning durability of a carpet according to the invention under conditions intended to simulate a 5 year cycle of maintenance.
  • Figure 9 illustrates determination of the catalytic formaldehyde degradation property of the laminates according to the invention.
  • Figure 10 illustrates determination of the catalytic benzene degradation property of the laminates according to the invention.
  • the present invention relates to floor covering exhibiting catalytic properties to reduce VOC-level in the indoor air.
  • the present invention provides solutions to indoor air problems by providing floor covering having air clarifying, anti staining, self-cleaning, antimicrobial and deodorizing properties.
  • air clarifying properties means that the substrate showing such properties can remove unpleasant odors, and/or removes and decompose harmful substances and contaminants in the air.
  • the present invention relates in particular to laminates comprising a decorative upper layer, optionally a protective overlay and optionally a base layer, characterized in that the decorative upper layer comprises a web of fibers having deposited therein and/or thereon photocatalyst particles embedded in a binder.
  • the laminates according to the invention comprise a decorative upper layer, a protective overlay and optionally a base layer, characterized in that said protective overlay comprises a web of fibers having deposited therein and/or thereon photocatalyst particles embedded in a binder.
  • a protective overlay refers to one or more overlay.
  • particle is to be understood in a very broad sense, including powders, dusts, fine granulates, filings and fibers, i.e. all forms of particles able to be distributed over a surface in a largely even manner.
  • the overlay and the decorative layer according to the present invention comprise a fiber web made of any suitable fiber.
  • said fibers are cellulose fibers.
  • other materials either on the basis of cellulose or not, are not excluded.
  • said overlay and the decorative layer are made of thin sheet of paper.
  • oxide and non- oxide semiconductors such as TiO 2 , ZnO, SiO 3 ; Ti 1-x Sn x O 2 , SrTiO 3 , Fe 2 O 3 , CdS, CdSe, W0 3 , FeTiO 3 , GaP, GaAs, GeAs, RuO 2 , MoS 3 , LaRhO 3 , CdFeO 3 , Bi 2 O 3 , MoS 2 , ln 2 O 3 , CdO, SnO 2 , SiC, InP and/or mixture thereof.
  • oxide and non- oxide semiconductors such as TiO 2 , ZnO, SiO 3 ; Ti 1-x Sn x O 2 , SrTiO 3 , Fe 2 O 3 , CdS, CdSe, W0 3 , FeTiO 3 , GaP, GaAs, GeAs, RuO 2 , MoS 3 , LaRhO 3 , CdFeO 3 , Bi 2
  • TiO 2 , ZnO, SiO 3 ; CdS, CdSe, GaP, MoS 3 , SiC, and the like are used. In an embodiment they are used on a nanoscale size. They are excellent in the points that they show a deodorant function, an antimicrobial function or an antistain function due to decomposition of an organic compound by oxidation. Among these, TiO 2 , Fe 2 O 3 , ZnO, SnO 2 , and the like are available in the point that starting materials are obtained cheaply, and further an anatase type TiO 2 and SnO 2 are more preferred in the point that fine particles having higher activity can be easily obtained. Rutile form TiO 2 metalized with copper, silver, platinum or other metals may also be used. The photocatalyst particles having photocatalytic function of the present application may be used either any one kind of these or in combination of two kinds or more by mixing.
  • Photocatalyst described herein are able to break down many organic pollutants totally or partially.
  • TiO 2 as anatase is preferred since high photocatalytic purification has been observed because of its strong oxidation power, high chemical durability and non-toxicity.
  • TiO 2 is an inorganic oxide, showing no absorption of any fraction of the visible light, thus it is not colored. In the region of shorter wavelength a strong absorption of UV radiation is observed. This is due to the promotion of an electron out of the valence band into the conductive band. In its anatase modification the band gap is 3.05 eV. In its tuned form the band gap is 2.8 eV. In this process photo energy is transferred into chemical energy.
  • said photocatalyst particles may be doped or tuned by adding one or more element within the crystal lattice of said photocatalyst.
  • said photocatalyst particles can be doped with elements selected from the group comprising Nb, Mo, Cr, V, Cu, Mg, Ag, Ru, Au, N, Nd, Pd, Pt, Fe, Ni, Mn and the like. Said elements can be the atom as such or ion form of said atoms.
  • titanium oxide catalysts can be implanted from the surface to deep inside of the bulk of the photocatalyst in an amount of at least 10 15 ions per g of the photocatalyst.
  • incorporating specific metal ions into the titanium oxide catalysts allows the catalyst to absorb light not only in the ultraviolet region but also in the visible light regions of about 400 to 800 nm.
  • the present invention provides laminates comprising overlay layer or decorative layer having a web of fiber comprising photocatalyst particles embedded in a suitable binder.
  • suitable binder include melamine resin, urethane resin, celluloid, chitin, starch sheet, polyvinyl alcohol, polyester resins, urea-formaldehyde, dicyandiamide-formaldehyde, epoxy resins, polyurethane resins, (poly)silane resins, (poly)siloxane resins, silazane resins, acrylamide resins, acrylic silicon resins, acrylurethane resins, polyacrylamide resins and the like and mixtures thereof.
  • the laminate may comprises a decorative layer as used in the prior art and an overlay according to the invention.
  • Said decorative layer for example, can be made of paper impregnated with resin, which can be imprinted with a variety of patterns, such as a wood pattern, a pattern in the form of stone, cork, or similar or even with a fancy pattern. It is clear that still other layers can be provided to the laminate, such as an intermediate layer upon which the decorative layer is provided.
  • the base layer of the laminate of the present invention may be selected from the group comprising of fiber board, particle board, a plastic sheet, wood and the like.
  • Said base layer may be made of finely-ground wood which preferably is glued, more particularly, watertight glued. Still more particularly, said base can be made of HDF board (High Density Fiberboard) or MDF (Medium Density Fiberboard). In a preferred embodiment, said base layer is MDF.
  • a backing layer also referred as balancing sheet or counteracting layer
  • balancing sheet can be applied at the underside of the base layer forming a counterbalancing element for the top layers and, thus, guaranteeing the stability of the form of the floor laminate.
  • This balancing sheet may consist of a material, for example paper, impregnated with a resin, for example, a melamine resin.
  • the laminates according to the invention exhibit anti staining, selfcleaning, antimicrobial and deodorizing properties. These laminates have a surface profile with improved properties over the current art.
  • the present invention further relates to decorative layers as described above.
  • said decorative layer is made of cellulose fibers, such as paper.
  • said decorative layer is impregnated with a composition comprising photocatalyst particles and a binder. Examples of suitable photocatalysts have been described herein.
  • said decorative layer comprises on or in its fiber web TiO 2 particles, and more preferably anatase TiO 2 .
  • the photocatalyst particles used in said decorative layer may be doped with elements as described above. Suitable binders embedding said particles are the same as that described above.
  • the decorative layers according to the invention according to the present invention can be used for manufacture and decoration of laminates, furniture components, flooring laminates and other surfaces where decoration is needed.
  • the present invention also relates to protective overlay comprised of a fiber web having deposited thereon or therein photocatalyst particles embedded in a binder.
  • Suitable binders embedding said particles are the same as that described above.
  • Suitable photocatalyst particles comprised in said overlay are the same as that described above.
  • Said photocatalyst may be additionally doped as described above.
  • said overlay is provided with TiO 2 particles and more in a particular with anatase TiO 2 .
  • the protective overlay is made of one or more material layers such as cellulose fibers for example very thin layers of paper. Said overly may be a transparent or translucent, specially made cellulose paper into which additional abrasion- resistant particles can be woven, or which can be impregnated with any other abrasion- resistant particles, which give the laminate the desired resistance to wear and tear and the hardness required for long-term use.
  • abrasion-resistant particles include but are not limited to mineral particles such as silica, alumina, alundun, corundum, emery, spinel, as well as other materials such as tungsten carbide, zirconium boride, titanium nitride, tantalum carbide, beryllium carbide, silicon carbide, aluminum boride, boron carbide, diamond dust, and mixtures thereof.
