Classifications

• • H—ELECTRICITY
  • H10—SEMICONDUCTOR DEVICES; ELECTRIC SOLID-STATE DEVICES NOT OTHERWISE PROVIDED FOR
  • H10P—GENERIC PROCESSES OR APPARATUS FOR THE MANUFACTURE OR TREATMENT OF DEVICES COVERED BY CLASS H10
  • H10P72/00—Handling or holding of wafers, substrates or devices during manufacture or treatment thereof
  • H10P72/04—Apparatus for manufacture or treatment
  • H10P72/0431—Apparatus for thermal treatment
  • H10P72/0434—Apparatus for thermal treatment mainly by convection
• • C—CHEMISTRY; METALLURGY
  • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
  • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
  • C23C16/00—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes
  • C23C16/44—Chemical coating by decomposition of gaseous compounds, without leaving reaction products of surface material in the coating, i.e. chemical vapour deposition [CVD] processes characterised by the method of coating
  • C23C16/4401—Means for minimising impurities, e.g. dust, moisture or residual gas, in the reaction chamber
  • C23C16/4405—Cleaning of reactor or parts inside the reactor by using reactive gases

Definitions

• the present invention relates to a method for cleaning a heat treatment apparatus for performing a film forming process on a processing target such as a semiconductor wafer. Background technology
• a film forming process and an etching process are performed on a semiconductor wafer.
• various processes such as a film forming process and an etching process are performed on a semiconductor wafer.
• semiconductor wafers are placed on a quartz wafer boat, for example, at a constant pitch. Then, the wafer boat is loaded into the processing container and heated to a predetermined temperature under reduced pressure.
• a processing gas for film formation is supplied to the wafer surface. As a result, decomposition products or reaction products of the processing gas are deposited on the wafer.
• Such a cleaning process is performed not only in the so-called batch-type hot wall type LP-CVD (Chemica 1 Vapor Deposition) (LP-CVD) apparatus described above, but also in a single-wafer processing in which wafers are processed one by one. This is also necessary for membrane devices.
• LP-CVD Cyhemica 1 Vapor Deposition
• a gas containing, for example, C 1 F 3 gas is introduced into the processing container as a cleaning gas, and the cleaning gas removes unnecessary films attached to the wafer boat surface, the processing container inner surface, and the like.
• HF gas is also used as a cleaning gas depending on the type of unnecessary film to be removed.
• a gas having high selectivity between the material constituting the processing container and the film type to be removed by etching is excellent as an etching gas.
• the etching gas a gas that easily reacts with the type of film to be removed by etching and can be efficiently removed, but does not easily react with the constituent materials of the processing container or the like is suitable. ing. ''
• the material constituting the processing vessel or wafer boat and the unnecessary film to be removed by etching are similar or the same type of material, the above selectivity cannot be obtained sufficiently. .
• a silicon oxide film (SiO 2 ) is deposited on the surface of a semiconductor wafer using TEOS (tetraethylorthosilicate) in a heat treatment apparatus in which a processing vessel and a wafer boat are formed of quartz.
• TEOS tetraethylorthosilicate
• the material of such treatment vessel also unnecessary film adhered to the surface of such treatment vessel also is different from the density of the molecule, a S i 0 2 as the main.
• HF gas has conventionally been used alone or together with an inert gas as a carrier gas as a cleaning gas.
• the HF gas has an etching rate (Cl 2) for Si 02 deposited by TE 0 S
• the cleaning process takes a long time because the cleaning rate is not large enough.
• the end point of the cleaning process obtained in advance by calculation or the like may be significantly different from the end point of the actual cleaning process in which unnecessary films are completely removed.
• An object of the present invention is an unnecessary film adhered to a structure in a heat treatment apparatus.
• an object of the present invention is to efficiently and quickly remove an arsenic glass film of TEOS, which is an unnecessary film attached to a structure in a heat treatment apparatus, at a high etching rate, thereby improving the throughput and improving the structure.
• An object of the present invention is to provide a method of cleaning a heat treatment apparatus, which can suppress damage to an object.
• an object of the present invention is to efficiently and quickly remove a boron glass film made of TE0S, which is an unnecessary film attached to a structure in a heat treatment apparatus, at a high etching rate, thereby improving a throughput.
