WO2004074334A1 - 吸液性シート及び非水電解液電池パック - Google Patents
吸液性シート及び非水電解液電池パック Download PDFInfo
- Publication number
- WO2004074334A1 WO2004074334A1 PCT/JP2004/001691 JP2004001691W WO2004074334A1 WO 2004074334 A1 WO2004074334 A1 WO 2004074334A1 JP 2004001691 W JP2004001691 W JP 2004001691W WO 2004074334 A1 WO2004074334 A1 WO 2004074334A1
- Authority
- WO
- WIPO (PCT)
- Prior art keywords
- liquid
- absorbent sheet
- absorbent
- electrolyte
- resin layer
- Prior art date
Abstract
Description
Claims