  • the overlays according to the present invention can be used for manufacture of decorative laminates, furniture components, flooring laminates and other surfaces where wear protection is needed.
  • the present invention also relates to a process for the manufacture of overlays and decorative layers and laminates according to the invention.
  • the decorative layer and the protective overlay according to the present invention are prepared according to a process comprising the step of (a) providing a fiber web layer, (b) treating said fiber web layer with a photocatalyst composition comprising photocatalytic particles, a binder and optionally at least one solvent, and (c) hardening said treated fiber web to obtain a decorative layer or a protective overlay comprising a web of fibers having deposited therein and/or thereon photocatalyst particles embedded in a binder.
  • Suitable photocatalyst particles used in the photocatalyst composition have been described above and are selected from the group comprising TiO 2 , ZnO, SiO 3 ; Ti 1-x Sn x O 2 , SrTiO 3 , Fe 2 O 3 , CdS, CdSe, WO 3 , FeTiO 3 , GaP, GaAs, GeAs, RuO 2 , MoS 3 , LaRhO 3 , CdFeO 3 , Bi 2 0 3 , MoS 2 , ln 2 O 3 , CdO, SnO 2 , SiC, InP and/or mixture thereof.
  • TiO 2 is used on a nanoscale size.
  • the photocatalyst when the composition comprises a suspension in a solvent, the photocatalyst may be employed in an amount ranging from 0.01 to 5 % by weight, for example in an amount ranging from 0.01 to 1% by weight and for example in an amount ranging from 0.05 to 0.3 %.
  • binder examples include but are not limited to melamine resin, urethane resin, celluloid, chitin, starch sheet, polyvinyl alcohol, polyester resins, urea-formaldehyde, dicyandiamide-formaldehyde, epoxy resins, polyurethane resins, (poly)silane resins, (poly)siloxane resins, silazane resins, acrylamides resins, acrylic silicon resins, acrylurethane resins, polyacrylamide resins and the like and mixtures thereof.
  • the binder when the composition comprises a suspension in a solvent, the binder may be employed in an amount ranging from 0.01 to 5 % by weight, for example in an amount ranging from 0.01 to 1 % by weight and for example in an amount ranging from 0.05 to 0.3 %.
  • said photocatalyst composition comprises a solvent.
  • Suitable solvents can be selected from the group comprising water, ethylene glycol butyl ether, aliphatic linear, branched or cyclic or mixed aromatic-aliphatic alcohols having 4 to 20 carbon atoms, such as methanol, ethanol, butanol, 2-propanol, isobutanol, isopropanol. benzyl alcohol, methoxypropanol or furfuryl alcohol; and the like, and/or mixture thereof.
  • said solvent is selected from the group comprising water, ethylene glycol butyl ether, ethanol and the like, and/or mixture thereof.
  • said solvent is water.
  • the photocatalyst composition may further comprise additional solvent such as for example ethylene glycol butyl ether.
  • said photocatalyst composition is a suspension comprising the photocatalyst particles, a binder and at least one solvent.
  • the solvent can be employed individually or as a mixture, and in particular in a amount ranging from 50 to 99 % by weight, for example in an amount ranging from 80 to 99% by weight and for example in an amount ranging from 90 to 99 %.
  • the photocatalyst particles can be dispersed or otherwise introduced into a molten, uncrosslinked, uncured or dissolved form of a suitable binder.
  • the photocatalyst composition for use in the present invention may further comprise antimicrobial agents. Although not limiting, up to 1 % by weight of antimicrobial agents may be added to the photocatalyst composition.
  • Antimicrobial agents suitable for said photocatalyst composition may be any chemical capable of preventing the growth of or killing microorganisms.
  • suitable antimicrobial agents include, but are not limited to, quaternary ammonium, phenolic, amide, acid, and nitro compounds, and mixtures thereof.
  • quaternary ammonium compounds include, but are not limited to, 2-(3-anilinovinylul)3,4-dimethyl- oxazolinium iodide, alkylisoquinolium bromide, benzalkonium chloride, benzethonium chloride, cetylpyhdinium chloride, chlorhexidine gluconate, chlorhexidine hydrochloride, lauryl trimethyl ammonium compounds, methylbenzethonium chloride, stearyltrimethyl ammonium chloride, and mixtures thereof.
  • Suitable phenolic compounds include, but are not limited to, benzyl alcohol, p-chlorophenol, chlorocresol, chloroxylenol, cresol, o-cymene-ol (BIOSOL), hexachlorophene, hinokitiol, isopropylmethylphenol, parabens (having methyl, ethyl, propyl, butyl, isobutyl, isopropyl, and/or sodium methyl substituents), phenethyl alcohol, phenol, phenoxyethanol, o-phynylphenol, resorcin, resorcin monoacetate, sodium parabens, sodium phenolsulfonate, thioxolone, 2,4,4'- trichloro hydroxidiphenyl ether, zinc phenolsuflonate, di-tert.-butyl phenole, hydrochinone, and mixtures thereof.
  • benzyl alcohol p
  • Suitable amides include, but are not limited to, diazolidinyl urea, 2,4-imidazolidinedione (HYDATOIN), 3,4,4'-trichlorocarbanilide, 3- trifluoromethyl-4,41-dichlorocarbanilide, undecylenic acid monoethanolamide, and mixtures thereof, more preferably still 2,4-imidazolidinedione.
  • HYDATOIN 2,4-imidazolidinedione
  • 3,4,4'-trichlorocarbanilide 3,4,4'-trichlorocarbanilide, 3- trifluoromethyl-4,41-dichlorocarbanilide, undecylenic acid monoethanolamide, and mixtures thereof, more preferably still 2,4-imidazolidinedione.
  • suitable acids include, but are not limited to, ascorbic acid, benzoate, benzoic acid, citric acid, dehydroacetic acid, potassium sorbate, salicylic acid derivatives such as acetyl salicylic acid, salicylic acid aldehyde, sodium citrate, sodium dehydroacetate, sodium salicylate, sodium salicylic acid, sorbic acid, undecylenic acid, zinc undecylenate, and mixtures thereof.
  • suitable nitro compounds include, but are not limited to, 2-bromo nitro-2,3-propanediol (BRONOPOL), and methyldibromo glutaronitrile and propyulene glycol (MERGUARD), and mixtures thereof.
  • said antimicrobial agent is hinokitiol.
  • the photocatalyst composition according to the present invention may further comprise abrasion-resistant particles.
  • suitable abrasion-resistant particles include but are not limited to mineral particle such as silica, alumina, alundun, corundum, emery, spinel, as well as other materials such as tungsten carbide, zirconium boride, titanium nitride, tantalum carbide, beryllium carbide, silicon carbide, aluminum boride, boron carbide, diamond dust, and mixtures thereof.
  • mineral particle such as silica, alumina, alundun, corundum, emery, spinel
  • other materials such as tungsten carbide, zirconium boride, titanium nitride, tantalum carbide, beryllium carbide, silicon carbide, aluminum boride, boron carbide, diamond dust, and mixtures thereof.
  • aluminum oxide is the preferred particles.
  • the photocatalyst composition according to the present invention may also contain auxiliaries or additives such as absorbents, rheological modifiers, plasticizers, antifoaming agents, antifouling agents, thixotropic agents, pigments, fillers, aggregates, extenders, reinforcing agents, flow control agents, catalysts, pigment pastes, mineral oils, wetting agents, adhesion promoters, thickening agents, flame-retarding agents, antioxidants, elastomers, antisettling agents, diluents, UV light stabilizers, air release agents, solvents, dispersing aids, and mixtures thereof, additional hardeners and additional curable compounds, depending on the application.
  • auxiliaries or additives such as absorbents, rheological modifiers, plasticizers, antifoaming agents, antifouling agents, thixotropic agents, pigments, fillers, aggregates, extenders, reinforcing agents, flow control agents, catalysts, pigment pastes, mineral oils, wetting agents
  • the photocatalyst composition can be formulated as comprising 0.10 to 0.15 % by weight of photocatalyst particles, 0.10 to 0.20 % by weight of antimicrobial agent, 0.10 to 0.15% by weight of a binder, 0.03 to 0.05 % by weight of a solvent and above 98 % by weight of water.
  • the photocatalyst composition can be formulated as comprising 0.10 to 0.15 % by weight of TiO 2 , 0.10 to 0.20 % by weight of hinokitiol, 0.10 to 0.15% by weight of a binder, 0.03 to 0.05 % by weight of ethylene glycol butyl ether and above 98 % by weight of water.
  • Said treating step (b) is an impregnating step.
  • said treating step (b) is selected from the group comprising dipping, flooding, coil coating, spraying, centrifuging, screen printing, vacuum infiltrating and the like.
  • the next step in the process according to the invention consists of the curing also referred as drying step (c).
  • the treated layer according to the invention is solidified, cured or otherwise hardened and processed to produce the overlay or decorative layer according to the invention.
  • the term "cured” or “dried” as used herein is not limited to materials which are cross-linked, but is open to materials which set, harden or solidify by any known means such as polymerization, heating, removal of solvent, freezing, chemical reaction, etc.