• Another object of the present invention is to provide a cleaning method for a heat treatment apparatus that can also suppress damage to a structure.
• the present invention relates to a cleaning method for a heat treatment apparatus for performing a film formation process of a SiO 2 film using TEOS on a processing target in a processing chamber capable of being evacuated, comprising a HF gas and an NH 3 gas.
• the cleaning method of the heat treatment apparatus further comprises a cleaning step of supplying the inside of the processing container.
• a mixed gas of HF gas and NH 3 gas acts as a cleaning gas to suppress damage to structures in the heat treatment apparatus, and to form a SiO 2 film formed by TEOS. (Silicon oxide film) It is possible to remove it efficiently.
• the temperature of the processing container is in a range of 100 to 300 ° C.
• the pressure in the processing container is 53200 Pa (400 Torr) or more.
• the supply amount of the HF gas is equal to or more than the supply amount of the NH 3 gas.
• the present invention also relates to a method for cleaning a heat treatment apparatus for performing a process of forming an As SG film on a target object using TEOS in a processing chamber capable of being evacuated, comprising: A cleaning method for a heat treatment apparatus, comprising: a cleaning step of supplying three gases into the processing container.
• a mixed gas of HF gas and NH 3 gas acts as a cleaning gas to suppress damage to structures in the heat treatment apparatus, and to reduce an As SG film formed by TEOS ( It is possible to quickly and efficiently remove an unnecessary adhered film (arsenic glass film).
• the present invention provides a cleaning method of a heat treatment apparatus for performing a film forming process B SG film using a TE OS against the object to be processed in a vacuum evacuable processing vessel, HF gas and NH 3
• a cleaning method for a heat treatment apparatus comprising: a cleaning step of supplying gas into the processing container.
• a mixed gas of HF gas and NH 3 gas acts as a cleaning gas to suppress damage to structures in the heat treatment apparatus, and to reduce the BSG film (boron) formed by TEOS. It is possible to quickly and efficiently remove unnecessary adhered films (glass films).
• FIG. 1 is a configuration diagram illustrating an example of a heat treatment apparatus in which a cleaning method according to the present invention is performed.
• FIG. 2 is a diagram showing a comparison result of the etching rate of a silicon oxide film by TEOS and the etching rate of a quartz material.
• FIG. 3 is a configuration diagram showing another example of the heat treatment apparatus in which the cleaning method according to the present invention is performed.
• FIG. 4 is a configuration diagram showing still another example of the heat treatment apparatus in which the cleaning method according to the present invention is performed.
• FIG. 1 is a configuration diagram illustrating an example of a heat treatment apparatus in which a cleaning method according to the present invention is performed.
• the heat treatment apparatus 2 has a vertical processing vessel 8 having a double-quartz structure made of quartz and having an inner cylinder 4 and an outer cylinder 6.
• a processing space S in the inner cylinder 4 accommodates a quartz wafer boat 10 as support means for holding the object to be processed.
• semiconductor wafers W as objects to be processed are held in multiple stages at a predetermined beach.
• the pitch may be constant or may vary depending on the position.
• a cap 12 is provided to open and close the lower part of the processing container 8.
• the rotary shaft 16 is provided on the cap 12 through a magnetic fluid seal 14.
• a rotary table 18 is provided at the upper end of the rotary shaft 16.
• a heating cylinder 20 made of Ishige is provided on the table 18.
• the wafer boat 10 is placed on the heat retaining cylinder 20.
• the rotating shaft 16 is attached to an arm 24 of a boat elevator 22 that can be moved up and down, and can be moved up and down integrally with the cap 12 and the wafer boat 10 and the like.
• the wafer boat 10 can be moved into and out of the processing vessel 8 through the bottom of the processing vessel 8 by the vertical movement by the boat elevator 22.
• the wafer boat 10 may be in a fixed state without being rotated.
• a manifold 26 made of, for example, stainless steel is joined to the lower end opening of the processing container 8.
• the manifold 26 is provided with a film forming gas supply system 28 that supplies a film forming gas.
• the film forming gas supply system 28 has a film forming gas nozzle 30 penetrating through the manifold 26.
• a flow controller 32 such as a mass flow controller is interposed in the film forming gas nozzle 30.
• the connected gas supply path 34 is connected.
• a TEOS source 36 for storing TEOS as a film forming gas is connected to the gas supply path 34.
• this Ma two hold 26 as a cleaning gas 11? Gas and 1 ⁇ 11 3 HF gas supply system 38 and the NH 3 gas supply system 40 for introducing into the gas treatment vessel 8 it it individually It is provided in.
• the HF gas supply system 38 has an HF gas nozzle 42 penetrating through the manifold 26.
• the HF gas nozzle 42 is connected to a gas supply path 46 in which a flow controller 44 such as a muff opening controller is interposed.
• the HF gas source 48 is connected to the gas supply path 46.
• the NH 3 gas supply system 40 has an NH 3 gas nozzle 50 penetrating through the manifold 26.
• the NH 3 gas nozzle 50 is connected to a gas supply path 54 in which a flow controller 52 such as a mass flow controller is provided on the way.
• An NH 3 gas source 56 is connected to the gas supply path 54. Accordingly, each gas supplied from each of the nozzles 30, 42, and 50 rises in the processing space S (wafer accommodation area) in the inner cylinder 4, and turns back downward at the ceiling, and the inner cylinder 4 and the outer cylinder It flows down in the gap between 6 and.
• An exhaust port 58 communicating with the gap between the inner cylinder 4 and the outer cylinder 6 is provided on the bottom side wall of the outer cylinder 6.
• the exhaust port 58 is connected to a vacuum exhaust system 64 including an exhaust path 60 and a vacuum pump 62.
• a vacuum exhaust system 64 including an exhaust path 60 and a vacuum pump 62.
• a heat insulating layer 66 is provided on the outer periphery of the processing container 8.
• a heating heater 68 as a heating means is provided on the inner side of the heat insulating layer 66.
• the wafer W located inside the processing container 8 is heated to a predetermined temperature.
• the overall size of the processing container 8 for example, the size of the wafer W to be formed is 8 inches, and the number of wafers held in the wafer boat 10 is about 150 (about 130 product wafers, dummy wafers, etc.).
• the diameter of the inner cylinder 4 is about 260 to 270 mm
• the diameter of the outer cylinder 6 is about 275 to 285 mm
• the height of the processing container 8 is about 1280 mm.
• the number of wafers held in the wafer boat 10 may be about 25 to 50 in some cases.
• the diameter of the inner cylinder 4 is about 380 to 420 mm
• the diameter of the outer cylinder 6 is about 450 to 500 mm
• the height of the processing vessel 8 is about 800. mm. Note that these numerical values are merely examples.
• a sealing member 70 such as a ring is provided between the cap 12 and the manifold 26 to seal the space therebetween, and is provided between the manifold 26 and the lower end of the outer cylinder 6. Is provided with a sealing member 72 such as an O-ring for sealing here.
• a gas supply system for supplying an inert gas such as N 2 gas is further provided.
• the unprocessed large number of semiconductor wafers W are held in multiple stages at a predetermined pitch in the wafer port 10.
• the wafer boat 10 in this state is inserted into the processing container 8 from below by driving the boat elevator 22 upward.
• the cap 12 seals the inside of the processing container 8.
• the inside of the processing container 8. is preheated in advance.
• the supply voltage to the heating heater 68 is increased, and the temperature of the wafer W is increased to a predetermined processing temperature.
• the inside of the processing container 8 is evacuated by the evacuation system 64.
• the flow 03 from the TEOS source 36 of the film forming gas supply system 28 is introduced into the processing vessel 8 through the film forming gas nozzle 30 while controlling the flow rate.
• the TEOS gas undergoes a thermal decomposition reaction while ascending in the processing vessel 8, and forms a SiO 2 film on the surface of the wafer W.
• the supply of the TEOS gas is stopped, and the residual gas in the processing container 8 is purged and discharged with N 2 gas or the like. Thereafter, the wafer boat 10 is lowered, and the processed wafer W is taken out. Then, a series of film forming processes as described above are repeatedly performed. By repeating such a film forming process, unnecessary films on the internal structures, for example, the surface of the processing vessel 8 including the inner tube 4 and the outer tube 6, the surface of the wafer boat 10, and the surface of the heat retaining tube 20 are formed. i 0 2 film) adheres. Therefore, a cleaning process for shaving and removing these unnecessary films is performed regularly or irregularly.