  • the treated layer may be a decorative layer or an overlay.
  • said drying step may be performed by thermal hardening such as by heating, by infra red treatment, using laser and the like. Said heating may be performed for example using a metal plate, or a traditional oven and the like. Said drying step may also be performed using radiation hardening such as UV, VIS, laser hardening, electron beam hardening and the like. When the drying step is a heating step the temperature may range from room temperature to 350 °C.
  • the photocatalyst composition for use herein is applied, coated or impregnated to the surface of a fibrous sheet using a suitable coating device.
  • the photocatalyst composition according to the invention can be applied to the sheet by any process used for applying a coating.
  • Non-limiting examples of devices for depositing the photocatalyst composition according to the invention particles include a secondary headbox or a slot orifice coating head applicator.
  • the term "slot orifice coater" as used herein is used in the same manner it is used in the art, namely, to designate a coater having a central cavity which opens on and feeds a slot through which the coating is forced under pressure.
  • the laminate of the present invention is suitably made according to standard practice and suitably has a conventional construction.
  • the laminate is formed by superposing the different layers.
  • the final laminate is made in the typical way such as by stacking the different layers on a suitable press or pressing plate die and subjecting the assembly to sufficient heat and pressure between the bottom pressing plate die and a highly polished upper pressing plate die for a time sufficient to produce the desired decorative laminate.
  • the conditions of pressing for both high pressure laminate and low-pressure laminate are standard and well known.
  • the laminates are realized according to the classical technique which is applied for forming DPL (Direct Pressure Laminate). It is evident that, according to a variant, the overlay and the decorative layer, already before their application on the base layer, may consist of a single layer.
  • the laminate according to the present invention can be cut into individual panels.
  • the laminates can be cut into floor panels of suitable sizes. These floor panels can be of various shape, for example, rectangular or square, or of any other shape. In an embodiment, they can be manufactured in an elongated form, with a length of for example 1 to 2 meters.
  • the thickness can also vary. Although non-limiting, said thickness may range from 0.1 mm to 45 mm.
  • Non limiting examples of suitable thickness range from 0.1 mm to 3 mm, from 5 to 15 mm, for example 8 mm.
  • the panels can be provided on their side with suitable tongue and groove coupling.
  • the groove and tongue profile is milled along the edges of the support, thereby allowing the individual panels to be joined up during the laying process.
  • the dimensions of the profiles are designed so that adjacent panels can be pushed or hit into each other.
  • the laminates or panels according to the invention can treated at their sides with a surface densifying agent, more particularly a surface hardening agent, which preferably is chosen from the following series of products: impregnation agents, pore-sealing agents, lacquers, resins, oils, paraffines and similar.
  • a surface densifying agent more particularly a surface hardening agent, which preferably is chosen from the following series of products: impregnation agents, pore-sealing agents, lacquers, resins, oils, paraffines and similar.
  • This treatment can be performed over the complete surface of the sides or only over well-defined portions thereof, for example, exclusively the surfaces of the tongue and groove.
  • the treatment with a surface densifying agent offers, in combination with the snap-together effect of the tongue and groove, the advantage that in various aspects better coupling features, are obtained. As a result of this, the coupling parts better keep their shape and strength, even if the floor panels are engaged and disassembled repeatedly.
  • the floor laminates or panels according to the present invention can be applied in various ways. They can be attached at the underlying floor, either by gluing or by nailing them on. According to another possibility, the floor laminates may be installed loosely onto the underground, whereby the floor laminates may mutually match into each other by means of a tongue and groove coupling, whereby mostly they are glued together in the tongue and groove, too.
  • the floor obtained in this manner also called a floating parquet flooring, has as an advantage that it is easy to install and that the complete floor surface can move which often is convenient in order to receive possible expansion and shrinkage phenomena.
  • the floor laminates may also be provided at the edges of two opposite sides, with coupling parts, co-operating with each other, substantially in the form of a tongue and a groove, whereby the coupling parts are provided with integrated mechanical locking means made in one piece with the panels which prevent the drifting apart of two coupled floor panels.
  • the floor covering preferably is formed by joining the floor laminates into each other free of glue.
  • the connections are of such nature that the floor panels can be disassembled without being damaged, such that, for example, when moving, they can be taken along in order to be placed again. It is, however, clear that gluing between tongue and groove is not excluded.
  • the present invention provides laminates, and protective or decorative layer having photocatalytic functions such as deodorant, antimicrobial activities and the like.
  • the invention is intended for so-called laminated floors, but generally it can also be applied for other kinds of floor covering, comprising hard floor panels, such as veneer parquet, prefabricated parquet, or other floor panels which can be compared to laminated floor.
  • the invention is also suitable for carpets and mats such as car mats and the like.
  • said floor covering is a carpet which has undergone a post-treatment with a finishing composition comprising the photocatalyst composition described above, optionally in combination with stain resists such as grease and water stain fluoride-based repellent.
  • the term "carpet" encompasses carpets, rug, mats and the like.
  • the finishing composition comprises (a) the photocatalyst composition as described above (b) a liquid carrier and optionally (c) a coarcervate.
  • Said composition may further comprise soil resists products such as fluorocarbon to impart water and oil repellency.
  • the finishing composition may also comprise a stain resists.
  • the finishing composition may further comprise a softener for extra bulk.
  • the finishing composition comprises the photocatalyst particles in an amount ranging from 0.01 to 5 % by weight of the photocatalytic composition, preferably from 0.01 to 1% by weight and most preferably from 0.05 to 0.3 % by weight.
  • the photocatalyst composition to be used in the finishing composition is added in a concentration comprised between 1 to 50 % by weight, preferably from 5 to 35 % by weight, more preferably from 7 to 20 % by weight, yet more preferably from 7 to 13 % by weight, most preferably from 8 to 9 %.
  • the liquid carrier is preferably an aqueous system.
  • the carrier can also contain a low molecular weight organic solvent that is highly soluble in water, e.g., C1 to C4 monohydric alcohols, C2 to C6 polyhydric alcohols, such as alkylene glycols and polyalkylene glycols, alkylene carbonates, and mixtures thereof.
  • a low molecular weight organic solvent that is highly soluble in water, e.g., C1 to C4 monohydric alcohols, C2 to C6 polyhydric alcohols, such as alkylene glycols and polyalkylene glycols, alkylene carbonates, and mixtures thereof.
  • these water-soluble solvents include ethanol, propanol and isopropanol.
  • the liquid carrier and the solvent to be used in the finishing composition and/or in the photocatalyst composition are each independently selected from the group comprising water, alkylene glycols, polyalkylene glycols, alkylene carbonates, ethanol, propanol and isopropanol and mixtures thereof.
  • Water is a preferred liquid carrier due to its low cost, availability, safety, and environmental compatibility.
  • the water can be distilled, deionized, or tap water.
  • Highly preferred materials of this class of liquid carriers are those that do not cause any significant color change, nor impart any discoloration, such as graying or yellowing, to the carpets to which they are applied, either during treatment followed by drying and/or curing, or after the drying and/or curing step followed by normal exposure to the elements, such as air, moisture or sunlight exposure.