• the wafer port 10 that does not hold the wafer W is inserted into the processing container 8. Then, the inside of the processing container 8 is sealed. The temperature in the processing container 8 is maintained at a predetermined temperature. In this state, HF gas whose flow rate is controlled is introduced into the processing container 8 from the HF gas nozzle 42 of the HF gas supply system 38 as a cleaning gas. On the other hand, although the flow rate is controlled from the NH 3 gas nozzle 50 of the NH 3 gas supply system 40, the NH 3 gas is introduced into the processing vessel 8.
• the HF gas and the NH 3 gas separately introduced into the processing container 8 are mixed while rising in the processing container 8.
• the cleaning processing time at this time is a time obtained by dividing the integrated amount of the unnecessary film by the etching rate, and can be obtained, for example, by calculation.
• the processing temperature is preferably in the range of 100 to 300 ° C. Further, it is preferable that the processing pressure is 53200 Pa (400 Torr) or more, and the supply amount of HF gas to NH gas is equal to or higher than that of HF gas and the HF gas is rich.
• FIG. 2 is a diagram showing a comparison result between the etching rate of a silicon oxide film and the etching rate of a quartz material by TEOS.
• the temperature during the cleaning process was set to 300 ° C, which is the temperature during the conventional general cleaning process, and the processing pressure was set to 400 Torr (53200 Pa).
• the evaluation was “ ⁇ ” (somewhat good) or “ ⁇ ” (good).
• the flow ratio of HF gas to NH 3 gas is set to 1000: 1000 or 1820: 182, respectively, that is, the supply amount of HF gas is set to be equal to or more than the supply amount of NH 3 gas.
• the etching rates of the silicon oxide film by TEOS were 26.8 nm / min and 96.6 nm / min, respectively. These etching rates were 67 to 240 times higher than those of the conventional method.
• the time required for the cleaning process is reduced, and the operation rate (throughput) of the apparatus can be improved.
• the etching rates for the quartz material were 69.1 nm / min and 196.6 nm / min, respectively. These are quite large, as in the case of the conventional method (170.1 nm / min).
• the overall time required for the cleaning process is significantly reduced, so that even if an error occurs in the end point of the cleaning process, the time during which the cleaning process is erroneously performed excessively is short. Therefore, damage to the quartz material can be significantly suppressed.
• the cleaning process time is calculated as 60 minutes, the cleaning process may be excessively performed for 6 minutes.
• the cleaning processing time is 0.6 minutes (when the etching rate is 96.6 nm / min), so that it is 0.06 minutes (3.6 seconds).
• the cleaning process may be excessively performed. Therefore, in the case of the method of the present invention, the damage given to the quartz material can be suppressed much smaller.
• the evaluation was “ ⁇ ”.
• the etching rate of the silicon oxide film by TEOS was 0.6 nm / min, which was about 1.5 times larger than the conventional method of 0.4 nmZmin. That is, also in this case, although not as large as in the case of the HF gas rich state described above, a sufficient effect can be expected. In this case, the etching rate for the quartz material is 15.9 nm / min, which is considerably small. Therefore, damage to the quartz material when the cleaning process is performed excessively can be suppressed accordingly.
• the processing temperature is maintained at 300 ° C (same as in FIG. 2), the processing pressure is set to 150 Torr (lower than in FIG. 2), and the flow ratio of HF gas to NH 3 gas is 1:
• the silicon oxide film by TEOS was hardly etched.
• the processing pressure was set to be higher than 400 Torr under the same conditions as above, the silicon oxide film of TEOS was sufficiently etched. Therefore, it was confirmed that the pressure during the cleaning process is preferably set to 400 Torr or more.
• the processing temperature is set to 400 ° C (higher than in FIG. 2)
• the processing pressure is set to 400 Torr (same as in FIG. 2)
• the flow rate ratio between HF gas and NH 3 gas is set.
• the processing temperature is set to 100 ° C (lower than in FIG. 2)
• the processing pressure is set to 400 Torr (same as in FIG. 2), and the flow rate ratio between HF gas and NH 3 gas is reduced. 1: 1 (l OOO sc cm: l OOO sccm) and the cleaning process was performed.
• the silicon oxide film was etched by TESOS at an etching rate of 6 nm / min, confirming the effectiveness of the cleaning process.
• the cleaning process was performed at room temperature under the same conditions as above.
• the silicon oxide film by TEOS was not etched. Therefore, it was confirmed that the treatment temperature was preferably set in the range of 100 to 300 ° C.
• FIG. 3 is a configuration diagram showing another example of the heat treatment apparatus in which the cleaning method according to the present invention is performed.