  • the level of liquid carrier to be used in the finishing composition can typically be from 50% to 99% of the composition, for example from 75% to 95%, and preferably from 80% to 90 % of the composition, for example 87 to 89 %.
  • the coacervate for use in the finishing composition assists in solubilising the particles and provides a uniform film at the fiber surface.
  • Said coacervate can be selected form the group comprising Levalin VKU-N (Bayer), Primasol SD (BASF), Irgapadol PN New (Ciba), Lyogen AF (Clariant AG), Intratex AF (Crompton & Knowles) and the like.
  • the amount of coacervate to be used in the finishing composition can typically vary from 0 to 15 %, for example from 1 to 10 %, for example from 2 to 5 % and preferably from 2 to 4 %.
  • the binder to be used can be selected from the group comprising melamine resin, urethane resin, celluloid, chitin, starch sheet, polyvinyl alcohol, polyester resins, urea-formaldehyde, dicyandiamide- formaldehyde, epoxy resins, polyurethane resins, (poly)silane resins, (poly)siloxane resins, silazane resins, acrylamides resins, acrylic silicon resins, acrylurethane resins, polyacrylamide resins and the like and mixtures thereof.
  • the binder is used in an amount ranging from 0.01 to 5 % by weight of the photocatalyst composition, preferably from 0.01 to 1 % by weight, more preferably from 0.05 to 0.3 % by weight.
  • Suitable carpet fiber material which can be treated with the finishing composition are materials comprising for example, wool, polyamide, polyurethanes, polyester, polyacrylonitrile, polypropylene, polyethylene and cellulose-containing fiber materials of all kinds, for example natural cellulose fibers, such as cotton, linen, jute and hemp, and also regenerated cellulose.
  • the materials may also be used as blends of natural fibers like cotton, wool or jute with each other or with synthetic fiber materials like PES, Nylon or polypropylene or blends of synthetic fiber materials with each other.
  • Typical fiber blends are of polyacrylonitrile-polyester, polyamide/polyester, polyester/cotton, polyester/viscose and polyester/wool.
  • stain resists and soil resists may be used in the finishing composition.
  • Suitable stain resists are polymers containing phenol-formaldehyde, methacrylic acid, maleic acid, sulfonated fatty acids, and blends of the above.
  • Suitable soil resists are polymers containing fluorochemical residues with the most preferred being cationically dispersed. The use of cationic fluorochemicals in combination with anionic stain resists typically gives better fluorine retention.
  • Suitable stain resists for the practice of this invention include, but are not limited to, phenol formaldehyde polymers or copolymers such as CEASESTAIN and STAINAWAY (from American Emulsions Company, Inc., Dalton, Ga.), MESITOL (from Bayer Corporation, Pittsburgh, Pa.), ERIONAL (from Ciba Corporation, Greensboro, N.C.), TAMOL (from Rohm & Haas Co.), BAYPROTECT CL or CSDTM (from Bayer AG), INTRATEX (from Crompton & Knowles Colors, Inc., Charlotte, N.C.), NYLOFIXANTM P (from Sandoz Corp.), ACRYSOLTM (from Rohm and Haas Company) and CARBOPOLTM (from B.
  • phenol formaldehyde polymers or copolymers such as CEASESTAIN and STAINAWAY (from American Emulsions Company, Inc., Dalton, Ga.), MESITOL (from Bayer Corporation, Pittsburgh, Pa.),
  • LEUKOTANTM family of materials such as LeukotanTM 970, LeukotanTM 1027, LeukotanTM 1028, and LeukotanTM QR 1083 (from Rohm and Haas Company), and sulfonated fatty acids from Rockland React-Rite, Inc., Rockmart, Ga.).
  • Suitable soil resists for the practice of the present invention include, but are not limited to, fluorochemical emulsions such as AMGUARD (from American Emulsions Company, Inc., Dalton, Ga.), SOFTECH (from Dyetech, Inc., Dalton, Ga.), LANAPOL (from Lenmar Chemical Corporation, Dalton, Ga.), SCOTCHGARD FC series carpet protectors (from 3M Company, St. Paul, Minn.), NK GUARD (from Nicca USA, Inc., Fountain Head, N.C.), UNIDYNE (from Diakin America, Inc., Decatur, Ala.), and ZONYL such as Zonyl 555, N-130 and N-119 (from E. I.
  • fluorochemical emulsions such as AMGUARD (from American Emulsions Company, Inc., Dalton, Ga.), SOFTECH (from Dyetech, Inc., Dalton, Ga.), LANAPOL (from Lenmar Chemical Corporation, Dalton, Ga.), SCOTC
  • the amount of the stain resists and/or soils resists used in the preparations of the finishing composition of the present invention are the amounts typically employed in the carpet and fabric industry and would be well known to those skilled in the art. Ordinarily, depending upon the nature of the stain resist and/or soils resist and the carpet being treated and its location, the resists are applied to the material in an amount to result in a treatment rate of 0.1 wt % to 20 wt % based upon the weight of the weight of the carpet being treated and the amount of stain resists and/or soils resists.
  • the treatment rate will be from 0.15 wt % to 10 wt %, preferably from 0.2 wt % to 4 wt %, more preferably from 0.25 wt % to 2 wt %.
  • the stain resists and/or soils resists is applied to give a treat rate of 0.25 wt % to 1.0 wt % based upon the weight of the carpet being treated.
  • the finishing composition of the present invention may be provided with other active ingredients depending upon the application or surface to be treated.
  • One such additional ingredient which may be utilized in the finishing composition depending upon the application is a foaming agent for producing a foam composition for treating the relatively absorbent surfaces of the carpet.
  • foaming agents include lauryl sulphate, ammonium lauryl sulphate, sodium lauryl sulphate.
  • the additional ingredients would be utilized in the compositions at the usually employed concentrations, generally 5 % by weight or less based upon the total weight of the finishing composition.
  • the finishing composition is prepared by emulsifying the photocatalyst composition in water, using equipment such as a sonnicator, homogenizer, microfluidizer, high shear blending equipment and the like.
  • the finishing composition may be applied to the surface at any stage during its manufacture.
  • the finishing composition may be utilized to treat the precursor filaments, yarns or fibers prior to their use in the conventional manufacturing process.
  • the filament or yarn may be run through a bath containing the finishing composition or the finishing composition may be sprayed on the filament.
  • the filaments or yarns are dried and then further processed into carpet in the normal manner.
  • the carpet during the manufacturing process may be immersed, sprayed or otherwise treated with the finishing composition.
  • the carpet fibers may be sprayed or otherwise treated with the finishing composition prior to being inserted into the primary backing.
  • the fibers may also be treated once they have been inserted into the primary backing, either before or after the backing adhesive and secondary backing material have been applied.
  • the finishing composition may also be applied to the finished carpet as a final step prior to drying and rolling.
  • the carpet would be sprayed or otherwise treated with the finishing composition, after which time the carpet would be dried in the usual manner and rolled onto the roll.
  • the finishing composition can be applied to the carpet in an amount ranging from 10 g/m 2 to 100 g/m 2 of surface, for example from 20 g/m 2 to 70 g/m 2 , preferably from 40 g/m 2 to 60 g/m 2 , and preferably in an amount of 50 g/m 2 .
  • the finishing compositions according to the present invention can be applied to the carpets by a variety of methods. Examples of such methods include, but are not limited to, beck dying procedures, continuous dyeing procedures, brushing, dipping, spraying, padding, roll-coating, foaming or the like.
  • the finishing compositions can be applied to the carpet as such or in combination with other fluorofinishes, stainblockers, processing aids, lubricants, anti-stains, etc.
  • the compositions can also be blended with other agents that have oil/water repellency and soil release properties and applied to the carpets. They can be applied to dyed and undyed carpeting.
  • the finishing composition is formulated as foam and can be roll-coated on the carpet. Once the finishing composition applied the coated carpets exhibit fibers having uniform and even coating of photocatalyst particles of an average size of 2 ⁇ m with a spread of 0,5 to 4 ⁇ m.
  • said finishing composition is provided as a foam.
  • the finishing composition can then be applied by means of a foam applicator.
  • Foam application has several advantages, it allows exact quantity controllable application and an even application without any stripes. Low wet pick-up is observed and an adjustable penetration of the composition can be obtained. In addition this mode of application requires only little space. It is also ecologically beneficial and has a minimum impact on speed.
  • the finishing composition can be applied after dyeing, before drying. In another embodiment the finishing composition can be applied during finishing.
  • the finishing composition can be applied as aqueous formulation in diluted, solubilised, emulsified or dispersed form.
  • finishing composition Another option would be to apply the finishing composition to an installed carpet.
  • the finishing composition When applying the finishing composition to an installed carpet, it is not essential, but preferred that the finishing composition be applied thoroughly and evenly throughout the length of the pile, especially reaching down to the base of the pile fiber. This is generally achieved by applying an aqueous foaming finishing composition to the carpet and then working the fibers to improve the contact, distribution and penetration of the finishing composition. This is most commonly achieved by use of a pile brush operated either by hand or automatically for example, utilizing a cleaning device such as is commonly available commercially.
  • the fibers of the carpet may initially be wetted through an application of a detergent solution. This is most commonly applied where the installed carpet is cleaned using a cleaning machine prior to the application of the finishing composition .
  • the finishing composition may be applied and worked into the carpet, utilizing the pile brush. Once the carpet has been so treated, it is dried, either by allowing it to dry in the air at ambient temperature or through the use of hot air blown through the pile of the carpet to increase the speed of drying of the carpet.
  • the finishing composition may be applied in many different ways. The composition may be applied by dipping the material in the finishing composition or by spraying the composition onto the fibrous material. In any of these cases, once the fiber or carpet is treated with the finishing composition , the treated carpet material is allowed to dry by way of applied heat or simply by ambient drying.
  • the carpet backing and/or carpet cushion underlayment may also be treated with the finishing composition.
  • the carpet backing and/or carpet cushion underlayment may be treated during the manufacturing process, or prior to its installation.
  • the carpet cushion underlayment may also be similarly treated during the installation of the carpet cushion underlayment.
  • the present invention is in no way limited to the forms of embodiment described herein, on the contrary may such floor covering such as carpets, floor laminates, overlay and decorative layer, as well as said process, be realized in different variants without leaving the scope of the invention.
  • the surprising properties of the floor covering according to the invention are shown in the present examples wherein the VOC degradation properties of the floor covering of the invention are illustrated.
  • the following examples illustrate the use of the present invention but are not to be construed as limiting the scope of the present invention.
  • VOC degradation properties of the floor covering according to the invention are determined.
  • the tested VOC reference substances for indoor air were benzene, Formaldehyde (HCHO), TVOC (total volatile organic compound) and cigarette smoke polluted indoor air (tobacco odor).
  • the tested gas 4 flows out a container 15 comprising said gas in a concentrated form.
  • the gas flows out of tube 6 through a regulation valve 8 into tube 9 which is connected to the test chamber 2.
  • the concentrated gas is diluted and adjusted to the wanted concentration by means of pure air 6 flowing trough tube 7 connected to the regulation valve 8.
  • the air/gas mixture flows into tube 9 which is connected to the test chamber 2.
  • the sample 1 to be analyzed is placed in the test chamber 2 which comprise a UV bulb 3.
  • the gas flows out of the test chamber 2 through tube 10.
  • a data logger 11 is connected to the arrangement and control and/or measure the temperature, humidity and/or flow rate.
  • the tested gas flowing out of the test chamber 2 through tubing 10 is sampled through a valve 12 which is connected 17 to an olfactometer 13 and is also connected 16 to a sampling tube 4 for gas analysis.
  • Example 1 Determination of the catalytic formaldehyde degradation property of the carpets according to the invention under continuous aeration
  • the catalytic activity of TiO2 coated carpet was measured by the analysis of the effect of the coated carpets on formaldehyde degradation under continuous aeration.
  • the carpet samples were made from 40 cm x 40 cm carpet pieces. From these carpet pieces, carpet samples of 7.8 cm x 7.8 cm were manufactured and masked by means of an aluminum tape in order to avoid edge effects during the measurement of the catalytic degradation of the formaldehyde. Formaldehyde degradation was investigated under continuous aeration by chamber testing and compared with uncoated carpet samples, and with a control measurement performed in the test chamber without sample.
  • test chambers are airtight aluminum boxes which have a volume of 49.58 I, the proportion between the tested sample and the chamber volume amounts to 1.23 m 2 /m 3 in a standard inspection surface of 61 cm 2 .
  • the carpet samples were placed in the center of the test chambers and locked therein.
  • a UV lamp of 80 W was fixed in the chamber on the top.
  • a defined formaldehyde concentration of 220 ⁇ g/m 3 +/- 30 ⁇ g/m 3 (which corresponds to the average formaldehyde content in a smoker room) was applied in the test chamber by means of a continuous air supply over a Teflon hose at an air exchange rate of 0.5/h.
  • the test chambers were operated at a temperature of 20°C and a relative humidity of 50 %.
  • the formaldehyde originates from a 50 NI content high-grade steel container containing a concentrated formaldehyde atmosphere of 54000 ⁇ g/m 3 , in constant equilibrium between liquid and gaseous state at 20 °C and 50 % relative humidity.
  • the formaldehyde flows out of this container at an air flow of 3.0 l/h (50 ml/min) and is mixed with pure air in ratio of 1 :245.
  • the air flows out of the test chambers at a flow rate of 180 l/h, wherein 24.8 I were sampled by means of diaphragm pumps.
  • the initial fluctuations in formaldehyde content observed in the test chamber are due mainly to errors due for examples to sampling point, time needed to adjust the concentration inside the test chamber and the like. This is verifyed by the measurements performed in the test chambers without samples. A clear difference between the samples according to the invention and the controls can be seen after 8 h.
  • the samples according to the invention permit to obtain a clear decrease of the concentration from 220 ⁇ g/m 3 to a final concentration of 40-60 ⁇ g/m 3 which is well below the legal limit value of 120 ⁇ g/m 3 .
  • Example 2 Determination of the catalytic benzene degradation property of the carpets according to the invention under continuous aeration.
  • a concentration of 45 ⁇ g/m 3 +/- 15 ⁇ g/m 3 was applied in the test chamber by means of a continuous air supply over a Teflon hose at an air exchange rate of 0.5/h.
  • the test chambers were operated at a temperature of 20°C and a relative humidity of 50 %.
  • the benzene originates from a 50 NI content high-grade steel container containing a concentrated benzene atmosphere of 11200 ⁇ g/m 3 , in constant equilibrium between liquid and gaseous state at 20 °C and 50 % relative humidity.
  • the benzene flows out of this container at an air flow of 3.0 l/h (50 ml/min) and is mixed with pure air in ratio of 1 :26.
  • the air flows out of the test chambers at a flow rate of 180 l/h, wherein 24.8 I were sampled by means of diaphragm pumps.
  • Example 3 Olfactory evaluation of tobacco odor deodorant property of the carpets according to the invention
  • cigarette smoke -corresponding to the content of a room wherein 50 cigarettes are consumed daily- was applied in the test chamber by means of a continuous air supply over a Teflon hose at an air exchange rate of 0.5/h.
  • the test chambers were operated at a temperature of 20°C and a relative humidity of 50 %.
  • the cigarette smoke originates from a 50 NI content high-grade steel container containing a concentrated cigarette smoke atmosphere at 20 °C and 50 % relative humidity.
  • the cigarette smoke flows out of this container at an air flow of 5.2 l/h (87 ml/min) and is mixed with pure air in ratio of 1 :3.6 so as to obtain in the test chamber a concentration equivalent to the smoke of 50 cigarettes consumed daily.
  • the olfactometry measurements were performed according to the respective VDI recommendation 388I, Sheet I and II, whereby the odor intensity (Gl with a scaling from 0 to 5 corresponding to 5: intense odor, 4: strong odor, 3: readily perceptible, 2: weak odor perceptible, 1 : barely perceptible odor, 0: no odor) and the odor development/ Hedonik (GA with a scaling from -5 to +5 ) were evaluated. Three independent test persons made the respective odor evaluation and means values were calculated.
  • Example 4 Determination of the catalytic TVOC degradation property of the carpets according to the invention under continuous aeration.