• the heat treatment device shown in Fig. 3 is a heat treatment device that performs As SG film (arsenic glass film) film formation processing on a target object using TEOS in a processing chamber that can be evacuated.
• As SG film arsenic glass film
• the heat treatment apparatus shown in FIG. 3 is provided with a second film-forming gas supply system 128 for supplying TE0A gas for film-forming.
• the second film-forming gas supply system 128 has a second film-forming gas nozzle 130 penetrating through the manifold 26.
• the second film forming gas nozzle 130 is connected to a gas supply path 134 in which a flow controller 132 such as a mass flow controller is provided in the middle.
• a TE OA source 136 for storing TE OA as a second film forming gas is connected to the gas supply path 134.
• the processing volume is controlled while controlling the flow rate of TEOA gas. It can be supplied in the container 8.
• FIG. 3 the same parts as those of the heat treatment apparatus in FIG. 1 are denoted by the same reference numerals, and the description is omitted.
• a large number of unprocessed semiconductor wafers W are held on the wafer boat 10 at a predetermined pitch in multiple stages.
• the wafer boat 10 in this state is inserted into the processing container 8 from below by driving the boat elevator 22 upward.
• the cap 12 seals the inside of the processing container 8.
• the inside of the processing container 8 is preheated in advance.
• the supply voltage to the heating heater 68 is increased, and the temperature of the wafer W is increased to a predetermined processing temperature.
• the inside of the processing container 8 is evacuated by the evacuation system 64.
• the target 03 from the TEOS source 36 of the film forming gas supply system 28 is introduced into the processing vessel 8 via the film forming gas nozzle 30 while controlling the flow rate.
• TEOA from the TEOA source 136 of the second film-forming gas supply system 128 is introduced into the processing vessel 8 through the second film-forming gas nozzle 130 while controlling the flow rate.
• the TEOS gas and TEOA gas undergo a thermal decomposition reaction while rising in the processing vessel 8 to form an AsSG film deposited on the surface of the wafer W.
• the supply of the TEOS gas and the TEOA gas is stopped, and the residual gas in the processing container 8 is purged and discharged by the N 2 gas or the like. After that, the wafer boat 10 is lowered, and the processed wafer W is taken out. Then, a series of film forming processes as described above are repeatedly performed.
• unnecessary films are formed on internal structures, for example, the surface of the processing vessel 8 including the inner cylinder 4 and the outer cylinder 6, the surface of the wafer boat 10, and the surface of the heat retaining cylinder 20.
• SG film adheres. Therefore, a cleaning process for shaving off and removing these unnecessary films regularly or irregularly. Is performed.
• the wafer boat 10 that does not hold the wafer W is inserted into the processing container 8. Then, the inside of the processing container 8 is sealed. The temperature in the processing container 8 is maintained at a predetermined temperature. In this state, HF gas of which flow rate is controlled is introduced into the processing vessel 8 from the HF gas nozzle 42 of the HF gas supply system 38 as a cleaning gas. On the other hand, the flow rate is controlled from the NH 3 gas nozzle 50 of the NH 3 gas supply system 40, but NH 3 gas is introduced into the processing vessel 8.
• the HF gas and the NH 3 gas separately introduced into the processing container 8 are mixed while rising in the processing container 8.
• This mixed gas etches away the As SG film of TEOS and TEOA adhered to the surfaces of the heat retaining cylinder 20, the wafer boat 10, the inner cylinder 4, the outer cylinder 6, and the like, that is, cleans.
• the time for the cleaning process at this time is a time obtained by dividing the integrated amount of the unnecessary film by the etching rate, and is obtained, for example, by calculation.
• the processing temperature is preferably in the range of 100 to 300 ° C.
• the processing pressure is preferably 53200 Pa (400 Torr) or more, and the supply amount of HF gas to NH 3 gas is preferably equal to or more than that, and the HF gas is preferably in a rich state.
• FIG. 4 is a configuration diagram illustrating still another example of the heat treatment apparatus in which the cleaning method according to the present invention is performed.
• the heat treatment apparatus shown in Fig. 4 is a heat treatment apparatus that performs BSG film (boron glass film) deposition processing on a target object using TEOS in a processing vessel that can be evacuated.
• the heat treatment apparatus of FIG. 4, the third film forming gas supply system 228 is provided for supplying BC1 3 gas for film formation.