  • cigarette smoke -corresponding to the content of a room wherein 50 cigarettes are consumed daily- was applied in the test chambers by means of a continuous air supply over a Teflon hose at an air exchange rate of 0.5/h.
  • the test chambers were operated at a temperature of 20°C and a relative humidity of 50 %.
  • the cigarette smoke originates from a 50 NI content high-grade steel container containing a concentrated cigarette smoke atmosphere at 20 °C and 50 % relative humidity.
  • the cigarette smoke flows out of this container at an air flow of 5.2 l/h (87 ml/min) and is mixed with pure air in ratio of 1 :3.6 so as to obtain in the test chamber a concentration equivalent to the smoke of 50 cigarettes consumed daily.
  • the air flowed out of the test chambers and 24.8 I were sampled by means of diaphragm pumps.
  • TVOC content The determination of the total content of volatile organic compounds (TVOC content) was performed by a portable gas chromatograph PE Photovac Voyager. In order to obtain representative values, 5 measurements were performed every 10 min. Calibration of the chromatograph was performed using a defined toluol standard. The detection used a photoionization detector with quick-change electrodeless discharge UV lamp, 10.6 eV.
  • the catalytic degradation property was measured by the analysis of the effect of the coated carpets on formaldehyde degradation under different UV light expositions.
  • the carpet samples were made from 40 cm x 40 cm carpet pieces. From these carpet pieces, carpet samples of 7.8 cm x 7.8 cm were manufactured and masked by means of an aluminum tape in order to avoid edge effects during the measurement of the catalytic degradation of the formaldehyde. Formaldehyde degradation was investigated under continuous aeration by chamber testing and compared with uncoated carpet samples, and with a control without sample.
  • test chambers are airtight aluminum boxes which have a volume of 49.58 I, the proportion between the tested sample and the chamber volume amounts to 1.23 m 2 /m 3 in a standard inspection surface of 61 cm 2 .
  • the carpet samples were placed in the center of the test chambers and locked therein.
  • a UV lamp 3 mW/cm 2 was fixed in the chamber on the top.
  • the experiment was set up in accordance with the usual daily light intensities which can be expected during the different seasons and weather conditions.
  • the experiment started by simulating winter conditions consisting of 10-hour light exposure under cloudy conditions which is estimated at 0.15 Wcm 2 for 10 hours, with half-hour irradiation of 3 mW/cm 2 .
  • the experiment carried on by extending the daily irradiating duration by 1 , 2, 4, 6 and 8 hours, in order to simulate irradiation expected during the transition periods of spring and autumn in the as well as maximum exposure in the summer time area.
  • the results were compared to those obtained using uncoated carpet samples or control measurements without samples.
  • a defined formaldehyde concentration of 220 ⁇ g/m 3 +/- 30 ⁇ g/m 3 (which corresponds to the average formaldehyde content in a smoker room) was applied in the test chamber by means of a continuous air supply over a Teflon hose at an air exchange rate of 0.5/h.
  • the test chambers were operated at a temperature of 20°C and a relative humidity of 50 %.
  • the formaldehyde originates from a 50 NI content high-grade steel container containing a concentrated formaldehyde atmosphere of 54000 ⁇ g/m 3 , in constant equilibrium between liquid and gaseous state at 20 °C and 50 % relative humidity.
  • the formaldehyde flows out of this container at an air flow of 3.0 l/h (50 ml/min) and is mixed with pure air in ratio of 1 :245.
  • the air flows out of the test chambers at a flow rate of 130 l/h, wherein 24.8 I were sampled by means of diaphragm pumps.
  • Example 6 Determination of the air cleaning durability of a carpet according to the invention under conditions intended to simulate a 5 year cycle of maintenance.
  • the air cleaning durability of a carpet according to the invention was evaluated under conditions intended to simulate a 5 year cycle of maintenance.
  • the carpet samples were made from 200 cm x 100 cm carpet pieces which were vacuum cleaned.
  • the carpet pieces were vacuumed 500 times each with a back and forth motion using a usual household-vacuum cleaner of 1200 Watt. This treatment corresponds to a usual regular cycle 2 times weekly carpet care over 5 years. Subsequently, a laundering took place at 30 °C with the addition of a commercial carpet preservative agent.
  • carpet samples of 7.8 cm x 7.8 cm were manufactured and masked by means of an aluminum tape in order to avoid edge effects during the measurement of the catalytic degradation of the formaldehyde.
  • the test chambers are airtight aluminum boxes which have a volume of 49.58 I, the proportion between the tested sample and the chamber volume amounts to 1.23 m 2 /m 3 in a standard inspection surface of 61 cm 2 .
  • the carpet samples were placed in the center of the test chambers and locked therein.
  • a UV lamp 3 mW/cm 2 was fixed in the chamber on the top.
  • the samples were incubated over a period of 14 days with constant irradiation by a UV lamp with a radiation intensity of 3 mW/cm 2 .
  • As a control sample a carpet according to the invention which had not been vacuumed was used.
  • a defined formaldehyde concentration of 220 ⁇ g/m 3 +/- 30 ⁇ g/m 3 was applied in the test chamber by means of a continuous air supply over a Teflon hose at an air exchange rate of 0.5/h.
  • the tests chambers were operated at a temperature of 20°C and a relative humidity of 50 %.
  • the formaldehyde originates from a 50 NI content high-grade steel container containing a concentrated formaldehyde atmosphere of 54000 ⁇ g/m 3 , in constant equilibrium between liquid and gaseous state at 20 °C and 50 % relative humidity.
  • the formaldehyde flows out of this container at an air flow of 3.0 l/h (50 ml/min) and is mixed with pure air in ratio of 1 :245.
  • the air flows out of the test chambers at a flow rate of 180 l/h, wherein 24.8 I are sampled by means of diaphragm pumps.
  • the catalytic activity of the laminates according to the invention was measured by the analysis of the formaldehyde degradation under continuous aeration, sample 0 (without titanium dioxide), sample 1 (with 0.076 % titanium dioxide) and sample 2 (with 1 % titanium dioxide).
  • the laminates used in this experiment consisted of 30 cm x 10 cm laminates. From these laminates, samples of 7.8 cm x 7.8 cm were manufactured and masked by means of an aluminum tape in order to avoid edge effects during the measurement of the catalytic degradation of formaldehyde. Formaldehyde degradation was investigated under continuous aeration by chamber testing and compared control samples.
  • test chambers are airtight aluminum boxes which have a volume of 49.58 I, the proportion between the tested sample and the chamber volume amounts to 1.23 m 2 /m 3 in a standard inspection surface of 61 cm 2 .
  • the carpet samples were placed in the center of the test chambers and locked therein.
  • a UV lamp 3 mW/cm 2 was fixed in the chamber on the top.
  • a defined formaldehyde concentration of 220 ⁇ g/m 3 +/- 30 ⁇ g/m 3 (which corresponds to the average formaldehyde content in a smoker room) was applied in the test chamber by means of a continuous air supply over a Teflon hose at an air exchange rate of 0.5/h.
  • the test chambers were operated at a temperature of 20°C and a relative humidity of 50 %.
  • the formaldehyde originates from a 50 NI content high-grade steel container containing a concentrated formaldehyde atmosphere of 54.000 ⁇ g/m 3 , in constant equilibrium between liquid and gaseous state at 20 °C and 50 % relative humidity.
  • the formaldehyde flows out of this container at an air flow of 3.0 l/h (50 ml/min) and is mixed with pure air in ratio of 1 :245.
  • the air flows out of the test chambers at a flow rate of 180 l/h, wherein 24.8 I were sampled by means of diaphragm pumps.
  • Example 8 Determination of the catalytic benzene degradation property of the laminates according to the invention
  • a concentration of 45 ⁇ g/m 3 +/- 15 ⁇ g/m 3 was applied in the test chamber by means of a continuous air supply over a Teflon hose at an air exchange rate of 0.5/h.
  • the test chambers were operated at a temperature of 20°C and a relative humidity of 50 %.
  • the benzene originates from a 50 NI content high-grade steel container containing a concentrated benzene atmosphere of 11200 ⁇ g/m 3 , in constant equilibrium between liquid and gaseous state at 20 °C and 50 % relative humidity.
  • the benzene flows out of this container at an air flow of 3.0 l/h (50 ml/min) and is mixed with pure air in ratio of 1 :26 .
  • the air flows out of the test chambers at a flow rate of 180 l/h, wherein 24.8 I were sampled by means of diaphragm pumps.
  • the laboratory tests were performed according to the respective DIN procedures and/or regulations wherein the benzene concentration was measured by use of the Tenax absorbent. Subsequently, the samples were examined by gas chromatography with the GG/FID/ECD.

Landscapes

  • Engineering & Computer Science (AREA)
  • Textile Engineering (AREA)
  • Architecture (AREA)
  • Civil Engineering (AREA)
  • Structural Engineering (AREA)
  • Catalysts (AREA)
PCT/EP2005/000354 2004-01-16 2005-01-14 Photocatalytic particles in floor laminates WO2005068181A1 (en)

Priority Applications (1)

Application Number Priority Date Filing Date Title
EP05706894A EP1715995A1 (de) 2004-01-16 2005-01-14 Photokatalytische teilchen in bodenlaminat

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
EP04447013 2004-01-16
EP04447013.6 2004-01-16

Publications (1)

Publication Number Publication Date
WO2005068181A1 true WO2005068181A1 (en) 2005-07-28

Family

ID=34778236

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP2005/000354 WO2005068181A1 (en) 2004-01-16 2005-01-14 Photocatalytic particles in floor laminates

Country Status (2)

Country Link
EP (1) EP1715995A1 (de)
WO (1) WO2005068181A1 (de)

Cited By (16)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2007040890A2 (en) * 2005-09-30 2007-04-12 3M Innovative Properties Company Photocatalytic coating
WO2007144718A2 (en) * 2006-06-13 2007-12-21 Flooring Industries Limited, Sarl Method for manufacturing coated panels and coated panel
BE1017168A5 (nl) * 2006-06-13 2008-03-04 Flooring Ind Ltd Werkwijze voor het vervaardigen van vloerpanelen en vloerpaneel.
GB2445548A (en) * 2007-01-13 2008-07-16 Philip Reed Laminate comprising particle board, and metal in thermoset resin
EP1961556A1 (de) * 2007-02-22 2008-08-27 Hermes Schleifkörper GmbH Zusammengesetzter Werkstoff, Paneel, das solchen zusammengesetzten Werkstoff umfasst, Verfahren zum Herstellen solcher zusammengesetzter Werkstoffe und solcher Paneele
WO2009062516A3 (en) * 2007-11-16 2009-08-27 Scf Technologies A/S Photocatalytic boards or panels and a method of manufacturing thereof
US20100029471A1 (en) * 2006-11-27 2010-02-04 Ruei-Shan Wang Photocatalyst-synthesized fiber product
EP2174780A1 (de) 2008-10-10 2010-04-14 Sika Technology AG Aufwickelbarer Fliesenaufbau, Verfahren zur Herstellung sowie die Verwendung
WO2011093785A1 (en) * 2010-01-29 2011-08-04 Välinge Innovation AB Method for applying nanoparticles
WO2013006125A1 (en) * 2011-07-05 2013-01-10 Välinge Photocatalytic Ab Coated wood products and method of producing coated wood products
WO2014098762A1 (en) * 2012-12-21 2014-06-26 Välinge Photocatalytic Ab A method for coating a building panel and a building panel
US9375750B2 (en) 2012-12-21 2016-06-28 Valinge Photocatalytic Ab Method for coating a building panel and a building panel
US9573126B2 (en) 2012-03-20 2017-02-21 Valinge Photocatalytic Ab Photocatalytic composition
US9945075B2 (en) 2013-09-25 2018-04-17 Valinge Photocatalytic Ab Method of applying a photocatalytic dispersion
US9963609B2 (en) 2009-03-23 2018-05-08 Valinge Photocatalytic Ab Production of titania nanoparticle colloidal suspensions with maintained crystallinity by using a bead mill with micrometer sized beads
WO2020226600A2 (en) 2019-05-06 2020-11-12 Alpay Aytekin Composition used in coating inorganic compounds used in the production of laminate flooring

Families Citing this family (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN111939944B (zh) * 2020-07-28 2022-09-06 西北师范大学 一种硒化镉量子点/二硫化钼复合光催化剂的制备与应用
CN112246246A (zh) * 2020-09-30 2021-01-22 常州烯奇新材料有限公司 一种可见光响应的光触媒复合材料及其制备方法

Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1998052871A1 (fr) * 1997-05-23 1998-11-26 Kyorasha Co., Ltd. Matiere contenant de l'oxyde de titane et son procede de preparation
JPH1120067A (ja) * 1998-06-08 1999-01-26 Toto Ltd 貼着用光触媒機能材
JPH11207189A (ja) * 1998-01-22 1999-08-03 Lintec Corp 酸化チタンの被着方法
JP2000262905A (ja) * 1999-03-18 2000-09-26 Inax Corp 光触媒タイル
JP2002178459A (ja) * 2000-12-18 2002-06-26 National Institute Of Advanced Industrial & Technology 光触媒担持印刷物
WO2002085989A1 (en) * 2001-04-25 2002-10-31 Nanopac Ltd. Photocatalytic coating material having photocatalytic activity and adsorption property and method for preparing the same
JP2002371479A (ja) * 2001-06-08 2002-12-26 Kuraray Co Ltd 壁 紙
JP2003019764A (ja) * 2001-07-09 2003-01-21 Achilles Corp 光触媒機能を有する装飾シート
JP2003071967A (ja) * 2001-08-31 2003-03-12 Takiron Co Ltd 光触媒層を最外層に形成した化粧板

Patent Citations (9)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO1998052871A1 (fr) * 1997-05-23 1998-11-26 Kyorasha Co., Ltd. Matiere contenant de l'oxyde de titane et son procede de preparation
JPH11207189A (ja) * 1998-01-22 1999-08-03 Lintec Corp 酸化チタンの被着方法
JPH1120067A (ja) * 1998-06-08 1999-01-26 Toto Ltd 貼着用光触媒機能材
JP2000262905A (ja) * 1999-03-18 2000-09-26 Inax Corp 光触媒タイル
JP2002178459A (ja) * 2000-12-18 2002-06-26 National Institute Of Advanced Industrial & Technology 光触媒担持印刷物
WO2002085989A1 (en) * 2001-04-25 2002-10-31 Nanopac Ltd. Photocatalytic coating material having photocatalytic activity and adsorption property and method for preparing the same
JP2002371479A (ja) * 2001-06-08 2002-12-26 Kuraray Co Ltd 壁 紙
JP2003019764A (ja) * 2001-07-09 2003-01-21 Achilles Corp 光触媒機能を有する装飾シート
JP2003071967A (ja) * 2001-08-31 2003-03-12 Takiron Co Ltd 光触媒層を最外層に形成した化粧板

Non-Patent Citations (10)

* Cited by examiner, † Cited by third party
Title
DATABASE WPI Section Ch Week 199941, Derwent World Patents Index; Class D22, AN 1999-487016, XP002330852 *
DATABASE WPI Section Ch Week 200063, Derwent World Patents Index; Class J04, AN 2000-650450, XP002330851 *
DATABASE WPI Section Ch Week 200276, Derwent World Patents Index; Class D22, AN 2002-700542, XP002283098 *
DATABASE WPI Section Ch Week 200330, Derwent World Patents Index; Class D22, AN 2003-305277, XP002283101 *
DATABASE WPI Section Ch Week 200365, Derwent World Patents Index; Class A97, AN 2003-682980, XP002283099 *
PATENT ABSTRACTS OF JAPAN vol. 1999, no. 04 30 April 1999 (1999-04-30) *
PATENT ABSTRACTS OF JAPAN vol. 2002, no. 10 10 October 2002 (2002-10-10) *
PATENT ABSTRACTS OF JAPAN vol. 2003, no. 04 2 April 2003 (2003-04-02) *
PATENT ABSTRACTS OF JAPAN vol. 2003, no. 05 12 May 2003 (2003-05-12) *
PATENT ABSTRACTS OF JAPAN vol. 2003, no. 07 3 July 2003 (2003-07-03) *