• the third film-forming gas supply system 228 has a third film-forming gas nozzle 230 penetrating through the manifold 26.
• a gas supply path 234 in which a flow controller 232 such as a mass opening controller is disposed in the middle of the third film forming gas nozzle 230 is connected.
• the gas supply channel 234, BC 1 3 source 236 for storing the BC 1 gas as the third film forming gas is connected.
• BC 1 3 gas can be supplied into the processing barber unit 8 being flow controlled.
• FIG. 4 Other configurations of the heat treatment apparatus of FIG. 4 are the same as those of the heat treatment apparatus of FIG. 4 in FIG. 4, the same parts as those of the heat treatment apparatus in FIG. 1 are denoted by the same reference numerals, and description thereof is omitted.
• a large number of unprocessed semiconductor wafers W are held on the wafer boat 10 at a predetermined pitch in multiple stages.
• the wafer boat 10 in this state is inserted into the processing container 8 from below by driving the boat elevator 22 upward.
• the cap 12 seals the inside of the processing container 8.
• the inside of the processing container 8 is preheated in advance.
• the supply voltage to the heater 68 is increased, and the temperature of the wafer W is raised to a predetermined processing temperature.
• the inside of the processing container 8 is evacuated by the evacuation system 64.
• TEOS from the TEOS source 36 of the film forming gas supply system 28 is introduced into the processing vessel 8 via the film forming gas nozzle 30 while controlling the flow rate.
• BC 1 3 gas from BC 1 3 source 236 of the third film forming gas supply system 228 is introduced into the flow controlled while the third film forming gas nozzle 230 through the processing vessel 8.
• the TEOS gas and BC1 3 gas, and the thermal decomposition reaction while increasing the the processing container 8 is formed by depositing BSG film on the surface of the wafer W.
• the supply of TEOS gas and BC1 3 gas The process is stopped, and the residual gas in the processing vessel 8 is purged and discharged with N 2 gas or the like. Thereafter, the wafer port 10 is lowered, and the processed wafer W is taken out. Then, a series of film forming processes as described above are repeatedly performed.
• unnecessary films for example, the surface of the processing vessel 8 including the inner tube 4 and the outer tube 6
• the surface of the wafer boat 10 and the surface of the heat retaining tube 20 are formed. and 8 are attached (BSG films by 1 3). Accordingly, periodic certain stomach irregularly, cleaning process ⁇ Wareru for removing scraped off these unwanted films.
• the wafer boat 10 that does not hold the wafer W is inserted into the processing container 8. Then, the inside of the processing container 8 is sealed. The temperature in the processing container 8 is maintained at a predetermined temperature. In this state, HF gas of which flow rate is controlled is introduced into the processing vessel 8 from the HF gas nozzle 42 of the HF gas supply system 38 as a cleaning gas. On the other hand, although the flow rate is controlled from the third gas nozzle 50 of the third gas supply system 40, the third gas is introduced into the processing vessel 8.
• the HF gas and the third gas separately introduced into the processing container 8 are mixed while rising in the processing container 8.
• the cleaning processing time at this time is a time obtained by dividing the integrated amount of the unnecessary film by the etching rate, and can be obtained, for example, by calculation.
• the processing temperature is preferably in the range of 100 to 300 ° C.
• the processing pressure is 5320 OPa (400 Torr) or more, and the supply amount of HF gas to NH gas is equal to or higher than that, and the HF gas is rich.
• the object to be processed is not limited to a semiconductor wafer, but may be applied to a heat treatment apparatus for a glass substrate or an LCD substrate.

Landscapes

• Chemical & Material Sciences (AREA)
• General Chemical & Material Sciences (AREA)
• Chemical Kinetics & Catalysis (AREA)
• Engineering & Computer Science (AREA)
• Materials Engineering (AREA)
• Mechanical Engineering (AREA)
• Metallurgy (AREA)
• Organic Chemistry (AREA)
• Chemical Vapour Deposition (AREA)

Priority Applications (1)

Applications Claiming Priority (2)

Publications (1)

Family

ID=33308045

Family Applications (1)

Country Status (4)

Cited By (2)

Families Citing this family (4)

Citations (3)

Family Cites Families (5)

• 2004
  • 2004-04-20 KR KR1020057016741A patent/KR20060002807A/ko not_active Ceased
  • 2004-04-20 US US10/553,828 patent/US20060216949A1/en not_active Abandoned
  • 2004-04-20 WO PCT/JP2004/005644 patent/WO2004095555A1/ja not_active Ceased
  • 2004-04-22 TW TW093111276A patent/TW200504849A/zh not_active IP Right Cessation

Patent Citations (3)

Also Published As

Similar Documents

Legal Events