Cited By (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2007040890A2 (en) * 2005-09-30 2007-04-12 3M Innovative Properties Company Photocatalytic coating
WO2007040890A3 (en) * 2005-09-30 2007-10-04 3M Innovative Properties Co Photocatalytic coating
WO2007144718A2 (en) * 2006-06-13 2007-12-21 Flooring Industries Limited, Sarl Method for manufacturing coated panels and coated panel
BE1017168A5 (nl) * 2006-06-13 2008-03-04 Flooring Ind Ltd Werkwijze voor het vervaardigen van vloerpanelen en vloerpaneel.
WO2007144718A3 (en) * 2006-06-13 2008-03-13 Flooring Ind Ltd Method for manufacturing coated panels and coated panel
US20100029471A1 (en) * 2006-11-27 2010-02-04 Ruei-Shan Wang Photocatalyst-synthesized fiber product
GB2445548A (en) * 2007-01-13 2008-07-16 Philip Reed Laminate comprising particle board, and metal in thermoset resin
EP1961556A1 (de) * 2007-02-22 2008-08-27 Hermes Schleifkörper GmbH Zusammengesetzter Werkstoff, Paneel, das solchen zusammengesetzten Werkstoff umfasst, Verfahren zum Herstellen solcher zusammengesetzter Werkstoffe und solcher Paneele
EP1974906A3 (de) * 2007-02-22 2008-12-24 Hermes Schleifkörper GmbH Zusammengesetzter Werkstoff
WO2009062516A3 (en) * 2007-11-16 2009-08-27 Scf Technologies A/S Photocatalytic boards or panels and a method of manufacturing thereof
EP2687373A1 (de) 2007-11-16 2014-01-22 Välinge Photocatalytic AB Impregnierungsflüssigkeit und Verfahren zur Herstellung von photokatalytisch aktiven Platten oder Paneelen unter Verwendung dieser Flüssigkeit
EP2687372A1 (de) 2007-11-16 2014-01-22 Välinge Photocatalytic AB Nanoteilchen enthaltende photokatalytische Platten oder Tafeln und Herstellungsverfahren dafür
EP2174780A1 (de) 2008-10-10 2010-04-14 Sika Technology AG Aufwickelbarer Fliesenaufbau, Verfahren zur Herstellung sowie die Verwendung
US9963609B2 (en) 2009-03-23 2018-05-08 Valinge Photocatalytic Ab Production of titania nanoparticle colloidal suspensions with maintained crystallinity by using a bead mill with micrometer sized beads
WO2011093785A1 (en) * 2010-01-29 2011-08-04 Välinge Innovation AB Method for applying nanoparticles
WO2013006125A1 (en) * 2011-07-05 2013-01-10 Välinge Photocatalytic Ab Coated wood products and method of producing coated wood products
US11045798B2 (en) 2011-07-05 2021-06-29 Valinge Photocatalytic Ab Coated wood products and method of producing coated wood products
US9573126B2 (en) 2012-03-20 2017-02-21 Valinge Photocatalytic Ab Photocatalytic composition
US9375750B2 (en) 2012-12-21 2016-06-28 Valinge Photocatalytic Ab Method for coating a building panel and a building panel
WO2014098762A1 (en) * 2012-12-21 2014-06-26 Välinge Photocatalytic Ab A method for coating a building panel and a building panel
US11666937B2 (en) 2012-12-21 2023-06-06 Valinge Photocatalytic Ab Method for coating a building panel and a building panel
US9945075B2 (en) 2013-09-25 2018-04-17 Valinge Photocatalytic Ab Method of applying a photocatalytic dispersion
WO2020226600A2 (en) 2019-05-06 2020-11-12 Alpay Aytekin Composition used in coating inorganic compounds used in the production of laminate flooring
EP3966038A4 (de) * 2019-05-06 2022-06-15 Alpay, Aytekin Zusammensetzung zur beschichtung anorganischer verbindungen zur herstellung von laminatböden

Also Published As

Publication number Publication date
EP1715995A1 (de) 2006-11-02

Similar Documents

Publication Publication Date Title
EP1715995A1 (de) Photokatalytische teilchen in bodenlaminat
US20100297434A1 (en) Photocatalytic boards or panels and a method of manufacturing thereof
KR101552072B1 (ko) 내오염성과 내수성을 갖는 텍스타일 패브릭 시트 및 이의 제조방법
EP2510074B1 (de) Verwendung von wässrigen schmutzabweisenden dispersionen, weiche schmutzabweisende artikel und verfahren zu ihrer herstellung
EP1358077B1 (de) Schmutzabweisende härtbare beschichtung für ein laminat
KR100661168B1 (ko) 탈취 및 살균 효과를 갖는 직물 성형물의 제조 방법
AU2009329357A1 (en) Painter's canvas including an agent capable of trapping formaldehyde and manufacturing process
WO2007144718A2 (en) Method for manufacturing coated panels and coated panel
KR20070069165A (ko) Ｖｏｃ 제거 기능을 갖는 섬유직물
AU2011209990B2 (en) Method for applying nanoparticles
AU2015346292B2 (en) Soil-resistant, stain-resistant fluorine-free coatings and methods of applying on materials
WO2014113650A1 (en) Curing methods and products produced therefrom
CN103608533A (zh) 涂覆的木制品以及制备涂覆的木制品的方法
AU2004258134A1 (en) Methods and compositions for improving light-fade resistance and soil repellency of textiles and leathers
KR101423279B1 (ko) 미끄럼 방지용 마루판의 제조방법 및 그 미끄럼 방지용 마루판
CN110373915A (zh) 一种可吸收降解甲醛的环保无纺布墙纸及其制备工艺
JP2018008417A (ja) 化粧板
KR100730031B1 (ko) 천연광물을 이용한 건축용 내장 패널
JP6829006B2 (ja) アミノ−ホルムアルデヒド樹脂含浸紙の製造方法、及び化粧板の製造方法
KR102440351B1 (ko) 대리석 보호필름과 보호필름 커팅 장치 및 이들을 이용한 대리석 코팅 시공 방법
EP3204156B1 (de) Verfahren zur herstellung eines fotokatalytischen bituminösen produkts
KR20130123801A (ko) 바이오 액체 벽지 조성물 및 바이오 액체벽지 조성물 제조방법
JP2012016851A (ja) 積層体
WO2014206802A1 (de) Laminat mit aminoplastharz enthaltender beschichtung
JP7473820B2 (ja) 浸透性組成物

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AE AG AL AM AT AU AZ BA BB BG BR BW BY BZ CA CH CN CO CR CU CZ DE DK DM DZ EC EE EG ES FI GB GD GE GH GM HR HU ID IL IN IS JP KE KG KP KR KZ LC LK LR LS LT LU LV MA MD MG MK MN MW MX MZ NA NI NO NZ OM PG PH PL PT RO RU SC SD SE SG SK SL SY TJ TM TN TR TT TZ UA UG US UZ VC VN YU ZA ZM ZW

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): BW GH GM KE LS MW MZ NA SD SL SZ TZ UG ZM ZW AM AZ BY KG KZ MD RU TJ TM AT BE BG CH CY CZ DE DK EE ES FI FR GB GR HU IE IS IT LT LU MC NL PL PT RO SE SI SK TR BF BJ CF CG CI CM GA GN GQ GW ML MR NE SN TD TG

121 Ep: the epo has been informed by wipo that ep was designated in this application
DPEN Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed from 20040101)
NENP Non-entry into the national phase

Ref country code: DE

WWW Wipo information: withdrawn in national office

Country of ref document: DE

WWE Wipo information: entry into national phase

Ref document number: 2005706894

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 2005706894

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 2005706894

Country of ref document: EP